JP2006509635A - クラッド層および鉄合金の被覆層を有するろう付けシート製品およびその製造方法 - Google Patents
クラッド層および鉄合金の被覆層を有するろう付けシート製品およびその製造方法 Download PDFInfo
- Publication number
- JP2006509635A JP2006509635A JP2004559801A JP2004559801A JP2006509635A JP 2006509635 A JP2006509635 A JP 2006509635A JP 2004559801 A JP2004559801 A JP 2004559801A JP 2004559801 A JP2004559801 A JP 2004559801A JP 2006509635 A JP2006509635 A JP 2006509635A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- alloy
- iron
- brazing
- brazed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
クラッド層および鉄合金の被覆層を有するろう付けシート製品およびその製造方法
コア金属シート、該コアシートの少なくとも片側に、ケイ素を4〜14重量%の量で含んでなるアルミニウムろう付け合金のクラッド層、を含んでなり、さらに該クラッド層の少なくとも一つの外側表面上に鉄−X合金のめっき層を含んでなり、その際、Xは、スズ、亜鉛、マンガン、および銅からなる群の一つ以上から選択され、クラッド層およびその外側にあるすべての層が、ろう付け操作のための金属充填剤を形成し、Fe:Xのモル比が10:(0.3〜6)である組成を有する、ろう付けシート製品を開示する。本発明は、そのようなろう付け製品の製造方法、およびこのろう付け製品から製造された少なくとも一個の部品を含んでなる、ろう付けされた組立品にも関する。
コア金属シート、該コアシートの少なくとも片側に、ケイ素を4〜14重量%の量で含んでなるアルミニウムろう付け合金のクラッド層、を含んでなり、さらに該クラッド層の少なくとも一つの外側表面上に鉄−X合金のめっき層を含んでなり、その際、Xは、スズ、亜鉛、マンガン、および銅からなる群の一つ以上から選択され、クラッド層およびその外側にあるすべての層が、ろう付け操作のための金属充填剤を形成し、Fe:Xのモル比が10:(0.3〜6)である組成を有する、ろう付けシート製品を開示する。本発明は、そのようなろう付け製品の製造方法、およびこのろう付け製品から製造された少なくとも一個の部品を含んでなる、ろう付けされた組立品にも関する。
Description
本発明は、金属性のコアを含んでなり、そのコアの少なくとも片側に、ケイ素を4〜14重量%の量で含んでなるアルミニウム合金製のアルミニウムクラッド層、および別の金属層を有し、全体で、アルミニウムクラッド層およびその外側にあるすべての層がろう付け操作のための金属充填剤を形成する、ろう付けシート製品に関する。本発明は、そのようなろう付け製品の製造方法、およびこのろう付け製品から製造された少なくとも一つの部品を含んでなる、ろう付けされた組立品にも関する。
金属、例えばアルミニウムおよびアルミニウム合金、は、広範囲なろう付けおよび半田付け方法により接合することができる。ろう付けは、定義上、450℃より上に母材の液相線および下に固相線を有する金属充填剤または合金を使用する。ろう付けは、金属充填剤の融点により半田付けと区別され、半田は450℃未満で融解する。半田付け方法は、本発明の範囲内ではない。
ろう付けシート製品は、熱交換機、および他の類似の装置で広く使用されている。従来のアルミニウムろう付けシート製品は、コアまたは母材シート、典型的にはAluminium Association(「AA」)3xxx-シリーズのアルミニウム合金、を有し、そのコアシートクラッドの少なくとも一方の表面上にアルミニウムクラッド層を有し、そのアルミニウムクラッド層は、ケイ素を4〜14重量%、好ましくは7〜14重量%、の量で含んでなるAA4xxx-シリーズの合金から製造されている。アルミニウムクラッド層は、コアまたは母材合金に、この分野で公知の様々な方法、例えばロールボンディング、クラッド加工、爆発クラッド加工、溶射成形または半連続式または連続式鋳造方法、により結合させることができる。
制御雰囲気ろう付け(「CAB」)および真空ろう付け(「VB」)が、工業規模のアルミニウムろう付けに使用される2つの主要方法である。工業用真空ろう付けは、1950年代から使用されているのに対し、CABは、1980年代初期に、NOCOLOK(商標)ろう付けフラックスの導入後に一般的になった。真空ろう付けは、実質的に断続的工程であり、材料に高度の清浄さが要求される。存在する酸化アルミニウム層の分裂は、主としてクラッド合金からマグネシウムが蒸発するために引き起こされる。好適な装置のための投資は比較的高い。
CABは、ろう付けの前にろう付けフラックスを塗布しなければならないので、VBと比較して、ろう付けの前に追加の工程が必要である。アルミニウム合金をろう付けするのに使用するろう付けフラックス材料は、通常、アルカリ土類金属塩化物およびフッ化物の混合物からなり、フッ化アルミニウムまたは氷晶石を含むことがある。CABは、実質的な連続製法であり、その際、適切なろう付けフラックスを使用すれば、大量のろう付けした組立品を製造することができる。ろう付けフラックスは、ろう付け温度で酸化物層を溶解させ、クラッド合金を適切に流動させることができる。NOCOLOKフラックス材料を使用する場合、フラックスを塗布する前に、表面を十分に清浄にする必要がある。良好なろう付け結果を得るには、ろう付けフラックスを、ろう付けする組立品の全表面上に塗布する必要がある。これは、特定の種類の組立品では、それらの設計のために困難になる場合がある。例えば、蒸発装置型の熱交換機は内部表面が大きく、内部に到達するのが困難なので、問題が起こる。良好なろう付け結果を得るには、ろう付けの前にフラックスがアルミニウム表面に密着していなければならない。しかし、ろう付けフラックス材料は、乾燥後は小さな機械的振動により簡単に剥がれ落ちる。ろう付けサイクル中、腐食性の煙、例えばHF、が発生する。このために、炉に使用する材料に高度の耐食性が必要になる。
理想的には、CABに使用できるが、公知のろう付けフラックス塗布の必要性および欠点が無い材料を使用できるべきである。そのような材料は、ろう付け組立品の製造業者に供給し、組立品部品を形成した後、即使用できる。ろう付けフラックス処理操作をさらに行う必要がない。現在、工業的規模で使用されている無フラックスろう付け方法は一つしかない。この方法のための材料は、例えばAA3xxx-シリーズのコア合金から製造され、その片側または両側にAA4xxx-シリーズ合金のクラッドを備えた標準的なろう付けシートでよい。このろう付けシートを使用できる前に、自然に生じる酸化アルミニウム層がろう付けサイクルの際に妨害しないように、表面を変性させる必要がある。良好なろう付けを達成する方法は、クラッド合金の表面上に特定量のニッケルを堆積させることである。適切に塗布されれば、ニッケルは、恐らく発熱的に、下にあるアルミニウムと反応する。
アルミニウムろう付けシート製品のアルカリ性溶液におけるニッケルめっき方法は、US−A−3,970,237、US−A−4,028,200、およびUS−A−4,164,454のそれぞれから公知である。これらの文献によれば、ニッケルまたはコバルト、またはそれらの組合せ、を鉛との組合せで堆積させる。鉛の添加は、ろう付けサイクル中のアルミニウムクラッド合金の濡れ性を改良するために行う。これらのめっき方法の重要な特徴は、ニッケルがアルミニウムクラッド合金のケイ素粒子上に優先的に堆積することである。ろう付けに十分なニッケルを得るために、アルミニウムクラッド合金の表面は、ニッケル堆積のための核として作用するケイ素粒子を比較的大量に含むべきである。十分な核形成箇所を得るには、ケイ素粒子が埋め込まれているアルミニウムの一部を、酸洗の前に、化学的および/または機械的前処理により除去すべきであると考えられる。これは、ろう付けまたはクラッド合金のめっき作用のための核として役立つ、十分なケイ素で覆うために必要な条件であると考えられる。顕微鏡的尺度では、ろう付けシートのSi含有クラッドの表面は、ニッケル−鉛小球で覆われている。しかし、ろう付けシート上に好適なニッケルおよび/またはコバルト層を形成するための鉛の使用には、幾つかの欠点がある。製品、例えば自動車製品、に鉛を使用することは、好ましいことではなく、非常に近い将来、鉛を含んでなる製品、または鉛または鉛系成分を含んでなる一つ以上の中間処理工程を経て製造された製品は禁止されることさえ考えられる。
J.N.Mooij et al.による国際特許出願第WO00/71784号は、好ましくはめっきにより施された、亜鉛またはスズを含んでなる非常に薄い結合層を、AlSi合金クラッド層とニッケル層との間に設け、施されたニッケル層の結合を改良する、ろう付けシート製品を開示している。ニッケル層への鉛添加は、ビスマスの添加により置き換えられ、ろう付けシート製品の優れたろう付け特性を維持している。
ニッケルを含んでなる層を有する公知のろう付けシート製品の欠点は、ろう付けした製品の、ASTM G−85によるSWAAT試験での腐食寿命が限られていることである。無孔腐食寿命は、AA3003シリーズコア合金を有する場合、典型的には4〜6日であり、そのため、ろう付けシート製品の重要な用途が限られる。しかし、ろう付け製品における公知のニッケルめっきろう付けシートの幾つかの用途では、そのような比較的短い腐食寿命は有害ではない。良好な耐食性は、特に熱交換機、例えばラジエーターや冷却器、に使用するろう付け製品に重要な特性であると考えられる。A.J. Wittebrood et al.による国際特許出願第WO02/060639号(ここにその全文を参考として含める)によれば、Niめっきしたろう付けシート製品の腐食性能は、精選された合金化元素、特に厳選された量のスズ、の添加により、著しく改良することができる。
本発明の目的は、ろう付け操作、理想的には無フラックスCABろう付け操作、に使用する、ASTM G−85によるSWAAT試験で測定した時に、Niめっきしたろう付けシート製品と比較して、改良されたろう付け後の耐食性を有する、ろう付けシート製品を提供することである。
本発明の別の目的は、ろう付けシート製品の製造方法を提供することである。
本発明は、コア金属シート、および該コアシートの少なくとも片側に、ケイ素を4〜14重量%の量で含んでなるアルミニウムろう付け合金のクラッド層、を含んでなり、さらに該クラッド層の少なくとも一つの外側表面上に鉄−X合金のめっき層を含んでなり、その際、Xは、スズ、亜鉛、マンガン、および銅からなる群の一つ以上の構成員から選択され、クラッド層およびその外側にあるすべての層が、ろう付け操作のための金属充填剤を形成し、Fe:Xのモル比が10:(0.3〜6)である組成を有する、ろう付けシート製品に関する。本発明は、そのようなろう付け製品の製造方法、およびこのろう付け製品から製造された少なくとも一個の部品を含んでなる、ろう付けされた組立品にも関する。
本発明により、一態様で、コア金属シート、該コアシートの少なくとも片側に、ケイ素を4〜14重量%、好ましくは7〜14重量%、の量で含んでなるアルミニウムろう付け合金のクラッド層、を含んでなり、さらに該クラッド層の少なくとも一つの外側表面上に鉄−X合金のめっき層を含んでなり、その際、Xは、スズ、亜鉛、マンガン、および銅からなる群の一つ以上の構成員から選択され、クラッド層およびその外側にあるすべての層が、ろう付け操作のための金属充填剤を形成し、Fe:Xのモル比が10:(0.3〜6)、好ましくは10:(0.5〜<5)、である組成を有する、ろう付けシート製品を提供する。
めっきされた鉄−X合金は、ろう付けの際に、ろう付けフラックス材料、例えば公知のNOCOLOKフラックス、の非存在下で発熱反応を開始することが分かっている。鉄だけの上側層は、酸化に対して敏感であると考えられる。形成された表面酸化鉄は、ろう付け工程および/またはろう付け前のろう付けシート製品の形成操作に悪影響を及ぼす恐れがある。めっきされたFe−X層は、空気中で薄い、安定した表面酸化物被膜を形成することが分かっている。空気中でのさらなる酸化は、実質的に約300℃より高い温度でのみ起こるが、これはろう付け操作の前の貯蔵または取扱温度よりはるかに高い。金属Xは、ろう付け操作の際に溶融した金属充填剤の表面張力を下げるのに役立つように選択する。金属Xは、特にSWAAT環境にさらされた時に、ろう付け製品のろう付け後の腐食性能も改良することができる。本発明のろう付けシート製品、特にAA3xxx-シリーズコア合金を有する製品、では、ろう付け後のASTM G−85による無孔SWAAT腐食寿命が21日を超え、最も良い例では26日を超えているが、これは、同じアルミニウムコア合金を有する製品のための従来のNOCOLOKろう付けとの比較を含めて、先行技術より大幅に改良されている。最良の結果は、鉄−スズ合金のめっきにより達成されている。このろう付けシート製品は、ろう付けフラックス材料の非存在下、調整された雰囲気条件下で無フラックスろう付けし、非常に良いろう付け後の腐食性能を達成し、ろう付けシート製品の応用可能性を著しく高めている。
Fe−X合金のめっきには、幾つかの電解質、例えばFe−Sn合金またはFe−Sn−Bi合金をめっきするためのピロリン酸塩、を使用することができる。
ろう付けシート製品の一実施態様では、鉄−X合金を含んでなる層を電解めっき方法により形成する。しかし、他の技術、例えばめっき、熱浸漬(thermal dipping)、溶射、化学蒸着(「CVD)」および物理蒸着(「PVD」)または他の、ガスまたは蒸気相から金属または合金を堆積させる技術、も使用できる。
形成されるFe−X合金層は、厚さが最大で1.8μm、好ましくは最大で1.0μmである。1.8μmを超える被覆厚さは、長時間のめっきを必要とし、その後のろう付け操作の際に、溶融した金属充填剤のしわを引き起こすことがある。この鉄−X層に好ましい最小厚さは、約0.03μm、より好ましくは0.10μmである。
ろう付けシート製品の一実施態様では、クラッド層の外側表面とめっきした鉄−X合金の層との間に鉄または鉄合金を含んでなる層があり、この鉄または鉄合金を含んでなる層は、電解めっき法で形成するのが好ましい。好ましくは、この層は、80重量%以上の鉄、より好ましくは85重量%以上の鉄、さらに好ましくは90重量%以上の鉄、最も好ましくは96重量%以上の鉄または98重量%以上の鉄を含んでなる。この鉄または鉄合金層は、金属充填剤中に十分な未合金鉄が残り、ろう付けサイクル中に予想される発熱反応を確実に開始するために施す。この鉄または鉄合金を含んでなる層は、金属Xが鉄または鉄合金層中に存在することが必須ではないので、鉄−X合金層とは異なった組成を有することができる。
あるいは、この鉄または鉄合金を含んでなる層は、鉄−X合金層の上に付け、ろう付けを促進する二重層を形成することもできる。内側層は鉄−X合金層により形成し、外側層は鉄または鉄合金層により形成する。
また、この鉄または鉄合金を含んでなる層を形成するために、他の技術、例えばめっき、熱浸漬、溶射、CVDおよびPVDまたは他の、ガスまたは蒸気相から金属または合金を堆積させる技術、も使用できる。この、80重量%以上の鉄、より好ましくは85重量%以上の鉄、さらに好ましくは90重量%以上の鉄、最も好ましくは96重量%以上の鉄、または98重量%以上の鉄を含んでなる、鉄または鉄合金、例えばFeまたはFe−Bi、の施された層は、厚さが最大で2.0μm、好ましくは最大で1.0μm、より好ましくは0.05〜0.5μmである。2.0μmを超える被覆厚さは、長時間のめっきを必要とし、その後のろう付け操作の際に、溶融した金属充填剤のしわを引き起こすことがある。この鉄または鉄合金層に好ましい最小厚さは、約0.10μmである。
好ましくは、施した層のそれぞれ、例えば鉄または鉄合金層およびめっきした鉄−X合金層は、環境上の観点から、実質的に鉛を含まない。
一実施態様では、施した層のそれぞれ、すなわち所望により使用する鉄または鉄合金層およびめっきした鉄−X合金層は、実質的にニッケルを含まない。さらに、ニッケルの存在は、ろう付け製品のろう付け後の腐食性能に悪影響を及ぼすことがある。もう一つの利点は、ニッケル塩と比較して、めっき浴に使用する鉄塩は安価であり、無毒性なことである。
一実施態様で、本発明のろう付けシート製品は、AlSi合金クラッド層の外側表面と鉄または鉄合金を含んでなる薄い層との間、またはAlSi合金クラッド層の外側表面とめっきした鉄−X合金層との間に、中間結合層として、所望により使用する、好ましくは亜鉛またはスズを含んでなる薄い層をさらに特徴とする。この、好ましくは亜鉛製の中間結合層により、AlSi合金クラッド層と鉄または鉄合金を含んでなる薄い層との間に、非常に効果的な結合が形成され、この結合は、その後のろう付け製品の変形、例えば曲げ操作、の際にも有効である。好ましくは、中間結合層は、厚さが最大で0.5μm、より好ましくは最大で0.3μm、最も好ましくは0.01〜0.15μmである。厚さ約20〜30nmの使用により、最良の結果が得られている。この薄い結合層は、本発明のろう付け製品のろう付け後の腐食性能に悪影響を及ぼさないことが分かっている。
中間結合層を形成するために、例えばめっき、電解めっき、熱浸漬、溶射、CVDおよびPVDのような技術、または他の、ガスまたは蒸気相から金属または合金を堆積させる技術、も使用できる。
コア金属シートは、鋼、アルミニウム化鋼、ステンレス鋼、めっきまたは被覆されたステンレス鋼、青銅、黄銅、ニッケル、ニッケル合金、チタン、またはめっきまたは被覆されたチタンから製造することができる。
ろう付けシート製品の一実施態様では、コアシートはアルミニウム合金であり、好ましくはAA3xxx、AA5xxx、およびAA6xxx-シリーズのアルミニウム合金からなる群から選択される。
一実施態様では、各AlSi合金クラッド層は、厚さが、ろう付けシート製品の総厚の約2〜20%である。典型的なアルミニウムクラッド層の厚さは40〜80ミクロンである。アルミニウムコアシートの厚さは、典型的には最大で5mm、より好ましくは0.1〜2mmである。
一実施態様では、AlSi合金クラッド層およびその外側にあるすべての層が全体でろう付け操作のための金属充填剤を形成し、少なくとも、重量%で
Si5〜14%、
Fe0.15〜8%、好ましくは0.9〜5%、
X0.01〜7%、好ましくは0.35〜2%、その際、Xは、Sn、Zn、Mn、およびCuからなる群の一つ以上の構成員から選択され、
Sn0.0〜0.3%(Xとして存在しない場合)、
Zn0.0〜0.3%(Xとして存在しない場合)、
Mn0.0〜0.3%(Xとして存在しない場合)、
Cu0.0〜0.3%(Xとして存在しない場合)、
所望によりBi、Sb、In、およびPbの一種以上(好ましくは、Bi、Sb、In、およびPbの合計は0.4%以下である)、その際、
Bi0.0〜0.3%、
Sb0.0〜0.3%、
In0.0〜0.3%、
Pb0.0〜0.3%、
Ti0.0〜0.1%、
Sr0.0〜0.1%、
Mg0.0〜5%
残部アルミニウムおよび不可避不純物
を含んでなる組成を有するが、ただし、Fe:Xのモル比は10:(0.3〜6)、好ましくは10:(0.5〜<5)である。
Si5〜14%、
Fe0.15〜8%、好ましくは0.9〜5%、
X0.01〜7%、好ましくは0.35〜2%、その際、Xは、Sn、Zn、Mn、およびCuからなる群の一つ以上の構成員から選択され、
Sn0.0〜0.3%(Xとして存在しない場合)、
Zn0.0〜0.3%(Xとして存在しない場合)、
Mn0.0〜0.3%(Xとして存在しない場合)、
Cu0.0〜0.3%(Xとして存在しない場合)、
所望によりBi、Sb、In、およびPbの一種以上(好ましくは、Bi、Sb、In、およびPbの合計は0.4%以下である)、その際、
Bi0.0〜0.3%、
Sb0.0〜0.3%、
In0.0〜0.3%、
Pb0.0〜0.3%、
Ti0.0〜0.1%、
Sr0.0〜0.1%、
Mg0.0〜5%
残部アルミニウムおよび不可避不純物
を含んでなる組成を有するが、ただし、Fe:Xのモル比は10:(0.3〜6)、好ましくは10:(0.5〜<5)である。
Fe:Xのモル比が低すぎる場合、ろう付け後の腐食寿命に大きな改良は見られない。このモル比が高すぎる場合、ろう付け性があまり効果的ではなくなる。環境的な観点から、金属充填剤に鉛を使用することは避けた方が良い。
本発明の別の態様で、ろう付けシートの製造方法であって、(a)コア金属シート、該コアシートの少なくとも片側に、ケイ素を4〜14重量%の量で含んでなるアルミニウムろう付け合金のクラッド層、を含んでなるろう付けシート製品を用意する工程、(b)クラッド合金の外側表面を前処理する工程、(c)クラッド合金の前処理した外側表面の外側表面上に金属層をめっきする工程を含んでなり、該金属層が鉄−X合金を含んでなり、その際、Xは、スズ、亜鉛、マンガン、および銅からなる群の一つ以上の構成員から選択される、方法を提供する。
本発明のこの態様により、鉄合金、例えば鉄−スズ合金、でめっきしたろう付けシート製品の製造方法を提供するが、めっきされた鉄合金層により、類似のコアおよびクラッド層を有するが、代わりにめっきされたニッケルまたはニッケル合金層を有する製品と比較して、得られた製品のSWAAT試験で測定したろう付け後の腐食性能が改良される。SWAAT試験で測定したろう付け後の腐食性能は、同じアルミニウムコア合金およびクラッド合金を有するが、鉄またはニッケル層を施していない製品用の従来のNOCOLOKろう付けと比較しても、優れている。
金属Xがスズである実施態様では、純粋なスズ金属の上側層は、ろう付け前の条件、特に湿った条件下で、進行する酸化に対して敏感であることが分かっている。形成される表面酸化物は、ろう付け過程に悪影響を及ぼす恐れがある。めっきされた鉄−スズ層の形態でスズを与えることにより、最早遊離のスズは実質的に存在せず、それによってスズの有害な進行的酸化が回避される。めっきされたFe−Sn合金層は、空気中で薄い安定した表面酸化物被膜を形成することが分かっている。空気中でのそれ以上の酸化は、実質的に約320℃を超える温度でのみ起こる。
ろう付けシート製品のクラッドに対する鉄または鉄合金または鉄−X合金層の密着性は、極めて良好であるが、鉄または鉄合金または鉄−X合金層が上に堆積しているクラッドろう付け層の外側表面を適切に前処理することにより、さらに改良することができる。この前処理は、予備的な洗浄工程を含んでなり、その際に表面からグリース、油、または研磨化合物が除去される。これは、様々な方法で達成できるが、とりわけ、蒸気脱脂、溶剤洗浄、または溶剤エマルション洗浄により、行うことができる。また、穏やかなエッチングも使用できる。予備洗浄に続いて、表面は調整すべきである。幾つかの方法、例えばここに参考として含めるJ.N. Mooij et al.の国際特許出願第WO01/88226号、9頁、29行〜10頁、21行に記載されている方法、を順次行うことができる。別の有用な方法は、ここに参考として含めるJ.N. Mooij et al.の国際特許出願第WO02/086197号、1頁、22行〜5頁、23行に記載されている
一実施態様では、本発明の方法は、AlSi合金層の外側表面と、鉄または鉄合金または鉄−X合金を含んでなる層との間に、中間結合層として、好ましくは亜鉛またはスズを含んでなる薄い層を堆積させる前処理をさらに特徴とする。この中間結合層により、AlSi合金層と、鉄または鉄合金を含んでなる薄い層との間の非常に効果的な結合が形成され、その結合は、その後のろう付けシート製品の変形、例えば曲げ操作、の際にも有効である。そのような亜鉛の中間層を付けるのに最も好適な方法は、直接または浸漬めっきにより行う。好ましくは、施される中間結合層は、厚さが最大で0.5μm、より好ましくは最大で0.3μm、最も好ましくは0.01〜0.15μmである。厚さ約30nmの使用により、最良の結果が得られている。被覆の厚さが0.5μmを超えても、密着性の改良にとって、それ以上の優位性は得られないと考えられる。
本発明はさらに、ろう付け操作、特に無フラックスCAB操作、に使用するためのろう付けシート製品上に鉄およびスズを含んでなる層を堆積させるための、鉄−スズめっき浴の使用に関する。幾つかのFe−Sn合金浴、例えばpH8〜11、好ましくは8〜9で操作するピロリン酸塩電解質、を使用することができる。他は、例えば塩化物−硫酸塩浴から得られるFe−SnまたはSn−Fe合金である。
本発明は、ろう付けにより接合した部品の組立品、例えば、典型的には自動車用途向けの熱交換機、または燃料電池、典型的には電気化学的燃料電池、であって、部品の少なくとも一つが上記のろう付けシート製品または上記の方法により得られるろう付け製品である、組立品をさらに提供する。ろう付け操作は、好ましくは、ろう付けフラックス材料の非存在下における不活性雰囲気(CAB)中または真空下で行う。
一実施態様では、ろう付けにより接合すべき部品の少なくとも一個が上記のろう付けシート製品から製造されるか、または上記の本発明の方法により製造され、少なくとも一個の他の部品が、鋼、アルミニウム化鋼、ステンレス鋼、めっきまたは被覆されたステンレス鋼、青銅、黄銅、ニッケル、ニッケル合金、チタン、またはめっきまたは被覆されたチタンから製造される、ろう付けされた組立品を提供する。
以上、本発明を十分に説明したが、当業者には明らかなように、ここに記載する本発明の範囲から離れることなく、多くの変形および修正を行うことができる。
Claims (23)
- コア金属シート、および前記コアシートの少なくとも片側に、ケイ素を4〜14重量%の量で含んでなるアルミニウムろう付け合金のクラッド層、を含んでなり、さらに前記クラッド層の少なくとも一つの外側表面上に鉄−X合金の被覆層を含んでなり、その際、Xは、スズ、亜鉛、マンガン、および銅からなる群の一つ以上から選択され、前記クラッド層およびその外側にあるすべての層が、ろう付け操作のための金属充填剤を形成し、Fe:Xのモル比が10:(0.3〜6)である組成を有する、ろう付けシート製品。
- 前記鉄−X合金を含んでなる層が、めっき法により、好ましくは電解めっき法により形成される、請求項1に記載のろう付けシート製品。
- 前記鉄−X合金を含んでなる層が、PVD法により形成される、請求項1に記載のろう付けシート製品。
- 前記鉄−X合金を含んでなる層が、溶射法により形成される、請求項1に記載のろう付けシート製品。
- 前記クラッド層の前記外側表面と前記鉄−X合金層との間に、鉄または鉄合金を含んでなる、好ましくは電解めっき法により形成された層がある、請求項1〜4のいずれか一項に記載のろう付けシート製品。
- 前記クラッド層の前記外側表面と前記鉄または鉄合金を含んでなる層との間に、結合層としての層がある、請求項5に記載のろう付けシート製品。
- 前記クラッド層の前記外側表面と前記鉄または鉄合金を含んでなる層との間に、結合層として、亜鉛またはスズを含んでなる層がある、請求項5に記載のろう付けシート製品。
- 前記クラッド層の前記外側表面と前記鉄−X合金層との間に、結合層としての層がある、請求項1〜7のいずれか一項に記載のろう付けシート製品。
- 前記クラッド層の前記外側表面と前記鉄−X合金層との間に、結合層として、亜鉛またはスズを含んでなる層がある、請求項1〜7のいずれか一項に記載のろう付けシート製品。
- 前記結合層の厚さが0.5ミクロン以下、好ましくは0.3ミクロン以下である、請求項6〜9のいずれか一項に記載のろう付けシート製品。
- 前記施された鉄−X合金層の厚さが最大で1.8ミクロン、好ましくは最大で1.0ミクロンである、請求項1〜10のいずれか一項に記載のろう付けシート製品。
- 前記施された鉄−X合金層が、80重量%以上、好ましくは90重量%以上の鉄を含んでなる、請求項1〜11のいずれか一項に記載のろう付けシート製品。
- 前記コア金属シート(1)が、アルミニウム合金、鋼、アルミニウム化鋼、ステンレス鋼、めっきまたは被覆されたステンレス鋼、青銅、黄銅、ニッケル、ニッケル合金、チタン、およびめっきまたは被覆されたチタンからなる群の一つを含んでなる、請求項1〜12のいずれか一項に記載のろう付けシート製品。
- 前記コア金属シートが、好ましくはAA3xxx、AA5xxx、およびAA6xxx-シリーズのアルミニウム合金からなる群から選択された、アルミニウム合金から製造される、請求項1〜12のいずれか一項に記載のろう付けシート製品。
- ケイ素を4〜14重量%の量で含んでなる前記クラッド層およびその外側にあるすべての層が全体でろう付け操作のための金属充填剤を形成し、少なくとも、重量%で
Si5〜14%、
Fe0.15〜8%、
X0.01〜7%、その際、Xは、Sn、Zn、Mn、およびCuからなる群の一つ以上から選択され、
Sn0.0〜0.3%(Xとして存在しない場合)、
Zn0.0〜0.3%(Xとして存在しない場合)、
Mn0.0〜0.3%(Xとして存在しない場合)、
Cu0.0〜0.3%(Xとして存在しない場合)、
所望によりBi、Sb、In、およびPbの一種以上、その際、
Bi0.0〜0.3%、
Sb0.0〜0.3%、
In0.0〜0.3%、
Pb0.0〜0.3%、
Ti0.0〜0.1%、
Sr0.0〜0.1%、
Mg0.0〜5%
残部アルミニウムおよび不可避不純物
を含んでなる組成を有するが、ただし、Fe:Xのモル比は10:(0.3〜6)、好ましくは10:(0.5〜<5)である、請求項1〜14のいずれか一項に記載のろう付けシート製品。 - 請求項1〜15のいずれか一項に記載のろう付けシート製品の製造方法であって、(a)コア金属シート、前記コアシートの少なくとも片側に、ケイ素を4〜14重量%の量で含んでなるアルミニウムろう付け合金のクラッド層、を含んでなるろう付けシート製品を用意する工程、(b)前記クラッド合金の外側表面を前処理する工程、(c)前記クラッド合金の前記前処理した外側表面の外側表面上に金属層を施す工程を含んでなり、前記金属層が鉄−X合金を含んでなり、その際、Xが、スズ、亜鉛、マンガン、および銅からなる群の一つ以上から選択される、方法。
- 工程(b)の際に、前記クラッド層の前記外側表面が、結合層を付けることにより前処理される、請求項16に記載の方法。
- 工程(b)の際に、前記クラッド層の前記外側表面が、亜鉛またはスズの結合層を付けることにより前処理される、請求項16または17に記載の方法。
- 前記結合層を付けた後、前記鉄−X合金を含んでなる金属層を付ける前に、好ましくはめっきにより、85重量%を超える鉄を含んでなる層を施す、請求項16〜18のいずれか一項に記載の方法。
- 前記金属層が、前記クラッド合金の前記前処理された外側表面の前記外側表面上にめっきにより施される、請求項16〜19のいずれか一項に記載の方法。
- 前記金属層が、前記クラッド合金の前記前処理された外側表面の前記外側表面上にPVDにより施される、請求項16〜19のいずれか一項に記載の方法。
- ろう付けにより接合された部品の組立品であって、少なくとも一個の前記部品が、請求項1〜15のいずれか一項に記載のろう付けシート製品または請求項16〜21のいずれか一項に記載の方法により得られる製品である、組立品。
- 前記組立品が、真空下で、または不活性雰囲気中、ろう付けフラックス材料の非存在下でろう付けされる、請求項22に記載の組立品。