JP2008006622A - Frp molding and washing place floor pan - Google Patents
Frp molding and washing place floor pan Download PDFInfo
- Publication number
- JP2008006622A JP2008006622A JP2006177047A JP2006177047A JP2008006622A JP 2008006622 A JP2008006622 A JP 2008006622A JP 2006177047 A JP2006177047 A JP 2006177047A JP 2006177047 A JP2006177047 A JP 2006177047A JP 2008006622 A JP2008006622 A JP 2008006622A
- Authority
- JP
- Japan
- Prior art keywords
- smc
- sheet
- resin
- molded product
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、表面シートにより表面層を形成したFRP成形品及び洗い場床パンに関するものである。 The present invention relates to an FRP molded product having a surface layer formed of a surface sheet and a washing floor floor pan.
従来からSMCからなる基材層と、繊維補強材と、不織布に熱硬化性樹脂を含浸させた表面シートとを積層一体成形したFRP成形品が特許文献1により知られている。 Conventionally, Patent Document 1 discloses an FRP molded product in which a base material layer made of SMC, a fiber reinforcing material, and a surface sheet in which a nonwoven fabric is impregnated with a thermosetting resin are integrally laminated.
しかしながら、上記特許文献1に示された従来例にあっては、繊維補強材を、SMCからなる基材層と、熱硬化性樹脂を含浸させた表面シートとの間に介在させて全体を加熱加圧することで一体成形するものであるから、加熱加圧する際に基材層を形成するためのSMCの含浸樹脂が繊維補強材内に入り込み、更に、繊維補強材を通過して表面シート部分に圧入し、表面シートの表面に部分的にSMC中の含浸樹脂が突き抜けて露出するおそれがある。このようにして成形されるFRP成形品の表面層は表面シートにより形成されるのでFRP成形品の表面の特性は表面シートにより特定される特性となる。しかしながら、上記のように表面シートに部分的にSMC中の含浸樹脂が突き抜けて露出するため、FRP成形品の表面の一部のSMC中の含浸樹脂が突き抜けて露出する部分においては、表面シートにより特定される特性と異なり、表面特性が均一にならないという問題がある。 However, in the conventional example shown in Patent Document 1, the whole is heated by interposing a fiber reinforcing material between a base material layer made of SMC and a surface sheet impregnated with a thermosetting resin. Since it is integrally formed by pressurization, the SMC impregnation resin for forming the base material layer enters the fiber reinforcement when heated and pressurized, and further passes through the fiber reinforcement to the surface sheet portion. There is a possibility that the impregnated resin in the SMC may partially penetrate and be exposed on the surface of the topsheet. Since the surface layer of the FRP molded product formed in this way is formed by the surface sheet, the surface characteristics of the FRP molded product become the characteristics specified by the surface sheet. However, since the impregnated resin in the SMC partially penetrates and is exposed on the top sheet as described above, in the part where the impregnated resin in the SMC part of the surface of the FRP molded product penetrates and is exposed, Unlike the specified characteristics, there is a problem that the surface characteristics are not uniform.
また、上記特許文献1に示されたFRP成形品は、表面に微小なクラックや凹凸を形成する物理的処理やプラズマ処理やコロナ放電処理等による化学的処理により親水化処理を行うことで、表面の排水性及び乾燥性を良好にするようにしているが、この従来例にあっては、表面に物理的処理や化学的処理を施すことで親水化処理を行うものであるから、親水化処理のための特別な工程が必要となり、コストが高くなる。
本発明は上記の従来の問題点に鑑みて発明したものであって、SMCの含浸樹脂が表面層に突き抜けて露出することがなく、表面層を、表面シートのみによる均質な特性にすることができ、また、物理的処理や化学的処理による親水化処理を行うことなく簡単な構成で表面の親水性を持たせることができて表面の排水性や乾燥性に優れたFRP成形品及び洗い場床パンを提供することを課題とするものである。 The present invention has been invented in view of the above-mentioned conventional problems, and the SMC impregnated resin does not penetrate through the surface layer and is exposed, and the surface layer is made to have uniform characteristics only by the surface sheet. FRP molded products and washroom floors that can be made hydrophilic with a simple structure and have excellent surface drainage and drying properties without performing hydrophilic treatment by physical treatment or chemical treatment. The challenge is to provide bread.
上記課題を解決するために本発明に係るFRP成形品は、SMCからなる基材層1と、不織布に樹脂を含浸させた中間シートよりなる中間層2と、不織布に樹脂を含浸させた表面シートよりなる表面層3とを上下に積層一体成形したFRP成形品であって、上記SMCと表面シートとの間に介在される中間シートが上記SMCや表面シートよりも速硬性のものであることを特徴とするものである。
In order to solve the above problems, an FRP molded product according to the present invention includes a base material layer 1 made of SMC, an
このように表面シートを設けることで、表面をSMCとは別材料の層にできるのみならず、表面をSMCの材料とは別の層とするものにおいて、中間層2を形成するための中間シートがSMCや表面シートよりも速硬性であるので、厚みの厚い基材層1を形成するためのSMCの含浸樹脂が速硬性の中間シートにより遮られて表面シート側に突き抜けて露出することがなく、この結果、SMC成形品4の表面は表面シートのみによる均質な特性の表面層3とすることができる。
By providing the surface sheet in this way, not only the surface can be made of a layer different from the material of SMC, but also an intermediate sheet for forming the
また、表面シート、中間シートの含浸樹脂がSMCの含浸樹脂であるポリエステル樹脂よりも親水性の優れたアクリル樹脂又はポリ酢酸ビニル樹脂又はポリウレタン樹脂で構成してあることが好ましい。 Moreover, it is preferable that the impregnating resin of the top sheet and the intermediate sheet is made of an acrylic resin, a polyvinyl acetate resin, or a polyurethane resin having a hydrophilicity superior to that of the polyester resin that is an SMC impregnating resin.
このような構成とすることで、表面層3が親水性を有した表面シートのみにより構成され、表面層3にSMCの含浸樹脂が突き抜けて露出することによる親水性の低下を防ぐことができる。
By setting it as such a structure, the
また、表面シート、中間シートの不織布がガラス、あるいはガラスとポリエステルが混紗されたものであることが好ましい。 Moreover, it is preferable that the nonwoven fabric of a surface sheet and an intermediate | middle sheet | seat is what mixed glass or glass and polyester.
このような構成とすることで、成形後に表面層3、中間層2が透明になり、SMC色が透過してSMC色を生かすことができる。
With such a configuration, the
また、上記のようなFRP成形品4が洗い場床パン5であることが好ましい。 Moreover, it is preferable that the FRP molded product 4 as described above is the washroom floor pan 5.
本発明は、SMCの含浸樹脂が表面層に突き抜けて露出することがなく、表面層を、表面シートのみによる均質な特性にすることができ、表面の特性のばらつきが無い。 In the present invention, the impregnated resin of SMC does not penetrate through the surface layer and is exposed, and the surface layer can be made to have uniform characteristics only by the surface sheet, and there is no variation in surface characteristics.
また、表面シート、中間シートの含浸樹脂を親水性のあるアクリル樹脂又はポリ酢酸ビニル樹脂又はポリウレタン樹脂で構成することで、従来のように物理的処理や化学的処理を施すことで親水化処理を行うことなく簡単な構成で表面の親水性を持たせることができて表面の排水性や乾燥性に優れている。 Also, by making the impregnating resin of the top sheet and intermediate sheet with hydrophilic acrylic resin, polyvinyl acetate resin or polyurethane resin, the hydrophilic treatment can be performed by applying physical treatment or chemical treatment as before. It is possible to give the surface hydrophilicity with a simple configuration without performing it, and the surface has excellent drainage and drying properties.
以下、本発明を添付図面に示す実施形態に基いて説明する。 Hereinafter, the present invention will be described based on embodiments shown in the accompanying drawings.
本発明のSMC成形品4は、図1に示すように、SMCからなる基材層1と、その上の不織布に樹脂を含浸させた中間シートよりなる中間層2と、その上の不織布に樹脂を含浸させた表面シートよりなる表面層3との3層構造となっており、SMC、中間シート、表面シートとを同時成形することで3層を上下に積層一体成形して構成してある。
As shown in FIG. 1, the SMC molded product 4 of the present invention includes a base material layer 1 made of SMC, an
基材層1を形成するためのSMCはガラス繊維マットに樹脂を含浸させたもので、含浸樹脂として不飽和ポリエステル樹脂を挙げることができる。 The SMC for forming the base material layer 1 is obtained by impregnating a glass fiber mat with a resin, and examples of the impregnating resin include unsaturated polyester resins.
中間層2を形成するための中間シート、表面層3を形成するための表面シートはいずれも、不織布に樹脂を含浸したもので、この中間シート、表面シートに含浸する樹脂としてはSMCの含浸樹脂とは異なる樹脂、つまり、SMCの含浸樹脂であるポリエステル樹脂よりも親水性の優れたアクリル樹脂又はポリ酢酸ビニル樹脂又はポリウレタン樹脂が用いられる。また、中間シートはSMC、表面シートよりも速硬性のものが用いられる。中間シートを速硬性とするには例えば反応を速めるための触媒を添加する。
Both the intermediate sheet for forming the
上記のような硬化前のSMC、中間シート、表面シートを用いて成形金型により一体に同時成形してFRP成形品を成形するのであるが、この場合、下金型に表面シート、中間シート、SMCの順で載置するか、又は、下金型にSMC、中間シート、表面シートの順で載置し(つまり、意匠側となる方の金型側に表面シートが位置し、裏面側となる金型側にSMCが位置するようにする)、その後、上金型を移動して加熱加圧成形することで、SMCよりなる基材層1、中間シートよりなる中間層2、表面シートよりなる表面層3が積層一体化される。
The SRP before curing as described above, an intermediate sheet, and a surface sheet are integrally molded simultaneously by a molding die to form an FRP molded product. In this case, a surface sheet, an intermediate sheet, Place in the order of SMC, or place in the lower mold in the order of SMC, intermediate sheet, surface sheet (that is, the surface sheet is located on the mold side which is the design side, SMC is positioned on the mold side), and then the upper mold is moved and heated and pressed to form a base material layer 1 made of SMC, an
ここで、中間シートがSMC、表面シートよりも速硬性のものであるため、上記加熱加圧成形の際、中間シートがSMCや表面シートよりも速く硬化し、このため、加熱加圧により厚みの厚いSMCの含浸樹脂が中間シートを突き抜けて、更に、表面シートの表面側(金型と接する面)に突き抜けるのが防止される。したがって、成形されたFRP成形品4においては、表面層3にSMCの含浸樹脂が突き抜けて露出せず、表面層3は表面シートのみにより形成されることになり、表面シートとして親水性の優れたアクリル樹脂又はポリ酢酸ビニル樹脂又はポリウレタン樹脂を用いることで、優れた親水性を発揮できることになる。また、表面シートとしてアクリル樹脂を用いた場合は表面硬度も向上させることができる。
Here, since the intermediate sheet is faster-hardening than SMC and the surface sheet, the intermediate sheet is cured faster than SMC and the surface sheet during the heat and pressure molding. It is possible to prevent the thick SMC impregnating resin from penetrating the intermediate sheet and further penetrating to the surface side (surface in contact with the mold) of the surface sheet. Therefore, in the molded FRP molded product 4, the SMC impregnated resin does not penetrate through the
上記表面シート、中間シートの不織布としてはガラス、あるいはガラスとポリエステルが混紗されたものを用いることが好ましい。 It is preferable to use glass or a mixture of glass and polyester as the nonwoven fabric for the top sheet and intermediate sheet.
このように、表面シート、中間シートの不織布としてはガラス、あるいはガラスとポリエステルが混紗されたものを用いると、表面シート、中間シートが成形後に透明になり、SMC色が透過してSMC色を生かすことができる。 As described above, when the surface sheet and the nonwoven sheet of the intermediate sheet are made of glass or a mixture of glass and polyester, the surface sheet and the intermediate sheet become transparent after molding, and the SMC color is transmitted and the SMC color is changed. You can save it.
上記のようなFRP成形品4としては洗い場床パン5、あるいはカウンター等各種の水廻りで使用される商品であり、表面が親水性であるため、通常のSMC成形品に比べて、同じ残水量でも残水の表面積が大きくなるので、排水性が良くなると共に濡れてから乾燥するまでの時間が短くなり、排水性、乾燥性が優れたものとなる。また、湿気が少なくなるので、防カビ効果もある。 The FRP molded product 4 as described above is a product used in various places such as a washing floor pan 5 or a counter, and since the surface is hydrophilic, the amount of residual water is the same as that of a normal SMC molded product. However, since the surface area of the residual water is increased, the drainage is improved and the time from wet to dry is shortened, and the drainage and drying are excellent. Further, since the moisture is reduced, there is also an antifungal effect.
以下、本発明の実施例を説明する。 Examples of the present invention will be described below.
(実施例)
○ SMC
不飽和ポリエステル樹脂(スチレン希釈40%)80重量部、ポリスチレン系低収縮化剤(スチレン希釈20%)20重量部、炭酸カルシウム150重量部、ステアリン酸亜鉛5重量部、酸化マグネシウム1重量部、t−ブチルパーベンゾエート1重量部、パラベンゾキノン0.1重量部、着色剤(スチレン希釈20%)5重量部、スチレンモノマー5重量部を配合したコンパウンドを作成し、このコンパウンド重量に対して22%(つまり、コンパウンド重量100に対して22パーセント)配合してSMCを作成した。
(Example)
○ SMC
80 parts by weight of unsaturated polyester resin (styrene dilution 40%), 20 parts by weight of polystyrene-based low shrinkage agent (styrene dilution 20%), 150 parts by weight of calcium carbonate, 5 parts by weight of zinc stearate, 1 part by weight of magnesium oxide, t -A compound containing 1 part by weight of butyl perbenzoate, 0.1 part by weight of parabenzoquinone, 5 parts by weight of a colorant (20% styrene dilution), and 5 parts by weight of styrene monomer was prepared, and 22% of the compound weight ( In other words, SMC was prepared by blending 22% based on the compound weight of 100).
○ 表面シート
ガラス不織布(目付け50g/m2)に硬化に要する時間をSMCの硬化時間と合わせるように硬化遅延剤を添加したアクリル系樹脂(目付け50g/m2)を含浸して表面シートを形成した。このアクリル系樹脂は硬化を遅延させるために硬化遅延剤を添加したもので、140℃の熱板上で5分間で硬化する(SMCの硬化時間と同じ)ように調整されたものを使用している。
○ A surface sheet is formed by impregnating an acrylic resin (weight per unit weight 50 g / m 2 ) to which a curing retarder is added so that the time required for curing the surface sheet glass nonwoven fabric (weight per unit 50 g / m 2 ) matches the curing time of SMC. did. This acrylic resin has a curing retarder added to delay curing, and is prepared so that it cures on a hot plate at 140 ° C. in 5 minutes (same as SMC curing time). Yes.
○ 中間シート
ガラス不織布(目付け50g/m2)に硬化を速めるための触媒を添加したアクリル系樹脂(目付け50g/m2)を含浸して中間シートを形成した。このアクリル系樹脂は硬化を速めるための触媒を添加したもので、140℃の熱板上で1分間で硬化するように調整されたものを使用している。
○ to form an intermediate sheet intermediate sheet glass nonwoven acrylic resin with the addition of catalysts to accelerate the cure (basis weight 50 g / m 2) to (basis weight 50 g / m 2) was impregnated. This acrylic resin is added with a catalyst for accelerating curing, and is prepared so as to be cured on a hot plate at 140 ° C. in 1 minute.
○ 成形条件
上記のようにして得た表面シート、中間シート、SMC(900g)の順に金型(サイズ300mm×300mm)にセットし、下金型(意匠側)を145℃、上金型(裏面側)を130℃、プレス圧7MPa、成形時間5分で加熱加圧成形して実施例のFRP成形品を成形した。
Molding conditions Set the top sheet, intermediate sheet, and SMC (900 g) in the above order in the mold (size 300 mm x 300 mm), lower mold (design side) at 145 ° C, upper mold (back surface) The FRP molded product of the example was molded by heat and pressure molding at 130 ° C., a press pressure of 7 MPa, and a molding time of 5 minutes.
(比較例)
上記SMC(900g)のみを金型(サイズ300mm×300mm)にセットし、下金型(意匠側)を145℃、上金型(裏面側)を130℃、プレス圧7MPa、成形時間5分で加熱加圧成形して比較例のFRP成形品を成形した。
(Comparative example)
Only SMC (900 g) is set in a mold (size 300 mm × 300 mm), the lower mold (design side) is 145 ° C., the upper mold (back side) is 130 ° C., the press pressure is 7 MPa, and the molding time is 5 minutes. The FRP molded product of the comparative example was molded by heat and pressure molding.
上記のようにして得た実施例のFRP成形品と、比較例のFRP成形品を中性洗剤で洗浄、乾燥後、接触角と鉛筆硬度の性能を評価した。結果を下記の表1に示す。 The FRP molded product of the example obtained as described above and the FRP molded product of the comparative example were washed with a neutral detergent, dried, and then evaluated for contact angle and pencil hardness performance. The results are shown in Table 1 below.
上記表1で明らかなように、実施例のFRP成形品は比較例のFRP成形品に比べ、接触角が下がって親水性が優れたものとなり、鉛筆硬度が上がることが判る。 As apparent from Table 1 above, it can be seen that the FRP molded product of the example has a lower contact angle and superior hydrophilicity than the FRP molded product of the comparative example, and the pencil hardness is increased.
1 基材層
2 中間層
3 表面層
4 SMC成形品
5 洗い場床パン
DESCRIPTION OF SYMBOLS 1
Claims (4)