JP2008030987A - 焼成炉での廃プラスチックの利用方法 - Google Patents
焼成炉での廃プラスチックの利用方法 Download PDFInfo
- Publication number
- JP2008030987A JP2008030987A JP2006205747A JP2006205747A JP2008030987A JP 2008030987 A JP2008030987 A JP 2008030987A JP 2006205747 A JP2006205747 A JP 2006205747A JP 2006205747 A JP2006205747 A JP 2006205747A JP 2008030987 A JP2008030987 A JP 2008030987A
- Authority
- JP
- Japan
- Prior art keywords
- waste plastic
- fuel
- rotary kiln
- blown
- chlorine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】焼成炉内の原料を燃料の燃焼により加熱して焼成品を製造する際に、前記燃料の一部として塩素含有樹脂を含む廃プラスチックを用いる方法であって、前記焼成炉内に水または水蒸気を吹き込むことを特徴とする焼成炉での廃プラスチックの利用方法を用いる。燃料の燃焼用空気とともに水または水蒸気を吹き込むこと、水または水蒸気の吹き込み量と、廃プラスチックに由来して吹き込まれる塩素量とのモル比が、1以上となるように水または水蒸気の吹き込みを行うことが好ましい。
【選択図】図1
Description
(1)焼成炉内の原料を燃料の燃焼により加熱して焼成品を製造する際に、前記燃料の一部として塩素含有樹脂を含む廃プラスチックを用いる方法であって、前記焼成炉内に水または水蒸気を吹き込むことを特徴とする焼成炉での廃プラスチックの利用方法。
(2)燃料の燃焼用空気とともに水または水蒸気を吹き込むことを特徴とする(1)に記載の焼成炉での廃プラスチックの利用方法。
(3)水または水蒸気の吹き込み量と、廃プラスチックに由来して吹き込まれる塩素量とのモル比が、1以上となるように水または水蒸気の吹き込みを行うことを特徴とする(1)または(2)に記載の焼成炉での廃プラスチックの利用方法。
CaCO3+2HCl=CaCl2+CO2+H2O・・・(c)
CaO+2HCl=CaCl2+H2O・・・(d)
従って、系内に水あるいは水蒸気が共存すれば、CaCl2の脱塩素反応が進行し、生石灰中へのCaCl2の混入を極めて低く抑えることが可能である。しかしながら、ロータリーキルン内の塩化水素生成領域〜キルン出口間のガス中の水分濃度は極めて低いことから、本発明では、ロータリーキルン内に水または水蒸気を吹き込むことで、水分濃度を高めるものとする。水または水蒸気は、ロータリーキルンの主燃料の燃焼用空気とともに吹き込むことが好ましい。または、ロータリーキルン出口に水蒸気あるいは水噴霧用ランスを設置し、ロータリーキルン内に水または水蒸気を吹き込むことが好ましい。水または水蒸気の吹き込み位置は、塩化水素が生成する位置より出口側であること、廃プラスチック吹込みランスあるいはバーナーより入口側であることが好ましい。炉内に吹き込まれた水あるいは水蒸気は、CaCl2をCaOへ変換するため、製造された生石灰または焼成ドロマイトの塩素含有量が低下する。水または水蒸気は、ロータリーキルン内を転動する生石灰または焼成ドロマイトに直接吹き付けることがより効果的である。
2 入口
3 原料
4 出口
5 吹き込み口
6 廃プラスチック吹き込み口
7 主燃料の火炎
10 ダイス孔
11 リングダイ
12(12a、12b) 転動ローラ
13 カッター
14 投入口
15 プラスチック造粒物
16 排出口
21 破砕工程
22 異物除去工程
23 造粒工程
24 吹き込み工程
25 ロータリーキルン
A 主燃料
B 燃焼用空気
C 廃プラスチック
D 燃焼用空気
E HCl生成領域
F CaCl2分解優先領域
G CaCl2生成優先領域
Claims (3)
- 焼成炉内の原料を燃料の燃焼により加熱して焼成品を製造する際に、前記燃料の一部として塩素含有樹脂を含む廃プラスチックを用いる方法であって、前記焼成炉内に水または水蒸気を吹き込むことを特徴とする焼成炉での廃プラスチックの利用方法。
- 燃料の燃焼用空気とともに、水または水蒸気を吹き込むことを特徴とする請求項1に記載の焼成炉での廃プラスチックの利用方法。
- 水または水蒸気の吹き込み量と、廃プラスチックに由来して吹き込まれる塩素量とのモル比が、1以上となるように水または水蒸気の吹き込みを行うことを特徴とする請求項1または請求項2に記載の焼成炉での廃プラスチックの利用方法。