JP2009191215A - Water-soluble solid drawing material - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a water-soluble solid drawing material which has high strength, a coloring material of which is excellently dispersed and which provides a drawn line not causing color irregularity even if it is traced with water. <P>SOLUTION: The water-soluble solid drawing material is composed of at least a coloring material and a sulfonic acid-modified polyvinyl acetate or a partially saponified substance of the sulfonic acid-modified polyvinyl acetate, and further contains a body material such as talc and a lubricant in addition to the base materials. A suitable use amount of the sulfonic acid-modified polyvinyl acetate or the partially saponified substance of the sulfonic acid-modified polyvinyl acetate is in a range of 0.2-30 wt.% based on the whole solid drawing material. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

  The present invention relates to a water-soluble solid drawing material from which a drawing surface in the form of a watercolor paint can be obtained with water after drawing.

Conventional water-soluble solid drawing materials are mainly water-soluble resins and pigments such as polyvinyl alcohol and carboxymethyl cellulose, which are made water-soluble by adding a surfactant to wax or pigment (see Patent Document 1). In particular, a partially saponified product of polyvinyl acetate is known as a material that contributes to the strength and writing quality of a solid drawing material (see Patent Document 2).
JP-A-9-67542 JP 2002-201399 A

  When a surfactant is used, moisture is absorbed, resulting in a problem that strength is deteriorated and breaks easily. Patent Document 2 solves this problem. However, even if the above materials are used, the improvement in strength is still not sufficient, and if the strength is increased, the writing feel becomes rough and the colorability deteriorates, and the method of melting the image line by water is not sufficient. Furthermore, there is a problem with the dispersibility of the coloring material. In other words, since the dispersibility is insufficient, the colorant does not spread uniformly on the paper surface when the drawn image line is traced with water, resulting in color unevenness.

  The present invention relates to a water-soluble solid drawing material having high strength, excellent writing quality, and extremely good dispersion of a coloring material. The first aspect of the present invention includes at least a coloring material and a sulfonic acid-modified polyvinyl acetate. The gist.

  Further, the second gist is that it comprises at least a coloring material and a partially saponified product of sulfonic acid-modified polyvinyl acetate.

  The water-soluble solid drawing material of the present invention has high strength and smooth writing, and since the coloring material is uniformly dispersed in the solid drawing material, there is no color unevenness when the image line is traced with water after drawing. It has the feature that vividness is obtained.

  The solid drawing material of the present invention achieves the purpose of preventing color unevenness with high strength by blending at least a coloring material with sulfonic acid-modified polyvinyl acetate or a saponified product of sulfonic acid-modified polyvinyl acetate.

  As the coloring material, any of conventionally known pigments and dyes can be used. For example, inorganic pigments, organic pigments, white pigments, pearl pigments, metal pigments, fluorescent pigments and the like can be used alone or in combination. Specific examples of the inorganic pigment include carbon black, iron black, ultramarine blue, and petal, and examples of the organic pigment include azo pigments, indigo pigments, phthalocyanine pigments, quinacridone pigments, and thioindigo pigments. Examples of white pigments include titanium oxide and zinc oxide, and examples of fluorescent pigments include daylight fluorescent pigments and phosphorescent pigments. Examples of the dye include known ones such as phthalocyanine dyes, pyrazolone dyes, nigrosine dyes, anthraquinone dyes, and azo dyes. The colorant is used alone or in combination as appropriate depending on the desired quality such as transparency and concealment. The amount of the coloring material used varies greatly depending on the type, but is preferably 1 to 50% by weight based on the total amount of the water-soluble solid drawing material from the viewpoint of color development and drawing properties.

As the binder used in the water-soluble solid drawing material of the present invention, sulfonic acid-modified polyvinyl acetate or a partially saponified product of sulfonic acid-modified polyvinyl acetate, which is a water-soluble resin, is used. The sulfonic acid-modified polyvinyl acetate is a polyvinyl acetate having a chemical formula represented by — (CH ₂ —CHOCOCH ₃ ) _n —, in which the OCOCH ₃ portion is partially changed to a SO ₃ X group, that is, a sulfonic acid group. Here, SO ₃ X is a sulfonic acid metal salt. Partially saponified sulfonic acid-modified polyvinyl acetate, a chemical formula _- (CH 2 -CHOCOCH _{3) -} vinyl acetate unit represented by the chemical formula _- and vinyl alcohol unit represented - (CH 2 -CHOH) The OCOCH ₃ part of the vinyl acetate unit is partly changed to a SO ₃ X group, that is, a sulfonic acid group. The combination ratio of vinyl acetate units and vinyl alcohol units is the degree of saponification. When the degree of saponification is 0, that is, when the vinyl alcohol unit is 0 mol%, sulfonic acid-modified polyvinyl acetate is obtained. Further, when the degree of saponification is less than 100, that is, less than 100 mol% in vinyl alcohol units, the characteristics of the present invention can be obtained.

  The amount of sulfonic acid-modified polyvinyl acetate or partially saponified product of sulfonic acid-modified polyvinyl acetate is preferably 0.2 to 30% by weight, particularly preferably 0.5 to 20% by weight, based on the total amount of the water-soluble solid drawing material. . When the amount is less than 0.2% by weight, the intended effect is not sufficiently obtained. When the amount is more than 30% by weight, the drawing material becomes hard, and the writing quality and colorability are likely to deteriorate.

  The saponified sulfonic acid-modified polyvinyl acetate or partially saponified sulfonic acid-modified polyvinyl acetate is a thermoplastic water-soluble resin that melts in water at the same time as it dissolves in water, and has excellent properties in dispersion of the mixture, It has a great effect as a binder and is excellent in property stability. For this reason, the reason is not clear, but as a result, the water-soluble solid drawing material has high strength, smooth writing, and stable performance with good colorability without color unevenness due to partial substitution of the sulfonic acid group. Is obtained.

  In addition to the above materials, a lubricant may be used in combination as necessary to improve the coating performance. Examples of the lubricant include conventionally known oils and fats, waxes, higher fatty acids and the like, such as wood wax, beeswax, Examples thereof include carnauba wax, montan wax, paraffin wax, stearic acid, polyethylene glycol, palmitic acid, higher alcohols, and esters thereof. Further, an anionic, nonionic or cationic surfactant may be added, and an extender may be added as an extender or filler. Specific examples include talc, clay, silica, calcium carbonate, alumina, mica, potassium titanate, glass flake, corn starch, starch, boron nitride and the like, and talc and calcium carbonate are particularly preferable. In addition, a viscosity modifier, a fungicide, an antiseptic, an antibacterial agent, a fragrance and the like may be added as necessary.

  In addition to the material used in the present invention, a water-soluble or thermoplastic resin may be used in combination as the binder, and in particular, for example, polyethylene, polyacetal, polypropylene, polystyrene, acrylic resin, polyvinyl acetate, etc. that melts with heat. These thermoplastic resins can be used alone or in combination.

  As a method for producing the water-soluble solid drawing material of the present invention, for example, the above components are mixed and heated and kneaded with a kneader, three rolls, etc., and the obtained kneaded product is directly or pelletized and injected and poured under heating. Or the method of producing a water-soluble solid drawing material by extrusion is mentioned. Next, examples of the present invention will be described. “Parts” is “parts by weight”.

Pigment Blue 15: 3 (coloring material) 10 parts Titanium oxide (coloring material) 5 parts Sulphonic acid-modified polyvinyl acetate (binding material) 10 parts Polyethylene glycol (lubricant) 10 parts Stearic acid (lubricant) 7 parts Talc (Body) Material) 58 parts After kneading with a heating kneader and a heated three roll using the above materials, a blue water-soluble solid drawing material having a diameter of 3 mm was obtained by heating extrusion. This water-soluble solid drawing material has high strength and good dispersibility, and a vivid drawing surface having no color unevenness can be obtained when traced with water.

  In Example 1, a partially saponified product of sulfonic acid-modified polyvinyl acetate (saponification degree 45) was used in place of the sulfonic acid-modified polyvinyl acetate as the binder, and the blue color was changed using the same process as in Example 1. A water-soluble solid drawing material was obtained.

(Comparative Example 1)
In Example 1, instead of the sulfonic acid-modified polyvinyl acetate as a binder, a partially saponified product of polyvinyl acetate (saponification degree 70) was used, and a blue water-soluble solid was obtained using the same process as in Example 1. A drawing material was obtained.

(Comparative Example 2)
In Example 1, instead of sulfonic acid-modified polyvinyl acetate as a binder, polyvinyl alcohol was added, and further 100 parts of water was added, and after kneading with a kneader and three rolls, extrusion was performed with an appropriate amount of water, followed by drying. A blue water-soluble solid drawing material was obtained.

  About each said Examples 1 and 2 and Comparative Examples 1 and 2, evaluation of bending strength, writing taste, and water dispersibility was performed. The results are shown in Table 1. The bending strength test is a measurement comparison of three-point bending with a span of 30 mm using a rheometer. Written taste is determined by the sense of writing. ◎ is good and ○ is slightly good. Water dispersibility is determined by visual inspection of the degree of colorant dispersion, that is, color unevenness when the colored surface is rubbed with a paintbrush containing water. ◎ is good, ○ is slightly good, and × is bad.

  As is clear from Table 1, the water-soluble solid drawing material of the present invention has stable performance such as smooth writing, no color unevenness, and vivid image lines despite its high strength. I understand.

  Since the strength is high and there is no color unevenness, stable use with high commercial value is possible.

Claims (2)

  A water-soluble solid drawing material comprising at least a coloring material and sulfonic acid-modified polyvinyl acetate.   A water-soluble solid drawing material comprising at least a coloring material and a partially saponified product of sulfonic acid-modified polyvinyl acetate.