JP2005131607A - Method for forming pattern face - Google Patents
Method for forming pattern face Download PDFInfo
- Publication number
- JP2005131607A JP2005131607A JP2003373399A JP2003373399A JP2005131607A JP 2005131607 A JP2005131607 A JP 2005131607A JP 2003373399 A JP2003373399 A JP 2003373399A JP 2003373399 A JP2003373399 A JP 2003373399A JP 2005131607 A JP2005131607 A JP 2005131607A
- Authority
- JP
- Japan
- Prior art keywords
- coating
- paint
- colored
- weight
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、建築物、土木構造物等の表面化粧に好適な模様面の形成方法に関するものである。 The present invention relates to a method for forming a pattern surface suitable for surface decoration of buildings, civil engineering structures, and the like.
従来、建築物の内外壁面、天井、床等、あるいは土木構造物の表面等に対し、各種色彩による模様を形成する方法の一つとして、コンビネーション塗工法と呼ばれる方法が知られている。この方法は、ゴムかん、スポンジ等に塗料を含ませた後、被塗面に対してこれらを繰返し押し当て、さらに別の色相の塗料を同様の方法で塗り重ねることにより多彩な模様を形成させるというものである。
また、特開２０００−２４５８７号公報（特許文献１）には、擬木調の多彩模様を形成する方法が記載されている。該公報に記載の方法は、有機溶剤型塗料を塗装した後、その表面にローラをローリングさせて筋状の凹凸を形成させ、次いで茶色塗料を塗装し、さらに黒色塗料を塗装してその凸部のみを拭き取る、というものである。
2. Description of the Related Art Conventionally, a method called a combination coating method is known as one of methods for forming patterns with various colors on the inner and outer wall surfaces, ceilings, floors, etc. of buildings or the surface of civil engineering structures. In this method, paints are included in rubber cans, sponges, etc., and then repeatedly pressed against the surface to be coated, and further paints of different hues are applied in the same way to form various patterns. That's it.
Japanese Laid-Open Patent Publication No. 2000-24587 (Patent Document 1) describes a method of forming a pseudo-tree-like colorful pattern. In the method described in the publication, after applying an organic solvent-type paint, a roller is rolled on the surface to form streak-like irregularities, then a brown paint is applied, and then a black paint is applied, and the convex portions are applied. Only wipe off.
しかしながら、上述のような方法は、いずれも非常に繁雑であり、多大な手間と時間を要するという問題点がある。また、塗装作業者の熟練した技能を必要とするため、その仕上り具合は作業者の熟練度合によって大きく左右されやすく、常に一定水準の品質で仕上げられるというものではない。
本発明はこのような点に鑑みなされたものであり、その目的は、塗装作業者の熟練度合に頼ることなく、比較的簡単な作業で、美観性に優れた多彩な模様が形成できる塗装方法を提供することである。
However, all the methods as described above are very complicated, and there is a problem that a lot of labor and time are required. In addition, since the skill required by the painter is required, the finishing condition is greatly influenced by the skill of the worker, and it is not always possible to finish with a certain level of quality.
The present invention has been made in view of the above points, and the purpose thereof is a coating method capable of forming a variety of patterns with excellent aesthetics by a relatively simple operation without depending on the skill level of the coating operator. Is to provide.
本発明者は、上記目的を達成するため鋭意検討を行なった結果、液状着色塗料が内包された着色粒子を含む塗料を基材に塗着させた後、該着色粒子を押圧具で処理する方法に想到し、本発明を完成させるに到った。
すなわち、本発明は以下の特徴を有するものである。
１．（１）基材に対し、液状着色塗料が内包された着色粒子を少なくとも１種以上含む多彩模様塗料を塗付し、基材上に該着色粒子を分散配置する工程、
（２）塗膜の乾燥前に、押圧具を用いて該着色粒子を押圧しつつ引き伸ばす工程、
（３）塗膜を乾燥させる工程、
を有することを特徴とする模様面の形成方法。
As a result of intensive studies to achieve the above object, the present inventor has applied a paint containing colored particles containing a liquid colored paint to a substrate, and then treated the colored particles with a pressing tool. The present invention has been completed.
That is, the present invention has the following characteristics.
1. (1) A step of applying a multi-color paint containing at least one kind of colored particles containing a liquid colored paint to a base material, and dispersing and arranging the colored particles on the base material.
(2) A step of stretching the colored particles while pressing the colored particles using a pressing tool before drying the coating film,
(3) a step of drying the coating film,
A method for forming a pattern surface, comprising:
本発明によれば、塗装作業者の熟練度合に頼ることなく、比較的簡単な作業で、美観性に優れた多彩な模様が形成できる。 According to the present invention, various patterns having excellent aesthetics can be formed by a relatively simple operation without depending on the skill level of the painter.
以下、本発明をその実施の形態に基づき詳細に説明する。 Hereinafter, the present invention will be described in detail based on the embodiments.
本発明は、主に、建築物の内外壁面、天井、床等、あるいは土木構造物の表面等に適用することができる。このような部位を構成する基材としては、例えば、コンクリート、モルタル、サイディングボード、押出成形板、石膏ボード、パーライト板、合板、プラスチック板、金属板、木工板、ガラス、陶磁器タイル等の各種基材が挙げられる。
これら基材は、何らかの表面処理（フィラー処理、サーフェーサー処理、シーラー処理等）が施されたものや、予め着色塗料等で着色されたものでもよく、既に塗膜が形成されたものや、壁紙が貼り付けられたものであってもよい。また、基材としては、通常、表面が平滑なものを使用するが、作業工程に支障をきたさなければ、ある程度微細な凹凸を有するものも使用できる。
The present invention can be applied mainly to the inner and outer wall surfaces, ceilings, floors, etc. of buildings, or the surface of civil engineering structures. Examples of the base material constituting such a part include various bases such as concrete, mortar, siding board, extrusion board, gypsum board, pearlite board, plywood board, plastic board, metal board, wood board, glass and ceramic tile. Materials.
These base materials may have been subjected to some surface treatment (filler treatment, surfacer treatment, sealer treatment, etc.), or may be pre-colored with a colored paint or the like. It may be affixed. Moreover, as a base material, what has a smooth surface is normally used, However, The thing which has a certain micro unevenness | corrugation can also be used if it does not interfere with a work process.
本発明の第１工程では、基材に対し、液状着色塗料が内包された着色粒子を少なくとも１種以上含む多彩模様塗料を塗付し、基材上に該着色粒子を分散配置する。 In the first step of the present invention, a multi-color paint containing at least one kind of colored particles containing a liquid colored paint is applied to the base material, and the colored particles are dispersed on the base material.
第１工程で使用可能な多彩模様塗料としては、第２工程での引き伸ばしによる模様形成が可能であれば特に制限されず、公知の多彩模様塗料、または市販の多彩模様塗料等を使用することができる。多彩模様塗料は、ＪＩＳ Ｋ５６６７（２００２）「多彩模様塗料」に規定されており、塗料を構成する分散媒と着色粒子の組み合わせによって、水中油型（Ｏ／Ｗ型）、油中水型（Ｗ／Ｏ型）、油中油型（Ｏ／Ｏ型）及び水中水型（Ｗ／Ｗ型）の４種類に分類される。本発明では、この中でも、水中油型（Ｏ／Ｗ型）、または水中水型（Ｗ／Ｗ型）の多彩模様塗料が好適である。 The multicolor pattern paint that can be used in the first step is not particularly limited as long as the pattern can be formed by stretching in the second step, and a known multicolor pattern paint or a commercially available multicolor pattern paint may be used. it can. The multicolored paint is defined in JIS K5667 (2002) “Multicolored paint”. Oil-in-water type (O / W type), water-in-oil type (W / O type), oil-in-oil type (O / O type), and water-in-water type (W / W type). In the present invention, among them, an oil-in-water type (O / W type) or a water-in-water type (W / W type) multicolored paint is preferable.
着色粒子内部の液状着色塗料は、第２工程での引き伸ばしによる模様形成が可能であれば、ある程度ゲル化した状態であってもよい。
着色粒子の色相は、最終的に形成される模様に応じて適宜設定すればよい。本発明において使用する多彩模様塗料としては、通常２色以上、好ましくは３〜８色程度の着色粒子が含まれるものが好適である。
多彩模様塗料における着色粒子の粒径も、最終的に形成される模様に応じて適宜設定すればよいが、通常は０．０１〜５ｍｍ、好ましくは０．１〜２ｍｍ程度である。粒子径が異なる着色粒子を種々組み合せることによって、意匠性の幅を広げることもできる。
The liquid colored paint inside the colored particles may be in a gelled state to some extent as long as the pattern can be formed by stretching in the second step.
What is necessary is just to set suitably the hue of a colored particle according to the pattern finally formed. As the multicolored paint used in the present invention, those containing usually 2 or more, preferably 3 to 8 colored particles are suitable.
The particle size of the colored particles in the multicolored paint may be appropriately set according to the pattern finally formed, but is usually about 0.01 to 5 mm, preferably about 0.1 to 2 mm. By combining various colored particles having different particle diameters, the range of design properties can be expanded.
第１工程において着色粒子を分散配置するには、多彩模様塗料を吹き付け塗装すればよいが、多彩模様塗料の組成に応じてローラー塗装、刷毛塗り等の方法を採用することもできる。
多彩模様塗料の塗付量は、最終的な模様の種類によって異なるが、通常０．１〜１ｋｇ／ｍ２程度である。
In order to disperse and arrange the colored particles in the first step, it is only necessary to spray and apply a multicolored paint, but depending on the composition of the multicolored paint, methods such as roller coating and brush coating can also be employed.
The amount of the multicolor paint applied varies depending on the final pattern type, but is usually about 0.1 to 1 kg / m 2 .
本発明の第２工程では、第１工程で塗付された塗料の乾燥前に、押圧具を用いて着色粒子を押圧しつつ引き伸ばす。この工程では、押圧によって着色粒子を意図的に破壊し、粒子内部の液状着色塗料を引き伸ばすことで模様を形成させる。 In the second step of the present invention, before drying the paint applied in the first step, the colored particles are stretched while being pressed using a pressing tool. In this step, the colored particles are intentionally broken by pressing, and a pattern is formed by stretching the liquid colored paint inside the particles.
押圧具としては、鏝、へら、ローラー等が使用できる。既存の建築物や土木構造物に対して適用する場合には、鏝、へら等が好適である。
工場内において、サイディングボード、押出成形板、石膏ボード、金属板等の板状基材に適用する場合には、押圧具と、板状基材が搬送可能な手段とを備えた装置を用意し、多彩模様塗料塗装後に板状基材表面が押圧具に接触して通過するようにすればよい。
As the pressing tool, a scissors, a spatula, a roller or the like can be used. When applied to an existing building or civil engineering structure, a fence, a spatula, etc. are suitable.
In the factory, when applying to plate-like substrates such as siding boards, extrusion-molded plates, gypsum boards, metal plates, etc., prepare a device equipped with a pressing tool and means that can convey the plate-like substrate. The plate-like base material surface may pass through the pressing tool after painting with the multicolor paint.
押圧具への荷重の程度は、着色粒子が潰れて引き伸ばしが可能となる範囲内で適宜設定することができる。押圧具の荷重を調整することによって、形成される模様の長さ、幅、厚み等を変化させることもできる。
押圧具で着色粒子を引き伸ばす方向は、所望の模様に応じて設定することができる。例えば、直線的な模様を形成する場合には、一定方向へまっすぐに引き伸ばせばよい。また、円弧状の模様を形成する場合には、半円を描くように引き伸ばせばよい。その他ランダムに引き伸ばしを行なうこともできる。
押圧具においては、予め水、溶剤等で湿らせておくこともできる。これにより、押圧具への多彩模様塗料の付着を抑制し、作業効率を高めることができる。
The degree of the load applied to the pressing tool can be appropriately set within a range in which the colored particles can be crushed and stretched. By adjusting the load of the pressing tool, the length, width, thickness and the like of the pattern to be formed can be changed.
The direction in which the colored particles are stretched by the pressing tool can be set according to the desired pattern. For example, when a linear pattern is formed, it may be stretched straight in a certain direction. When an arc-shaped pattern is formed, the pattern may be stretched so as to draw a semicircle. It is also possible to perform stretching at random.
In the pressing tool, it can be previously moistened with water, a solvent or the like. Thereby, adhesion of the colorful pattern coating material to a pressing tool can be suppressed, and work efficiency can be improved.
本発明の第３工程では、第２工程で形成した塗膜を乾燥させる。乾燥は通常、常温で行えばよいが、必要に応じ加温することもできる。
以上の工程により、本発明では種々の模様を形成することができる。具体的には、第１工程における多彩模様塗料の種類、第２工程における押圧具の種類、処理時の荷重や方向等を適宜組み合せることによって、所望の模様を得ることができる。本発明では、例えば、木目調、大理石調等の模様が形成できる。
In the third step of the present invention, the coating film formed in the second step is dried. Drying is usually performed at room temperature, but can be heated as necessary.
Through the above steps, various patterns can be formed in the present invention. Specifically, a desired pattern can be obtained by appropriately combining the type of multicolored paint in the first step, the type of pressing tool in the second step, the load and direction during processing, and the like. In the present invention, for example, a wood grain pattern, a marble pattern or the like can be formed.
本発明では、必要に応じ、クリヤー塗料を塗付することもできる。特に耐候性が要求される構造物外部の部位に施工する際には、保護の目的でクリヤー塗料を塗付するのが好ましい。
クリヤー塗料としては公知のものが使用できる。例えば、アクリル樹脂系、ウレタン樹脂系、エポキシ樹脂系、アクリルシリコン系、フッ素系等が挙げられる。クリヤー塗料は、水性系または溶剤系のいずれであってもよく、艶の程度（艶消しタイプ、艶有りタイプ等）についても特に限定されない。
クリヤー塗料による塗装は、公知の塗付方法によれば良く、例えば吹き付け塗装、ローラー塗装、刷毛塗り等の各種の塗装方法により実施することができる。クリヤー塗料の塗付量は、通常０．１〜０．４ｋｇ／ｍ２程度である。
In the present invention, a clear paint can be applied as necessary. It is preferable to apply a clear paint for the purpose of protection, particularly when the construction is performed on a part outside the structure where weather resistance is required.
Known clear paints can be used. For example, an acrylic resin system, a urethane resin system, an epoxy resin system, an acrylic silicon system, a fluorine system, etc. are mentioned. The clear paint may be either water-based or solvent-based, and the degree of gloss (matte type, glossy type, etc.) is not particularly limited.
Coating with the clear paint may be performed by a known coating method, and can be performed by various coating methods such as spray coating, roller coating, and brush coating. The application amount of the clear paint is usually about 0.1 to 0.4 kg / m 2 .
以下に実施例を示し、本発明の特徴をより明確にする。 Examples are given below to clarify the features of the present invention.
（多彩模様塗料の製造）
着色粒子分散液Ａ
まず、容器内にアクリル樹脂エマルション（固形分５０％）２００重量部を仕込み、攪拌羽根の回転速度を１８００ｒｐｍとして攪拌を行いながら、ヒドロキシエチルセルロース３重量部と、消泡剤１重量部と、水２５０重量部とを均一に混合することにより、分散媒Ａを製造した。
次に、別の容器内にアクリル樹脂エマルション９０重量部を仕込み、攪拌羽根の回転速度を１８００ｒｐｍとして攪拌を行いながら、ガラクトマンナン３重量％水溶液１８０重量部と、黄色顔料分散液４０重量部と、赤色顔料分散液３０重量部と、黒色顔料分散液５重量部と、消泡剤５重量部と、水８０重量部とを均一に混合することにより着色塗料Ａ（淡褐色）を製造した。
上述の分散媒Ａに対し、分散安定剤としてホウ酸アンモニウム５重量％水溶液を８重量部加え、攪拌羽根の回転速度を９００ｒｐｍとして均一に混合した後、さらに攪拌を継続しながら着色塗料Ａを徐々に添加・分散することにより、０．８〜１．２ｍｍの淡褐色粒子が分散した着色粒子分散液Ａを得た。
(Manufacture of multicolored paint)
Colored particle dispersion A
First, 200 parts by weight of an acrylic resin emulsion (solid content 50%) was charged in a container, and while stirring at a stirring blade rotation speed of 1800 rpm, 3 parts by weight of hydroxyethyl cellulose, 1 part by weight of an antifoaming agent, and 250 parts of water were added. Dispersion medium A was produced by uniformly mixing with parts by weight.
Next, 90 parts by weight of an acrylic resin emulsion was charged in another container, and while stirring at a rotation speed of a stirring blade of 1800 rpm, 180 parts by weight of a 3% by weight galactomannan aqueous solution, 40 parts by weight of a yellow pigment dispersion, A colored paint A (light brown) was produced by uniformly mixing 30 parts by weight of a red pigment dispersion, 5 parts by weight of a black pigment dispersion, 5 parts by weight of an antifoaming agent, and 80 parts by weight of water.
8 parts by weight of an aqueous solution of ammonium borate 5% by weight as a dispersion stabilizer is added to the dispersion medium A described above, and the mixture is uniformly mixed at a rotation speed of the stirring blade of 900 rpm. By adding and dispersing in, a colored particle dispersion A in which 0.8 to 1.2 mm of light brown particles were dispersed was obtained.
着色粒子分散液Ｂ
着色塗料Ａに代えて、アクリル樹脂エマルション９０重量部、ガラクトマンナン３重量％水溶液１８０重量部、黄色顔料分散液２５重量部、赤色顔料分散液４５重量部、黒色顔料分散液２０重量部、消泡剤５重量部、水８０重量部からなる着色塗料Ｂ（濃褐色）を使用した以外は、着色粒子分散液Ａと同様の製造方法で着色粒子分散液Ｂを得た。
Colored particle dispersion B
Instead of the colored paint A, 90 parts by weight of acrylic resin emulsion, 180 parts by weight of 3% by weight galactomannan aqueous solution, 25 parts by weight of yellow pigment dispersion, 45 parts by weight of red pigment dispersion, 20 parts by weight of black pigment dispersion, defoaming Colored particle dispersion B was obtained by the same production method as colored particle dispersion A, except that colored paint B (dark brown) consisting of 5 parts by weight of the agent and 80 parts by weight of water was used.
着色粒子分散液Ｃ
着色塗料Ａに代えて、アクリル樹脂エマルション９０重量部、ガラクトマンナン３重量％水溶液１８０重量部、黒色顔料分散液９０重量部、消泡剤５重量部、水８０重量部からなる着色塗料Ｃ（黒色）を使用した以外は、着色粒子分散液Ａと同様の製造方法で着色粒子分散液Ｃを得た。
Colored particle dispersion C
Instead of the colored paint A, a colored paint C (black) comprising 90 parts by weight of an acrylic resin emulsion, 180 parts by weight of a 3% by weight galactomannan aqueous solution, 90 parts by weight of a black pigment dispersion, 5 parts by weight of an antifoaming agent, and 80 parts by weight of water. The colored particle dispersion C was obtained by the same production method as the colored particle dispersion A, except that
以上の方法で得られた着色粒子分散液Ａと着色粒子分散液Ｂと着色粒子分散液Ｃを、４０：４０：２０の重量比率で混合することにより、多彩模様塗料を製造した。 By mixing the colored particle dispersion A, the colored particle dispersion B, and the colored particle dispersion C obtained by the above method in a weight ratio of 40:40:20, a multicolor paint was produced.
（模様面形成）
予めシーラーが塗装されたスレート板に対し、上記多彩模様塗料を塗付量０．６ｋｇ／ｍ２でスプレー塗装し、３種の着色粒子をほぼ均一に分散配置させた。その直後、塗装面に鏝を接触させつつ一定方向に直線的に押圧した。押圧後、室温で２４時間させ、その外観を確認した。
以上の方法によって、木目調の模様面を簡単に得ることができた。この実施例で得られた模様面を図１に示す。
(Pattern surface formation)
The slate plate previously coated with a sealer was spray-coated with the above-mentioned multicolored paint at a coating amount of 0.6 kg / m 2 to disperse the three kinds of colored particles almost uniformly. Immediately after that, it was linearly pressed in a certain direction with a heel in contact with the painted surface. After pressing, the appearance was confirmed for 24 hours at room temperature.
By the above method, a woodgrain pattern surface could be easily obtained. The pattern surface obtained in this example is shown in FIG.
Claims (1)
（２）塗膜の乾燥前に、押圧具を用いて該着色粒子を押圧しつつ引き伸ばす工程、
（３）塗膜を乾燥させる工程、
を有することを特徴とする模様面の形成方法。 (1) A step of applying a multi-color paint containing at least one kind of colored particles containing a liquid colored paint to a base material, and dispersing and arranging the colored particles on the base material.
(2) A step of stretching the colored particles while pressing the colored particles using a pressing tool before drying the coating film,
(3) a step of drying the coating film,
A method for forming a pattern surface, comprising: