JP2010152155A - Photosensitive resin composition and method for manufacturing etched substrate - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a photosensitive resin composition for obtaining a resin pattern which has good strippability while having satisfactory chemical resistance, and which exhibits good adhesiveness to a metal film on a base material, and to provide a method for manufacturing an etched substrate using such a resin pattern. <P>SOLUTION: The photosensitive resin composition includes an alkali-soluble resin (A) prepared by reacting an acid radical-containing acrylic resin with an alicyclic epoxy group-containing unsaturated compound, a polyfunctional monomer (B) having tri- or higher functionality, a nitrogen-containing monofunctional monomer (C), and a photoinitiator (D). <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

  The present invention relates to a photosensitive resin composition and a method for producing a substrate to be etched.

  In recent years, wiring for driving display devices such as plasma display panels and wiring for printed circuit boards for mounting electronic components have been demanded to increase the resolution of the screen and electronic components have been mounted at higher density. As demands for these are increasing, miniaturization and densification are progressing. These wirings are formed by forming a resin pattern called an etching mask on the surface of a substrate provided with a uniform metal film by photolithography, and then removing the metal film not covered by the etching mask by etching. (For example, refer to Patent Document 1). Then, after the etching process is completed, the resin pattern used as an etching mask is removed with an alkaline stripping solution, and a finely processed wiring is completed on the substrate.

Here, various types of metal are used in consideration of required electrical characteristics, etc., and a multilayer metal wiring in which a plurality of different types of metal are laminated as required is also used. Used (see, for example, Patent Document 2). As described above, there are various types of metals to be etched, and various etching solutions used for the etching process such as acidic and alkaline. In some cases, a multilayer metal film in which a plurality of different types of metal films are stacked may be etched in stages using a plurality of types of etchants. For this reason, the resin pattern used as an etching mask is required to have chemical resistance (etching resistance) that does not peel off even when an acidic or alkaline etching solution is used.
JP 2003-131369 A JP 2000-11863 A

  In order to impart chemical resistance to the resin pattern used as an etching mask, the crosslink density inside the resin pattern may be increased. This prevents the chemical from penetrating into the resin pattern, and prevents the resin pattern from swelling and peeling during the etching process.

However, when the crosslink density of the resin pattern is increased, the resin pattern is not easily peeled off when an attempt is made to peel off the resin pattern using a stripping solution after the etching process is completed. In that case, the residue of the resin pattern remains on the substrate to cause a product defect, or the process of peeling the resin pattern takes a long time, resulting in a decrease in work efficiency. Moreover, even if the chemical resistance of the resin pattern is high, if the adhesion between the metal film on the substrate and the resin pattern is not sufficient, the etching solution may enter between the metal film and the resin pattern. The resin pattern that is an etching resist is peeled off during the etching process. In this case, even a necessary wiring portion is removed by the etching solution, which leads to a product defect.
Further, in order to prevent contamination of the line in the process, a step of washing and drying an acidic or alkaline solution used as an etching solution is required before the peeling step. In general, after cleaning with pure water, drying is performed by air blowing. However, in the air blowing process, if the adhesion is not sufficient and the pattern is peeled off, it becomes a cause of line contamination (to become dust), which is preferable. Absent.

  The present invention has been made in view of the above situation, and has a good releasability while having a sufficient chemical resistance and exhibits a good adhesiveness with a metal film on a substrate. It aims at providing the photosensitive resin composition for obtaining a resin pattern, and the manufacturing method of the to-be-etched base | substrate using such a resin pattern.

  As a result of extensive research, the present inventors have developed a polyfunctionality that increases the crosslink density of a resin pattern in an alkali-soluble resin produced by a reaction between an acid group-containing acrylic resin and an alicyclic epoxy group-containing unsaturated compound. Combining monomers with a monofunctional monomer that suppresses excessive increase in the crosslink density of the resin pattern, especially nitrogen-containing monofunctional monomers, and polymerizing them in the presence of a photoinitiator to produce a resin pattern As a result, it was found that the obtained resin pattern showed good chemical resistance and peelability, and the adhesion between the metal film on the substrate and the resin pattern was improved, and the present invention was completed.

  The first aspect of the present invention is an alkali-soluble resin (A) produced by a reaction between an acid group-containing acrylic resin and an alicyclic epoxy group-containing unsaturated compound, a trifunctional or higher polyfunctional monomer (B), , A photosensitive resin composition containing a nitrogen-containing monofunctional monomer (C) and a photopolymerization initiator (D).

  According to a second aspect of the present invention, there is provided a step of coating the photosensitive resin composition on a substrate to form a photosensitive resin layer, selectively exposing the photosensitive resin layer, and developing the resin. An exposure / development process for forming a pattern; an etching process for selectively etching the substrate using the resin pattern as a mask; and a peeling process for peeling the resin pattern using a peeling solution. A method for manufacturing a substrate to be etched.

  According to the present invention, a photosensitive resin composition for obtaining a resin pattern having good chemical resistance while having good releasability and good adhesion to a metal film on a substrate. Things are provided. Moreover, the manufacturing method of the to-be-etched base | substrate using such a resin pattern is provided.

  Hereinafter, although embodiment of this invention is described, this invention is not limited to the following embodiment at all.

<Photosensitive resin composition>
First, the photosensitive resin composition of the present invention will be described. The photosensitive resin composition of the present invention comprises an alkali-soluble resin (A) produced by a reaction between an acid group-containing acrylic resin and an alicyclic epoxy group-containing unsaturated compound, and a trifunctional or higher polyfunctional monomer (B). And a nitrogen-containing monofunctional monomer (C) and a photopolymerization initiator (D).

[Alkali-soluble resin (A) produced by reaction of acid group-containing acrylic resin and alicyclic epoxy group-containing unsaturated compound]
The alkali-soluble resin (hereinafter, also referred to as “component (A)”) contained in the photosensitive resin composition of the present invention comprises a part of acid groups derived from the acid group-containing acrylic resin (a1) and an alicyclic epoxy. An epoxy group derived from the group-containing unsaturated compound (a2) is reacted to introduce an unsaturated group derived from the alicyclic epoxy group-containing unsaturated compound (a2) necessary for curing with active energy rays. is there.
Each component is as follows.

[Acid group-containing acrylic resin (a1)]
Acid group-containing acrylic resins (hereinafter also referred to as “component (a1)”) include acids having an ethylenically unsaturated bond, esters of (meth) acrylic acid, vinyl aromatic compounds, amide-based unsaturated compounds. A copolymer obtained by copolymerizing one or more selected from monomers such as compounds and polyolefin-based compounds can be used. Specifically, an acid having an ethylenically unsaturated bond such as (meth) acrylic acid, 2-carboxyethyl (meth) acrylate, 2-carboxypropyl (meth) acrylate, and (anhydrous) maleic acid is an essential component. Methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, stearyl (meth) acrylate, hydroxyethyl (meth) acrylate, hydroxypropyl ( Esters of (meth) acrylic acid such as (meth) acrylate; vinyl aromatic compounds such as styrene, α-methylstyrene, vinyltoluene, p-chlorostyrene; (meth) acrylamide, diacetone acrylamide, N-methylolacrylamide, N − Amide-type unsaturated compounds such as toximethylacrylamide; Polyolefin-type monomers such as butadiene, isoprene and chloroprene, and (meth) acrylonitrile, methyl isopropenyl ketone, vinyl acetate, Veova monomer (shell chemical products), vinyl propionate, Examples thereof include a copolymer obtained by copolymerizing one or more monomers selected from other monomers such as vinyl pivalate.

  The acid value of the component (a1) is preferably 15 mgKOH / g or more and in the range of 40 to 500 mgKOH / g. When the component (a1) has such an acid value, the component (a1) is reacted with an alicyclic epoxy group-containing unsaturated compound (a2) described later to cause the component (A) to have a desired amount of unsaturation. Even after the introduction of groups, a sufficient amount of acid groups remains in the component (A). Thereby, (A) component can have the outstanding developability.

[Aliphatic epoxy group-containing unsaturated compound (a2)]
As the alicyclic epoxy group-containing unsaturated compound (hereinafter also referred to as “component (a2)”), a compound having one ethylenically unsaturated group and an alicyclic epoxy group in one molecule is preferable. Specific examples include compounds represented by the following formulas (I) to (XV).

Here, R ⁴ is independently a hydrogen atom or a methyl group. R < ⁵ > is a C1-C6 bivalent aliphatic saturated hydrocarbon group each independently. R ⁶ is each independently a divalent hydrocarbon group having 1 to 10 carbon atoms. l is an integer of 0-10. R ⁵ is preferably a linear or branched alkylene group such as a methylene group, an ethylene group, a propylene group, a tetramethylene group, an ethylethylene group, a pentamethylene group, or a hexamethylene group. Examples of R ⁶ include a methylene group, an ethylene group, a propylene group, a tetramethylene group, an ethylethylene group, a pentamethylene group, a hexamethylene group, a phenylene group, a cyclohexylene group, —CH ₂ —Ph—CH ₂ — (Ph Is a phenylene group).

[Preparation of alkali-soluble resin (A)]
The component (A) is prepared by reacting the components (a1) and (a2) and introducing an unsaturated group into the component (a1). Specifically, for example, it is prepared by reacting an inert organic solvent solution of the component (a1) with the component (a2) at about 20 to 120 ° C. for about 1 to 5 hours. Examples of the inert organic solvent include, but are not limited to, alcohols, esters, aliphatic or aromatic hydrocarbons. The ratio of the component (a1) to the component (a2) can be changed according to the type of monomer used for the synthesis of the component (a1), but the ratio of the component (a2) to the component (a1) is 15 mol%. The above is preferable. If the ratio of the component (a2) to the component (a1) is 15 mol% or more, the resin pattern obtained by curing the photosensitive resin composition containing the component (A) has good etching resistance. Can be granted.

  The mass average molecular weight of the component (A) thus prepared can be determined by a gel permeation chromatography method, and the value is preferably 1000 to 100,000, more preferably 3000 to 70000, and still more preferably 9000 to 30000. is there. Since the component (A) has a double bond in the side chain, it can be cured by light in the presence of a photopolymerization initiator. That is, since the component (A) which is a resin has high photosensitivity, it is possible to improve the curing density when crosslinked, and to increase the degree of curing of the photosensitive resin composition by exposure. it can. Moreover, since it has an acid group in the side chain, it is possible to perform development with an alkaline developer or to remove the formed resin pattern with an alkaline stripping solution. The acid value of such component (A) is preferably 20 to 200 mgKOH / g, more preferably 30 to 150 mgKOH / g, and further preferably 50 to 140 mgKOH / g. By setting it to the lower limit value or more, excellent developability can be obtained, and by setting the upper limit value or less, etching resistance is improved and an excellent pattern shape is obtained. Moreover, etching resistance can be improved by having an alicyclic group derived from the component (a2).

[Trifunctional or higher polyfunctional monomer (B)]
The photosensitive resin composition of the present invention contains a trifunctional or higher polyfunctional monomer (hereinafter also referred to as “component (B)”). Here, “a trifunctional or higher polyfunctional monomer” means a monomer component having three or more ethylenic double bonds per molecule that can be addition-polymerized by light irradiation in the presence of a photopolymerization initiator. It is. The photosensitive resin composition of the present invention includes such a polyfunctional monomer component to form a resin pattern having a high crosslinking density and excellent chemical resistance.

  Examples of the component (B) include pentaerythritol tetra (meth) acrylate, ethylene oxide-modified pentaerythritol tetra (meth) acrylate, propylene oxide-modified pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, and dipentaerythritol. Trifunctional or higher acrylate such as hexa (meth) acrylate, polyfunctional urethane (meth) acrylate obtained by reacting polyisocyanate compound with hydroxy group-containing (meth) acrylate monomer, polyhydric alcohol and N-methylol (meth) Examples include condensates with acrylamide. These polyfunctional monomers can be used alone or in combination of two or more. Moreover, the softness | flexibility of a resin layer improves by using polyfunctional urethane (meth) acrylate in combination with another polyfunctional monomer.

  In addition, when making the resin pattern which is an etching mask into a thin film of 1-3 micrometers, it is preferable to use a monomer more than 6 functional especially among the (B) component illustrated above. When the resin pattern is formed as a thin film, it is a severe condition from the viewpoint of etching resistance, that is, chemical resistance to acids and alkalis. Under such conditions, a monomer having 6 or more functional groups is used as the component (B). By doing so, the crosslink density inside the resin pattern can be increased, and good chemical resistance can be imparted to the resin pattern. Examples of such a monomer having 6 or more functional groups include dipentaerythritol hexa (meth) acrylate, polyfunctional urethane (meth) acrylate obtained by reacting a polyisocyanate compound and a hydroxyl group-containing (meth) acrylate monomer, And a condensate of a monohydric alcohol and N-methylol (meth) acrylamide. Among them, dipentaerythritol hexaacrylate (DPHA) is preferably used for forming a strong resin pattern having high etching resistance. These hexafunctional or higher functional monomers can be used alone or in combination of two or more, and the above trifunctional or higher functional monomers can also be used in combination.

  The component (B) is preferably contained in an amount of 110 to 300 parts by mass, and more preferably 115 to 200 parts by mass with respect to 100 parts by mass of the component (A). By setting it to the lower limit value or more, excellent etching resistance can be obtained, and by setting it to the upper limit value or less, the resin pattern can be satisfactorily removed with an alkaline stripping solution after the etching process is completed.

[Nitrogen-containing monofunctional monomer (C)]
The photosensitive resin composition of the present invention contains a nitrogen-containing monofunctional monomer (hereinafter also referred to as “component (C)”). A monofunctional monomer means a monomer having one ethylenically unsaturated group. When the photosensitive resin composition of the present invention contains the monofunctional component (C), the crosslink density inside the resin pattern is prevented from becoming excessively high, and the resin pattern film is flexible and resistant to alkali stripping solution. Good peelability can be imparted. In addition, since the component (C) is monofunctional and has a nitrogen atom in the molecule, when the component (C) is incorporated into the resin molecule by a polymerization reaction, the nitrogen atom contained in the component (C) is The resin pattern is disposed so as to face outward with respect to the main chain of the resin contained in the resin pattern. For this reason, the nitrogen atom contained in (C) component will be utilized in order to improve adhesion | attachment with the metal film on a base material, and the adhesiveness of a resin pattern and the metal film on a base material will improve. .

（一般式（１）中、Ａは単結合又は炭素数１〜５のアルキレン基を示し、Ｒ^１は水素原子又はメチル基を示し、Ｒ^２、Ｒ^３はそれぞれ独立に水素原子、又は置換基を有していてもよい炭化水素基を示す。Ｒ^２、Ｒ^３がともに炭化水素基の場合、互いに結合して環構造を形成していてもよい。） The component (C) is preferably a compound represented by the following general formula (1).

(In General Formula (1), A represents a single bond or an alkylene group having 1 to 5 carbon atoms, R ¹ represents a hydrogen atom or a methyl group, and R ² and R ³ each independently represents a hydrogen atom or a substituent. (In the case where both R ² and R ³ are hydrocarbon groups, they may be bonded to each other to form a ring structure.)

In the general formula (1), the hydrocarbon group in R ² and R ³ may be an aromatic hydrocarbon group or an aliphatic hydrocarbon group. Carbon number of a hydrocarbon group becomes like this. Preferably it is 1-10, More preferably, it is 1-6. More specifically, examples of the aliphatic hydrocarbon group include a linear or branched aliphatic hydrocarbon group, an aliphatic hydrocarbon group containing a ring in the structure, and the like. The aliphatic hydrocarbon group is preferably an alkyl group having 1 to 10 carbon atoms, and more preferably an alkyl group having 1 to 5 carbon atoms. Examples of the substituent that the hydrocarbon group may have include an alkyl group, an alkoxy group, a halogen atom, a halogenated alkyl group, a hydroxyl group, an oxygen atom (═O, —O—), a hydroxyalkyl group, A cyano group etc. are mentioned.
In the general formula (1), when R ² and R ³ are bonded to each other to form a ring structure, the divalent hydrocarbon group represented by R ² and R ³ preferably has 3 to 6 carbon atoms, More preferably, it has 4 to 5 carbon atoms. The divalent hydrocarbon group represented by R ² and R ³ may have an oxygen atom (—O—) and a nitrogen atom (—N═, —NH—).

  The component (C) is preferably a monomer such that the homopolymer obtained by polymerizing the component (C) has a glass transition temperature (Tg) of 80 ° C. or higher. As already described, the component (C) is a component that also has a role of preventing the resin pattern from having a high crosslink density, and acts in the direction of reducing chemical resistance from the viewpoint of the crosslink density. However, when the component (C) satisfies such a Tg condition, chemical resistance can be imparted to the resin pattern. As a result, the chemical resistance of the resin pattern is improved and the etching resistance is improved. Become. Examples of such component (C) include acrylamide (Tg of homopolymer: 179 ° C., the same applies hereinafter), methacrylamide (171 ° C.), N-methyl acrylamide (171 ° C.), dimethyl acrylamide (119 ° C.), N-isopropyl. Acrylamide (134 ° C), acryloylmorpholine (145 ° C), N-tert-butylacrylamide (135 ° C), N-phenylacrylamide (160 ° C), diacetone acrylamide (86 ° C), acryloylpiperidine (116 ° C), diethylacrylamide (81 ° C.), 2-hydroxyethylacrylamide (98 ° C.), dimethylaminopropylacrylamide (134 ° C.) and the like. Among these, acrylamide, methacrylamide, N-methyl acrylamide, acryloyl morpholine, and N-phenyl acrylamide with a homopolymer Tg of 140 ° C. or higher are more preferable, and acryloyl morpholine is most preferable.

  The component (C) is preferably 10 to 80 parts by mass, more preferably 20 to 75 parts by mass, and still more preferably 30 to 70 parts by mass with respect to 100 parts by mass of the component (A). By setting it to the lower limit or higher, good flexibility, peelability and adhesion to the substrate can be imparted to the resin pattern, and by setting the upper limit or lower, the crosslink density of the resin pattern is excessively reduced. Is prevented and good drug resistance is obtained.

[Photoinitiator (D)]
Although it does not specifically limit as a photoinitiator (henceforth "(D) component") contained in the photosensitive resin composition of this invention, For example, 1-hydroxy cyclohexyl phenyl ketone, 2-hydroxy-2 -Methyl-1-phenylpropan-1-one, 1- [4- (2-hydroxyethoxy) phenyl] -2-hydroxy-2-methyl-1-propan-1-one, 1- (4-isopropylphenyl) 2-hydroxy-2-methylpropan-1-one, 1- (4-dodecylphenyl) -2-hydroxy-2-methylpropan-1-one, 2,2-dimethoxy-1,2-diphenylethane-1 -One, bis (4-dimethylaminophenyl) ketone, 2-methyl-1- [4- (methylthio) phenyl] -2-morpholinopropan-1-one, Dil-2-dimethylamino-1- (4-morpholinophenyl) -butan-1-one, ethanone-1- [9-ethyl-6- (2-methylbenzoyl) -9H-carbazol-3-yl]- 1- (o-acetyloxime), 2,4,6-trimethylbenzoyldiphenylphosphine oxide, 4-benzoyl-4'-methyldimethylsulfide, 4-dimethylaminobenzoic acid, methyl 4-dimethylaminobenzoate, 4-dimethyl Ethyl aminobenzoate, butyl 4-dimethylaminobenzoate, 4-dimethylamino-2-ethylhexylbenzoic acid, 4-dimethylamino-2-isoamylbenzoic acid, benzyl-β-methoxyethyl acetal, benzyldimethyl ketal, 1-phenyl -1,2-propanedione-2- (o-ethoxycarbonyl) oxy , Methyl o-benzoylbenzoate, 2,4-diethylthioxanthone, 2-chlorothioxanthone, 2,4-dimethylthioxanthone, 1-chloro-4-propoxythioxanthone, thioxanthene, 2-chlorothioxanthene, 2,4- Diethylthioxanthene, 2-methylthioxanthene, 2-isopropylthioxanthene, 2-ethylanthraquinone, octamethylanthraquinone, 1,2-benzanthraquinone, 2,3-diphenylanthraquinone, azobisisobutyronitrile, benzoyl peroxide, cumene Peroxide, 2-mercaptobenzoimidazole, 2-mercaptobenzoxazole, 2-mercaptobenzothiazole, 2- (o-chlorophenyl) -4,5-di (m-methoxyphenyl) -imidazolyl dimer Benzophenone, 2-chlorobenzophenone, p, p'-bisdimethylaminobenzophenone, 4,4'-bisdiethylaminobenzophenone, 4,4'-dichlorobenzophenone, 3,3-dimethyl-4-methoxybenzophenone, benzyl, benzoin Benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin n-butyl ether, benzoin isobutyl ether, benzoin butyl ether, acetophenone, 2,2-diethoxyacetophenone, p-dimethylacetophenone, p-dimethylaminopropiophenone, dichloro Acetophenone, trichloroacetophenone, p-tert-butylacetophenone, p-dimethylaminoacetophenone, p-tert-butyltrichloro Acetophenone, p-tert-butyldichloroacetophenone, α, α-dichloro-4-phenoxyacetophenone, thioxanthone, 2-methylthioxanthone, 2-isopropylthioxanthone, dibenzosuberone, pentyl-4-dimethylaminobenzoate, 9-phenylacridine, 1,7-bis- (9-acridinyl) heptane, 1,5-bis- (9-acridinyl) pentane, 1,3-bis- (9-acridinyl) propane, p-methoxytriazine, 2,4,6- Tris (trichloromethyl) -s-triazine, 2-methyl-4,6-bis (trichloromethyl) -s-triazine, 2- [2- (5-methylfuran-2-yl) ethenyl] -4,6- Bis (trichloromethyl) -s-triazine, 2- [2- (furan-2- L) ethenyl] -4,6-bis (trichloromethyl) -s-triazine, 2- [2- (4-diethylamino-2-methylphenyl) ethenyl] -4,6-bis (trichloromethyl) -s-triazine 2- [2- (3,4-dimethoxyphenyl) ethenyl] -4,6-bis (trichloromethyl) -s-triazine, 2- (4-methoxyphenyl) -4,6-bis (trichloromethyl)- s-triazine, 2- (4-ethoxystyryl) -4,6-bis (trichloromethyl) -s-triazine, 2- (4-n-butoxyphenyl) -4,6-bis (trichloromethyl) -s- Triazine, 2,4-bis-trichloromethyl-6- (3-bromo-4-methoxy) phenyl-s-triazine, 2,4-bis-trichloromethyl-6- (2-bromo 4-methoxy) phenyl-s-triazine, 2,4-bis-trichloromethyl-6- (3-bromo-4-methoxy) styrylphenyl-s-triazine, 2,4-bis-trichloromethyl-6- (2 -Bromo-4-methoxy) styrylphenyl-s-triazine and the like. These photopolymerization initiators can be used alone or in combination of two or more.

  Although content of (D) component should just adjust suitably according to content of (A)-(C) component, it is 1-30 mass parts with respect to 100 mass parts of alkali-soluble resin (A). Is preferable, 5-25 mass parts is more preferable, and 10-20 mass parts is further more preferable. By setting it as said range, sufficient heat resistance and chemical-resistance can be acquired, a coating-film formation ability can be improved, and photocuring failure can be suppressed.

[Sensitizer (E)]
The photosensitive resin composition of the present invention may contain a compound having a thiol group as a sensitizer (hereinafter also referred to as “(E) component”). S radicals are generated by a thiol reaction, and the polymerization reaction by S radicals accelerates the curing of the photosensitive resin composition without being affected by oxygen inhibition, thereby improving the residual film ratio of the pattern in development, As such component (E), esters such as trimethylolpropane tris (3-mercaptopropionate), 2-mercaptoethanol, 1-thioglycerol, glycerol monothioglycolate , Alcohols such as 4-mercaptophenol; thioglycolic acid, 3-mercaptopropionic acid, 2-mercaptopro Carboxylic acids such as on acid, thiomalic acid, mercaptoisobutyric acid, meso-2,3-dimercaptoisobutyric acid, thiosalicylic acid; amines such as 2-aminoethanethiol, 2-aminobenzenethiol, 4-aminobenzenethiol; And cysteine.

  What is necessary is just to adjust suitably content of (E) component in the photosensitive resin composition according to content of (A)-(C) component, but it is 0 with respect to 100 mass parts of alkali-soluble resin (A). 0.1-30 parts by mass is preferable, 0.5-25 parts by mass is more preferable, 0.8-20 parts by mass is further preferable, and 1-15 parts by mass is particularly preferable. By setting it as said range, developability and etching tolerance can be improved.

[Monomer component]
The photosensitive resin composition of the present invention can contain various monomer components in addition to the above components. Examples of such a monomer component include a compound having an ethylenically unsaturated group, and a monofunctional monomer having one ethylenically unsaturated group (except for the component (C)) and two ethylenically unsaturated groups. And a polyfunctional monomer having a saturated group. One or more of these components are appropriately selected and used according to the properties required for the photosensitive resin composition, such as polymerization reactivity and monomer viscosity. The amount of the monomer component added is preferably 80 parts by mass or less, more preferably 1 to 60 parts by mass with respect to 100 parts by mass of the component (A). By setting it to the upper limit or less, a sufficient crosslinking density is maintained inside the resin pattern, and resistance to acidic or alkaline etching solutions can be improved.

[Organic solvent]
The photosensitive resin composition of the present invention preferably contains an organic solvent for improving coating properties and adjusting the viscosity. Examples of the organic solvent include ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol mono-n-propyl ether, ethylene glycol mono-n-butyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol mono-n- Propyl ether, diethylene glycol mono-n-butyl ether, triethylene glycol monomethyl ether, triethylene glycol monoethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol mono-n-propyl ether, propylene glycol mono-n-butyl ether , Dipropylene glycol monomethyl ether , (Poly) alkylene glycol monoalkyl ethers such as dipropylene glycol monoethyl ether, dipropylene glycol mono-n-propyl ether, dipropylene glycol mono-n-butyl ether, tripropylene glycol monomethyl ether, tripropylene glycol monoethyl ether (Poly) alkylene glycol monoalkyl ether acetates such as ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol monomethyl ether acetate, diethylene glycol monoethyl ether acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate; Diethylene glycol Other ethers such as methyl ether, diethylene glycol methyl ethyl ether, diethylene glycol diethyl ether, tetrahydrofuran; ketones such as methyl ethyl ketone, cyclohexanone, 2-heptanone, 3-heptanone; methyl 2-hydroxypropionate, ethyl 2-hydroxypropionate, etc. Alkyl 2-lactic acid esters; ethyl 2-hydroxy-2-methylpropionate, methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 3-ethoxypropionate, ethyl 3-ethoxypropionate, ethyl ethoxyacetate, hydroxy Ethyl acetate, methyl 2-hydroxy-3-methylbutanoate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, 3-methyl-3-methoxybutyrate Tylpropionate, ethyl acetate, n-propyl acetate, i-propyl acetate, n-butyl acetate, i-butyl acetate, n-pentyl formate, i-pentyl acetate, n-butyl propionate, ethyl butyrate, n-butyrate Other esters such as propyl, i-propyl butyrate, n-butyl butyrate, methyl pyruvate, ethyl pyruvate, n-propyl pyruvate, methyl acetoacetate, ethyl acetoacetate, ethyl 2-oxobutanoate; toluene, xylene, etc. Aromatic hydrocarbons; amides such as N-methylpyrrolidone, N, N-dimethylformamide, N, N-dimethylacetamide, and the like. These solvents can be used alone or in combination of two or more.

  The content of the organic solvent is not particularly limited, and is appropriately set according to the coating film thickness at a concentration that can be applied to a substrate or the like. In this case, the solid content concentration is preferably 5 to 70% by mass, and more preferably 10 to 60% by mass.

[Other ingredients]
The photosensitive resin composition of this invention can contain additives, such as an antifoamer and surfactant, as another component as needed. The antifoaming agent is not particularly limited, and examples thereof include silicone-based and fluorine-based compounds. The surfactant is not particularly limited, and examples thereof include anionic, cationic, and nonionic compounds.

<Method for manufacturing substrate to be etched>
Next, the manufacturing method of the to-be-etched base | substrate which uses the photosensitive resin composition of the said invention is demonstrated. The manufacturing method of the to-be-etched base | substrate using the said photosensitive resin composition is also one of this invention. The method for producing a substrate to be etched according to the present invention includes (1) a step of applying the photosensitive resin composition of the present invention on a substrate to form a photosensitive resin layer, and (2) selecting the photosensitive resin layer. Exposure / development process in which a resin pattern is formed by developing after exposure to light, (3) an etching process for selectively etching the substrate using the resin pattern as a mask, and (4) using a stripping solution. And a peeling step of peeling the resin pattern. In the present invention, the “base” means that a film to be etched is formed on a substrate such as glass. A metal film is exemplified as the film to be etched.

  First, (1) the process of applying the photosensitive resin composition of the present invention on a substrate to form a photosensitive resin layer will be described.

In this step, the photosensitive resin composition of the present invention is applied onto a substrate to form a photosensitive resin layer.
In many cases, a glass substrate is used as a substrate for producing a substrate. On the glass substrate, a metal film to be etched is formed by vapor deposition or sputtering, and a substrate to be etched is produced. The metal forming the metal film includes a metal oxide having conductivity in addition to the metal, for example, a metal such as Ni, Cr, Au, Mo, W, Pt, Ti, Cu, Pd, Ag, These metal alloys, metal oxides such as In ₂ O ₃ —SnO ₂ , semiconductors such as polysilicon, and the like can be given. Although the metal film may be a single layer, the present invention is also characterized in that a composite metal film composed of a plurality of metal films having different etching conditions can be selectively etched. As such a composite metal film, a Cr / Cu / Cr laminated film in which a first Cr (chromium) layer, a Cu (copper) layer, and a second Cr layer are formed is exemplified.

  A photosensitive resin composition is applied to the substrate using a contact transfer type coating device such as a roll coater, reverse coater, bar coater, slit coater, etc., or a non-contact type coating device such as a spinner (rotary coating device) or a curtain flow coater. The photosensitive resin layer is formed on the substrate by applying and drying to remove the solvent.

  The thickness of the photosensitive resin layer is not particularly limited, but it is preferable that the thickness of the resin pattern serving as an etching mask is 1 to 5 μm. By setting it to the lower limit value or more, good chemical resistance can be imparted to the resin pattern, and by setting it to the upper limit value or less, good peelability can be imparted to the resin pattern.

  Next, (2) an exposure / development process in which the photosensitive resin layer is selectively exposed and then developed to form a resin pattern will be described.

In order to selectively expose the photosensitive resin layer, the exposure may be performed by irradiating an active energy ray such as an ultraviolet ray or an excimer laser through a light shielding pattern. For the exposure, a light source that emits ultraviolet rays such as a high-pressure mercury lamp, a xenon lamp, or a carbon arc lamp can be used. Although the energy dose to be irradiated varies depending on the composition of the photosensitive resin composition, it is preferably, for example, about 5 to 2000 mJ / cm ² .

  Next, a resin pattern is created by developing the exposed resin layer with a developer. The development method is not particularly limited, and for example, an immersion method, a spray method, or the like can be used. Specific examples of the developer include organic ones such as monoethanolamine, diethanolamine, and triethanolamine, and aqueous solutions such as sodium hydroxide, potassium hydroxide, sodium carbonate, ammonia, and quaternary ammonium salts. Then, the developed resin pattern may be post-baked and cured by heating. The post-bake temperature is preferably 150 to 250 ° C.

  Next, (3) an etching process for selectively etching the substrate using the resin pattern as a mask will be described.

  As an etching method, for example, a commonly performed wet etching method in which the substrate is immersed in an etching solution may be used. As the etching solution used for wet etching, an acidic type or alkaline type may be selected as appropriate in accordance with an object to be etched. Examples of acidic etching solutions include aqueous solutions of acidic components such as hydrochloric acid, sulfuric acid, hydrofluoric acid, and phosphoric acid, and mixed aqueous solutions of acidic components and salts of ferric chloride, ammonium fluoride, potassium permanganate, and the like. Is done. As the acidic component, a combination of a plurality of acidic components may be used. In addition, alkaline type etching solutions include sodium hydroxide, potassium hydroxide, ammonia, organic amines, aqueous solutions of alkali components such as organic amine salts such as tetramethylammonium hydroxide, alkaline components and potassium permanganate. A mixed aqueous solution of a salt such as A combination of a plurality of alkali components may be used as the alkali component.

  In the method for producing a substrate to be etched according to the present invention, although not particularly limited, the temperature of the etching solution is preferably 45 ° C. or lower. The resin pattern used as an etching mask in the present invention is particularly excellent for acidic and alkaline etching solutions in such a temperature range by being formed using the above-described photosensitive resin composition of the present invention. Demonstrate resistance. Therefore, the resin pattern is prevented from peeling off during the etching process, and the portion where the resin pattern does not exist is selectively etched.

  In addition, since the resin pattern used as an etching mask in the method for manufacturing a substrate to be etched according to the present invention has high chemical resistance as described above, for example, a plurality of types of metal films are formed on a substrate. The method for manufacturing a substrate to be etched according to the present invention is preferably applied even under severe conditions in which etching is repeatedly performed using different types of etching solutions sequentially on a metal film.

As such an example, there is a case where the above-described substrate on which the first Cr layer, the Cu layer, and the second Cr layer are sequentially formed is etched. In this type of substrate, for example, the second Cr layer and Cu layer located on the outermost surface are etched using an acidic etchant, and then the first Cr layer is etched using an alkaline etchant. . According to the method of manufacturing a substrate to be etched according to the present invention, etching is performed without peeling the resin pattern on a substrate that requires an etching step under acidic conditions and an etching step under alkaline conditions. be able to.
After the etching, a cleaning process and a drying process may be performed as necessary to prevent line contamination. For example, the cleaning process is performed by cleaning the substrate with pure water for 10 to 300 seconds at room temperature. For the drying process, the air blow pressure (about 0.1 to 5 kg / cm ² ) is appropriately adjusted using an air blow. Just do it.

  Next, (4) the peeling process which peels the said resin pattern using peeling liquid is demonstrated.

Although it does not specifically limit as a peeling method of a resin pattern, For example, the method of immersing a board | substrate for 5 to 30 minutes in 30-80 degreeC, Preferably it is 50-80 degreeC in the peeling liquid under stirring. The resin pattern used as an etching mask in the present invention exhibits excellent chemical resistance at 45 ° C. or lower as described above, but exhibits a property of swelling by an alkaline stripping solution when the chemical temperature is 50 ° C. or higher. . Due to such properties, when the peeling step is performed using a peeling solution of 50 to 80 ° C., there is an advantage that the process time is shortened and the peeling residue of the resin pattern is reduced. That is, by providing a difference in the chemical temperature between the etching process and the peeling process, the resin pattern used as an etching mask in the present invention exhibits good chemical resistance in the etching process, while in the peeling process. Good peelability will be exhibited, and both conflicting properties of chemical resistance and peelability can be satisfied.
Examples of the stripper include inorganic alkali components such as sodium hydroxide and potassium hydroxide, and organic alkali components such as tertiary amine and quaternary ammonium salt, water, dimethyl sulfoxide, N-methylpyrrolidone, or these. What was melt | dissolved in this mixed solution is mentioned. You may peel by the spray method, the shower method, the paddle method etc. using said peeling liquid.

  The present invention will be described more specifically with reference to the following examples. However, these examples are illustrative of the present invention and are not intended to limit the scope of the invention.

<Preparation of photosensitive resin composition>
According to Table 1 and Table 2, the photosensitive resin composition of Examples 1-14 and Comparative Examples 1-3 was prepared. Each component described in Table 1 is as follows. In addition, 45 mass% DPGME (dipropylene glycol monomethyl ether) solution was produced for alkali-soluble resin (A), and it used for preparation of the photosensitive resin composition. The numerical value described in Table 1 and Table 2 represents a mass part. Here, in Table 1, 100 parts by mass of the alkali-soluble resin (A-1 or A-2) means that the solid content of the alkali-soluble resin is 100 parts by mass.

［式（２）中、Ｒ^７はアルキル基またはヒドロキシアルキル基を表し、式（２）、式（３）及び式（４）中、Ｘは水素原子又はメチル基を表す。］
Ａ−２：ベンジルメタクリレート及びメタクリル酸の共重合体（ベンジルメタクリレート／メタクリル酸＝８０：２０（質量比）、質量平均分子量６００００） Alkali-soluble resin (A)
A-1: Cyclomer ACA Z250 (manufactured by Daicel Chemical Industries, Ltd., mass average molecular weight 20000, acid value 101.7 mg KOH / g, produced by reaction of acid group-containing acrylic resin and alicyclic epoxy group-containing unsaturated compound) It is a resin composed of structural units represented by the following formula (2), formula (3) and formula (4).

[In Formula (2), R ⁷ represents an alkyl group or a hydroxyalkyl group, and in Formula (2), Formula (3), and Formula (4), X represents a hydrogen atom or a methyl group. ]
A-2: Copolymer of benzyl methacrylate and methacrylic acid (benzyl methacrylate / methacrylic acid = 80: 20 (mass ratio), mass average molecular weight 60000)

Monomer (B)
B-1: DPHA (dipentaerythritol hexaacrylate, hexafunctional monomer)
B-2: CN9006 (Sartomer, urethane acrylate, hexafunctional monomer)

Nitrogen-containing monofunctional monomer (C)
C-1: Acryloylmorpholine

Other monomers B'-1: 2-Phenoxyethyl acrylate B'-2: Isobornyl acrylate

Photopolymerization initiator (D)
IR369: Irgacure 369 (Ciba Specialty Chemicals)
EAB-F: 4,4′-bis (diethylamino) benzophenone (Hodogaya Chemical Co., Ltd.)

Sensitizer (E)
E-1: Trimethylolpropane trimercaptopropionate

<Creation of substrate to be etched>
A glass substrate (thickness 1.8 mm) on which the second Cr layer / Cu layer / first Cr layer was laminated was produced by sputtering, and used as an evaluation substrate. In the evaluation substrate, the second Cr layer and the first Cr layer are located at the outermost surface and the lowermost layer, respectively, and the Cu layer is located between them. The thickness of each layer is 100 nm for the second Cr layer, 2.0 μm for the Cu layer, and 50 nm for the first Cr layer. A photosensitive resin composition was applied to the evaluation substrate using a spin coater and dried at 65 ° C. for 6 minutes to obtain an evaluation substrate having a photosensitive resin layer having a thickness of 2.5 μm. Subsequently, these photosensitive resin layers are exposed to ultraviolet rays (light source: ultrahigh pressure) with an exposure amount of 25 mJ / cm ² (a composition containing a sensitizer) or 50 mJ / cm ² (a composition containing no sensitizer) through a negative mask. A mercury lamp was selectively irradiated, and a resin pattern was formed by spray development at 30 ° C. for 120 seconds using a 0.25 mass% sodium carbonate solution as a developer, followed by pure water washing and air blow drying. Thereafter, the formed resin pattern was subjected to post-exposure by irradiating with ultraviolet rays (light source: ultra-high pressure mercury lamp) at an exposure amount of 300 mJ / cm ² .

Next, etching was performed on the evaluation substrate on which the resin pattern was formed. First, the evaluation substrate is immersed for 5 minutes in an acidic etching solution at 35 ° C. made of an aqueous solution of about 15% by mass of hydrochloric acid (* in order to evaluate the resistance, the immersion time is longer than the normal process), and the second substrate located on the outermost surface. The Cr layer was etched and washed with pure water. Thereafter, a 0.3 / 0.3 / 0.3 (mol / L ratio) HCl / FeCl ₃ / Cu ²⁺ aqueous solution is prepared as an acidic etching solution, and the evaluation substrate is immersed in the acidic etching solution at 30 ° C. The Cu layer was etched for 60 seconds while being swung, and washed with pure water. Finally, the evaluation substrate is immersed for 10 minutes in an alkaline etching solution at 40 ° C. in which 5% by mass of potassium permanganate is added to 5% by mass of Na ₂ SiO ₃ aqueous solution, and the first Cr layer located at the bottom layer is formed. Etched and washed with pure water.

  After completion of the etching process (including a process of cleaning with pure water (at 23 ° C. for 60 seconds)), air blow drying with an air gun was performed. Thereafter, an alkaline stripping solution was used to strip the resin pattern present on the evaluation substrate. As the stripping solution, a 12 mass% sodium hydroxide aqueous solution heated to 60 ° C was used.

<Evaluation>
For each of the photosensitive resin compositions of Examples 1 to 14 and Comparative Examples 1 to 3, as described above, an evaluation substrate having a resin pattern with a film thickness of 2.5 μm was prepared, etched and developed. Remaining film rate, resistance to chemicals (etching resistance), pattern adhesion after cleaning / air blow process after etching, time required for peeling of resin pattern after etching, and presence / absence of residue after peeling of resin pattern evaluated. The evaluation results are shown in Tables 3 and 4. The evaluation method and evaluation criteria for each item are as follows.

[Remaining film properties during development]
Evaluation was made based on the residual ratio of the resin pattern film after the photosensitive resin layer was exposed and spray developed.
○: Residual film ratio after development of photocured resin pattern is 90% or more Δ: Residual film ratio after development of photocured resin pattern is 50% or more and less than 90% ×: After development of photocured resin pattern The remaining film rate is less than 50%

[Acid and alkali resistance]
It evaluated by observing the peeling state of the resin pattern after completion | finish of the etching process of a 2nd Cr layer, Cu layer, and 1st Cr layer.
(Double-circle): The peeling of the resin pattern after completion | finish of an etching process is not observed.
○: Little peeling of the resin pattern after the etching process is observed.
Δ: Peeling occurred on part of the resin pattern (less than 30% in area ratio) during the etching process.
X: Peeling occurred in most of the resin pattern (30% or more in area ratio) during the etching process.

[Pattern adhesion after etching and air blowing]
After the etching step, pattern adhesion after cleaning with pure water (at 23 ° C. for 60 seconds) and air blow drying with an air gun was evaluated.

(Double-circle): In the pattern dimension of exposure amount 25mJ / cm < ² >, line width 20micrometer pitch 80micrometer, pattern peeling is not observed but it adheres.
○: In a pattern dimension with an exposure amount of 50 mJ / cm ² or less, a line width of 30 μm, and a pitch of 90 μm, pattern peeling is not observed and adhesion is observed.
X: Pattern peeling is observed in a pattern dimension with an exposure amount of 25 mJ / cm ² or less and a line width of 30 μm and a pitch of 90 μm.

[Pattern linearity after etching and air blowing]
After completion of the etching step, pattern linearity after cleaning with pure water (at 23 ° C. for 60 seconds) and air blow drying with an air gun was evaluated according to the following criteria. Note that the dimensions of the pattern used for the evaluation are a line width of 30 μm and a pitch of 90 μm.
○: No wave shape of the pattern is seen and the linearity is high.
Δ: Slight wave shape is seen in the pattern.
X: The wave shape is seen in the pattern and the linearity is low.

[Peeling time]
After the etching process was completed, the evaluation was made based on the time required for peeling the resin pattern with an alkaline stripping solution.
○: Time required for peeling is 120 seconds or less ×: Time required for peeling exceeds 120 seconds

[Peelability]
The resin pattern residue remaining on the substrate was observed and evaluated after the resin pattern was peeled off with an alkaline stripping solution.
○: Resin pattern residue does not exist after peeling.
Δ: Resin pattern remains slightly after peeling.
X: A large amount of the resin pattern remains after peeling.

  Regarding Table 4, since Comparative Example 1 had insufficient acid-alkali resistance, evaluation after the etching process was not performed. In Comparative Examples 2 to 5, the pattern adhesion after the etching / air blowing process was insufficient, and part of the pattern was peeled off, so the subsequent peeling process was not evaluated, but the pattern linearity in the remaining pattern For reference, () is also written.

As described in Table 3 and Table 4, Examples 1 to 8 have good acid / alkali resistance (chemical resistance) with respect to Comparative Examples 1 to 5, and in the cleaning / air blowing process after the etching process. Was confirmed to have sufficient pattern adhesion. From this, by using an alkali-soluble resin or a nitrogen-containing monofunctional monomer produced by a reaction between an acid group-containing acrylic resin and an alicyclic epoxy group-containing unsaturated compound in the photosensitive resin composition, It is understood that chemical resistance is improved. In general, when a monofunctional monomer is added, the cross-linking density inside the resin after curing is reduced, so it is expected that this will be disadvantageous in terms of chemical resistance, but the nitrogen-containing monofunctional monomer used in the present invention If used, the chemical resistance and adhesion are improved as described above, contrary to such expectations. This is presumably because the adhesion of the resin pattern to the surface of the substrate was improved by the nitrogen atoms contained in the monomer. In this respect, Comparative Examples 4 and 5 using a monofunctional monomer containing no nitrogen atom have insufficient adhesion after the etching / air blowing step.
By the way, as already described, when a large amount of polyfunctional monomer is used, the crosslink density inside the resin is improved, which is advantageous in terms of chemical resistance but disadvantageous in terms of releasability. In this regard, by using a nitrogen-containing monofunctional monomer as in the photosensitive resin composition of the present invention, chemical resistance and adhesion can be imparted to the resin pattern without excessively increasing the crosslinking density inside the resin. Therefore, it can be seen that the contradictory performance of chemical resistance and adhesion and peelability can be achieved.

  Moreover, when Example 7 and Comparative Example 3 are compared, it is understood that the acid / alkali resistance of the resin pattern is improved by the presence of the nitrogen-containing monofunctional monomer. The presence of the nitrogen-containing monofunctional monomer improved the acid / alkali resistance of the resin pattern because the adhesion between the resin pattern and the substrate improved, and the etching solution entered the resin pattern and the substrate. It is thought that this was prevented.

  Moreover, when Example 6 and Example 7 are compared, it is understood that both have no peeling of the resin pattern after an etching process. However, it can be seen that Example 6 is superior in pattern adhesion after etching and air blowing at a low exposure amount as compared with Example 7. This is considered to be because the addition of a sensitizer improves the sensitivity and causes a sufficient polymerization reaction, so that even a pattern with a smaller dimension is less susceptible to the influence of chemicals during etching.

Claims (8)

  Alkali-soluble resin (A) produced by reaction of acid group-containing acrylic resin and alicyclic epoxy group-containing unsaturated compound, trifunctional or higher polyfunctional monomer (B), and nitrogen-containing monofunctional monomer (C) And a photopolymerization initiator (D). The said nitrogen-containing monofunctional monomer (C) is represented by following General formula (1), The photosensitive resin composition of Claim 1 characterized by the above-mentioned.

(In General Formula (1), A represents a single bond or an alkylene group having 1 to 5 carbon atoms, R ¹ represents a hydrogen atom or a methyl group, and R ² and R ³ each independently represents a hydrogen atom or a substituent. (In the case where both R ² and R ³ are hydrocarbon groups, they may be bonded to each other to form a ring structure.)   Content of the said nitrogen-containing monofunctional monomer (C) is 10-60 mass parts with respect to 100 mass parts of said alkali-soluble resin (A), The photosensitive resin composition of Claim 1 or 2 characterized by the above-mentioned. object.   The photosensitive resin composition according to claim 1, wherein the polyfunctional monomer (B) has 6 or more functional groups.   5. The photosensitive resin composition according to claim 4, wherein the content of the polyfunctional monomer (B) is 110 to 300 parts by mass with respect to 100 parts by mass of the alkali-soluble resin (A).   Furthermore, a sensitizer (E) is contained, The photosensitive resin composition of any one of Claim 1 to 5 characterized by the above-mentioned. Applying a photosensitive resin composition according to any one of claims 1 to 6 on a substrate to form a photosensitive resin layer;
An exposure / development process in which the photosensitive resin layer is selectively exposed and then developed to form a resin pattern;
An etching step of selectively etching the substrate using the resin pattern as a mask;
And a peeling step of peeling off the resin pattern using a peeling liquid. The base is formed by sequentially forming a first Cr layer, a Cu layer, and a second Cr layer on a substrate,
The etching step includes a step of selectively etching the second Cr layer using an acidic etchant, a step of selectively etching the Cu layer using an acidic etchant, and an alkaline etchant. And a step of selectively etching the first Cr layer by using the method of manufacturing a substrate to be etched according to claim 7.