JP2007277297A - Yellow ink composition - Google Patents
Yellow ink composition Download PDFInfo
- Publication number
- JP2007277297A JP2007277297A JP2006102076A JP2006102076A JP2007277297A JP 2007277297 A JP2007277297 A JP 2007277297A JP 2006102076 A JP2006102076 A JP 2006102076A JP 2006102076 A JP2006102076 A JP 2006102076A JP 2007277297 A JP2007277297 A JP 2007277297A
- Authority
- JP
- Japan
- Prior art keywords
- yellow
- ink composition
- yellow ink
- weight
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、高明度（高Ｌ*）領域のみならず低明度のイエロー領域、即ち低Ｌ*且つａ*がゼロ近傍且つ高ｂ*における色再現性にも優れるとともに、記録画像が大気中のオゾンガス等に暴露された際の耐性（耐ガス性）に優れるイエローインク組成物に関する。 The present invention has excellent color reproducibility not only in a high lightness (high L *) region but also in a low lightness yellow region, that is, low L * and a * near zero and high b *, and the recorded image is in the atmosphere. The present invention relates to a yellow ink composition having excellent resistance (gas resistance) when exposed to ozone gas or the like.
従来、カラーインクジェット記録用のインクセットに備えられているイエローインクは、画像をドットにより表現した際に、ドットが肉眼で粒状に視認できるような状態を防ぐため、比較的明度の高いものが用いられている。高明度なイエローインクは、例えば、ＣＩＥ（Commission Internationale d'Eclairage；国際照明委員会）が規定するＬａｂ表色系によれば、「高Ｌ*且つａ*がゼロ近傍且つ高ｂ*」となる。 Conventionally, the yellow ink provided in the ink set for color ink jet recording has a relatively high brightness in order to prevent a state in which dots can be visually recognized by the naked eye when the image is expressed by dots. It has been. For example, according to the Lab color system defined by the CIE (Commission Internationale d'Eclairage), the high brightness yellow ink is “high L * and a * is near zero and high b *”. .
「高Ｌ*且つａ*がゼロ近傍且つ高ｂ*」なイエローインクを用いると、粒状性が改善される反面、Ｌ*値（明度）が約６０以下の中明度〜低明度の領域において、ｂ*値の高い色の再現性が不十分になるという問題がある。 When yellow ink with “high L * and a * is near zero and high b *” is used, the graininess is improved, but the L * value (brightness) is about 60 or less in the middle lightness to low lightness region. There is a problem that the reproducibility of a color having a high b * value is insufficient.
このような問題を解決するために、高明度のイエローインクとは別に、ダークイエローと呼ばれる低明度のイエローインクをさらに備えるインクセットを用いる方法が提案されている（例えば、特許文献１を参照）。 In order to solve such a problem, a method of using an ink set that further includes a low-lightness yellow ink called dark yellow in addition to a high-lightness yellow ink has been proposed (see, for example, Patent Document 1). .
また、イエローインクに含まれる顔料固形分を増加させることによって、中〜低明度における高ｂ*値を実現する方法も用いられている（例えば、特許文献２を参照）。 In addition, a method of achieving a high b * value at medium to low brightness by increasing the pigment solid content contained in the yellow ink is also used (see, for example, Patent Document 2).
一方、Ｃ．Ｉ．ピグメントイエロー１２８とＣ．Ｉ．ピグメントイエロー１１０の２種のイエロー顔料を含んでなるイエローインク組成物によって、イエロー領域における広範囲な色再現性を得る方法も開示されている（例えば、特許文献３を参照）。 On the other hand, C.I. I. Pigment yellow 128 and C.I. I. A method of obtaining a wide range of color reproducibility in the yellow region by using a yellow ink composition comprising two types of yellow pigments of CI Pigment Yellow 110 is also disclosed (see, for example, Patent Document 3).
さらに、本出願人によって、ＣＩＥで規定のＸＹＺ表示系におけるＺ値が２３のとき、Ｙ値が８６以上であるイエローインク組成物が提供されている（特許文献４）。このイエローインク組成物は、低明度の黄色を再現性よく表現することができるものである。
しかし、ダークイエローを使用する方法では、インクの色数が増えるために色作りが複雑化し、コストも高くなる傾向があり、顔料固形分を増加させる方法では、光沢の劣化を引き起こす場合がある。 However, in the method using dark yellow, the number of ink colors increases, so that color creation becomes complicated and the cost tends to increase. In the method in which the pigment solid content is increased, the gloss may be deteriorated.
Ｃ．Ｉ．ピグメントイエロー１２８とＣ．Ｉ．ピグメントイエロー１１０をブレンドする方法では、１種類の顔料を含むインクよりは広範囲な色再現性を得ることができるが、イエロー領域における暗部の色再現性は十分でない。また、色相角が離れた顔料種の混合なので、２次色の彩度が低くなる傾向があり、特にＣ．Ｉ．ピグメントイエロー１１０が赤味を帯びているため、インクセットに用いると緑色が低彩度となる。 C. I. Pigment yellow 128 and C.I. I. In the method of blending CI Pigment Yellow 110, it is possible to obtain a wider range of color reproducibility than ink containing one type of pigment, but the color reproducibility of the dark part in the yellow region is not sufficient. In addition, since the mixture of pigment types having different hue angles, the saturation of the secondary color tends to be lowered. I. Since Pigment Yellow 110 is reddish, green has low saturation when used in an ink set.
特許文献４に開示のイエローインク組成物では、中明度〜低明度の領域において、ｂ*値の高い色の再現性がある程度達成できる。しかし、イエローインク組成物による記録画像は大気中のオゾンガス等に暴露されることが多く、この際の記録画像の耐性（耐ガス性）ついては、未だ満足した効果が得られていないのが現状である。 With the yellow ink composition disclosed in Patent Document 4, color reproducibility with a high b * value can be achieved to some extent in the medium lightness to low lightness range. However, the recorded image of the yellow ink composition is often exposed to ozone gas in the atmosphere, and the satisfactory effect (gas resistance) of the recorded image at this time has not yet been obtained. is there.
そこで、本発明は、高明度（高Ｌ*）領域のみならず低明度のイエロー領域、即ち「低Ｌ*且つａ*がゼロ近傍且つ高ｂ*」における色再現性にも優れるとともに、耐ガス性に優れるイエローインク組成物を提供することを目的とする。 Therefore, the present invention has excellent color reproducibility not only in a high lightness (high L *) region but also in a low lightness yellow region, that is, “low L * and a * is close to zero and high b *”, and is gas resistant. An object of the present invention is to provide a yellow ink composition having excellent properties.
本発明者は、下記発明１を提供することにより、前記目的を達成したものである。
１．色材としての顔料として、Ｃ．Ｉ．ピグメントイエロー１２９及びＣ．Ｉ．ピグメントイエロー７４を含有し、それらの重量比（前者／後者）が１／６〜３／７である、イエローインク組成物。
The present inventor achieves the object by providing the following invention 1.
1. As a pigment as a coloring material, C.I. I. Pigment yellow 129 and C.I. I. A yellow ink composition containing Pigment Yellow 74 and having a weight ratio (the former / the latter) of 1/6 to 3/7.
また、本発明は、以下の発明をそれぞれ提供する。
２．ＣＩＥで規定のＸＹＺ表示系におけるＺ値が２３のとき、Ｙ値が８９．１〜９５である、前記１記載のイエローインク組成物。
The present invention also provides the following inventions.
2. The yellow ink composition as described in 1 above, wherein the Y value is 89.1 to 95 when the Z value in an XYZ display system defined by CIE is 23.
３．前記Ｃ．Ｉ．ピグメントイエロー１２９が、組成物中の全顔料固形分の、少なくとも１０重量％含まれる、前記１又は２記載のイエローインク組成物。 3. C. above. I. 3. The yellow ink composition according to 1 or 2 above, wherein the pigment yellow 129 is contained at least 10% by weight of the total pigment solid content in the composition.
４．色材としての顔料と共に、該顔料を分散させるための分散剤を、該顔料に対して１０〜１４０重量％含む、前記１〜３の何れかに記載のイエローインク組成物。 4). 4. The yellow ink composition as described in any one of 1 to 3 above, containing a pigment as a color material and a dispersant for dispersing the pigment in an amount of 10 to 140% by weight based on the pigment.
５．高沸点有機溶媒を０．１〜３０重量％含む、前記１〜４の何れかに記載のイエローインク組成物。 5. 5. The yellow ink composition according to any one of 1 to 4 above, containing 0.1 to 30% by weight of a high boiling point organic solvent.
６．浸透促進剤を１〜２０重量％含む、前記１〜５の何れかに記載のイエローインク組成物。 6). 6. The yellow ink composition according to any one of 1 to 5 above, containing 1 to 20% by weight of a penetration accelerator.
７．アセチレングリコール系化合物およびシリコーン系化合物の少なくとも一つを０．０１〜５重量％含む、前記１から６の何れかに記載のイエローインク組成物。 7). 7. The yellow ink composition according to any one of 1 to 6 above, containing 0.01 to 5% by weight of at least one of an acetylene glycol compound and a silicone compound.
８．前記１〜７の何れかに記載のイエローインク組成物を含むインクカートリッジ。 8). An ink cartridge comprising the yellow ink composition according to any one of 1 to 7 above.
９．前記１〜７の何れかに記載のイエローインク組成物を用いて画像を形成する記録方法。 9. 8. A recording method for forming an image using the yellow ink composition according to any one of 1 to 7 above.
１０．前記１〜７の何れかに記載のイエローインク組成物を用いて画像を形成する記録システム。 10. A recording system for forming an image using the yellow ink composition according to any one of 1 to 7 above.
１１．前記１〜７の何れかに記載のイエローインク組成物を用いて画像が形成されてなる記録物。 11. 8. A recorded matter in which an image is formed using the yellow ink composition according to any one of 1 to 7 above.
本発明によれば、高明度（高Ｌ*）領域のみならず低明度のイエロー領域、即ち「低Ｌ*且つａ*がゼロ近傍且つ高ｂ*」における色再現性にも優れるとともに、耐ガス性に優れるイエローインク組成物を提供することができる。 According to the present invention, not only the high lightness (high L *) region but also the low lightness yellow region, that is, “low L * and a * is close to zero and high b *” is excellent in color reproducibility and gas resistance. A yellow ink composition having excellent properties can be provided.
また、本発明の実施形態によれば、高明度から低明度の広い領域にわたって、黄色を再現性よく表現することができる。さらに、高Ｌ*〜低Ｌ*にわたる広い領域において、黄色の色再現性および色安定性に優れ、シアン等他のインクと混合しなくても、ａ*軸近傍かつ高ｂ*の純粋な黄色の色の調整が可能である。 Further, according to the embodiment of the present invention, yellow can be expressed with high reproducibility over a wide region from high brightness to low brightness. Furthermore, in a wide range from high L * to low L *, yellow is excellent in color reproducibility and color stability, and is pure yellow near the a * axis and high b * without mixing with other inks such as cyan. Can be adjusted.
また、本発明は、上記イエローインク組成物を用いて画像を形成する記録方法を提供するものである。この記録方法によれば、低明度のイエロー領域の色再現性に優れとともに、耐ガス性に優れ、インクジェット法により吐出された場合も吐出重量の変化による発色のばらつきが小さく、ドット表現による粒状性も目立たない良質な記録画像を得ることができる。 The present invention also provides a recording method for forming an image using the above yellow ink composition. According to this recording method, it has excellent color reproducibility in the low-lightness yellow region, excellent gas resistance, and even when ejected by the ink-jet method, there is little variation in color development due to changes in ejection weight, and graininess due to dot expression. It is possible to obtain a high-quality recorded image that is inconspicuous.
また、本発明は、上記イエローインク組成物を用いて画像を形成する記録システムを提供するものである。この記録システムによれば、低明度のイエロー領域の色再現性に優れとともに、耐ガス性に優れ、インクジェット法により吐出された場合も吐出重量の変化による発色のばらつきが小さく、ドット表現による粒状性も目立たない良質な記録画像を得ることができる。 The present invention also provides a recording system for forming an image using the yellow ink composition. This recording system has excellent color reproducibility in the low-lightness yellow area, excellent gas resistance, small color variation due to changes in the discharge weight even when ejected by the inkjet method, and graininess due to dot expression. It is possible to obtain a high-quality recorded image that is inconspicuous.
さらに、本発明は、上記イエローインク組成物を用いて画像が形成されてなる記録物を提供するものである。この記録物は、低明度のイエロー領域の色再現性に優れとともに、耐ガス性に優れ、インクジェット法により吐出された場合も吐出重量の変化による発色のばらつきが小さく、ドット表現による粒状性も目立たない良質なものである。 Furthermore, the present invention provides a recorded matter in which an image is formed using the yellow ink composition. This recorded product has excellent color reproducibility in the low-lightness yellow region, excellent gas resistance, small variation in color due to change in discharge weight even when ejected by the inkjet method, and graininess due to dot expression is also conspicuous There is no good quality.
〔イエローインク組成物〕
以下に本発明に係るイエローインク組成物について、その好ましい実施態様に基づき説明する。
[Yellow ink composition]
Hereinafter, the yellow ink composition according to the present invention will be described based on preferred embodiments thereof.
本発明に係るイエローインク組成物は、上述の通り、色材としての顔料として、Ｃ．Ｉ．ピグメントイエロー１２９（以下「ＰＹ１２９」と略記することもある。）及びＣ．Ｉ．ピグメントイエロー７４（以下「ＰＹ７４」と略記することもある。）を含有し、それらの重量比（前者／後者）が１／６〜３／７、好ましくは１／５〜１／３である。かかる範囲内で配合した構成によれば、高明度（高Ｌ*）領域のみならず低明度のイエロー領域、即ち低Ｌ*且つａ*がゼロ近傍且つ高ｂ*における色再現性にも優れるとともに、耐ガス性に優れる。 As described above, the yellow ink composition according to the present invention includes C.I. I. Pigment Yellow 129 (hereinafter sometimes abbreviated as “PY129”) and C.I. I. Pigment Yellow 74 (hereinafter sometimes abbreviated as “PY74”), and the weight ratio (the former / the latter) is 1/6 to 3/7, preferably 1/5 to 1/3. According to the composition blended within this range, not only the high lightness (high L *) region but also the low lightness yellow region, that is, low L * and a * are near zero and high in color reproducibility at high b *. Excellent gas resistance.
また、本発明においては、高明度から低明度の広いイエロー領域におけるバランスがより良好な色再現性を得ることができる点から、ＣＩＥで規定のＸＹＺ表示系におけるＺ値が２３のとき、Ｙ値が８９．１〜９５、特に８９．２〜９２、とりわけ８９．３〜９０であることが好ましい。Ｚ値は、インク組成物の希釈水溶液の紫外可視透過スペクトルから算出することができる。インク組成物に含まれる顔料濃度が変化すると、Ｚ値が２３になるための希釈倍率も変動するが、あるインクのＺ値が２３となるように希釈した場合にＹ値が上記範囲となることが好ましい。ここで、Ｚ値は、例えばＵ３３００（日立製作所社製）を用いて、スキャンスピード６００ｎｍ／ｍｉｎ、測定波長範囲３８０〜８００ｎｍ、スリット幅２．０ｎｍの条件で透過率測定し、Ｄ６５光源、視野角２度において算出することにより得ることができる。 Further, in the present invention, since a color balance with a better balance in a wide yellow region from high brightness to low brightness can be obtained, when the Z value in the XYZ display system defined by CIE is 23, the Y value Is preferably 89.1 to 95, more preferably 89.2 to 92, especially 89.3 to 90. The Z value can be calculated from the ultraviolet-visible transmission spectrum of the diluted aqueous solution of the ink composition. When the concentration of the pigment contained in the ink composition changes, the dilution ratio for changing the Z value to 23 also fluctuates. Is preferred. Here, the Z value is measured using the U3300 (manufactured by Hitachi, Ltd.) under the conditions of a scan speed of 600 nm / min, a measurement wavelength range of 380 to 800 nm, and a slit width of 2.0 nm, a D65 light source, and a viewing angle. It can be obtained by calculating at twice.
本発明に係るイエローインクは、好ましくは重量１００倍希釈以上３０００倍希釈以下の範囲において、より好ましくは重量５００倍希釈以上２５００倍希釈以下の範囲において、さらに好ましくは重量１０００倍希釈以上２０００倍希釈以下の範囲において、ＣＩＥによって規定されるＸＹＺ表示系におけるＺ値が２３のとき、Ｙ値が上記範囲内であれば好ましい。 The yellow ink according to the present invention is preferably in the range of 100 times to 3000 times dilution, more preferably in the range of 500 times to 2500 times dilution, more preferably 1000 times to 2000 times dilution. In the following ranges, when the Z value in the XYZ display system defined by CIE is 23, it is preferable that the Y value is within the above range.
本発明に係るイエローインク組成物に用いるＰＹ１２９は金属錯塩顔料である。金属錯塩顔料を含むイエローインクは、低明度のイエロー領域を再現性良く表現することができる。また、金属錯塩顔料を含むインクを用いることによって、記録物の画像堅牢性にも優れたインクセットとすることができる。 PY129 used in the yellow ink composition according to the present invention is a metal complex pigment. A yellow ink containing a metal complex pigment can express a low brightness yellow region with good reproducibility. Further, by using an ink containing a metal complex pigment, an ink set excellent in image fastness of recorded matter can be obtained.
また、もう一方のＰＹ７４は、比較的高明度なイエロー顔料である。かかるイエロー顔料を上記金属錯塩顔料と混合することで、高明度領域から低明度領域まで広くイエローの安定性および再現性に優れたインク組成物を得ることができる。これにより、インクジェット法によりドット状に吐出された場合にも粒状性が目立たなくなるという効果も得られる。また、このような構成により、複数種類のイエローインクを用いなくても、イエロー領域における低明度と高明度の再現性をバランスよく向上させることができる。 The other PY74 is a yellow pigment with relatively high brightness. By mixing such a yellow pigment with the metal complex pigment, an ink composition having a wide range of yellow and low lightness and excellent yellow stability and reproducibility can be obtained. Thereby, the effect that the graininess becomes inconspicuous even when ejected in a dot shape by the ink jet method is also obtained. In addition, with such a configuration, the reproducibility of low brightness and high brightness in the yellow region can be improved in a balanced manner without using a plurality of types of yellow ink.
本発明に係るイエローインク組成物は、色材として顔料を使用するとともに、該顔料を分散するための分散剤を含有するものが好ましい。分散剤としては、この種の顔料インクにおけるものと同様のものを特に制限なく用いることができ、例えば、カチオン性分散剤、アニオン性分散剤、ノニオン性分散剤や界面活性剤等が挙げられる。アニオン性分散剤の例としては、ポリアクリル酸、ポリメタクリル酸、アクリル酸−アクリロニトリル共重合体、酢酸ビニル−アクリル酸エステル共重合体、アクリル酸−アクリル酸アルキルエステル共重合体、スチレン−アクリル酸共重合体、スチレン−メタクリル酸共重合体、スチレン−アクリル酸−アクリル酸アルキルエステル共重合体、スチレン−メタクリル酸−アクリル酸アルキルエステル共重合体、スチレン−α−メチルスチレン−アクリル酸共重合体、スチレン−α−メチルスチレン−アクリル酸−アクリル酸アルキルエステル共重合体、スチレン−マレイン酸共重合体、ビニルナフタレン−マレイン酸共重合体、酢酸ビニル−エチレン共重合体、酢酸ビニル−脂肪酸ビニルエチレン共重合体、酢酸ビニル−マレイン酸エステル共重合体、酢酸ビニル−クロトン酸共重合体、酢酸ビニル−アクリル酸共重合体等が挙げられる。また、アニオン性界面活性剤の例としては、ドデシルベンゼンスルホン酸ナトリウム、ラウリル酸ナトリウム、ポリオキシエチレンアルキルエーテルサルフェートのアンモニウム塩等が挙げられ、ノニオン性界面活性剤の例としては、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルエステル、ポリオキシエチレンソルビタン脂肪酸エステル、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレンアルキルアミン、ポリオキシエチレンアルキルアミド等が挙げられ、これらの１種又は２種以上が用いられる。特に、顔料の分散安定性を高める観点から、スチレン−（メタ）アクリル酸共重合体を用いることが好ましい。 The yellow ink composition according to the present invention preferably uses a pigment as a coloring material and contains a dispersant for dispersing the pigment. As the dispersant, those similar to those in this type of pigment ink can be used without particular limitation, and examples thereof include a cationic dispersant, an anionic dispersant, a nonionic dispersant, and a surfactant. Examples of anionic dispersants include polyacrylic acid, polymethacrylic acid, acrylic acid-acrylonitrile copolymer, vinyl acetate-acrylic acid ester copolymer, acrylic acid-acrylic acid alkyl ester copolymer, styrene-acrylic acid. Copolymer, styrene-methacrylic acid copolymer, styrene-acrylic acid-alkyl acrylate copolymer, styrene-methacrylic acid-alkyl acrylate copolymer, styrene-α-methylstyrene-acrylic acid copolymer Styrene-α-methylstyrene-acrylic acid-alkyl acrylate copolymer, styrene-maleic acid copolymer, vinyl naphthalene-maleic acid copolymer, vinyl acetate-ethylene copolymer, vinyl acetate-fatty acid vinyl ethylene Copolymer, vinyl acetate-maleic ester Examples include copolymers, vinyl acetate-crotonic acid copolymers, vinyl acetate-acrylic acid copolymers, and the like. Examples of anionic surfactants include sodium dodecylbenzenesulfonate, sodium laurate, ammonium salt of polyoxyethylene alkyl ether sulfate, and examples of nonionic surfactants include polyoxyethylene alkyl. Examples include ether, polyoxyethylene alkyl ester, polyoxyethylene sorbitan fatty acid ester, polyoxyethylene alkylphenyl ether, polyoxyethylene alkylamine, polyoxyethylene alkylamide, and the like, and one or more of these are used. In particular, it is preferable to use a styrene- (meth) acrylic acid copolymer from the viewpoint of enhancing the dispersion stability of the pigment.
前記分散剤は、前記各インク中において、前記顔料の重量を基準として、固形分換算で、通常１４０重量％以下で含まれる。 The dispersant is usually contained in each ink in an amount of 140% by weight or less in terms of solid content based on the weight of the pigment.
前記分散剤は、前記顔料の重量を基準として、固形分換算で好ましくは１０〜１４０重量％、更に好ましくは１０〜１００重量％、更に一層好ましくは１０〜４０重量％含まれる。また、インク量に対する分散剤の含有量は、固形分換算で好ましくは０．１〜１０重量％、更に好ましくは０．３〜３重量％である。 The dispersant is preferably contained in an amount of 10 to 140% by weight, more preferably 10 to 100% by weight, and still more preferably 10 to 40% by weight in terms of solid content, based on the weight of the pigment. Further, the content of the dispersant with respect to the ink amount is preferably 0.1 to 10% by weight, more preferably 0.3 to 3% by weight in terms of solid content.
また、本発明に係るイエローインク組成物は、インクジェット記録用に用いた場合に、インクの乾燥を防いでインクジェットプリンタのヘッドでの目詰まりを防止する観点から、高沸点有機溶媒を含むものが好ましい。高沸点有機溶媒としては、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、プロピレングリコール、ブチレングリコール、１，２，６−ヘキサントリオール、チオグリコール、ヘキシレングリコール、グリセリン、トリメチロールエタン、トリメチロールプロパン等の多価アルコール類；エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコールモノメチルエーテル、トリエチレングリコールモノエチルエーテル、トリエチレングリコールモノブチルエーテル等の多価アルコールのアルキルエーテル類；尿素、２−ピロリドン、Ｎ−メチル−２−ピロリドン、１，３−ジメチル−２−イミダゾリジノン、トリエタノールアミン等の有機アルカリ、糖アルコール等の糖類等が挙げられ、これらの１種又は２種以上が用いられる。特に、グリセリンとともに、トリエタノールアミン等の有機アルカリを添加することが、目詰まり防止の向上と、色材の分散性を安定させ、記録画像の光沢を向上させるため好ましい。 In addition, the yellow ink composition according to the present invention preferably contains a high-boiling organic solvent from the viewpoint of preventing ink from drying and preventing clogging at the head of an inkjet printer when used for inkjet recording. . Examples of the high boiling point organic solvent include ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, polypropylene glycol, propylene glycol, butylene glycol, 1,2,6-hexanetriol, thioglycol, hexylene glycol, glycerin, and trimethylol. Polyhydric alcohols such as ethane and trimethylolpropane; ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, triethylene glycol monomethyl ether, triethylene glycol monoethyl ether, tri Multivalent such as ethylene glycol monobutyl ether Alkyl ethers of alcohol; urea, 2-pyrrolidone, N-methyl-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, organic alkalis such as triethanolamine, saccharides such as sugar alcohol, etc. These 1 type (s) or 2 or more types are used. In particular, it is preferable to add an organic alkali such as triethanolamine together with glycerin in order to improve the prevention of clogging, stabilize the dispersibility of the coloring material, and improve the gloss of the recorded image.
前記高沸点有機溶媒は、インク中、好ましくは０．１〜３０重量％、更に好ましくは０．５〜２５重量％含有される。 The high boiling point organic solvent is preferably contained in the ink in an amount of 0.1 to 30% by weight, more preferably 0.5 to 25% by weight.
また、これらの高沸点有機溶媒のうちトリエタノールアミンは、インクのｐＨ調整剤及び分散安定剤としての機能をも有するものであり、その機能を良好に発揮する点で、該トリエタノールアミンを各インク中において０．１〜１０重量％の範囲内で使用することが好ましい。 Of these high-boiling organic solvents, triethanolamine also has a function as an ink pH adjuster and dispersion stabilizer. The ink is preferably used in the range of 0.1 to 10% by weight.
また、本発明に係るイエローインク組成物は、記録媒体への濡れ性を高めてインクの浸透性を高める観点から、浸透促進剤を含有させることができる。浸透促進剤としては、例えば、メタノール、エタノール、ｉｓｏ−プロピルアルコール等のアルコール類；エチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコールモノブチルエーテル、プロピレングリコールモノブチルエーテル、ジプロピレングリコールモノブチルエーテル等の多価アルコールの低級アルキルエーテル；１，２−ペンタンジオール、１，２−ヘキサンジオール等のジオール等が挙げられ、これらの１種又は２種以上が用いられる。特に、ジエチレングリコールモノブチルエーテル、トリエチレングリコールモノブチルエーテル若しくは１，２−ヘキサンジオール、またはこれらの２種以上を用いることが好ましい。 In addition, the yellow ink composition according to the present invention can contain a penetration accelerator from the viewpoint of increasing the wettability to the recording medium and increasing the permeability of the ink. Examples of the penetration enhancer include alcohols such as methanol, ethanol, iso-propyl alcohol; ethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, triethylene glycol monobutyl ether, propylene glycol monobutyl ether, dipropylene glycol mono Examples include lower alkyl ethers of polyhydric alcohols such as butyl ether; diols such as 1,2-pentanediol and 1,2-hexanediol, and one or more of these are used. In particular, it is preferable to use diethylene glycol monobutyl ether, triethylene glycol monobutyl ether, 1,2-hexanediol, or two or more thereof.
前記浸透促進剤は、前記インク中、好ましくは１〜２０重量％、更に好ましくは１〜１０重量％含有される。 The penetration enhancer is preferably contained in the ink in an amount of 1 to 20% by weight, more preferably 1 to 10% by weight.
また、本発明に係るイエローインク組成物は、前記浸透促進剤と同様に、記録媒体への濡れ性を高めてインクの浸透性を高める観点から、アニオン性界面活性剤、ノニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤等の各種界面活性剤を用いることもでき、特に、アセチレングリコール系化合物やシリコーン系化合物を用いることが好ましい。該アセチレングリコール系化合物としては、市販されているものを用いることができ、例えば、オルフィンＹ、サーフィノール８２、４４０、４６５、４８５（何れも商品名、エア・プロダクツ・アンド・ケミカルズ社製）、オルフィンＳＴＧ、オルフィンＥ１０１０（何れも商品名、日信化学株式会社製）等が挙げられ、これらの１種又は２種以上が用いられる。特に、オルフィンＥ１０１０、サーフィノール４６５を用いることが好ましい。また、該シリコーン系化合物としては、市販品としてＢＹＫ３４７、３４８またはＢＹＫＵＶ３５１０（ビックケミージャパン製）等のポリシロキサン系化合物を用いることができる。該アセチレングリコール系化合物及び／又は該シリコーン系化合物は、前記インク中、好ましくは０．０１〜５重量％、更に好ましくは０．１〜１．０重量％、特に好ましくは０．１〜０．５重量％含有される。 In addition, the yellow ink composition according to the present invention is an anionic surfactant, a nonionic surfactant, and a nonionic surfactant from the viewpoint of increasing the wettability to a recording medium and increasing the permeability of the ink, similarly to the penetration accelerator. Various surfactants such as a cationic surfactant and an amphoteric surfactant can also be used, and it is particularly preferable to use an acetylene glycol compound or a silicone compound. As the acetylene glycol-based compound, commercially available compounds can be used. For example, Olfin Y, Surfynol 82, 440, 465, 485 (all trade names, manufactured by Air Products and Chemicals), Orphine STG, Olphine E1010 (both are trade names, manufactured by Nissin Chemical Co., Ltd.) and the like are used, and one or more of these are used. In particular, it is preferable to use Olphine E1010 and Surfynol 465. Moreover, as this silicone type compound, polysiloxane type compounds, such as BYK347, 348 or BYKUV3510 (made by Big Chemie Japan), can be used as a commercial item. The acetylene glycol compound and / or the silicone compound is preferably 0.01 to 5% by weight, more preferably 0.1 to 1.0% by weight, and particularly preferably 0.1 to 0. 5% by weight is contained.
また、本発明に係るイエローインク組成物は、インクの乾燥時間を短縮する観点から、低沸点有機溶媒を含むことができる。該低沸点有機溶媒としては、例えば、メタノール、エタノール、ｎ−プロピルアルコール、ｉｓｏ−プロプルアルコール、ｎ−ブタノール、ｓｅｃ−ブタノール、ｔｅｒｔ−ブタノール、ｉｓｏ−ブタノール、ｎ−ペンタノール等が挙げられ、これらの１種又は２種以上が用いられる。特に、一価アルコールが好ましい。 Further, the yellow ink composition according to the present invention can contain a low boiling point organic solvent from the viewpoint of shortening the drying time of the ink. Examples of the low boiling point organic solvent include methanol, ethanol, n-propyl alcohol, iso-propyl alcohol, n-butanol, sec-butanol, tert-butanol, iso-butanol, n-pentanol and the like. These 1 type (s) or 2 or more types are used. In particular, monohydric alcohol is preferable.
本発明に係るイエローインク組成物は、前述した顔料、分散剤、高沸点有機溶媒、浸透促進剤、アセチレングリコール系化合物及び／又はシリコーン系化合物等の成分を含有し、通常、バランスとして水を含有するものである。水は、イオン交換水、限外濾過水、逆浸透水、蒸留水等の純水又は超純水を用いることが好ましい。特に、これらの水を、紫外線照射又は過酸化水素添加等により滅菌処理した水は、長期間に亘ってカビやバクテリアの発生が防止されるので好ましい。 The yellow ink composition according to the present invention contains components such as the aforementioned pigment, dispersant, high boiling point organic solvent, penetration enhancer, acetylene glycol compound and / or silicone compound, and usually contains water as a balance. To do. It is preferable to use pure water or ultrapure water such as ion exchange water, ultrafiltration water, reverse osmosis water, or distilled water. In particular, water obtained by sterilizing these waters by ultraviolet irradiation or addition of hydrogen peroxide is preferable because generation of mold and bacteria is prevented over a long period of time.
本発明に係るイエローインク組成物には、更に必要に応じて、水溶性ロジン類等の定着剤、安息香酸ナトリウム等の防黴剤・防腐剤、アロハネート類等の酸化防止剤・紫外線吸収剤、キレート剤、酸素吸収剤、ｐＨ調整剤等の添加剤を含有させることができ、これらの１種又は２種以上が用いられる。 If necessary, the yellow ink composition according to the present invention further includes a fixing agent such as a water-soluble rosin, an antifungal agent / preservative such as sodium benzoate, an antioxidant / ultraviolet absorber such as allophanates, Additives such as chelating agents, oxygen absorbers, and pH adjusters can be contained, and one or more of these can be used.
本発明に係るイエローインク組成物は、従来公知の装置、例えば、ボールミル、サンドミル、アトライター、バスケットミル、ロールミル等を使用して、従来の顔料インクと同様に調製することができる。調製に際しては、メンブレンフィルターやメッシュフィルター等を用いて粗大粒子を除去することが好ましい。 The yellow ink composition according to the present invention can be prepared in the same manner as a conventional pigment ink by using a conventionally known apparatus such as a ball mill, a sand mill, an attritor, a basket mill, a roll mill and the like. In the preparation, it is preferable to remove coarse particles using a membrane filter, a mesh filter or the like.
本発明に係るイエローインク組成物は、その用途に特に制限はないが、ノズルからインクの液滴を吐出させ、該液滴を記録媒体に付着させて文字や図形等の画像を形成する記録方法であるインクジェット記録方法に用いられることが好ましく、特にオンデマンド型のインクジェット記録方法に用いられることが好ましい。オンデマンド型のインクジェット記録方法としては、例えば、プリンターヘッドに配設された圧電素子を用いて記録を行う圧電素子記録方法、プリンターヘッドに配設された発熱抵抗素子のヒーター等による熱エネルギーを用いて記録を行う熱ジェット記録方法等が挙げられ、何れのインクジェット記録方法にも好適に使用できる。 The use of the yellow ink composition according to the present invention is not particularly limited, but a recording method of forming an image such as a character or a figure by ejecting ink droplets from a nozzle and attaching the droplets to a recording medium It is preferably used for an inkjet recording method, and particularly preferably used for an on-demand inkjet recording method. As an on-demand type ink jet recording method, for example, a piezoelectric element recording method that performs recording using a piezoelectric element disposed in a printer head, or a thermal energy generated by a heater of a heating resistance element disposed in the printer head is used. And a thermal jet recording method for recording, and can be suitably used for any ink jet recording method.
本発明に係るイエローインク組成物は、画像を形成するための記録媒体として、インクジェット記録方法等において通常用いられる記録媒体に制限なく適用できるが、塗工層を有するメディアや普通紙（被記録面に繊維が露呈している記録媒体）等に好適に適用される。特に、本発明に係るイエローインク組成物は、塗工層を有するメディアに適用すれば、画像を形成した際のドット表現による粒状性の目立ちの抑制を顕著に得ることができる。 The yellow ink composition according to the present invention can be applied as a recording medium for forming an image without limitation to a recording medium usually used in an ink jet recording method or the like. The recording medium in which the fibers are exposed to the like) is suitably applied. In particular, when the yellow ink composition according to the present invention is applied to a medium having a coating layer, it is possible to remarkably suppress noticeable graininess due to dot expression when an image is formed.
本明細書において、「塗工層を有するメディア」とは、前述したイエローインク組成物を用いて画像を形成する面（被記録面）が少なくとも塗工層で被覆されているものの全てを意味する。この塗工層を有するメディアは、通常、８５度光沢度が１２０以下のものが用いられる。ここで、８５度光沢度は、日本電色工業株式会社製の「ＰＧ１Ｍ」等を用いて測定される。尚、測定に際しては、標準光沢板８５度光沢度が１００を示すように予め測定装置を調整しておく。 In the present specification, “medium having a coating layer” means all of the surfaces (recording surface) on which an image is formed by using the yellow ink composition described above, which are covered with at least the coating layer. . As the media having this coating layer, those having an 85 degree gloss of 120 or less are usually used. Here, the 85 degree glossiness is measured by using “PG1M” manufactured by Nippon Denshoku Industries Co., Ltd. In the measurement, the measuring apparatus is adjusted in advance so that the standard gloss plate 85 degree glossiness is 100.
塗工層を有するメディアとしては、８５度光沢度が７０〜１２０である鏡面調メディア、例えば、１ｍ以上離れたところから蛍光灯を当てた場合に該蛍光灯の写像の輪郭が目視で確認できるような樹脂コート層を有するメディア等が挙げられ、その代表的な一例として、８５度光沢度が８１であるセイコーエプソン社製の「ＰＧＰＰ（Premium Glossy Photo Paper）」が挙げられる。 As media having a coating layer, specular tone media having a glossiness of 85 to 70 to 120, for example, when a fluorescent lamp is applied from a distance of 1 m or more, the contour of the fluorescent lamp can be visually confirmed. Examples of such media include a resin coating layer, and a typical example thereof is “PGPP (Premium Glossy Photo Paper)” manufactured by Seiko Epson Corporation having an 85 degree gloss of 81.
また、塗工層を有するメディアの別の例としては、８５度光沢度が１０〜７０であるセミグロス調メディアや、８５度光沢度が１０以下であるマット調メディア等が挙げられる。 Other examples of media having a coating layer include semi-glossy media having an 85 ° glossiness of 10 to 70, and matte media having an 85 ° glossiness of 10 or less.
また、本発明に係るイエローインク組成物は、Ｌ版等の比較的小さなサイズのメディア（好ましくは塗工層を有するメディア）に対して低解像度で記録しても、ドット表現による粒状性を極めて抑制できる。このため、本発明に係るイエローインク組成物は、Ｌ版等の比較的小さなサイズのメディアに対して特に有用である。 In addition, the yellow ink composition according to the present invention has extremely high granularity due to dot expression even when recording at a low resolution on a relatively small size medium (preferably a medium having a coating layer) such as an L plate. Can be suppressed. For this reason, the yellow ink composition according to the present invention is particularly useful for a medium having a relatively small size such as an L plate.
〔インクカートリッジ〕
本発明によれば、前述したイエローインク組成物を含むインクカートリッジを提供することができる。かかるインクカートリッジによって、本発明の目的、即ち、低Ｌ*且つａ*がゼロ近傍且つ高ｂ*における色再現性、及び耐ガス性を容易に達成できる。
〔ink cartridge〕
According to the present invention, an ink cartridge containing the yellow ink composition described above can be provided. With such an ink cartridge, the object of the present invention, that is, color reproducibility and gas resistance at low L * and a * near zero and high b * can be easily achieved.
〔記録方法〕
次に、本発明の記録方法について説明する。
〔Recording method〕
Next, the recording method of the present invention will be described.
本発明は、前述したイエローインク組成物を用いて画像を形成する記録方法、即ち、色材としての顔料として、Ｃ．Ｉ．ピグメントイエロー１２９及びＣ．Ｉ．ピグメントイエロー７４を含有し、それらの重量比（前者／後者）が１／６〜３／７であるイエローインク組成物を用いて画像を形成する方法であり、特に、前述した実施形態のイエローインク組成物を用いる記録方法が好適である。尚、本発明の記録方法は、前記イエローインク組成物を用いる点以外については、通常のインクジェット記録方法等と同様にして実施される。 The present invention relates to a recording method for forming an image using the above-described yellow ink composition, that is, as a pigment as a coloring material, C.I. I. Pigment yellow 129 and C.I. I. This is a method of forming an image using a yellow ink composition containing Pigment Yellow 74 and having a weight ratio (the former / the latter) of 1/6 to 3/7. In particular, the yellow ink of the above-described embodiment A recording method using the composition is preferred. The recording method of the present invention is carried out in the same manner as a normal ink jet recording method except that the yellow ink composition is used.
本発明に係るインクジェット記録方法によれば、イエロー領域において高明度および低明度で色再現性、及び耐ガス性の向上した画像を得ることができ、記録時の温度、機体間の差、インク粘度、インク供給力等に起因する吐出量のばらつきがあっても、色再現性への影響が小さい画像を得ることができる。 According to the ink jet recording method of the present invention, it is possible to obtain an image with improved color reproducibility and gas resistance at high brightness and low brightness in the yellow region, the temperature during recording, the difference between the machine bodies, the ink viscosity. Even if there is a variation in the ejection amount due to the ink supply force or the like, it is possible to obtain an image with little influence on the color reproducibility.
本発明の記録方法においては、Ｄｕｔｙ１００％のインク重量が、７〜１３mg／inch2となるように画像を形成することが好ましい。 In the recording method of the present invention, it is preferable to form an image so that the ink weight of 100% duty is 7 to 13 mg / inch 2 .
また、混合色は、Ｄｕｔｙ１２０％のインク重量が、８〜１６mg／inch2となるように画像を形成することが好ましい。 Further, it is preferable that the mixed color forms an image so that the ink weight of Duty 120% is 8 to 16 mg / inch 2 .
尚、本明細書において、「Ｄｕｔｙ」とは、下記式で定義され、算出される値Ｄの単位を示すものである。 In this specification, “Duty” is defined by the following formula and indicates a unit of the calculated value D.
Ｄ＝〔実印字ドット数／（縦解像度×横解像度）〕×１００また、Ｄｕｔｙ１００％とは、画素に対する単色の最大インク重量を意味する。 D = [actual print dot number / (vertical resolution × horizontal resolution)] × 100 Duty 100% means the maximum ink weight of a single color for a pixel.
〔記録システム〕
本発明は、前述したイエローインク組成物を用いて画像を形成する記録システムであり、特に、前述した実施形態に係るイエローインク組成物を用いるインクジェットプリンタ等の記録装置その他の記録システムが好適である。
[Recording system]
The present invention is a recording system for forming an image using the above-described yellow ink composition, and is particularly suitable for a recording apparatus such as an ink jet printer using the yellow ink composition according to the above-described embodiment or other recording systems. .
〔記録物〕
本発明は、前述したイエローインク組成物を用いて画像が形成されてなる記録物であり、特に、前述した実施形態のイエローインク組成物を用いたものが好適である。
[Recorded material]
The present invention is a recorded matter in which an image is formed using the above-described yellow ink composition, and in particular, those using the yellow ink composition of the above-described embodiment are suitable.
〔変更形態〕
本発明は、前述した各実施形態を好適に提供するものであるが、これらの実施形態に限定されず、その趣旨を逸脱しない範囲内で種々の変更が可能である。
[Modification]
The present invention suitably provides each of the embodiments described above, but is not limited to these embodiments, and various modifications can be made without departing from the spirit of the present invention.
以下に、本発明の実施例および試験例を挙げて、本発明をより具体的に説明するが、本発明はかかる実施例により何等制限されるものではない。 EXAMPLES Hereinafter, the present invention will be described more specifically with reference to examples and test examples of the present invention. However, the present invention is not limited to the examples.
〔インクの調製〕
本発明に係るイエローインク組成物として、ＰＹ１２９及びＰＹ７９を所定重量比で含むイエローインク組成物（Ｙ１）および（Ｙ２）を調製した。
[Preparation of ink]
As yellow ink compositions according to the present invention, yellow ink compositions (Y1) and (Y2) containing PY129 and PY79 at a predetermined weight ratio were prepared.
＜イエローインク（Ｙ１）＞
Ｃ．Ｉ．ピグメントイエロー１２９ ０．７５重量％
Ｃ．Ｉ．ピグメントイエロー７４ ２．２５重量％
分散剤(スチレン−アクリル酸共重合体) ０．９重量％
グリセリン １０．０重量％
１，２−ヘキサンジオール １０．０重量％
ＢＹＫ３４８ ０．３重量％
(ビッグケミー・ジャパン社製シリコーン系界面活性剤)
トリエタノールアミン ０．９重量％
純水 残量
計１００．０重量％
<Yellow ink (Y1)>
C. I. Pigment Yellow 129 0.75% by weight
C. I. Pigment Yellow 74 2.25% by weight
Dispersant (styrene-acrylic acid copolymer) 0.9% by weight
Glycerin 10.0% by weight
1,2-hexanediol 10.0% by weight
BYK348 0.3 wt%
(Silicone surfactant manufactured by Big Chemie Japan)
Triethanolamine 0.9% by weight
Pure water remaining
100.0% by weight
＜イエローインク（Ｙ２）＞
Ｃ．Ｉ．ピグメントイエロー１２９ ０．５０重量％
Ｃ．Ｉ．ピグメントイエロー７４ ２．５０重量％
分散剤(スチレン−アクリル酸共重合体) ０．９重量％
グリセリン １０．０重量％
１，２−ヘキサンジオール １０．０重量％
ＢＹＫ３４８ ０．３重量％
(ビッグケミー・ジャパン社製シリコーン系界面活性剤)
トリエタノールアミン ０．９重量％
純水 残量
計１００．０重量％
<Yellow ink (Y2)>
C. I. Pigment Yellow 129 0.50% by weight
C. I. Pigment Yellow 74 2.50% by weight
Dispersant (styrene-acrylic acid copolymer) 0.9% by weight
Glycerin 10.0% by weight
1,2-hexanediol 10.0% by weight
BYK348 0.3 wt%
(Silicone surfactant manufactured by Big Chemie Japan)
Triethanolamine 0.9% by weight
Pure water remaining
100.0% by weight
また、比較例として、ＰＹ１２９及びＰＹ７９を含むが本発明に係る所定重量比の範囲内にはないイエローインク組成物（ｙ１）および（ｙ２）を調製した。 As comparative examples, yellow ink compositions (y1) and (y2) containing PY129 and PY79 but not within the predetermined weight ratio range according to the present invention were prepared.
＜イエローインク（ｙ１）＞
Ｃ．Ｉ．ピグメントイエロー１２９ ０．３０重量％
Ｃ．Ｉ．ピグメントイエロー７４ ２．７０重量％
分散剤(スチレン−アクリル酸共重合体) ０．９重量％
グリセリン １０．０重量％
１，２−ヘキサンジオール １０．０重量％
ＢＹＫ３４８ ０．３重量％
(ビッグケミー・ジャパン社製シリコーン系界面活性剤)
トリエタノールアミン ０．９重量％
純水 残量
計１００．０重量％
<Yellow ink (y1)>
C. I. Pigment Yellow 129 0.30% by weight
C. I. Pigment Yellow 74 2.70% by weight
Dispersant (styrene-acrylic acid copolymer) 0.9% by weight
Glycerin 10.0% by weight
1,2-hexanediol 10.0% by weight
BYK348 0.3 wt%
(Silicone surfactant manufactured by Big Chemie Japan)
Triethanolamine 0.9% by weight
Pure water remaining
100.0% by weight
＜イエローインク（ｙ２）＞
Ｃ．Ｉ．ピグメントイエロー１２９ １．００重量％
Ｃ．Ｉ．ピグメントイエロー７４ ２．００重量％
（上記２種のイエロー顔料の重量比＝１：１）
分散剤(スチレン−アクリル酸共重合体) ０．９重量％
グリセリン １０．０重量％
１，２−ヘキサンジオール １０．０重量％
ＢＹＫ３４８ ０．３重量％
(ビッグケミー・ジャパン社製シリコーン系界面活性剤)
トリエタノールアミン ０．９重量％
純水 残量
計１００．０重量％
<Yellow ink (y2)>
C. I. Pigment Yellow 129 1.00% by weight
C. I. Pigment Yellow 74 2.00% by weight
(Weight ratio of the above two yellow pigments = 1: 1)
Dispersant (styrene-acrylic acid copolymer) 0.9% by weight
Glycerin 10.0% by weight
1,2-hexanediol 10.0% by weight
BYK348 0.3 wt%
(Silicone surfactant manufactured by Big Chemie Japan)
Triethanolamine 0.9% by weight
Pure water remaining
100.0% by weight
〔オゾンガス暴露評価〕
上記実施例、及び比較例で作成した各インクを用いて、ＰＭ−９２０Ｃ（セイコーエプソン株式会社製）でＯＤ＝１．０の単色パッチを写真用紙＜光沢＞（セイコーエプソン株式会社製）に印字した。印刷物を２４時間自然乾燥した後、オゾンウェザーメーター（スガ試験機(株)製）５０ＰＰＭ２４℃／６０％ＲＨで４８時間暴露し、曝露前、曝露後それぞれの印刷物をグレタグマクベスＳＰＭ−５０（グレタグマクベス社製）を用い、Ｄ５０光源、視野角２°で測定し、ＣＩＥで規定するＬ*値、ａ*値、ｂ*値を得た。これより試験前後における色差ΔＥ*ａｂを次式から求めた。
ΔＥ＊ａｂ=[(ΔＬ＊)2＋(Δａ＊)2＋(Δｂ＊)2]1/2
[Ozone gas exposure assessment]
Using each ink created in the above examples and comparative examples, a single color patch with OD = 1.0 is printed on photo paper <gloss> (manufactured by Seiko Epson Corporation) with PM-920C (manufactured by Seiko Epson Corporation). did. The printed matter was air-dried for 24 hours, and then exposed to ozone weather meter (manufactured by Suga Test Instruments Co., Ltd.) at 50 PPM for 24 hours at 24 ° C./60% RH. Before and after exposure, each printed matter was Gretag Macbeth SPM-50 (Gretag Macbeth). And L * value, a * value, and b * value specified by CIE were obtained using a D50 light source and a viewing angle of 2 °. From this, the color difference ΔE * ab before and after the test was obtained from the following equation.
ΔE * ab = [(ΔL *) 2 + (Δa *) 2 + (Δb *) 2 ] 1/2
測定結果を次の表に示す。
〔各インクの希釈水溶液のＸ値、Ｙ値およびＺ値の測定〕
上記実施例、及び比較例で作成した各インクからそれぞれ希釈水溶液を調製し、Ｕ−３３００（日立製作所製）で、縦１ｃｍ×横１ｃｍ×高さ４ｃｍ、容量４ｍｌの石英セルを用い、以下の条件で測定を行った。光源ランプのスリット幅２ｍｍ、測定間隔のスキャンスピード６００ｎｍ／ｍｉｎ、透過率０．０〜１００．０％Ｔ、測定範囲３８０〜８００ｎｍでホトマル電圧２００Ｖ、光源ランプを３４０ｎｍ切り替えでＤ２ランプ、Ｗ１ランプとして、紫外可視透過スペクトルをそれぞれ測定し、ＣＩＥで規定のＸＹＺ表示系における、Ｘ値、Ｙ値、Ｚ値をＤ６５光源、視野角２°の条件で算出した。これらの値をグラフにプロットして曲線で結び、この曲線からＺ値が２３．００のときのＸ値及びＹ値の値を決定し、次の表に示す。
[Measurement of X value, Y value and Z value of dilute aqueous solution of each ink]
A diluted aqueous solution was prepared from each of the inks prepared in the above examples and comparative examples, and U-3300 (manufactured by Hitachi, Ltd.) was used with a quartz cell having a height of 1 cm, a width of 1 cm, a height of 4 cm, and a capacity of 4 ml. Measurement was performed under the conditions. The slit width of the light source lamp is 2 mm, the scanning speed of the measurement interval is 600 nm / min, the transmittance is 0.0 to 100.0% T, the photovoltage is 200 V in the measurement range of 380 to 800 nm, and the light source lamp is switched to 340 nm as the D2 lamp and W1 lamp. The UV-visible transmission spectrum was measured, and the X value, Y value, and Z value in the XYZ display system defined by CIE were calculated under the conditions of a D65 light source and a viewing angle of 2 °. These values are plotted on a graph and connected by a curve. From this curve, the X value and Y value when the Z value is 23.00 are determined and are shown in the following table.
〔各インクのＬ*値、a*値およびｂ*値の測定〕
上記実施例、及び比較例で作成した各インクをＰＭ−９２０Ｃ（セイコーエプソン株式会社製）でＤｕｔｙを２５〜２５５％まで変化させ、写真用紙＜光沢＞（セイコーエプソン株式会社製）に印字した。得られた印刷物をグレタグマクベスＳＰＭ−５０（グレタグマクベス社製）を用い、Ｄ５０光源、視野角２°で測定し、ＣＩＥで規定するＬ*値、ａ*値、ｂ*値を得た。
[Measurement of L * value, a * value and b * value of each ink]
Each of the inks prepared in the above Examples and Comparative Examples was printed on photographic paper <gloss> (Seiko Epson Corporation) with PM-920C (Seiko Epson Corporation) while changing the Duty from 25 to 255%. The obtained printed matter was measured using a Gretag Macbeth SPM-50 (manufactured by Gretag Macbeth) with a D50 light source and a viewing angle of 2 °, and L * value, a * value, and b * value defined by CIE were obtained.
測定値を次の表に示す。
本発明は、高明度（高Ｌ*）領域のみならず低明度のイエロー領域、即ち「低Ｌ*且つａ*がゼロ近傍且つ高ｂ*」における色再現性に優れるとともに、耐ガス性に優れるイエローインク組成物、並びに、該組成物を含むインクカートリッジ、該組成物を用いて画像を形成する記録方法及び記録システム、及び該組成物を用いて画像が形成された記録物として産業上の利用可能性を有する。 The present invention is excellent in color reproducibility not only in a high lightness (high L *) region but also in a low lightness yellow region, that is, “low L * and a * is near zero and high b *”, and is excellent in gas resistance. YELLOW INK COMPOSITION, INK CARTRIDGE CONTAINING THE COMPOSITION, RECORDING METHOD AND RECORDING SYSTEM FOR FORMING IMAGE USING THE COMPOSITION, AND INDUSTRIAL USE AS RECORDED PRODUCT WITH IMAGE FORMED USING THE COMPOSITION Have potential.
Claims (11)
A recorded matter in which an image is formed using the yellow ink composition according to claim 1.