JP2004299203A

JP2004299203A - Packaging material for aromatic

Info

Publication number: JP2004299203A
Application number: JP2003093820A
Authority: JP
Inventors: Noriko Asaoka; 紀子浅岡
Original assignee: Toppan Printing Co Ltd
Current assignee: Toppan Inc
Priority date: 2003-03-31
Filing date: 2003-03-31
Publication date: 2004-10-28
Anticipated expiration: 2023-03-31
Also published as: JP4258252B2

Abstract

<P>PROBLEM TO BE SOLVED: To suppress delamination due to the deterioration of an adhesive between an aroma-retaining aluminum foil layer and a non-aroma-retaining film layer caused by an aroma and to prevent damage of a preserving function of a vessel and an adverse effect on the product quality of an aromatic even when the delamination occurs. <P>SOLUTION: An aroma-retaining film layer 3, an adhesive layer 4, a gas-barrier resin layer 41, a peelable resin layer 5 and the non-aroma-retaining film layer 6 are stacked in this sequence. The aroma-retaining film layer 3, the adhesive layer 4 and the gas-barrier resin layer 41 are so laminated as to be easy to peel from the non-aroma-retaining film layer 6 by the medium of the peelable resin layer 5. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【産業上の利用分野】
本発明は、固形状や顆粒状や液体状などの芳香剤を収容包装した包装体から、剥離性フィルムを剥離することにより、包装体側に気体透過性のあるフィルムを残して剥離できる芳香剤包装材料及び芳香剤容器用蓋料に関する。
【０００２】
【従来の技術】
従来から、芳香剤包装用の容器としては、ガスバリア性のあるガラス製やプラスチック製などのボトル状、カップ状、トレー状など各種形状の容器の開口部に紙や不織布製の通気性シートや樹脂製の通気性シートによるインナー蓋材を被せて熱融着シールし、その開口部に、ガスバリア性のある密封性のプラスチックキャップを施蓋密封した芳香剤入り容器などが用いられている。
【０００３】
また、通気性シートやフィルムを用いて製袋し、芳香剤を入れて包装した複数の小袋を、ガスバリア性樹脂フィルムを用いて製袋したパウチ内に収容して密封シール包装した芳香剤入り容器などがある。
【０００４】
また近年では、一般に芳香剤を包装するためのプラスチック容器や、容器の開口部を密封シールするシール蓋材（シート）あるいは密封性パウチに用いる包装材料としては、香気が容器の外に蒸散して芳香剤が劣化しないように長期保存性を考慮して、樹脂フィルム製の包装材料の中間層に、ガスバリア性のアルミニウム箔や、酸化ケイ素や酸化アルミニウム等の金属酸化物を蒸着したポリエチレンテレフタレートフィルムを保香性層として積層したガスバリア性の複合積層材料が用いられている。
【０００５】
このガスバリア性の複合積層材料は、特に芳香剤を容器内に収容した状態で使用する形態の簡易容器の蓋材に多用されており、蓋材の表面層にガスバリア性のアルミニウム層を保香性層として適用した易剥離性のガスバリア性複合積層材料として使用されている。
【０００６】
この易剥離性のガスバリア性複合積層材料は、使用前の保管中は、保香性層による保香性により香気の蒸散は防止され、使用する際には、容器蓋材表面側にある保香性フィルム層を剥離することにより、容器開口部側に積層材料の非ガスバリア性（通気性）の残留蓋材フィルムである非保香性フィルム（シーラント）が残るようになっており、容器側に残留した非保香性フィルムを通して芳香剤の香気を蒸散できるようになっている。
【０００７】
【発明が解決しようとする課題】
ところで、上記ガスバリア性複合積層材料の保香性フィルム層と非保香性フィルム層との層間は、使用する際に容易に剥離できるように、易剥離性の接着剤を介して積層接着しているために、容器内の芳香剤の蒸気が、非保香性フィルムを通して接着剤を劣化させたり、保香性フィルム層と非保香性フィルム層との間でデラミネーションが発生して、蓋材の保香性フィルム層と非保香性フィルム層との界面に不規則な剥離領域や空隙が発生したり、陳列保管中や運搬中に、保香性フィルム層が非保香性フィルム層から完全に剥離して、容器外への芳香剤の蒸散損失や劣化が発生して、容器の保存機能にダメージを与え、芳香剤の製品品質に悪い影響を及ぼす心配があった。
【０００８】
本発明は、保香性層と非保香性フィルム層との間でのデラミネーションを抑制するとともに、たとえデラミネーションが発生しても、容器の保存機能にダメージを与えることなく、芳香剤の製品品質に対する悪影響を及ぼさないようにすることにある。
【０００９】
【課題を解決するための手段】
本発明の請求項１に係る発明は、保香性フィルム層３と接着剤層４とガスバリア性樹脂層４１と剥離性樹脂層５と非保香性フィルム層６とをこの順に積層し、保香性フィルム層３と接着剤層４とガスバリア性樹脂層４１とを、前記剥離性樹脂層５を介して非保香性フィルム層６から易剥離可能に積層したことを特徴とする芳香剤包装材料である。
【００１０】
本発明の請求項２に係る発明は、上記請求項１に係る芳香剤包装材料において、前記ガスバリア性樹脂層４１がエチレン−ビニルアルコール共重合体樹脂からなることを特徴とする芳香剤包装材料である。
【００１１】
本発明の請求項３に係る発明は、上記請求項１又は２に係る芳香剤包装材料において、前記ガスバリア性樹脂層４１と剥離性樹脂層５との間にナイロン樹脂層４２を備えることを特徴とする芳香剤包装材料である。
【００１２】
本発明の請求項４に係る発明は、上記請求項１乃至請求項３のいずれか１項に係る芳香剤包装材料において、前記非保香性フィルム層６が直鎖型低密度ポリエチレン樹脂からなることを特徴とする芳香剤包装材料である。
【００１３】
本発明の請求項５に係る発明は、上記請求項１乃至請求項３のいずれか１項に係る芳香剤包装材料において、前記非保香性フィルム層６がポリプロピレン樹脂からなることを特徴とする芳香剤包装材料である。
【００１４】
本発明の請求項６に係る発明は、上記請求項１乃至請求項５のいずれか１項に係る芳香剤包装材料において、前記剥離性樹脂層５が凝集易剥離性樹脂からなることを特徴とする芳香剤包装材料である。
【００１５】
本発明の請求項７に係る発明は、上記請求項１乃至請求項５のいずれか１項に係る芳香剤包装材料において、前記剥離性樹脂層５が前記非保香性フィルム層６に対して層間易剥離性を呈する層間易剥離性樹脂からなることを特徴とする芳香剤包装材料である。
【００１６】
本発明の請求項８に係る発明は、上記請求項４に係る芳香剤包装材料において、前記剥離性樹脂層５が前記直鎖型低密度ポリエチレン樹脂による非保香性フィルム層６に対して層間易剥離性を呈するポリプロピレン樹脂からなることを特徴とする芳香剤包装材料である。
【００１７】
本発明の請求項９に係る発明は、上記請求項５に係る芳香剤包装材料において、前記剥離性樹脂層５が前記ポリプロピレン樹脂による非保香性フィルム層６に対して層間易剥離性を呈する直鎖型低密度ポリエチレン樹脂からなることを特徴とする芳香剤包装材料である。
【００１８】
本発明の請求項１０に係る発明は、上記請求項３乃至９のいずれか１項に係る芳香剤包装材料において、前記ガスバリア性樹脂層４１及びナイロン樹脂層４２及び剥離性樹脂層５の三層と、非保香性フィルム層６とを共押し出しラミネートにてこの順に積層したことを特徴とする芳香剤包装材料である。
【００１９】
本発明の請求項１１に係る発明は、上記請求項１乃至請求項１０のいずれか１項に係る芳香剤包装材料において、前記保香性フィルム層３の外面に印刷基材層２を積層したことを特徴とする芳香剤包装材料である。
【００２０】
本発明の請求項１２に係る発明は、上記請求項１乃至請求項１１のいずれか１項に係る芳香剤包装材料を、芳香剤包装容器の蓋材に用いることを特徴とする芳香剤包装材料である。
【００２１】
本発明の請求項１３に係る発明は、上記請求項１乃至請求項１２のいずれか１項に係る芳香剤包装材料を、芳香剤包装袋の全部若しくは一部に用いることを特徴とする芳香剤包装材料である。
【００２２】
【発明の実施の形態】
本発明の芳香剤包装材料の実施の形態は、図１の積層断面図に示すように、保香性フィルム層３と接着剤層４とガスバリア性樹脂層４１と剥離性樹脂層５と非保香性フィルム層６（シーラント層）とをこの順に積層したもので、保香性フィルム層３とガスバリア性樹脂層４１との間は接着剤層４により接着されているもので、保香性フィルム層３及びガスバリア性樹脂層４１と、非保香性フィルム層６とを、前記剥離性樹脂層５を介して易剥離可能にしたものである。
【００２３】
前記保香性フィルム層３に使用するフィルムとしては、ガスバリア性のあるアルミニウム箔あるいは酸化ケイ素や酸化アルミニウム等の金属酸化物を蒸着した金属酸化物蒸着ポリエチレンテレフタレートフィルムが用いられ、また、前記ガスバリア性樹脂層４１としては、エチレン−ビニルアルコール共重合体樹脂（ＥＶＯＨ）が用いられ、また、ガスバリア性樹脂層４１と剥離性樹脂層５との間にはナイロン樹脂層４２（ＮＹ）が積層される。
【００２４】
また、前記非保香性フィルム層６としては、直鎖型低密度ポリエチレン樹脂（ＬＬＤＰＥ）、又はポリプロピレン樹脂（ＰＰ）が用いられる。
【００２５】
前記剥離性樹脂層５としては、該樹脂層５の層内における凝集力に抗して、その層内を二分割状態に容易に引き裂くことができるような凝集易剥離性樹脂を用いることができる。
【００２６】
また、剥離性樹脂層５としては、前記非保香性フィルム層６に対して接着力の弱い層間易剥離性を呈する層間易剥離性樹脂を用いてもよい。
【００２７】
例えば、非保香性フィルム層６に直鎖型低密度ポリエチレン樹脂を用いた場合には、前記剥離性樹脂層５として層間易剥離性を呈するポリプロピレン樹脂を用い、非保香性フィルム層６にポリプロピレン樹脂を用いた場合には、前記剥離性樹脂層５として層間易剥離性を呈する直鎖型低密度ポリエチレン樹脂を用いることができる。
【００２８】
本発明の芳香剤包装材料は、前記ガスバリア性樹脂層４１及びナイロン樹脂層４２及び剥離性樹脂層５の三層と非保香性フィルム層６とを、４種４層の共押し出しラミネート機にて、この順に積層してラミネートすることができ、その後に、このようにして得られた積層材料の前記ガスバリア性樹脂層４１の表面に、例えばウレタン系の接着剤層４を介して、印刷基材層２と中間層として保香性フィルム層３とを積層ラミネートして形成することができる。
【００２９】
本発明の芳香剤包装材料の前記保香性フィルム層３の外面には、ポリエチレンテレフタレートフィルム、あるいは坪量８５ｇ／ｍ^２程度の片面アート紙などの印刷基材層２を積層することができ、該印刷基材層２の表面若しくは裏面側には容器の包装内容に関する適宜なる情報を印刷表示することができる。また、保香性フィルム層として、酸化ケイ素や酸化アルミニウム等の金属酸化物を蒸着したポリエチレンテレフタレートフィルムを用いた場合、このフィルムに直接、美麗な印刷層を形成することも可能である。
【００３０】
本発明の芳香剤包装材料の用途としては、例えば、芳香剤を包装する容器の蓋材の材料に用いることができ、あるいは芳香剤包装袋を製袋するための全部若しくは一部の製袋用材料として用いることができる。
【００３１】
図２（Ａ）は、本発明の芳香剤包装材料を、芳香剤を収容したプラスチック製のトレー状容器３０の密封用蓋材２０として使用した場合の斜視図、（Ｂ）はその側断面図であり、図３（Ａ）は、本発明の芳香剤包装材料を、芳香剤を収容したプラスチック製のカップ状容器３０の密封用蓋材２０として使用した場合の斜視図、（Ｂ）はその側断面図である。
【００３２】
図２（Ａ）、（Ｂ）、又は図３（Ａ）、（Ｂ）に示すように、芳香剤を収容した容器３０のフランジ部３２に、蓋材２０の周辺部２２を非保香性フィルム層６にて熱融着して密封したものであり、例えば、容器３０のフランジ部３２がポリエチレン樹脂製である場合には、芳香剤包装材料の非保香性フィルム層６（シーラント層）に直鎖型低密度ポリエチレン樹脂を用いたヒートシール性の良好な蓋材２０を用いるものであり、容器３０のフランジ部３２がポリプロピレン樹脂製である場合は、芳香剤包装材料の非保香性フィルム層６（シーラント層）にポリプロピレン樹脂を用いたヒートシール性の良好な蓋材２０を用いるものである。
【００３３】
そして、例えば、蓋材２０の一部周辺部２２に摘み部２４（必要に応じてその周辺部２２から突出する摘み部２４）を設け、該周辺部２２と摘み部２４との間には、非保香性フィルム層６を切断する切れ目線ａを設ける。
【００３４】
このような容器３０内の芳香剤は、蓋材２０の保香性フィルム層３とガスバリア性樹脂層４１によって芳香剤の香気が容器外側に蒸散せずに密封状態が保持できる。
【００３５】
容器３０内の芳香剤を容器外側に蒸散させて使用する際には、図２（Ｂ）、又は図３（Ｂ）に示すように、蓋材２０の摘み部２４を摘んで引っ張り上げることにより、容器３０側に通気性の非保香性フィルム層６が残った状態で、保香性フィルム層３、ガスバリア性樹脂層４１、ナイロン樹脂層４２を剥離することができ、容器３０内に収容した芳香剤の香気を非保香性フィルム層６を通して外側に蒸散させることができる。
【００３６】
また、図４は、本発明の芳香剤包装材料を、芳香剤を収容したトレー状容器３０を外側から密封包装するためのプラスチックフィルム製のパウチ６１の製袋用材料の全部又は一部として使用した場合の斜視図、図５は、本発明の芳香剤包装材料を、芳香剤を収容した１個乃至複数個の分包体５１（小袋）を密封包装するためのプラスチックフィルム製のパウチ６１の製袋用材料の全部又は一部として使用した場合の斜視図である。
【００３７】
図４に示す芳香剤を収容したトレー状容器３０は、そのフランジ部３２にシート状蓋材５１の周辺部５２をヒートシールして収容包装したものであるが、容器３０本体及び／又は蓋材５１は、必ずしもプラスチック製である必要はなく、単なる紙製であってもよく、また、ガスバリア性を備えている必要もなく、密封包装されている必要もない。
【００３８】
また、図５に示す芳香剤を収容した分包体５１は、必ずしもプラスチックフィルム製である必要はなく、単なる紙製であってもよく、また、ガスバリア性を備えている必要もなく、密封包装されている必要もない。
【００３９】
本発明の芳香剤包装材料を用いて製袋したパウチ６１、又は本発明の芳香剤包装材料とガスバリア性のある他のプラスチックフィルム材料とを併用して製袋したパウチ６１内に、図４、図５に示す芳香剤を収容した容器３０又は分包体５１を装填して密封シール包装することにより、容器３０又は分包体５１内の芳香剤は、芳香剤包装材料の蓋材２０の保香性フィルム層３とガスバリア性樹脂層４１、又は本発明の芳香剤包装材料の蓋材２０の保香性フィルム層３とガスバリア性樹脂層４１と、ガスバリア性の他のプラスチックフィルム材料によって、芳香剤の香気を容器外側に蒸散させずに密封状態を保持できる。
【００４０】
そして、図４、図５に示す容器３０又は分包体５１内の芳香剤を容器外側に蒸散させて使用する際には、密封シールしたパウチ６１における本発明の芳香剤包装材料にて製袋した部分の端部（又は摘み部、必要に応じてその端部から突出する摘み部）を摘んで引っ張り上げることにより、パウチ６１側に通気性の非保香性フィルム層６が残った状態で、保香性フィルム層３、ガスバリア性樹脂層４１、ナイロン樹脂層４２を剥離することができ、パウチ６１内に収容した容器３０又は分包体５１内の芳香剤の香気を非保香性フィルム層６を通して外側に蒸散させることができる。
【００４１】
なお、上記パウチ６１の製袋材料に、本発明の芳香剤包装材料とガスバリア性のある他のプラスチックフィルム材料とを併用する場合において、本発明の芳香剤包装材料の非保香性フィルム層６（シーラント層）に直鎖型低密度ポリエチレン樹脂を用いる場合には、ガスバリア性のある他のプラスチックフィルム材料のシーラント層にはポリエチレン樹脂を用い、本発明の芳香剤包装材料の非保香性フィルム層６（シーラント層）にポリプロピレン樹脂を用いる場合には、ガスバリア性のある他のプラスチックフィルム材料のシーラント層にはポリプロピレン樹脂を用いることが望ましい。
【００４２】
【実施例】
本発明の芳香剤包装材料の積層構成の具体的実施例を下記に示す。
【００４３】
（積層構成材料）
▲１▼印刷基材層
ポリエチレンテレフタレートフィルム：１２μｍ
▲２▼印刷基材層と保香性（ガスバリア性）フィルム層との間の接着剤層
ウレタン系接着剤（５ｇ／ｍ^２）
▲３▼保香性（ガスバリア性）フィルム層
アルミニウム箔（７〜９μｍ）
▲４▼保香性（ガスバリア性）フィルム層とＥＶＯＨ層との間の接着剤層
ウレタン系接着剤（５ｇ／ｍ^２）
▲５▼共押し出し積層材料
ＥＶＯＨ（厚さ１５μｍ）／ＮＹ（厚さ１５μｍ）／ウレタン系接着剤／凝集易剥離性樹脂（ポリエチレン樹脂厚さ３０μｍ）／ＬＬＤＰＥ（厚さ２０μｍ）
▲６▼共押し出し積層材料
ＥＶＯＨ（厚さ１５μｍ）／ＮＹ（厚さ１５μｍ）／ウレタン系接着剤／ＰＰ（厚さ１０μｍ）／ＬＬＤＰＥ（厚さ２０μｍ）
▲７▼共押し出し積層材料
ＥＶＯＨ（厚さ１５μｍ）／ＮＹ（厚さ１５μｍ）／ウレタン系接着剤／凝集易剥離性樹脂（ＰＰ厚さ３０μｍ）／ＰＰ（厚さ２５μｍ）
▲８▼共押し出し積層材料
ＥＶＯＨ（厚さ１５μｍ）／ＮＹ（厚さ１５μｍ）／ウレタン系接着剤／ＬＬＤＰＥ（厚さ１０μｍ）／ＰＰ（厚さ２０μｍ）
【００４４】
＜実施例１＞
▲１▼／▲２▼／▲３▼／▲４▼／▲５▼
【００４５】
＜実施例２＞
▲１▼／▲２▼／▲３▼／▲４▼／▲６▼
【００４６】
＜実施例３＞
▲１▼／▲２▼／▲３▼／▲４▼／▲７▼
【００４７】
＜実施例４＞
▲１▼／▲２▼／▲３▼／▲４▼／▲８▼
【００４８】
【発明の効果】
本発明の芳香剤包装材料は、保香性フィルム層と接着剤層とガスバリア性樹脂層と剥離性樹脂層と非保香性フィルム層とをこの順に積層し、保香性フィルム層と接着剤層とガスバリア性樹脂層とを、前記剥離性樹脂層を介して非保香性フィルム層から易剥離可能に積層したものであり、非保香性フィルム層を通して接着剤層方向に移行する容器内の固形状や顆粒状やゼリー状などの芳香剤から気化する芳香蒸気を、保香性フィルム層を接着している接着剤層と非保香性フィルム層との間に介在しているガスバリア性樹脂層によって遮断することができ、保香性フィルム層とガスバリア性樹脂層とを接着している接着剤の劣化を防止できる効果がある。
【００４９】
そのため、保香性フィルム層とガスバリア性樹脂層との間のデラミネーションの発生を回避でき、保香性フィルム層とガスバリア性樹脂層との界面に不規則な剥離領域や空隙が発生したり、陳列保管中や運搬中に、保香性フィルム層がガスバリア性樹脂層から完全に剥離するような現象を防止することができる。また本発明の芳香剤包装材料は、芳香剤用の包装材料に限定されることなく、気化性の消臭剤や防虫剤などを包装する包装材料としても利用展開が可能である。
【００５０】
また、たとえ保香性フィルム層とガスバリア性樹脂層との間でデラミネーションが発生して、保香性フィルム層とガスバリア性樹脂層との界面に不規則な剥離領域や空隙が発生したとしても、非保香性フィルム層側にはガスバリア性樹脂層が残るため、容器の保香機能にダメージを与えることなく、芳香剤の製品品質に対する悪影響を及ぼさない効果がある。
【００５１】
また、本発明の芳香剤包装材料は、エチレン−ビニルアルコール共重合体によるガスバリア性樹脂層と非保香性フィルム層との間にナイロン樹脂層を備えており、ガスバリア性樹脂層とナイロン樹脂層とにより材料のエッジ切れを防止する効果が付加されるものである。
【図面の簡単な説明】
【図１】本発明の芳香剤包装材料の実施の形態を説明する積層断面図。
【図２】（Ａ）は本発明の芳香剤包装材料を、トレー状容器の蓋材として使用した場合の斜視図、（Ｂ）はその側断面図。
【図３】（Ａ）は本発明の芳香剤包装材料を、カップ状容器の蓋材として使用した場合の斜視図、（Ｂ）はその側断面図。
【図４】本発明の芳香剤包装材料を、パウチ容器として使用した場合の一例を示す斜視図。
【図５】本発明の芳香剤包装材料を、パウチ容器として使用した場合の他の例を示す斜視図。
【符号の説明】
１…芳香剤包装材料２…印刷基材層３…保香性フィルム層
４１…ガスバリア性樹脂層４２…ナイロン樹脂層５…剥離性樹脂層
６…非保香性フィルム層
２０…蓋材２４…摘み部３０…容器３２…フランジ部
５０…蓋材５１…分包体６１…パウチ[0001]
[Industrial applications]
The present invention relates to a fragrance package that can be peeled off by peeling a peelable film from a package containing and packing a fragrance such as solid, granular, or liquid, leaving a gas-permeable film on the package side. The present invention relates to materials and lids for fragrance containers.
[0002]
[Prior art]
Conventionally, containers for packaging air fresheners include gas-barrier glass and plastic bottles, cups, trays, and other various shapes of containers such as air-permeable sheets made of paper or nonwoven fabric or resin. There is used a container containing an fragrance and the like, which is covered with an inner lid member made of a gas permeable sheet, heat-sealed and sealed with a gas-barrier sealing plastic cap at its opening.
[0003]
In addition, a plurality of small bags made by using a breathable sheet or film and packed with an air freshener are housed in a pouch made by using a gas barrier resin film and hermetically sealed and packaged with an air freshener. and so on.
[0004]
In recent years, in general, as a plastic container for packaging a fragrance, a sealing lid material (sheet) for hermetically sealing the opening of the container, or a packaging material used for a sealing pouch, the aroma evaporates out of the container. In consideration of long-term storage characteristics so that the fragrance does not deteriorate, a gas barrier aluminum foil or a polyethylene terephthalate film on which a metal oxide such as silicon oxide or aluminum oxide is deposited on the intermediate layer of the resin film packaging material. A gas-barrier composite laminated material laminated as a scent-retaining layer is used.
[0005]
This gas-barrier composite laminate material is frequently used for a lid material of a simple container particularly used in a state in which an fragrance is contained in a container, and a gas-barrier aluminum layer is provided on the surface layer of the lid material for fragrance retention. It is used as an easily peelable gas barrier composite laminate material applied as a layer.
[0006]
This easily peelable gas-barrier composite laminated material prevents fragrance from evaporating due to the fragrance retention property of the fragrance retention layer during storage before use, and when used, retains the fragrance on the surface of the container lid material. The non-scent-retaining film (sealant), which is a non-gas-barrier (breathable) residual lid material film of the laminated material, is left on the container opening side by peeling off the conductive film layer. The fragrance of the fragrance can be evaporated through the remaining non-scent-retaining film.
[0007]
[Problems to be solved by the invention]
By the way, the interlayer between the scent-retaining film layer and the non-scent-retentive film layer of the gas-barrier composite laminate material is laminated and adhered via an easily peelable adhesive so that it can be easily peeled off when used. As a result, the vapor of the fragrance in the container degrades the adhesive through the non-scent-retaining film, or delamination occurs between the scent-retaining film layer and the non-scent-retaining film layer, and Irregular peeling areas and voids are generated at the interface between the fragrance-preventing film layer and the non-perfume-preserving film layer of the material. There is a concern that the fragrance will be completely removed from the container, causing loss of fragrance and deterioration of the fragrance outside the container, damaging the storage function of the container and adversely affecting the product quality of the fragrance.
[0008]
The present invention suppresses delamination between the scent-retaining layer and the non-scent-retentive film layer, and even if delamination occurs, does not damage the storage function of the container, and does not affect the fragrance. The purpose is to have no adverse effect on product quality.
[0009]
[Means for Solving the Problems]
In the invention according to claim 1 of the present invention, the fragrance retaining film layer 3, the adhesive layer 4, the gas barrier resin layer 41, the peelable resin layer 5, and the non-fragrance retaining film layer 6 are laminated in this order. A fragrance packaging characterized in that the fragrance film layer 3, the adhesive layer 4, and the gas barrier resin layer 41 are laminated so as to be easily peelable from the non-fragrance retaining film layer 6 via the peelable resin layer 5. Material.
[0010]
The invention according to claim 2 of the present invention is the fragrance packaging material according to claim 1, wherein the gas barrier resin layer 41 is made of an ethylene-vinyl alcohol copolymer resin. is there.
[0011]
The invention according to claim 3 of the present invention is characterized in that in the fragrance packaging material according to claim 1 or 2, a nylon resin layer 42 is provided between the gas barrier resin layer 41 and the peelable resin layer 5. Fragrance packaging material.
[0012]
The invention according to claim 4 of the present invention is the fragrance packaging material according to any one of claims 1 to 3, wherein the non-scent-retaining film layer 6 is made of a linear low-density polyethylene resin. It is a fragrance packaging material characterized by the above-mentioned.
[0013]
The invention according to claim 5 of the present invention is characterized in that, in the fragrance packaging material according to any one of claims 1 to 3, the non-scent-retaining film layer 6 is made of a polypropylene resin. It is a fragrance packaging material.
[0014]
The invention according to claim 6 of the present invention is characterized in that, in the fragrance packaging material according to any one of claims 1 to 5, the peelable resin layer 5 is made of an easily cohesive peelable resin. Fragrance packaging material.
[0015]
The invention according to claim 7 of the present invention is the fragrance packaging material according to any one of claims 1 to 5, wherein the releasable resin layer 5 is disposed on the non-scent-retaining film layer 6. A fragrance packaging material characterized by being composed of an easily delaminated resin exhibiting easy delamination.
[0016]
The invention according to claim 8 of the present invention is the fragrance packaging material according to claim 4, wherein the releasable resin layer 5 has an interlayer between the non-scent-retaining film layer 6 made of the linear low-density polyethylene resin. A fragrance packaging material comprising a polypropylene resin exhibiting easy peelability.
[0017]
According to a ninth aspect of the present invention, in the fragrance packaging material according to the fifth aspect, the releasable resin layer 5 exhibits easy interlayer delamination with respect to the non-fragrance retaining film layer 6 made of the polypropylene resin. A fragrance packaging material comprising a linear low-density polyethylene resin.
[0018]
The invention according to claim 10 of the present invention provides the fragrance packaging material according to any one of claims 3 to 9, wherein the gas barrier resin layer 41, the nylon resin layer 42, and the peelable resin layer 5 have three layers. And a non-scented film layer 6 are laminated in this order by co-extrusion lamination.
[0019]
According to an eleventh aspect of the present invention, in the fragrance packaging material according to any one of the first to tenth aspects, a printing base material layer 2 is laminated on an outer surface of the fragrance retaining film layer 3. It is a fragrance packaging material characterized by the above-mentioned.
[0020]
According to a twelfth aspect of the present invention, there is provided a fragrance packaging material, wherein the fragrance packaging material according to any one of the first to eleventh aspects is used for a lid of a fragrance packaging container. It is.
[0021]
An invention according to claim 13 of the present invention is characterized in that the fragrance packaging material according to any one of claims 1 to 12 is used for all or a part of a fragrance packaging bag. It is a packaging material.
[0022]
BEST MODE FOR CARRYING OUT THE INVENTION
In the embodiment of the fragrance packaging material of the present invention, as shown in the laminated sectional view of FIG. 1, the fragrance retaining film layer 3, the adhesive layer 4, the gas barrier resin layer 41, the releasable resin layer 5, and the non- The scented film layer 6 (sealant layer) is laminated in this order, and the scented film layer 3 and the gas barrier resin layer 41 are bonded by the adhesive layer 4 to form the scented film. The layer 3, the gas-barrier resin layer 41, and the non-scent-retaining film layer 6 are easily peelable via the peelable resin layer 5.
[0023]
As the film used for the scent-retaining film layer 3, an aluminum foil having gas barrier properties or a metal oxide-deposited polyethylene terephthalate film obtained by depositing a metal oxide such as silicon oxide or aluminum oxide is used. As the resin layer 41, an ethylene-vinyl alcohol copolymer resin (EVOH) is used, and a nylon resin layer 42 (NY) is laminated between the gas barrier resin layer 41 and the peelable resin layer 5. .
[0024]
As the non-scent-retaining film layer 6, a linear low-density polyethylene resin (LLDPE) or a polypropylene resin (PP) is used.
[0025]
As the peelable resin layer 5, a cohesive easily peelable resin capable of easily tearing the inside of the resin layer 5 into two divided states against the cohesive force in the resin layer 5 can be used. .
[0026]
Further, as the releasable resin layer 5, an easily releasable interlayer resin having a weak adhesive strength to the non-scent-retaining film layer 6 and exhibiting easy releasability between layers may be used.
[0027]
For example, when a straight-chain low-density polyethylene resin is used for the non-scent-retaining film layer 6, a polypropylene resin exhibiting easy interlayer delamination is used for the releasable resin layer 5. When a polypropylene resin is used, a linear low-density polyethylene resin exhibiting easy interlayer delamination can be used as the releasable resin layer 5.
[0028]
In the fragrance packaging material of the present invention, the three layers of the gas barrier resin layer 41, the nylon resin layer 42, and the releasable resin layer 5 and the non-scent-retaining film layer 6 are coextruded into four types and four layers by a laminating machine. Then, it can be laminated in this order and laminated, and thereafter, a printing base is provided on the surface of the gas barrier resin layer 41 of the thus obtained laminated material via, for example, a urethane-based adhesive layer 4. It can be formed by laminating and laminating the material layer 2 and the fragrance retaining film layer 3 as an intermediate layer.
[0029]
On the outer surface of the fragrance retaining film layer 3 of the fragrance packaging material of the present invention, a printing substrate layer 2 such as a polyethylene terephthalate film or a single-sided art paper having a basis weight of about 85 g / m ² can be laminated. Appropriate information on the package contents of the container can be printed and displayed on the front or back side of the printing base material layer 2. When a polyethylene terephthalate film on which a metal oxide such as silicon oxide or aluminum oxide is deposited is used as the scent-retaining film layer, a beautiful print layer can be formed directly on the film.
[0030]
The use of the fragrance packaging material of the present invention, for example, can be used as a material for a lid material of a container for packaging fragrance, or for all or a part of bag making for making a fragrance packaging bag It can be used as a material.
[0031]
FIG. 2A is a perspective view when the fragrance packaging material of the present invention is used as a sealing lid 20 of a plastic tray-like container 30 containing fragrance, and FIG. 2B is a side sectional view thereof. FIG. 3A is a perspective view when the fragrance packaging material of the present invention is used as a sealing lid 20 of a plastic cup-shaped container 30 containing an fragrance, and FIG. It is a side sectional view.
[0032]
As shown in FIGS. 2 (A) and 2 (B), or FIGS. 3 (A) and 3 (B), the peripheral portion 22 of the lid 20 is attached to the flange portion 32 of the container 30 containing the fragrance. Sealed by heat-sealing with the film layer 6. For example, when the flange portion 32 of the container 30 is made of polyethylene resin, the non-scent-retaining film layer 6 of the fragrance packaging material (sealant layer) In the case where the lid member 20 having good heat sealing properties using a linear low-density polyethylene resin is used, and the flange portion 32 of the container 30 is made of polypropylene resin, the non-fragrance retaining property of the fragrance packaging material is used. A lid material 20 having good heat sealing properties using a polypropylene resin for the film layer 6 (sealant layer) is used.
[0033]
Then, for example, a knob portion 24 (a knob portion 24 protruding from the peripheral portion 22 as necessary) is provided in a part peripheral portion 22 of the lid member 20, and between the peripheral portion 22 and the knob portion 24, A cut line a for cutting the non-scented film layer 6 is provided.
[0034]
The fragrance in such a container 30 can be kept in a sealed state without the fragrance of the fragrance evaporating to the outside of the container by the fragrance retaining film layer 3 and the gas barrier resin layer 41 of the lid 20.
[0035]
When the fragrance in the container 30 is evaporated to the outside of the container and used, as shown in FIG. 2 (B) or FIG. 3 (B), the knob 24 of the lid member 20 is pinched and pulled up. With the breathable non-scented film layer 6 remaining on the container 30 side, the scented film layer 3, the gas barrier resin layer 41, and the nylon resin layer 42 can be peeled off and housed in the container 30. The fragrance of the fragrance can be evaporated to the outside through the non-scent-retaining film layer 6.
[0036]
FIG. 4 shows the use of the fragrance packaging material of the present invention as all or a part of a material for forming a pouch 61 made of a plastic film for hermetically packaging a tray-like container 30 containing fragrance from the outside. FIG. 5 is a perspective view of a pouch 61 made of a plastic film for hermetically packaging one or a plurality of packets 51 (small bags) containing a fragrance in the fragrance packaging material of the present invention. It is a perspective view at the time of using as all or some of materials for bag making.
[0037]
The tray-like container 30 containing the fragrance shown in FIG. 4 is one in which the peripheral portion 52 of the sheet-like lid member 51 is heat-sealed and packaged in the flange portion 32 thereof. 51 does not necessarily need to be made of plastic, may be made of only paper, and does not need to have gas barrier properties, nor does it need to be hermetically packaged.
[0038]
Also, the package 51 containing the fragrance shown in FIG. 5 does not necessarily need to be made of a plastic film, may be made of simple paper, and does not need to have a gas barrier property. It doesn't even have to be.
[0039]
In a pouch 61 made by using the fragrance packaging material of the present invention or a pouch 61 made by using the fragrance packaging material of the present invention in combination with another plastic film material having gas barrier properties, FIG. The container 30 or the package 51 containing the fragrance shown in FIG. 5 is loaded and hermetically sealed and packaged, so that the fragrance in the container 30 or the package 51 is retained on the lid 20 of the fragrance packaging material. The aromatic film layer 3 and the gas barrier resin layer 41, or the fragrance retaining film layer 3 and the gas barrier resin layer 41 of the lid member 20 of the fragrance packaging material of the present invention, and the other gas barrier plastic film material The sealed state can be maintained without evaporating the aroma of the agent to the outside of the container.
[0040]
When the fragrance in the container 30 or the package 51 shown in FIGS. 4 and 5 is evaporated to the outside of the container and used, the bag is formed with the fragrance packaging material of the present invention in the hermetically sealed pouch 61. By pulling and pulling up the end (or the knob, and the knob protruding from the end as necessary) of the portion thus formed, the air-permeable non-scent-retaining film layer 6 remains on the pouch 61 side. , The fragrance retaining film layer 3, the gas barrier resin layer 41, and the nylon resin layer 42 can be peeled off, and the fragrance of the fragrance in the container 30 or the package 51 housed in the pouch 61 can be removed from the non-fragrance retaining film. It can evaporate outward through the layer 6.
[0041]
In the case where the fragrance packaging material of the present invention and another plastic film material having gas barrier properties are used in combination for the bag making material of the pouch 61, the non-scent-retaining film layer 6 of the fragrance packaging material of the present invention is used. When a linear low-density polyethylene resin is used for the (sealant layer), a polyethylene resin is used for the sealant layer of another plastic film material having gas barrier properties, and the non-scent-retaining film of the fragrance packaging material of the present invention is used. When a polypropylene resin is used for the layer 6 (sealant layer), it is desirable to use a polypropylene resin for the sealant layer of another plastic film material having gas barrier properties.
[0042]
【Example】
Specific examples of the laminated structure of the fragrance packaging material of the present invention are shown below.
[0043]
(Laminated components)
(1) Printed substrate layer polyethylene terephthalate film: 12 μm
{Circle around (2)} An adhesive layer between the printing substrate layer and the scent-retaining (gas barrier) film layer Urethane-based adhesive (5 g / m ² )
(3) Fragrance-retaining (gas barrier) film layer aluminum foil (7 to 9 μm)
{Circle around (4)} Adhesive layer between fragrance retaining (gas barrier) film layer and EVOH layer Urethane adhesive (5 g / m ² )
{Circle around (5)} Coextruded laminated material EVOH (thickness 15 μm) / NY (thickness 15 μm) / urethane-based adhesive / cohesive easily peelable resin (polyethylene resin thickness 30 μm) / LLDPE (thickness 20 μm)
(6) Co-extruded laminated material EVOH (thickness 15 μm) / NY (thickness 15 μm) / urethane adhesive / PP (thickness 10 μm) / LLDPE (thickness 20 μm)
{Circle around (7)} Co-extruded laminated material EVOH (thickness 15 μm) / NY (thickness 15 μm) / urethane adhesive / cohesive easily peelable resin (PP thickness 30 μm) / PP (thickness 25 μm)
(8) Co-extruded laminated material EVOH (thickness 15 μm) / NY (thickness 15 μm) / urethane adhesive / LLDPE (thickness 10 μm) / PP (thickness 20 μm)
[0044]
<Example 1>
(1) / (2) / (3) / (4) / (5)
[0045]
<Example 2>
(1) / (2) / (3) / (4) / (6)
[0046]
<Example 3>
(1) / (2) / (3) / (4) / (7)
[0047]
<Example 4>
(1) / (2) / (3) / (4) / (8)
[0048]
【The invention's effect】
The fragrance packaging material of the present invention is obtained by laminating a fragrance retaining film layer, an adhesive layer, a gas barrier resin layer, a peelable resin layer, and a non-fragrance retaining film layer in this order, and forming a fragrance retaining film layer and an adhesive. In which a layer and a gas barrier resin layer are laminated so as to be easily peelable from the non-scent-retentive film layer via the releasable resin layer, and are transferred in the direction of the adhesive layer through the non-scent-retentive film layer. Gas barrier properties between the adhesive layer that adheres the fragrance-retaining film layer and the non-fragrance-repelling film layer to the fragrance vapor that evaporates from the solid, granular, or jelly-like fragrance It can be blocked by the resin layer, and has the effect of preventing deterioration of the adhesive bonding the fragrance retaining film layer and the gas barrier resin layer.
[0049]
Therefore, the occurrence of delamination between the fragrance retaining film layer and the gas barrier resin layer can be avoided, and an irregular peeling region or void is generated at the interface between the fragrance retaining film layer and the gas barrier resin layer, It is possible to prevent a phenomenon in which the fragrance retaining film layer is completely separated from the gas barrier resin layer during display storage or transportation. Further, the fragrance packaging material of the present invention is not limited to packaging materials for fragrances, but can also be used and developed as packaging materials for packaging volatile deodorants and insect repellents.
[0050]
Further, even if delamination occurs between the fragrance retaining film layer and the gas barrier resin layer, an irregular peeling region or void occurs at the interface between the fragrance retaining film layer and the gas barrier resin layer. Since the gas-barrier resin layer remains on the non-fragrance-retaining film layer side, there is an effect that the fragrance does not adversely affect the product quality without damaging the fragrance retention function of the container.
[0051]
Further, the fragrance packaging material of the present invention includes a nylon resin layer between the gas barrier resin layer of the ethylene-vinyl alcohol copolymer and the non-scent-retaining film layer, and the gas barrier resin layer and the nylon resin layer. Thus, the effect of preventing the edge of the material from being cut is added.
[Brief description of the drawings]
FIG. 1 is a laminated sectional view illustrating an embodiment of a fragrance packaging material of the present invention.
FIG. 2A is a perspective view when the fragrance packaging material of the present invention is used as a lid for a tray-like container, and FIG. 2B is a side sectional view thereof.
FIG. 3A is a perspective view when the fragrance packaging material of the present invention is used as a lid of a cup-shaped container, and FIG. 3B is a side sectional view thereof.
FIG. 4 is a perspective view showing an example when the fragrance packaging material of the present invention is used as a pouch container.
FIG. 5 is a perspective view showing another example when the fragrance packaging material of the present invention is used as a pouch container.
[Explanation of symbols]
DESCRIPTION OF SYMBOLS 1 ... Fragrance packaging material 2 ... Printing base material layer 3 ... Flavor retaining film layer 41 ... Gas barrier resin layer 42 ... Nylon resin layer 5 ... Releasable resin layer 6 ... Non-fragrance retaining film layer 20 ... Lid material 24 ... Knob part 30 ... Container 32 ... Flange part 50 ... Lid material 51 ... Packing body 61 ... Pouch

Claims

Laminating a fragrance retaining film layer, an adhesive layer, a gas barrier resin layer, a peelable resin layer, and a non-fragrance retaining film layer in this order, a fragrance retaining film layer, an adhesive layer, and a gas barrier resin layer, A fragrance packaging material, wherein the fragrance packaging material is laminated so as to be easily peelable from the non-scent-retaining film layer via the peelable resin layer.

The fragrance packaging material according to claim 1, wherein the gas barrier resin layer is made of an ethylene-vinyl alcohol copolymer resin.

The fragrance packaging material according to claim 1 or 2, further comprising a nylon resin layer between the gas barrier resin layer and the peelable resin layer.

The fragrance packaging material according to any one of claims 1 to 3, wherein the non-scent-retaining film layer comprises a linear low-density polyethylene resin.

The fragrance packaging material according to any one of claims 1 to 3, wherein the non-scent-retaining film layer is made of a polypropylene resin.

The fragrance packaging material according to any one of claims 1 to 5, wherein the peelable resin layer is made of a cohesive easily peelable resin.

The fragrance packaging material according to any one of claims 1 to 5, wherein the releasable resin layer is made of an easily delaminated resin exhibiting an easily delaminated property with respect to the non-fragrance retaining film layer. A fragrance packaging material.

5. The fragrance packaging material according to claim 4, wherein the releasable resin layer is made of a polypropylene resin exhibiting easy interlayer delamination with respect to the non-scent-retaining film layer made of the linear low-density polyethylene resin. Air freshener packaging material.

The fragrance packaging material according to claim 5, wherein the releasable resin layer (5) is made of a straight-chain low-density polyethylene resin exhibiting easy delamination with respect to the non-scent-retaining film layer (6) made of the polypropylene resin. Fragrance packaging material.

The fragrance packaging material according to any one of claims 3 to 9, wherein the three layers of the gas barrier resin layer, the nylon resin layer, and the peelable resin layer, and the non-scent-retaining film layer are co-extruded and laminated. A fragrance packaging material which is laminated in this order.

The fragrance packaging material according to any one of claims 1 to 10, wherein a printing base material layer is laminated on an outer surface of the fragrance retaining film layer.

A fragrance packaging material, wherein the fragrance packaging material according to any one of claims 1 to 11 is used for a lid of a fragrance packaging container.

A fragrance packaging material, wherein the fragrance packaging material according to any one of claims 1 to 12 is used for all or a part of a fragrance packaging bag.