JP2009197093A - Magenta ink composition, ink cartridge, and recording system and recorded material using the same - Google Patents
Magenta ink composition, ink cartridge, and recording system and recorded material using the same Download PDFInfo
- Publication number
- JP2009197093A JP2009197093A JP2008038741A JP2008038741A JP2009197093A JP 2009197093 A JP2009197093 A JP 2009197093A JP 2008038741 A JP2008038741 A JP 2008038741A JP 2008038741 A JP2008038741 A JP 2008038741A JP 2009197093 A JP2009197093 A JP 2009197093A
- Authority
- JP
- Japan
- Prior art keywords
- ink composition
- magenta ink
- weight
- solid solution
- composition according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、新規なマゼンタインク組成物に関する。特に、記録した際の発色性、粒状性、及び光沢性に優れ、インクジェット式記録ヘッドでの目詰まりを起こしにくく、さらに高彩度かつ高明度なレッド領域の色再現性と紫領域の色再現性に優れたマゼンタインク組成物に関し、さらには、これを含むインクカートリッジ、これを用いた記録システム及び記録物に関する。 The present invention relates to a novel magenta ink composition. In particular, it has excellent color developability, graininess, and glossiness during recording, is less likely to cause clogging with an ink jet recording head, and has high chroma and lightness color reproducibility in the red region and purple color reproducibility. The present invention relates to an excellent magenta ink composition, and further relates to an ink cartridge including the same, a recording system using the same, and a recorded matter.
従来、カラーインクジェット記録用のマゼンタインクとしては、単一結晶型のＣ．Ｉ．ピグメントレッド１２２や、Ｃ．Ｉ．ピグメントバイオレット１９、３２などの顔料を色材として用いたマゼンタインクが提案されている（例えば、特許文献１、特許文献２を参照）。 Conventionally, as a magenta ink for color ink jet recording, a single crystal type C.I. I. Pigment red 122, C.I. I. Magenta inks using pigments such as pigment violet 19 and 32 as color materials have been proposed (see, for example, Patent Document 1 and Patent Document 2).
単一結晶型のＣ．Ｉ．ピグメントレッド１２２（以下、単一結晶型ＰＲ１２２ということがある）は、発色性、粒状性、及び光沢性に比較的優れており、また、発色性が良好なため顔料濃度を比較的低くしても色再現性が比較的良好であることが分かっている。
しかしながら、より一層、記録した際の発色性、粒状性、及び光沢性に優れ、さらに高彩度かつ高明度なレッド領域の色再現性と紫領域の色再現性に優れたマゼンタインクの提供が望まれている。
C. single crystal type C.I. I. Pigment Red 122 (hereinafter sometimes referred to as “single crystal type PR122”) is relatively excellent in color developability, graininess, and glossiness, and has good color developability so that the pigment concentration is relatively low. Has also been found to have relatively good color reproducibility.
However, it is desirable to provide a magenta ink that is excellent in color development, graininess, and glossiness during recording, and has excellent color reproducibility in the red region and in the purple region that is highly saturated and light. ing.
また、Ｃ．Ｉ．ピグメントバイオレット１９、３２（以下、それぞれＰＶ１９、ＰＶ３２ということがある）についても、記録した際の発色性、粒状性、及び光沢性、さらに高彩度かつ高明度なレッド領域の色再現性と紫領域の色再現性のさらなる改善が望まれている。
すなわち、ＰＶ１９は高Ｌ*値は得られるもののａ*値が比較的小さく、さらなる高彩度が望まれていた。また、ＰＶ１９はｂ*値が比較的大きいために、低明度な紫領域の色再現性に優れたマゼンタインクの提供が望まれていた。一方、ＰＶ３２は高ａ*値及び高Ｌ*値が十分に実現されておらず、さらなる高明度が望まれていた。また、発色性、粒状性、及び光沢性のさらなる向上も望まれていた。
In addition, C.I. I. Pigment Violet 19 and 32 (hereinafter sometimes referred to as PV19 and PV32, respectively) also have color development, graininess, and gloss when recorded, as well as color reproducibility in the red region with high chroma and lightness, and in the purple region. Further improvement of color reproducibility is desired.
That is, although PV19 can obtain a high L * value, the a * value is relatively small, and further high saturation is desired. Further, since PV19 has a relatively large b * value, it has been desired to provide a magenta ink excellent in color reproducibility in a low brightness purple region. On the other hand, PV32 has not sufficiently realized a high a * value and a high L * value, and further high brightness has been desired. In addition, further improvements in color developability, graininess, and gloss have been desired.
そこで、本発明は、記録した際の発色性、粒状性、及び光沢性に優れ、インクジェット式記録ヘッドでの目詰まりを起こしにくく、さらに高彩度かつ高明度なレッド領域の色再現性と紫領域の色再現性に優れたマゼンタインク組成物を提供することを目的の一つとする。 Therefore, the present invention is excellent in color developability, graininess, and glossiness at the time of recording, is less likely to be clogged with an ink jet recording head, and has high color saturation and high brightness red area color reproducibility and purple area. One object is to provide a magenta ink composition having excellent color reproducibility.
また、本発明は、上記の優れたマゼンタインク組成物を含むインクカートリッジを提供することを他の目的とする。 Another object of the present invention is to provide an ink cartridge containing the above-described excellent magenta ink composition.
また、本発明は、上記の優れたマゼンタインク組成物を用いた記録システム及び記録物を提供することを更に他の目的とする。 Another object of the present invention is to provide a recording system and a recorded matter using the above-described excellent magenta ink composition.
本発明者らは、鋭意研究を重ねた結果、色材として、可視域（４００〜８００ｎｍ）における吸収スペクトルが、少なくとも、波長５１０ｎｍ〜５３５ｎｍに１つの吸収ピーク（Ａ）と、波長５５０〜５７０ｎｍに１つの吸収ピーク（Ｂ）と、を有し、前記吸収ピーク（Ａ）のピーク値の、前記吸収ピーク（Ｂ）のピーク値に対する相対値（Ａ／Ｂ）が、０．９＜Ａ／Ｂ＜１．０である、マゼンタインク組成物が、発色性、粒状性、及び光沢性に優れ、さらに高彩度かつ高明度なレッド領域の色再現性と紫領域の色再現性に優れることを見出し、本発明を完成するに至った。 As a result of intensive studies, the inventors have found that, as a colorant, the absorption spectrum in the visible region (400 to 800 nm) has at least one absorption peak (A) at wavelengths of 510 nm to 535 nm and wavelengths of 550 to 570 nm. One absorption peak (B), and the relative value (A / B) of the peak value of the absorption peak (A) to the peak value of the absorption peak (B) is 0.9 <A / B <1.0, found that the magenta ink composition is excellent in color developability, graininess, and gloss, and is excellent in color reproducibility in the red region and purple region in high saturation and brightness, The present invention has been completed.
すなわち、本発明は、（１）可視域（４００〜８００ｎｍ）における吸収スペクトルが、少なくとも、波長５１０ｎｍ〜５３５ｎｍに１つの吸収ピーク（Ａ）と、波長５５０〜５７０ｎｍに１つの吸収ピーク（Ｂ）と、を有し、前記吸収ピーク（Ａ）のピーク値の、前記吸収ピーク（Ｂ）のピーク値に対する相対値（Ａ／Ｂ）が、０．９＜Ａ／Ｂ＜１．０である、マゼンタインク組成物；
（２）波長５２０ｎｍにおける吸収スペクトル値（Ｃ）の、前記吸収ピーク（Ｂ）のピーク値に対する相対値（Ｃ／Ｂ）が、０．９３＜Ｃ／Ｂ＜１．０である、前記（１）記載のマゼンタインク組成物；
（３）γ型Ｃ．Ｉ．ピグメントバイオレット１９と、Ｃ．Ｉ．ピグメントレッド２０２と、の固溶体を、マゼンタインク組成物中２重量％以上含む、前記（１）又は（２）に記載のマゼンタインク組成物；
（４）γ型Ｃ．Ｉ．ピグメントバイオレット１９及びＣ．Ｉ．ピグメントレッド２０２の固溶体と、Ｃ．Ｉ．ピグメントバイオレット１９と、を含む、前記（１）又は（２）に記載のマゼンタインク組成物；
（５）γ型Ｃ．Ｉ．ピグメントバイオレット１９及びＣ．Ｉ．ピグメントレッド２０２の固溶体を、マゼンタインク組成物中１重量％以上２重量％未満と、Ｃ．Ｉ．ピグメントバイオレット１９と、を含む、前記（１）又は（２）に記載のマゼンタインク組成物；
（６）Ｃ．Ｉ．ピグメントレッド２０９を含む、前記（１）又は（２）に記載のマゼンタインク組成物；
（７）炭素数５〜１０の分岐を有してもよいアルカンジオールを３重量％以上１５重量％以下含む、前記（１）〜（６）の何れかに記載のマゼンタインク組成物；
（８）界面活性剤として、ポリオルガノシロキサンを含む、前記（１）〜（７）の何れかに記載のマゼンタインク組成物；
（９）前記ポリシロキサン類は、下記一般式で表されるポリオルガノシロキサンである、前記（８）記載のマゼンタインク組成物
（１０）前記ポリシロキサン類は、下記一般式で表されるポリオルガノシロキサンである、前記（８）記載のマゼンタインク組成物
（１１）インクジェット式記録に用いられる前記（１）〜（１０）の何れかに記載のインクジェット記録用マゼンタインク組成物；
（１２）前記（１）〜（１１）の何れかに記載のマゼンタインク組成物を含むインクカートリッジ；
（１３）前記（１）〜（１１）の何れかに記載のマゼンタインク組成物を用いて画像を形成する記録システム；
（１４）前記（１）〜（１１）の何れかに記載のマゼンタインク組成物を用いて画像が形成されてなる記録物；を提供する。
That is, the present invention has (1) an absorption spectrum in the visible region (400 to 800 nm) having at least one absorption peak (A) at wavelengths of 510 nm to 535 nm and one absorption peak (B) at wavelengths of 550 to 570 nm. The relative value (A / B) of the peak value of the absorption peak (A) with respect to the peak value of the absorption peak (B) is 0.9 <A / B <1.0. An ink composition;
(2) The relative value (C / B) of the absorption spectrum value (C) at a wavelength of 520 nm with respect to the peak value of the absorption peak (B) is 0.93 <C / B <1.0. ) Magenta ink composition as described above;
(3) γ-type C.I. I. Pigment violet 19 and C.I. I. The magenta ink composition according to (1) or (2) above, containing a solid solution of CI Pigment Red 202 in an amount of 2% by weight or more in the magenta ink composition;
(4) γ-type C.I. I. Pigment violet 19 and C.I. I. Pigment Red 202 solid solution, C.I. I. A magenta ink composition according to (1) or (2), comprising Pigment Violet 19;
(5) γ-type C.I. I. Pigment violet 19 and C.I. I. Pigment Red 202 is a solid solution of 1% by weight or more and less than 2% by weight in the magenta ink composition; I. A magenta ink composition according to (1) or (2), comprising Pigment Violet 19;
(6) C.I. I. The magenta ink composition according to the above (1) or (2), which contains CI Pigment Red 209;
(7) The magenta ink composition according to any one of the above (1) to (6), comprising 3 to 15% by weight of an alkanediol which may have a branch having 5 to 10 carbon atoms;
(8) The magenta ink composition according to any one of (1) to (7), which contains polyorganosiloxane as a surfactant;
(9) The magenta ink composition according to (8), wherein the polysiloxane is a polyorganosiloxane represented by the following general formula:
(10) The magenta ink composition according to (8), wherein the polysiloxane is a polyorganosiloxane represented by the following general formula:
(11) The magenta ink composition for ink jet recording according to any one of (1) to (10), which is used for ink jet recording;
(12) An ink cartridge containing the magenta ink composition according to any one of (1) to (11);
(13) A recording system for forming an image using the magenta ink composition according to any one of (1) to (11);
(14) A recorded matter in which an image is formed using the magenta ink composition according to any one of (1) to (11).
本発明によれば、記録した際の発色性、粒状性、及び光沢性に優れ、インクジェット式記録ヘッドでの目詰まりを起こしにくく、さらに高彩度かつ高明度なレッド領域の色再現性と紫領域の色再現性に優れたマゼンタインク組成物、当該優れたマゼンタインク組成物を含むインクカートリッジ、並びに当該優れたマゼンタインク組成物を用いた記録システム及び記録物が提供される。 According to the present invention, the color developability, graininess, and glossiness at the time of recording are excellent, clogging is hardly caused in an ink jet recording head, and the color reproducibility of a red area with high saturation and high brightness and the purple area. Provided are a magenta ink composition excellent in color reproducibility, an ink cartridge containing the excellent magenta ink composition, a recording system and a recorded matter using the excellent magenta ink composition.
次に、本発明の実施の形態について説明する。以下の実施形態は、本発明を説明するための例示であり、本発明をこの実施形態にのみ限定する趣旨ではない。本発明は、その要旨を逸脱しない限り、さまざまな形態で実施することができる。 Next, an embodiment of the present invention will be described. The following embodiment is an example for explaining the present invention, and is not intended to limit the present invention only to this embodiment. The present invention can be implemented in various forms without departing from the gist thereof.
〔マゼンタインク組成物〕
本発明のマゼンタインク組成物は、可視域（４００〜８００ｎｍ）における吸収スペクトルが、少なくとも、波長５１０ｎｍ〜５３５ｎｍに１つの吸収ピーク（Ａ）と、波長５５０〜５７０ｎｍに１つの吸収ピーク（Ｂ）と、を有し、前記吸収ピーク（Ａ）のピーク値の、前記吸収ピーク（Ｂ）のピーク値に対する相対値（Ａ／Ｂ）が、０．９＜Ａ／Ｂ＜１．０であるものである。
このような構成としたことにより、記録した際の発色性、粒状性、及び光沢性に優れ、インクジェット式記録ヘッドでの目詰まりを起こしにくく、さらに高彩度かつ高明度なレッド領域の色再現性と紫領域の色再現性に優れたマゼンタインク組成物が提供される。
[Magenta ink composition]
The magenta ink composition of the present invention has an absorption spectrum in the visible region (400 to 800 nm) having at least one absorption peak (A) at wavelengths of 510 nm to 535 nm and one absorption peak (B) at wavelengths of 550 to 570 nm. The relative value (A / B) of the peak value of the absorption peak (A) with respect to the peak value of the absorption peak (B) is 0.9 <A / B <1.0. is there.
By adopting such a configuration, it is excellent in color development, graininess, and glossiness at the time of recording, is less likely to cause clogging in an ink jet recording head, and has high color saturation and lightness in the color reproducibility of the red region. A magenta ink composition excellent in color reproducibility in the purple region is provided.
本発明のマゼンタインク組成物は、発色性が良好なため顔料濃度を比較的低くしても高彩度かつ高明度の領域での色再現性が優れている。顔料濃度が比較的低くても色再現性に優れているので、顔料濃度を高めることによってインクの粘度が高くなってしまうことを防ぐことができる。
また、本発明のマゼンタインク組成物は、顔料を高濃度化した場合の普通紙における発色性の向上が顕著である。
さらに、本発明のマゼンタインク組成物は、耐ガス性、耐光性、及び耐メタメリズム性にも優れている。
The magenta ink composition of the present invention has excellent color reproducibility, so that even if the pigment concentration is relatively low, color reproducibility is excellent in a high chroma and high brightness region. Since the color reproducibility is excellent even when the pigment concentration is relatively low, it is possible to prevent the viscosity of the ink from increasing by increasing the pigment concentration.
Further, the magenta ink composition of the present invention is remarkably improved in color development on plain paper when the pigment concentration is increased.
Furthermore, the magenta ink composition of the present invention is excellent in gas resistance, light resistance and metamerism resistance.
なお、マゼンタインク組成物の可視域（４００〜８００ｎｍ）における吸収スペクトルの測定は、一般的な紫外可視光吸収スペクトル測定装置を用いて測定することができる。 In addition, the measurement of the absorption spectrum in the visible region (400-800 nm) of a magenta ink composition can be measured using a general ultraviolet visible light absorption spectrum measuring apparatus.
上記マゼンタインク組成物は、波長５２０ｎｍにおける吸収スペクトル値（Ｃ）の、前記吸収ピーク（Ｂ）のピーク値に対する相対値（Ｃ／Ｂ）が、０．９３＜Ｃ／Ｂ＜１．０である、ことが好ましい。
このような好適な構成とすることにより、上記の本発明の効果に加えて、特に粒状性及び発色性が顕著に優れたマゼンタインク組成物が提供される。
In the magenta ink composition, the relative value (C / B) of the absorption spectrum value (C) at a wavelength of 520 nm to the peak value of the absorption peak (B) is 0.93 <C / B <1.0. Is preferable.
By adopting such a suitable configuration, in addition to the effects of the present invention described above, a magenta ink composition that is particularly excellent in graininess and color developability is provided.
上記マゼンタインク組成物は、６０度鏡面光沢が２０以上の記録媒体に記録した場合、該記録媒体において、０〜１００％までの濃度の異なるパッチを階調印刷したときに得られる吸収スペクトルを平均化し、吸収スペクトルの最大ピーク値に対する相対値として、以下の（１）〜（４）の全ての特性を有することが好ましい。
（１）波長５２０ｎｍの相対吸収スペクトル値が０．９３〜１．０
（２）波長５３０ｎｍの相対吸収スペクトル値が０．８０〜１．０
（３）波長５４０ｎｍの相対吸収スペクトル値が０．７０〜０．９５
（４）波長５６０ｎｍの相対吸収スペクトル値が０．９５〜１．０
When the magenta ink composition is recorded on a recording medium having a 60-degree specular gloss of 20 or more, the average absorption spectrum obtained when gradation-printing patches having different densities from 0 to 100% is recorded on the recording medium. It is preferable to have all the following characteristics (1) to (4) as relative values with respect to the maximum peak value of the absorption spectrum.
(1) The relative absorption spectrum value at a wavelength of 520 nm is 0.93 to 1.0.
(2) The relative absorption spectrum value at a wavelength of 530 nm is 0.80 to 1.0.
(3) The relative absorption spectrum value at a wavelength of 540 nm is 0.70 to 0.95.
(4) The relative absorption spectrum value at a wavelength of 560 nm is 0.95 to 1.0.
上記マゼンタインク組成物は、γ型Ｃ．Ｉ．ピグメントバイオレット１９及びＣ．Ｉ．ピグメントレッド２０２の固溶体を、マゼンタインク組成物中２重量％以上含むことが好ましい。
このような好適な構成とすることにより、上記の本発明の効果に加えて、特に粒状性、発色性、光沢性、耐メタメリズム性、耐ガス性、耐光性が顕著に優れたマゼンタインク組成物が提供される。
The magenta ink composition contains γ-type C.I. I. Pigment violet 19 and C.I. I. It is preferable that 2% by weight or more of the solid solution of Pigment Red 202 is included in the magenta ink composition.
By adopting such a suitable configuration, in addition to the effects of the present invention described above, a magenta ink composition that is particularly excellent in graininess, color development, glossiness, metamerism resistance, gas resistance, and light resistance. Is provided.
「γ型Ｃ．Ｉ．ピグメントバイオレット１９と、Ｃ．Ｉ．ピグメントレッド２０２と、の固溶体」とは、γ型ＰＶ１９と、ＰＲ２０２とが固体で互いに溶けた状態をなす結晶を意味する。
上記固溶体のγ型ＰＶ１９とＰＲ２０２との量比は本発明の範囲内で適宜調整できるが、γ型ＰＶ１９の重量がＰＶ２０２の重量よりも大きいことが好ましい。
The “solid solution of γ-type CI Pigment Violet 19 and CI Pigment Red 202” means a crystal in which γ-type PV19 and PR202 are solid and are dissolved in each other.
The amount ratio of γ-type PV19 and PR202 in the solid solution can be appropriately adjusted within the scope of the present invention, but the weight of γ-type PV19 is preferably larger than the weight of PV202.
前記固溶体の好適な例の粉末Ｘ線回折分析の結果を図１に示す。本分析においては、Pa
Nalytical X'PertProを用いて、深さ０．５ｍｍのガラスセルに試料を詰めて測定した。
The result of the powder X-ray diffraction analysis of the suitable example of the said solid solution is shown in FIG. In this analysis, Pa
Using Nalytical X'PertPro, the sample was packed in a glass cell having a depth of 0.5 mm and measured.
上記好適なマゼンタインク組成物は、所定の固溶体を少なくとも含むことを特徴とするものであって、該固溶体を含む限り、ＰＶ１９、ＰＶ３２等のその他のマゼンタ系顔料あるいはその他の顔料をさらに含んでいてもよい。また、該固溶体のγ型ＰＶ１９とＰＲ２０２との量比は本発明の範囲内で適宜調整できるものである。 The preferred magenta ink composition is characterized in that it contains at least a predetermined solid solution, and as long as it contains the solid solution, it further contains other magenta pigments such as PV19 and PV32 or other pigments. Also good. In addition, the amount ratio of γ-type PV19 and PR202 in the solid solution can be appropriately adjusted within the scope of the present invention.
上記マゼンタインク組成物は、γ型Ｃ．Ｉ．ピグメントバイオレット１９及びＣ．Ｉ．ピグメントレッド２０２の固溶体と、Ｃ．Ｉ．ピグメントバイオレット１９と、を含むことが好ましい。
このような好適な構成とすることにより、記録した際の発色性に優れ、また高彩度かつ高明度なレッド領域の色再現性及び紫領域の色再現性に優れたマゼンタインク組成物が提供される。
The magenta ink composition contains γ-type C.I. I. Pigment violet 19 and C.I. I. Pigment Red 202 solid solution, C.I. I. Pigment Violet 19 is preferably included.
By having such a suitable configuration, a magenta ink composition is provided that has excellent color developability at the time of recording, and also has high chroma and high brightness red area color reproducibility and purple area color reproducibility. .
上記マゼンタインク組成物は、γ型Ｃ．Ｉ．ピグメントバイオレット１９及びＣ．Ｉ．ピグメントレッド２０２の固溶体を、マゼンタインク組成物中１重量％以上２重量％未満と、Ｃ．Ｉ．ピグメントバイオレット１９と、を含むことが好ましい。
このような好適な構成とすることにより、記録した際の発色性に優れ、また高彩度かつ高明度なレッド領域の色再現性及び紫領域の色再現性に優れたマゼンタインク組成物が提供される。
The magenta ink composition contains γ-type C.I. I. Pigment violet 19 and C.I. I. Pigment Red 202 is a solid solution of 1% by weight or more and less than 2% by weight in the magenta ink composition; I. Pigment Violet 19 is preferably included.
By having such a suitable configuration, a magenta ink composition is provided that has excellent color developability at the time of recording, and also has high chroma and high brightness red area color reproducibility and purple area color reproducibility. .
上記マゼンタインク組成物が固溶体及びＰＶ１９を含む場合、固溶体の重量／ＰＶ１９の重量の比（前者／後者）は、９０／１０以下であることが、粒状性の点から好ましい。 When the magenta ink composition contains a solid solution and PV19, the ratio of the weight of solid solution / weight of PV19 (the former / the latter) is preferably 90/10 or less from the viewpoint of granularity.
上記マゼンタインク組成物は、Ｃ．Ｉ．ピグメントレッド２０９を含むものであってもよい。
このような好適な構成とすることにより、記録した際の発色性に優れ、また高彩度かつ高明度なレッド領域の色再現性及び紫領域の色再現性に優れたマゼンタインク組成物が提供される。
The magenta ink composition includes C.I. I. Pigment Red 209 may be included.
By having such a suitable configuration, a magenta ink composition is provided that has excellent color developability at the time of recording, and also has high chroma and high brightness red area color reproducibility and purple area color reproducibility. .
本発明に係るマゼンタインク組成物は、色材として顔料を使用するとともに、該顔料を分散するための分散剤を含有するものが好ましい。分散剤は、この種の顔料インクに使用可能であるものを特に制限なく用いることができ、例えば、カチオン性分散剤、アニオン性分散剤、ノニオン性分散剤や界面活性剤等が挙げられる。
アニオン性分散剤の例としては、ポリアクリル酸、ポリメタクリル酸、アクリル酸−アクリロニトリル共重合体、酢酸ビニル−アクリル酸エステル共重合体、アクリル酸−アクリル酸アルキルエステル共重合体、スチレン−アクリル酸共重合体、スチレン−メタクリル酸共重合体、スチレン−アクリル酸−アクリル酸アルキルエステル共重合体、スチレン−メタクリル酸−アクリル酸アルキルエステル共重合体、スチレン−α−メチルスチレン−アクリル酸共重合体、スチレン−α−メチルスチレン−アクリル酸−アクリル酸アルキルエステル共重合体、スチレン−マレイン酸共重合体、ビニルナフタレン−マレイン酸共重合体、酢酸ビニル−エチレン共重合体、酢酸ビニル−脂肪酸ビニルエチレン共重合体、酢酸ビニル−マレイン酸エステル共重合体、酢酸ビニル−クロトン酸共重合体、酢酸ビニル−アクリル酸共重合体等が挙げられる。
ノニオン性分散剤としては、ポリビニルピロリドン、ポリプロピレングリコール、ビニルピロリドン−酢酸ビニル共重合体等が挙げられる。
分散剤としての界面活性剤としては、ドデシルベンゼンスルホン酸ナトリウム、ラウリル酸ナトリウム、ポリオキシエチレンアルキルエーテルサルフェートのアンモニウム塩等のアニオン性界面活性剤、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルエステル、ポリオキシエチレンソルビタン脂肪酸エステル、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレンアルキルアミン、ポリオキシエチレンアルキルアミド等のノニオン性界面活性剤、が挙げられる。特に、顔料の分散安定性を高める観点から、スチレン−（メタ）アクリル酸共重合体を用いることが好ましい。
The magenta ink composition according to the present invention preferably uses a pigment as a coloring material and contains a dispersant for dispersing the pigment. As the dispersant, those that can be used for this kind of pigment ink can be used without particular limitation, and examples thereof include a cationic dispersant, an anionic dispersant, a nonionic dispersant, and a surfactant.
Examples of anionic dispersants include polyacrylic acid, polymethacrylic acid, acrylic acid-acrylonitrile copolymer, vinyl acetate-acrylic acid ester copolymer, acrylic acid-acrylic acid alkyl ester copolymer, styrene-acrylic acid. Copolymer, styrene-methacrylic acid copolymer, styrene-acrylic acid-alkyl acrylate copolymer, styrene-methacrylic acid-alkyl acrylate copolymer, styrene-α-methylstyrene-acrylic acid copolymer Styrene-α-methylstyrene-acrylic acid-alkyl acrylate copolymer, styrene-maleic acid copolymer, vinyl naphthalene-maleic acid copolymer, vinyl acetate-ethylene copolymer, vinyl acetate-fatty acid vinyl ethylene Copolymer, vinyl acetate-maleic ester Examples include copolymers, vinyl acetate-crotonic acid copolymers, vinyl acetate-acrylic acid copolymers, and the like.
Nonionic dispersants include polyvinyl pyrrolidone, polypropylene glycol, vinyl pyrrolidone-vinyl acetate copolymer, and the like.
Surfactants as dispersants include anionic surfactants such as sodium dodecylbenzenesulfonate, sodium laurate, ammonium salt of polyoxyethylene alkyl ether sulfate, polyoxyethylene alkyl ether, polyoxyethylene alkyl ester, polyoxyethylene alkyl ester Nonionic surfactants such as oxyethylene sorbitan fatty acid ester, polyoxyethylene alkylphenyl ether, polyoxyethylene alkylamine, polyoxyethylene alkylamide, and the like. In particular, it is preferable to use a styrene- (meth) acrylic acid copolymer from the viewpoint of enhancing the dispersion stability of the pigment.
分散剤は、マゼンタインク組成物中、固形分換算で好ましくは、０．１〜１０重量％、更に好ましくは、０．３〜６重量％含有される。 In the magenta ink composition, the dispersant is preferably contained in an amount of 0.1 to 10% by weight, more preferably 0.3 to 6% by weight in terms of solid content.
上記マゼンタインク組成物は、炭素数５〜１０の分岐を有してもよいアルカンジオールを３重量％以上１５重量％以下含むことが好ましい。
特に、水溶性の１，２−アルカンジオールを８〜１５重量％含むことが好ましい。あるいは、水溶性の両末端アルカンジオールを３〜８重量％含むことが好ましい。４−メチル−１，２−ペンタンジオール、１，２−ペンタンジオール、３，３−ジメチル−１，２−ブタンジオール、４，４−ジメチル−１，２−ペンタンジオール、５−メチル−１，２−ヘキサンジオール，１，２−ヘキサンジオール、１，２−ヘプタンジオール、１，２−オクタンジオールが好ましい。さらには、４−メチル−１，２−ペンタンジオール、１，２−ヘキサンジオールが好ましい。
The magenta ink composition preferably contains 3% by weight or more and 15% by weight or less of an alkanediol which may have a branch having 5 to 10 carbon atoms.
In particular, it is preferable to contain 8 to 15% by weight of water-soluble 1,2-alkanediol. Or it is preferable to contain 3 to 8 weight% of water-soluble both terminal alkanediol. 4-methyl-1,2-pentanediol, 1,2-pentanediol, 3,3-dimethyl-1,2-butanediol, 4,4-dimethyl-1,2-pentanediol, 5-methyl-1, 2-hexanediol, 1,2-hexanediol, 1,2-heptanediol, and 1,2-octanediol are preferred. Furthermore, 4-methyl-1,2-pentanediol and 1,2-hexanediol are preferable.
また、マゼンタインク組成物は、湿潤剤として、多価アルコール類、糖類、エチレンオキサイド鎖を有する多価アルコール類を１種又は２種以上含むことが好ましい。
湿潤剤を加えることによって、インクジェット記録用に用いた場合に、インクの乾燥を防いでインクジェットプリンタのヘッドでの目詰まりが抑制される。
湿潤剤としては、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、プロピレングリコール、ブチレングリコール、１，２，６−ヘキサントリオール、チオグリコール、ヘキシレングリコール、グリセリン、トリメチロールエタン、トリメチロールプロパン等の多価アルコール類；糖アルコール等の糖類；エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコールモノメチルエーテル、トリエチレングリコールモノエチルエーテル、トリエチレングリコールモノブチルエーテル等のエチレンオキサイド鎖を有する多価アルコール類；等が挙げられ、これらの１種又は２種以上が用いられる。
Further, the magenta ink composition preferably contains one or more polyhydric alcohols having a polyhydric alcohol, a saccharide, and an ethylene oxide chain as a wetting agent.
By adding a wetting agent, when used for inkjet recording, the ink is prevented from drying and clogging at the head of the inkjet printer is suppressed.
Examples of the wetting agent include ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, polypropylene glycol, propylene glycol, butylene glycol, 1,2,6-hexanetriol, thioglycol, hexylene glycol, glycerin, trimethylolethane, Polyhydric alcohols such as trimethylolpropane; sugars such as sugar alcohol; ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, triethylene glycol monomethyl ether, triethylene glycol mono Ethyl ether, triethylene glycol monobutyl ether Polyhydric alcohols having an ethylene oxide chain such as ether, and the like, these one or more is used.
湿潤剤は、各インク中、固形分換算で好ましくは３〜１６重量％含有されることが好ましい。 The wetting agent is preferably contained in each ink in an amount of 3 to 16% by weight in terms of solid content.
また、上記マゼンタインク組成物は、浸透剤として、ラクトン類、ラクラム類（ピロリドン類）、アルカンジオール類、グリコールエーテル類を１種又は２種以上含むことが好ましい。浸透剤を加えることによって、記録媒体への濡れ性を高めてインクの浸透性を高めることができる。
浸透剤としては、例えば、２−ピロリドン、Ｎ−メチル−２−ピロリドン等のピロリドン類；１，２−ペンタンジオール、１，２−ヘキサンジオール等のアルカンジオール等；エチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコールモノブチルエーテル、プロピレングリコールモノブチルエーテル、ジプロピレングリコールモノブチルエーテル等のグリコールエーテル類；が挙げられ、これらの１種又は２種以上含むことが好ましい。
The magenta ink composition preferably contains one or more lactones, lactams (pyrrolidones), alkanediols, and glycol ethers as penetrants. By adding a penetrating agent, it is possible to increase the wettability of the recording medium and increase the penetrability of the ink.
Examples of penetrants include pyrrolidones such as 2-pyrrolidone and N-methyl-2-pyrrolidone; alkane diols such as 1,2-pentanediol and 1,2-hexanediol; ethylene glycol monomethyl ether and diethylene glycol monoethyl And glycol ethers such as ether, diethylene glycol monobutyl ether, triethylene glycol monobutyl ether, propylene glycol monobutyl ether, dipropylene glycol monobutyl ether, and the like, and preferably one or more of these are included.
浸透剤は、各インク中、固形分換算で好ましくは８〜１５重量％含有される。 The penetrant is preferably contained in each ink in an amount of 8 to 15% by weight in terms of solid content.
また、上記マゼンタインク組成物は、界面活性剤として、アセチレングリコール類、ポリシロキサン類を１種又は２種以上含むことが好ましい。界面活性剤を加えることによって、記録媒体への濡れ性を高めてインクの浸透性を高めることができる。 The magenta ink composition preferably contains one or more acetylene glycols and polysiloxanes as a surfactant. By adding a surfactant, it is possible to increase the wettability of the recording medium and increase the permeability of the ink.
上記マゼンタインク組成物は、界面活性剤として、ポリオルガノシロキサンを含むことが好ましい。 The magenta ink composition preferably contains polyorganosiloxane as a surfactant.
上記マゼンタインク組成物がポリオルガノシロキサンを含む場合、一種のポリオルガノシロキサンを含んでもよいし、又は二種以上のポリオルガノシロキサンを含んでもよい。 When the magenta ink composition contains a polyorganosiloxane, it may contain one type of polyorganosiloxane or two or more types of polyorganosiloxane.
上記マゼンタインク組成物は、界面活性剤として、下記一般式で表されるポリオルガノシロキサンを含むことが好ましい。
このような好適な構成とすることにより、光沢感が一層向上した記録物を得ることができる。
The magenta ink composition preferably contains a polyorganosiloxane represented by the following general formula as a surfactant.
With such a suitable configuration, a recorded matter with further improved gloss can be obtained.
又は、上記マゼンタインク組成物は、界面活性剤として、上記一般式で表されるポリオルガノシロキサンに加えて、さらに、下記一般式で表されるポリオルガノシロキサンを含むことが好ましい。
このような好適な構成とすることにより、印刷本紙に記録した際の凝集むらを抑制することができる。
Alternatively, the magenta ink composition preferably contains a polyorganosiloxane represented by the following general formula in addition to the polyorganosiloxane represented by the general formula as a surfactant.
By adopting such a suitable configuration, it is possible to suppress the uneven aggregation when recording on the printing paper.
また、上記マゼンタインク組成物は、インクの乾燥時間を短縮する観点から、低沸点有機溶媒を含んでもよい。該低沸点有機溶媒としては、例えば、メタノール、エタノール、ｎ−プロピルアルコール、ｉｓｏ−プロプルアルコール、ｎ−ブタノール、ｓｅｃ−ブタノール、ｔｅｒｔ−ブタノール、ｉｓｏ−ブタノール、ｎ−ペンタノール等が挙げられ、これらの１種又は２種以上が用いられる。特に、一価アルコールが好ましい。 The magenta ink composition may contain a low-boiling organic solvent from the viewpoint of shortening the drying time of the ink. Examples of the low boiling point organic solvent include methanol, ethanol, n-propyl alcohol, iso-propyl alcohol, n-butanol, sec-butanol, tert-butanol, iso-butanol, n-pentanol and the like. These 1 type (s) or 2 or more types are used. In particular, monohydric alcohol is preferable.
上記マゼンタインク組成物は、前述した顔料、分散剤、湿潤剤、低沸点有機溶媒、浸透剤、界面活性剤等の成分を含有し、バランスとして水を含有することが好ましい。水は、イオン交換水、限外濾過水、逆浸透水、蒸留水等の純水又は超純水を用いることが好ましい。特に、これらの水を、紫外線照射又は過酸化水素添加等により滅菌処理した水は、長期間に亘ってカビやバクテリアの発生が防止されるので好ましい。 The magenta ink composition preferably contains components such as the pigment, dispersant, wetting agent, low-boiling organic solvent, penetrant, and surfactant described above, and preferably contains water as a balance. It is preferable to use pure water or ultrapure water such as ion exchange water, ultrafiltration water, reverse osmosis water, or distilled water. In particular, water obtained by sterilizing these waters by ultraviolet irradiation or addition of hydrogen peroxide is preferable because generation of mold and bacteria is prevented over a long period of time.
上記マゼンタインク組成物には、更に必要に応じて、水溶性ロジン類等の定着剤、安息香酸ナトリウム等の防黴剤・防腐剤、アロハネート類等の酸化防止剤・紫外線吸収剤、キレート剤、酸素吸収剤、ｐＨ調整剤等の添加剤を含有させることができ、これらの１種又は２種以上が用いられる。 If necessary, the magenta ink composition further includes a fixing agent such as a water-soluble rosin, an antifungal agent / preservative such as sodium benzoate, an antioxidant / ultraviolet absorber such as an allophanate, a chelating agent, Additives such as oxygen absorbers and pH adjusters can be contained, and one or more of these are used.
ｐＨ調整剤としては、水酸化カリウム、水酸化ナトリウム、トリエタノールアミン、トリプロパノールアミン等を挙げることができる。ｐＨ調整剤の添加量は目的とするｐＨに応じて決定される。 Examples of the pH adjuster include potassium hydroxide, sodium hydroxide, triethanolamine, tripropanolamine and the like. The amount of pH adjuster added is determined according to the target pH.
上記マゼンタインク組成物は、その用途に特に制限はないが、ノズルからインクの液滴を吐出させ、該液滴を記録媒体に付着させて文字や図形等の画像を形成する記録方法であるインクジェット記録方法に用いられることが好ましく、特にオンデマンド型のインクジェット記録方法に用いられることが好ましい。オンデマンド型のインクジェット記録方法としては、例えば、プリンターヘッドに配設された圧電素子を用いて記録を行う圧電素子記録方法、プリンターヘッドに配設された発熱抵抗素子のヒーター等による熱エネルギーを用いて記録を行う熱ジェット記録方法等が挙げられ、何れのインクジェット記録方法にも好適に使用できる。 The magenta ink composition is not particularly limited in its application, but is an inkjet which is a recording method in which ink droplets are ejected from nozzles and adhered to a recording medium to form images such as characters and figures. It is preferably used in a recording method, and particularly preferably used in an on-demand ink jet recording method. As an on-demand type ink jet recording method, for example, a piezoelectric element recording method that performs recording using a piezoelectric element disposed in a printer head, or a thermal energy generated by a heater of a heating resistance element disposed in the printer head is used. And a thermal jet recording method for recording, and can be suitably used for any ink jet recording method.
本発明のマゼンタインク組成物は、インクジェット式記録に用いられる、インクジェット記録用マゼンタインク組成物であってもよい。 The magenta ink composition of the present invention may be a magenta ink composition for inkjet recording used for inkjet recording.
〔インクカートリッジ〕
本発明のインクカートリッジは、上記のマゼンタインク組成物を含むものである。
本発明に係るインクカートリッジによれば、記録した際の発色性、粒状性、及び光沢性に優れ、インクジェット式記録ヘッドでの目詰まりを起こしにくく、さらに高彩度かつ高明度なレッド領域の色再現性に優れた画像を得ることができる。
〔ink cartridge〕
The ink cartridge of the present invention contains the magenta ink composition described above.
According to the ink cartridge of the present invention, the color reproducibility, graininess, and glossiness during recording are excellent, the ink recording head is less likely to be clogged, and the color reproducibility of the red region with high chroma and lightness is high. An excellent image can be obtained.
〔記録システム〕
本発明の記録システムは、上記のマゼンタインク組成物を用いて画像を形成するものである。
本発明に係る記録システムによれば、記録した際の発色性、粒状性、及び光沢性に優れ、インクジェット式記録ヘッドでの目詰まりを起こしにくく、さらに高彩度かつ高明度なレッド領域の色再現性に優れた画像を得ることができる。
[Recording system]
The recording system of the present invention forms an image using the magenta ink composition described above.
According to the recording system of the present invention, the color reproducibility, graininess, and glossiness during recording are excellent, the ink recording head is less likely to be clogged, and the color reproducibility of the high-saturation and high-brightness red region. An excellent image can be obtained.
〔記録物〕
本発明の記録物は、上記のマゼンタインク組成物を用いて画像が形成されてなる。
本発明に係るマゼンタインク組成物は、画像を形成するための記録媒体として、インクジェット記録方法等において通常用いられる記録媒体に制限なく適用できるが、塗工層を有するメディアや普通紙（被記録面に繊維が露呈している記録媒体）等に好適に適用される。
[Recorded material]
The recorded material of the present invention is formed by forming an image using the magenta ink composition described above.
The magenta ink composition according to the present invention can be applied as a recording medium for forming an image without limitation to a recording medium usually used in an ink jet recording method or the like. The recording medium in which the fibers are exposed to the like) is suitably applied.
以下、本発明を実施例によりさらに詳細に説明するが、本発明はこれらの実施例に限定されるものではない。当業者は、以下に示す実施例のみならず様々な変更を加えて実施することが可能であり、かかる変更も本特許請求の範囲に包含される。 EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, this invention is not limited to these Examples. Those skilled in the art can implement various modifications as well as the following embodiments, and such modifications are also included in the scope of the claims.
〔実施例Ａ〕
マゼンタインクとして、γ型ＰＶ１９とＰＲ２０２との固溶体（以下、固溶体という。また122AIと表記する場合がある。）であって、図１に示すＸ線回折スペクトルを示す固
溶体を２重量％含むマゼンタインク組成物Ｍ１を以下の配合により調製した。
＜Ｍ１；実施例１＞
固溶体 ２．０重量％
スチレンアクリル酸共重合樹脂 ２．８重量％
グリセリン １２．０重量％
１，２−ヘキサンジオール ７．０重量％
トリエタノールアミン ０．９重量％
ＫＦ−３５３Ａ（信越化学工業株式会社製） ０．１重量％
純水 残量
計 １００．０重量％
[Example A]
As a magenta ink, a magenta ink that is a solid solution of γ-type PV19 and PR202 (hereinafter referred to as a solid solution, and sometimes referred to as 122AI), and contains 2% by weight of a solid solution that exhibits the X-ray diffraction spectrum shown in FIG. Composition M1 was prepared according to the following formulation.
<M1; Example 1>
Solid solution 2.0% by weight
Styrene acrylic acid copolymer resin 2.8% by weight
Glycerin 12.0% by weight
1,2-hexanediol 7.0% by weight
Triethanolamine 0.9% by weight
KF-353A (manufactured by Shin-Etsu Chemical Co., Ltd.) 0.1% by weight
Pure water remaining
Total 100.0% by weight
＜Ｍ２；実施例２＞
Ｍ１の固溶体２．０重量％に代えて、ＰＶ１９を０．３３重量％及び固溶体を１．６７重量％（ＰＶ１９／固溶体＝１／５（重量比））マゼンタインクとして用いた以外は、Ｍ１と同様の配合によりマゼンタインク組成物Ｍ２を調製した。
<M2; Example 2>
M1 and M1 were used except that instead of M1 solid solution 2.0% by weight, PV19 0.33% by weight and solid solution 1.67% by weight (PV19 / solid solution = 1/5 (weight ratio)). A magenta ink composition M2 was prepared by the same formulation.
＜Ｍ３；実施例３＞
Ｍ１の固溶体２．０重量％に代えて、ＰＶ１９を０．４重量％及び固溶体を１．６重量％（ＰＶ１９／固溶体＝１／４（重量比））マゼンタインクとして用いた以外は、Ｍ１と同様の配合によりマゼンタインク組成物Ｍ３を調製した。
<M3; Example 3>
M1 and M1 except that M1 was used as a magenta ink in place of 2.0% by weight of solid solution of M1, and 0.4% by weight of PV19 and 1.6% by weight of solid solution (PV19 / solid solution = 1/4 (weight ratio)). A magenta ink composition M3 was prepared by the same formulation.
＜Ｍ４；実施例４＞
Ｍ１の固溶体２．０重量％に代えて、ＰＶ１９を０．５重量％及び固溶体を１．５重量％（ＰＶ１９／固溶体＝１／３（重量比））マゼンタインクとして用いた以外は、Ｍ１と同様の配合によりマゼンタインク組成物Ｍ４を調製した。
<M4; Example 4>
M1 and M1 except that M1 was used as a magenta ink in place of 2.0% by weight of M1 solid solution and 0.5% by weight of PV19 and 1.5% by weight of solid solution (PV19 / solid solution = 1/3 (weight ratio)). A magenta ink composition M4 was prepared by the same formulation.
＜Ｍ５；実施例５＞
Ｍ１の固溶体２．０重量％に代えて、ＰＶ１９を１．０重量％及び固溶体を１．０重量％（ＰＶ１９／固溶体＝１／１（重量比））マゼンタインクとして用いた以外は、Ｍ１と同様の配合によりマゼンタインク組成物Ｍ５を調製した。
<M5; Example 5>
M1 is the same as M1 except that 1.0% by weight of PV19 and 1.0% by weight of solid solution (PV19 / solid solution = 1/1 (weight ratio)) magenta ink were used instead of 2.0% by weight of the solid solution of M1. A magenta ink composition M5 was prepared by the same formulation.
＜Ｍ６；実施例６＞
Ｍ１の固溶体２．０重量％に代えて、ＰＶ１９を１．５重量％及び固溶体を０．５重量％（ＰＶ１９／固溶体＝３／１（重量比））マゼンタインクとして用いた以外は、Ｍ１と同様の配合によりマゼンタインク組成物Ｍ６を調製した。
<M6; Example 6>
M1 and M1 except that M1 was used as a magenta ink in place of 2.0% by weight of M1 solid solution and 1.5% by weight of PV19 and 0.5% by weight of solid solution (PV19 / solid solution = 3/1 (weight ratio)). A magenta ink composition M6 was prepared by the same formulation.
＜Ｍ７；実施例７＞
Ｍ１の固溶体２．０重量％に代えて、ＰＶ１９を２．０重量％マゼンタインクとして用いた以外は、Ｍ１と同様の配合によりマゼンタインク組成物Ｍ７を調製した。
<M7; Example 7>
A magenta ink composition M7 was prepared by the same composition as M1, except that PV19 was used as a 2.0 wt% magenta ink instead of 2.0 wt% of the solid solution of M1.
上記のようにして調製した各インク組成物Ｍ１〜Ｍ７を、インクジェットプリンタ（商品名「Ａ５５０」、セイコーエプソン（株）製）のインクカートリッジに装着し、記録媒体ＰＧＰＰ（セイコーエプソン（株）製)に、１４４０×１４４０ｄｐｉの解像度で、写真用紙・フォト・色補正なしモードにて記録を行い、各記録物について、SPM-50（グレタグマクベス社製）でD50光源，視野角2度，フィルターなしで，CIEで規定するL＊値，a＊値，ｂ＊値を測定し、測定波長範囲４００〜８００nmにおける反射スペクトルを測定した。
記録は、Ｄｕｔｙを０〜１００％の間で１０％ごとに変化させて行い、各波長における平均値を求め、さらに標準化して吸収値を求めた。「ｄｕｔｙ」は、Ｄｕｔｙ＝（実印字ドット数）／（縦解像度×横解像度）×１００（％）で定義される。
Each ink composition M1 to M7 prepared as described above is mounted on an ink cartridge of an ink jet printer (trade name “A550”, manufactured by Seiko Epson Corporation), and a recording medium PGPP (manufactured by Seiko Epson Corporation). In addition, recording is performed in a photo paper / photo / color correction-free mode at a resolution of 1440 × 1440 dpi. For each recorded matter, a D50 light source with a viewing angle of 2 degrees and no filter is used with an SPM-50 (made by Gretag Macbeth). The L * value, a * value, and b * value specified by CIE were measured, and the reflection spectrum in the measurement wavelength range of 400 to 800 nm was measured.
Recording was performed by changing the Duty from 0 to 100% every 10%, obtaining an average value at each wavelength, and further standardizing to obtain an absorption value. “Duty” is defined by Duty = (actual print dot count) / (vertical resolution × horizontal resolution) × 100 (%).
実施例１〜７について、波長５１０〜５７０ｎｍにおける吸収値を表１に示す。 Table 1 shows the absorption values at wavelengths of 510 to 570 nm for Examples 1 to 7.
図２は、実施例１〜７の測定結果をグラフ化したものである。図２に示すように、いずれのマゼンタインク組成物も、波長５１０ｎｍ〜５３５ｎｍに１つの吸収ピーク（Ａ）と、波長５６０ｎｍ付近に１つの吸収ピーク（Ｂ）と、を有しており、かつ、波長５６０ｎｍにおける吸収値を１とした場合に、波長５１０ｎｍ〜５３５ｎｍにおける各吸収ピークの吸収値は０．９＜Ａ／Ｂ＜１．０であった。 FIG. 2 is a graph of the measurement results of Examples 1-7. As shown in FIG. 2, each magenta ink composition has one absorption peak (A) at a wavelength of 510 nm to 535 nm, and one absorption peak (B) near a wavelength of 560 nm, and When the absorption value at a wavelength of 560 nm was 1, the absorption value of each absorption peak at a wavelength of 510 nm to 535 nm was 0.9 <A / B <1.0.
〔実施例Ｂ〕
マゼンタインクとして、γ型ＰＶ１９とＰＲ２０２との固溶体（以下、固溶体という）であって、図１に示すＸ線回折スペクトルを示す固溶体を０．９重量％、ＰＶ１９を０．
１重量％含むマゼンタインク組成物Ｍ８を以下の配合により調製した。
＜Ｍ８；実施例８＞
固溶体 ０．９重量％
ＰＶ１９ ０．１重量％
スチレンアクリル酸共重合樹脂 ２．８重量％
グリセリン １２．０重量％
１，２−ヘキサンジオール ７．０重量％
トリエタノールアミン ０．９重量％
ＫＦ−３５３Ａ（信越化学工業株式会社製） ０．１重量％
純水 残量
計 １００．０重量％
[Example B]
As a magenta ink, a solid solution of γ-type PV19 and PR202 (hereinafter referred to as a solid solution), 0.9% by weight of the solid solution showing the X-ray diffraction spectrum shown in FIG.
A magenta ink composition M8 containing 1% by weight was prepared by the following formulation.
<M8; Example 8>
Solid solution 0.9% by weight
PV19 0.1% by weight
Styrene acrylic acid copolymer resin 2.8% by weight
Glycerin 12.0% by weight
1,2-hexanediol 7.0% by weight
Triethanolamine 0.9% by weight
KF-353A (manufactured by Shin-Etsu Chemical Co., Ltd.) 0.1% by weight
Pure water remaining
Total 100.0% by weight
＜Ｍ９；実施例９＞
ＰＶ１９を０．１２５重量％及び固溶体を０．８７５重量％（ＰＶ１９／固溶体＝１／７（重量比））マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ９を調製した。
<M9; Example 9>
A magenta ink composition M9 was prepared by the same composition as M8 except that 0.125% by weight of PV19 and 0.875% by weight of the solid solution (PV19 / solid solution = 1/7 (weight ratio)) were used as the magenta ink. .
＜Ｍ１０；実施例１０＞
ＰＶ１９を０．１６７重量％及び固溶体を０．８３３重量％（ＰＶ１９／固溶体＝１／５（重量比））マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１０を調製した。
<M10; Example 10>
A magenta ink composition M10 was prepared by the same composition as M8 except that 0.167% by weight of PV19 and 0.833% by weight of solid solution (PV19 / solid solution = 1/5 (weight ratio)) were used as magenta ink. .
＜Ｍ１１；実施例１１＞
ＰＶ１９を０．２重量％及び固溶体を０．８重量％（ＰＶ１９／固溶体＝１／４（重量比））マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１１を調製した。
<M11; Example 11>
A magenta ink composition M11 was prepared by the same composition as M8 except that 0.2% by weight of PV19 and 0.8% by weight of solid solution (PV19 / solid solution = 1/4 (weight ratio)) were used as magenta ink. .
＜Ｍ１２；実施例１２＞
ＰＶ１９を０．２５重量％及び固溶体を０．７５重量％（ＰＶ１９／固溶体＝１／３（重量比））マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１２を調製した。
<M12; Example 12>
A magenta ink composition M12 was prepared by the same composition as M8 except that 0.25 wt% of PV19 and 0.75 wt% of solid solution (PV19 / solid solution = 1/3 (weight ratio)) were used as magenta ink. .
＜Ｍ１３；実施例１３＞
ＰＶ１９を０．３３重量％及び固溶体を０．６７重量％（ＰＶ１９／固溶体＝１／２（重量比））マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１３を調製した。
<M13; Example 13>
A magenta ink composition M13 was prepared by the same composition as M8 except that 0.33 wt% of PV19 and 0.67 wt% of solid solution (PV19 / solid solution = 1/2 (weight ratio)) were used as magenta ink. .
＜Ｍ１４；実施例１４＞
ＰＶ１９を０．５重量％及び固溶体を０．５重量％（ＰＶ１９／固溶体＝１／１（重量比））マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１４を調製した。
<M14; Example 14>
A magenta ink composition M14 was prepared by the same composition as M8 except that 0.5% by weight of PV19 and 0.5% by weight of solid solution (PV19 / solid solution = 1/1 (weight ratio)) were used as magenta ink. .
＜Ｍ１５；実施例１５＞
固溶体を１．０重量％、マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１５を調製した。
<M15; Example 15>
A magenta ink composition M15 was prepared by the same composition as M8 except that 1.0% by weight of the solid solution was used as a magenta ink.
上記のようにして調製した各インク組成物Ｍ８〜Ｍ１５を、インクジェットプリンタ（商品名「Ａ５５０」、セイコーエプソン（株）製）のインクカートリッジに装着し、記録媒体ＰＧＰＰ（セイコーエプソン（株）製)に、１４４０×１４４０ｄｐｉの解像度で、写真用紙・フォト・色補正なしモードにて記録を行い、各記録物について、可視域（４００〜８００ｎｍ）における吸収値を上記同様にして求めた。 Each ink composition M8 to M15 prepared as described above is mounted on an ink cartridge of an inkjet printer (trade name “A550”, manufactured by Seiko Epson Corporation), and a recording medium PGPP (manufactured by Seiko Epson Corporation). In addition, recording was performed at a resolution of 1440 × 1440 dpi in a photographic paper / photo / no color correction mode, and the absorption value in the visible region (400 to 800 nm) was determined in the same manner as described above.
実施例８〜１５について、波長５１０〜５７０ｎｍにおける吸収値を表２に示す。 Table 2 shows the absorption values at wavelengths of 510 to 570 nm for Examples 8 to 15.
図３は、実施例８〜１５の測定結果をグラフ化したものである。図３に示すように、いずれのマゼンタインク組成物も、波長５１０ｎｍ〜５３５ｎｍに１つの吸収ピーク（Ａ）と、波長５６０ｎｍ付近に１つの吸収ピーク（Ｂ）と、を有しており、かつ、波長５６０ｎｍ付近におけるピーク値を１とした場合に、波長５１０ｎｍ〜５３５ｎｍにおける各吸収ピークの吸収値は０．９＜Ａ／Ｂ＜１．０であった。 FIG. 3 is a graph of the measurement results of Examples 8-15. As shown in FIG. 3, each magenta ink composition has one absorption peak (A) at a wavelength of 510 nm to 535 nm and one absorption peak (B) near a wavelength of 560 nm, and When the peak value in the vicinity of the wavelength of 560 nm was 1, the absorption value of each absorption peak at the wavelength of 510 nm to 535 nm was 0.9 <A / B <1.0.
〔実施例Ｃ〕
マゼンタインクとして、γ型ＰＶ１９とＰＲ２０２との固溶体（以下、固溶体という）であって、図１に示すＸ線回折スペクトルを示す固溶体を含むマゼンタインク組成物Ｍ１
６〜Ｍ１９を以下の配合により調製した。
[Example C]
As a magenta ink, a magenta ink composition M1 containing a solid solution of γ-type PV19 and PR202 (hereinafter referred to as a solid solution) and showing the X-ray diffraction spectrum shown in FIG.
6-M19 was prepared with the following formulation.
＜Ｍ１６；実施例１６＞
固溶体を３．０重量％、マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１６を調製した。
<M16; Example 16>
A magenta ink composition M16 was prepared by the same composition as M8 except that 3.0% by weight of the solid solution was used as a magenta ink.
＜Ｍ１７；実施例１７＞
固溶体を４．０重量％、マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１７を調製した。
<M17; Example 17>
A magenta ink composition M17 was prepared by the same formulation as M8, except that 4.0% by weight of the solid solution was used as a magenta ink.
＜Ｍ１８；実施例１８＞
固溶体を５．０重量％、マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１８を調製した。
<M18; Example 18>
A magenta ink composition M18 was prepared by the same composition as M8 except that 5.0% by weight of the solid solution was used as a magenta ink.
＜Ｍ１９；実施例１９＞
固溶体を６．０重量％、マゼンタインクとして用いた以外は、Ｍ８と同様の配合によりマゼンタインク組成物Ｍ１９を調製した。
<M19; Example 19>
A magenta ink composition M19 was prepared by the same formulation as M8 except that 6.0% by weight of the solid solution was used as a magenta ink.
上記のようにして調製した各インク組成物Ｍ１６〜Ｍ１９を、インクジェットプリンタ（商品名「Ａ５５０」、セイコーエプソン（株）製）のインクカートリッジに装着し、記録媒体ＰＧＰＰ（セイコーエプソン（株）製)に、１４４０×１４４０ｄｐｉの解像度で、写真用紙・フォト・色補正なしモードにて記録を行い、各記録物について、可視域（４００〜８００ｎｍ）における吸収値を上記同様にして求めた。 Each ink composition M16 to M19 prepared as described above is mounted on an ink cartridge of an ink jet printer (trade name “A550”, manufactured by Seiko Epson Corporation), and a recording medium PGPP (manufactured by Seiko Epson Corporation). In addition, recording was performed at a resolution of 1440 × 1440 dpi in a photographic paper / photo / no color correction mode, and the absorption value in the visible region (400 to 800 nm) was determined in the same manner as described above.
実施例１、１５〜１９について、波長５１０〜５７０ｎｍにおける吸収値を表３に示す。 Table 3 shows the absorption values at wavelengths of 510 to 570 nm for Examples 1 and 15 to 19.
図４は、実施例１、１５〜１９の測定結果をグラフ化したものである。図４に示すように、いずれのマゼンタインク組成物も、波長５１０ｎｍ〜５３５ｎｍに１つの吸収ピーク（Ａ）と、波長５６０ｎｍ付近に１つの吸収ピーク（Ｂ）と、を有しており、かつ、波長５６０ｎｍ付近におけるピーク値を１とした場合に、波長５１０ｎｍ〜５３５ｎｍにおける各吸収ピークの吸収値は０．９＜Ａ／Ｂ＜１．０であった。 FIG. 4 is a graph showing the measurement results of Examples 1 and 15-19. As shown in FIG. 4, each magenta ink composition has one absorption peak (A) at a wavelength of 510 nm to 535 nm and one absorption peak (B) near a wavelength of 560 nm, and When the peak value in the vicinity of the wavelength of 560 nm was 1, the absorption value of each absorption peak at the wavelength of 510 nm to 535 nm was 0.9 <A / B <1.0.
Claims (14)
前記吸収ピーク（Ａ）のピーク値の、前記吸収ピーク（Ｂ）のピーク値に対する相対値（Ａ／Ｂ）が、０．９＜Ａ／Ｂ＜１．０である、マゼンタインク組成物。 The absorption spectrum in the visible region (400 to 800 nm) has at least one absorption peak (A) at wavelengths of 510 nm to 535 nm and one absorption peak (B) at wavelengths of 550 to 570 nm,
The magenta ink composition, wherein a relative value (A / B) of the peak value of the absorption peak (A) to the peak value of the absorption peak (B) is 0.9 <A / B <1.0.