JP2009235852A - Waterproof sheet

Info

Publication number: JP2009235852A
Application number: JP2008085806A
Authority: JP
Inventors: Norihiko Sawabe; 則彦澤邊; Michio Kamiya; 通夫神谷
Original assignee: Ube Industries Ltd
Current assignee: Ube Corp
Priority date: 2008-03-28
Filing date: 2008-03-28
Publication date: 2009-10-15

Abstract

<P>PROBLEM TO BE SOLVED: To obtain a waterproof sheet which can surely prevent the leakage of water from upper surfaces of various structures and peripheries of them, and can maintain the beauty of the surfaces of the various structures by preventing stains from being generated on the surfaces of the various structures by raindrops even if rainwater coming into contact with the waterproof sheet applied to the upper surfaces of the various structures drops. <P>SOLUTION: The waterproof sheet comprises a base material layer containing a polyester film, and a modified asphalt layer bonded to the polyester film. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明は、住宅のバルコニー手摺り壁などの各種構造体の天端部などからの漏水を防止するための防水シートに関する。 The present invention relates to a waterproof sheet for preventing water leakage from the top end of various structures such as a balcony handrail wall of a house.

従来、住宅のバルコニー手摺り壁などの壁天端部やその周辺からの漏水を防止するために、アスファルトフェルトなどの防水性シートが用いられている。 Conventionally, waterproof sheets such as asphalt felt have been used in order to prevent water leakage from the top of the wall such as a balcony handrail wall of the house and its surroundings.

完全な防水・防湿効果を有するモルタル下地複合シートとして、例えば、特許文献１には、吸水指数が１．０〜６．５である不織布と、その不織布の片面にアルミニウム箔が接合されており、さらに、そのアルミニウム箔の他面にアスファルト組成物を積層されたもので、不織布の厚みが０．１〜１．０ｍｍで、アルミニウム箔の厚みが１〜５０μｍであり、アスファルト組成物の厚みが０．２〜５．０ｍｍであるように全面にわたって積層されているモルタル下地複合シートが開示されている。 As a mortar base composite sheet having a complete waterproof / moisture-proof effect, for example, in Patent Document 1, a non-woven fabric having a water absorption index of 1.0 to 6.5 and an aluminum foil are bonded to one side of the non-woven fabric, Furthermore, the asphalt composition is laminated on the other surface of the aluminum foil, the thickness of the nonwoven fabric is 0.1 to 1.0 mm, the thickness of the aluminum foil is 1 to 50 μm, and the thickness of the asphalt composition is 0. A mortar base composite sheet that is laminated over the entire surface so as to be 2 to 5.0 mm is disclosed.

また、特許文献２には、バルコニー手摺り壁天端の笠木取り付け部において、ビス貫通部の止水効果が高く、全体の防水性能にも優れた防水構造を得るための防水工法として、バルコニー手摺り壁天端部に、片面粘着不織布防水シートを一定幅で圧着貼りし、その上から軟質の塗膜型ゴム系防水材を塗布せしめたことを特徴とする笠木取り付け部の防水工法が開示されている。
特開平９−３００５２５号特開２００１−３２４７２号 Further, Patent Document 2 discloses a balcony hand method as a waterproofing method for obtaining a waterproof structure having a high water-stopping effect at the screw penetration part and excellent in overall waterproof performance at the top of the balcony handrail wall. A waterproofing method for a headboard mounting portion is disclosed, in which a single-sided adhesive non-woven waterproof sheet is pressure-bonded to the top end of a sliding wall with a certain width, and a soft coating-type rubber waterproofing material is applied thereon. ing.
JP-A-9-300525 JP 2001-32472 A

各種構造体の天端部およびその周辺からの漏水を確実に防止することができるとともに、構造体天端に施工した防水シートに接触した雨水が、雨垂れとなった場合にも、雨垂れによる各種構造体の表面の汚れの発生を防止することができ、各種構造体の表面の美観を維持することができる防水シートを得ることを目的とする。 It is possible to reliably prevent water leakage from the top edge of various structures and its surroundings, and even if rainwater that comes in contact with the waterproof sheet constructed on the top of the structure becomes raindrops, various structures due to raindrops An object of the present invention is to obtain a waterproof sheet that can prevent the occurrence of dirt on the surface of the body and maintain the aesthetic appearance of the surfaces of various structures.

本発明は、ポリエステルフィルムを含む基材層と、ポリエステルフィルムに接着する改質アスファルト層とを含む防水シートである。 The present invention is a waterproof sheet including a base material layer including a polyester film and a modified asphalt layer that adheres to the polyester film.

本発明の防水シートの好ましい態様を以下に示す。本発明では、これらの態様を適宜組み合わせることができる。
（１）基材層が、ポリエステル不織布をさらに含み、ポリエステルフィルムと、ポリエステル不織布との間に接着層をさら含む。
（２）接着層が、ポリエチレンからなる接着層である。
（３）ポリエステル不織布が、単位面積質量２０〜２００ｇ／ｍ^２であり、接着層が、厚さ５〜１００μｍであり、ポリエステルフィルムが、厚さ２〜５０μｍである。
（４）防水シートの厚さが、０．３〜１．５ｍｍである。 The preferable aspect of the waterproof sheet of this invention is shown below. In the present invention, these embodiments can be appropriately combined.
(1) The base material layer further includes a polyester nonwoven fabric, and further includes an adhesive layer between the polyester film and the polyester nonwoven fabric.
(2) The adhesive layer is an adhesive layer made of polyethylene.
(3) The polyester nonwoven fabric has a unit area mass of 20 to 200 g / m ² , the adhesive layer has a thickness of 5 to 100 μm, and the polyester film has a thickness of 2 to 50 μm.
(4) The waterproof sheet has a thickness of 0.3 to 1.5 mm.

また、本発明は、上記防水シートを、防水構造体の天端部を覆うように施工した防水構造体である。 Moreover, this invention is the waterproof structure which constructed the said waterproof sheet so that the top end part of a waterproof structure might be covered.

また、本発明は、ポリエステル不織布およびポリエステルフィルムを用意する工程と、ポリエステルフィルムとポリエステル不織布との間に溶融状態のポリエチレンを流し込み、加圧接着して接着層を形成することにより調製することによって基材層を形成する工程と、ポリエステルフィルムに、改質アスファルト層を接着する工程とを含む、防水シートの製造方法である。 The present invention also includes a step of preparing a polyester non-woven fabric and a polyester film, and by preparing a melted polyethylene by pouring between the polyester film and the polyester non-woven fabric to form an adhesive layer by pressure bonding. It is a manufacturing method of a waterproof sheet, including a step of forming a material layer and a step of bonding a modified asphalt layer to a polyester film.

本発明の防水シートによって、各種構造体の天端部およびその周辺からの漏水を確実に防止することができるとともに、構造体天端に施工した防水シートに接触した雨水が雨垂れとなった場合にも、雨垂れによる各種構造体の表面の汚れの発生を防止することができ、各種構造体の表面の美観を維持することができる防水シートを得ることができる。 With the waterproof sheet of the present invention, it is possible to reliably prevent water leakage from the top end of various structures and the periphery thereof, and when rainwater that comes into contact with the waterproof sheet constructed on the top of the structure becomes raindrops. In addition, it is possible to prevent the occurrence of dirt on the surfaces of various structures due to rain dripping, and to obtain a waterproof sheet that can maintain the aesthetic appearance of the surfaces of the various structures.

本発明の防水シートは、ポリエステルフィルムを含む基材層と、ポリエステルフィルムに接着する改質アスファルト層とを含む防水シートである。また、本発明の防水シートは、好ましくは、基材層が、ポリエステル不織布をさらに含み、ポリエステルフィルムと、ポリエステル不織布との間に接着層をさら含む防水シートである。本発明の防水シートは、特に、壁体の壁天端部の防水を行うために好ましく用いることができる。以下、本発明の防水シートについて詳しく説明する。 The waterproof sheet of the present invention is a waterproof sheet including a base material layer including a polyester film and a modified asphalt layer that adheres to the polyester film. The waterproof sheet of the present invention is preferably a waterproof sheet in which the base material layer further includes a polyester nonwoven fabric, and further includes an adhesive layer between the polyester film and the polyester nonwoven fabric. In particular, the waterproof sheet of the present invention can be preferably used for waterproofing the top of the wall. Hereinafter, the waterproof sheet of the present invention will be described in detail.

図１に、本発明の防水シート１３の模式断面図の一例を示す。本発明の防水シート１３は、ポリエステルフィルム２３を含む基材層２４と、改質アスファルト層２５とを含む防水シート１３である。本発明に用いる防水シート１３の基材層２４は、ポリエステルフィルム２３の他にポリエステル不織布２１をさらに含み、ポリエステルフィルム２３とポリエステル不織布２１とが、接着層２２を用いて接着されていることが、基材層２４の機械的強度を強化するために好ましい。 In FIG. 1, an example of the schematic cross section of the waterproof sheet 13 of this invention is shown. The waterproof sheet 13 of the present invention is a waterproof sheet 13 including a base material layer 24 including a polyester film 23 and a modified asphalt layer 25. The base material layer 24 of the waterproof sheet 13 used in the present invention further includes a polyester nonwoven fabric 21 in addition to the polyester film 23, and the polyester film 23 and the polyester nonwoven fabric 21 are bonded using the adhesive layer 22. This is preferable for enhancing the mechanical strength of the base material layer 24.

接着層２２は、ポリエステルフィルム２３とポリエステル不織布２１とを接着できるものであればその種類は問わないが、防水シート１３の機械的強度をさらに強化するためにポリエチレンからなる接着層であることが好ましい。なお、ポリエチレンは、その性質を妨げない範囲でおよび／またはその性質の向上のために、添加物および／またはフィラーを適宜含むことができる。ポリエステルフィルム２３とポリエステル不織布２１との間に溶融状態のポリエチレンを流し込み、ロールコーターなどを用いて加圧接着してポリエチレンの接着層２２を形成することにより、基材層２４を調製することができる。すなわち、本発明の防水シート１３の基材層２４は、ポリエステル不織布２１、ポリエチレンの接着層２２およびポリエステルフィルム２３の順に層をなし、ポリエステルフィルム２３が改質アスファルト層２５と接する構造であることが好ましい。本発明の防水シート１３は、耐水性、遮水性および化学成分に対する非透過性に優れるポリエステルフィルム２３を、基材層２４のうち、改質アスファルト層２５と接する層に用いることによって、より優れた防水性能が得られるのみならず、改質アスファルト層２５の成分の、基材層２４への滲み出しを遮断することができる。 The adhesive layer 22 may be of any type as long as it can adhere the polyester film 23 and the polyester nonwoven fabric 21, but is preferably an adhesive layer made of polyethylene in order to further enhance the mechanical strength of the waterproof sheet 13. . Polyethylene can appropriately contain additives and / or fillers as long as the properties are not hindered and / or for improvement of the properties. The base material layer 24 can be prepared by pouring molten polyethylene between the polyester film 23 and the polyester nonwoven fabric 21 and forming a polyethylene adhesive layer 22 by pressure bonding using a roll coater or the like. . That is, the base material layer 24 of the waterproof sheet 13 of the present invention has a structure in which the polyester nonwoven fabric 21, the polyethylene adhesive layer 22 and the polyester film 23 are formed in this order, and the polyester film 23 is in contact with the modified asphalt layer 25. preferable. The waterproof sheet 13 of the present invention is more excellent by using the polyester film 23 that is excellent in water resistance, water impermeability and non-permeability to chemical components in a layer in contact with the modified asphalt layer 25 in the base material layer 24. Not only can waterproof performance be obtained, but also the components of the modified asphalt layer 25 can be prevented from seeping into the base material layer 24.

本発明の防水シート１３に用いるポリエステルフィルム２３については、製造方法などは特に限定されず、市販のものを適宜選択して使用することができる。ポリエステルフィルム２３の厚さは、好ましくは２〜５０μｍの範囲であり、さらに好ましくは５〜３０μｍの範囲であり、より好ましくは８〜２０μｍの範囲であり、特に好ましくは１０〜１５μｍの範囲のものを好ましく使用できる。このような厚さのポリエステルフィルム２３を用いることによって、高い防水性能と、化学成分に対する優れた非透過性とを有する防水シート１３を得ることができる。 About the polyester film 23 used for the waterproof sheet 13 of this invention, a manufacturing method etc. are not specifically limited, A commercially available thing can be selected suitably and can be used. The thickness of the polyester film 23 is preferably in the range of 2 to 50 μm, more preferably in the range of 5 to 30 μm, more preferably in the range of 8 to 20 μm, and particularly preferably in the range of 10 to 15 μm. Can be preferably used. By using the polyester film 23 having such a thickness, it is possible to obtain a waterproof sheet 13 having high waterproof performance and excellent non-permeability with respect to chemical components.

本発明の防水シート１３に用いるポリエステル不織布２１は、製造方法などは特に限定されず、市販のものを適宜選択して使用することができる。ポリエステル不織布２１の目付け量（単位面積質量）としては、好ましくは２０〜２００ｇ／ｍ^２の範囲であり、さらに好ましくは３０〜１５０ｇ／ｍ^２の範囲であり、より好ましくは３５〜１００ｇ／ｍ^２の範囲であり、特に好ましくは４０〜８０ｇ／ｍ^２の範囲のものを好適に使用することができる。 The manufacturing method etc. are not specifically limited for the polyester nonwoven fabric 21 used for the waterproof sheet 13 of the present invention, and a commercially available one can be appropriately selected and used. The basis weight of the nonwoven polyester fabric 21 (mass per unit area), preferably in the range of 20 to 200 g / ^{m 2,} more preferably in the range of 30 to 150 g / ^{m 2,} more preferably 35~100g / ^{m 2} In particular, those in the range of 40 to 80 g / m ² can be suitably used.

本発明の防水シート１３は、ポリエステルフィルム２３とポリエステル不織布２１との間に溶融状態のポリエチレンを流し込み、ロールコーターを用いて加圧接着して調製された基材層２４を好ましく使用できる。本発明の防水シート１３の基材層２４をこのような構造にすることによって、溶融ポリエチレンを介してポリエステルフィルム２３とポリエステル不織布２１とが強固に接着され、機械的強度と、耐候性とに優れた基材層２４を得ることができる。 In the waterproof sheet 13 of the present invention, a base material layer 24 prepared by pouring molten polyethylene between the polyester film 23 and the polyester nonwoven fabric 21 and pressure-bonding using a roll coater can be preferably used. By forming the base material layer 24 of the waterproof sheet 13 of the present invention in such a structure, the polyester film 23 and the polyester nonwoven fabric 21 are firmly bonded via molten polyethylene, and are excellent in mechanical strength and weather resistance. The base material layer 24 can be obtained.

基材層２４において、接着層２２の厚さが、好ましくは５〜１００μｍの範囲、さらに好ましくは１０〜７０μｍの範囲、より好ましくは１５〜５０μｍの範囲、特に好ましくは２０〜４０μｍの範囲であることにより、より高い機械的強度と、より良好な耐候性とを得ることができる。 In the base material layer 24, the thickness of the adhesive layer 22 is preferably in the range of 5 to 100 μm, more preferably in the range of 10 to 70 μm, more preferably in the range of 15 to 50 μm, and particularly preferably in the range of 20 to 40 μm. As a result, higher mechanical strength and better weather resistance can be obtained.

本発明の防水シート１３の改質アスファルト層２５の材料として、改質アスファルトを用いる。改質アスファルトは、アスファルトおよびポリマーを含むもの、アスファルト、ポリマーおよび無機充填材の３成分を含むものなどを用いることが出来る。具体的には、改質アスファルトとしては、アスファルト１００重量部に対し、ポリマー１０〜４０重量部および無機充填材０〜２０重量部を含むものを用いることが好ましい。 Modified asphalt is used as a material for the modified asphalt layer 25 of the waterproof sheet 13 of the present invention. As the modified asphalt, one containing asphalt and polymer, one containing three components of asphalt, polymer and inorganic filler can be used. Specifically, it is preferable to use a modified asphalt containing 10 to 40 parts by weight of a polymer and 0 to 20 parts by weight of an inorganic filler with respect to 100 parts by weight of asphalt.

改質アスファルトは、アスファルトおよびポリマーを含むもの、アスファルト、ポリマーおよび無機充填材の３成分を含むものなどを１２０〜２００℃で３〜３０時間加熱混合して調製したものを用いることが、防水・防湿性、伸縮性などに優れているために好ましい。 As the modified asphalt, it is possible to use one prepared by heat mixing at 120 to 200 ° C. for 3 to 30 hours, including one containing asphalt and polymer, one containing three components of asphalt, polymer and inorganic filler. It is preferable because it is excellent in moisture resistance, stretchability and the like.

改質アスファルトには、以上述べた成分のほかに、プロセスオイル、ワセリン、セレシン、石油樹脂など、一般に合成樹脂やゴムの配合で用いられる撥水剤、顔料、増粘剤、耐光剤、耐候剤などの無機や有機の配合剤を添加してもよい。 In addition to the components described above, modified asphalt includes process oil, petrolatum, ceresin, petroleum resin, and other water repellents, pigments, thickeners, light-proofing agents, and weathering agents that are commonly used in blending synthetic resins and rubbers. An inorganic or organic compounding agent such as may be added.

改質アスファルトにおいて、アスファルトとしては、天然アスファルトやアスファルタイトなど天然に産するもの、ストレートアスファルト、ブローンアスファルト、カットバックアスファルト等の石油アスファルト、またはこれらのアスファルトの混合物等が好ましい。 In the modified asphalt, as the asphalt, natural asphalt, natural asphaltite, petroleum asphalt such as straight asphalt, blown asphalt, cutback asphalt, or a mixture of these asphalts is preferable.

改質アスファルトに含まれるポリマーとしては、天然ゴム、合成ゴム、天然ゴムと合成ゴムとの混合物、ポリエチレン、エチレン酢酸ビニル共重合体、エチレンとアクリル酸誘導体との共重合体、ポリプロピレン、ポリブテン−１、ポリ４−メチルペンテン−１、ポリスチレン、アクリロニトリル・スチレン共重合体、ＡＢＳ樹脂、ポリ塩化ビニル、ポリアクリロニトリルおよびスチレンとブタジエンとの重合体（例えば、ＳＢＳ、ＳＢＲなど）等の中から選択される１種以上のものを使用することができる。特に、改質アスファルトに含まれるポリマーとしては、ＳＢＳ、ＳＢＲあるいはＢＲなどのゴム系を使用することが好適である。 Polymers contained in the modified asphalt include natural rubber, synthetic rubber, a mixture of natural rubber and synthetic rubber, polyethylene, ethylene vinyl acetate copolymer, copolymer of ethylene and acrylic acid derivative, polypropylene, polybutene-1 , Poly-4-methylpentene-1, polystyrene, acrylonitrile / styrene copolymer, ABS resin, polyvinyl chloride, polyacrylonitrile, and a polymer of styrene and butadiene (for example, SBS, SBR, etc.) One or more types can be used. In particular, as the polymer contained in the modified asphalt, it is preferable to use a rubber system such as SBS, SBR, or BR.

改質アスファルトに含まれる無機充填材としては、炭酸カルシウム、ケイ酸マグネシウム、ケイ酸カルシウム、ケイ酸アルミニウム、無水ケイ酸、クレー、カーボンブラック、タルク、マイカ、硫酸バリウム、珪藻土およびシリカ等の粒子状無機充填材並びに石綿およびガラス繊維などの繊維状無機充填材の中から選択される１種以上のものを用いることができる。 The inorganic filler contained in the modified asphalt includes calcium carbonate, magnesium silicate, calcium silicate, aluminum silicate, anhydrous silicic acid, clay, carbon black, talc, mica, barium sulfate, diatomaceous earth, silica, etc. One or more selected from inorganic fillers and fibrous inorganic fillers such as asbestos and glass fibers can be used.

改質アスファルト層２５に用いる改質アスファルトの針入度は、好ましくは１００ｄｍｍ〜３５０ｄｍｍの範囲、さらに好ましくは１５０ｄｍｍ〜３２０ｄｍｍの範囲、より好ましくは２００ｄｍｍ〜３００ｄｍｍの範囲、特に好ましくは２４０ｄｍｍ〜２９０ｄｍｍの範囲であることが、柔軟性に優れるために好ましい。なお、針入度は、ＪＩＳＫ２２０７−１９９６に規定された方法により測定することができる。 The penetration of the modified asphalt used for the modified asphalt layer 25 is preferably in the range of 100 dmm to 350 dmm, more preferably in the range of 150 dmm to 320 dmm, more preferably in the range of 200 dmm to 300 dmm, and particularly preferably in the range of 240 dmm to 290 dmm. It is preferable that it is excellent in flexibility. The penetration can be measured by the method defined in JIS K2207-1996.

改質アスファルト層２５に用いる改質アスファルトの軟化点は、好ましくは５０〜９５℃の範囲、さらに好ましくは６０〜９３℃の範囲、より好ましくは６８〜９１℃の範囲、特に好ましくは７０〜８５℃の範囲であることが、良好な柔軟性を有するために好ましい。なお、針入度は、ＪＩＳＫ２２０７−１９９６に規定された方法により測定することができる。 The softening point of the modified asphalt used for the modified asphalt layer 25 is preferably in the range of 50 to 95 ° C, more preferably in the range of 60 to 93 ° C, more preferably in the range of 68 to 91 ° C, and particularly preferably in the range of 70 to 85. It is preferable that the temperature is in the range of ° C. in order to have good flexibility. The penetration can be measured by the method defined in JIS K2207-1996.

改質アスファルト層２５に用いる改質アスファルトの１６０℃の粘度は、好ましくは５００００〜１０００００ｍＰａ・ｓｅｃの範囲、さらに好ましくは好ましくは５５０００〜９００００ｍＰａ・ｓｅｃの範囲、より好ましくは５８０００〜８００００ｍＰａ・ｓｅｃの範囲、特に好ましくは好ましくは６００００〜７５０００ｍＰａ・ｓｅｃの範囲であることが、ポリエステルフィルムとの接着性に優れることから好ましい。 The 160 ° C. viscosity of the modified asphalt used for the modified asphalt layer 25 is preferably in the range of 50,000 to 100,000 mPa · sec, more preferably in the range of 55,000 to 90,000 mPa · sec, more preferably in the range of 58000 to 80,000 mPa · sec. Particularly preferably, it is preferably in the range of 60000-75000 mPa · sec because of excellent adhesion to the polyester film.

本発明の防水シート１３は、上述の基材層２４のポリエステルフィルム２３が露出する面と、改質アスファルト層２５とを接着することによって得ることができる。本発明において使用する防水シート１３の厚さは、好ましくは０．３〜１．５ｍｍであること、さらに好ましくは０．４〜１．２ｍｍであること、より好ましくは０．４５〜１ｍｍであること、特に好ましくは０．５〜０．９ｍｍであることが、優れた防水性能と良好な施工作業性とを併せて得ることができることから好ましい。 The waterproof sheet 13 of the present invention can be obtained by bonding the surface of the base material layer 24 where the polyester film 23 is exposed and the modified asphalt layer 25. The thickness of the waterproof sheet 13 used in the present invention is preferably 0.3 to 1.5 mm, more preferably 0.4 to 1.2 mm, and more preferably 0.45 to 1 mm. In particular, the thickness of 0.5 to 0.9 mm is preferable because excellent waterproof performance and good workability can be obtained together.

本発明の防水シートは、ＪＩＳＡ６０１３に準拠して測定した、防水シートの長手方向の引張強度が、好ましくは６０Ｎ／ｃｍ以上、さらに好ましくは６５Ｎ／ｃｍ以上、より好ましくは７０Ｎ／ｃｍ以上、特に好ましくは７５Ｎ／ｃｍ以上であり、防水シートの幅方向の引張強度が、好ましくは２５Ｎ／ｃｍ以上、さらに好ましくは３０Ｎ／ｃｍ以上、より好ましくは３３Ｎ／ｃｍ以上、特に好ましくは３５Ｎ／ｃｍ以上であることが耐久性の高い防水層を形成できることから好ましい。 The waterproof sheet of the present invention has a tensile strength in the longitudinal direction of the waterproof sheet measured according to JIS A 6013, preferably 60 N / cm or more, more preferably 65 N / cm or more, more preferably 70 N / cm or more, Particularly preferably, the tensile strength in the width direction of the waterproof sheet is preferably 25 N / cm or more, more preferably 30 N / cm or more, more preferably 33 N / cm or more, and particularly preferably 35 N / cm or more. It is preferable that a highly durable waterproof layer can be formed.

本発明の防水シートは、ＪＩＳＡ６０１３に準拠して測定した、防水シートの長手方向の引裂強度が、好ましくは５Ｎ以上、さらに好ましくは７Ｎ以上、より好ましくは８Ｎ以上、特に好ましくは９Ｎ以上であり、防水シートの幅方向の引裂強度が、好ましくは１２Ｎ以上、さらに好ましくは１４Ｎ以上、より好ましくは１６Ｎ以上、特に好ましくは１７Ｎ以上であることが高耐久な防水層を形成できることから好ましい。 The waterproof sheet of the present invention has a tear strength in the longitudinal direction of the waterproof sheet measured according to JIS A 6013, preferably 5N or more, more preferably 7N or more, more preferably 8N or more, and particularly preferably 9N or more. In addition, the tear strength in the width direction of the waterproof sheet is preferably 12 N or more, more preferably 14 N or more, more preferably 16 N or more, and particularly preferably 17 N or more, because a highly durable waterproof layer can be formed.

本発明の防水シートは、ＪＩＳＡ６０１３に準拠して測定した、防水シートの長手方向の伸び率が、好ましくは３０％以上、さらに好ましくは４０％以上、より好ましくは４５％以上、特に好ましくは５０％以上であり、防水シートの幅方向の伸び率が、好ましくは４０％以上、さらに好ましくは５０％以上、より好ましくは６０％以上、特に好ましくは６５％以上であることが下地変形に追従できる防水層を形成できることから好ましい。 In the waterproof sheet of the present invention, the elongation in the longitudinal direction of the waterproof sheet, measured in accordance with JIS A 6013, is preferably 30% or more, more preferably 40% or more, more preferably 45% or more, particularly preferably. 50% or more, and the elongation in the width direction of the waterproof sheet is preferably 40% or more, more preferably 50% or more, more preferably 60% or more, and particularly preferably 65% or more to follow the underlying deformation. It is preferable because a waterproof layer can be formed.

本発明の防水シートは、ＡＳＴＭＤ９０３に準拠して測定した、１８０°剥離強度が、好ましくは２０Ｎ／２５ｍｍ以上、さらに好ましくは２２Ｎ／２５ｍｍ以上、より好ましくは２５Ｎ／２５ｍｍ以上、さらに好ましくは２８Ｎ／２５ｍｍ以上であることが剥離抵抗性が高い防水層を形成できることから好ましい。 The waterproof sheet of the present invention has a 180 ° peel strength measured in accordance with ASTM D 903, preferably 20 N / 25 mm or more, more preferably 22 N / 25 mm or more, more preferably 25 N / 25 mm or more, and further preferably 28 N. / 25 mm or more is preferable because a waterproof layer having high peeling resistance can be formed.

また、本発明の防水シートは、本発明の防水シートを敷設して形成した壁体に、各種付帯物を釘を用いて取り付けた場合にも、良好な防水性を保持していることが好ましいため、優れた釘穴シール性を有していることが好ましい。 Further, the waterproof sheet of the present invention preferably retains good waterproof properties even when various accessories are attached to the wall formed by laying the waterproof sheet of the present invention using nails. Therefore, it is preferable to have excellent nail hole sealing performance.

本発明の防水シート１３は、改質アスファルト層２５が露出する面に、剥離紙２６を有することが好ましい。その場合には、改質アスファルト層２５の予期せぬ場所への付着等を防止するなど、施工の際の作業性を向上することができる。 The waterproof sheet 13 of the present invention preferably has a release paper 26 on the surface where the modified asphalt layer 25 is exposed. In that case, workability at the time of construction can be improved, such as preventing the modified asphalt layer 25 from adhering to an unexpected place.

本発明の防水シート１３を製造するためには、まず、ポリエステル不織布２１およびポリエステルフィルム２３を用意する。次に、ポリエステルフィルム２３とポリエステル不織布２１との間に溶融状態のポリエチレンを流し込み、ロールコーターを用いて加圧接着して調製することによってポリエチレンの接着層２２を形成し、基材層２４を得る。次に、基材層２４のポリエステルフィルム２３に、改質アスファルト層２５を接着することによって、本発明の防水シート１３を得ることができる。 In order to manufacture the waterproof sheet 13 of the present invention, first, a polyester nonwoven fabric 21 and a polyester film 23 are prepared. Next, polyethylene in a molten state is poured between the polyester film 23 and the polyester nonwoven fabric 21 and is prepared by pressure bonding using a roll coater to form a polyethylene adhesive layer 22 to obtain a base material layer 24. . Next, the waterproof sheet 13 of the present invention can be obtained by adhering the modified asphalt layer 25 to the polyester film 23 of the base material layer 24.

本発明の防水シート１３は、防水が必要な構造体であれば、どこへでも施工することができる。本発明の防水シート１３の施工の際には、改質アスファルト層２５が、構造体と接するように施工することにより、改質アスファルト層２５の成分の、基材層２４への滲み出しを遮断することができる。 The waterproof sheet 13 of the present invention can be applied anywhere as long as the structure requires waterproofing. When the waterproof sheet 13 of the present invention is applied, the modified asphalt layer 25 is applied so as to be in contact with the structure, thereby preventing the components of the modified asphalt layer 25 from seeping into the base material layer 24. can do.

本発明の防水シート１３は、住宅のバルコニー手摺り壁などの各種壁体の壁天端部およびその周辺からの漏水を防止するため、各種壁体の壁天端部に対して施工することが好ましい。本発明の防水シート１３を、各種壁体の壁天端部を覆うように施工することによって、防水性に優れる防水壁体を得ることができる。以下に、本発明の防水シート１３を用いた防水壁体の製造方法の例を説明する。 The waterproof sheet 13 of the present invention can be applied to the wall top edge of various wall bodies in order to prevent water leakage from the wall top edge of various wall bodies such as a balcony handrail wall of a house and its surroundings. preferable. By constructing the waterproof sheet 13 of the present invention so as to cover the wall top end portions of various wall bodies, a waterproof wall body having excellent waterproof properties can be obtained. Below, the example of the manufacturing method of the waterproofing wall body using the waterproof sheet 13 of this invention is demonstrated.

図２（ａ）は、本発明の防水シート１３を用いた壁天端部の防水方法について施工手順を示すものである。（１）壁体１１の壁天端部の付着物などを除去して清浄にしたのち、（２）改質アスファルト層２５が壁体１１に面し、かつ防水シート１３が壁天端部を跨ぐように、防水シート１３を配置し、壁体１１の両側面の少なくとも一部および壁天端部に貼り付ける。このように防水シート１３を貼り付けることによって、防水シート１３の改質アスファルト層２５が壁天端部および壁体１１の両側面の少なくとも一部と接することになる。また、改質アスファルト層２５は、壁体１１に接着する面とは反対側の面を、ポリエステルフィルム２３を含む基材層２４によって覆われている状態となる。また、本発明では、防水シート１３が壁天端部を跨ぐように防水シート１３を配置し、さらに壁体１１の下部まで防水シート１３を貼り付けることができ、このように防水シート１３を貼り付けた場合には、壁天端部に加え、壁体１１の側面部全体をも防水することができる。（３）次に、防水シート１３を貼り付けた部分を含む壁体１１の側面（表面と裏面）にモルタル１４を施工して養生・硬化させる。モルタル１４が硬化したのち壁天端部に笠木設置用のスペーサー１５を所定の間隔で固定し、スペーサー１５の上に笠木１６を設置して固定する。笠木１６と壁体１１との隙間部分にはシリコーンなどのコーキング材１７を用いてシーリングする。 Fig.2 (a) shows a construction procedure about the waterproofing method of the wall ceiling end part using the waterproof sheet 13 of this invention. (1) After removing the deposits and the like on the wall top end of the wall body 11 and cleaning it, (2) the modified asphalt layer 25 faces the wall body 11 and the waterproof sheet 13 covers the wall top end. The waterproof sheet 13 is disposed so as to straddle, and is attached to at least a part of both side surfaces of the wall body 11 and the top of the wall. By sticking the waterproof sheet 13 in this way, the modified asphalt layer 25 of the waterproof sheet 13 comes into contact with at least a part of the wall top end and both side surfaces of the wall body 11. Further, the modified asphalt layer 25 is in a state where the surface opposite to the surface that adheres to the wall 11 is covered with the base material layer 24 including the polyester film 23. Moreover, in this invention, the waterproof sheet 13 can be arrange | positioned so that the waterproof sheet 13 may straddle a wall top edge part, and also the waterproof sheet 13 can be affixed to the lower part of the wall body 11, and the waterproof sheet 13 is stuck in this way. When attached, in addition to the top of the wall, the entire side surface of the wall 11 can be waterproofed. (3) Next, the mortar 14 is applied to the side surfaces (front surface and back surface) of the wall body 11 including the portion to which the waterproof sheet 13 is attached, and is cured and cured. After the mortar 14 has hardened, the headboard installation spacer 15 is fixed to the top of the wall at a predetermined interval, and the headboard 16 is installed on the spacer 15 and fixed. Sealing is performed using a caulking material 17 such as silicone in a gap portion between the headboard 16 and the wall body 11.

図２（ｂ）は、本発明の防水シート１３を用いた壁天端部の防水方法について好ましい施工手順を示すものである。（１）壁体１１の壁天端部の付着物などを除去して清浄にしたのち、天端部に構造用合板１２を配置して固定する。構造用合板１２の幅は、壁体の厚さ（両側面間の長さ）より０ｍｍ超（０ｍｍを含まない）〜２０ｍｍ大きいものを使用する。（２）次に、防水シート１３が、設置した構造用合板１２を跨ぐように、防水シート１３を配置し、壁体１１の両側面の少なくとも一部および構造用合板１２に貼り付ける。したがって、防水シート１３は、構造用合板１２を跨いで巻き込むような構造となる。このとき、防水シート１３は、改質アスファルト層２５が構造用合板１２および壁体１１の両側面の少なくとも一部と接することになる。また、改質アスファルト層２５は、構造用合板１２および壁体１１に接着する面とは反対側の面を、ポリエステルフィルム２３を含む基材層２４によって覆われている状態となる。また、壁体１１の下部まで防水シート１３を貼り付けることができ、その場合には、壁天端部に加え、壁体１１の側面部全体をも防水することができる。（３）次に、防水シート１３を貼り付けた部分を含む壁体１１の側面（表面と裏面）にモルタル１４を施工して養生・硬化させたのち、壁天端部に笠木設置用のスペーサー１５を所定の間隔で固定し、スペーサー１５の上に笠木１６を設置して固定する。さらに、笠木１６と壁体１１との隙間部分にはシリコーンなどのコーキング材１７を用いてシーリングする。本方法を用いて得られる壁体１１は、構造用合板１２の存在のため、雨垂れによる壁体１１の側面への汚れ発生の防止を確実にするために好ましい。 FIG.2 (b) shows a preferable construction procedure about the waterproofing method of the wall top end part using the waterproof sheet 13 of this invention. (1) After removing the deposits and the like on the wall top end of the wall 11 and cleaning it, the structural plywood 12 is disposed and fixed on the top end. The width of the structural plywood 12 is greater than 0 mm (excluding 0 mm) to 20 mm larger than the wall thickness (length between both side surfaces). (2) Next, the waterproof sheet 13 is disposed so that the waterproof sheet 13 straddles the installed structural plywood 12, and is attached to at least a part of both side surfaces of the wall body 11 and the structural plywood 12. Therefore, the waterproof sheet 13 has a structure in which it is wound over the structural plywood 12. At this time, in the waterproof sheet 13, the modified asphalt layer 25 comes into contact with at least a part of the both sides of the structural plywood 12 and the wall body 11. The modified asphalt layer 25 is in a state where the surface opposite to the surface bonded to the structural plywood 12 and the wall 11 is covered with the base material layer 24 including the polyester film 23. Moreover, the waterproof sheet 13 can be affixed to the lower part of the wall body 11, and in that case, in addition to a wall top end part, the whole side part of the wall body 11 can be waterproofed. (3) Next, after the mortar 14 is applied to the side surfaces (front and back surfaces) of the wall body 11 including the portion where the waterproof sheet 13 is pasted and cured and cured, a spacer for installing the headboard at the top of the wall 15 is fixed at a predetermined interval, and the headboard 16 is installed on the spacer 15 and fixed. Further, the gap between the headboard 16 and the wall 11 is sealed using a caulking material 17 such as silicone. The wall body 11 obtained by using this method is preferable in order to ensure the prevention of contamination on the side surface of the wall body 11 due to dripping because of the presence of the structural plywood 12.

以上のような方法により、本発明の防水シート１３を用いた、防水性に優れる防水壁体を得ることができる。 By the above method, the waterproof wall body excellent in waterproofness using the waterproof sheet 13 of this invention can be obtained.

上述の、防水壁体の製造方法において、本発明の防水シート１３を壁体１１に貼り付ける際に、改質アスファルト層２５が壁体１１に面するように貼り付けるので、改質アスファルト層２５は、ポリエステルフィルム２３に覆われる状態となる。そのため、防水シート１３に雨水が付着した場合に、改質アスファルト層２５への雨水の浸透をポリエステルフィルム２３によって遮断し、雨水と改質アスファルト層２５との接触を防ぐことができる。その結果、壁天端の防水シート１３に接触した雨水が雨垂れとなった場合にも、改質アスファルト層２５からの成分の溶出を回避することができる。同様に、各種構造体の天端部を覆うように本発明の防水シート１３を施工することにより、雨垂れによる各種構造体の表面の汚れの発生を防止することができる各種防水構造体を得ることができ、各種防水構造体の表面の美観を維持することができる。 In the above-described method for manufacturing a waterproof wall, when the waterproof sheet 13 of the present invention is attached to the wall 11, the modified asphalt layer 25 is attached so as to face the wall 11. Is covered with the polyester film 23. Therefore, when rainwater adheres to the waterproof sheet 13, the penetration of rainwater into the modified asphalt layer 25 can be blocked by the polyester film 23, and contact between the rainwater and the modified asphalt layer 25 can be prevented. As a result, the elution of components from the modified asphalt layer 25 can be avoided even when rainwater that has come into contact with the waterproof sheet 13 at the top of the wall becomes dripping. Similarly, by applying the waterproof sheet 13 of the present invention so as to cover the top end portions of various structures, various waterproof structures that can prevent the occurrence of dirt on the surfaces of the various structures due to rain dripping are obtained. It is possible to maintain the beauty of the surface of various waterproof structures.

上記の汚れの発生は、図２に示すモルタル１４を施工する際にも発生することがしばしばあるが、本発明の防水シート１３を用いることにより、改質アスファルト層２５からの成分の溶出を回避することができるため、各種構造体の表面の汚れの発生を防止し、各種構造体の表面の美観を維持することができる。 The occurrence of the above-mentioned stains often occurs when the mortar 14 shown in FIG. 2 is applied, but by using the waterproof sheet 13 of the present invention, elution of components from the modified asphalt layer 25 is avoided. Therefore, it is possible to prevent the occurrence of contamination on the surfaces of various structures and maintain the aesthetic appearance of the surfaces of the various structures.

本発明の防水シート１３は、美観維持が特に必要となるバルコニーの手摺り壁天端部の防水に対して用いる場合に、特に優れた効果を奏する。 The waterproof sheet 13 of the present invention has a particularly excellent effect when it is used for waterproofing the top end portion of a handrail wall of a balcony where aesthetic maintenance is particularly required.

本発明の防水シート１３を用いることによって得られる壁体等の各種構造体は、構造体天端の防水シート１３に接触した雨水が、雨垂れとなった場合にも、雨垂れによる各種構造体の表面の汚れの発生を防止することのでき、各種構造体の表面の美観を維持することができる。 Various structures such as a wall obtained by using the waterproof sheet 13 of the present invention have a surface of various structures caused by rain dripping even when rain water that comes in contact with the waterproof sheet 13 at the top of the structure becomes rain dripping. The occurrence of contamination can be prevented, and the aesthetic appearance of the surfaces of various structures can be maintained.

以下、本発明を実施例に基づき、さらに詳細に説明する。但し、本発明は下記実施例により制限されるものでない。 Hereinafter, the present invention will be described in more detail based on examples. However, the present invention is not limited by the following examples.

（比較例１、実施例１）
表１に示すように、２種類の防水シートを用いて、図３に示すように、木造壁体（高さ１０００ｍｍ、幅３０００ｍｍ、壁厚１５０ｍｍ）の壁天端部を跨ぐように、防水シートを木造壁体に貼り付けることによって２つの防水試験体を製作し、防水試験体を屋外に設置して屋外曝露を行った。防水シートは、表１に示す構成および性能を有するものを使用した。なお、ポリエステル不織布と、ポリエステルフィルムとは、ＰＥ（ポリエチレン）ラミネート層を接着層として、ロールコーターを用いて接着した。 (Comparative Example 1, Example 1)
As shown in Table 1, using two types of waterproof sheets, as shown in FIG. 3, the waterproof sheet extends across the top of the wall of the wooden wall (height 1000 mm, width 3000 mm, wall thickness 150 mm). Two waterproof test specimens were manufactured by sticking to a wooden wall, and the waterproof test specimens were installed outdoors and exposed outdoors. A waterproof sheet having the configuration and performance shown in Table 1 was used. The polyester nonwoven fabric and the polyester film were bonded using a roll coater with a PE (polyethylene) laminate layer as an adhesive layer.

屋外に防水試験体を設置してから２週間経過後、木造壁体の防水シート貼付け部分から下方部分への雨垂れ汚れの発生状況を観察した。屋外曝露期間中に雨天の日が２日あったにもかかわらず、実施例１の防水シートを用いた防水試験体の木造壁体の側面（防水シート貼付け部分から下方部分）には、雨垂れによる汚れは全く認められなかった。一方、比較例１の防水シートを用いた防水試験体の木造壁体の側面（防水シート貼付け部分から下方部分）には、雨垂れに伴う薄茶色の汚れが発生していた。 Two weeks after the waterproof test specimen was installed outdoors, the occurrence of dripping dirt from the waterproof sheet-attached part of the wooden wall to the lower part was observed. Even though there were two rainy days during the outdoor exposure period, the side of the wooden wall body of the waterproof test body using the waterproof sheet of Example 1 (from the waterproof sheet pasting part to the lower part) was caused by raindrops. No stain was observed. On the other hand, on the side surface of the wooden wall body of the waterproof test body using the waterproof sheet of Comparative Example 1 (the lower part from the waterproof sheet-attached portion), a light brown stain accompanying rain dripping occurred.

本発明の防水シートを木造壁体の壁天端部を跨ぐように貼り付けた防水試験体の場合、防水シートが遮水性に優れるポリエステルフィルムの層を有するため、防水シートに雨水がかかった場合に、雨水の浸透を遮断することによって、雨水が改質アスファルト層と接触することを防ぐことができたためと推考される。 In the case of the waterproof test body in which the waterproof sheet of the present invention is pasted so as to straddle the top of the wall of the wooden wall body, since the waterproof sheet has a layer of a polyester film excellent in water shielding, when the waterproof sheet is exposed to rain water Moreover, it is considered that the rainwater could be prevented from coming into contact with the modified asphalt layer by blocking the penetration of the rainwater.

図５に示すように、防水シートを貫通するようにスクリュウ釘を配置し、その上に水頭１５０ｍｍとなるように水を配置する針穴シール性試験を行なった。この試験開始から２４時間後に、防水シートからの漏水の有無を確認した。その結果、表１に「○」として示すように、実施例１の防水シートからの漏水は認められなかったことから、本発明に用いる防水シートは、優れた針穴シール性を有していることが明らかとなった。 As shown in FIG. 5, a screw hole sealability test was performed in which a screw nail was disposed so as to penetrate the waterproof sheet, and water was disposed on the screw nail so as to have a head of 150 mm. After 24 hours from the start of the test, the presence or absence of water leakage from the waterproof sheet was confirmed. As a result, as shown as “◯” in Table 1, water leakage from the waterproof sheet of Example 1 was not recognized, so the waterproof sheet used in the present invention has excellent needle hole sealing properties. It became clear.

本発明の防水シートの模式断面図（一例）である。It is a schematic cross section (an example) of the waterproof sheet of the present invention. 本発明の壁天端部の防水方法の手順の一例を示す模式断面図であり、（ａ）壁天端部に構造用合板を設けない場合、および（ｂ）壁天端部に構造用合板を設ける場合を示す模式断面図である。It is a schematic cross section which shows an example of the procedure of the waterproofing method of the wall top end part of this invention, (a) When a structural plywood is not provided in a wall top end part, and (b) Structural plywood in a wall top end part It is a schematic cross section which shows the case where it provides. 本発明の防水シートを壁天端部を跨ぐように貼り付けた防水試験体の斜視図である。It is a perspective view of the waterproof test body which affixed the waterproof sheet of this invention so that a wall top end part might be straddled. ポリエステルフィルムの層を有しない防水シートの模式断面図（一例）である。It is a schematic cross section (an example) of the waterproof sheet which does not have a layer of a polyester film. 防水シートの釘穴シール性の試験方法を示す模式断面図である。It is a schematic cross section which shows the test method of the nail hole sealing property of a waterproof sheet.

Explanation of symbols

１１：壁体
１２：構造用合板
１３：防水シート
１４：モルタル
１５：スペーサー
１６：笠木
２１：ポリエステル不織布
２２：接着層
２３：ポリエステルフィルム
２４：基材層
２５：改質アスファルト層
２６：剥離紙 DESCRIPTION OF SYMBOLS 11: Wall 12: Structural plywood 13: Waterproof sheet 14: Mortar 15: Spacer 16: Kasagi 21: Polyester nonwoven fabric 22: Adhesive layer 23: Polyester film 24: Base material layer 25: Modified asphalt layer 26: Release paper

Claims

A waterproof sheet comprising a base material layer including a polyester film and a modified asphalt layer adhered to the polyester film.

The waterproof sheet according to claim 1, wherein the base material layer further comprises a polyester nonwoven fabric, and further comprises an adhesive layer between the polyester film and the polyester nonwoven fabric.

The waterproof sheet according to claim 2, wherein the adhesive layer is an adhesive layer made of polyethylene.

The polyester nonwoven fabric has a unit area mass of 20 to 200 g / m ² .
The adhesive layer has a thickness of 5 to 100 μm;
The waterproof sheet according to claim 2 or 3, wherein the polyester film has a thickness of 2 to 50 µm.

The waterproof sheet according to any one of claims 1 to 4, wherein the thickness of the waterproof sheet is 0.3 to 1.5 mm.

The waterproof structure which constructed the waterproof sheet of any one of Claims 1-5 so that the top end part of a waterproof structure might be covered.

Preparing a polyester nonwoven fabric and a polyester film;
A step of forming a base material layer by pouring molten polyethylene between a polyester film and a polyester nonwoven fabric, and preparing by bonding under pressure to form an adhesive layer;
And a step of adhering the modified asphalt layer to the polyester film.