JP2009081038A - Nickel-hydrogen secondary battery - Google Patents
Nickel-hydrogen secondary battery Download PDFInfo
- Publication number
- JP2009081038A JP2009081038A JP2007249197A JP2007249197A JP2009081038A JP 2009081038 A JP2009081038 A JP 2009081038A JP 2007249197 A JP2007249197 A JP 2007249197A JP 2007249197 A JP2007249197 A JP 2007249197A JP 2009081038 A JP2009081038 A JP 2009081038A
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- oxide particles
- negative electrode
- nickel
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明はニッケル水素二次電池に関する。 The present invention relates to a nickel metal hydride secondary battery.
ニッケル水素二次電池は、種々の用途に用いられており、例えば、電子・電気機器や電動工具のバッテリに用いられている。
ニッケル水素二次電池は、容器内に収容された正極、負極、及びアルカリ電解液を有する。正極は、水酸化ニッケル若しくは高次水酸化ニッケルの粒子を正極活物質として含み、負極は、負極活物質としての水素を吸蔵・放出可能な水素吸蔵合金の粒子を含む。
Nickel metal hydride secondary batteries are used for various applications, for example, batteries for electronic / electrical equipment and electric tools.
A nickel metal hydride secondary battery has a positive electrode, a negative electrode, and an alkaline electrolyte housed in a container. The positive electrode includes particles of nickel hydroxide or higher-order nickel hydroxide as a positive electrode active material, and the negative electrode includes particles of a hydrogen storage alloy capable of occluding and releasing hydrogen as the negative electrode active material.
そして正極には、酸素過電圧の低下を抑制して高温下での充電効率を向上すべく、希土類酸化物の粉末を添加することが知られている(例えば特許文献1参照)。また負極には、水素吸蔵合金粒子の耐食性を高めてサイクル特性を向上すべく、希土類酸化物の粉末を添加することが知られている(例えば特許文献2参照)。
ところで近年、環境意識の高まりから、鉛蓄電池からニッケル水素二次電池への需要のシフトが進行している。具体的には、ニッケル水素二次電池がバックアップ用途や防災関連用途にも使用されている。
バックアップ用途や防災関連用途への適用に伴い、従来のニッケル水素二次電池には、長期信頼性、とりわけ高温下での連続充電特性の更なる向上が求められている。
By the way, in recent years, a shift in demand from lead-acid batteries to nickel-metal hydride secondary batteries has progressed due to an increase in environmental awareness. Specifically, nickel metal hydride secondary batteries are also used for backup applications and disaster prevention related applications.
With the application to backup use and disaster prevention related use, the conventional nickel metal hydride secondary battery is required to further improve long-term reliability, in particular, continuous charge characteristics at high temperatures.
本発明は上述の事情に基づいてなされたもので、その目的とするところは、高温下での良好な充電効率が確保されるとともに、高温下での連続充電特性に優れたニッケル水素二次電池を提供することにある。 The present invention has been made based on the above-mentioned circumstances, and its object is to ensure a good charging efficiency at high temperatures and a nickel-hydrogen secondary battery excellent in continuous charging characteristics at high temperatures. Is to provide.
上記の目的を達成すべく、本発明者らは種々の検討を重ね、正極及び負極に添加される酸化物粒子における炭素濃度が高温下での連続充電特性に影響を与えることを見出し、本発明に想到した。
すなわち、本発明によれば、容器内に正極、負極及びアルカリ電解液を備えるニッケル水素二次電池において、前記正極は、水酸化ニッケル若しくは高次水酸化ニッケルを含有する正極活物質粒子と、Y、Yb、Tm、Er、Gd及びLuよりなる群から選択された少なくとも1種の添加元素及び炭素を含有する正極用酸化物粒子とを含み、前記負極は、水素吸蔵合金を含有する負極活物質粒子と、前記正極用酸化物粒子が含有する前記添加元素と同じ種類の添加元素を少なくとも含有する負極用酸化物粒子とを含み、前記正極用酸化物粒子における炭素の質量濃度は、前記負極用酸化物粒子における炭素の質量濃度よりも大であることを特徴とするニッケル水素二次電池が提供される(請求項1)。
In order to achieve the above object, the present inventors have made various studies and found that the carbon concentration in the oxide particles added to the positive electrode and the negative electrode affects the continuous charging characteristics at high temperature. I came up with it.
That is, according to the present invention, in a nickel metal hydride secondary battery including a positive electrode, a negative electrode, and an alkaline electrolyte in a container, the positive electrode includes positive electrode active material particles containing nickel hydroxide or higher-order nickel hydroxide, and Y , Yb, Tm, Er, Gd and Lu, and at least one additive element selected from the group consisting of oxide particles for positive electrode containing carbon and the negative electrode containing a hydrogen storage alloy Particles and a negative electrode oxide particle containing at least the same type of additional element as the additional element contained in the positive electrode oxide particle, and the mass concentration of carbon in the positive electrode oxide particle is A nickel-metal hydride secondary battery characterized by having a mass concentration higher than that of carbon in oxide particles is provided.
好ましくは、前記正極用酸化物粒子及び負極用酸化物粒子は、前記添加元素としてYを含有する(請求項2)。 Preferably, the positive electrode oxide particles and the negative electrode oxide particles contain Y as the additional element (Claim 2).
本発明の請求項1のニッケル水素二次電池では、正極用酸化物粒子における炭素の質量濃度が、負極用酸化物粒子における炭素の質量濃度よりも大である。この結果として、このニッケル水素二次電池は、高温下での良好な充電効率が確保されているのみならず、高温下での連続充電特性にも優れ、長寿命である。それ故、このニッケル水素二次電池は、バックアップ用途や防災関連用途に好適する。
In the nickel metal hydride secondary battery according to
請求項2のニッケル水素二次電池は、正極用酸化物粒子及び負極用酸化物粒子がYを含むことにより、高温下での連続充電特性において一層優れている。
The nickel metal hydride secondary battery according to
図1は、本発明の一実施形態に係るニッケル水素二次電池を示す。
ニッケル水素二次電池は、有底円筒形状の外装缶1を容器として備え、外装缶1の中に電極群2が収容されている。電極群2は、正極3及び負極4を、セパレータ5を介して渦巻状に巻回してなり、電極群2の最外周には、その渦巻き方向でみて負極4の外端側の部位が配置され、負極4が外装缶1の内周壁と電気的に接続されている。また、外装缶1の中には、図示しないアルカリ電解液が収容され、アルカリ電解液としては、例えば水酸化カリウム水溶液と、水酸化ナトリウム水溶液や水酸化リチウム水溶液などとを混合したものを用いることができる。
FIG. 1 shows a nickel metal hydride secondary battery according to an embodiment of the present invention.
The nickel metal hydride secondary battery includes a bottomed cylindrical
外装缶1の開口内には、リング状の絶縁性ガスケット6を介して、中央にガス抜き孔7を有する円形の蓋板8が配置されている。これら絶縁性ガスケット6及び蓋板8は、かしめ加工された外装缶1の開口縁によって固定されている。電極群2の正極3と蓋板8の内面との間には、これらの間を電気的に接続する正極リード9が配置されている。一方、蓋板8の外面には、ガス抜き孔7を閉塞するようにゴム製の弁体10が配置され、更に、弁体10を囲むようにフランジ付きの円筒形状の正極端子11が取り付けられている。
A circular lid plate 8 having a gas vent hole 7 in the center is disposed in the opening of the
また、外装缶1の開口縁上には環状の絶縁板12が配置され、正極端子11は絶縁板12を貫通して突出している。符号13は、外装チューブに付されており、外装チューブ13は絶縁板12の周縁、外装缶1の外周面及び底壁周縁を被覆している。
電極群2中の正極3は、例えば非焼結式ニッケル電極であり、導電性の正極基板と、正極基板に保持された正極合剤とからなる。正極基板としては、例えば、ニッケルめっきが施された網状、スポンジ状、繊維状、フエルト状の金属多孔体を用いることができる。
An annular
The
正極合剤は、図1の一方の円内に概略的に示したように、主成分としての正極活物質粒子14、正極用酸化物粒子15及び結着剤16を少なくとも含み、正極活物質粒子14及び正極用酸化物粒子15は、結着剤16によって正極基板に固定されている。
結着剤16としては、例えば、カルボキシメチルセルロース、メチルセルロース、PTFEディスパージョン、HPCディスパージョンなどを用いることができる。
As schematically shown in one circle of FIG. 1, the positive electrode mixture includes at least positive electrode
As the
正極活物質粒子14は必須の主成分として水酸化ニッケル系化合物を含む。水酸化ニッケル系化合物としては、水酸化ニッケル、ニッケルの平均価数が2価よりも大の水酸化ニッケル(高次水酸化ニッケル)、又は水酸化ニッケルと高次水酸化ニッケルの混合物を用いることができる。また、正極活物質粒子14は、任意の添加成分として、例えば亜鉛やコバルトを含んでいてもよく、水酸化ニッケル系化合物と、亜鉛やコバルトとは、固溶体を形成していてもよい。
The positive electrode
なお、水酸化ニッケル系化合物は、電池反応によって変化し、電池が放電状態にあるときに水酸化ニッケル又は高次水酸化ニッケルの状態となる。
正極活物質粒子14の表面の少なくとも一部若しくは全部は、好ましくは、被覆層17で覆われ、被覆層17は、コバルト化合物を主成分としている。そして、コバルト化合物は、乱れた結晶構造を有し且つコバルトの平均価数が2価以上であるのが好ましい。
The nickel hydroxide-based compound changes depending on the battery reaction, and becomes nickel hydroxide or higher-order nickel hydroxide when the battery is in a discharged state.
At least a part or all of the surface of the positive electrode
上述した正極3は、例えば、正極活物質粒子14の粉末、正極用酸化物粒子15の粉末、結着剤16、及び水を混練して正極用スラリを調製し、この正極用スラリが塗着・充填されたスラリ付きの正極基板を、スラリの乾燥を経てから圧延・裁断することにより作製可能である。
電極群2中の負極4は(水素吸蔵合金電極)は、導電性の負極基板と、負極基板に保持された負極合剤とからなり、負極基板としては、例えば、パンチングメタルを用いることができる。
In the
The negative electrode 4 (hydrogen storage alloy electrode) in the
負極合剤は、図1の他方の円内に概略的に示したように、水素吸蔵合金粒子20、負極用酸化物粒子21及び結着剤22を少なくとも含み、必要に応じて導電剤を更に含む。なお、水素吸蔵合金は負極活物質である水素を吸蔵・放出可能であるため、本明細書では、水素吸蔵合金粒子20のことを負極活物質粒子ともいう。
水素吸蔵合金粒子20としては、例えば、結晶構造がAB5型のものや、AB5型とAB2型とを合わせたような超格子型のものを用いることができる。結着剤22としては、例えば、カルボキシメチルセルロース、メチルセルロース、PTFEディスパージョン、HPC、ポリアクリル酸ナトリウムなどを単独若しくは混合して用いることができる。また、導電剤としては、例えばカーボン粉末などを用いることができる。
As schematically shown in the other circle of FIG. 1, the negative electrode mixture includes at least hydrogen
As the hydrogen
上述した負極4は、水素吸蔵合金粒子20の粉末、負極用酸化物粒子21の粉末、結着剤22、水、及び必要に応じて配合される導電剤から成る負極用スラリを調整し、負極スラリが塗着された負極基板を、乾燥を経てから圧延・裁断して作製することができる。
ここで、正極3の正極用酸化物粒子15は、Y(イットリウム)、Yb(イッテルビウム)、Tm(ツリウム)、Er(エルビウム)、Gd(ガドリニウム)及びLu(ルテチウム)よりなる群から選択された少なくとも1種の添加元素を主成分として含むとともに、炭素を不純物として含有する酸化物である。例えば、正極用酸化物粒子15における炭素の質量濃度は、0.05wt.%超0.4wt.%以下の範囲にある。
The
Here, the positive
一方、負極4の負極用酸化物粒子21は、正極用酸化物粒子15に含まれる添加元素と同一種類の添加元素を主成分として少なくとも含む酸化物である。すなわち、負極用酸化物粒子21も、Y(イットリウム)、Yb(イッテルビウム)、Tm(ツリウム)、Er(エルビウム)、Gd(ガドリニウム)及びLu(ルテチウム)よりなる群から選択された少なくとも1種の添加元素を含むが、正極用酸化物粒子15及び負極用酸化物粒子21は、同一種類の添加元素を含む。好ましくは、正極用酸化物粒子15及び負極用酸化物粒子21は、添加元素としてYを含む。
On the other hand, the negative
そして、負極用酸化物粒子21は、添加元素の他に不純物として炭素を含有していてもよいが、正極用酸化物粒子15における炭素の質量濃度が、平均して、負極用酸化物粒子21における炭素の質量濃度よりも大きくなるよう、負極用酸化物粒子21における炭素の質量濃度は制限される。例えば、負極用酸化物粒子21における炭素の質量濃度は、0.05wt.%以上0.4wt.%未満の範囲にある。
The negative
正極用酸化物粒子15及び負極用酸化物粒子21における炭素の質量濃度は、例えば、反応中間体である希土類−有機酸化合物を焼成し希土類酸化物を得る際に、任意の温度、任意の時間焼成することで調整することができる。正極用酸化物粒子15及び負極用酸化物粒子21における炭素の質量濃度は、湿式分析によって確認することができる。
なお、正極用酸化物粒子15及び負極用酸化物粒子21の平均粒径は、例えば1μm〜5μmの範囲にある。また、正極3に含まれる正極用酸化物粒子15の量は、100質量部の正極活物質粒子14に対し、例えば、0.1質量部〜2.0質量部の範囲にある。一方、負極4に含まれる負極用酸化物粒子21の量は、100質量部の負極活物質粒子20に対し、例えば、0.1質量部〜2.0質量部の範囲にある。
The mass concentration of carbon in the positive
The average particle diameter of the positive
上述したニッケル水素二次電池では、正極用酸化物粒子15における炭素の質量濃度が、負極用酸化物粒子21における炭素の質量濃度よりも大である。この結果として、このニッケル水素二次電池は、高温下での良好な充電効率が確保されているのみならず、高温下での連続充電特性にも優れている。
特に、正極用酸化物粒子15及び負極用酸化物粒子21が添加元素としてYを含むニッケル水素二次電池は、高温下での連続充電特性において一層優れている。
In the nickel hydride secondary battery described above, the mass concentration of carbon in the positive
In particular, the nickel metal hydride secondary battery in which the positive
1.酸化物粒子の作製
Y、Yb、Tm、Er、Gd及びLuの有機酸化合物を原材料として、任意の温度で任意の時間、それら有機酸化合物を焼成することにより、Y、Yb、Tm、Er、Gd及びLuの酸化物をそれぞれ生成した。得られた酸化物は、Y2O3、Yb2O3、Tm2O3、Er2O3、Gd2O3及びLu2O3をそれぞれ主成分として含有するとともに、不純物としての炭素を含有する。酸化物における炭素の質量濃度は、焼成温度、焼成時間を調整することにより、0.4、0.2又は0.05wt.%に調整した。
1. Production of Oxide Particles Using organic acid compounds of Y, Yb, Tm, Er, Gd, and Lu as raw materials, by firing these organic acid compounds at an arbitrary temperature for an arbitrary time, Y, Yb, Tm, Er, Gd and Lu oxides were produced, respectively. The obtained oxide contains Y 2 O 3 , Yb 2 O 3 , Tm 2 O 3 , Er 2 O 3 , Gd 2 O 3 and Lu 2 O 3 as main components, and contains carbon as an impurity. contains. The mass concentration of carbon in the oxide was adjusted to 0.4, 0.2, or 0.05 wt.% By adjusting the firing temperature and firing time.
2.正極の作製
生成した酸化物粒子と、結晶構造が乱され且つコバルトの平均価数が2価以上のコバルト化合物の被覆層が表面に形成された水酸化ニッケルの正極活物質粒子と、結着剤としてのPTFEディスパージョンと、純水とを、正極活物質粒子中の水酸化ニッケル100質量部に対し酸化物粒子1質量部、PTFEディスパージョン(比重1.5、固形分60質量%)1質量部(固形分換算)、純水30質量部の割合にて混練し、正極用スラリを調製した。正極基板としてのニッケル多孔体(多孔度95、平均孔径300μm)に、得られた正極スラリを所定の充填量にて充填したものを、正極スラリの乾燥後、所定厚みに圧延してから所定寸法に切断し、非焼結式正極を作製した。
2. Production of positive electrode Oxide particles produced, positive electrode active material particles of nickel hydroxide having a disordered crystal structure and a coating layer of a cobalt compound having an average cobalt valence of 2 or more, and a binder, and a binder PTFE dispersion and pure water as 1 part by weight of oxide particles, 100 parts by weight of nickel hydroxide in the positive electrode active material particles, 1 part by weight of PTFE dispersion (specific gravity 1.5, solid content 60% by weight) Solid content) and kneaded at a ratio of 30 parts by mass of pure water to prepare a positive electrode slurry. A nickel porous body (porosity 95, average pore diameter 300 μm) as a positive electrode substrate filled with the obtained positive electrode slurry with a predetermined filling amount, dried to a predetermined thickness after drying the positive electrode slurry, and then with predetermined dimensions A non-sintered positive electrode was produced.
3.負極の作製
生成した酸化物粒子と、水素吸蔵合金粒子と、結着剤としてのポリアクリル酸ナトリウム、カルボキシメチルセルロース及びPTFEディスパージョンと、純水とを、水素吸蔵合金粒子100質量部に対し、酸化物粒子1質量部、ポリアクリル酸ナトリウム0.5質量部、カルボキシメチルセルロース0.12質量部、PTFEディスバージョン(比重1.5、固形分60質量%)1.0質量部(固形分換算)、カーボンブラック1.0質量部、及び、純水30質量部の割合にて混練して負極用スラリを調製した。調製した負極用スラリを塗着したパンチングメタルを、負極用スラリの乾燥を経てからロール圧延・裁断して、負極を作製した。
3. Production of negative electrode Oxidized oxide particles, hydrogen storage alloy particles, sodium polyacrylate, carboxymethyl cellulose and PTFE dispersion as binders, and pure water were oxidized to 100 parts by mass of hydrogen storage alloy particles. 1 part by weight of particles, 0.5 part by weight of sodium polyacrylate, 0.12 part by weight of carboxymethylcellulose, 1.0 part by weight (specific gravity 1.5, solid content 60% by weight) 1.0 part by weight (converted to solids), 1.0 part by weight of carbon black, and A slurry for negative electrode was prepared by kneading at a ratio of 30 parts by mass of pure water. The punched metal coated with the prepared negative electrode slurry was roll-rolled and cut after the negative electrode slurry was dried to prepare a negative electrode.
4.ニッケル水素二次電池の組立て
得られた正極と負極とを、ポリアミド系不織布からなるセパレータを介して渦巻状に巻回し、電極群を作製した。得られた電極群を外装缶内に収納して所定の取付工程を行った後、外装缶内に水酸化カリウム水溶液を主成分とする8Nのアルカリ電解液を注液した。そして、外装缶の開口を蓋板等を用いて封口し、公称容量が1200mAhでAAサイズの密閉円筒形ニッケル水素二次電池を組み立てた。
4). Assembling of the nickel metal hydride secondary battery The obtained positive electrode and negative electrode were spirally wound through a separator made of a polyamide non-woven fabric to produce an electrode group. The obtained electrode group was housed in an outer can and subjected to a predetermined attachment process, and then an 8N alkaline electrolyte mainly composed of an aqueous potassium hydroxide solution was injected into the outer can. Then, the opening of the outer can was sealed with a cover plate or the like, and an AA-sized sealed cylindrical nickel-metal hydride secondary battery with a nominal capacity of 1200 mAh was assembled.
このとき正極に用いる酸化物粒子(正極用酸化物粒子)と負極に用いる酸化物粒子(負極用酸化物粒子)を変更することによって、実施例1〜8及び比較例1〜18のニッケル水素二次電池を組み立てた。実施例1〜8及び比較例1〜18における正極用酸化物粒子及び負極用酸化物粒子の種類及びそれらにおける炭素濃度は、表1に示した通りである。また、表1には、正極用酸化物粒子における炭素濃度をAとし、負極用酸化物粒子における炭素濃度をBとしたときに、後者に対する前者の比A/Bを炭素の質量濃度比として示した。 At this time, by changing the oxide particles used for the positive electrode (oxide particles for positive electrode) and the oxide particles used for the negative electrode (oxide particles for negative electrode), the nickel hydride of Examples 1 to 8 and Comparative Examples 1 to 18 were changed. The next battery was assembled. The types of the positive electrode oxide particles and the negative electrode oxide particles in Examples 1 to 8 and Comparative Examples 1 to 18 and the carbon concentration thereof are as shown in Table 1. Table 1 also shows the former ratio A / B as the carbon mass concentration ratio, where A is the carbon concentration in the positive electrode oxide particles and B is the carbon concentration in the negative electrode oxide particles. It was.
なお、比較例12では、正極及び負極に酸化物粒子を使用しなかった。そして、比較例13〜18では、正極及び負極のうち一方のみに酸化物粒子を使用した。
5.電池の特性評価
作製された実施例1〜8及び比較例1〜18の各ニッケル水素二次電池について以下の評価を行った。
In Comparative Example 12, oxide particles were not used for the positive electrode and the negative electrode. In Comparative Examples 13 to 18, oxide particles were used for only one of the positive electrode and the negative electrode.
5). Battery Characteristic Evaluation The following evaluations were performed on the produced nickel-hydrogen secondary batteries of Examples 1 to 8 and Comparative Examples 1 to 18.
(1)高温充電試験
各電池に、25℃の周囲温度にて、120mA(0.1It)の充電電流で16時間の充電を行った後、同じく25℃の周囲温度にて、1200mA(1It)の放電電流で放電終止電圧が1.0Vになるまで放電させ、このときの放電容量を測定した。それから、60℃の周囲温度にて、120mA(0.1It)の充電電流で16時間の充電を行った後、25℃の周囲温度にて、1200mA(1It)の放電電流で放電終止電圧が1.0Vになるまで放電させ、このときの放電容量を測定した。先の放電容量に対する後の放電容量の比率を、60℃充電効率として表1に示す。
(1) High-temperature charging test Each battery was charged at 120mA (0.1It) at an ambient temperature of 25 ℃ for 16 hours and then 1200mA (1It) at an ambient temperature of 25 ℃. A discharge current was discharged until the final discharge voltage reached 1.0 V, and the discharge capacity at this time was measured. Then, after charging for 16 hours at a charging current of 120mA (0.1It) at an ambient temperature of 60 ° C, the end-of-discharge voltage is 1.0V at a discharging current of 1200mA (1It) at an ambient temperature of 25 ° C. It was made to discharge until it became, and the discharge capacity at this time was measured. The ratio of the subsequent discharge capacity to the previous discharge capacity is shown in Table 1 as 60 ° C. charging efficiency.
(2)連続充電耐久特性試験(JIS C 8705 JT)
各電池に、55℃の周囲温度にて、40mA(0.033It)の充電電流で28日間の充電を行った後、直ちに同じく55℃の周囲温度にて、1200mA(1It)の放電電流で放電終止電圧が1.1Vになるまで放電させる充放電サイクルを10サイクル行い、1サイクル目と10サイクル目に放電容量を測定した。表1に、1サイクル目及び10サイクル目の放電容量ととともに、1サイクル目の放電容量をXとし、10サイクル目の放電容量をYとしたときに、前者に対する後者の比Y/Xを容量維持率として示す。また、公称容量(1200mAh)に対する10サイクル目の放電容量Yの比も、公称容量比として表1に示す。
(2) Continuous charge durability characteristic test (JIS C 8705 JT)
Each battery was charged for 28 days at 55 ° C ambient temperature with 40mA (0.033It) charge current, then immediately discharged at 1200mA (1It) discharge current at 55 ° C ambient temperature. Ten charge / discharge cycles were performed until the voltage reached 1.1 V, and the discharge capacity was measured in the first and tenth cycles. In Table 1, when the discharge capacity of the first cycle is X and the discharge capacity of the 10th cycle is Y, together with the discharge capacity of the first cycle and the 10th cycle, the ratio Y / X of the latter to the former is the capacity. Shown as maintenance rate. The ratio of the discharge capacity Y at the 10th cycle to the nominal capacity (1200 mAh) is also shown in Table 1 as the nominal capacity ratio.
(3)試験結果
表1から次のことが明らかである。
(i)正極に正極用酸化物粒子を使用した実施例1〜8及び比較例1〜11、16〜18では、正極に正極用酸化物粒子を使用しなかった比較例12〜15に比べて、60℃充電効率が高かった。これより、実施例1〜8では、高温下での良好な連続充電特性が確保されていることがわかる。
(3) Test results From Table 1, the following is clear.
(I) In Examples 1 to 8 and Comparative Examples 1 to 11 and 16 to 18 in which the positive electrode oxide particles were used for the positive electrode, compared with Comparative Examples 12 to 15 in which the positive electrode oxide particles were not used for the positive electrode. The charging efficiency at 60 ℃ was high. From this, in Examples 1-8, it turns out that the favorable continuous charge characteristic under high temperature is ensured.
(ii)炭素の質量濃度比(A/B)が1よりも大の実施例1〜8では、炭素の質量濃度比(A/B)が1以下の比較例1〜11に比べて、容量維持率(Y/X)が高い。これより、正極用酸化物粒子における炭素の質量濃度が負極用酸化物粒子における炭素の質量濃度よりも大であることによって、高温下での連続充電特性が向上することがわかる。
(iii)特に、正極用酸化物粒子及び負極用酸化物粒子の主成分がY2O3である実施例1〜3では、他の実施例4〜8に比べて、容量維持率(Y/X)が90%を超えて顕著に向上している。これより、正極用酸化物粒子及び負極用酸化物粒子の主成分がY2O3であるのが好ましいこと、換言すれば、正極用酸化物粒子及び負極用酸化物粒子が添加元素としてYを含むのが好ましいことがわかる。
(Ii) In Examples 1 to 8 in which the carbon mass concentration ratio (A / B) is larger than 1, the capacity is larger than that in Comparative Examples 1 to 11 in which the carbon mass concentration ratio (A / B) is 1 or less. Maintenance rate (Y / X) is high. From this, it can be seen that the continuous charge characteristics at high temperatures are improved when the mass concentration of carbon in the oxide particles for positive electrode is larger than the mass concentration of carbon in the oxide particles for negative electrode.
(Iii) In particular, in Examples 1 to 3 in which the main component of the positive electrode oxide particles and the negative electrode oxide particles is Y 2 O 3 , the capacity retention ratio (Y / X) markedly improved over 90%. From this, it is preferable that the main component of the oxide particles for positive electrodes and the oxide particles for negative electrodes is Y 2 O 3 , in other words, the oxide particles for positive electrodes and the oxide particles for negative electrodes are Y as an additive element. It turns out that it is preferable to include.
本発明は上述した一実施形態及び実施例に限定されることはなく、種々変形が可能であり、例えば、電池は角形電池であってもよく、電池の機械的な構造は格別限定されることはない。 The present invention is not limited to the above-described embodiment and examples, and various modifications are possible. For example, the battery may be a rectangular battery, and the mechanical structure of the battery is particularly limited. There is no.
1 外装缶(容器)
2 電極群
3 正極
4 負極
5 セパレータ
14 正極活物質粒子
15 正極用酸化物粒子
20 負極活物質粒子
21 負極用酸化物粒子
1 Exterior can (container)
2
14 Cathode active material particles
15 Oxide particles for positive electrode
20 Negative electrode active material particles
21 Negative electrode oxide particles
Claims (2)
前記正極は、
水酸化ニッケル若しくは高次水酸化ニッケルを含有する正極活物質粒子と、
Y、Yb、Tm、Er、Gd及びLuよりなる群から選択された少なくとも1種の添加元素及び炭素を含有する正極用酸化物粒子とを含み、
前記負極は、
水素吸蔵合金を含有する負極活物質粒子と、
前記正極用酸化物粒子が含有する前記添加元素と同じ種類の添加元素を少なくとも含有する負極用酸化物粒子とを含み、
前記正極用酸化物粒子における炭素の質量濃度は、前記負極用酸化物粒子における炭素の質量濃度よりも大である
ことを特徴とするニッケル水素二次電池。 In a nickel metal hydride secondary battery comprising a positive electrode, a negative electrode and an alkaline electrolyte in a container,
The positive electrode is
Positive electrode active material particles containing nickel hydroxide or higher order nickel hydroxide;
Including positive electrode oxide particles containing at least one additional element selected from the group consisting of Y, Yb, Tm, Er, Gd, and Lu, and carbon,
The negative electrode is
Negative electrode active material particles containing a hydrogen storage alloy;
Including negative electrode oxide particles containing at least the same kind of additive elements as the additive elements contained in the positive electrode oxide particles,
The nickel-hydrogen secondary battery, wherein the mass concentration of carbon in the positive electrode oxide particles is larger than the mass concentration of carbon in the negative electrode oxide particles.