JP2007331231A - Film for whiteboard - Google Patents

Film for whiteboard Download PDF

Info

Publication number
JP2007331231A
JP2007331231A JP2006165762A JP2006165762A JP2007331231A JP 2007331231 A JP2007331231 A JP 2007331231A JP 2006165762 A JP2006165762 A JP 2006165762A JP 2006165762 A JP2006165762 A JP 2006165762A JP 2007331231 A JP2007331231 A JP 2007331231A
Authority
JP
Japan
Prior art keywords
whiteboard
active energy
energy ray
film
coating layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2006165762A
Other languages
Japanese (ja)
Inventor
Koichi Hirayama
浩一 平山
Chihiro Shintani
千尋 新谷
Aya Takeda
彩 武田
Kenichi Matsumoto
健一 松本
Tatsuo Meguro
達夫 目黒
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AZUSA KK
NIPPON RIKAGAKU KOGYO KK
SANYO KK
TOYO HOZAI KK
Sanyo KK
Original Assignee
AZUSA KK
NIPPON RIKAGAKU KOGYO KK
SANYO KK
TOYO HOZAI KK
Sanyo KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by AZUSA KK, NIPPON RIKAGAKU KOGYO KK, SANYO KK, TOYO HOZAI KK, Sanyo KK filed Critical AZUSA KK
Priority to JP2006165762A priority Critical patent/JP2007331231A/en
Publication of JP2007331231A publication Critical patent/JP2007331231A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a film for a whiteboard which makes excellent the writing properties, erasability and antiglare properties of the whiteboard. <P>SOLUTION: The film 13 for the whiteboard is formed on the surface of a substrate 12 for the whiteboard and the film 13 is constituted by forming an activation energy beam cured type resin film layer 15 on the surface of a transparent plastic film 14. The activation energy beam cured type resin film layer 15 contains spherical particulates 16 and an activation energy beam cured type silicone resin 17. It is desirable that the thickness of the layer 15 is 1-8 μm and that the average particle diameter of the particulates 16 is 2-10 μm. <P>COPYRIGHT: (C)2008,JPO&INPIT

Description

本発明は、ホワイトボードの表面材として用いるホワイトボード用フィルムに関するものであり、更に詳しくは、ホワイトボードの筆記性、消去性及び防眩性が優れたものとなるホワイトボード用フィルムに関するものである。   The present invention relates to a whiteboard film used as a surface material of a whiteboard, and more particularly to a whiteboard film that has excellent whiteboard writing properties, erasability and antiglare properties. .

従来、表面にエンボス加工が施された所要粗度を有するシート材が知られている。このシート材を所定の基板に貼着して、筆記用ボードとして使用する場合には、エンボス加工の凹凸によって筆記性が向上することとなる。   Conventionally, a sheet material having a required roughness whose surface is embossed is known. When this sheet material is attached to a predetermined substrate and used as a writing board, the writing property is improved by the embossed irregularities.

なお、ホワイトボード用シートとしては、例えば特開2002−362092号公報又は特開2004−148589号公報に開示されたものが知られている(特許文献1、2参照)。
特開2002−362092号公報 特開2004−148589号公報
In addition, as a sheet | seat for whiteboards, what was disclosed by Unexamined-Japanese-Patent No. 2002-362092 or Unexamined-Japanese-Patent No. 2004-148589 is known, for example (refer patent document 1, 2).
JP 2002-362092 A JP 2004-148589 A

従来例のシート材を用いた筆記用ボードにおいては、マーカーがエンボス加工の凹凸部位に付着するので、クリーナーで拭き取ったときに文字等が消えにくいという欠点を有する。つまり、文字等の消去性が悪いこととなる。   In the writing board using the sheet material of the conventional example, since the marker adheres to the embossed uneven portion, there is a disadvantage that characters and the like are difficult to disappear when wiped with a cleaner. That is, the erasability of characters and the like is poor.

また、エンボス加工の加工精度は必ずしも均一ではなく、加工時の温度やシート材の硬柔又は厚薄等の違いによって、凹凸が不均一に形成されるおそれがある。この場合は、筆記用ボードの筆記性、消去性及び防眩性等が不均一になり、筆記した部位によって異なるという不都合が生ずる。   In addition, the processing accuracy of embossing is not necessarily uniform, and unevenness may be formed unevenly due to differences in temperature during processing or the flexibility or thickness of the sheet material. In this case, the writing board, the erasability, the anti-glare property and the like of the writing board become non-uniform, and there arises a disadvantage that the writing board differs depending on the written part.

従って、従来例における場合においては、筆記用ボードの筆記性、消去性及び防眩性等を向上させることと、それらの性能を均一にすることとに解決しなければならない課題を有している。   Therefore, in the case of the conventional example, there is a problem that must be solved to improve the writing property, erasability, anti-glare property, etc. of the writing board and to make the performance uniform. .

前記従来例の課題を解決する具体的手段として本発明は、ホワイトボード用の基板の表面に形成するホワイトボード用フィルムであって、該ホワイトボード用フィルムは、透明プラスチックフィルムの表面に、活性エネルギー線硬化型樹脂被膜層を形成してなり、該活性エネルギー線硬化型樹脂被膜層は、球状の微粒子及び活性エネルギー線硬化型シリコーン樹脂を含有してなることを特徴とするホワイトボード用フィルムを提供するものである。   As a specific means for solving the problems of the conventional example, the present invention provides a whiteboard film formed on the surface of a whiteboard substrate, the whiteboard film having an active energy on the surface of a transparent plastic film. Provided is a film for whiteboard comprising a linear curable resin coating layer, wherein the active energy ray curable resin coating layer contains spherical fine particles and an active energy ray curable silicone resin. To do.

また、前記活性エネルギー線硬化型樹脂被膜層は、厚さが1〜8μmの範囲であり、前記微粒子の平均粒径は、2〜10μmの範囲である構成としたものであり、更に、前記活性エネルギー線硬化型樹脂被膜層は、該樹脂が100重量部に対して、活性エネルギー線硬化型シリコーン樹脂が0.1〜20重量部の範囲で含有する構成としたものである。   The active energy ray-curable resin coating layer has a thickness in the range of 1 to 8 μm, and the average particle size of the fine particles is in the range of 2 to 10 μm. The energy ray curable resin coating layer is configured to contain the active energy ray curable silicone resin in the range of 0.1 to 20 parts by weight with respect to 100 parts by weight of the resin.

本発明に係るホワイトボード用フィルムは、ホワイトボード用の基板の表面に形成するホワイトボード用フィルムであって、該ホワイトボード用フィルムは、透明プラスチックフィルムの表面に、活性エネルギー線硬化型樹脂被膜層を形成してなり、該活性エネルギー線硬化型樹脂被膜層は、球状の微粒子及び活性エネルギー線硬化型シリコーン樹脂を含有してなることによって、ホワイトボードの表面に極微細で且つ均一な凹凸形状が形成されることとなる。従って、この凹凸形状により筆記性及び消去性が向上するだけでなく、光の反射が拡散するので防眩性に優れることとなる。更には、活性エネルギー線硬化型樹脂被膜層は硬質であり耐擦傷性が高く、ホワイトボードの表面が傷つきにくいという種々の優れた効果を奏する。   The whiteboard film according to the present invention is a whiteboard film formed on the surface of a whiteboard substrate, and the whiteboard film is an active energy ray-curable resin coating layer on the surface of a transparent plastic film. The active energy ray curable resin coating layer contains spherical fine particles and an active energy ray curable silicone resin, so that the surface of the whiteboard has an extremely fine and uniform uneven shape. Will be formed. Therefore, the concavo-convex shape not only improves the writing property and erasability but also improves the antiglare property because the reflection of light diffuses. Furthermore, the active energy ray-curable resin coating layer is hard, has high scratch resistance, and exhibits various excellent effects that the surface of the whiteboard is hardly damaged.

また、活性エネルギー線硬化型樹脂被膜層は、厚さが1〜8μmの範囲であり、前記微粒子の平均粒径は、2〜10μmの範囲であることによって、活性エネルギー線硬化型樹脂被膜層の表面に微粒子が数μm均一に突出することとなる。従って、ホワイトボードの表面に極微細で均一な凹凸形状が形成されるので、筆記性、消去性及び防眩性が向上し、それらの性能が均一なものになるという優れた効果を奏する。   The active energy ray-curable resin coating layer has a thickness in the range of 1 to 8 μm, and the average particle size of the fine particles is in the range of 2 to 10 μm. The fine particles protrude uniformly on the surface by several μm. Therefore, since a very fine and uniform uneven shape is formed on the surface of the whiteboard, the writing property, the erasing property and the anti-glare property are improved, and there is an excellent effect that the performance becomes uniform.

更に、前記活性エネルギー線硬化型樹脂被膜層は、該樹脂が100重量部に対して、活性エネルギー線硬化型シリコーン樹脂が0.1〜20重量部の範囲で含有することによって、ホワイトボードの表面が滑性をもって形成されるので、筆記性や、特に消去性がいっそう向上するという優れた効果を奏する。   Furthermore, the active energy ray-curable resin coating layer contains the active energy ray-curable silicone resin in the range of 0.1 to 20 parts by weight with respect to 100 parts by weight of the resin, thereby allowing the surface of the whiteboard to Is formed with a slippery property, so that it has an excellent effect that the writing property and particularly the erasability are further improved.

次に、本発明の実施の形態について図面を参照しながら説明する。まず、図1は、ホワイトボード11の一部を拡大して略示的に示した断面図である。このホワイトボード11は、基板12の表面に接着等の所定の手段でホワイトボード用フィルム13が設けられている。   Next, embodiments of the present invention will be described with reference to the drawings. First, FIG. 1 is a cross-sectional view schematically showing an enlarged part of the whiteboard 11. The whiteboard 11 is provided with a whiteboard film 13 on the surface of the substrate 12 by a predetermined means such as adhesion.

基板12は、アルミニウムやスチール等の金属材又はホーロー等で、所定厚さの板状に形成されており、その表面が白色又は所要の色彩に着色されている。   The substrate 12 is made of a metal material such as aluminum or steel or enamel, and is formed in a plate shape having a predetermined thickness, and the surface thereof is colored white or in a required color.

ホワイトボード用フィルム13は、透明プラスチックフィルム14の表面に、活性エネルギー線硬化型樹脂被膜層15を形成してなる。   The whiteboard film 13 is formed by forming an active energy ray-curable resin coating layer 15 on the surface of a transparent plastic film 14.

透明プラスチックフィルム14は、透明性のあるプラスチックのフィルムであり、具体的に一例を上げれば、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリエステルフィルム、ポリエチレンフィルム、ポリプロピレンフィルム、又はセロファン等である。   The transparent plastic film 14 is a transparent plastic film. Specifically, examples thereof include polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polyester film, polyethylene film, polypropylene film, and cellophane.

活性エネルギー線硬化型樹脂は、紫外線等の活性エネルギー線を照射することにより硬化するハードコート用樹脂であり、例えば、アクリル系樹脂又はシロキサン系樹脂等の従来周知のハードコート用樹脂を用いる。そして、このハードコート用樹脂に光重合開始剤等の従来周知の添加剤を添加して、所定の方法で紫外線等を照射することにより、活性エネルギー線硬化型樹脂被膜層15が形成される。
活性エネルギー線硬化型樹脂被膜層15は、厚さが1〜8μmの範囲であることが望ましい。また、活性エネルギー線硬化型樹脂被膜層15は硬質であり、耐擦傷性が高く、ホワイトボード11の表面に傷がつきにくいこととなる。
The active energy ray curable resin is a hard coat resin that is cured by irradiating active energy rays such as ultraviolet rays. For example, a conventionally known hard coat resin such as an acrylic resin or a siloxane resin is used. An active energy ray-curable resin coating layer 15 is formed by adding a conventionally known additive such as a photopolymerization initiator to the hard coat resin and irradiating it with ultraviolet rays or the like by a predetermined method.
The active energy ray-curable resin coating layer 15 preferably has a thickness in the range of 1 to 8 μm. Further, the active energy ray curable resin coating layer 15 is hard, has high scratch resistance, and the surface of the whiteboard 11 is hardly damaged.

また、活性エネルギー線硬化型樹脂被膜層15は、平均粒径が2〜10μmの範囲の球状の微粒子16と、活性エネルギー線硬化型シリコーン樹脂17とを含有してなる。   The active energy ray-curable resin coating layer 15 contains spherical fine particles 16 having an average particle size in the range of 2 to 10 μm and an active energy ray-curable silicone resin 17.

球状の微粒子16は、具体的に一例を上げれば、シリカ、アルミナ、チタニア、ジルコニア、雲母、タルク又は炭酸カルシウム等の球状の無機微粒子である。   Specifically, the spherical fine particles 16 are spherical inorganic fine particles such as silica, alumina, titania, zirconia, mica, talc, or calcium carbonate.

活性エネルギー線硬化型シリコーン樹脂17は、上述のように、紫外線等の活性エネルギー線を照射することにより硬化するハードコート用樹脂であり、従来周知のシリコーン系樹脂を用いる。
このように、活性エネルギー線硬化型樹脂被膜層15に、活性エネルギー線硬化型シリコーン樹脂17が含有されることにより、表面が滑性をもって形成されることとなる。
なお、活性エネルギー線硬化型シリコーン樹脂17は、活性エネルギー線硬化型樹脂100重量部に対して、0.1〜20重量部の範囲で含有することが望ましい。
As described above, the active energy ray-curable silicone resin 17 is a hard coat resin that is cured by irradiation with active energy rays such as ultraviolet rays, and a conventionally known silicone resin is used.
As described above, when the active energy ray-curable resin coating layer 15 contains the active energy ray-curable silicone resin 17, the surface is formed with lubricity.
The active energy ray-curable silicone resin 17 is desirably contained in the range of 0.1 to 20 parts by weight with respect to 100 parts by weight of the active energy ray-curable resin.

このような構成のホワイトボード用フィルム13は、活性エネルギー線硬化型樹脂被膜層15の表面に微粒子16が数μm均一に突出することとなる。つまり、ホワイトボード11の表面に極微細で均一な凹凸形状が形成されるので、筆記性、消去性及び防眩性が向上し、それらの性能が均一なものになる。なお、活性エネルギー線硬化型樹脂被膜層15の表面に形成される凹凸形状は、その粗さがRa=0.5〜1.5の範囲にあることが望ましい。   In the whiteboard film 13 having such a configuration, the fine particles 16 protrude uniformly on the surface of the active energy ray-curable resin coating layer 15 by several μm. That is, since an extremely fine and uniform uneven shape is formed on the surface of the whiteboard 11, the writing property, the erasing property and the antiglare property are improved, and the performance is uniform. In addition, as for the uneven | corrugated shape formed in the surface of the active energy ray hardening-type resin coating layer 15, it is desirable that the roughness exists in the range of Ra = 0.5-1.5.

次に、本発明の実施例及び比較例について説明し、それぞれの例において得られた評価を示す。なお、筆記具は、固形マーカー(キットパス(登録商標):日本理化学工業(株)社製)を使用した。
また、筆記のしやすさとしての「筆記性」の評価は、ホワイトボードに通常の筆記状態で直径約10cmの円を連続して5回書いた時の滑らかさ、即ち、運筆の軽さを「良好」「普通」「不良」の3段階で評価した。
ホワイトボードに描いた描線の「消去性」の評価は、上記「筆記性」の評価で書いた円を、クリーナー(ダストレスクリーナー(登録商標):日本理化学工業(株)社製)を用いて、2回往復で消した時の消去面のムラを「良好」「普通」「不良」の3段階で評価した。
「防眩性」の評価は、ホワイトボードの光の反射具合を目視で判定して「良好」「不良」の2段階で評価した。
Next, Examples and Comparative Examples of the present invention will be described, and evaluations obtained in the respective examples will be shown. The writing instrument used was a solid marker (Kitpath (registered trademark): manufactured by Nippon Riken Kogyo Co., Ltd.).
In addition, the evaluation of “writeability” as the ease of writing is based on the smoothness when writing a circle of about 10 cm in diameter on a whiteboard five times in a normal writing state, that is, the lightness of writing. The evaluation was made in three stages: “good”, “normal”, and “bad”.
For the evaluation of “erasability” of drawn lines drawn on the whiteboard, use the cleaner (Dustless Cleaner (registered trademark): manufactured by Nihon Riken Kogyo Co., Ltd.) using the circle written in the above evaluation of “writing performance”. The unevenness of the erased surface when erased by two reciprocations was evaluated in three levels: “good”, “normal”, and “bad”.
The “antiglare property” was evaluated in two stages of “good” and “bad” by visually judging the light reflection state of the whiteboard.

活性エネルギー線硬化型樹脂被膜層の厚さが1〜8μmの範囲であり、球状の微粒子の平均粒径が2〜10μmの範囲であり、活性エネルギー線硬化型樹脂被膜層に活性エネルギー線硬化型シリコーン樹脂が0.1〜20重量部の範囲で含有してなるホワイトボード用フィルムを接着したホワイトボードを使用した(図1参照)。   The thickness of the active energy ray-curable resin coating layer is in the range of 1 to 8 μm, the average particle size of the spherical fine particles is in the range of 2 to 10 μm, and the active energy ray-curable resin coating layer has an active energy ray-curable resin coating layer. The white board which adhered the film for white boards which silicone resin contains in the range of 0.1-20 weight part was used (refer FIG. 1).

この実施例1のホワイトボードは、「筆記性:良好」「消去性:良好」「防眩性:良好」の評価が得られた。   The whiteboard of Example 1 was evaluated as “writing property: good”, “erasability: good”, and “antiglare property: good”.

[比較例1]
活性エネルギー線硬化型樹脂被膜層の厚さが1〜8μmの範囲であり、球状の微粒子の平均粒径が10μmを越えるものであり、活性エネルギー線硬化型樹脂被膜層に活性エネルギー線硬化型シリコーン樹脂が0.1〜20重量部の範囲で含有してなるホワイトボード用フィルムを接着したホワイトボードを使用した(図2参照)。
[Comparative Example 1]
The thickness of the active energy ray-curable resin coating layer is in the range of 1 to 8 μm, and the average particle size of the spherical fine particles exceeds 10 μm. The white board which adhered the film for white boards which resin contains in the range of 0.1-20 weight part was used (refer FIG. 2).

この比較例1のホワイトボードは、「筆記性:普通」「消去性:不良」「防眩性:良好」の評価が得られた。
従って、実施例1のホワイトボード用フィルムと比較して、微粒子の平均粒径を増大したことで、「筆記性」と「消去性」とが共に低下している。
The whiteboard of Comparative Example 1 was evaluated as “writing property: normal”, “erasability: poor”, and “antiglare property: good”.
Therefore, as compared with the whiteboard film of Example 1, both the “writing property” and the “erasability” are lowered by increasing the average particle size of the fine particles.

[比較例2]
活性エネルギー線硬化型樹脂被膜層の厚さが1〜8μmの範囲であり、球状の微粒子の平均粒径が2μm未満であり、活性エネルギー線硬化型樹脂被膜層に活性エネルギー線硬化型シリコーン樹脂が0.1〜20重量部の範囲で含有してなるホワイトボード用フィルムを接着したホワイトボードを使用した(図3参照)。
[Comparative Example 2]
The thickness of the active energy ray-curable resin coating layer is in the range of 1 to 8 μm, the average particle size of the spherical fine particles is less than 2 μm, and the active energy ray-curable silicone resin is applied to the active energy ray-curable resin coating layer. The white board which adhered the film for white boards contained in the range of 0.1-20 weight part was used (refer FIG. 3).

この比較例2のホワイトボードは、「筆記性:普通」「消去性:良好」「防眩性:不良」の評価が得られた。
従って、実施例1のホワイトボード用フィルムと比較して、微粒子の平均粒径を縮小したことで、「筆記性」と「防眩性」とが共に低下している。
The whiteboard of Comparative Example 2 was evaluated as “writing property: normal”, “erasability: good”, and “antiglare property: poor”.
Therefore, compared with the whiteboard film of Example 1, both the “writing property” and the “antiglare property” are reduced by reducing the average particle size of the fine particles.

[比較例3]
活性エネルギー線硬化型樹脂被膜層の厚さが1〜8μmの範囲であり、球状の微粒子の平均粒径が2〜10μmの範囲であり、活性エネルギー線硬化型樹脂被膜層に活性エネルギー線硬化型シリコーン樹脂が未含有のホワイトボード用フィルムを接着したホワイトボードを使用した(図4参照)。
[Comparative Example 3]
The thickness of the active energy ray-curable resin coating layer is in the range of 1 to 8 μm, the average particle size of the spherical fine particles is in the range of 2 to 10 μm, and the active energy ray-curable resin coating layer has an active energy ray-curable resin coating layer. The white board which adhere | attached the film for white boards which does not contain a silicone resin was used (refer FIG. 4).

この比較例3のホワイトボードは、「筆記性:普通」「消去性:不良」「防眩性:良好」の評価が得られた。
従って、実施例1のホワイトボード用フィルムと比較して、活性エネルギー線硬化型シリコーン樹脂を含有しないことで、「筆記性」と「消去性」とが共に低下している。
The whiteboard of Comparative Example 3 was evaluated as “writing property: normal”, “erasability: poor”, and “antiglare property: good”.
Therefore, compared with the whiteboard film of Example 1, both the “writing property” and the “erasability” are lowered by not containing the active energy ray-curable silicone resin.

[比較例4]
活性エネルギー線硬化型樹脂被膜層の厚さが1〜8μmの範囲であり、不定形状の微粒子の平均粒径が4μmであり、活性エネルギー線硬化型樹脂被膜層に活性エネルギー線硬化型シリコーン樹脂が0.1〜20重量部の範囲で含有してなるホワイトボード用フィルムを接着したホワイトボードを使用した(図5参照)。
[Comparative Example 4]
The thickness of the active energy ray curable resin coating layer is in the range of 1 to 8 μm, the average particle size of the irregularly shaped fine particles is 4 μm, and the active energy ray curable silicone resin is applied to the active energy ray curable resin coating layer. The white board which adhered the film for white boards contained in the range of 0.1-20 weight part was used (refer FIG. 5).

この比較例1のホワイトボードは、「筆記性:良好」「消去性:不良」「防眩性:良好」の評価が得られた。
従って、実施例1のホワイトボード用フィルムと比較して、不定形状の微粒子を含有させたことで、「消去性」が低下している。
The whiteboard of Comparative Example 1 was evaluated as “writing property: good”, “erasability: poor”, and “antiglare property: good”.
Therefore, compared with the whiteboard film of Example 1, the “erasability” is lowered by containing irregularly shaped fine particles.

以上の実施例1、及び比較例1〜4について、それぞれの例において得られた評価を表1に示す。

Figure 2007331231
Table 1 shows the evaluations obtained in each of Examples 1 and Comparative Examples 1 to 4 described above.
Figure 2007331231

以上の実施例1、及び比較例1〜4で説明したように、微粒子の平均粒径を増大すると、ホワイトボードの表面に形成される凹凸形状が大きくなり、その結果「筆記性」と特に「消去性」とが低下する(図2参照)。
また、微粒子の平均粒径を縮小すると、ホワイトボードの表面に形成される凹凸形状が小さくなり、その結果「筆記性」と特に「防眩性」とが共に低下する(図3参照)。
そして、活性エネルギー線硬化型樹脂被膜層に活性エネルギー線硬化型シリコーン樹脂を含有しないことで、ホワイトボードの表面の滑性が低下するので、その結果「筆記性」と特に「消去性」とが共に低下する(図4参照)。
更に、球状の微粒子に替えて、不定形状の微粒子を含有させたことで、ホワイトボードの表面に形成される凹凸形状の均一性が失われ、その結果、特に「消去性」が低下することとなる(図5参照)。
As described in Example 1 and Comparative Examples 1 to 4 above, when the average particle size of the fine particles is increased, the uneven shape formed on the surface of the whiteboard is increased. As a result, “writing property” and particularly “ "Erasability" decreases (see FIG. 2).
Further, when the average particle size of the fine particles is reduced, the uneven shape formed on the surface of the whiteboard is reduced, and as a result, both “writing property” and particularly “antiglare property” are reduced (see FIG. 3).
Further, since the active energy ray curable resin coating layer does not contain the active energy ray curable silicone resin, the slipperiness of the surface of the whiteboard is reduced, and as a result, "writing property" and particularly "erasability" are obtained. Both decrease (see FIG. 4).
Furthermore, by incorporating irregularly shaped fine particles instead of spherical fine particles, the uniformity of the irregular shape formed on the surface of the whiteboard is lost, and as a result, the “erasability” is particularly reduced. (See FIG. 5).

本発明に係るホワイトボードの一部を拡大して略示的に示した断面図である。It is sectional drawing which expanded and showed roughly a part of whiteboard concerning this invention. 比較例1に係るホワイトボードの一部を拡大して略示的に示した断面図である。10 is a cross-sectional view schematically showing an enlarged part of a whiteboard according to Comparative Example 1. FIG. 比較例2に係るホワイトボードの一部を拡大して略示的に示した断面図である。10 is an enlarged schematic cross-sectional view of a part of a whiteboard according to Comparative Example 2. FIG. 比較例3に係るホワイトボードの一部を拡大して略示的に示した断面図である。10 is an enlarged schematic cross-sectional view of a part of a whiteboard according to Comparative Example 3. FIG. 比較例4に係るホワイトボードの一部を拡大して略示的に示した断面図である。10 is an enlarged schematic cross-sectional view of a part of a whiteboard according to Comparative Example 4. FIG.

符号の説明Explanation of symbols

11 ホワイトボード
12 基板
13 ホワイトボード用フィルム
14 透明プラスチックフィルム
15 活性エネルギー線硬化型樹脂被膜層
16 微粒子
17 活性エネルギー線硬化型シリコーン樹脂
DESCRIPTION OF SYMBOLS 11 White board 12 Board | substrate 13 White board film 14 Transparent plastic film 15 Active energy ray-curable resin coating layer 16 Fine particle 17 Active energy ray-curable silicone resin

Claims (3)

ホワイトボード用の基板の表面に形成するホワイトボード用フィルムであって、
該ホワイトボード用フィルムは、透明プラスチックフィルムの表面に、活性エネルギー線硬化型樹脂被膜層を形成してなり、
該活性エネルギー線硬化型樹脂被膜層は、球状の微粒子及び活性エネルギー線硬化型シリコーン樹脂を含有してなること
を特徴とするホワイトボード用フィルム。
A whiteboard film formed on the surface of a whiteboard substrate,
The whiteboard film is formed by forming an active energy ray-curable resin coating layer on the surface of a transparent plastic film,
The active energy ray-curable resin coating layer comprises spherical fine particles and an active energy ray-curable silicone resin.
前記活性エネルギー線硬化型樹脂被膜層は、厚さが1〜8μmの範囲であり、前記微粒子の平均粒径は、2〜10μmの範囲であること
を特徴とする請求項1に記載のホワイトボード用フィルム。
2. The whiteboard according to claim 1, wherein the active energy ray-curable resin coating layer has a thickness in a range of 1 to 8 μm, and an average particle diameter of the fine particles is in a range of 2 to 10 μm. Film.
前記活性エネルギー線硬化型樹脂被膜層は、該樹脂が100重量部に対して、活性エネルギー線硬化型シリコーン樹脂が0.1〜20重量部の範囲で含有すること
を特徴とする請求項1に記載のホワイトボード用フィルム。
The active energy ray-curable resin coating layer contains 0.1 to 20 parts by weight of an active energy ray-curable silicone resin with respect to 100 parts by weight of the resin. The whiteboard film as described.
JP2006165762A 2006-06-15 2006-06-15 Film for whiteboard Pending JP2007331231A (en)