JP2006181816A - 剥離ライナーおよび該剥離ライナーが用いられた両面粘着テープ又はシート - Google Patents
剥離ライナーおよび該剥離ライナーが用いられた両面粘着テープ又はシート Download PDFInfo
- Publication number
- JP2006181816A JP2006181816A JP2004376665A JP2004376665A JP2006181816A JP 2006181816 A JP2006181816 A JP 2006181816A JP 2004376665 A JP2004376665 A JP 2004376665A JP 2004376665 A JP2004376665 A JP 2004376665A JP 2006181816 A JP2006181816 A JP 2006181816A
- Authority
- JP
- Japan
- Prior art keywords
- release
- treatment layer
- sensitive adhesive
- release agent
- peel strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 剥離ライナーは、基材の両面に離型処理層が形成された構成を有しており、基材の一方の面側の離型処理層が熱硬化型シリコーン系剥離剤により形成され、且つ基材の他方の面側の離型処理層が電離性放射線硬化型シリコーン系剥離剤により形成されていることを特徴とする。電離性放射線硬化型シリコーン系剥離剤としては、紫外線硬化型シリコーン系剥離剤が好適である。熱硬化型シリコーン系剥離剤により形成された離型処理層は、粘着面に対する剥離強度が小さい側の離型処理層として利用でき、電離性放射線硬化型シリコーン系剥離剤により形成された離型処理層は、粘着面に対する剥離強度が大きい側の離型処理層として利用できる。
【選択図】 なし
Description
本発明の剥離ライナーは、基材の一方の面に熱硬化型シリコーン系剥離剤により形成された離型処理層(「熱硬化型シリコーン系離型処理層」と称する場合がある)を有しており、且つ基材の他方の面に電離性放射線硬化型シリコーン系剥離剤により形成された離型処理層(「電離性放射線硬化型シリコーン系離型処理層」と称する場合がある)を有している。このように、剥離ライナーは、基材の両面に離型処理層が形成されているとともに、この両面の離型処理層うち一方の離型処理層が、電離性放射線硬化型シリコーン系離型処理層である構成を有しているので、この電離性放射線硬化型離型処理層を重面側離型処理層(粘着面に対する剥離強度が大きい側の離型処理層)として用いることにより、重面側離型処理層の粘着面に対する剥離強度の経時変化を長期間にわたり抑制又は防止させることができる。
熱硬化型シリコーン系剥離剤としては、熱により硬化が生じるタイプのシリコーン系剥離剤であれば特に制限されないが、熱による付加反応型の架橋(硬化反応)により硬化して剥離性皮膜を形成するタイプの熱付加反応型シリコーン系剥離剤を好適に用いることができる。熱硬化型シリコーン系剥離剤は、単独で又は2種以上を組み合わせて使用することができる。
電離性放射線硬化型シリコーン系剥離剤としては、電離性放射線(α線、β線、γ線、中性子線、電子線や、紫外線など)により硬化が生じるタイプのシリコーン系剥離剤であれば特に制限されないが、紫外線照射による架橋(硬化反応)により硬化して剥離性皮膜を形成するタイプの紫外線硬化型シリコーン系剥離剤を好適に用いることができる。電離性放射線硬化型シリコーン系剥離剤は、単独で又は2種以上を組み合わせて使用することができる。
本発明の剥離ライナーでは、基材(剥離ライナー用基材)が用いられている。このような剥離ライナー用基材としては、特に制限されず、プラスチック系基材、紙系基材、繊維系基材などの各種基材を用いることができる。剥離ライナー用基材は、単層、積層体のいずれの形態を有していてもよい。剥離ライナー用基材において、プラスチック系基材としては、各種のプラスチック系基材から適宜選択して用いることができ、例えば、ポリオレフィン系基材(ポリエチレン系基材、ポリプロピレン系基材等)、ポリエステル系基材(ポリエチレンテレフタレート系基材、ポリエチレンナフタレート系基材、ポリブチレンテレフタレート系基材等)、ポリアミド系基材(いわゆる「ナイロン」系基材)、セルロース系基材(いわゆる「セロハン」系基材)などが挙げられる。また、紙系基材としては、各種の紙系基材から適宜選択して用いることができ、例えば、和紙、洋紙、上質紙、グラシン紙、クラフト紙、クルパック紙、クレープ紙、クレーコート紙、トップコート紙、合成紙などが挙げられる。
剥離強度の低下率(%)=[(W0−W)/W0]×100
本発明の両面粘着テープ又はシートは、前記剥離ライナーを1枚用いて、各剥離処理層(電離性放射線硬化型シリコーン系離型処理層や、熱硬化型シリコーン系離型処理層)により各粘着面を保護している構成を有している。すなわち、両面粘着テープ又はシートは、両面の粘着面が1枚の剥離ライナーにより保護されている構成を有しており、剥離ライナーとして、前記剥離ライナーが用いられている。
本発明の両面粘着テープ又はシートにおいて、粘着剤層を形成する粘着剤としては、例えば、公知の粘着剤から適宜選択して用いることができる。このような粘着剤としては、例えば、アクリル系粘着剤、ゴム系粘着剤、シリコーン系粘着剤、ビニルアルキルエーテル系粘着剤、ポリエステル系粘着剤、ポリアミド系粘着剤、ウレタン系粘着剤、フッ素系粘着剤、これらの粘着剤に融点が約200℃以下の熱溶融性樹脂を配合したクリ−プ特性改良型粘着剤などが挙げられる。粘着剤は単独で又は2種以上組み合わせて使用することができる。
両面粘着テープ又はシートにおいて、基材(両面粘着テープ又はシート用基材)としては、特に制限されず、粘着テープ又はシート等の接着シート類の基材として公知の基材から適宜選択して用いることができる。具体的には、両面粘着テープ又はシート用基材としては、例えば、各種プラスチック材(例えば、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、ポリエチレン、ポリプロピレン等)によるフィルムやシートなどのプラスチック系基材;マニラ麻、レーヨン製繊維、ポリエステル製繊維、パルプ繊維等の各種繊維を原料とする繊維系基材(織布、不織布、フェルト、ネットなど);和紙、合成紙などの紙系基材;ゴムシートなどのゴム系基材;発泡シートなどの発泡体;アルミニウム箔などの金属系基材や、これらの積層体等が挙げられる。両面粘着テープ又はシート用基材は、単層の形態、積層された形態のいずれの形態を有していてもよい。
シリコーン系剥離剤として、商品名「KS−847T」(信越化学株式会社製;熱硬化型ポリジメチルシロキサン):100重量部に対して、白金系触媒(商品名「CAT−PL−50T」信越化学株式会社製)を1重量部配合し、ヘプタンにより固形分濃度が1.0重量%となるように調整して、熱硬化型シリコーン系剥離剤(「軽面側剥離剤A」と称する場合がある)を調製した。
シリコーン系剥離剤として、商品名「X−62−7622」(信越化学株式会社製;紫外線硬化型ポリジメチルシロキサン):100重量部に対して、紫外線開裂型開始剤(商品名「CAT7605」信越化学株式会社製)を1重量部配合し、ヘプタンにより固形分濃度が1.0重量%となるように調整して、紫外線硬化型シリコーン系剥離剤(「重面側剥離剤A」と称する場合がある)を調製した。
シリコーン系剥離剤として、商品名「X−62−7629」(信越化学株式会社製;紫外線硬化型ポリジメチルシロキサン):100重量部に対して、紫外線開裂型開始剤(商品名「CAT7605」信越化学株式会社製)を1重量部配合し、ヘプタンにより固形分濃度が1.0重量%となるように調整して、紫外線硬化型シリコーン系剥離剤(「重面側剥離剤B」と称する場合がある)を調製した。
シリコーン系剥離剤として、商品名「X−62−7629」(信越化学株式会社製;紫外線硬化型ポリジメチルシロキサン):90重量部に対して、商品名「X−62−7655」(信越化学株式会社製;紫外線硬化型ポリジメチルシロキサン)を10重量部の割合で混合した紫外線硬化型ポリジメチルシロキサン混合物:100重量部に対して、紫外線開裂型開始剤(商品名「CAT7605」信越化学株式会社製)を1重量部配合し、ヘプタンにより固形分濃度が1.0重量%となるように調整して、紫外線硬化型シリコーン系剥離剤(「重面側剥離剤C」と称する場合がある)を調製した。
シリコーン系剥離剤として、商品名「KS−774」(信越化学株式会社製;熱硬化型ポリジメチルシロキサン):100重量部に対して、白金系触媒(商品名「CAT−PL−3」信越化学株式会社製)を0.7重量部配合し、ヘプタンにより固形分濃度が1.0重量%となるように調整して、熱硬化型シリコーン系剥離剤(「重面側剥離剤D」と称する場合がある)を調製した。
シリコーン系剥離剤として、商品名「X−62−2087」(信越化学株式会社製;熱硬化型ポリジメチルシロキサン):100重量部に対して、白金系触媒(商品名「CAT−PL−50T」信越化学株式会社製)を1重量部配合し、ヘプタンにより固形分濃度が1.0重量%となるように調整して、熱硬化型シリコーン系剥離剤(「重面側剥離剤E」と称する場合がある)を調製した。
シリコーン系剥離剤として、商品名「KS−841」(信越化学株式会社製;熱硬化型ポリジメチルシロキサン):100重量部に対して、白金系触媒(商品名「CAT−PL−50T」信越化学株式会社製)を1重量部配合し、ヘプタンにより固形分濃度が1.0重量%となるように調整して、熱硬化型シリコーン系剥離剤(「重面側剥離剤F」と称する場合がある)を調製した。
シリコーン系剥離剤として、商品名「KS−839L」(信越化学株式会社製;熱硬化型ポリジメチルシロキサン):100重量部に対して、白金系触媒(商品名「CAT−PL−50T」信越化学株式会社製)を1重量部配合し、ヘプタンにより固形分濃度が1.0重量%となるように調整して、熱硬化型シリコーン系剥離剤(「重面側剥離剤G」と称する場合がある)を調製した。
実施例1〜3、比較例1〜4、および参考例1により得られた剥離ライナーについて、下記の測定方法又は評価方法により、離型処理層における粘着面に対する剥離強度、該剥離強度の低下率、残留接着力、剥離異常の有無を測定又は評価した。評価結果は表1に示した。なお、参考例1により得られた剥離ライナーについては、環境温度50℃の条件下、1日間放置(エージング)した後、測定又は評価を行った。
まず、剥離ライナーを、60℃且つ湿度90%RHの環境下で21日間(3週間)放置したものを経時サンプルとし、該放置前の剥離ライナー(エージング後の剥離ライナー)を初期サンプルとする。
前記剥離強度の測定方法より測定された初期サンプルの剥離強度(W0)と、経時サンプルの剥離強度(W)とを用いて、次式により、剥離強度の低下率(%)を求める。
剥離強度の低下率(%)=[(W0−W)/W0]×100
剥離強度の測定方法1と同様にして、まず、剥離ライナーを、60℃且つ湿度90%RHの環境下で21日間放置したものを経時サンプルとし、該放置前の剥離ライナー(すなわち、エージング後の剥離ライナー)を初期サンプルとする。次に、商品名「No.31B」(日東電工株式会社製;ポリエステル基材を有する粘着テープ、幅:19mm)を、初期サンプルまたは経時サンプルに、粘着テープの粘着面が、初期サンプルまたは経時サンプルの所定の離型処理層[実施例1〜3および比較例1〜4により得られた剥離ライナーについては、重面側離型処理層(重面側離型処理層A〜G)、参考例1により得られた剥離ライナーについては、軽面側離型処理層A]の表面に接触する形態で、ハンドローラーを用いて貼り合わせ、50℃の環境下、1日間放置した。その後、粘着テープ(商品名「No.31B」)を初期サンプルまたは経時サンプルより剥がした後、粘着テープをステンレス板にハンドローラーを用いて貼り合わせ、さらに、室温下で30分間放置した後、引張試験機にて、補助板を用いて、23℃且つ50%RHの環境下、180°の剥離角度で、引張速度300mm/minで粘着テープを50mm引き剥がした時の応力を測定し、その際の応力の平均値を読み取り、該応力の平均値を剥離強度(F)(N/50mm)とする。
残留接着力(%)=(F/F0)×100
剥離強度の測定方法1と同様にして、まず、剥離ライナーを、60℃且つ湿度90%RHの環境下で21日間放置したものを経時サンプルとし、該放置前の剥離ライナー(すなわち、エージング後の剥離ライナー)を初期サンプルとする。
剥離強度の低下率の測定方法1と同様に、前記剥離強度の測定方法2より測定された初期サンプルの剥離強度(W0)と、経時サンプルの剥離強度(W)とを用いて、次式により、剥離強度の低下率(%)を求める。
剥離強度の低下率(%)=[(W0−W)/W0]×100
実施例1〜3および比較例1〜4により得られた剥離ライナーについて、剥離異常の有無の評価を行う。まず、剥離強度の測定方法1等と同様にして、剥離ライナーを、60℃且つ湿度90%RHの環境下で21日間放置して、経時サンプルを作製する。また、粘着テープとして、商品名「No.502」(日東電工株式会社製;アクリル系両面粘着テープ、幅:50mm;粘着テープA)、商品名「No.5000NS」(日東電工株式会社製;アクリル系両面粘着テープ、幅:50mm;粘着テープB)、商品名「KSR−532P」(日東電工株式会社製;アクリル系両面粘着テープ、幅:50mm;粘着テープC)を用いる。
2 両面粘着テープ
2a 粘着剤層
2b 基材(両面粘着テープ用基材)
2c 粘着剤層
3 剥離ライナー
3a 軽面側離型処理層
3b 基材(剥離ライナー用基材)
3c 重面側離型処理層
Claims (5)
- 基材の両面に離型処理層が形成された構成を有する剥離ライナーであって、基材の一方の面側の離型処理層が熱硬化型シリコーン系剥離剤により形成され、且つ基材の他方の面側の離型処理層が電離性放射線硬化型シリコーン系剥離剤により形成されていることを特徴とする剥離ライナー。
- 電離性放射線硬化型シリコーン系剥離剤が紫外線硬化型シリコーン系剥離剤である請求項1記載の剥離ライナー。
- 熱硬化型シリコーン系剥離剤により形成された離型処理層が、粘着面に対する剥離強度が小さい側の離型処理層として利用され、電離性放射線硬化型シリコーン系剥離剤により形成された離型処理層が、粘着面に対する剥離強度が大きい側の離型処理層として利用される請求項1又は2記載の剥離ライナー。
- 電離性放射線硬化型シリコーン系剥離剤により形成された離型処理層が、粘着面に対する剥離強度(剥離角度:180°、引張速度:300mm/min、23℃、50%RH)が0.1〜1.0N/50mmであり、且つ温度60℃且つ湿度90%RHの環境下で21日間放置した際の剥離強度の低下率が50%以下である特性を有している請求項3記載の剥離ライナー。
- 両面の粘着面が1枚の剥離ライナーにより保護されている構成を有している両面粘着テープ又はシートであって、剥離ライナーとして、請求項1乃至4の何れかの項に記載の剥離ライナーが用いられていることを特徴とする両面粘着テープ又はシート。