JP5030400B2 - Coloring composition erasable by washing - Google Patents
Coloring composition erasable by washing Download PDFInfo
- Publication number
- JP5030400B2 JP5030400B2 JP2005209771A JP2005209771A JP5030400B2 JP 5030400 B2 JP5030400 B2 JP 5030400B2 JP 2005209771 A JP2005209771 A JP 2005209771A JP 2005209771 A JP2005209771 A JP 2005209771A JP 5030400 B2 JP5030400 B2 JP 5030400B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- water
- pigment
- weight
- pigment dispersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、墨汁、絵具、マーキングペン用インキ等として用いることができる着色材組成物に関する。さらに詳細には、紙に塗布した場合、高湿度下で滲みを生じることなく、また布、不織布などの繊維集合体に付着した場合に、簡単な水洗（洗濯）により消去することができる着色材組成物に関する。 The present invention relates to a colorant composition that can be used as ink, paint, marking pen ink, and the like. More specifically, a coloring material that can be erased by simple washing (washing) when applied to paper, without causing bleeding under high humidity, or when adhering to a fiber assembly such as cloth or nonwoven fabric. Relates to the composition.
従来の墨汁は、衣服などの繊維に付着した場合、乾燥すると洗濯で消去することは困難であった。一方、現在洗濯で消去できる墨汁が提案されている。
しかし、これらの着色材組成物は染料を使用したものであり、その構成要素から紙に塗布した場合、高湿度下での滲みの問題があった。 However, these colorant compositions use dyes, and when applied to paper from their constituent elements, there is a problem of bleeding under high humidity.
本発明の課題は、紙に塗布した場合、高湿度下で滲みを生じることなく、また布、不織布などの繊維集合体に付着した場合に、簡単な水洗（洗濯）により消去することができる着色材組成物を提供するところにある。 The problem of the present invention is that coloring can be eliminated by simple water washing (washing) when applied to paper, without causing bleeding under high humidity, or when adhering to a fiber assembly such as cloth or nonwoven fabric. The material composition is to be provided.
本発明は、着色顔料、顔料分散樹脂、常温（２５℃）で乾燥後に水消去性能を持つ消去性樹脂及び水を含む着色材組成物であって、
上記消去性樹脂として、鹸化度７５〜９８ｍｏｌ％、粘度が３０．０ｍＰａ・ｓｅｃ（４％水溶液、２０℃）以下のポリビニルアルコールを１０重量％以上含む、洗濯により消去可能な着色材組成物である。
The present invention is a colorant composition comprising a color pigment, a pigment dispersion resin, an erasable resin having water erasability after drying at room temperature (25 ° C.), and water,
The erasable resin is a colorant composition erasable by washing, comprising 10% by weight or more of polyvinyl alcohol having a saponification degree of 75 to 98 mol% and a viscosity of 30.0 mPa · sec (4% aqueous solution, 20 ° C.) or less. .
また本発明は、着色顔料、顔料分散樹脂と水を少なくとも配合し分散して顔料分散体を得た後、この顔料分散体に、鹸化度７５〜９８ｍｏｌ％、粘度が３０．０ｍＰａ・ｓｅｃ（４％水溶液、２０℃）以下のポリビニルアルコールを１０重量％以上含む消去性樹脂水溶液を添加することを特徴とする、洗濯により消去可能な着色材組成物の製造方法である。 In the present invention, a pigment dispersion is obtained by blending and dispersing at least a color pigment, a pigment dispersion resin, and water, and then the saponification degree is 75 to 98 mol% and the viscosity is 30.0 mPa · sec (4 % Aqueous solution, 20 ° C.) or less, an erasable resin aqueous solution containing 10% by weight or more of polyvinyl alcohol is added.
これにより、染料を用いていないので高湿度下での滲みなどの問題が生ずることがなくなって衣服などの繊維に上記着色材組成物が付着しても、洗濯による消去性が向上する。
従って、墨汁、サインペン用インキ、マーキングペン用インキなどの粘度が２００ｍＰａ・ｓ以下の着色材組成物のほか、高粘度の絵の具等の着色材組成物に適用して、洗濯により消去可能な着色材組成物を提供することができる。
Thereby, since no dye is used, problems such as bleeding under high humidity do not occur, and even if the colorant composition adheres to fibers such as clothes, the erasability by washing is improved.
Therefore, in addition to colorant compositions having a viscosity of 200 mPa · s or less, such as ink for ink, sign pen ink, marking pen ink, etc., colorants that can be erased by washing can be applied to colorant compositions such as high-viscosity paints. A composition can be provided.
＜着色顔料＞
本発明で用いられる着色顔料は、粒径が細かく、着色効果を有することが求められる。具体的には粒径０．０５〜０．５μｍの顔料が好ましい。例えば、カーボンブラック、アニリンブラック、鉄黒、モノアゾ、アンスラキノン、キナクリドン、フタロシアニン、群青、紺青、アンスラキノンを用いることができる。
<Coloring pigment>
The color pigment used in the present invention is required to have a fine particle size and a coloring effect. Specifically, a pigment having a particle size of 0.05 to 0.5 μm is preferable. For example, carbon black, aniline black, iron black, monoazo, anthraquinone, quinacridone, phthalocyanine, ultramarine blue, bitumen, and anthraquinone can be used.
着色顔料の配合量は、着色材組成物全量に対して１〜１０重量％、好ましくは２〜７重量％である。着色顔料が着色材組成物全量に対して１重量％未満の場合は、発色が低下する。着色顔料が着色材組成物全量に対して１０重量％を越える場合は、粘度が上がって筆記や描画し難くなるほか、繊維に付着した後落ちにくくなる。 The blending amount of the color pigment is 1 to 10% by weight, preferably 2 to 7% by weight, based on the total amount of the colorant composition. When the color pigment is less than 1% by weight based on the total amount of the colorant composition, the color development is lowered. When the color pigment exceeds 10% by weight with respect to the total amount of the colorant composition, the viscosity increases and it becomes difficult to write or draw, and it is difficult to drop after adhering to the fiber.
＜水消去性樹脂＞
本発明では、後添加樹脂として水消去性樹脂を用いる。そして、常温（２５℃）で乾燥後に水に対する溶解性が高く、粘度がある程度低い水消去性能を持つ水溶性樹脂を用いることが重要である。この水消去性樹脂としては、鹸化度７５ｍｏｌ％以上〜９８ｍｏｌ％未満、粘度が３０．０ｍＰａ・ｓｅｃ（４％水溶液、２０℃）以下のポリビニルアルコールを用いる。例えば、クラレ社製、商品名「PVA403」を挙げることができる。鹸化度７５ｍｏｌ％以上〜９８ｍｏｌ％未満、好ましくは７８ｍｏｌ％以上〜８２ｍｏｌ％未満、粘度が３０．０ｍＰａ・ｓｅｃ（４％水溶液、２０℃）以下、好ましくは１０ｍＰａ・ｓｅｃ（４％水溶液、２０℃）以下、及び２ｍＰａ・ｓｅｃ（４％水溶液、２０℃）以上のポリビニルアルコールを用いることにより、適度な粘性を保って使用感が良好でありながら、洗濯による水消去性が良好な着色材組成物を提供することができる。鹸化度７５ｍｏｌ％未満では、粘度が高くなりすぎて使用感が低下する。鹸化度９８ｍｏｌ％を超えると、常温（２５℃）で乾燥した塗膜塗膜に対し洗濯による水消去性が不十分である。また、粘度が３０．０ｍＰａ・ｓｅｃ（４％水溶液、２０℃）を超えても、粘度が高くなりすぎて使用感が低下する。
<Water erasable resin>
In the present invention, a water erasable resin is used as the post-added resin. It is important to use a water-soluble resin having a water erasing performance that is highly soluble in water after drying at room temperature (25 ° C.) and has a low viscosity. As this water erasable resin, polyvinyl alcohol having a saponification degree of 75 mol% or more and less than 98 mol% and a viscosity of 30.0 mPa · sec (4% aqueous solution, 20 ° C.) or less is used. For example, a product name “PVA403” manufactured by Kuraray Co., Ltd. can be mentioned. Degree of saponification 75 mol% or more to less than 98 mol%, preferably 78 mol% or more to less than 82 mol%, viscosity is 30.0 mPa · sec (4% aqueous solution, 20 ° C.) or less, preferably 10 mPa · sec (4% aqueous solution, 20 ° C.) By using polyvinyl alcohol having a viscosity of 2 mPa · sec (4% aqueous solution, 20 ° C.) or higher, a colorant composition having good water erasability by washing while maintaining an appropriate viscosity and good usability. Can be provided. If the degree of saponification is less than 75 mol%, the viscosity becomes too high and the feeling in use decreases. If the degree of saponification exceeds 98 mol%, the water erasability by washing is insufficient for the coating film dried at room temperature (25 ° C.). Moreover, even if a viscosity exceeds 30.0 mPa * sec (4% aqueous solution, 20 degreeC), a viscosity will become high too much and a usability | use_condition will fall.
一方、本発明で用いる上記ポリビニルアルコールは重合度１００〜６００、好ましくは３５０〜４５０のものを用いることが好ましい。このポリビニルアルコールは、着色材組成物全量に対して１０重量％を超え〜２７重量％未満、好ましくは１２重量％以上〜２６重量％以下含有する。このポリビニルアルコールが１０重量％以下では、洗濯による水消去性が低下し、２７重量％以上では粘度が高くなり、使用感が低下する。 On the other hand, the polyvinyl alcohol used in the present invention preferably has a polymerization degree of 100 to 600, preferably 350 to 450. This polyvinyl alcohol contains more than 10% by weight and less than 27% by weight, preferably 12% by weight or more and 26% by weight or less, based on the total amount of the colorant composition. If the polyvinyl alcohol is 10% by weight or less, the water erasability by washing is lowered, and if it is 27% by weight or more, the viscosity is increased and the feeling of use is lowered.
＜顔料分散樹脂＞
前記顔料を分散させる顔料分散樹脂としては、水に溶解可能で、着色顔料を顔料分散体として分散させ、かつ分散安定性に優れる水溶性樹脂を含有することが好ましい。具体的には、カルボキシメチルセルロース、アラビヤガム、デキストリン、スチレンアクリル共重合体、スチレンマレイン酸共重合体、ポリアクリル酸、ポリビニルアルコールを例示することができ、スチレンアクリル共重合体、スチレンマレイン酸共重合体、エチレンマレイン酸共重合体、ポリビニルアルコールが好適に用いられる。なお、顔料分散樹脂としてポリビニルアルコールを用いる場合は前記後添加する水消去性樹脂と異なり格別限定されず、顔料を分散し且つ前記の通りの水溶性樹脂であれば採用することができる。
<Pigment dispersion resin>
The pigment-dispersed resin for dispersing the pigment preferably contains a water-soluble resin that is soluble in water, disperses the colored pigment as a pigment dispersion, and is excellent in dispersion stability. Specific examples include carboxymethyl cellulose, gum arabic, dextrin, styrene acrylic copolymer, styrene maleic acid copolymer, polyacrylic acid, and polyvinyl alcohol. Styrene acrylic copolymer, styrene maleic acid copolymer , Ethylene maleic acid copolymer and polyvinyl alcohol are preferably used. In addition, when using polyvinyl alcohol as a pigment dispersion resin, unlike the water erasable resin added later, it is not particularly limited, and any water-soluble resin as described above can be employed as long as it disperses the pigment.
この着色顔料は、この顔料分散樹脂と水とを含む顔料分散体として用いることができる。この顔料分散樹脂の配合量は、着色材組成物全量に対して０．１〜１０重量％、好ましくは０．５〜１．５重量％である。この顔料分散樹脂が０．１重量％未満であれば、経時で顔料の凝集が起こりやすくなり、１０重量％を超えると、顔料分散時にゲル化し易くなる。 The colored pigment can be used as a pigment dispersion containing the pigment dispersion resin and water. The amount of the pigment-dispersed resin is 0.1 to 10% by weight, preferably 0.5 to 1.5% by weight, based on the total amount of the colorant composition. If the pigment-dispersed resin is less than 0.1% by weight, the aggregation of the pigment is likely to occur with time, and if it exceeds 10% by weight, gelation is likely to occur when the pigment is dispersed.
この顔料分散樹脂としては酸価１１０〜２２０の樹脂、好ましくは酸価２１０〜２２０の樹脂を好適に用いることができる。例えば、酸価が１１０〜２２０、好ましくは酸価２１０〜２２０である、スチレンアクリル共重合体、スチレンマレイン酸共重合体、エチレンマレイン酸共重合体などを挙げることができる。そして、前記着色顔料Ｐと前記顔料分散樹脂及び水消去性樹脂から構成される水溶性樹脂Ｒとの重量比（Ｐ／Ｒ比）が１／１〜１／３０とすることにより、着色顔料含有の着色材組成物において洗濯消去性を更に向上することが可能となる。なお、酸価は常法による測定される。 As the pigment dispersion resin, a resin having an acid value of 110 to 220, preferably a resin having an acid value of 210 to 220 can be suitably used. Examples thereof include styrene acrylic copolymers, styrene maleic acid copolymers, and ethylene maleic acid copolymers having an acid value of 110 to 220, preferably an acid value of 210 to 220. The weight ratio (P / R ratio) between the colored pigment P and the water-soluble resin R composed of the pigment dispersion resin and the water erasable resin is set to 1/1 to 1/30. In this colorant composition, it is possible to further improve the washing erasability. The acid value is measured by a conventional method.
また前記着色顔料Ｐと前記顔料分散樹脂Ａの重量比（Ｐ／Ａ比）は１０／１〜１．５／１、好ましくは５／１〜２／１の配合比とすることにより、着色顔料含有の着色材組成物において洗濯消去性を更に向上することが可能となる。
＜その他＞
The weight ratio (P / A ratio) between the color pigment P and the pigment dispersion resin A is 10/1 to 1.5 / 1, preferably 5/1 to 2/1. It becomes possible to further improve the washing erasability in the contained colorant composition.
<Others>
また、本発明では、更に加えて、前記分散された着色顔料の顔料分散体に洗濯消去性を向上させる水溶性樹脂Ｂとして、特に酸価が２００〜２６０、好ましくは２００〜２４０の水溶性樹脂を好適に用いることができる。例えば、酸価が２００〜２６０、好ましくは２００〜２４０である、スチレンアクリル共重合体、スチレンマレイン酸共重合体、エチレンマレイン酸共重合体を挙げることができる。 Further, in the present invention, the water-soluble resin B having an acid value of 200 to 260, preferably 200 to 240 is particularly used as the water-soluble resin B for improving the washing erasability in the pigment dispersion of the dispersed color pigment. Can be suitably used. Examples thereof include styrene acrylic copolymers, styrene maleic acid copolymers, and ethylene maleic acid copolymers having an acid value of 200 to 260, preferably 200 to 240.
前記水溶性樹脂Ｂは、着色材組成物全量に対して好ましくは１〜３０重量％、より好ましくは１０〜２５重量％含有する。 The water-soluble resin B is preferably contained in an amount of 1 to 30% by weight, more preferably 10 to 25% by weight, based on the total amount of the colorant composition.
このように、前記特定のポリビニルアルコールに加えて、酸価１１０〜２２０の樹脂で着色顔料を分散し、酸価２００〜２６０の樹脂Ｂで水溶性を増大させることにより、着色顔料含有の着色材組成物において洗濯消去性をさらに一層向上することが可能となる。 In this way, in addition to the specific polyvinyl alcohol, the color pigment is dispersed with a resin having an acid value of 110 to 220, and the water solubility is increased with the resin B having an acid value of 200 to 260. It becomes possible to further improve the washing erasability in the composition.
なお、前記水溶性樹脂樹脂Ｂと前記顔料分散体樹脂Ａの重量比（Ｂ／Ａ）は０．９〜３０が好ましい。このような範囲とすることにより、着色顔料が分散される樹脂Ａと、水により洗濯消去性を発現する樹脂Ｂとの相乗作用を一層発揮することができる。 In addition, as for the weight ratio (B / A) of the said water-soluble resin resin B and the said pigment dispersion resin A, 0.9-30 are preferable. By setting it as such a range, the synergistic effect of resin A in which a color pigment is disperse | distributed and resin B which expresses washing erasability with water can be exhibited further.
また、水による洗濯消去性を更に増大させるために、前記水溶性樹脂、特にカルボン酸を有する水溶性樹脂Ｂを加える場合、これが水に溶解し、アルカリ性を呈し、中和したこれらの樹脂が塗布又は筆記して乾燥した後でも水に溶解する中和剤を含ませることが好ましい。具体的には、スチレンアクリル共重合体、スチレンマレイン酸共重合体、エチレンマレイン酸共重合体の群から選ばれる水溶性樹脂Ｂである場合、上記中和剤を含ませることが好ましい。中和剤としては、無機塩類、アルカノールアミン類、アルキルアミン類及びジアミン類の群から選ばれる。無機塩類としては、水酸化リチウム、水酸化ナトリウム、水酸化カリウムなどが挙げられ、アルカノールアミン類としてはモノエタノールアミン、ジエタノールアミン、トリエタノールアミン、モノイソプロパノールアミン、ジイソパノールアミン、トリイソパノールアミンなどが挙げられ、ジアミン類としてはエチレンジアミン、プロピレンジアミン、Ｎ，Ｎ，Ｎ’，Ｎ’−テトラメチルエチレンジアミンが挙げられる。特に、上記アルキルアミン類、無機塩類が中和した前記樹脂が乾燥した後でも、水による消去性が高く好ましい。なお、中和剤としてアンモニアを用いると、塗膜又は筆跡の乾燥の際、アンモニアが揮発するため、洗濯消去性が低下しやすい。 Further, in order to further increase the washing erasability with water, when adding the water-soluble resin, particularly the water-soluble resin B having carboxylic acid, it is dissolved in water, becomes alkaline, and these neutralized resins are applied. Alternatively, it is preferable to include a neutralizing agent that dissolves in water even after writing and drying. Specifically, when the water-soluble resin B is selected from the group consisting of a styrene acrylic copolymer, a styrene maleic acid copolymer, and an ethylene maleic acid copolymer, the neutralizing agent is preferably included. The neutralizing agent is selected from the group of inorganic salts, alkanolamines, alkylamines and diamines. Examples of inorganic salts include lithium hydroxide, sodium hydroxide, and potassium hydroxide. Examples of alkanolamines include monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, diisopanolamine, and triisopanolamine. Examples of diamines include ethylenediamine, propylenediamine, and N, N, N ′, N′-tetramethylethylenediamine. In particular, even after the resin neutralized with the alkylamines and inorganic salts is dried, the erasability with water is high, which is preferable. In addition, when ammonia is used as a neutralizing agent, when the coating film or handwriting is dried, the ammonia is volatilized, so that the washing erasability tends to be lowered.
前記中和剤は、着色材組成物全量に対して０．１〜２０重量％、好ましくは１．０〜１５重量％含有する。
その他必要に応じて、グリセリン、プロピレングリコール、エチレングリコール等の多価アルコールや、防腐防黴剤を添加しても良い。
The neutralizing agent is contained in an amount of 0.1 to 20% by weight, preferably 1.0 to 15% by weight, based on the total amount of the colorant composition.
In addition, you may add polyhydric alcohols, such as glycerol, propylene glycol, and ethylene glycol, and antiseptic / antifungal agents as needed.
なお、本発明の着色材組成物は、着色顔料、顔料分散体樹脂と水を少なくとも配合し分散してまず顔料分散体を得た後、この顔料分散体に後添加で前記特定のポリビニルアルコールの水溶液を添加することによって得ることができる。また、前記その他の水溶性樹脂をさらに加える場合は、前記特定のポリビニルアルコールの水溶液とともに後添加して得ることができる。 The colorant composition of the present invention is obtained by mixing at least a color pigment, a pigment dispersion resin, and water to obtain a pigment dispersion, and then adding the specific polyvinyl alcohol to the pigment dispersion by post-addition. It can be obtained by adding an aqueous solution. Moreover, when adding the said other water-soluble resin further, it can add after obtaining with the aqueous solution of the said specific polyvinyl alcohol.
表１に示す組成にて、着色顔料、顔料分散樹脂及び水を含む顔料分散体、ＰＶＡ及び水を含む樹脂液、水、必要に応じて顔料濡れ剤を配合し、ビーズミル（ダイノーミル：シンマルエンタープライゼス社製）にて１時間分散を行う。次に、この顔料分散体にポリビニルアルコールの水溶液を添加し３０分攪拌して、墨汁の着色材組成物を得る。これらについて、鹸化度及び粘度を測定した。試験サンプル数はｎ＝３である。 In the composition shown in Table 1, a pigment dispersion containing a color pigment, a pigment dispersion resin and water, a resin liquid containing PVA and water, water, and a pigment wetting agent as necessary are blended, and a bead mill (Dynomill: Shinmaru Enterprise) For 1 hour. Next, an aqueous solution of polyvinyl alcohol is added to the pigment dispersion and stirred for 30 minutes to obtain a ink coloring material composition. About these, the saponification degree and the viscosity were measured. The number of test samples is n = 3.
（表注）
１）商品名：Monarch800（カーボンブラック／CABOT社製） ２０重量％、ＰＶＡ４０３（クラレ社製） ４重量％、残部が水の顔料分散体
２）商品名：Monarch800（カーボンブラック／ＣＡＢＯＴ社製）：２０重量％、Ｊｏｎｃｒｙ１678（ジョンソンポリマー社製） ４重量％、樹脂中和剤（水酸化ナトリウム） ０．５重量％、残部が水の顔料分散体
３）商品名：シムラファーストレッド４１２７（Ｐ.Ｒ.２６７／大日本インキ社製） ２０重量％、ＰＶＡ４０３（クラレ社製） ４重量％、残部が水の顔料分散体
４）商品名：ファーストゲンブルーＴＧＲ（Ｐ.Ｂ.１５:３／大日本インキ社製）２０重量％、ＰＶＡ４０３（クラレ社製） ４重量％、残部が水の顔料分散体
５）ＰＶＡ４０３（ＰＶＡ／クラレ社製）の３０重量％水溶液
６）Ｂ−１７（ＰＶＡ／デンカ社製）の２０重量％水溶液
７）Ｃ−５００（ＰＶＡ／日本合成社製）の２０重量％水溶液
８）ＰＶＡ１０５（ＰＶＡ／クラレ社製）の３０重量％水溶液
９）Ｂ−３３（ＰＶＡ／デンカ社製）の２０重量％水溶液
１０）前記１）〜４）の顔料分散体中の顔料の含有量
１１）前記５）〜９）のＰＶＡ樹脂液において鹸化度９８ｍｏｌ％未満のＰＶＡの配合量
１２）前記５）〜９）のＰＶＡ樹脂液において鹸化度９８ｍｏｌ％以上のＰＶＡの配合量
(Table note)
1) Product name: Monarch800 (carbon black / manufactured by CABOT) 20% by weight, PVA403 (manufactured by Kuraray) 4% by weight, the balance being a pigment dispersion of water 2) Product name: Monarch800 (carbon black / manufactured by CABOT): 20% by weight, Joncry 1678 (manufactured by Johnson Polymer Co., Ltd.) 4% by weight, resin neutralizer (sodium hydroxide) 0.5% by weight, the balance being water pigment dispersion 3) Product name: Shimura First Red 4127 (PR .267 / manufactured by Dainippon Ink Co., Ltd.) 20% by weight, PVA403 (manufactured by Kuraray Co., Ltd.) 4% by weight, the balance being water pigment dispersion 4) Product name: Fast Gen Blue TGR (P.B.15: 3 / Dainippon) 5% by weight of PVA403 (manufactured by Kuraray Co., Ltd.) 5) 30% by weight aqueous solution of PVA403 (manufactured by PVA / Kuraray Co., Ltd.) 6) B-17 (PV) / 20% by weight aqueous solution of Denka) 7) 20% by weight aqueous solution of C-500 (PVA / Nihon Gosei) 8) 30% by weight aqueous solution of PVA105 (PVA / Kuraray) 9) B-33 (PVA) 10) 20% by weight aqueous solution of Denka) 10) Content of pigment in the pigment dispersions of 1) to 4) 11) Formulation of PVA having a saponification degree of less than 98 mol% in the PVA resin liquids of 5) to 9) Amount 12) A blending amount of PVA having a saponification degree of 98 mol% or more in the PVA resin liquids 5) to 9).
＜鹸化度の測定方法＞
上記実施例及び比較例を含め、本発明における鹸化度はＪＩＳ Ｋ ６７２６に準拠して測定した。
<Measurement method of saponification degree>
The saponification degree in the present invention was measured according to JIS K 6726, including the above Examples and Comparative Examples.
＜粘度の測定方法＞
上記実施例及び比較例を含め、本発明における粘度はＪＩＳ Ｋ ６７２６に準拠して測定した。
<Measurement method of viscosity>
Viscosity in the present invention was measured according to JIS K 6726, including the examples and comparative examples.
次に、綿ブロード（晒）の試験布に水を含まない画筆（平筆４号）を用いて、この各試験サンプルの墨汁組成物を塗布し、室温で指触乾燥するまでそれぞれ放置した。その後、乾燥後の各試験サンプルを洗濯機でｐＨが弱アルカリ性の合成洗剤を使用して（洗濯槽の水量に対して０．２重量％）２０℃で１５分間洗濯し、１５分間水洗した。乾燥後に各試験サンプルを目視で観察し、評価した。 Next, the ink composition of each test sample was applied to a cotton broad (bleached) test cloth using a paint brush that does not contain water (Flat Brush No. 4) and left to stand until it was dry to the touch at room temperature. Thereafter, each test sample after drying was washed for 15 minutes at 20 ° C. using a synthetic detergent having a weak pH (0.2% by weight based on the amount of water in the washing tub) in a washing machine, and then washed with water for 15 minutes. Each test sample was visually observed and evaluated after drying.
＜消去性評価＞
○が合格、△×が不合格である。
○：汚れが除去されている。
△：色、筆跡がはっきりわかる。
×：全く落ちない。
<Eraseability evaluation>
○ is acceptable and Δ × is unacceptable.
○: Dirt is removed.
Δ: Color and handwriting clearly understood.
X: It does not fall at all.
＜書き味評価＞
○が合格、△×が不合格である。
○：非常になめらかである。
△：もたつきがある。
×：もたつきがひどく、ほとんど書けない。
<Writing evaluation>
○ is acceptable and Δ × is unacceptable.
○: Very smooth.
(Triangle | delta): There is slack.
X: The stickiness is bad and almost cannot be written.
表１より、本実施例の着色材組成物であれば、染料を用いていないので高湿度下での滲みなどの問題が生ずることなく、誤って衣服などの繊維に上記着色材組成物が付着しても、洗濯による消去性が向上する。また、書き味も良好である。 From Table 1, since the dye composition is not used in the colorant composition of this example, the above colorant composition is mistakenly attached to fibers such as clothes without causing problems such as bleeding under high humidity. Even so, the erasability by washing is improved. Moreover, the writing quality is also good.
本発明の着色材組成物は、墨汁（墨液）、絵具のほか、マーキングペン用インキ等の水性インキ組成物として用いることができる。
The colorant composition of the present invention can be used as a water-based ink composition such as ink for marking pens in addition to ink (ink ink) and paint.
Claims (3)
顔料分散樹脂、
常温（２５℃）で乾燥後に水消去性能を持つ消去性樹脂及び
水
を含む着色材組成物であって、
前記着色顔料は、前記顔料分散樹脂と水とを含む顔料分散体として用いられ、
前記消去性樹脂は、後添加樹脂として用いられ、
前記消去性樹脂は、
鹸化度７５〜９８ｍｏｌ％、
粘度が３０．０ｍＰａ・ｓｅｃ（４％水溶液、２０℃）以下の
ポリビニルアルコールを着色材組成物全量に対して１０重量％以上、２７重量％未満を
含む消去性樹脂水溶液からなる洗濯により消去可能な墨汁。 Coloring pigments,
Pigment dispersion resin,
A colorant composition comprising an erasable resin having water erasing performance after drying at room temperature (25 ° C.) and water,
The colored pigment is used as a pigment dispersion containing the pigment dispersion resin and water,
The erasable resin is used as a post-addition resin,
The erasable resin is
Saponification degree 75-98 mol%,
Laundry made of an erasable resin aqueous solution containing polyvinyl alcohol having a viscosity of 30.0 mPa · sec (4% aqueous solution, 20 ° C) or less, containing 10% by weight or more and less than 27 % by weight based on the total amount of the colorant composition. Can be erased by ink .
この顔料分散体に、鹸化度７５〜９８ｍｏｌ％、粘度が３０．０ｍＰａ・ｓｅｃ（４％水溶液、２０℃）以下のポリビニルアルコールを着色材組成物全量に対して１０重量％以上、２７重量％未満を含む消去性樹脂水溶液を添加することを特徴とする、洗濯により消去可能な墨汁の製造方法。
After coloring pigment, pigment dispersion resin and water are blended and dispersed to obtain a pigment dispersion,
To this pigment dispersion, polyvinyl alcohol having a saponification degree of 75 to 98 mol% and a viscosity of 30.0 mPa · sec (4% aqueous solution, 20 ° C.) or less is 10% by weight or more and less than 27 % by weight based on the total amount of the colorant composition. A method for producing ink that can be erased by washing , comprising adding an aqueous erasable resin solution containing the shampoo .