JP2011001275A - Phosphazene ring-having unsaturated carboxylate compound - Google Patents

Abstract

PROBLEM TO BE SOLVED: To enhance flame retardancy without deteriorating the heat resistance and high temperature reliability of a molded resin article.SOLUTION: A resin composition comprising a phosphazene ring-having unsaturated carboxylate compound represented by formula (1) [wherein (n) is an integer of 1 to 6, at least one of groups A is an unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group, and the others are each 1 to 8C alkoxy or a 6 to 20C aryloxy] and a resin component is produced, and then molded.

Description

  The present invention relates to unsaturated carboxylate compounds, and particularly to unsaturated carboxylate compounds having a phosphazene ring useful as a flame retardant.

  Epoxy carboxylate resins such as epoxy acrylate resins and epoxy methacrylate resins are widely used in industrial and consumer devices, especially electrical products, as functional polymer materials such as photosensitive materials, optical materials, dental materials and electronic materials. It has been. In recent years, in these fields, more advanced and severe performance / physical properties are required, and at the same time, resin materials using epoxy acrylate resins are desired to be highly functional in terms of heat resistance and moisture resistance. Since it has the property of being easily combusted, it is required to impart flame retardancy. For example, when this resin material is used as a photo solder resist in the production of a printed wiring board, a halogen compound or a mixture of a halogen-containing compound and an antimony compound such as antimony oxide is added as a general flame retardant. However, the resin material containing such a flame retardant is a halogen-based gas that may impair the electrical and mechanical properties of electronic components or pollute the environment during combustion or molding. May occur. Therefore, recently, as a flame retardant for the resin material, a non-halogen-based material that hardly generates a halogen-based gas at the time of combustion or molding, for example, a metal hydrate system such as aluminum hydroxide or magnesium hydroxide Flame retardants and phosphorus-based flame retardants such as red phosphorus, phosphate ester, condensed phosphate ester, phosphate amide, and ammonium polyphosphate as described in Patent Documents 1 to 3 have come to be frequently used. Yes.

  Among these, metal hydrate flame retardants exhibit a flame retardant effect because the endothermic reaction of dehydration pyrolysis and the accompanying water release occur in a temperature range that overlaps the thermal decomposition and combustion start temperature of the resin material. However, in order to enhance the effect, it is necessary to add a large amount to the resin material. For this reason, the molded article of the resin material containing this kind of flame retardant has a drawback that the mechanical strength is impaired. On the other hand, among phosphoric flame retardants, phosphoric acid ester and condensed phosphoric acid ester-based ones have a plasticizing effect, so when added in a large amount to the resin material in order to increase the flame retardancy, There are disadvantages such as reduced mechanical strength. In addition, phosphate esters, phosphate amides, and ammonium polyphosphates are easily hydrolyzed, so in materials for the production of resin molded products that require mechanical and electrical long-term reliability. It is practically difficult to use.

  Therefore, as a flame retardant for resin materials, use of a phosphazene flame retardant, which is one of phosphorus flame retardants, as described in Patent Document 4, for example, has been studied. Phosphazene-based flame retardants are less plastic and hydrolysable than other phosphorus-based flame retardants, and can be added to resin materials to increase the effective flame resistance of resin materials. Is expected to be able to.

  However, when the amount of the phosphazene-based flame retardant is increased with respect to the resin material, the heat resistance is lowered, and there is a possibility that the reliability of the resin molded product at a high temperature is lowered. Specifically, in the case of a thermoplastic resin-based resin material, the phosphazene-based flame retardant is likely to bleed out (elution) from the resin molding at a high temperature, and in the case of a thermosetting resin-based resin material If the resin molded product is deformed such as blisters at a high temperature, and the resin molded product is used in the electric / electronic field such as a laminated substrate, there is a possibility of causing a problem such as a short circuit due to the deformation.

Japanese Patent Laid-Open No. 9-258446 JP 2001-72835 A JP 2001-183820 A JP 2001-75270 A

  An object of the present invention is to make it possible to improve the flame retardancy of a phosphazene flame retardant without impairing the heat resistance of the resin molded body.

  As a result of repeated studies to solve the above-mentioned problems, the present inventors have found that when an unsaturated carboxylate compound having a phosphazene ring is used, a resin molded article excellent in heat resistance and flame retardancy can be obtained. I found it.

  The present invention relates to an unsaturated carboxylate compound having a phosphazene ring, and more specifically to an unsaturated carboxylate compound having a phosphazene ring represented by the following formula (1).

In the formula (1), n represents an integer of 1 to 6, A represents a group selected from the group consisting of the following A1, A2, and A3 groups, and at least one is an A3 group.
A1 group: an alkoxy group having 1 to 8 carbon atoms in which at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.
A2 group: an aryloxy group having 6 to 20 carbon atoms in which at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.
A3 group: at least one unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group selected from the group consisting of the following A3-1 group, A3-2 group and A3-3 group.

A3-1 group: an aryloxy group containing an unsaturated carbonyloxy-2-hydroxypropoxy group represented by the following formula (2).

In formula (2), R ^{1 to} R ⁵ are groups selected from the group consisting of an unsaturated carbonyloxy-2-hydroxypropoxy group, a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group. , At least one is an unsaturated carbonyloxy-2-hydroxypropoxy group.

式（３）中、Ｒ^６〜Ｒ^８は、水素原子若しくは炭素数１〜６のアルキル基を示し、Ｙは、ビフェニレン基若しくはナフチル基を示す。 A3-2 group: an unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group represented by the following formula (3).

In formula (3), R < ⁶ > -R < ⁸ > shows a hydrogen atom or a C1-C6 alkyl group, Y shows a biphenylene group or a naphthyl group.

式（４）中、Ｒ^９〜Ｒ^１１は、水素原子若しくは炭素数１〜６のアルキル基を示し、Ｚは、Ｏ、Ｓ、ＳＯ_２、ＣＨ_２、ＣＨ（ＣＨ_３）、Ｃ（ＣＨ_３）_２、Ｃ（ＣＦ_３）_２、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４ＣＨ_２、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４Ｃ（ＣＨ_３）_２およびＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４ＳＯ_２からなる群から選ばれる原子若しくは原子団を示す。 A3-3 group: an unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group represented by the following formula (4).

In formula (4), R ^{9 to} R ¹¹ represent a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and Z represents O, S, SO ₂ , CH ₂ , CH (CH ₃ ), C (CH ₃ ). ) ₂ , C (CF ₃ ) ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ CH ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ An atom or atomic group selected from the group consisting of C (CH ₃ ) ₂ and OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ SO ₂ is shown.

  In the unsaturated carboxylate compound having a phosphazene ring according to the present invention, a part of A in the formula (1) may be a glycidyloxy group-containing group.

  In the unsaturated carboxylate compound having a phosphazene ring according to the present invention, the unsaturated carbonyloxy group in the unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group which is the A3 group in the formula (1) is usually acryloyloxy. Selected from the group consisting of a group, a methacryloyloxy group, a tigloyloxy group and a crotoyloxy group. In the formula (1), n is usually preferably 1 or 2. Furthermore, the compound of formula (1) is usually preferably one in which 1 to (2n + 2) of (2n + 4) A are A3 groups.

  The unsaturated carboxylate compound having a phosphazene ring according to the present invention may be a mixture of two or more of the different n in formula (1), and is acid-modified with a polybasic acid anhydride. Also good. Here, the polybasic acid anhydride for acid modification is usually at least one selected from the group consisting of an aromatic dicarboxylic acid anhydride, an aliphatic dicarboxylic acid anhydride, and an alicyclic dicarboxylic acid anhydride.

  The method for producing an unsaturated carboxylate compound having a phosphazene ring according to the present invention includes a glycidyloxy group-containing cyclic phosphazene compound represented by the following formula (5) and an unsaturated monocarboxylic acid represented by the following formula (9). And the step of reacting.

In the formula (1), n represents an integer of 1 to 6, E represents a group selected from the group consisting of the following E1, E2, and E3 groups, and at least one is an E3 group.
E1 group: An alkoxy group having 1 to 8 carbon atoms in which at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.
E2 group: an aryloxy group having 6 to 20 carbon atoms in which at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.
E3 group: At least one glycidyloxy group-containing aryloxy group selected from the group consisting of the following E3-1 group, E3-2 group, and E3-3 group.

式（６）中、Ｇ^１〜Ｇ^５は、グリシジルオキシ基、水素原子、炭素数１〜６のアルキル基、アルケニル基およびアリール基からなる群から選ばれる基であり、少なくとも１つがグリシジルオキシ基である。 E3-1 group: A glycidyloxy group-containing aryloxy group represented by the following formula (6).

In Formula (6), G ^{1 to} G ⁵ are groups selected from the group consisting of a glycidyloxy group, a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group, and at least one is a glycidyloxy group. It is.

式（７）中、Ｌはビフェニレン基若しくはナフチル基を示す。 E3-2 group: A glycidyloxy group-containing aryloxy group represented by the following formula (7).

In formula (7), L represents a biphenylene group or a naphthyl group.

式（８）中、Ｍは、Ｏ、Ｓ、ＳＯ_２、ＣＨ_２、ＣＨ（ＣＨ_３）、Ｃ（ＣＨ_３）_２、Ｃ（ＣＦ_３）_２、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４ＣＨ_２、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４Ｃ（ＣＨ_３）_２およびＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４ＳＯ_２からなる群から選ばれる原子若しくは原子団を示す。 E3-3 group: A glycidyloxy group-containing aryloxy group represented by the following formula (8).

In the formula (8), M represents O, S, SO ₂ , CH ₂ , CH (CH ₃ ), C (CH ₃ ) ₂ , C (CF ₃ ) ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H _{4, OCH 2 CH (OH)} CH 2 OC 6 H 4 CH 2, OCH 2 CH (OH) CH 2 OC 6 H 4 C (CH 3) 2 and _{OCH 2 CH (OH) CH 2} OC 6 H 4 SO 2 An atom or atomic group selected from the group consisting of

式（９）において、Ｒ^１２〜Ｒ^１４は、水素原子若しくは炭素数１〜６のアルキル基を示す。

In Formula (9), R < ¹² > -R < ¹⁴ > shows a hydrogen atom or a C1-C6 alkyl group.

  The polymerizable composition according to the present invention contains at least two kinds of unsaturated carboxylate compounds having a phosphazene ring according to the present invention. Moreover, the polymeric composition which concerns on the other form of this invention contains the unsaturated carboxylate compound which has the phosphazene ring which concerns on this invention, and an active energy ray hardening compound.

  The resin composition of the present invention contains the unsaturated carboxylate compound having a phosphazene ring according to the present invention and at least one resin component selected from the group consisting of a thermoplastic resin and a thermosetting resin.

  The resin molded body of the present invention is obtained by curing the polymerizable composition or the resin composition of the present invention. The electrical / electronic component of the present invention uses the resin molded body of the present invention.

  When the unsaturated carboxylate compound having a phosphazene ring according to the present invention is mixed with a resin material for forming a resin molded body, the flame retardancy can be enhanced without impairing the heat resistance of the resin molded body. In addition, the unsaturated carboxylate compound having a phosphazene ring according to the present invention is a resin molded article excellent in heat resistance and flame retardancy by curing itself or with other polymerizable compound. Can be formed.

  According to the production method of the present invention, the unsaturated carboxylate compound having a phosphazene ring according to the present invention can be produced.

  The polymerizable composition and the resin composition of the present invention can form a resin molded article having excellent heat resistance and flame retardancy, which is particularly useful in electrical / electronic component applications.

Unsaturated carboxylate compound having phosphazene ring The unsaturated carboxylate compound having a phosphazene ring according to the present invention is represented by the following formula (1).

  In the formula (1), n represents an integer of 1 to 6, preferably an integer of 1 to 4, and particularly preferably 1 or 2. That is, as an unsaturated carboxylate compound having a phosphazene ring, an unsaturated carboxylate compound having a cyclotriphosphazene (trimer) in which n is 1 and a cyclotetraphosphazene (tetramer) in which n is 2 are particularly preferable. It is an unsaturated carboxylate compound. The unsaturated carboxylate compound having a phosphazene ring may be a mixture of two or more different n.

  In the formula (1), A represents a group selected from the group consisting of the following A1, A2, and A3 groups.

[A1 group]
An alkoxy group having 1 to 8 carbon atoms; This alkoxy group may be substituted with at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group.

  Examples of such alkoxy groups include methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec-butoxy, tert-butoxy, n-pentyloxy, and n-hexyloxy. Group, n-heptyloxy group, n-octyloxy group, ethenyloxy group, 1-propenyloxy group, 2-propenyloxy group, isopropenyloxy group, 3-butenyloxy group, 2-methyl-2-propenyloxy group, 4 -Pentenyloxy group, 2-hexenyloxy group, 1-propyl-2-butenyloxy group, 5-octenyloxy group, benzyloxy group, 2-phenylethoxy group and the like can be mentioned. Among these, a methoxy group, an ethoxy group, an n-propoxy group, a 2-propenyloxy group and a benzyloxy group are preferable, and an ethoxy group and an n-propoxy group are particularly preferable.

[Group A2]
An aryloxy group having 6 to 20 carbon atoms; In the aryloxy group, at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.

  Examples of such aryloxy groups include phenoxy group, methylphenoxy group, dimethylphenoxy group, ethylphenoxy group, ethylmethylphenoxy group, diethylphenoxy group, n-propylphenoxy group, isopropylphenoxy group, isopropylmethylphenoxy group, Isopropylethylphenoxy group, diisopropylphenoxy group, n-butylphenoxy group, sec-butylphenoxy group, tert-butylphenoxy group, n-pentylphenoxy group, n-hexylphenoxy group, ethenylphenoxy group, 1-propenylphenoxy group, 2-propenylphenoxy group, isopropenylphenoxy group, 1-butenylphenoxy group, sec-butenylphenoxy group, 1-pentenylphenoxy group, 1-hexenylphenoxy group, Nirufenokishi group, naphthyloxy group, and an anthryl group and phenanthryloxy groups and the like. Of these, a phenoxy group, a methylphenoxy group, a dimethylphenoxy group, a diethylphenoxy group, a 2-propenylphenoxy group, a phenylphenoxy group, and a naphthyloxy group are preferable, and a phenoxy group, a methylphenoxy group, a dimethylphenoxy group, and a naphthyloxy group are particularly preferable. preferable.

[Group A3]
At least one unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group selected from the group consisting of the following A3-1 group, A3-2 group, and A3-3 group.
The unsaturated carbonyloxy group in the unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group is usually selected from an acryloyloxy group, a methacryloyloxy group, a tigloyloxy group, and a crotoyloxy group.

式（２）において、Ｒ^１〜Ｒ^５は、不飽和カルボニルオキシ−２−ヒドロキシプロポキシ基、水素原子、炭素数１〜６のアルキル基、アルケニル基およびアリール基からなる群から選ばれる基であり、少なくとも１つが不飽和カルボニルオキシ−２−ヒドロキシプロポキシ基である。 A3-1 group: an aryloxy group containing an unsaturated carbonyloxy-2-hydroxypropoxy group represented by the following formula (2).

In Formula (2), R ^{1 to} R ⁵ are groups selected from the group consisting of an unsaturated carbonyloxy-2-hydroxypropoxy group, a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group. , At least one is an unsaturated carbonyloxy-2-hydroxypropoxy group.

  Examples of the unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group represented by the formula (2) include 4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group, 2-methyl-3- ( 3-acryloyloxy-2-hydroxypropoxy) -phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -4-methyl-phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -5-methyl-phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group, 2-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) -phenyl Oxy group, 3-methyl-4- (3-acryloyloxy-2- Droxypropoxy) -phenyloxy group, 4- (3-acryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -4-ethyl -Phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -5-ethyl-phenyloxy group, 3-ethyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group, 4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group, 2-methyl-3- (3-methacryloyloxy-2-hydroxypropoxy) -phenyloxy group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -4-methyl-phenyloxy group, 3- (3-methyl Acryloyloxy-2-hydroxypropoxy) -5-methyl-phenyloxy group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group, 2-methyl-4- (3-methacryloyl) Oxy-2-hydroxypropoxy) -phenyloxy group, 3-methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) -phenyloxy group, 4- (3-methacryloyloxy-2-hydroxypropoxy) -3, 5-dimethyl-phenyloxy group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -4-ethyl-phenyloxy group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-ethyl-phenyloxy Group and 3-ethyl-4- (3-methacryloyloxy Ci-2-hydroxypropoxy) phenyloxy group and the like.

  Among these, 4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -4-methyl-phenyloxy group, 3-methyl-4- (3 -Acryloyloxy-2-hydroxypropoxy) -phenyloxy group, 4- (3-acryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group, 4- (3-methacryloyloxy-2-hydroxypropoxy) ) Phenyloxy group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -4-methyl-phenyloxy group, 3-methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) -phenyloxy group and 4 -(3-Methacryloyloxy-2-hydroxypropo Iii) -3,5-dimethyl-phenyloxy group is preferred, 4- (3-acryloyloxy-2-hydroxypropoxy) -phenyloxy group, 3-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) -Phenyloxy group, 4- (3-acryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group, 4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group, 3-methyl- 4- (3-methacryloyloxy-2-hydroxypropoxy) -phenyloxy group and 4- (3-methacryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group are particularly preferred.

A3-2 group: an unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group represented by the following formula (3).

式（３）において、Ｒ^６〜Ｒ^８は水素原子若しくは炭素数１〜６のアルキル基を示し、Ｙはビフェニレン基若しくはナフチル基を示す。

In Formula (3), R ^{6 to} R ⁸ represent a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and Y represents a biphenylene group or a naphthyl group.

  Examples of the unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group represented by the formula (3) include a 2- (4 ′-(3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 3 -(4 '-(3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 4- (4'-(3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 4- (3- Acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 5- (3-acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 6- (3-acryloyloxy-2-hydroxypropoxy) naphthyl- 1-oxy group, 2- (4 ′-(3-methacryloyloxy-2- Droxypropoxy) phenyl) phenyloxy group, 3- (4 ′-(3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 4- (4 ′-(3-methacryloyloxy-2-hydroxypropoxy) Phenyl) phenyloxy group, 4- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 5- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group and 6- (3 -Methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group and the like.

  Among these, 3- (4 ′-(3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 4- (4 ′-(3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 4 -(3-acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 3- (4 '-(3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 4- (4'-(3 -Methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group and 4- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group are preferred, and 4- (4 '-(3-acryloyloxy-2) -Hydroxypropoxy) phenyl) phenyloxy group, 4- (3-acrylic Yloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 4- (4 ′-(3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group and 4- (3-methacryloyloxy-2-hydroxypropoxy) A naphthyl-1-oxy group is particularly preferred.

A3-3 group: an unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group represented by the following formula (4).

式（４）において、Ｒ^９〜Ｒ^１１は、水素原子若しくは炭素数１〜６のアルキル基を示し、Ｚは、Ｏ、Ｓ、ＳＯ_２、ＣＨ_２、ＣＨ（ＣＨ_３）、Ｃ（ＣＨ_３）_２、Ｃ（ＣＦ_３）_２、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４ＣＨ_２、ＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４Ｃ（ＣＨ_３）_２およびＯＣＨ_２ＣＨ（ＯＨ）ＣＨ_２ＯＣ_６Ｈ_４ＳＯ_２からなる群から選ばれる原子若しくは原子団を示す。

In Formula (4), R ^{9 to} R ¹¹ represent a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and Z represents O, S, SO ₂ , CH ₂ , CH (CH ₃ ), C (CH ₃ ). ) ₂ , C (CF ₃ ) ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ CH ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ An atom or atomic group selected from the group consisting of C (CH ₃ ) ₂ and OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ SO ₂ is shown.

Here, in R ^{9 to} R ¹¹ , R ⁹ and R ¹⁰ are hydrogen atoms, R ¹¹ is preferably a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, R ⁹ and R ¹⁰ are hydrogen atoms, and R 9 ¹¹ is particularly preferably a hydrogen atom or a methyl group having 1 carbon atom.

Further, Z _{is, O, SO 2, CH 2} , C (CH 3) 2, OCH 2 CH (OH) CH 2 OC 6 H 4, OCH 2 CH (OH) CH 2 OC 6 H 4 C (CH 3) ₂ and OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ SO ₂ are preferred, O, SO ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ and OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ SO ₂ is particularly preferred.

  In formula (1), A includes (2n + 4) A, and at least one of them is an A3 group. Therefore, the unsaturated carboxylate compound having the phosphazene ring of the present invention represented by the formula (1) can be roughly divided into the following forms.

[Form 1]
All (2n + 4) A's are A3 groups. In this case, all of A may be the same A3 group or two or more A3 groups.

  Examples of the unsaturated carboxylate compound having a phosphazene ring of this form include an unsaturated carboxylate compound having a cyclotriphosphazene ring in which n is 1 in formula (1), and a cyclo in which n in formula (1) is 2. An unsaturated carboxylate compound having a tetraphosphazene ring, an unsaturated carboxylate compound having a cyclopentaphosphazene ring in which n is 3 in formula (1), and a cyclohexaphosphazene ring in which n is 4 in formula (1) A saturated carboxylate compound wherein all of A are 4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group, 2-methyl-3- (3-acryloyloxy-2-hydroxypropoxy) -phenyloxy Group, 3- (3-acryloyloxy-2-hydroxypropoxy) -4 Methyl-phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -5-methyl-phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group, 2-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) -phenyloxy group, 3-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) -phenyloxy group, 4- (3-acryloyl) Oxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group, 3- (3-acryloyloxy-2-hydroxypropoxy) -4-ethyl-phenyloxy group, 3- (3-acryloyloxy-2- Hydroxypropoxy) -5-ethyl-phenyloxy group, 3-ethyl-4- 3-acryloyloxy-2-hydroxypropoxy) phenyloxy group, 2- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 3- (4- (3-acryloyloxy-2-hydroxy) Propoxy) phenyl) phenyloxy group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 4- (3-acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 5- (3-acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 6- (3-acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 4- (4- (3-acryloyloxy) -2-hydroxypropoxy) phenyloxy) phenylo Xoxy group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylthio) phenyloxy group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenyloxy group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylethylidene) phenyloxy group, 4- (4- (3 -Acryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylhexafluoroisopropylidene) phenyloxy group, 4- (3- (4 -(4- (3-acryloyloxy- -Hydroxypropoxy) phenyl) phenoxy) -2-hydroxypropoxy) phenyloxy group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxypropoxy) Phenyloxy group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenyl) -2-hydroxypropoxy) phenyloxy group, 4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group, 2-methyl- 3- (3-Methacryloyloxy-2 Hydroxypropoxy) -phenyloxy group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -4-methyl-phenyloxy group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-methyl-phenyloxy Group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group, 2-methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) -phenyloxy group, 3-methyl- 4- (3-methacryloyloxy-2-hydroxypropoxy) -phenyloxy group, 4- (3-methacryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group, 3- (3-methacryloyloxy- 2-Hydroxypropoxy) -4-ethyl-pheny Ruoxy group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-ethyl-phenyloxy group, 3-ethyl-4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group, 2- (4 -(3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 3- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group, 4- (4- (3-methacryloyloxy) 2-hydroxypropoxy) phenyl) phenyloxy group, 4- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group, 5- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy The group 6- (3-methacryloyloxy-2- Droxypropoxy) naphthyl-1-oxy group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy) phenyloxy group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) Phenylthio) phenyloxy group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenyloxy group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group 4- (4- (3- (methacryloyloxy-2-hydroxypropoxy) phenylethylidene) phenyloxy group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy group, 4- (4- (3-Metac Royloxy-2-hydroxypropoxy) phenylhexafluoroisopropylidene) phenyloxy group, 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2-hydroxypropoxy) phenyl An oxy group, a 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxypropoxy) phenyloxy group, a 4- (3- (4- (4- (3-Methacryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group and 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) Sulfonyl) phenyl) -2-hydride Roxypropoxy) those which are a kind of A3 group selected from the group A3 consisting of phenyloxy groups, those in which all of A are two or more kinds of A3 groups selected from the A3 group, and any mixtures thereof Can be mentioned.

[Form 2]
A part (that is, at least one) of (2n + 4) A is an A3 group, and the other A is a group selected from the A1 group and the A2 group. When two or more of (2n + 4) A are A3 groups, each A3 group may be the same or different. Further, A other than A3 group may be all the same A1 group or A2 group, or two or more kinds of A1 groups or A2 groups or one kind or two or more kinds of A1 groups and A2 groups are mixed. It may be in the state.

  As the unsaturated carboxylate compound having a phosphazene ring of this form, 1 to (2n + 2) out of (2n + 4) A are A3 groups. In particular, an unsaturated carboxylate compound having a cyclotriphosphazene ring in which n of formula (1) is 1, an unsaturated carboxylate compound having a cyclotetraphosphazene ring in which n of formula (1) is 2, formula (1) An unsaturated carboxylate compound having a cyclopentaphosphazene ring in which n is 3 and an unsaturated carboxylate compound having a cyclohexaphosphazene ring in which n is 4 in formula (1), wherein (2n + 4) A Among them, those having 1 to (2n + 2) A3 groups and mixtures thereof are preferable.

  When this type of unsaturated carboxylate compound having a phosphazene ring is used, a resin molded article having superior heat resistance (ie, glass transition) compared to the case of using an epoxy unsaturated carboxylate compound having another phosphazene ring. This is advantageous in that a resin molded body having a higher temperature can be realized.

  In addition, it is determined by TOF-MS analysis of an unsaturated carboxylate compound having a phosphazene ring or an intermediate in the production process thereof, whether 1 to (2n + 2) of (2n + 4) A is an A3 group. Can be confirmed.

Examples of the unsaturated carboxylate compound having a phosphazene ring of this form include an unsaturated carboxylate compound having a cyclotriphosphazene ring in which n is 1 in the formula (1), and a cyclo in which n in the formula (1) is 2. An unsaturated carboxylate compound having a tetraphosphazene ring, an unsaturated carboxylate compound having a cyclopentaphosphazene ring in which n is 3 in formula (1), and a cyclohexaphosphazene ring in which n is 4 in formula (1) A saturated carboxylate compound, wherein A is a combination of 4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group which is A3 group and n-propoxy group which is A1 group, and is A3 group 4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group and A2 group. Combination with phenoxy group, combination of 4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group as A3 group and methylphenoxy group as A2 group, 2-methyl- as A3 group Combination of 3- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group and phenoxy group which is A2 group, 2-methyl-3- (3-acryloyloxy-2-hydroxypropoxy) which is A3 group Combination of phenyloxy group and methylphenoxy group which is A2 group, 3- (3-acryloyloxy-2-hydroxypropoxy) -4-methyl-phenyloxy group which is A3 group and n-propoxy which is A1 group In combination with a group, 3- (3-acryloyloxy-2-hydroxypropoxy) which is an A3 group Combination of 4-methyl-phenyloxy group and phenoxy group which is A2 group, 3- (3-acryloyloxy-2-hydroxypropoxy) -4-methyl-phenyloxy group which is A3 group and A2 group A combination with a methylphenoxy group, a combination of 3- (3-acryloyloxy-2-hydroxypropoxy) -5-methyl-phenyloxy group which is an A3 group and an n-propoxy group which is an A1 group, Combination of 3- (3-acryloyloxy-2-hydroxypropoxy) -5-methyl-phenyloxy group which is A3 group and phenoxy group which is A2 group, 3- (3-acryloyl which is A3 group Oxy-2-hydroxypropoxy) -5-methyl-phenyloxy group and A2 group methylphenoxy group, A3 group 3- (3-acryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group and n-propoxy group which is A1 group, 3- (3-acryloyloxy-2 which is A3 group -Hydroxypropoxy) -6-methyl-phenyloxy group in combination with phenoxy group which is A2 group, 3- (3-acryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group which is A3 group And a combination of a methylphenoxy group which is an A2 group, a combination of 2-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group which is an A3 group and an n-propoxy group which is an A1 group 2-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group which is A3 group A combination of a phenoxy group that is an A2 group, a combination of a 2-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group that is an A3 group and a methylphenoxy group that is an A2 group, A combination of 3-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group which is A3 group and n-propoxy group which is A1 group, 3-methyl-4- ( 3-acryloyloxy-2-hydroxypropoxy) phenyloxy group and A2 group phenoxy group in combination, A3 group 3-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group In combination with a methylphenoxy group which is an A2 group, 4- (3-acryloyloxy-2-yl which is an A3 group A combination of droxypropoxy) -3,5-dimethyl-phenyloxy group and n-propoxy group which is A1 group, 4- (3-acryloyloxy-2-hydroxypropoxy) -3,5 which is A3 group A combination of dimethyl-phenyloxy group and phenoxy group which is A2 group, 4- (3-acryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group which is A3 group and A2 group A combination with a certain methylphenoxy group, a combination of 3- (3-acryloyloxy-2-hydroxypropoxy) -4-ethyl-phenyloxy group which is an A3 group and an n-propoxy group which is an A1 group, The A3 group 3- (3-acryloyloxy-2-hydroxypropoxy) -4-ethyl-phenyloxy group and the A2 group In combination with an enoxy group, in combination with an A3 group 3- (3-acryloyloxy-2-hydroxypropoxy) -4-ethyl-phenyloxy group and an A2 group methylphenoxy group, Combination of certain 3- (3-acryloyloxy-2-hydroxypropoxy) -5-ethyl-phenyloxy group and n-propoxy group which is A1 group, 3- (3-acryloyloxy-2 which is A3 group -Hydroxypropoxy) -5-ethyl-phenyloxy group in combination with phenoxy group which is A2 group, 3- (3-acryloyloxy-2-hydroxypropoxy) -5-ethyl-phenyloxy group which is A3 group In combination with a methylphenoxy group which is A2 group, 3-ethyl-4- (3-acryloyloxy- which is A3 group -Hydroxypropoxy) -phenyloxy group in combination with n-propoxy group which is A1 group, 3-ethyl-4- (3-acryloyloxy-2-hydroxypropoxy) -phenyloxy group which is A3 group and A2 In combination with a phenoxy group as a group, in a combination of 3-ethyl-4- (3-acryloyloxy-2-hydroxypropoxy) -phenyloxy group as an A3 group and a methylphenoxy group as an A2 group, A combination of 3- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group which is A3 group and n-propoxy group which is A1 group, 3- (4- ( 3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group and phenoxy group which is A2 group A combination of 3- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group which is A3 group and methylphenoxy group which is A2 group, 4- (4- Combination of (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group and n-propoxy group which is A1 group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) which is A3 group ) Phenyl) A combination of phenyloxy group and phenoxy group which is A2 group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group which is A3 group and methyl which is A2 group In combination with a phenoxy group, 4- (3-acryloyloxy-2-hydroxypropoxy) which is an A3 group Combination of naphthyl-1-oxy group and n-propoxy group which is A1 group, 4- (3-acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group which is A3 group and phenoxy which is A2 group In combination with a group, 4- (3-acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group which is an A3 group and a methylphenoxy group which is an A2 group, 5- Combination of (3-acryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group with n-propoxy group which is A1 group, 5- (3-acryloyloxy-2-hydroxypropoxy) naphthyl which is A3 group A combination of a -1-oxy group and a phenoxy group which is an A2 group, a 5- (3-acryloyloxy-2-hydride which is an A3 group A combination of a xypropoxy) naphthyl-1-oxy group and a methylphenoxy group which is an A2 group, and a 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy) phenyloxy group which is an A3 group Combination of n-propoxy group which is A1 group, combination of 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy) phenyloxy group which is A3 group and phenoxy group which is A2 group A combination of 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy) phenyloxy group which is an A3 group and a methylphenoxy group which is an A2 group, and 4- (4) which is an A3 group 4- (3-acryloyloxy-2-hydroxypropoxy) phenylthio) phenyloxy group and A1 group. Combination of n-propoxy group, combination of 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylthio) phenyloxy group which is A3 group and phenoxy group which is A2 group, A3 group A combination of 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylthio) phenyloxy group and methylphenoxy group which is A2 group, 4- (4- (3-acryloyl) which is A3 group Oxy-2-hydroxypropoxy) phenylsulfonyl) A combination of phenyloxy group and n-propoxy group which is A1 group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylsulfonyl which is A3 group ) Combination of phenyloxy group and phenoxy group which is A2 group, 4- (A3 group which is 4- ( 4- (3-acryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenyloxy group in combination with A2 group methylphenoxy group, A3 group 4- (4- (3-acryloyloxy-2-phenyl) A combination of hydroxypropoxy) benzyl) phenyloxy group and n-propoxy group which is A1 group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group which is A3 group and A2 A combination of a phenoxy group as a group, a combination of a 4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group as an A3 group and a methylphenoxy group as an A2 group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl as the A3 group A combination of a n-propoxy group that is an A1 group and a 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylethylidene) phenyloxy group and an A2 group that are A3 groups. A combination with a certain phenoxy group, a combination of 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylethylidene) phenyloxy group with an A3 group and a methylphenoxy group with an A2 group, A3 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl isopropylidene) phenyloxy group which is a group and an n-propoxy group which is an A1 group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy A combination of a phenoxy group which is an A2 group, a 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy group which is an A3 group and a methylphenoxy group which is an A2 group; A combination of 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylhexafluoroisopropylidene) phenyloxy group which is an A3 group and an n-propoxy group which is an A1 group, A3 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylhexafluoroisopropylidene) phenyloxy group which is a group and a phenoxy group which is an A2 group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl hexafluoroisopropyl A combination of (ropyridene) phenyloxy group and methylphenoxy group which is A2 group, 4- (3- (4- (4- (3- (acryloyloxy-2-hydroxypropoxy) phenyl) phenoxy)-which is A3 group 2-hydroxypropoxy) phenyloxy group and A1 group
4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2-hydroxypropoxy) phenyloxy group which is an A3 group in combination with a certain n-propoxy group 4- (3- (4- (4- (3- (acryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2-hydroxypropoxy) phenyl in combination with phenoxy group which is A2 group and A3 group Combination of oxy group and methylphenoxy group which is A2 group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxy which is A3 group A combination of propoxy) phenyloxy group and n-propoxy group which is A1 group, 4- (3- (4- ( -(3-acryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxypropoxy) A combination of phenyloxy group and phenoxy group which is A2 group, 4- (3- (4- (4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxypropoxy) a combination of a phenyloxy group and a methylphenoxy group which is an A2 group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with n-propoxy group which is A1 group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) ) Phenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (3- (4- (4- (3-acryloyloxy-) 2-hydroxypropoxy) phenyl isopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group and A2 group methylphenoxy group, A3 group 4- (3- (4- (4- (4- ( 3-acryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenoxy) -2-hydroxypropoxy) a combination of phenyloxy group and n-propoxy group which is A1 group, 4- (3- (4 -(4- (3-acryloyloxy-2-hydroxypropoxy) phenylsulfonyl) fe Noxy) -2-hydroxypropoxy) phenyloxy group and A2 group phenoxy group in combination, A3 group 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy)) Phenylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy group and A2 group methylphenoxy group, A3 group 4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group and A1 A combination with the n-propoxy group which is a group, a combination of 4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, an A3 group 4- (3-Methacryloyloxy-2-hydroxypropoxy) phenyloxy group and A2 group In combination with a certain methylphenoxy group, in combination with a 2-methyl-3- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group as an A3 group and a phenoxy group as an A2 group, A combination of a certain 2-methyl-3- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group and a methylphenoxy group that is A2 group, 3- (3-methacryloyloxy-2-hydroxy that is A3 group A combination of propoxy) -4-methyl-phenyloxy group and n-propoxy group which is A1 group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -4-methyl-phenyloxy group which is A3 group In combination with phenoxy group which is A2 group, 3- (3-methacryloyloxy which is A3 group 2-hydroxypropoxy) -4-methyl-phenyloxy group and A2 group methylphenoxy group in combination, A3 group 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-methyl-phenyl A combination of an oxy group and an n-propoxy group that is an A1 group, a 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-methyl-phenyloxy group that is an A3 group, and a phenoxy group that is an A2 group A combination of 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-methyl-phenyloxy group which is an A3 group and a methylphenoxy group which is an A2 group, 3- N- which is (3-methacryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group and A1 group In combination with propoxy group, in combination with A3 group 3- (3-methacryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group and A2 group phenoxy group, A3 group Combination of 3- (3-methacryloyloxy-2-hydroxypropoxy) -6-methyl-phenyloxy group and methylphenoxy group which is A2 group, 2-methyl-4- (3-methacryloyloxy which is A3 group 2-hydroxypropoxy) phenyloxy group in combination with the A1 group n-propoxy group, A3 group 2-methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group and A2 In combination with a phenoxy group which is a group, 2-methyl-4- (3-methacryloyloxy which is an A3 group 2-hydroxypropoxy) phenyloxy group in combination with A2 group methylphenoxy group, A3 group 3-methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group and A1 group A combination of a certain n-propoxy group, a combination of a 3-methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, an A3 group A combination of 3-methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group and methylphenoxy group which is A2 group, 4- (3-methacryloyloxy-2-group which is A3 group Hydroxypropoxy) -3,5-dimethyl-phenyloxy group and n-propoxy group which is A1 group A combination of 4- (3-methacryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, 4 which is an A3 group -(3-methacryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group in combination with methylphenoxy group which is A2 group, 3- (3-methacryloyloxy-2-group which is A3 group Hydroxypropoxy) -4-ethyl-phenyloxy group in combination with n-propoxy group which is A1 group, 3- (3-methacryloyloxy-2-hydroxypropoxy) -4-ethyl-phenyloxy which is A3 group In combination with a phenoxy group which is an A2 group and 3- (3-methacryloyloxy-2-hydride which is an A3 group Roxypropoxy) -4-ethyl-phenyloxy group and A2 group methylphenoxy group in combination, A3 group 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-ethyl-phenyloxy group In combination with n-propoxy group which is A1 group, combination of 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-ethyl-phenyloxy group which is A3 group and phenoxy group which is A2 group A combination of 3- (3-methacryloyloxy-2-hydroxypropoxy) -5-ethyl-phenyloxy group which is A3 group and methylphenoxy group which is A2 group, 3-ethyl- which is A3 group 4- (3-Methacryloyloxy-2-hydroxypropoxy) -phenyloxy group and n-propoxy group which is A1 group In combination with a group, 3-ethyl-4- (3-methacryloyloxy-2-hydroxypropoxy) -phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, 3 which is an A3 group -Ethyl-4- (3-methacryloyloxy-2-hydroxypropoxy) -phenyloxy group in combination with methylphenoxy group which is A2 group, 3- (4- (3-methacryloyloxy-2 which is A3 group) -Hydroxypropoxy) phenyl) phenyloxy group in combination with n-propoxy group which is A1 group, 3- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group which is A3 group In combination with a phenoxy group that is an A2 group, 3- (4- (3-methacryloyloxy-2-) that is an A3 group A combination of droxypropoxy) phenyl) phenyloxy group and methylphenoxy group which is A2 group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group which is A3 group and A1 In combination with n-propoxy group which is a group, in combination with 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group which is A3 group and phenoxy group which is A2 group A combination of 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group which is A3 group and methylphenoxy group which is A2 group, 4- (3-methacryloyl which is A3 group Oxy-2-hydroxypropoxy) naphthyl-1-oxy group and n-propoxy group which is A1 group A combination of 4- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group which is an A3 group and a phenoxy group which is an A2 group, 4- (3 -Methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group in combination with A2 group methylphenoxy group, A3 group 5- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1- Combination of oxy group and n-propoxy group which is A1 group, combination of 5- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group which is A3 group and phenoxy group which is A2 group A 5- (3-methacryloyloxy-2-hydroxypropoxy) naphthyl-1-oxy group which is an A3 group A combination of a methylphenoxy group that is two groups, a 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy) phenyloxy group that is an A3 group, and an n-propoxy group that is an A1 group Combination, A3 group 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy) phenyloxy group and A2 group phenoxy group, A3 group 4- ( 4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy) phenyloxy group in combination with A2 group methylphenoxy group, A3 group 4- (4- (3-methacryloyloxy-2- Combination of hydroxypropoxy) phenylthio) phenyloxy group and n-propoxy group which is A1 group Combination of 4- (4- (3- (methacryloyloxy-2-hydroxypropoxy) phenylthio) phenyloxy group which is A3 group and phenoxy group which is A2 group, 4- (4- (3- (3- Combination of methacryloyloxy-2-hydroxypropoxy) phenylthio) phenyloxy group and methylphenoxy group which is A2 group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylsulfonyl) which is A3 group Combination of phenyloxy group and n-propoxy group which is A1 group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenyloxy group which is A3 group and phenoxy which is A2 group In combination with a group, the A3 group 4- (4- (3-methacryloylio 4- (4- (3- (methacryloyloxy-2-hydroxypropoxy) benzyl) phenyl which is a combination of Axy group and methylphenoxy group which is A2 group, and 2-methylpropoxy) phenylsulfonyl) phenyloxy group N-pro which is oxy group and A1 group
A combination of Poxy group, A3 group 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group and A2 group phenoxy group, A3 group Combination of 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group and methylphenoxy group which is A2 group, 4- (4- (3-methacryloyloxy-) which is A3 group 2-hydroxypropoxy) phenylethylidene) phenyloxy group in combination with n1-propoxy group which is A1 group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylethylidene) phenyl which is A3 group Combination of oxy group and phenoxy group which is A2 group, 4- (4- (3 Combination of methacryloyloxy-2-hydroxypropoxy) phenylethylidene) phenyloxy group and methylphenoxy group which is A2 group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylisopropiyl which is A3 group Ridene) A combination of phenyloxy group and n-propoxy group which is A1 group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy group and A2 group which is A3 group In combination with a phenoxy group that is A3, in combination with 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy group that is an A3 group and a methylphenoxy group that is an A2 group , A3 group 4- (4- (3-metac Royloxy-2-hydroxypropoxy) phenylhexafluoroisopropylidene) A combination of phenyloxy group and n-propoxy group which is A1 group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) which is A3 group ) Phenylhexafluoroisopropylidene) A combination of phenyloxy group and phenoxy group which is A2, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylhexafluoroisopropylidene) phenyl which is A3 group Combination of oxy group and methylphenoxy group which is A2 group, 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2-hydroxy which is A3 group Propoxy) with phenyloxy group and A1 group 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with a certain n-propoxy group, A3 group 4- (3- (4- (4- (3- (methacryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2-hydroxypropoxy) phenyl in combination with phenoxy group which is A2 group and A3 group Combination of oxy group and methylphenoxy group which is A2 group, 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxy which is A3 group A combination of propoxy) phenyloxy group and n-propoxy group which is A1 group, 4- (3- ( -(4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with phenoxy group which is A2 group, 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxypropoxy) phenyloxy group and A2 group methylphenoxy group, A3 group 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with an A1 group n-propoxy group, 4- (3- (4- (4- (3-methacryloyloxy-2-hydride) which is the A3 group Xypropoxy) phenyl isopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (3- (4- (4- (3-methacryloyl) Oxy-2-hydroxypropoxy) phenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with methylphenoxy group which is A2 group, 4- (3- (4- (4 -(3-Methacryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenoxy) -2-hydroxypropoxy) A combination of phenyloxy group and n-propoxy group which is A1 group, 4- (3- (4- (4- (3-Methacryloyloxy-2-hydroxypropoxy) fe Nylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group and A3 group 4- (3- (4- (4- (3-methacryloyloxy-2) Mention may be made of -hydroxypropoxy) phenylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy groups in combination with methylphenoxy groups which are A2 groups and any mixtures thereof.

  Among them, an unsaturated carboxylate compound having a cyclotriphosphazene ring in which n in formula (1) is 1, an unsaturated carboxylate compound having a cyclotetraphosphazene ring in which n in formula (1) is 2, and formula (1 ), An unsaturated carboxylate compound having a cyclopentaphosphazene ring in which n is 3, wherein A is an A3 group 4- (3-acryloyl-2-hydroxypropoxy) phenyloxy group and an A2 group phenoxy In combination with a group, in combination with 2-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, 3- Methyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group and phenoxy which is A2 group A combination of 4- (3-acryloyloxy-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, and an A3 group Combination of 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group and phenoxy group which is A2 group, 4- (4- (3-acryloyloxy-2 which is A3 group) -Hydroxypropoxy) phenyloxy) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylthio) phenyloxy group and A2 In combination with a phenoxy group which is a group, 4- (4- (3-acryloyloxy-2-hydride) which is an A3 group A combination of xypropoxy) phenylsulfonyl) phenyloxy group and phenoxy group which is A2 group, 4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group and A2 group which are A3 groups A combination with a phenoxy group which is A3, a combination of 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylethylidene) phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, A3 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy group, which is a group, and a phenoxy group which is an A2 group, 4- (3- (4 -(4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2 -Hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) A combination of 2-hydroxypropoxy) phenyloxy group and phenoxy group which is A2 group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylisopropiyl) which is A3 group Liden) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (3- (4- (4- (3-acryloyloxy-2-hydroxy) Propoxy) phenylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy group and A2 group Combination with phenoxy group, combination of 4- (3-methacryloyl-2-hydroxypropoxy) phenyloxy group which is A3 group and phenoxy group which is A2 group, 2-methyl-4-form which is A3 group A combination of (3-methacryloyl-2-hydroxypropoxy) phenyloxy group and phenoxy group which is A2 group, 3-methyl-4- (3-methacryloyl-2-hydroxypropoxy) phenyloxy group which is A3 group and Combination of phenoxy group which is A2 group, combination of 4- (3-methacryloyl-2-hydroxypropoxy) -3,5-dimethyl-phenyloxy group which is A3 group and phenoxy group which is A2 group , A3 group 4- (4- (3-methacryloyl-2-hydroxypropoxy) phenyl) phenyloxy In combination with phenoxy group as A2 group, in combination with 4- (4- (3-methacryloyl-2-hydroxypropoxy) phenyloxy) phenyloxy group as A3 group and phenoxy group as A2 group , A combination of 4- (4- (3-methacryloyl-2-hydroxypropoxy) phenylthio) phenyloxy group which is A3 group and phenoxy group which is A2 group, 4- (4- (3- (3- Combination of methacryloyl-2-hydroxypropoxy) phenylsulfonyl) phenyloxy group and phenoxy group which is A2 group, 4- (4- (3-methacryloyl-2-hydroxypropoxy) benzyl) phenyloxy group which is A3 group In combination with phenoxy group which is A2 group, 4- (4- (3-methacryloyl) which is A3 group 2-hydroxypropoxy) phenylethylidene) phenyloxy group and a phenoxy group that is A2 group, 4- (4- (3-methacryloyl-2-hydroxypropoxy) phenylisopropylidene) phenyloxy that is A3 group In combination with a phenoxy group which is an A2 group and 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2-hydroxypropoxy) which is an A3 group Combination of phenyloxy group and phenoxy group which is A2 group, 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) -2-hydroxy which is A3 group A combination of propoxy) phenyloxy group and phenoxy group which is A2 group, A3 group Combination of a certain 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group and a phenoxy group which is an A2 group And 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy group which is the A3 group and the phenoxy group which is the A2 group Combinations as well as any mixtures thereof are preferred.

  In particular, an unsaturated carboxylate compound having a cyclotriphosphazene ring in which n of formula (1) is 1 and an unsaturated carboxylate compound having a cyclotetraphosphazene ring in which n of formula (1) is 2, Is a combination of 2-methyl-4- (3-acryloyloxy-2-hydroxypropoxy) phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, 3-methyl-4- ( 3-acryloyloxy-2-hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (3-acryloyloxy-2-hydroxypropoxy) -3,5-dimethyl- Combination of phenyloxy group and phenoxy group which is A2 group, 4- (4- (3-acryloyloxy) which is A3 group 2-hydroxypropoxy) phenyl) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenyloxy group In combination with phenoxy group as A2 group, in combination with 4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group as A3 group and phenoxy group as A2 group , A combination of 4- (3-acryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, 4- (3- (4- (4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2- A combination of droxypropoxy) phenyloxy group and phenoxy group which is A2 group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) benzyl) phenoxy) which is A3 group A combination of 2-hydroxypropoxy) phenyloxy group and phenoxy group which is A2 group, 4- (3- (4- (4- (3-acryloyloxy-2-hydroxypropoxy) phenylisopropiyl) which is A3 group Liden) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (3- (4- (4- (3-acryloyloxy-2-hydroxy) Propoxy) phenylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy group and A2 group A combination with an enoxy group, a combination of 2-methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group which is an A3 group and a phenoxy group which is an A2 group, 3 which is an A3 group -Methyl-4- (3-methacryloyloxy-2-hydroxypropoxy) phenyloxy group and A2 group phenoxy group, A3 group 4- (3-methacryloyloxy-2-hydroxypropoxy)- Combination of 3,5-dimethyl-phenyloxy group and phenoxy group which is A2 group, 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenyloxy group and A2 group which are A3 groups In combination with a phenoxy group which is 4- (4- (3-methacryloyloxy-2-hydride) which is an A3 group Xylpropoxy) phenylsulfonyl) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) benzyl) phenyloxy group and A2 group A combination with a phenoxy group that is A3, a combination of 4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenylisopropylidene) phenyloxy group that is an A3 group and a phenoxy group that is an A2 group, Combination of 4- (3- (4- (4- (3-methacryloyloxy-2-hydroxypropoxy) phenyl) phenoxy) -2-hydroxypropoxy) phenyloxy group which is A3 group and phenoxy group which is A2 group 4- (3- (4- (4- (3-methacryloyloxy-) which is the A3 group -Hydroxypropoxy) benzyl) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group, A3 group 4- (3- (4- (4- (3-methacryloyloxy) 2-Hydroxypropoxy) phenyl isopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group in combination with A2 group phenoxy group and A3 group 4- (3- (4- (4- ( Preference is given to combinations of 3-methacryloyloxy-2-hydroxypropoxy) phenylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy groups with phenoxy groups which are A2 groups and any mixtures thereof.

Process for producing unsaturated carboxylate compound having phosphazene ring The unsaturated carboxylate compound having a phosphazene ring according to the present invention reacts a precursor glycidyloxy group-containing cyclic phosphazene compound with an unsaturated monocarboxylic acid (addition reaction). ) Can be manufactured.

The glycidyloxy group-containing cyclic phosphazene compound used here is represented by the following formula (5).

  In the formula (5), n represents an integer of 1 to 6, preferably an integer of 1 to 4, and particularly preferably 1 or 2. That is, particularly preferable glycidyloxy group-containing cyclic phosphazene compounds are glycidyloxy group-containing cyclotriphosphazene (trimer) in which n is 1 and glycidyloxy group-containing cyclotetraphosphazene (tetramer) in which n is 2. . The glycidyloxy group-containing cyclic phosphazene compound may be a mixture of two or more different n.

  In the formula (5), E is a group selected from the group consisting of the following E1, E2, and E3 groups, and at least one of E is an E3 group.

[E1 group]
An alkoxy group having 1 to 8 carbon atoms; This alkoxy group may be substituted with at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group. Examples of such alkoxy groups and preferred ones thereof include those mentioned in the description of the A1 group.

[E2 group]
An aryloxy group having 6 to 20 carbon atoms; In the aryloxy group, at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted. Examples of such aryloxy groups and preferred ones thereof include those mentioned in the description of the A2 group.

[E3 group]
A group selected from the group consisting of the following E3-1 group, E3-2 group, and E3-3 group.

式（６）において、Ｇ^１〜Ｇ^５は、グリシジルオキシ基、水素原子、炭素数１〜６のアルキル基、アルケニル基およびアリール基からなる群から選ばれる基であり、少なくとも１つがグリシジルオキシ基である。 E3-1 group: A glycidyloxy group-containing aryloxy group represented by the following formula (6).

In Formula (6), G ^{1 to} G ⁵ are groups selected from the group consisting of a glycidyloxy group, a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group, and at least one is a glycidyloxy group. It is.

  Examples of the glycidyloxy group-containing aryloxy group represented by the formula (6) include 2-glycidyloxyphenyloxy group, 3-glycidyloxyphenyloxy group, 4-glycidyloxyphenyloxy group, 2-glycidyloxy-3-methyl- Phenyloxy group, 2-glycidyloxy-4-methyl-phenyloxy group, 2-glycidyloxy-5-methyl-phenyloxy group, 2-glycidyloxy-6-methyl-phenyloxy group, 2-methyl-3-glycidyl Oxy-phenyloxy group, 3-glycidyloxy-4-methyl-phenyloxy group, 3-glycidyloxy-5-methyl-phenyloxy group, 3-glycidyloxy-6-methyl-phenyloxy group, 2-methyl-4 -Glycidyloxy-phenyloxy group, 3-methyl-4-g Sidyloxy-phenyloxy group, 2-glycidyloxy-3,4-dimethyl-phenyloxy group, 2-glycidyloxy-3,5-dimethyl-phenyloxy group, 2-glycidyloxy-3,6-dimethyl-phenyloxy group 2-glycidyloxy-4,5-dimethyl-phenyloxy group, 2-glycidyloxy-4,6-dimethyl-phenyloxy group, 2-glycidyloxy-5,6-dimethyl-phenyloxy group, 3-glycidyloxy -2,4-dimethyl-phenyloxy group, 3-glycidyloxy-2,5-dimethyl-phenyloxy group, 3-glycidyloxy-2,6-dimethyl-phenyloxy group, 3-glycidyloxy-4,5- Dimethyl-phenyloxy group, 3-glycidyloxy-4,6-dimethyl-phenyloxy Group, 3-glycidyloxy-5,6-dimethyl-phenyloxy group, 4-glycidyloxy-2,3-dimethyl-phenyloxy group, 4-glycidyloxy-2,5-dimethyl-phenyloxy group, 4-glycidyl Oxy-2,6-dimethyl-phenyloxy group, 4-glycidyloxy-3,5-dimethyl-phenyloxy group, 4-glycidyloxy-3,6-dimethyl-phenyloxy group, 2-glycidyloxy-3,4 , 5-trimethyl-phenyloxy group, 2-glycidyloxy-3,4,6-trimethyl-phenyloxy group, 2-glycidyloxy-3,5,6-trimethyl-phenyloxy group, 2-glycidyloxy-4, 5,6-trimethyl-phenyloxy group, 2,4,5-trimethyl-3-glycidyloxy-phenyloxy Si group, 2,5,6-trimethyl-3-glycidyloxy-phenyloxy group, 3-glycidyloxy-4,5,6-trimethyl-phenyloxy group, 2,3,5-trimethyl-4-glycidyloxy- Phenyloxy group, 2,3,6-trimethyl-4-glycidyloxy-phenyloxy group, 2-glycidyloxy-3,4,5,6-tetramethyl-phenyloxy group, 3-glycidyloxy-2,4 5,6-tetramethyl-phenyloxy group, 4-glycidyloxy-2,3,5,6-tetramethyl-phenyloxy group, 2,3-diglycidyloxy-4-methyl-phenyloxy group, 2,3 -Diglycidyloxy-5-methyl-phenyloxy group, 2,3-diglycidyloxy-6-methyl-phenyloxy group, 2,4-diglycidyl Xyl-3-methyl-phenyloxy group, 2,4-diglycidyloxy-5-methyl-phenyloxy group, 2,4-diglycidyloxy-6-methyl-phenyloxy group, 2,5-diglycidyloxy- 3-methyl-phenyloxy group, 2,5-diglycidyloxy-4-methyl-phenyloxy group, 2,5-diglycidyloxy-6-methyl-phenyloxy group, 2,6-diglycidyloxy-3- Methyl-phenyloxy group, 2,6-diglycidyloxy-4-methyl-phenyloxy group, 2,6-diglycidyloxy-5-methyl-phenyloxy group, 2-glycidyloxy-3-ethyl-phenyloxy group 2-glycidyloxy-4-ethyl-phenyloxy group, 2-glycidyloxy-5-ethyl-phenyloxy group, 2-glycidyl group Zyloxy-6-ethyl-phenyloxy group, 2-ethyl-3-glycidyloxy-phenyloxy group, 3-glycidyloxy-4-ethyl-phenyloxy group, 3-glycidyloxy-5-ethyl-phenyloxy group, 3 -Glycidyloxy-6-ethyl-phenyloxy group, 2-ethyl-4-glycidyloxy-phenyloxy group, 3-ethyl-4-glycidyloxy-phenyloxy group, 2-glycidyloxy-3-allyl-phenyloxy group 2-glycidyloxy-4-allyl-phenyloxy group, 2-glycidyloxy-5-allyl-phenyloxy group, 2-glycidyloxy-6-allyl-phenyloxy group, 2-allyl-3-glycidyloxy-phenyl An oxy group, a 3-glycidyloxy-4-allyl-phenyloxy group, 3-glycidyloxy-5-allyl-phenyloxy group, 3-glycidyloxy-6-allyl-phenyloxy group, 2-allyl-4-glycidyloxy-phenyloxy group, 3-allyl-4-glycidyloxy-phenyloxy Group, 2-glycidyloxy-3-phenyl-phenyloxy group, 2-glycidyloxy-4-phenyl-phenyloxy group, 2-glycidyloxy-5-phenyl-phenyloxy group, 2-glycidyloxy-6-phenyl- Phenyloxy group, 2-glycidyloxy-3-hydroxy-phenyloxy group, 3-glycidyloxy-4-phenyl-phenyloxy group, 3-glycidyloxy-5-phenyl-phenyloxy group, 3-glycidyloxy-6- Phenyl-phenyloxy group, 2-phenyl-4-glyci Ruoxy-phenyloxy group, 3-phenyl-4-glycidyloxy-phenyloxy group, 2-methyl-3-ethyl-4-glycidyloxy-phenyloxy group, 2-methyl-4-glycidyloxy-5-ethyl-phenyl Oxy group, 2-methyl-4-glycidyloxy-6-ethyl-phenyloxy group, 2-ethyl-3-methyl-4-glycidyloxy-phenyloxy group, 2-ethyl-4-glycidyloxy-5-methyl- Examples thereof include a phenyloxy group and a 2-ethyl-4-glycidyloxy-6-methyl-phenyloxy group.

  Among these, 3-glycidyloxyphenyloxy group, 4-glycidyloxyphenyloxy group, 3-glycidyloxy-4-methyl-phenyloxy group, 3-glycidyloxy-5-methyl-phenyloxy group, 2-methyl-4 -Glycidyloxy-phenyloxy group, 3-methyl-4-glycidyloxy-phenyloxy group, 3-glycidyloxy-2,4-dimethyl-phenyloxy group, 3-glycidyloxy-2,5-dimethyl-phenyloxy group 3-glycidyloxy-4,5-dimethyl-phenyloxy group, 4-glycidyloxy-2,6-dimethyl-phenyloxy group, 4-glycidyloxy-3,5-dimethyl-phenyloxy group, 2,3, 5-trimethyl-4-glycidyloxy-phenyloxy group, 3-glycidyloxy -2,4,5,6-tetramethyl-phenyloxy group, 4-glycidyloxy-2,3,5,6-tetramethyl-phenyloxy group, 3-glycidyloxy-4-ethyl-phenyloxy group, 3 -Glycidyloxy-5-ethyl-phenyloxy group, 3-ethyl-4-glycidyloxy-phenyloxy group, 3-glycidyloxy-4-allyl-phenyloxy group, 3-glycidyloxy-5-allyl-phenyloxy group 3-allyl-4-glycidyloxy-phenyloxy group, 3-glycidyloxy-4-phenyl-phenyloxy group, 3-glycidyloxy-5-phenyl-phenyloxy group and 3-phenyl-4-glycidyloxy-phenyl An oxy group is preferred, 4-glycidyloxyphenyloxy group, 3-methyl-4-g Shijiruokishi - phenyl group, 3,5-4-glycidyloxy-dimethyl - phenyl group and 4-glycidyloxy-3,5-dimethyl - phenyl group is particularly preferred.

式（７）において、Ｌは、ビフェニレン基若しくはナフチル基を示す。 E3-2 group: A glycidyloxy group-containing aryloxy group represented by the following formula (7).

In the formula (7), L represents a biphenylene group or a naphthyl group.

  As the glycidyloxy group-containing aryloxy group represented by the formula (7), 2- (4-glycidyloxyphenyl) phenyloxy group, 3- (4-glycidyloxyphenyl) phenyloxy group, 4- (4-glycidyloxy) Phenyl) phenyloxy group, 4-glycidyloxynaphthyl-1-oxy group, 5-glycidyloxynaphthyl-1-oxy group, 6-glycidyloxynaphthyl-1-oxy and the like. Among these, 3- (4-glycidyloxyphenyl) phenyloxy group, 4- (4-glycidyloxyphenyl) phenyloxy group, 4-glycidyloxynaphthyl-1-oxy group and 5-glycidyloxynaphthyl-1-oxy group are included. 4- (4-Glycidyloxyphenyl) phenyloxy group and 4-glycidyloxynaphthyl-1-oxy group are particularly preferable.

E3-3 group: A glycidyloxy group-containing aryloxy group represented by the following formula (8).

In the formula (8), M represents O, S, SO ₂ , CH ₂ , CH (CH ₃ ), C (CH ₃ ) ₂ , C (CF ₃ ) ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H _{4, OCH 2 CH (OH)} CH 2 OC 6 H 4 CH 2, OCH 2 CH (OH) CH 2 OC 6 H 4 C (CH 3) 2 and _{OCH 2 CH (OH) CH 2} OC 6 H 4 SO 2 An atom or atomic group selected from the group consisting of

  Examples of the glycidyloxy-containing aryloxy group represented by the formula (8) include 4- (4-glycidyloxyphenyloxy) phenyloxy group, 4- (4-glycidyloxyphenylthio) phenyloxy group, 4- (4-glycidyl). Oxyphenylsulfonyl) phenyloxy group, 4- (4-glycidyloxybenzyl) phenyloxy group, 4- (4-glycidyloxyphenylethylidene) phenyloxy group, 4- (4-glycidyloxyphenylisopropylidene) phenyloxy group, 4- (4-glycidyloxyphenyl hexafluoroisopropylidene) phenyloxy group, 4- (3- (4- (4-glycidyloxyphenyl) phenoxy) -2-hydroxypropoxy) phenyloxy group, 4- (3- ( 4- (4-Glycidyloxyben) L) phenoxy) -2-hydroxypropoxy) phenyloxy group, 4- (3- (4- (4-glycidyloxyphenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group and 4- (3- (4 And-(4-glycidyloxyphenylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy group.

  Among these, 4- (4-glycidyloxyphenyloxy) phenyloxy group, 4- (4-glycidyloxyphenylthio) phenyloxy group, 4- (4-glycidyloxyphenylsulfonyl) phenyloxy group, 4- (4- Glycidyloxybenzyl) phenyloxy group, 4- (4-glycidyloxyphenylisopropylidene) phenyloxy group, 4- (3- (4- (4-glycidyloxyphenyl) phenoxy) -2-hydroxypropoxy) phenyloxy group, 4- (3- (4- (4-glycidyloxybenzyl) phenoxy) -2-hydroxypropoxy) phenyloxy group, 4- (3- (4- (4-glycidyloxyphenylisopropylidene) phenoxy) -2-hydroxy Propoxy) phenyloxy group and 4- (3- ( -(4-glycidyloxyphenylsulfonyl) phenoxy) -2-hydroxypropoxy) phenyloxy group is preferred, 4- (4-glycidyloxyphenylsulfonyl) phenyloxy group, 4- (4-glycidyloxybenzyl) phenyloxy group, 4- (4-glycidyloxyphenylisopropylidene) phenyloxy group, 4- (3- (4- (4-glycidyloxyphenyl) phenoxy) -2-hydroxypropoxy) phenyloxy group, 4- (3- (4- (4-glycidyloxybenzyl) phenoxy) -2-hydroxypropoxy) phenyloxy group, 4- (3- (4- (4-glycidyloxyphenylisopropylidene) phenoxy) -2-hydroxypropoxy) phenyloxy group and 4- (3- (4- (4-Gly Jill oxy) phenoxy) -2-hydroxypropoxy) phenyl group are particularly preferred.

  Various glycidyloxy group-containing cyclic phosphazene compounds as described above can be produced based on various literatures, for example, the methods described in Non-Patent Literature 1 and Patent Literatures 5 and 6 below.

PHOSPHAZENES, A WORLDWIDE INSIGHT, M.C. GLERIA, R.A. DE JAEGER, 2004, NOVA SCIENCE PUBLISHERS INC. Company JP 2001-335703 A JP 2007-153748 A

式（９）において、Ｒ^１２〜Ｒ^１４は、水素原子若しくは炭素数１〜６のアルキル基を示す。 On the other hand, the unsaturated monocarboxylic acid used in the production of the unsaturated carboxylate compound having a phosphazene ring according to the present invention is represented by the following formula (9).

In Formula (9), R < ¹² > -R < ¹⁴ > shows a hydrogen atom or a C1-C6 alkyl group.

  In addition, what is preferable as unsaturated monocarboxylic acid shown by Formula (9) is acrylic acid, methacrylic acid, crotonic acid, and tiglic acid.

  The reaction method of a glycidyloxy group-containing cyclic phosphazene compound and an unsaturated monocarboxylic acid is described in many known literatures and can be appropriately selected according to the type of E3 group. For example, as described in Patent Document 7 below, the proportion of the unsaturated group-containing monocarboxylic acid is 0.2 to 1.3 mol with respect to 1 mol of the epoxy group contained in the glycidyloxy group-containing phosphazene compound. The reaction is conducted by heating to 60 to 150 ° C., preferably 70 to 130 ° C. in a solvent or in the absence of a solvent. At this time, for the purpose of preventing gelation due to polymerization during the reaction, it is preferable to use a known polymerization inhibitor such as hydroquinones such as hydroquinone and p-methylhydroquinone in the presence of air. In order to shorten the reaction time, quaternary ammonium salts such as benzyltriethylammonium chloride and tetramethylammonium chloride, pyridines such as pyridine, 2-picoline and 2,6-lutidine lutidine, or triphenylphosphine and tributylphosphine Phosphines or known esterification accelerators can be used.

JP-A-44-31472

  The unsaturated carboxylate compound having a phosphazene ring according to the present invention may have a glycidyloxy group in addition to the unsaturated carbonyloxy-2-hydroxypropoxy group. That is, in the unsaturated carboxylate compound having a phosphazene ring according to the present invention, a part of A in the formula (1) may be a glycidyloxy group-containing group. This glycidyloxy group-containing group is usually one in which the glycidyloxy group of the glycidyloxy group-containing cyclic phosphazene compound represented by the formula (5) used in the above production method remains as it is without reacting with the unsaturated monocarboxylic acid. It is. More specifically, a part of the glycidyloxy group of the E3-1 group remains unreacted, an unreacted E3-2 group or an unreacted E3-3 group. Such glycidyloxy group-containing groups may contain two or more types of unsaturated carboxylate compounds having this form of phosphazene ring.

Acid-modified unsaturated carboxylate compound having a phosphazene ring The unsaturated carboxylate compound having a phosphazene ring according to the present invention may be acid-modified using a polybasic acid anhydride. Since the acid-modified unsaturated carboxylate compound having a phosphazene ring has increased solubility in a dilute alkaline aqueous solution, when the polymerizable composition or resin composition described later is used as a solder resist for circuit board production, the dilute alkaline aqueous solution is used. Development becomes possible and processability is improved.

  Polybasic acid anhydrides used for acid modification are aromatic dicarboxylic acid anhydrides, alicyclic dicarboxylic acid anhydrides and aliphatic dicarboxylic acid anhydrides, such as maleic anhydride, succinic anhydride, itaconic anhydride. Acid, phthalic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, methyl tetraphthalic anhydride, methyl hexaphthalic anhydride, chlorendic anhydride, methyl nadic anhydride, trimellitic anhydride, pyromellitic anhydride, etc. be able to. Of these, maleic anhydride, succinic anhydride, itaconic anhydride, phthalic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, methyltetraphthalic anhydride, methylhexaphthalic anhydride, trimellitic anhydride, and pyromellitic anhydride Acid is preferred.

  The acid-modified unsaturated carboxylate compound having a phosphazene ring can be produced by reacting an unsaturated carboxylate compound having a phosphazene ring with a polybasic acid anhydride. The reaction for this can be carried out with reference to a known reaction method between an unsaturated carboxylate compound having a hydroxyl group and a polybasic acid anhydride.

  At this time, the polybasic acid anhydride is preferably used in an amount of 0.01 to 1.2 equivalents relative to the hydroxyl equivalent of the unsaturated carboxylate compound having a phosphazene ring. It is more preferable to set the equivalent.

  Further, the reaction may be carried out without a solvent or in a solvent. In the case of using a solvent, the usable solvent is not particularly limited. For example, aromatic hydrocarbons such as toluene, xylene, chlorobenzene, dichlorobenzene, and solvent naphtha, acetone, methyl ethyl ketone, and methyl isobutyl ketone are used. Examples of ketones, ethers such as diethyl ether, diisopropyl ether and tetrahydrofuran (THF), and esters such as ethyl acetate, butyl acetate, methyl cersolob acetate, ethyl cersolob acetate, diethylene glycol monomethyl ether acetate and diethylene glycol monoethyl ether acetate be able to. The reaction temperature is not particularly limited as long as the acid-modified unsaturated carboxylate compound having a generated phosphazene ring is not thermally polymerized, but it is usually preferably set to 60 to 130 ° C.

Polymerizable composition The polymerizable composition of the present invention contains at least two kinds of unsaturated carboxylate compounds having a phosphazene ring according to the present invention. Moreover, the polymerizable composition of the other form which concerns on this invention contains the unsaturated carboxylate compound which has the phosphazene ring which concerns on this invention, and an active energy ray hardening compound. In the polymerizable composition of this embodiment, two or more kinds of unsaturated carboxylate compounds having a phosphazene ring according to the present invention may be used in combination. These polymerizable compositions are materials for forming a resin molded body because a curing reaction proceeds and a resinous cured product is formed by blending a polymerization initiator as necessary and irradiating active energy rays. Can be used as

  The active energy ray-curable compound that can be used in the polymerizable composition is various and is not particularly limited. For example, 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, pentaerythritol triacrylate And hydroxyl-containing acrylates such as dipentaerythritol, water-soluble acrylates such as polyethylene glycol diacrylate and polypropylene glycol diacrylate, polyfunctional polyester acrylates of polyfunctional alcohols such as trimethylolpropane triacrylate and pentaerythritol tetraacrylate , Polyfunctional alcohols such as trimethylolpropane and hydrogenated bisphenol A, or polyfunctional phenols such as bisphenol A and biphenol Acrylic acid adducts of polyfunctional or monofunctional polyurethane acrylates, bisphenol A diglycidyl ethers, phenol novolacs or cresol novolac epoxy resins which are isocyanate modified products of the above hydroxyl group-containing acrylates And acrylates corresponding to these various acrylates. These may be used alone or in combination of two or more.

  The polymerization initiator that can be blended when curing the polymerizable composition is not particularly limited as long as it absorbs active energy rays and radically polymerizes unsaturated groups such as acryloyl groups and methacryloyl groups. Benzoins such as benzoin, benzoin methyl ether and benzoin ethyl ether and their alkyl ethers, acetophenone, 2,2-dimethoxy-2-phenylacetophenone, 2,2-diethoxy-2-phenylacetophenone and 1,1-dichloro Acetophenones such as acetophenone, 2-methyl-1- [4- (methylthio) phenyl] -2-morpholinoamino-1-propanone, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -1- Butanone and N, N-dimethylaminoacetofu Aminoacetophenones such as non, 2-hydroxy-2-methyl-1-phenylpropan-1-one, 1- [4- (2-hydroxyethoxy) -phenyl] -2-hydroxy-2-methyl-1-propane Α-hydroxy ketones such as -1-one and 1-hydroxy-cyclohexyl-phenyl-ketone, anthraquinones such as 2-methylanthraquinone, 2-ethylanthraquinone, 2-tert-butylanthraquinone and 1-chloroanthraquinone, 2, Thioxanthones such as 4-dimethylthioxanthone, 2-chlorothioxanthone and 2,4-diisopropylxanthone, ketals such as acetophenone dimethyl ketal and benzyldimethyl ketal, and organic peroxides such as benzoyl peroxide and cumene peroxide Thiols such as 2,4,5-triarylimidazole dimer, riboflavin tetrabutyrate, 2-mercaptobenzoimidazole, 2-mercaptobenzoxazole and 2-mercaptobenzothiazole, 2,4,6-tris-sec -Organic halides such as triazine, 2,2,2-tribromoethanol and tribromomethylphenylsulfone, benzophenones such as benzophenone and 4,4'-bisdiethylaminobenzophenone, and 2,4,6-trimethylbenzoyldiphenylphosphine oxide Etc. Of these, 2-hydroxy-2-methyl-1-phenylpropan-1-one, 2-methyl-1- [4- (methylthio) phenyl] -2-morpholinoamino-1-propanone and 2-benzyl-2- Dimethylamino-1- (4-morpholinophenyl) -1-butanone is particularly preferred.

  In the polymerizable composition containing the active energy ray-curable compound, the ratio of the unsaturated carboxylate compound having a phosphazene ring according to the present invention depends on various conditions such as the type of the active energy ray-curable compound and the use of the polymerizable composition. However, it is preferably set to 0.1 to 200 parts by weight with respect to 100 parts by weight of the active energy ray-curable compound in terms of solid content, and preferably 0.5 to 100 parts by weight. More preferably, it is set to 1 to 50 parts by weight. When the usage-amount of the unsaturated carboxylate compound which has a phosphazene ring is less than 0.1 weight part, there exists a possibility that the resin molding which consists of the said polymeric composition may not show sufficient flame retardance. On the other hand, if it exceeds 200 parts by weight, it may be difficult to obtain a resin molded product having characteristics expected from the active energy ray-curable compound used in the polymerizable composition.

  The above polymerization initiators may be used alone or in combination of two or more. In addition, the above-mentioned polymerization initiator may contain esters such as N, N-dimethylaminobenzoic acid ethyl ester, N, N-dimethylaminobenzoic acid isoamyl ester and N, N-dimethylaminobenzoic acid pentyl, and triethylamine. And a titanocene compound having an absorption in the visible light region (for example, “CGI manufactured by Ciba Specialty Chemicals Co., Ltd.). A polymerization initiation accelerator such as -784 ") can be added.

  The polymerizable composition of the present invention can be obtained by a heating polymerization method in which a polymerization initiator such as an organic peroxide or an azo compound is mixed and heated, or a room temperature polymerization method in which an organic peroxide and an accelerator are mixed. The curing reaction proceeds and a resinous cured product can be formed.

  The organic peroxide that can be used in these polymerization methods is not particularly limited, and examples thereof include tert-butylperoxybenzoate, tert-butylperoxy-2-ethylhexanoate, benzoyl peroxide, and cyclohexanone. Examples include peroxide, methyl ethyl ketone peroxide, and bis-4-tert-butylcyclohexyl peroxydicarbonate. These may be used alone or in combination of two or more.

  The accelerator that can be used in the room temperature polymerization method is not particularly limited. For example, octylic acid such as cobalt, iron, and manganese, and polyvalent metal salts such as naphthenate, dimethylaniline, diethylaniline, p-toluidine and ethanolamine. These may be used alone or in combination of two or more.

  The polymerizable composition of the present invention may contain various additives in a range that does not impair the intended physical properties, depending on the application. Examples of usable additives include natural silica, calcined silica, synthetic silica, amorphous silica, white carbon, alumina, aluminum hydroxide, magnesium hydroxide, calcium silicate, calcium carbonate, zinc borate, zinc stannate, and oxidation. Titanium, zinc oxide, molybdenum oxide, zinc molybdate, natural mica, synthetic mica, aerosil, kaolin, clay, talc, calcined kaolin, calcined clay, calcined talc, wollastonite, short glass fiber, fine glass powder, hollow glass and Inorganic fillers such as potassium titanate fibers, organic fibers such as aramid fibers and polyparaphenylenebenzbisoxazole fibers, surface treatment agents for fillers such as silane coupling agents, waxes, fatty acids and their metal salts, acid amides And mold release agents such as paraffin, phosphorus Esters, condensed phosphate esters, phosphate amides, phosphate amide esters, ammonium phosphate, red phosphorus, chlorinated paraffin, melamine, melamine cyanurate, melam, melem, melon and succinoguanamine, nitrogen-based flame retardants, silicone Flame retardants and flame retardants such as brominated flame retardants, flame retardant aids such as antimony trioxide, anti-dripping agents such as polytetrafluoroethylene (PTFE), UV absorbers such as benzotriazole, hindered phenols and styrene Antioxidants such as fluorinated phenols, photopolymerization initiators such as thioxanthone, fluorescent brighteners such as stilbene derivatives, curing agents, dyes, pigments, colorants, light stabilizers, photosensitizers, thickeners, lubricants Antifoaming agent, leveling agent, brightener, polymerization inhibitor, thixotropic agent, plasticizer, antistatic agent, etc. It can gel.

  Moreover, the polymeric composition of this invention can be adjusted to the viscosity which can be apply | coated with respect to various base materials by adding a solvent if needed and melt | dissolving. Solvents usable here include, for example, ketones such as acetone, methyl ethyl ketone and cyclohexanone, aromatic hydrocarbons such as benzene, toluene and xylene, celsorob, methyl cersorob, butyl cersorob, carbitol, methyl carbitol, butyl carbitol. , Glycol ethers such as propylene glycol monoethyl ether, propylene glycol monomethyl ether, dipropylene glycol dimethyl ether and triethylene glycol monoethyl ether; , Alcohols such as propanol, ethylene glycol and propylene glycol, and aliphatic hydrocarbons such as octane and decane Petroleum ether, petroleum solvents such as petroleum naphtha and solvent naphtha. These solvents may be used alone or in combination of two or more.

  As for the polymerizable composition of the present invention, the curing reaction proceeds by irradiating an active energy ray or heating for itself or the one containing the above-described polymerization initiator or the like, and a resinous cured product is obtained. Can be formed. Since this cured product exhibits a high glass transition temperature, it has excellent mechanical properties at high temperatures, that is, heat resistance, and also exhibits high flame retardancy. For this reason, the polymerizable composition of the present invention can be utilized as a material for producing a resin molding used in various applications, and as a material for coatings, adhesives and other applications.

Resin Composition The resin composition of the present invention comprises an unsaturated carboxylate compound having a phosphazene ring according to the present invention and at least one resin component selected from the group consisting of thermoplastic resins and thermosetting resins. . Here, two or more kinds of unsaturated carboxylate compounds having a phosphazene ring according to the present invention may be used.

  Examples of the thermoplastic resin that can be used in this resin composition include polyethylene resin, polyisoprene resin, polybutadiene resin, chlorinated polyethylene resin, polyvinyl chloride resin, styrene resin, impact-resistant polystyrene resin, acrylonitrile-styrene resin ( AS resin), acrylonitrile-butadiene-styrene resin (ABS resin), methyl methacrylate-butadiene-styrene resin (MBS resin), methyl methacrylate-acrylonitrile-butadiene-styrene resin (MABS resin), acrylonitrile-acrylic rubber-styrene resin (AAS) Resin), polymethyl acrylate resin, polymethyl methacrylate resin, polycarbonate resin, polyphenylene ether resin, modified polyphenylene ether resin, aliphatic polyamid Resin, aromatic polyamide resin, polyethylene terephthalate resin, polypropylene terephthalate resin, polytrimethylene terephthalate resin, polybutylene terephthalate resin and polyethylene naphthalate resin, etc. polyester resin, polyphenylene sulfide resin, polyether ether ketone resin, polysulfone resin, poly Examples include arylate resin, polyether ketone resin, polyether nitrile resin, polythioether sulfone resin, polyether sulfone resin, and liquid crystal polymer resin. Among these, as the modified polyphenylene ether resin, a reactive functional group such as a carboxyl group, an epoxy group, an amino group, a hydroxyl group or an anhydrous dicarboxyl group is usually grafted or copolymerized on a part or all of the polyphenylene ether resin. Those introduced by some method such as are preferable. In addition, when the resin composition is used as a material for casings or parts for electronic equipment, particularly OA equipment, AV equipment, communication equipment, and home appliances, a thermoplastic resin such as polyester resin, ABS resin, polycarbonate resin, It is preferable to use a modified polyphenylene ether resin or a polyamide resin.

  On the other hand, examples of thermosetting resins that can be used in this resin composition include polyurethane resins, phenol resins, melamine resins, urea resins, unsaturated polyester resins, diallyl phthalate resins, silicone resins, maleimide resins, and cyanate ester resins. And maleimide-cyanate resin, benzoxazine resin, polybenzimidazole resin, polyimide resin, polyamideimide resin, polyetherimide resin, polyesterimide resin, polycarbodiimide resin, and epoxy resin. Among these, polyimide resins such as polyimide resin, polyamideimide resin, polyetherimide resin, polyesterimide resin, polycarbodiimide resin, maleimide resin, maleimide-cyanate resin, etc., improve their handling processability and adhesiveness. In addition, thermoplasticity or solvent solubility may be imparted. In addition, the resin composition is used for electronic parts, particularly, sealing materials for various IC elements, substrate materials for wiring boards, insulating materials such as interlayer insulating materials and insulating adhesive materials, and Si-based insulating materials such as Si substrates or SiC substrates. When used as a conductive material and a surface protection material, it is preferable to use polyurethane, phenol resin, bismaleimide resin, cyanate ester resin, bismaleimide-cyanate ester resin, polyimide resin or epoxy resin as the thermosetting resin. preferable.

  In the resin composition of the present invention, the amount of the unsaturated carboxylate compound having a phosphazene ring can be appropriately set according to various conditions such as the type of the resin component and the use of the resin composition. It is preferable to set to 0.1 to 200 parts by weight with respect to 100 parts by weight of the resin component in terms of minutes, more preferably to set to 0.5 to 100 parts by weight, and to 1 to 50 parts by weight. Is particularly preferred. When the usage-amount of the unsaturated carboxylate compound which has a phosphazene ring is less than 0.1 weight part, the resin molding which consists of the said resin composition may not show sufficient flame retardance. On the other hand, if it exceeds 200 parts by weight, the original properties of the resin component may be impaired, and a resin molded product with such properties may not be obtained.

  The resin composition of the present invention is blended with various additives similar to those that can be blended with the polymerizable composition of the present invention, within the range that does not impair the intended physical properties, depending on the application and the type of resin component. can do.

  Moreover, the resin composition of this invention can also mix | blend the hardening | curing agent and hardening accelerator of a thermosetting resin as needed. The curing agent and curing accelerator that can be used are not particularly limited, and are usually amine compounds, phenol compounds, acid anhydrides, imidazoles, and organic metal salts. These can also use 2 or more types together.

  The thing preferable as a resin composition of this invention uses an epoxy resin as a resin component. The usable epoxy resin is not particularly limited as long as it is a compound having two or more epoxy groups in one molecule. For example, phenol novolac type epoxy resin, brominated phenol novolac type epoxy resin, orthocresol novolak Type epoxy resin, biphenyl novolak type epoxy resin, bisphenol-A novolak type epoxy resin and naphthol novolak type epoxy resin, etc., novolak type epoxy resin, bisphenol-A type epoxy resin, brominated Bisphenol-A type epoxy resin, bisphenol-F type epoxy resin, bisphenol-AD type epoxy resin, bisphenol-S type epoxy resin, biphenol type epoxy resin, naphthalene type epoxy resin, shiku Pentagen type epoxy resin, alkyl-substituted biphenol type epoxy resin, polyfunctional phenol type epoxy resin, phenol type epoxy resin obtained by reaction of phenols such as tris (hydroxyphenyl) methane and epichlorohydrin, trimethylolpropane, oligopropylene glycol, and the like Aliphatic epoxy resin obtained by reaction of alcohols such as hydrogenated bisphenol-A and epichlorohydrin, glycidyl ester epoxy obtained by reaction of hexahydrophthalic acid, tetrahydrophthalic acid or phthalic acid and epichlorohydrin or 2-methylepichlorohydrin Resin, glycidylamine epoxy obtained by reaction of amine such as diaminodiphenylmethane and aminophenol with epichlorohydrin Heterocyclic epoxy resins obtained by reaction of polyamines such as fats and isocyanuric acids with epichlorohydrin, phosphazene compounds having glycidyl groups, epoxy-modified phosphazene resins, isocyanate-modified epoxy resins, cycloaliphatic epoxy resins and urethane-modified epoxy resins, etc. Can be mentioned. Among these, phenol novolac type epoxy resins, orthocresol novolac type epoxy resins, bisphenol-A type epoxy resins, biphenol type epoxy resins, biphenyl novolac type epoxy resins, naphthalene type epoxy resins, polyfunctional phenol type epoxy resins and tris (hydroxy) Phenolic epoxy resins obtained by reaction of phenyl) methane with epichlorohydrin are preferred. These epoxy resins may be used alone or in combination of two or more.

  In the resin composition of the present invention using an epoxy resin as a resin component (hereinafter, such a resin composition may be referred to as “epoxy resin composition”), the unsaturated carboxylate compound having a phosphazene ring is an epoxy resin. It can function as a curing agent for epoxy resin by reacting with the epoxy group. Moreover, the epoxy resin composition may contain the other hardening | curing agent.

  Other curing agents used here are not particularly limited, and examples thereof include polyamine curing agents such as aliphatic polyamines, aromatic polyamines, and polyamide polyamines, hexahydrophthalic anhydride, and methyltetrahydrophthalic anhydride. Acid anhydride curing agents, phenolic curing agents such as phenol novolac and cresol novolac, phosphazene compounds having a hydroxy group or glycidyl group, Lewis acids such as boron trifluoride and their salts, and dicyandiamides it can. These may be used alone or in combination of two or more.

  In the epoxy resin composition, the content of the unsaturated carboxylate compound having a phosphazene ring or the total content of the unsaturated carboxylate compound having a phosphazene ring and another curing agent is the amount of the unsaturated phosphazene ring in the resin composition. While maintaining the above-mentioned use amount of the carboxylate compound, it is usually set to be 0.5 to 1.5 equivalents with respect to 1 equivalent of the epoxy group of the epoxy resin from the viewpoint of enhancing the curability of the epoxy resin. Is preferable, and it is more preferable to set to 0.6 to 1.2 equivalents. The ratio of the unsaturated carboxylate compound having a phosphazene ring in the total content of the unsaturated carboxylate compound having a phosphazene ring and the other curing agent is preferably set to 0.1 to 99% by weight, More preferably, it is set to 0.5 to 90% by weight. When the ratio of the unsaturated carboxylate compound which has a phosphazene ring is less than 0.1 weight%, the hardened | cured material of an epoxy resin composition may not show sufficient flame retardance.

  The epoxy resin composition may contain a curing accelerator. The curing accelerator that can be used is various and is not particularly limited. For example, imidazole compounds such as 2-methylimidazole and 2-ethylimidazole, 2- (dimethylaminomethyl) phenol, and the like. There may be mentioned tertiary amine compounds and triphenylphosphine compounds. When using a hardening accelerator, it is preferable to set the usage-amount to 0.01-15 weight part with respect to 100 weight part of epoxy resins, and it is more preferable to set to 0.1-10 weight part.

  The epoxy resin composition may contain a reactive diluent or an additive as necessary. Although the reactive diluent which can be used is not specifically limited, For example, aliphatic alkyl glycidyl ethers, such as butyl glycidyl ether, 2-ethylhexyl glycidyl ether, and allyl glycidyl ether, glycidyl methacrylate, and tertiary carboxylic acid glycidyl ester And alkyl glycidyl esters such as styrene oxide and phenyl glycidyl ether, cresyl glycidyl ether, ps-butylphenyl glycidyl ether and nonylphenyl glycidyl ether. These reactive diluents may be used alone or in combination of two or more. On the other hand, as the additive, those described above can be used.

  The resin composition of the present invention such as the above-mentioned epoxy resin composition can be prepared by mixing each component uniformly. When this resin composition is allowed to stand for 1 to 36 hours in a temperature range of about 100 to 250 ° C. depending on the resin component, a sufficient curing reaction proceeds to form a cured product. For example, when the epoxy resin composition is usually left at a temperature of 150 to 250 ° C. for 2 to 15 hours, a sufficient curing reaction proceeds to form a cured product. In such a curing process, the unsaturated carboxylate compound having a phosphazene ring of the present invention reacts with the resin component of the unsaturated carboxylate compound and is stably held in the cured product. It is hard to lose reliability. Moreover, the unsaturated carboxylate compound which has a phosphazene ring of this invention can improve the flame retardance of the said hardened | cured material, without impairing the mechanical characteristics (especially glass transition temperature) of such hardened | cured material. Therefore, the cured product obtained by the resin composition of the present invention is excellent in heat resistance and flame retardancy. For this reason, the resin composition of this invention can be utilized as a material for manufacture of various resin moldings, and for coating materials, adhesives, and other uses.

Resin molded body The resin molded body of the present invention comprises a cured product formed using the polymerizable composition or the resin composition of the present invention.

  This resin formed body can be obtained by charging the polymerizable composition or resin composition of the present invention into various molding machines, forming it into an arbitrary shape, and curing it by heating or irradiating active energy rays. . In addition, this resin molded product is obtained by dissolving the polymerizable composition or resin composition of the present invention in the above-described solvent, and various base materials such as glass fiber, carbon fiber, polyester fiber, polyamide fiber, alumina. It is obtained by impregnating a base material made of fiber or paper and heat-drying the prepreg obtained by heat drying or curing the prepreg by irradiating active energy rays. There may be. Furthermore, this resin molded body is molded and cured into a film by a method such as coating a coating material or printing ink obtained by dissolving the polymerizable composition or resin composition of the present invention in the above-described solvent. It may be a sheet or film.

  Since the resin molded body of the present invention is composed of the polymerizable composition or the resin composition according to the present invention, it is excellent in heat resistance and flame retardancy. For this reason, this resin molded body is used in electrical and electronic parts, and its constituent materials such as semiconductor encapsulants, circuit board elements (particularly metal-clad laminates, build-up wiring boards, printed wiring board boards, printed circuit boards) Wiring board adhesive, printed wiring board adhesive sheet, printed wiring board insulating circuit protective film, printed wiring board conductor, multilayer printed wiring board sealing material, circuit protective material, coverlay film and coverlay Ink, solder resist) and insulators are particularly preferred.

EXAMPLES The present invention will be specifically described below with reference to examples and the like, but the present invention is not limited by these. In the following, “unit” in “unit mol” means the smallest structural unit of a cyclic phosphazene compound, for example, (PNA ₂ ) for formula (1). In the following description, “%” and “parts” mean “% by weight” and “parts by weight”, respectively, unless otherwise specified.

The cyclic phosphazene compound obtained in the following synthesis examples and the unsaturated carboxylate compound having a phosphazene ring obtained in the examples include measurement of ¹ H-NMR spectrum and ³¹ P-NMR spectrum, CHNP elemental analysis, IR spectrum. , Measurement of elemental chlorine (residual chlorine) by potentiometric titration using silver nitrate after alkali melting, and the results of TOF-MS analysis.

  In the following synthesis examples and examples, the hydroxyl equivalent is defined in JIS K 0070-1992 “Testing methods for acid value, saponification value, ester value, iodine value, hydroxyl value and unsaponified product of chemical products”. The hydroxyl value (mgKOH / g) is measured according to the neutralization titration method of the hydroxyl value measuring method, and the value is converted into the hydroxyl equivalent (g / eq.). The epoxy equivalent (g / eq .: mass g of the composition containing 1 equivalent of an epoxy group) was measured according to the method defined in JIS K-7236 “How to Determine Epoxy Equivalent of Epoxy Resin”.

Synthesis Example 1 (Production of glycidyloxy group-containing cyclic phosphazene compound)
A 5-liter 4-necked flask equipped with a thermometer, stirrer, condenser and dropping funnel was charged with hexachlorocyclotriphosphazene (173.8 g, 1.50 unit mol) under a nitrogen stream, and toluene (2,000 mL). To dissolve. A solution of sodium 4-methoxyphenoxide (146.9 g, 1.01 mol) in THF (450 mL) was added dropwise thereto over 5 hours, and the mixture was stirred at 25 ° C. for 24 hours. This reaction solution was added to a toluene (1,250 g) suspension of sodium phenoxide (336.7 g, 2.90 mol) prepared in advance, and then refluxed at 110 ° C. for 10 hours. The reaction mixture was cooled to room temperature, washed twice with 5% aqueous sodium hydroxide solution, neutralized with dilute nitric acid, and further washed with water. The toluene layer was concentrated under reduced pressure to obtain 373.2 g of product. This product was charged into a 3 liter four-necked flask, and toluene (400 mL) and pyridine (159.8 g, 2.02 mol) were added and dissolved by stirring. Hydrogen chloride gas (97.3 g, 2.67 mol) was introduced into this at an internal temperature of 40 ° C. or lower with stirring. Thereafter, heating was started and toluene was distilled off, followed by heating and stirring at an internal temperature of 200 ° C. After confirming disappearance of the starting material by ¹ H-NMR measurement, the mixture was cooled and diluted with methyl isobutyl ketone (MIBK, 1,000 mL). The MIBK layer was washed with a 5% hydrochloric acid aqueous solution and a 1% hydrochloric acid aqueous solution in this order, neutralized with a 1% sodium hydroxide aqueous solution, and further washed with water. The MIBK layer was concentrated under reduced pressure to obtain 341.3 (yield 94.0%) product. The hydroxyl equivalent weight of this product is 373 g / eq. Met.

  This product was charged into a 3 liter four-necked flask and methanol (1,500 mL) and epichlorohydrin (169.3 g, 1.83 mol), 99% sodium hydroxide (38.8 g, 0.96 mol) were added. The mixture was heated and stirred at an internal temperature of 60 to 65 ° C. for 1 hour. The reaction mixture was concentrated under reduced pressure, diluted with MIBK (1,000 mL), and washed twice with deionized water (500 mL). The MIBK layer was concentrated under reduced pressure to obtain 372.8 g (yield 95.0%) of a brown oily product. The analysis result of this product was as follows.

¹ H-NMR spectrum (in heavy acetone, δ, ppm):
2.7 (1H), 2.9 (1H), 3.3 (1H), 3.9 (1H), 4.2 (1H), 6.5 to 7.3 (14.8H)
◎ ³¹ P-NMR spectrum (in heavy acetone, δ, ppm):
Trimer (P = N) ₃ 9.1 to 10.3
◎ CHNP elemental analysis:
Theoretical value C: 60.3%, H: 4.6%, N: 5.0%, P: 11.1%
Measured value C: 60.1%, H: 4.7%, N: 5.0%, P: 11.0%
◎ TOF-MS (m / z):
726,754,784
◎ Residual chlorine analysis:
<0.1%
◎ Epoxy equivalent:
440 g / eq.

From the above analysis results, the product _{[N 3 P 3 (OC 6} H 4 OC 3 H 5 O) (OC 6 H 5) 5], [N 3 P 3 (OC 6 H 4 OC 3 H 5 O ) ₂ (OC ₆ H ₅ ) ₄ ], [N ₃ P ₃ (OC ₆ H ₄ OC ₃ H ₅ O) ₃ (OC ₆ H ₅ ) ₃ ], the average composition of which is [NP (OC ₆ H ₄ OC ₃ H ₅ O) _1.35 (OC ₆ H ₅ ) _0.65 ] was confirmed to be a glycidyloxy group-containing phosphazene compound.

Synthesis Example 2 (Production of glycidyloxy group-containing cyclic phosphazene compound)
The same operation as in Synthesis Example 1 was carried out except that sodium 3-methyl-4-methoxyphenoxide (147.58 g, 1.01 mol) was used instead of sodium 4-methoxyphenoxide, and 401.1 g (yield 93.1). %) As a brown oily product. The analysis result of this product was as follows.
◎ ¹ H-NMR spectrum (in deuterated chloroform, δ, ppm):
2.1 (3H), 2.7 (1H), 2.9 (1H), 3.3 (1H), 3.6 (1H), 3.9 (1H), 6.7 to 7.2 ( 13H)
◎ ³¹ P-NMR spectrum (in deuterated chloroform, δ, ppm):
Trimer (P = N) ₃ 9.7-10.0
◎ CHNP elemental analysis:
Theoretical value C: 61.0%, H: 4.9%, N: 4.9%, P: 10.7%
Measured value C: 61.1%, H: 4.7%, N: 4.9%, P: 10.6%
◎ TOF-MS (m / z):
780, 866, 952
◎ Epoxy equivalent:
434 g / eq.

From the above analysis results, this product is [N ₃ P ₃ (OC ₆ H ₃ (CH ₃ ) OC ₃ H ₅ O) (OC ₆ H ₅ ) ₅ ], [N ₃ P ₃ (OC ₆ H ₃ ( CH ₃ ) OC ₃ H ₅ O) ₂ (OC ₆ H ₅ ) ₄ ] and [N ₃ P ₃ (OC ₆ H ₃ (CH ₃ ) OC ₃ H ₅ O) ₃ (OC ₆ H ₅ ) ₃ ] It was confirmed that the average composition was [N ₃ P ₃ (OC ₆ H ₃ (CH ₃ ) OC ₃ H ₅ O) _2.0 (OC ₆ H ₅ ) _4.0 ].

Synthesis Example 3 (Production of glycidyloxy group-containing cyclic phosphazene compound)
401.1 g (yield) was obtained in the same manner as in Synthesis Example 1 except that sodium 4-methoxy-3,5-dimethyl-phenoxide (147.58 g, 1.01 mol) was used instead of sodium 4-methoxyphenoxide. 93.1%) of a brown oily product was obtained. The analysis result of this product was as follows.

◎ ¹ H-NMR spectrum (in deuterated chloroform, δ, ppm):
2.2 (12.6H), 2.7 (2.1H), 2.9 (2.1H), 3.3 (2.1H), 3.6 (2.1H), 3.9 (2 .1H), 6.7-7.2 (23.7H)
◎ ³¹ P-NMR spectrum (in deuterated chloroform, δ, ppm):
Trimer (P = N) ₃ 9.4-9.7
◎ CHNP elemental analysis:
Theoretical value C: 61.8%, H: 5.2%, N: 4.7%, P: 10.3%
Measured value C: 61.6%, H: 5.3%, N: 4.7%, P: 10.2%
◎ TOF-MS (m / z):
794,894,993
◎ Epoxy equivalent:
453 g / eq.

From the above analysis results, the product _{[N 3 P 3 (OC 6} H 2 (CH 3) 2 OC 3 H 5 O) (OC 6 H 5) 5], [N 3 P 2 (OC 6 H 2 (CH ₃ ) ₂ OC ₃ H ₅ O) ₂ (OC ₆ H ₅ ) ₄ ] and [N ₃ P ₃ (OC ₆ H ₂ (CH ₃ ) ₂ OC ₃ H ₅ O) ₃ (OC ₆ H ₅ ) ₃ It was confirmed that the average composition was [N ₃ P ₃ (OC ₆ H ₂ (CH ₃ ) ₂ OC ₃ H ₅ O) _2.1 (OC ₆ H ₅ ) _3.9 ]. .

Synthesis Example 4 (Production of glycidyloxy group-containing cyclic phosphazene compound)
A 5-liter 4-necked flask equipped with a thermometer, stirrer, condenser and dropping funnel was charged with hexachlorocyclotriphosphazene (173.8 g, 1.50 unit mol) under a nitrogen stream, and toluene (2,000 mL). To dissolve. A solution of sodium 4- (4′-benzyloxyphenylisopropylidene) phenoxide (343.8 g, 1.01 mol) in THF (450 mL) was added dropwise thereto over 5 hours, and the mixture was stirred at 25 ° C. for 24 hours. This reaction solution was added to a toluene (1,250 g) suspension of sodium phenoxide (336.7 g, 2.90 mol) prepared in advance, and then refluxed at 110 ° C. for 15 hours. The reaction mixture was cooled to room temperature, 5% aqueous sodium hydroxide solution (500 mL) was added, and the mixture was transferred to a separatory funnel. After separating the aqueous layer, the toluene layer was washed with a 5% aqueous sodium hydroxide solution (500 mL), neutralized with dilute nitric acid, and further washed with water. The toluene layer was concentrated under reduced pressure, the concentrated residue was diluted with ethyl acetate (1,000 mL), charged into a 2-liter eggplant flask, charged with 5% palladium carbon catalyst (10 g), and an internal temperature of 20-30 under hydrogen atmosphere. Stir at 5 ° C. for 5 hours. After the catalyst was filtered off, the filtrate was concentrated under reduced pressure to obtain 476.8 g of a pale yellow solid product. This product had a hydroxyl equivalent weight of 481 g / eq. Met.

This product was charged into a 3 liter four-necked flask and methanol (2,000 mL) and epichlorohydrin (183.4 g, 1.98 mol), 99% sodium hydroxide (42.0 g, 1.04 mol) were added. The mixture was heated and stirred at an internal temperature of 60 to 65 ° C. for 1 hour. The reaction mixture was concentrated under reduced pressure, diluted with MIBK (1,000 mL), and washed twice with deionized water (500 mL). The MIBK layer was concentrated under reduced pressure to obtain 372.8 g (yield 95.0%) of a brown oily product. The analysis result of this product was as follows.
◎ ¹ H-NMR spectrum (in deuterated chloroform, δ, ppm):
1.8 (10H), 2.7 (1H), 2.9 (1H), 3.3 (1H), 3.9 (1H), 4.2 (1H), 6.7 to 7.2 ( 18H)
◎ ³¹ P-NMR spectrum (in deuterated chloroform, δ, ppm):
Trimer (P = N) ₃ 9.4-9.7
◎ CHNP elemental analysis:
Theoretical value C: 68.3%, H: 5.7%, N: 3.4%, P: 7.5%
Measured value C: 68.5%, H: 5.8%, N: 3.3%, P: 7.4%
◎ TOF-MS (m / z):
1017, 1180, 1343
◎ Epoxy equivalent:
432 g / eq.

From the above analysis results, the product _{[N 3 P 3 (OC 6} H 4 CH 2 C 6 H 4 OC 3 H 5 O) 2 (OC 6 H 5) 4], [N 3 P 3 (OC 6 _{H 4 CH 2 C 6 H 4} OC 3 H 5 O) 3 (OC 6 H 5) 3] and _{[N 3 P 3 (OC 6} H 4 CH 2 C 6 H 4 OC 3 H 5 O) 4 (OC 6 H ₅ ) ₄ ] and the average composition is [N ₃ P ₃ (OC ₆ H ₂ (CH ₃ ) ₂ OC ₃ H ₅ O) _1.95 (OC ₆ H ₅ ) _4.05 ]. It was confirmed.

Synthesis Example 5 (Production of glycidyloxy group-containing cyclic phosphazene compound)
Similar to Synthesis Example 4 except that sodium 4- (4′-benzyloxyphenylsulfone) phenoxide (366.0 g, 1.01 mol) was used instead of sodium 4- (4′-benzyloxyphenylisopropylidene) phenoxide. By operation, 534.1 g (95.0% yield) of a pale yellow solid product was obtained. The analysis result of this product was as follows.
◎ ¹ H-NMR spectrum (in deuterated chloroform, δ, ppm):
2.7 (1H), 2.9 (1H), 3.3 (1H), 3.9 (1H), 4.2 (1H), 6.7 to 7.2 (9H), 7.9 ( 9H)
◎ ³¹ P-NMR spectrum (in deuterated chloroform, δ, ppm):
Trimer (P = N) ₃ 9.4-9.7
◎ CHNP elemental analysis:
Theoretical value C: 57.0%, H: 4.1%, N: 3.2%, P: 7.1%
Measured value C: 57.2%, H: 4.2%, N: 3.1%, P: 7.0%
◎ TOF-MS (m / z):
1074, 1264, 1453
◎ Epoxy equivalent:
450 g / eq.

From the above analysis results, the product _{[N 3 P 3 (OC 6} H 4 SO 2 C 6 H 4 OC 3 H 5 O) 2 (OC 6 H 5) 4], [N 3 P 3 (OC 6 _{H 4 SO 2 C 6 H 4} OC 3 H 5 O) 3 (OC 6 H 5) 3] and _{[N 3 P 3 (OC 6} H 4 SO 2 C 6 H 4 OC 3 H 5 O) 4 (OC 6 H ₅ ) ₂ ] with an average composition of [N ₃ P ₃ (OC ₆ H ₄ SO ₂ C ₆ H ₄ OC ₃ H ₅ O) _2.1 (OC ₆ H ₅ ) _3.9 ]. I confirmed that there was.

Synthesis Example 6 (Production of glycidyloxy group-containing cyclic phosphazene compound)
A 5-liter 4-necked flask equipped with a thermometer, stirrer, condenser and dropping funnel was charged with hexachlorocyclotriphosphazene (173.8 g, 1.50 unit mol) under a nitrogen stream, and toluene (2,000 mL). To dissolve. A solution of sodium 4-methoxyphenoxide (146.9 g, 1.01 mol) in THF (450 mL) was added dropwise thereto over 5 hours, and the mixture was stirred at 25 ° C. for 24 hours. This reaction solution was added to a toluene (1,250 g) suspension of sodium phenoxide (336.7 g, 2.90 mol) prepared in advance, and then refluxed at 110 ° C. for 10 hours. The reaction mixture was cooled to room temperature, 5% aqueous sodium hydroxide solution (500 mL) was added, and the mixture was transferred to a separatory funnel. After separating the aqueous layer, the toluene layer was washed with a 5% aqueous sodium hydroxide solution (500 mL), neutralized with dilute nitric acid, and further washed with water. The toluene layer was concentrated under reduced pressure to obtain 373.2 g of product.

This product was charged into a 3 liter four-necked flask, and toluene (400 mL) and pyridine (159.8 g, 2.02 mol) were added and dissolved by stirring. Hydrogen chloride gas (97.3 g, 2.67 mol) was introduced into this at an internal temperature of 40 ° C. or lower with stirring. Thereafter, heating was started and toluene was distilled off, followed by heating and stirring at an internal temperature of 200 ° C. After confirming disappearance of the starting material by ¹ H-NMR measurement, the mixture was cooled, methyl isobutyl ketone (MIBK, 1,000 mL) and 5% aqueous hydrochloric acid (500 mL) were added, and the mixture was transferred to a separatory funnel. The aqueous layer was separated, and the MIBK layer was washed with 1% aqueous hydrochloric acid (500 mL), neutralized with dilute nitric acid, and further washed. The MIBK layer was concentrated under reduced pressure to obtain 341.3 product. The hydroxyl equivalent weight of this product is 373 g / eq. Met.

  This product was charged into a 3 liter four-necked flask and THF (700 mL), bisphenol A diglycidyl ether (epoxy equivalent: 170 g / eq., 389.3 g, 2.29 mol) and diazabicyclo- [5,4,0 ] -Undecene (17.1 g, 0.96 mol) was charged, and the mixture was heated and stirred at an internal temperature of 60 to 65 ° C. for 30 hours. The reaction mixture was concentrated under reduced pressure, diluted with chloroform (1,400 mL), transferred to a separatory funnel, and washed with a 1% aqueous nitric acid solution (700 mL). The chloroform layer was washed 3 times with deionized water (700 mL). The chloroform layer was dehydrated and concentrated under reduced pressure to obtain 730.6 g (yield 94%) of a brown solid product. The analysis result of this product was as follows.

◎ ¹ H-NMR spectrum (in deuterated chloroform, δ, ppm):
2.2 (12.6H), 2.7 (2.1H), 2.9 (2.1H), 3.3 (2.1H), 3.6 (2.1H), 3.9 (2 .1H), 6.7-7.2 (23.7H)
◎ ³¹ P-NMR spectrum (in deuterated chloroform, δ, ppm):
Trimer (P = N) ₃ 9.4-9.7
◎ CHNP elemental analysis:
Theoretical value C: 66.5%, H: 5.4%, N: 2.5%, P: 5.5%
Measured value C: 66.3%, H: 5.3%, N: 2.6%, P: 5.7%
◎ Epoxy equivalent:
706 g / eq.

From the above analysis results, this product is [N ₃ P ₃ (OC ₆ H ₄ OCH ₂ CHOHCH ₂ OC ₆ H ₄ C (CH ₃ ) ₂ C ₆ H ₄ OC ₃ H ₅ O) (OC ₆ H ₅ ) _{5], [N 3 P 3} (OC 6 H 4 OCH 2 CHOHCH 2 OC 6 H 4 C (CH 3) 2 C 6 H 4 OC 3 H 5 O) 2 (OC 6 H 5) 4] and _{[N 3} P ₃ (OC ₆ H ₄ OCH ₂ CHOHCH ₂ OC ₆ H ₄ C (CH ₃ ) ₂ C ₆ H ₄ OC ₃ H ₅ O) ₃ (OC ₆ H ₅ ) ₃ ], the average composition of which is [ the _{N 3 P 3 (OC 6 H} 4 OCH 2 CHOHCH 2 OC 6 H 4 C (CH 3) 2 C 6 H 4 OC 3 H 5 O) 2.0 (OC 6 H 5) 4.0] is confirmed.

Synthesis Example 7 (Production of glycidyloxy group-containing cyclic phosphazene compound)
The same operation as in Synthesis Example 6 was conducted except that bisphenol F diglycidyl ether (epoxy equivalent: 157 g / eq., 359.5 g, 2.29 mol) was used instead of bisphenol A diglycidyl ether, and 701 g (yield 94%). ) Was obtained as a brown solid product. The analysis result of this product was as follows.
◎ ¹ H-NMR spectrum (in deuterated chloroform, δ, ppm):
2.2 (12.6H), 2.7 (2.1H), 2.9 (2.1H), 3.3 (2.1H), 3.6 (2.1H), 3.9 (2 .1H), 6.7-7.2 (23.7H)
◎ ³¹ P-NMR spectrum (in deuterated chloroform, δ, ppm):
Trimer (P = N) ₃ 9.4-9.7
◎ CHNP elemental analysis:
Theoretical value C: 65.8%, H: 5.2%, N: 3.1%, P: 6.9%
Measured value C: 65.8%, H: 5.3%, N: 3.2%, P: 7.0%
◎ Epoxy equivalent:
684 g / eq.

From the above analysis results, this product is obtained as [N ₃ P ₃ (OC ₆ H ₄ OCH ₂ CHOHCH ₂ OC ₆ H ₄ CH ₂ C ₆ H ₄ OC ₃ H ₅ O) (OC ₆ H ₅ ) ₅ ], _{[N 3 P 2 (OC 6} H 4 OCH 2 CHOHCH 2 OC 6 H 4 CH 2 C 6 H 4 OC 3 H 5 O) 2 (OC 6 H 5) 4] and _{[N 3 P 3 (OC 6} H 4 OCH ₂ CHOHCH ₂ OC ₆ H ₄ CH ₂ C ₆ H ₄ OC ₃ H ₅ O) ₃ (OC ₆ H ₅ ) ₃ ], the average composition of which is [N ₃ P ₃ (OC ₆ H ₄ OCH ₂ CHOHCH ₂ OC ₆ H ₄ CH ₂ C ₆ H ₄ OC ₃ H ₅ O) _2.1 (OC ₆ H ₅ ) _3.9 ].

Synthesis Example 8 (Production of cyclic phosphazene compound)
PHOSPHORUS-NITROGEN COMPOUNDS, H.P. R. According to the method described in ALLCOCK, 1972, page 151, ACADEMIC PRESS, using a cyclophosphazene mixture of 81% hexachlorocyclotriphosphazene and 19% octachlorocyclotetraphosphazene [N = P (OC ₆ H ₅ ) ₂ ] ₃ and a mixture of [N = P (OC ₆ H ₅ ) ₂ ] ₄ (white solid / melting point: 65-112 ° C.).

Example 1 (Production of unsaturated carboxylate compound having phosphazene ring)
In a 1 liter flask equipped with a stirrer, thermometer, cooling pipe and air introduction pipe, 100.0 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 440 g / eq.) Obtained in Synthesis Example 1 and acrylic acid 17. 4 g, 1.0 g of methoquinone, 0.1 g of benzyltriethylamine hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 110 ° C. for 7 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture was 3.5 mgKOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 54.0%.

Example 2 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 98.5 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 434 g / eq.) Obtained in Synthesis Example 2 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 1. 1 to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring having a solid content of 53.7%.

Example 3 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 102.8 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 453 g / eq.) Obtained in Synthesis Example 3 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 1. 1 to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 54.0%.

Example 4 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 98.1 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 432 g / eq.) Obtained in Synthesis Example 4 was used in place of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 1. 1 to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 53.6%.

Example 5 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 102.2 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 450 g / eq.) Obtained in Synthesis Example 5 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 1. 1 to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 54.4%.

Example 6 (Production of unsaturated carboxylate compound having phosphazene ring)
In a 1 liter flask equipped with a stirrer, a thermometer, a cooling pipe and an air introduction pipe, 100.0 g of a glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 706 g / eq.) Obtained in Synthesis Example 6 and acrylic acid 10. 7 g, 0.5 g of methoquinone, 0.05 g of benzyltriethylamine hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 110 ° C. for 6 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture became 1.9 mgKOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 54.0%.

Example 7 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 97.1 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 684 g / eq.) Obtained in Synthesis Example 7 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 6. 6 to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 54.4%.

Example 8 (Production of unsaturated carboxylate compound having phosphazene ring)
10. A glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 440 g / eq.) Obtained in Synthesis Example 1 in a 1 liter flask equipped with a stirrer, a thermometer, a cooling pipe and an air introduction pipe, acrylic acid 11. 5 g, 0.5 g of methoquinone, 0.05 g of benzyltriethylamine hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 110 ° C. for 5 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture became 0.5 mgKOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 52.5%.

Example 9 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 98.5 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 434 g / eq.) Obtained in Synthesis Example 2 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 1. In the same manner as in No. 8, an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 52.1% was obtained.

Example 10 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 102.8 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 453 g / eq.) Obtained in Synthesis Example 3 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 1. In the same manner as in No. 8, an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 52.1% was obtained.

Example 11 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 98.1 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 432 g / eq.) Obtained in Synthesis Example 4 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 1. In the same manner as in No. 8, an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 52.0% was obtained.

Example 12 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 102.2 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 450 g / eq.) Obtained in Synthesis Example 5 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 1. In the same manner as in No. 8, an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 52.9% was obtained.

Example 13 (Production of unsaturated carboxylate compound having phosphazene ring)
In a 1 liter flask equipped with a stirrer, a thermometer, a cooling pipe and an air introduction pipe, 100.0 g of a glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 706 g / eq.) Obtained in Synthesis Example 6 and acrylic acid 5. 4 g, 0.5 g of methoquinone, 0.05 g of benzyltriethylamine hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 110 ° C. for 4 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture became 0.8 mgKOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring with a solid content of 51.5%.

Example 14 (Production of unsaturated carboxylate compound having phosphazene ring)
Example except that 97.1 g of the glycidyloxy group-containing cyclic phosphazene compound (epoxy equivalent: 684 g / eq.) Obtained in Synthesis Example 7 was used instead of the glycidyloxy group-containing cyclic phosphazene compound obtained in Synthesis Example 6. In the same manner as in No. 13, an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 50.8% was obtained.

Example 15 (Production of unsaturated carboxylate compound having phosphazene ring)
100.0 g of glycidyloxy group-containing phosphazene compound (epoxy equivalent: 440 g / eq.) Obtained in Synthesis Example 1 in a 1 liter flask equipped with a stirrer, thermometer, cooling pipe and air introduction pipe, 20.8 g of methacrylic acid Then, 1.0 g of methoquinone, 0.1 g of benzyltriethylamine hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 130 ° C. for 9 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture was 3.2 mg KOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 54.7%.

Example 16 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 15 except that 98.5 g of the glycidyloxy group-containing phosphazene compound (epoxy equivalent: 434 g / eq.) Obtained in Synthesis Example 2 was used in place of the glycidyloxy group-containing phosphazene compound obtained in Synthesis Example 1. The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 54.4%.

Example 17 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 15 except that 102.8 g of the glycidyloxy group-containing phosphazene compound (epoxy equivalent: 453 g / eq.) Obtained in Synthesis Example 3 was used instead of the glycidyloxy group-containing phosphazene compound obtained in Synthesis Example 1. The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 55.3%.

Example 18 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 15 The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 54.3%.

Example 19 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 15 except that 102.2 g of the glycidyloxy group-containing phosphazene compound (epoxy equivalent: 450 g / eq.) Obtained in Synthesis Example 5 was used instead of the glycidyloxy group-containing phosphazene compound obtained in Synthesis Example 1. The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 55.1%.

Example 20 (Production of unsaturated carboxylate compound having phosphazene ring)
100.0 g of a glycidyloxy group-containing phosphazene compound (epoxy equivalent: 706 g / eq.) Obtained in Synthesis Example 6 in a 1 liter flask equipped with a stirrer, a thermometer, a cooling pipe and an air introduction pipe, 10.7 g of methacrylic acid Then, 0.5 g of methoquinone, 0.05 g of benzyltriethylamine hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 110 ° C. for 6 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture became 1.9 mgKOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 52.9%.

Example 21 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 20 except that 97.1 g of the glycidyloxy group-containing phosphazene compound (epoxy equivalent: 684 g / eq.) Obtained in Synthesis Example 7 was used instead of the glycidyloxy group-containing phosphazene compound obtained in Synthesis Example 6. The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 52.2%.

Example 22 (Production of unsaturated carboxylate compound having phosphazene ring)
100.0 g of glycidyloxy group-containing phosphazene compound (epoxy equivalent: 440 g / eq.) Obtained in Synthesis Example 1 in a 1 liter flask equipped with a stirrer, a thermometer, a cooling pipe and an air introduction pipe, 13.7 g of methacrylic acid Then, 1.0 g of methoquinone, 0.1 g of benzyltriethylamine hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 130 ° C. for 7 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture was 0.5 mg KOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 53.0%.

Example 23 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 22 except that 98.5 g of the glycidyloxy group-containing phosphazene compound (epoxy equivalent: 434 g / eq.) Obtained in Synthesis Example 2 was used instead of the glycidyloxy group-containing phosphazene compound obtained in Synthesis Example 1. The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 52.6%.

Example 24 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 22 except that 102.8 g of the glycidyloxy group-containing phosphazene compound (epoxy equivalent: 453 g / eq.) Obtained in Synthesis Example 3 was used instead of the glycidyloxy group-containing phosphazene compound obtained in Synthesis Example 1. The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 53.6%.

Example 25 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 22 except that 98.1 g of the glycidyloxy group-containing phosphazene compound (epoxy equivalent: 432 g / eq.) Obtained in Synthesis Example 4 was used instead of the glycidyloxy group-containing phosphazene compound obtained in Synthesis Example 1. The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 52.5%.

Example 26 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 22 The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 53.4%.

Example 27 (Production of unsaturated carboxylate compound having phosphazene ring)
100.0 g of glycidyloxy group-containing phosphazene compound (epoxy equivalent: 706 g / eq.) Obtained in Synthesis Example 6 in a 1 liter flask equipped with a stirrer, thermometer, cooling pipe and air introduction pipe, 6.4 g of methacrylic acid Then, 0.3 g of methoquinone, 0.05 g of benzyltriethylamine hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 110 ° C. for 6 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture was 0.5 mg KOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 51.8%.

Example 28 (Production of unsaturated carboxylate compound having phosphazene ring)
Example 27 was used except that 97.1 g of the glycidyloxy group-containing phosphazene compound (epoxy equivalent: 684 g / eq.) Obtained in Synthesis Example 7 was used instead of the glycidyloxy group-containing phosphazene compound obtained in Synthesis Example 6. The same operation was performed to obtain an ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring having a solid content of 51.1%.

Synthesis Example 9 (Production of unsaturated carboxylate compound)
In a 1 liter flask equipped with a stirrer, thermometer, cooling pipe and air introduction pipe, 100.0 g of bisphenol A diglycidyl ether (epoxy equivalent: 170 g / eq.), 42.3 g of acrylic acid, 0.1 g of methoquinone, benzyltriethylamine 0.1 g of hydrochloride and 100 mL of ethyl carbitol acetate were charged, and the mixture was heated and stirred at 110 ° C. for 7 hours while introducing air at a rate of 50 mL / min. After confirming that the acid value of the reaction mixture was 3.5 mgKOH / g or less, the reaction mixture was cooled to obtain an ethyl carbitol acetate solution of bisphenol A acrylate compound having a solid content of 58.5%.

Synthesis Example 10 (Production of unsaturated carboxylate compound)
An ethyl carbitol acetate solution of a bisphenol A methacrylate compound having a solid content of 59.9% was used except that 50.6 g of methacrylic acid was used instead of acrylic acid used in Synthesis Example 9. Got.

Example 29 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
94.6 g of an ethyl carbitol acetate solution (solid content 54.0%) of the acrylate compound having a phosphazene ring obtained in Example 1 in a 200 ml flask equipped with a stirrer, a thermometer and a condenser tube and tetrahydrophthalic anhydride 15.2 g was charged and stirred at 80 ° C. for 8 hours. It was cooled after confirming that the peak derived from the acid anhydride disappeared by IR measurement, to obtain an ethyl carbitol acetate solution of an acid-modified acrylate compound having a phosphazene ring with a solid content of 60.4%.

Example 30 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
The ethyl carbitol acetate solution of the acrylate compound having the phosphazene ring obtained in Example 2 (solid content 53.7%) 94 instead of the ethyl carbitol acetate solution of the acrylate compound having the phosphazene ring obtained in Example 1 94 The same operation as in Example 29 was carried out except that 6 g was used to obtain an ethyl carbitol acetate solution of an acid-modified acrylate compound having a phosphazene ring having a solid content of 60.1%.

Example 31 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
In place of the ethyl carbitol acetate solution of the acrylate compound having a phosphazene ring obtained in Example 1, the ethyl carbitol acetate solution of the acrylate compound having a phosphazene ring obtained in Example 3 (solid content 54.0%) 95 The same procedure as in Example 29 was performed except that 6 g was used, to obtain an ethyl carbitol acetate solution of an acid-modified acrylate compound having a phosphazene ring with a solid content of 60.8%.

Example 32 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
Instead of the ethyl carbitol acetate solution of the acrylate compound having a phosphazene ring obtained in Example 1, an ethyl carbitol acetate solution of the acrylate compound having a phosphazene ring obtained in Example 4 (solid content 53.6%) 93 The same operation as in Example 29 was carried out except that 0.8 g was used to obtain an ethyl carbitol acetate solution of an acid-modified acrylate compound having a phosphazene ring with a solid content of 60.1%.

Example 33 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
96 Ethyl carbitol acetate solution of acrylate compound having phosphazene ring obtained in Example 5 (solid content 54.4%) 96 instead of the ethyl carbitol acetate solution of acrylate compound having phosphazene ring obtained in Example 1 The same operation as in Example 29 was carried out except that 1 g was used to obtain an ethyl carbitol acetate solution of an acid-modified acrylate compound having a phosphazene ring with a solid content of 60.6%.

Example 34 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
Instead of the ethyl carbitol acetate solution of the acrylate compound having a phosphazene ring obtained in Example 1, an ethyl carbitol acetate solution of the acrylate compound having a phosphazene ring obtained in Example 6 (solid content 54.0%) 73 The same operation as in Example 29 was performed except that .9 g was used to obtain an ethyl carbitol acetate solution of an acid-modified acrylate compound having a phosphazene ring with a solid content of 60.5%.

Example 35 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
The ethyl carbitol acetate solution of the acrylate compound having the phosphazene ring obtained in Example 7 (solid content 54.4%) 72 instead of the ethyl carbitol acetate solution of the acrylate compound having the phosphazene ring obtained in Example 1 72 Except that 0.0 g was used, the same operation as in Example 29 was performed to obtain an ethyl carbitol acetate solution of an acid-modified acrylate compound having a phosphazene ring having a solid content of 60.2%.

Example 36 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
The ethyl carbitol acetate solution of the methacrylate compound having the phosphazene ring obtained in Example 8 (solid content 54.7%) 96 instead of the ethyl carbitol acetate solution of the acrylate compound having the phosphazene ring obtained in Example 1 96 The same operation as in Example 29 was performed except that 0.0 g was used to obtain an ethyl carbitol acetate solution of an acid-modified epoxy methacrylate compound having a phosphazene ring having a solid content of 60.9%.

Example 37 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
The ethyl carbitol acetate solution of the methacrylate compound having the phosphazene ring obtained in Example 9 (solid content 54.4%) 96 instead of the ethyl carbitol acetate solution of the acrylate compound having the phosphazene ring obtained in Example 1 96 The same operation as in Example 29 was carried out except that 1 g was used to obtain an ethyl carbitol acetate solution of an acid-modified methacrylate compound having a phosphazene ring with a solid content of 60.6%.

Example 38 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
An ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring obtained in Example 10 (solid content 55.3%) 97 instead of the ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring obtained in Example 1 97 The same operation as in Example 29 was carried out except that 1 g was used to obtain an ethyl carbitol acetate solution of an acid-modified methacrylate compound having a phosphazene ring having a solid content of 61.3%.

Example 39 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
Instead of the ethyl carbitol acetate solution of the acrylate compound having a phosphazene ring obtained in Example 1, the ethyl carbitol acetate solution of the methacrylate compound having a phosphazene ring obtained in Example 11 (solid content: 54.3%) 95 The same operation as in Example 29 was performed except that 2 g was used to obtain an ethyl carbitol acetate solution of an acid-modified methacrylate compound having a phosphazene ring with a solid content of 60.6%.

Example 40 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
An ethyl carbitol acetate solution of a methacrylate compound having a phosphazene ring obtained in Example 12 (solid content 55.1%) 97 instead of the ethyl carbitol acetate solution of an acrylate compound having a phosphazene ring obtained in Example 1 97 The same operation as in Example 29 was carried out except that 0.5 g was used to obtain an ethyl carbitol acetate solution of an acid-modified methacrylate compound having a phosphazene ring having a solid content of 61.2%.

Example 41 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
The ethyl carbitol acetate solution of the methacrylate compound having the phosphazene ring obtained in Example 13 (solid content 52.9%) 74 instead of the ethyl carbitol acetate solution of the acrylate compound having the phosphazene ring obtained in Example 1 74 The same operation as in Example 29 was carried out except that 0.5 g was used to obtain an ethyl carbitol acetate solution of an acid-modified methacrylate compound having a phosphazene ring with a solid content of 60.9%.

Example 42 (Production of acid-modified unsaturated carboxylate compound having a phosphazene ring)
The ethyl carbitol acetate solution of the methacrylate compound having the phosphazene ring obtained in Example 14 (solid content 52.2%) 72 instead of the ethyl carbitol acetate solution of the acrylate compound having the phosphazene ring obtained in Example 1 72 The same operation as in Example 29 was performed except that .8 g was used to obtain an ethyl carbitol acetate solution of an acid-modified methacrylate compound having a phosphazene ring having a solid content of 60.5%.

Examples 43 to 70 (Preparation of resin composition and production of resin molding)
Unsaturated carboxylate compound having a phosphazene ring obtained in Examples 1 to 28, 2-methylimidazole (2MZ), methyl ethyl ketone (MEK) and orthocresol novolac epoxy resin (EOCN) (trade name “Nippon Kayaku Co., Ltd.” EOCN-1020-65 ": epoxy equivalent 197 g / eq.) Was mixed and dissolved in the ratios (parts by weight) shown in Tables 1 and 2 to prepare varnish (resin composition). The varnish was poured into a stainless steel mold, dried by heating at 140 ° C. for 20 minutes, and then heated and cured at 200 ° C. for 3 hours to produce a cured product (resin molded product). Here, two types of sheet-like cured products having a thickness of 1/16 inch and a thickness of 5 mm were produced. The cured product was confirmed to be cured by DSC measurement.

Comparative Examples 1 and 2 (Preparation of resin composition and production of resin molding)
Unsaturated carboxylate compounds obtained in Synthesis Examples 9 and 10, cyclic phosphazene compounds obtained in Synthesis Example 8, methyl ethyl ketone (MEK) and orthocresol novolac epoxy resin (EOCN) (trade name “EOCN” of Nippon Kayaku Co., Ltd. -1020-65 ": epoxy equivalent 197 g / eq.) Was mixed and dissolved in the ratios (parts by weight) shown in Tables 1 and 2 to prepare varnishes (resin compositions). The varnish was poured into a stainless steel mold, dried by heating at 140 ° C. for 20 minutes, and then heated and cured at 200 ° C. for 3 hours to produce a cured product (resin molded product). Here, two types of sheet-like cured products having a thickness of 1/16 inch and a thickness of 5 mm were produced. The cured product was confirmed to be cured by DSC measurement.

Evaluation 1
The sheet-like cured products obtained in Examples 43 to 70 and Comparative Examples 1 and 2 were evaluated for combustibility and heat resistance. In the evaluation of combustibility, a 1/16 inch thick sheet-like cured product was used as a test piece. In the evaluation of heat resistance, a sheet-like cured product having a thickness of 5 mm was used as a test piece. The evaluation method for each item is as follows. The results are shown in Tables 1 and 2.

(Combustion quality)
Based on Underwriters Laboratories Inc.'s UL-94 standard vertical combustion test, V-0, V depending on the total combustion time at the 10th flame contact and the presence or absence of cotton ignition due to dripping at the time of combustion. -1, V-2 and non-standard four stages. The evaluation criteria are shown below. The flame retardancy level decreases in the order of V-0, V-1, V-2, and out of specification.

V-0: All the following conditions are satisfied.
(A) The total extinguishing time after 10 times of flame contact is within 50 seconds, 5 test pieces twice each.
(B) The test piece was fired twice for each of the five test pieces, and the flame-out time after each contact was within 5 seconds.
(C) There is no ignition of the absorbent cotton under 300 mm due to the drop in all the test pieces.
(D) Growing after the second flame contact is within 30 seconds for all specimens.
(E) All specimens are not framing to the clamp.

V-1: All the following conditions are satisfied.
(A) The total flame extinguishing time after a total of 10 flame contact times is less than 250 seconds, 5 test pieces twice each.
(B) A test piece was fired twice for each of five test pieces, and the flame-out time after each contact was within 30 seconds.
(C) There is no ignition of the absorbent cotton under 300 mm due to the drop in all the test pieces.
(D) Growing after the second flame contact is within 60 seconds for all test pieces.
(E) All specimens are not framing to the clamp.

V-2: All the following conditions are satisfied.
(A) The total flame extinguishing time after a total of 10 flame contact times is less than 250 seconds, 5 test pieces twice each.
(B) A test piece was fired twice for each of five test pieces, and the flame-out time after each contact was within 30 seconds.
(C) At least one of the five test pieces is ignited on the absorbent cotton under 300 mm by the drop.
(D) Growing after the second flame contact is within 60 seconds for all test pieces.
(E) All specimens are not framing to the clamp.

(Heat-resistant)
The glass transition temperature (° C.) was measured by DSC-60 (trade name) manufactured by Shimadzu Corporation using the measurement method defined in JIS-K7121. The measurement environment is as follows. The higher the glass transition temperature, the better the heat resistance.

  Comparing the results of Examples 43 to 70 and Comparative Examples 1 and 2, Examples 43 to 70 are superior in flame retardancy and heat resistance to Comparative Examples 1 and 2.

Examples 71-98 (Preparation of polymerizable composition)
2-hydroxy-2-methyl-1-phenylpropan-1-one as a polymerization initiator was added to 100 parts (in terms of solid content) of an ethyl carbitol acetate solution of an unsaturated carboxylate compound having a phosphazene ring of Examples 1 to 28. Was added to prepare a polymerizable composition.

Evaluation 2
The polymerizable compositions obtained in Examples 71 to 98 were coated on a copper clad laminate with a screen printer, dried at 80 ° C. for 30 minutes using a blow dryer, and then passed through a pattern film with a high-pressure mercury lamp. An exposure of 2000 mJ / cm ² was performed. After the exposure, development was performed using methyl ethyl ketone to obtain a development pattern with a cured resin. The hardness of this cured resin was evaluated based on pencil scratch hardness (JIS K5600). The results are shown in Table 3 and Table 4.

Evaluation 3
The polymerizable composition prepared in Examples 71 to 98 was poured into a stainless steel mold, dried at 80 ° C. for 30 minutes, and then exposed to 2000 mJ / cm ^{2 with} a high-pressure mercury lamp. Thereafter, it was cured by heating at 200 ° C. for 6 hours to produce a 1/16 inch thick sheet-like cured product. This sheet-like cured product was confirmed to be cured by DSC measurement. About the obtained sheet-like hardened | cured material, the flame retardance and heat resistance were evaluated by the same method as the evaluation 1. The results are shown in Table 3 and Table 4.

Examples 99 to 112 (Preparation of polymerizable composition)
2-hydroxy-2-methyl-1-phenylpropane-1 as a polymerization initiator was added to 100 parts (in terms of solid content) of an ethyl carbitol acetate solution of an acid-modified unsaturated carboxylate compound having a phosphazene ring of Examples 29 to 42. -A polymerizable composition was prepared by adding 2 parts of ON.

Evaluation 4
The polymerizable compositions obtained in Examples 99 to 112 were coated on a copper clad laminate with a screen printer, dried at 80 ° C. for 30 minutes using a blow dryer, and then passed through a pattern film with a high-pressure mercury lamp. An exposure of 2000 mJ / cm ² was performed. After the exposure, development was performed using a 5% aqueous sodium hydroxide solution to obtain a development pattern of a cured resin product. The hardness of this cured resin was evaluated based on pencil scratch hardness (JIS K5600). The results are shown in Table 5.

Evaluation 5
The polymerizable composition prepared in Examples 99 to 112 was poured into a stainless steel mold, dried at 80 ° C. for 30 minutes, and then exposed to 2000 mJ / cm ^{2 with} a high-pressure mercury lamp. Thereafter, it was cured by heating at 200 ° C. for 6 hours to produce a 1/16 inch thick sheet-like cured product. This sheet-like cured product was confirmed to be cured by DSC measurement. About the obtained sheet-like hardened | cured material, the flame retardance and heat resistance were evaluated by the same method as the evaluation 1. The results are shown in Table 5.

  As is apparent from Tables 3, 4 and 5, the cured products of Examples 71 to 112 have a hardness that is preferable as a solder resist used in the production of printed circuit boards, and are also flame retardant and heat resistant. Is also good.

Claims (18)

The unsaturated carboxylate compound which has a phosphazene ring represented by following formula (1).

(In Formula (1), n shows the integer of 1-6, A shows the group chosen from the group which consists of following A1 group, A2 group, and A3 group, and at least one is A3 group.
A1 group: an alkoxy group having 1 to 8 carbon atoms in which at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.
A2 group: an aryloxy group having 6 to 20 carbon atoms in which at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.
A3 group: at least one unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group selected from the group consisting of the following A3-1 group, A3-2 group and A3-3 group.
A3-1 group: an aryloxy group containing an unsaturated carbonyloxy-2-hydroxypropoxy group represented by the following formula (2).

In formula (2), R ^{1 to} R ⁵ are groups selected from the group consisting of an unsaturated carbonyloxy-2-hydroxypropoxy group, a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group. , At least one is an unsaturated carbonyloxy-2-hydroxypropoxy group.
A3-2 group: an unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group represented by the following formula (3).

In formula (3), R < ⁶ > -R < ⁸ > shows a hydrogen atom or a C1-C6 alkyl group, Y shows a biphenylene group or a naphthyl group.
A3-3 group: an unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group represented by the following formula (4).

In formula (4), R ^{9 to} R ¹¹ represent a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, and Z represents O, S, SO ₂ , CH ₂ , CH (CH ₃ ), C (CH ₃ ). ) ₂ , C (CF ₃ ) ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ CH ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ An atom or atomic group selected from the group consisting of C (CH ₃ ) ₂ and OCH ₂ CH (OH) CH ₂ OC ₆ H ₄ SO ₂ is shown. )   The unsaturated carboxylate compound having a phosphazene ring according to claim 1, wherein a part of A in the formula (1) is a glycidyloxy group-containing group.   The unsaturated carbonyloxy group in the unsaturated carbonyloxy-2-hydroxypropoxy group-containing aryloxy group is selected from the group consisting of an acryloyloxy group, a methacryloyloxy group, a tigloyloxy group, and a crotoyloxy group. 3. An unsaturated carboxylate compound having a phosphazene ring according to 1 or 2.   The unsaturated carboxylate compound having a phosphazene ring according to any one of claims 1 to 3, wherein n in formula (1) is 1 or 2.   The unsaturated carboxylate compound having a phosphazene ring according to any one of claims 1 to 4, wherein in formula (1), 1 to (2n + 2) of (2n + 4) A are A3 groups.   The unsaturated carboxylate compound having a phosphazene ring according to any one of claims 1 to 5, which is a mixture of two or more of formulas (1) having different n.   The unsaturated carboxylate compound having a phosphazene ring according to any one of claims 1 to 6, which is acid-modified with a polybasic acid anhydride.   The phosphazene ring according to claim 7, wherein the polybasic acid anhydride is at least one selected from the group consisting of an aromatic dicarboxylic acid anhydride, an aliphatic dicarboxylic acid anhydride, and an alicyclic dicarboxylic acid anhydride. An unsaturated carboxylate compound having. A step of reacting a glycidyloxy group-containing cyclic phosphazene compound represented by the following formula (5) with an unsaturated monocarboxylic acid represented by the following formula (9):
A method for producing an unsaturated carboxylate compound having a phosphazene ring.

(In the formula (1), n represents an integer of 1 to 6, E represents a group selected from the group consisting of the following E1, E2, and E3 groups, and at least one is an E3 group.
E1 group: An alkoxy group having 1 to 8 carbon atoms in which at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.
E2 group: an aryloxy group having 6 to 20 carbon atoms in which at least one group selected from an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group may be substituted.
E3 group: At least one glycidyloxy group-containing aryloxy group selected from the group consisting of the following E3-1 group, E3-2 group, and E3-3 group.
E3-1 group: A glycidyloxy group-containing aryloxy group represented by the following formula (6).

In Formula (6), G ^{1 to} G ⁵ are groups selected from the group consisting of a glycidyloxy group, a hydrogen atom, an alkyl group having 1 to 6 carbon atoms, an alkenyl group, and an aryl group, and at least one is a glycidyloxy group. It is.
E3-2 group: A glycidyloxy group-containing aryloxy group represented by the following formula (7).

In formula (7), L represents a biphenylene group or a naphthyl group.
E3-3 group: A glycidyloxy group-containing aryloxy group represented by the following formula (8).

In the formula (8), M represents O, S, SO ₂ , CH ₂ , CH (CH ₃ ), C (CH ₃ ) ₂ , C (CF ₃ ) ₂ , OCH ₂ CH (OH) CH ₂ OC ₆ H _{4, OCH 2 CH (OH)} CH 2 OC 6 H 4 CH 2, OCH 2 CH (OH) CH 2 OC 6 H 4 C (CH 3) 2 and _{OCH 2 CH (OH) CH 2} OC 6 H 4 SO 2 An atom or atomic group selected from the group consisting of )

(In Formula (9), R < ¹² > -R < ¹⁴ > shows a hydrogen atom or a C1-C6 alkyl group.)   A polymerizable composition comprising at least two kinds of unsaturated carboxylate compounds having a phosphazene ring according to claim 1.   The resin molding obtained by hardening the polymeric composition of Claim 10.   The electrical / electronic component using the resin molding of Claim 11.   A polymerizable composition comprising the unsaturated carboxylate compound having a phosphazene ring according to claim 1 and an active energy ray-curable compound.   A resin molded article obtained by curing the polymerizable composition according to claim 13.   An electric / electronic component using the resin molded body according to claim 14.   A resin composition comprising the unsaturated carboxylate compound having a phosphazene ring according to claim 1 and at least one resin component selected from the group consisting of a thermoplastic resin and a thermosetting resin.   The resin molding obtained by hardening the resin composition of Claim 16.   An electric / electronic component using the resin molded body according to claim 17.