JP2008247877A - Aqueous eye shadow - Google Patents
Aqueous eye shadow Download PDFInfo
- Publication number
- JP2008247877A JP2008247877A JP2007094661A JP2007094661A JP2008247877A JP 2008247877 A JP2008247877 A JP 2008247877A JP 2007094661 A JP2007094661 A JP 2007094661A JP 2007094661 A JP2007094661 A JP 2007094661A JP 2008247877 A JP2008247877 A JP 2008247877A
- Authority
- JP
- Japan
- Prior art keywords
- component
- eye shadow
- powder
- aqueous eye
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は水性アイシャドウに関するものであり、みずみずしい使用感が得られ、密着性、発色、塗布膜の柔軟性および化粧もちに優れた水性アイシャドウを提供するものである。 The present invention relates to a water-based eye shadow, and provides a water-based eye shadow excellent in adhesion, color development, coating film flexibility, and makeup with a fresh feeling of use.
一般に、アイシャドウは、携帯性や使用性が簡単なため、粉体を圧縮成型した製品が多く使用されているが、使用時の伸び広がり、経時での化粧持ちが問題となっていた。使用時の伸び広がりのなめらかさや清涼感が得られるアイシャドウとして、水性アイシャドウについて種々の検討がなされている。例えば、固体でエラストマー性のポリオルガノシロキサンの粒子の水性懸濁物を用いて耐水性を向上する技術（例えば、特許文献１）や、皮膜形成ラジカルポリマーを含むポリマー系を用いることによって「移りのない」組成物を得る技術（例えば、特許文献２）、分子量３５００以下のポリエーテル変性シリコーンを添加することでシリコーン表面処理粉体の水中への分散性を高めた技術（例えば、特許文献３）があげられる。 In general, eye shadows are easy to carry and use, and therefore, products in which powder is compression-molded are often used. However, there has been a problem of spreading and spreading during use and long-lasting makeup. Various studies have been made on water-based eye shadows as eye shadows that can provide smoothness and a refreshing feeling during use. For example, a technique for improving water resistance using an aqueous suspension of solid, elastomeric polyorganosiloxane particles (for example, Patent Document 1) or a polymer system containing a film-forming radical polymer may Technology for obtaining a composition (for example, Patent Document 2), Technology for improving dispersibility of silicone surface-treated powder in water by adding a polyether-modified silicone having a molecular weight of 3500 or less (for example, Patent Document 3) Can be given.
しかしながら、水性化粧料で粉体が配合される場合は、塗布後に水、アルコール等の水性成分が揮発し、皮膚との密着性が悪い粉体がまばたき等によって動くことが原因でヨレが生じたり、また塗布中に水性成分が揮発することにより、粉体と皮膚との間で潤滑物質がなくなることが原因で使用時の止まりのきつさが感じられたりすることがあった。そこで、粉体の密着性をあげるために、皮膜形成剤を用いる場合、水性成分の乾燥過程で皮膜が収縮することによって、塗膜の柔軟性が損なわれることが問題となり、まだ解決されていない。しかも最近では、パール剤やラメ剤など光輝性粉体を使用したメークアップがテレビ、雑誌などで多数取上げられ愛用者も多い。ところが、経時においてパール剤やラメ剤の密着性が低下して、はがれ落ちる現象が見られることがあった。そこで、みずみずしい使用感が得られ、密着性が高く、塗布膜の柔軟性に優れ、経時において粉体のみならず、パール剤やラメ剤等の光輝性粉体の化粧持ちに優れた水性アイシャドウの開発が望まれていた。 However, when powders are formulated with aqueous cosmetics, water components such as water and alcohol volatilize after application, and the powder that has poor adhesion to the skin may move due to blinking, etc. In addition, due to the volatilization of the aqueous component during application, there may be a feeling of tightness in use due to the absence of the lubricating substance between the powder and the skin. Therefore, when a film forming agent is used to increase the adhesion of the powder, the film shrinks during the drying process of the aqueous component, which causes a problem that the flexibility of the coating film is lost and has not been solved yet. . Moreover, recently, many make-ups using glittering powders such as pearls and lamés have been picked up on TV and magazines, and there are many users. However, the adhesiveness of the pearl agent and the lame agent deteriorates with time, and a phenomenon of peeling off may be observed. Therefore, a water-based eye shadow that provides a fresh feeling of use, high adhesion, excellent flexibility of the coating film, and excellent makeup of glossy powders such as pearls and lamellars as well as powder over time. Development of was desired.
かかる実情において、本発明者らは上記課題を解決すべく鋭意研究を行った結果、水不溶性皮膜形成剤、多価アルコール、アニオン性界面活性剤、および粉体を配合することにより、水性成分によるみずみずしい使用感を損なわずに、水不溶性皮膜形成剤を配合することにより高い密着性を得て、アニオン性界面活性剤により顔料、パール剤やラメ剤等の粉体成分を均一に分散し発色を向上し、多価アルコールによって、この水不溶性皮膜形成剤や粉体等により形成される塗布膜に柔軟性を与え、これらを組み合わせることで化粧持ちに優れた水性アイシャドウが得られることを見出し本発明を完成するに至った。 In such a situation, the present inventors conducted extensive research to solve the above-mentioned problems, and as a result, a water-insoluble film-forming agent, a polyhydric alcohol, an anionic surfactant, and a powder were blended, thereby resulting in an aqueous component. High adhesion is obtained by blending a water-insoluble film forming agent without impairing the fresh feeling of use, and powder components such as pigments, pearl agents and lame agents are uniformly dispersed with an anionic surfactant to develop color. It is found that polyhydric alcohol gives flexibility to the coating film formed with this water-insoluble film-forming agent or powder, and combining them makes it possible to obtain an aqueous eye shadow with excellent makeup. The invention has been completed.
すなわち、本発明は、次の成分（ａ）〜（ｄ）；
（ａ）水不溶性皮膜形成剤を０．４〜４質量％（以下、単に「％」と示す。）
（ｂ）多価アルコールを１５〜４０％
（ｃ）アニオン性界面活性剤
（ｄ）粉体
を配合したことを特徴とした水性アイシャドウを提供するものである。
That is, the present invention provides the following components (a) to (d);
(A) 0.4 to 4% by mass of a water-insoluble film forming agent (hereinafter simply referred to as “%”)
(B) 15-40% of polyhydric alcohol
(C) An aqueous eye shadow characterized by containing an anionic surfactant (d) powder.
本発明の水性アイシャドウは、みずみずしい使用感、密着性、発色に優れ、塗布膜の柔軟性および顔料、パール剤やラメ剤などの粉体成分の化粧持ちに優れた水性アイシャドウである。 The water-based eye shadow of the present invention is a water-based eye shadow excellent in fresh feeling of use, adhesion, and color development, and excellent in the flexibility of the coating film and the makeup of powder components such as pigments, pearls and lamellars.
以下、本発明を詳細に説明する。
本発明の水性アイシャドウは、分散媒としての水相に、粉体を分散させた化粧料であり、静置時において、粉体は沈降していても分散していてもかまわず、また分散媒の水相も分離していてもかまわず、使用時振とうすることで、粉体は分散し、水相は連続相になるものであれば良い。その形態は水中に粉体を分散させた単純水系、前記単純水系に非乳化状態で油分を配合した多層型系、水中油型乳化物に粉体を分散させた水中油型系等が挙げられる。この中でも水中に粉体を分散させた単純水系が好ましい。
Hereinafter, the present invention will be described in detail.
The aqueous eye shadow of the present invention is a cosmetic in which a powder is dispersed in an aqueous phase as a dispersion medium, and the powder may be settled or dispersed at the time of standing. The aqueous phase of the medium may be separated as long as the powder is dispersed and the aqueous phase becomes a continuous phase by shaking during use. The form includes a simple water system in which powder is dispersed in water, a multilayer system in which oil is blended in the simple water system in a non-emulsified state, and an oil-in-water system in which powder is dispersed in an oil-in-water emulsion. . Among these, a simple aqueous system in which powder is dispersed in water is preferable.
本発明の水性アイシャドウに用いられる成分（ａ）水不溶性皮膜形成剤は通常化粧料に用いられる皮膜形成剤であれば特に制限はない。具体的には、アクリル酸アルキル共重合体、アクリル酸重合体、（メタ）アクリル酸アルキル重合体、（メタ）アクリル酸アクリル酸アルキル共重合体、（メタ）アクリル酸・（メタ）アクリル酸アルキル共重合体、（メタ）アクリル酸アルキル・スチレン共重合体等の（共）重合体類が挙げられる。
これらの皮膜形成剤は、本発明の水性アイシャドウに水性成分と混合して配合することもでき、水等の水性溶媒に分散させた、いわゆるポリマーエマルションとして配合することもでき、これらを一種又は二種以上用いることができる。
エマルションにしたものとしては、（メタ）アクリル酸アルキル共重合体エマルション、（メタ）アクリル酸アルキル重合体エマルション、（メタ）アクリル酸・（メタ）アクリル酸アルキル共重合体エマルション、（メタ）アクリル酸アルキル・スチレン共重合体エマルション、ビニルピロリドン・スチレン共重合体エマルション等が挙げられるが、中でも（メタ）アクリル酸アルキル共重合体をアンモニウム塩として水性媒体に分散したポリマーエマルションが、密着性の高い化粧膜持続させる効果に優れていて好ましい。
市販品としては、アクリル酸アルキル共重合体エマルションである、ＹＯＤＯＳＯＬ ＧＨ８００、ＧＨ８１０（以上、日本ＮＳＣ社製 それぞれ固形分４５％、固形分４６％）、ＰＬＥＸＴＯＬ Ｂ５００（ポリマーラテックス社製 固形分５０％）、アクリル酸アルキル・スチレン共重合体エマルションである、リカボンドＥＴ−Ｆ５２７（中央理化工業社製 固形分４５％）、ビニルピロリドン・スチレン共重合体エマルションである、ＡＮＴＡＲＡ ４３０（ＩＳＰ社製 固形分４０％）等が挙げられる。
The component (a) water-insoluble film forming agent used in the aqueous eye shadow of the present invention is not particularly limited as long as it is a film forming agent usually used in cosmetics. Specifically, alkyl acrylate copolymer, acrylic acid polymer, (meth) acrylic acid alkyl polymer, (meth) acrylic acid alkyl acrylate copolymer, (meth) acrylic acid / (meth) acrylic acid alkyl And (co) polymers such as copolymers and alkyl (meth) acrylate / styrene copolymers.
These film forming agents can be blended with the aqueous eye shadow of the present invention by mixing with an aqueous component, and can also be blended as a so-called polymer emulsion dispersed in an aqueous solvent such as water. Two or more kinds can be used.
The emulsions include (meth) acrylic acid alkyl copolymer emulsion, (meth) acrylic acid alkyl polymer emulsion, (meth) acrylic acid / (meth) acrylic acid alkyl copolymer emulsion, (meth) acrylic acid. Alkyl / styrene copolymer emulsions, vinylpyrrolidone / styrene copolymer emulsions, and the like. Among them, polymer emulsions in which (meth) acrylic acid alkyl copolymers are dispersed in aqueous media as ammonium salts are highly adhesive cosmetics. It is preferable because it is excellent in the effect of maintaining the film.
Commercially available products are alkyl acrylate copolymer emulsions such as YODOSOL GH800, GH810 (above, Nippon NSC, respectively 45% solids, 46% solids), PLEXTOL B500 (polymer latex 50% solids) , Ricabond ET-F527 (solid content 45%, manufactured by Chuo Rika Kogyo Co., Ltd.), which is an alkyl acrylate / styrene copolymer emulsion, ANTARA 430 (solid content 40%, manufactured by ISP), which is a vinylpyrrolidone / styrene copolymer emulsion ) And the like.
本発明の水性アイシャドウにおける成分（ａ）の配合量は０．３〜４％であり、０．５〜２％が好ましい。配合量がこの範囲であれば、みずみずしい使用感、高い密着性、塗膜の柔軟性、顔料、パール剤やラメ剤などの粉体成分の化粧持ちを持続させる効果に優れるものが得られる。成分（ａ）の配合量が０．３％未満では粉体成分の化粧持ちの点で劣り、４％を超えると塗膜の柔軟性が損なわれる。 The compounding amount of component (a) in the aqueous eye shadow of the present invention is 0.3-4%, preferably 0.5-2%. When the blending amount is within this range, it is possible to obtain a product that is excellent in a fresh feeling of use, high adhesion, flexibility of a coating film, and a long-lasting effect of powder components such as pigments, pearls, and lame agents. If the blending amount of the component (a) is less than 0.3%, the powder component is inferior in terms of cosmetic durability, and if it exceeds 4%, the flexibility of the coating film is impaired.
本発明の水性アイシャドウに用いられる成分（ｂ）の多価アルコールは通常化粧料に用いられるものであれば特に制限されず、例えばプロピレングリコール、１，３−ブチレングリコール、ジプロピレングリコール、ポリエチレングリコール等のグリコール類、グリセリン、ジグリセリン、ポリグリセリン等のグリセロール類等が挙げられ、これらを一種又は二種以上用いることができる。
本発明の水性アイシャドウにおける成分（ｂ）の配合量は１５〜４０％であり、好ましくは２０〜３０％である。本発明の水性アイシャドウに成分（ｂ）の多価アルコールを配合することにより、塗布後のうるおい感や塗布膜に柔軟性が付与され、使用感がさらに向上する。成分（ｂ）の配合量が１５％未満では塗布膜の柔軟性の点で劣り、４０％を超えると塗布膜がずるつき、粉体成分のヨレが発生し好ましくない。
The polyhydric alcohol of component (b) used in the aqueous eye shadow of the present invention is not particularly limited as long as it is usually used in cosmetics. For example, propylene glycol, 1,3-butylene glycol, dipropylene glycol, polyethylene glycol Glycerols such as glycerol, glycerol such as glycerin, diglycerin and polyglycerin, and the like can be used, and one or more of these can be used.
The compounding quantity of the component (b) in the aqueous eye shadow of the present invention is 15 to 40%, preferably 20 to 30%. By blending the component (b) polyhydric alcohol with the aqueous eye shadow of the present invention, the moist feeling after coating and the flexibility of the coating film are imparted, and the usability is further improved. If the blending amount of the component (b) is less than 15%, the coating film is inferior in flexibility, and if it exceeds 40%, the coating film is unsatisfactory and the powder component is distorted.
本発明に用いられる成分（ｃ）のアニオン性界面活性剤は通常化粧料に用いられるものであれば特に制限されず、例えばリン酸系、硫酸系、スルホン酸系、カルボン酸系のものが挙げられ、ポリオキシアルキルエーテルリン酸塩、アルキルリン酸塩、ポリオキシアルキレンアルキルエーテル硫酸塩、ポリオキシアルキレンアルキルエーテルカルボン酸塩などがあげられる。
本発明においては塩基性物質を対塩として使用するアニオン性界面活性剤が好ましい。中でもリン酸系のアニオン性界面活性剤であるジポリオキシエチレンアルキルエーテルリン酸塩またはトリポリオキシエチレンアルキルエーテルリン酸塩（両者をジ（トリ）ポリオキシエチレンアルキルエーテルリン酸塩」と記載することがある。）が最も好ましい。市販品としては、例えばニッコールＤＤＰ−２、ニッコールＤＤＰ−４、ニッコールＤＤＰ−６、ニッコールＤＤＰ−８、ニッコールＤＤＰ−１０（日光ケミカルズ社製）等が挙げられ、これらを一種又は二種以上用いることができる。
本発明に用いられる成分（ｃ）のアニオン性界面活性剤の配合量は０．０５〜０．４％が好ましく、さらに好ましくは０．１〜０．３％である。この範囲であると、顔料、パール剤やラメ剤などの粉体成分の分散に優れ、塗布後の発色が向上する点で好ましい。
成分（ｃ）の対塩に用いられる塩基性物質は通常化粧料に用いられるものであれば特に制限されず、例えばＬ−アルギニン、トリエタノールアミン、水酸化カリウム、水酸化ナトリウムなどが挙げられ、これらを一種又は二種以上用いることができる。
成分（ｃ）のアニオン性界面活性剤は塩基性物質とあらかじめ対塩を形成し、配合してもよいし、水性アイシャドウ中で対塩を形成してもよい。
The anionic surfactant of component (c) used in the present invention is not particularly limited as long as it is usually used in cosmetics, and examples thereof include phosphoric acid type, sulfuric acid type, sulfonic acid type, and carboxylic acid type. And polyoxyalkyl ether phosphates, alkyl phosphates, polyoxyalkylene alkyl ether sulfates, polyoxyalkylene alkyl ether carboxylates and the like.
In the present invention, an anionic surfactant using a basic substance as a counter salt is preferred. Above all, dipolyoxyethylene alkyl ether phosphates or tripolyoxyethylene alkyl ether phosphates (both of which are di (tri) polyoxyethylene alkyl ether phosphates) which are phosphoric anionic surfactants Is most preferred. Examples of commercially available products include Nikkor DDP-2, Nikkor DDP-4, Nikkor DDP-6, Nikkor DDP-8, Nikkor DDP-10 (manufactured by Nikko Chemicals), and the like, and one or more of these may be used. Can do.
The blending amount of the anionic surfactant of component (c) used in the present invention is preferably 0.05 to 0.4%, more preferably 0.1 to 0.3%. Within this range, it is preferable from the viewpoint of excellent dispersion of powder components such as pigments, pearl agents, and lame agents, and improvement of color development after coating.
The basic substance used for the counter salt of component (c) is not particularly limited as long as it is usually used in cosmetics, and examples thereof include L-arginine, triethanolamine, potassium hydroxide, sodium hydroxide, and the like. One or more of these can be used.
The anionic surfactant of component (c) forms a counter salt with a basic substance in advance, and may be blended, or may form a counter salt in an aqueous eye shadow.
本発明に用いられる成分（ｄ）の粉体は通常化粧料に使用されるものであれば板状、紡錘状、針状等の形状、粒子径、多孔質、無孔質等の粒子構造等により特に限定されず、光輝性粉体類、無機粉体類、有機粉体類、色素粉体類、複合粉体類等が挙げられる。
具体的には、光輝性粉体として、酸化チタン被覆雲母、酸化チタン被覆オキシ塩化ビスマス、酸化チタン被覆合成金雲母、ガラス末、酸化チタン被覆ガラス末、酸化鉄被覆ガラス末、酸化鉄被覆雲母チタン、黒酸化鉄被覆雲母チタン、酸化鉄・黒酸化鉄被覆雲母チタン、コンジョウ被覆雲母チタン、カルミン被覆雲母チタン、カルミン・コンジョウ被覆雲母チタン、酸化鉄・カルミン被覆雲母チタン、酸化鉄・コンジョウ被覆雲母チタン、酸化クロム被覆雲母チタン、黒酸化チタン被覆雲母チタン、オキシ塩化ビスマス、魚鱗箔、酸化鉄被覆雲母、有機顔料被覆雲母チタン、多層被覆雲母チタン、ケイ酸・酸化チタン被覆雲母、ベンガラ被覆無水ケイ酸、酸化チタン被覆無水ケイ酸、酸化チタン被覆酸化アルミニウム等のパール剤や、ポリエチレンテレフタレート・アルミニウム・エポキシ積層末、ポリエチレンテレフタレート・ポリオレフィン積層フィルム末、ポリエチレンテレフタレート・ポリメチルメタクリレート積層フィルム末等のラメ剤が挙げられる。
さらに、酸化鉄、コンジョウ、群青、無水ケイ酸、炭酸マグネシウム、炭酸カルシウム、水酸化アルミニウム、水酸化クロム、カーボンブラック、ケイ酸アルミニウム、ケイ酸マグネシウム、ケイ酸アルミニウムマグネシウム、雲母、スメクタイト、ベントナイト、カオリン、合成雲母、合成セリサイト、セリサイト、タルク、炭化珪素、硫酸バリウム、窒化ホウ素等の無機粉体類、赤色２２６号、黄色２０５号、黄色４０１号、青色４０４号等のタール系色素類、ステアリン酸マグネシウム、ステアリン酸亜鉛、Ｎ−アシルリジン、ポリエチレンテレフタレート、ポリスチレン、ナイロン、ポリメチルメタクリレート、ポリメチルシルセスキオキサンパウダー、オルガノポリシロキサンエラストマーパウダー等の有機粉体類等が挙げられ、これらを一種又は二種以上組み合わせて用いることができる。
また、これら粉体は一種または二種以上の複合化したものを用いても良く、フッ素化合物、シリコーン化合物、金属石ケン、ロウ、界面活性剤、油脂、炭化水素等を用いて公知の方法により表面処理を施したものであっても良い。
本発明に用いられる成分（ｄ）の粉体の配合量は、１５〜３０％が好ましく、さらに好ましくは２０〜２５％である。この範囲であれば、発色のよいものが得られる。また、粉体全量中、前記光輝性粉体を５〜２５％、さらには７〜２０％配合すると、発色、光輝性粉体特有の光輝性が発揮され好ましい。
If the powder of component (d) used in the present invention is usually used in cosmetics, the shape of a plate, spindle, needle, etc., particle diameter, porous, nonporous particle structure, etc. Are not particularly limited, and examples thereof include glitter powders, inorganic powders, organic powders, pigment powders, and composite powders.
Specifically, titanium oxide-coated mica, titanium oxide-coated bismuth oxychloride, titanium oxide-coated synthetic phlogopite, glass powder, titanium oxide-coated glass powder, iron oxide-coated glass powder, iron oxide-coated mica titanium , Black iron oxide coated mica titanium, iron oxide / black iron oxide coated mica titanium, conger coated mica titanium, carmine coated mica titanium, carmine / konjo coated mica titanium, iron oxide / carmine coated mica titanium, iron oxide / konjo coated mica titanium , Chromium oxide coated mica titanium, black titanium oxide coated mica titanium, bismuth oxychloride, fish scale foil, iron oxide coated mica, organic pigment coated mica titanium, multilayer coated mica titanium, silicic acid / titanium oxide coated mica, bengara coated silicic acid Pearling agents such as titanium oxide-coated silicic anhydride, titanium oxide-coated aluminum oxide, and polyester Terephthalate-aluminum-epoxy laminated powder, polyethylene terephthalate polyolefin laminated film powder, lame agent such as powder polyethylene terephthalate polymethyl methacrylate laminated film.
In addition, iron oxide, conger, ultramarine, anhydrous silica, magnesium carbonate, calcium carbonate, aluminum hydroxide, chromium hydroxide, carbon black, aluminum silicate, magnesium silicate, magnesium aluminum silicate, mica, smectite, bentonite, kaolin Synthetic mica, synthetic sericite, sericite, talc, silicon carbide, barium sulfate, boron nitride and other inorganic powders, red 226, yellow 205, yellow 401, blue 404 and other tar pigments, Organic powders such as magnesium stearate, zinc stearate, N-acyl lysine, polyethylene terephthalate, polystyrene, nylon, polymethyl methacrylate, polymethylsilsesquioxane powder, organopolysiloxane elastomer powder, etc. Can be used in combination one or two or more kinds of these.
These powders may be used singly or in combination of two or more, and may be obtained by known methods using fluorine compounds, silicone compounds, metal soaps, waxes, surfactants, oils and fats, hydrocarbons, and the like. It may have been subjected to a surface treatment.
The blending amount of the component (d) powder used in the present invention is preferably 15 to 30%, more preferably 20 to 25%. If it is this range, a thing with good coloring will be obtained. Further, if the glittering powder is blended in an amount of 5 to 25%, more preferably 7 to 20% in the total amount of the powder, it is preferable because the glittering property peculiar to coloring and glittering powder is exhibited.
本発明の水性アイシャドウにおける水の配合量は、成分（ａ）〜（ｄ）の配合量にも依存するが、概ね１５〜８０％が好ましい。 The blending amount of water in the aqueous eye shadow of the present invention depends on the blending amounts of the components (a) to (d), but is generally preferably 15 to 80%.
本発明の水性アイシャドウには、上記成分（ａ）〜（ｄ）の他、本発明の効果を損なわない範囲で、必要に応じて水性成分、油剤、水溶性高分子、界面活性剤、タンパク質、ムコ多糖、コラーゲン，エラスチン等の保湿剤、α−トコフェロール、アスコルビン酸等の酸化防止剤、ビタミン類、消炎剤、生薬等の美容成分、パラオキシ安息香酸エステル、フェノキシエタノール等の防腐剤、香料等を適宜配合することができる。 In addition to the components (a) to (d) described above, the aqueous eye shadow of the present invention includes an aqueous component, an oil agent, a water-soluble polymer, a surfactant, and a protein as necessary, as long as the effects of the present invention are not impaired. Moisturizers such as mucopolysaccharides, collagen and elastin, antioxidants such as α-tocopherol and ascorbic acid, vitamins, anti-inflammatory agents, cosmetic ingredients such as herbal medicines, antiseptics such as paraoxybenzoic acid esters and phenoxyethanol, and fragrances It can mix | blend suitably.
水性成分は、水に可溶な成分であれば何れでもよく、例えば、エチアルコール等のアルコール類、アロエベラ、ウイッチヘーゼル、ハマメリス、キュウリ、レモン、ラベンダー、ローズ等の植物抽出液が挙げられる。 The aqueous component may be any component that is soluble in water, and examples include alcohols such as ethialcohol, and plant extracts such as aloe vera, witch hazel, hamamelis, cucumber, lemon, lavender, and rose.
油剤は、エモリエント、消泡剤の目的で配合することができるが、０．１％以下であることが望ましく、通常化粧料に用いられる油性成分であり、通常化粧料に使用される油剤であれば、特に制限されない。例えば、炭化水素油として、スクワラン、流動パラフィン、ワセリン、ポリブテン、ポリイソブチレン、ポリイソブテン等、高級脂肪酸としては、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、ベヘン酸、オレイン酸、リノール酸、リノレン酸、アラキドン酸、エイコサペンタエン酸（ＥＰＡ）、ドコサヘキサエン酸（ＤＨＡ）、イソステアリン酸、１２−ヒドロキシステアリン酸等、高級アルコールとしては、ミリスチルアルコール、パルミチルアルコール、セトステアリルアルコール、ステアリルアルコール、ベヘニルアルコール等、エステル油としては、オレイン酸オレイル、オレイン酸オクチルドデシル、オレイン酸デシル、イソステアリン酸イソセチル、イソノナン酸イソトリデシル、ステアリン酸イソセチル、パルミチン酸イソプロピル、パルミチン酸−２−エチルヘキシル、パルミチン酸−２−ヘキシルデシル、ミリスチン酸イソプロピル、ミリスチン酸オクチルドデシル、ミリスチン酸ミリスチル、オクタン酸セチル、２−エチルヘキサン酸セチル、コハク酸−２−エチルヘキシル、リンゴ酸ジイソステアリル、ジイソステアリン酸ジグリセイル、トリイソステアリン酸ジグリセイル、モノイソステアリン酸アルキレングリコール、ジ−２−エチルヘキサン酸エチレングリコール、ジカプリン酸ネオペンチルグリコール、トリ−２−エチルヘキサン酸トリメチロールプロパン、テトラ−２−エチルヘキサン酸ペンタエリスリトール、ジペンタエリスリトール脂肪酸エステル、ロジン酸ペンタエリトリットエステル、１２−ヒドロキシステアリン酸コレステリル、Ｎ−ラウロイル−Ｌ−グルタミン酸−２−オクチルドデシルエステル等、シリコーン油としては、低重合度ジメチルポリシロキサン、高重合度ジメチルポリシロキサン、デカメチルシクロペンタシロキサン、オクタメチルシクロテトラシロキサン、アルコキシ変性ポリシロキサン、架橋型オルガノポリシロキサン、フッ素変性ポリシロキサン等、フッ素系油剤としては、パーフルオロポリエーテル、パーフルオロデカリン、パーフルオロオクタン等が挙げられ、これらの油剤は必要に応じて一種又は二種以上用いることができる。 The oil agent can be formulated for the purpose of emollient or antifoaming agent, but is preferably 0.1% or less, and is an oily component that is usually used in cosmetics. There is no particular limitation. For example, hydrocarbon oils such as squalane, liquid paraffin, petrolatum, polybutene, polyisobutylene, polyisobutene, etc., and higher fatty acids include lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, oleic acid, linoleic acid, linolenic acid , Arachidonic acid, eicosapentaenoic acid (EPA), docosahexaenoic acid (DHA), isostearic acid, 12-hydroxystearic acid, etc. Examples of higher alcohols include myristyl alcohol, palmityl alcohol, cetostearyl alcohol, stearyl alcohol, behenyl alcohol, and esters. Oils include oleyl oleate, octyldodecyl oleate, decyl oleate, isocetyl isostearate, isotridecyl isononanoate, isocetyl stearate, Isopropyl tartrate, 2-ethylhexyl palmitate, 2-hexyldecyl palmitate, isopropyl myristate, octyldodecyl myristate, myristyl myristate, cetyl octanoate, cetyl 2-ethylhexanoate, 2-ethylhexyl succinate, Diisostearyl malate, diglyceryl diisostearate, diglyceryl triisostearate, alkylene glycol monoisostearate, ethylene glycol di-2-ethylhexanoate, neopentyl glycol dicaprate, trimethylolpropane tri-2-ethylhexanoate, tetra- 2-ethylhexanoic acid pentaerythritol, dipentaerythritol fatty acid ester, rosin acid pentaerythritol ester, 12-hydroxystearic acid cholesterol Teryl, N-lauroyl-L-glutamic acid-2-octyldodecyl ester, etc. As silicone oil, low polymerization dimethylpolysiloxane, high polymerization dimethylpolysiloxane, decamethylcyclopentasiloxane, octamethylcyclotetrasiloxane, alkoxy modified Examples of the fluorine-based oil agent such as polysiloxane, cross-linked organopolysiloxane, fluorine-modified polysiloxane, and the like include perfluoropolyether, perfluorodecalin, perfluorooctane, and the like. The above can be used.
水溶性高分子は、粘度調整剤、感触調整剤等の目的で用いられるものであり、グアーガム、スクレロチウムガム、ジェランガム、ペクチン、寒天、コンドロイチン硫酸ナトリウム、ヒアルロン酸、アラビアガム、アルギン酸ナトリウム、カラギーナン、キサンタンガム、ローカストビーンガム、メチルセルロース、ヒドロキシエチルセルロース、カルボキシメチルセルロース、カルボキシビニルポリマー、アルキル変性カルボキシビニルポリマー、ポリビニルアルコール、ポリビニルピロリドン、ポリアクリル酸ナトリウム等が挙げられ、これらを一種又は二種以上用いることができる。本発明の水性アイシャドウにこれら水溶性高分子を含有する場合の配合量は、０．０１〜５％が好ましい。 Water-soluble polymers are used for the purpose of viscosity modifiers, feel modifiers, etc., and include guar gum, sclerotium gum, gellan gum, pectin, agar, chondroitin sulfate sodium, hyaluronic acid, gum arabic, sodium alginate, carrageenan , Xanthan gum, locust bean gum, methyl cellulose, hydroxyethyl cellulose, carboxymethyl cellulose, carboxy vinyl polymer, alkyl-modified carboxy vinyl polymer, polyvinyl alcohol, polyvinyl pyrrolidone, sodium polyacrylate, etc., and these may be used singly or in combination. it can. The blending amount when these water-soluble polymers are contained in the aqueous eye shadow of the present invention is preferably 0.01 to 5%.
本発明の水性アイシャドウは、以下に例示する方法で製造することができる。
成分（ｂ）の多価アルコールの一部および成分（ｃ）のアニオン性界面活性剤および成分（ｄ）の粉体および水の一部で分散処理した後に、この分散物を成分（ｂ）の多価アルコールの残分と水の残分および成分（ａ）の水不溶性皮膜形成剤との混合物に添加分散し水性アイシャドウを得ることができる。
The aqueous eye shadow of the present invention can be produced by the method exemplified below.
After the dispersion treatment with a part of the polyhydric alcohol of component (b) and the anionic surfactant of component (c) and the powder of component (d) and a part of water, the dispersion An aqueous eye shadow can be obtained by adding and dispersing in a mixture of the residue of polyhydric alcohol, the residue of water and the water-insoluble film forming agent of component (a).
本発明の水性アイシャドウの性状は、液状、クリーム状、固形状等が挙げられる。 Examples of the properties of the aqueous eye shadow of the present invention include liquid, cream and solid.
次に実施例を挙げて本発明を更に説明するが、本発明はこれによって何ら限定されるものではない。 EXAMPLES Next, although an Example is given and this invention is further demonstrated, this invention is not limited at all by this.
実施例１〜７および比較例１〜５水性アイシャドウ
表１に示す組成および下記に示す製造方法にて水性アイシャドウを調製した。得られた水性アイシャドウに関し、みずみずしい使用感、密着性、化粧持ち、塗布後の化粧膜の柔軟性について下記の方法により評価し、その結果をあわせて、表１に示した。
Examples 1 to 7 and Comparative Examples 1 to 5 Aqueous eye shadows Aqueous eye shadows were prepared by the composition shown in Table 1 and the production method shown below. With respect to the obtained aqueous eye shadow, fresh feeling in use, adhesion, makeup lasting, and flexibility of the decorative film after application were evaluated by the following methods, and the results are shown in Table 1.
＊１：ニッコール ＤＤＰ−６（日光ケミカルズ社製）
＊２：ニッコール ＴＤＰ−６（日光ケミカルズ社製）
＊３：ニッコール ＢＣ−２０ＴＸ（日光ケミカルズ社製）
＊４：ＹＯＤＯＳＯＬ ＧＨ８００Ｆ（日本エヌエスシー社製）
＊５：リカボンド ＥＴ−Ｆ５２７（中央理化工業社製）
（製造方法）
Ａ：成分（１）〜（６）を７０℃で均一に加熱溶解する。
Ｂ：Ａに成分（７）〜（１２）を混合し、三本ローラーにて分散処理する。
Ｃ：Ｂに成分（１３）〜（２１）を添加混合しディスパーにて分散後、脱気して液状の水性アイシャドウを得た。
* 1: Nikkor DDP-6 (Nikko Chemicals)
* 2: Nikkor TDP-6 (Nikko Chemicals)
* 3: Nikkor BC-20TX (Nikko Chemicals)
* 4: YODOSOL GH800F (made by NSC Japan)
* 5: Rikabond ET-F527 (Chuo Rika Kogyo Co., Ltd.)
(Production method)
A: Components (1) to (6) are uniformly heated and dissolved at 70 ° C.
B: Components (7) to (12) are mixed with A and dispersed by a three-roller.
C: Components (13) to (21) were added to and mixed with B, dispersed with a disper, and then deaerated to obtain a liquid aqueous eye shadow.
（評価方法）
下記評価項目について各々下記方法により評価を行った。
各試料について専門パネル２０名による使用テストを行った。パネル各人がイ〜ニの項目について下記絶対評価基準にて７段階に評価し評点を付け、各試料のパネル全員の評点合計から、その平均値を算出し、下記４段階判定基準により判定した。
尚、ロの密着性については、塗布時の化粧料の密着感を主眼とし、ハの化粧持ちについては、塗布後、専門パネルに通常の生活をしてもらい、３時間後の化粧膜について、ヨレや粉体のはがれないかを主眼とし、ニの塗布後の化粧膜の柔軟性については、ハと同様に３時間後の化粧膜について、ツッパリ感を主眼として評価してもらった。
(Evaluation methods)
The following evaluation items were evaluated by the following methods.
Each sample was tested for use by 20 specialist panels. Each panel member evaluated items 1 to 2 according to the following absolute evaluation criteria, assigned a score, and calculated the average value from the total score of all the panel members of each sample, and determined according to the following 4 criteria. .
Regarding the adhesiveness of b, the main focus is on the feeling of adhesion of the cosmetics at the time of application. Focusing on whether or not the flaking or powder peeled off, the softness of the cosmetic film after the application of d was evaluated mainly on the feeling of touch on the cosmetic film after 3 hours, as in C.
（官能評価項目）
イ．みずみずしい使用感
ロ．密着性
ハ．化粧持ち
ニ．塗布後の化粧膜の柔軟性
(Sensory evaluation items)
I. A fresh feeling of use. Adhesiveness c. Makeup dating. Flexibility of decorative film after application
（絶対評価）
（評点）：（評価）
６：非常に良い
５：良い
４：やや良い
３：普通
２：やや悪い
１：悪い
０：非常に悪い
（判定基準）
（評点平均値） （判定）
５点を超える ：非常に良好：◎
３．５点を超えて５点以下 ：良好 ：○
２点を超えて３．５点以下 ：やや不良 ：△
２点以下 ：不良 ：×
(Absolute evaluation)
(Score): (Evaluation)
6: Very good 5: Good 4: Somewhat good 3: Normal 2: Somewhat bad 1: Bad 0: Very bad (judgment criteria)
(Average score) (Judgment)
More than 5 points: Very good: ◎
Over 3.5 points and 5 points or less: Good: ○
Over 2 points and 3.5 points or less: Somewhat bad: △
2 points or less: Defect: ×
表1の結果から明らかなように、本発明の水性アイシャドウは、みずみずしい使用感、高い密着性、顔料、パール剤、ラメ剤などの粉体成分の化粧持ちに優れ、塗布後の化粧膜の柔軟性にも優れた水性アイシャドウであった。
一方、成分（ａ）の水不溶性皮膜形成剤の配合量を０．１８％とした（アクリル酸アルキル共重合体アンモニウムポリマーエマルションとしては０．４％）比較例１は、密着性や粉体成分の化粧持ちの点で劣るもので、更に化粧膜を均一に塗布することが困難であった。また、成分（ａ）の水不溶性皮膜形成剤の配合量を５．４％（アクリル酸アルキル共重合体アンモニウムポリマーエマルションとしては１２％）とした比較例２は水性アイシャドウにもかかわらず使用性のみずみずしさが損なわれ、塗布後の化粧膜は柔軟性がなくツッパリ感が強く感じられた。更に使用時の伸び広がりが悪いものだった。成分（ｂ）の多価アルコールの配合量を１０％とした比較例３についても塗布後の化粧膜に柔軟性がなく、ツッパリ感が感じられた。更に、成分（ｂ）の多価アルコールの配合量を４５％とした比較例４は経時で粉体成分がヨレ、化粧持ちに劣るものであった。また、成分（ｃ）のアニオン性界面活性剤を配合しない比較例５においては、製造時に粉体成分、特に赤色２２６号、青色４０４号、酸化鉄、雲母チタンの分散性が著しく低下し、製造後得られた水性アイシャドウと塗布後の色調が異なり化粧効果および化粧持ちに劣るものであった。
As is apparent from the results in Table 1, the aqueous eye shadow of the present invention has a fresh feeling of use, high adhesion, and excellent makeup of powder components such as pigments, pearl agents, and lame agents. It was a water-based eye shadow with excellent flexibility.
On the other hand, the blending amount of the water-insoluble film forming agent of component (a) was set to 0.18% (0.4% as an alkyl acrylate copolymer ammonium polymer emulsion). However, it was difficult to uniformly apply the decorative film. Further, Comparative Example 2 in which the blending amount of the water-insoluble film-forming agent of component (a) was 5.4% (12% as the alkyl acrylate copolymer ammonium polymer emulsion) was used in spite of the aqueous eye shadow. The freshness was impaired, and the coated film after application was not flexible and a strong feeling of touch was felt. Furthermore, the spread during use was poor. Also in Comparative Example 3 in which the blending amount of the polyhydric alcohol of component (b) was 10%, the decorative film after application was not flexible, and a feeling of touch was felt. Furthermore, in Comparative Example 4 in which the blending amount of the polyhydric alcohol of component (b) was 45%, the powder component was inferior and the makeup lasting inferior over time. Further, in Comparative Example 5 in which the anionic surfactant of component (c) is not blended, the dispersibility of the powder components, particularly red No. 226, blue No. 404, iron oxide, and mica titanium is significantly reduced during the production. The aqueous eye shadow obtained later was different in color tone after application and was inferior in makeup effect and long-lasting makeup.
Claims (5)
（ａ）水不溶性皮膜形成剤を０．３〜４質量％
（ｂ）多価アルコールを１５〜４０質量％
（ｃ）アニオン性界面活性剤
（ｄ）粉体
を配合したことを特徴とする水性アイシャドウ。 The following components (a) to (d);
(A) 0.3 to 4% by mass of a water-insoluble film forming agent
(B) 15-40 mass% of polyhydric alcohol
(C) An aqueous eye shadow comprising an anionic surfactant (d) powder.