Abstract

PROBLEM TO BE SOLVED: To provide a safe artificial nail which does not give rise to side effects, such as peeling of a sell nail or inflammation or the skin, and a method of forming the same. SOLUTION: The artificial nail 20 is formed by superposing thin silk fabrics of >=2 sheets, solidifying the silk fabrics by using, for example, a thermoplastic resin which matches well with the silk material, then cutting the fabrics to nail shapes of various sizes and individually molding the same by application of heat and pressure. The artificial nail formed in the manner described above is bonded to the self nail 1 from the root (right above the cuticle) so as to cover the entire part of the self nail 1 and thereafter the shapes of both sides are trimmed to conform with the self nail 1 and the artificial nail is finished by further trimming the front end to a desired length.

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a safe artificial nail which does not cause side effects such as peeling of a self nail and sore skin, and a method for forming the artificial nail.

[0002]

2. Description of the Related Art In recent years, a technique called nail art for adhering an artificial nail to a self nail for decoration has become popular.
Since it takes a long time of one and a half to two hours and it is impossible to move the fingertip almost fixedly during that time, it is impossible to perform it on your own, and the treatment is done at a specialty store. It was done. Since this does not require administrative permission, anyone could easily open the business under the name "Nail Salon", for example, as long as equipment such as materials, tools and medicines were prepared.

4 to 7 are views showing an example of such a conventional nail art treatment method. First, Fig. 4 (a)
As shown in FIG. 2, the adhesive 3 is applied to the tip of the customer's own nail 1 about 2 to 3 mm by using the small brush 2, and a semi-transparent resin artificial material called nail tip is applied on the adhesive 3. The rear end of the nail base piece 4 is bonded as shown in FIG.

If this step is left as it is, a step is formed between the own nail 1 and the base piece 4 of the artificial nail.
And a finishing file 5-2 are attached to each other to scrape off, and as shown in FIG. 2 (c), the entire surface of the base consisting of the own nail 1 and the artificial nail base piece 4 is made flat.

Next, as shown in FIG. 5, an undercoat liquid 6, an auxiliary agent 7, a pH (pH) adjusting liquid 8 and the like are used with an appropriate brush or brush so that the surface of the whole base is not uneven. Apply evenly to the bottom to prepare the base.

Then, for example, a solvent 9 called a liquid consisting of a solution of acrylic short-formers as shown in FIG. 6 (a) is applied to a brush-like brush 10 as shown in FIG. 6 (b). When the plastic powder 11 as shown in Fig. 7 (c) is attached to the tip and sucked up, the gel-like body 1 shown in Fig. 7 (a) in which the solvent 9 and the plastic powder 11 are completely integrated
2 is formed on the tip of the brush 10.

The gel-like material 12 is applied to the surface of the whole base consisting of the self-made nail 1 and the artificial nail base piece 4 which are prepared as described above.
Apply as shown in (a). This application is performed twice, so that the gel-like body 12 is double-applied.

After the curing agent is sprayed and the composition is hardened and dried by a hot air dryer, the surface is polished by a rotary file 13 as shown in FIG. 2 (b), and as shown in FIG. 2 (c). Make it smooth.

After that, the nails were fashionably enjoyed by applying ordinary manicure or writing a colorful pattern with a special quick-drying paint.

[0010]

However, among the customers who have been treated at the nail salon as described above, there are severe allergic side effects such as peeling of one's own nails from the fingertips and sore skin around the fingers. Happened frequently. Although the cause has not been medically confirmed, it has been revealed that allergies are caused by the various solutions shown in FIG. 5 and the solvent 9 and the plastic powder 11 shown in FIG. 6, particularly the plastic powder 11.

This side effect is so severe that it takes almost a year and a half to treat the patient until it is completely cured. As a result, the customer's feet have withdrawn and the nail salon has declined all at once. However,
There is a strong demand for women's revival of nail art, and the advent of safe artificial nails without side effects and a method of forming them is still desired.

The object of the present invention is to solve the above-mentioned conventional problems.
(EN) It is intended to provide a safe artificial nail that does not cause side effects such as peeling of the own nail and scratching of the skin, and a method for forming the same.

[0013]

First, the method for forming an artificial nail of the present invention according to claim 1 comprises the step of adhering an artificial nail base piece to a natural nail, and an entire surface of a base consisting of the natural nail and the artificial nail base piece. A step of adhering a silk cloth to the base material, a step of shaping the shape of the adhered silk cloth according to a base, a step of top-coating the surface of the silk cloth, and a step of polishing the surface of the top-coated silk cloth. Composed of.

The artificial nail base piece is adhered to the tip of the own nail as described in claim 2 for example, and is adhered from the root of the own nail as described in claim 3, for example. In addition, the silk cloth is, for example, as described in claim 4,
A plurality of sheets are laminated and adhered on the entire surface of the base.

Next, an artificial nail according to a fifth aspect of the present invention is formed by hardening a plurality of laminated silk fabrics with a resin liquid to form a nail shape.

[0016]

BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below with reference to the drawings. 1 (a), (b) and 2 (a),
(b) is a figure explaining the formation method of the safety artificial nail in a 1st embodiment. First, as shown in Fig. 1 (a),
It is the same as before until the artificial nail base piece 4 made of resin is adhered to the customer's own nail 1 to finish the whole flat (see FIGS. 4 (a), (b) and (c)). In this adhesion of the artificial nail base piece 4, safety is guaranteed by using a surgical adhesive that is used instead of suturing a wound after surgery or is used when directly attaching a wig to the head. Preferably.

After that, as shown in FIG. 1 (a), an appropriate amount of a resin adhesive 14 suitable for silk fabric, which will be described later, is applied to almost the central portion of the entire base consisting of the own nail 1 and the artificial nail base piece 4. Place it. Then, as shown in FIG. 2B, two pieces of silk cloth 15 of an appropriate size prepared in advance are cut into the shape of the large frame of the base (1, 4) by using the clip 16, and the cut first A piece of silk cloth 15 is placed on the base (1, 4) so that the end of the silk cloth 15 is in contact with the cuticle of the base of the finger, and a wooden or bamboo spatula is used to form the base (1, 4). The adhesive 14 between the silk cloths 15 is squeezed and spread out to bring the silk cloths 15 into close contact with the bases (1, 4).

Since only one piece is thin, the second piece of silk cloth 15
In the same manner as above, the adhesive 14 and the spatula are used to overlap and adhere to the first sheet. After that, the whole shape is adjusted as shown in FIG. 2 (a), and the silk-only resin liquid 18 is overcoated with a brush 17 and dried.

For the silk cloth 15, for example, a glossy silk fabric after scouring of a dense plain weave is used. The silk fabric after scouring is
It has a natural luster with good quality, and since it is densely struck, it does not look like cloth and forms a very good nail surface. As shown in Figure (b), the surface is lightly polished with a flexible rotary file 19 to finish, and the gloss of silk is further enhanced through the solidified resin liquid 18 of the top coat, and a beautiful artificial nail is created. .

Since silk is a natural protein, it is well adapted to human skin, and with a few exceptions, it is a safe material without the risk of causing allergies. Further, the artificial nail forming method described above is extremely safe because it does not use a solution having a strong action for preparation or a plastic powder that causes allergies after wearing.

In the above example, the artificial nail base piece 4 is adhered to the tip of the own nail 1. However, the invention is not limited to this. The nail 1 may be adhered so as to cover the whole, and in that case, the work of removing the step between the self-nails and the artificial nail base piece adhering portion and the smoothing work thereafter are not required, and the work is simplified. .

Alternatively, the artificial nail base piece may not be used as described above, and the artificial nail made of silk cloth may be directly adhered to the own nail. FIG. 3 is a diagram showing a second embodiment in which an artificial nail made of silk cloth is directly bonded to the own nail. The artificial nail 20 shown in the same figure is obtained by stacking two or more thin silk cloths, hardening them with a resin that is well compatible with silk cloth, for example, using a thermoplastic resin, and then cutting them into nails of various sizes. It is created by applying heat and pressure to.

After adhering this from the root of the self-nail 1 (immediately above the cuticle) so as to cover the whole self-nail 1, the shape of both sides is adjusted according to the self-nail 1 and the tip is further adjusted to a desired length. It is completed and prepared.

Also in this case, only silk and silk-specific resin, and silk-specific adhesive such as adhesives are used, and no solution such as a preparatory solution or plastic powder that causes allergies after wearing is used. Since it is not used, it is possible to enjoy wearing the artificial nail in an extremely safe state without the risk of causing problems such as peeling of the own nail or sore of the skin due to allergy.

[0025]

As described in detail above, according to the present invention, a silk cloth that is well adapted to human skin is used as a material for an artificial nail, and a solution having a strong action for preparation and a plastic powder that causes allergies after wearing. Since you do not use any of the above, you can enjoy the fashionable feeling by wearing artificial nails in an extremely safe state without the risk of causing problems such as peeling of your own nails or sore skin due to allergies.

[Brief description of drawings]

1A and 1B are views (Nos. 1 and 2) illustrating a method for forming a safe artificial nail according to the first embodiment.

2A and 2B are views (No. 3 and No. 4) for explaining the method for forming a safe artificial nail according to the first embodiment.

FIG. 3 is a diagram in which an artificial nail made of silk cloth according to the second embodiment is directly adhered to the own nail.

4 (a), (b), and (c) are diagrams showing a process of making a first foundation of a conventional nail art.

FIG. 5 is a view showing various chemical agents for undercoating of conventional nail art.

6 (a), (b) and (c) are diagrams for explaining a surface material of a conventional nail art.

7 (a), (b) and (c) are diagrams for explaining formation and finishing of the surface of a conventional nail art.

[Explanation of symbols]

1 own nail 2 small brush 3 adhesive 4 artificial nail base pieces 5 rasp 5-1 Arato 5-2 Finishing grind 6 Undercoat liquid 7 auxiliaries 8 pH adjustment liquid 9 solvent 10 brushes 11 plastic powder 12 Gel 14 Adhesive 15 silk cloth 16 sandwiches 17 small brush 18 Resin liquid 20 artificial nails

Claims (5)

[Claims] 1. A step of adhering an artificial nail base piece to a self nail, a step of adhering a silk cloth to the entire surface of a base consisting of the self nail and the artificial nail base piece, and the shape of the adhered silk cloth is adjusted to the base. A method for forming an artificial nail, comprising: a step of shaping, a step of top-coating the surface of the silk cloth, and a step of polishing the surface of the silk cloth that has been top-coated. 2. The method for forming an artificial nail according to claim 1, wherein the artificial nail base piece is bonded to a tip portion of the own nail. 3. The method for forming an artificial nail according to claim 1, wherein the artificial nail base piece is bonded from the root of the own nail. 4. The method for forming an artificial nail according to claim 1, wherein a plurality of the silk cloths are laminated and bonded to the entire surface of the base. 5. An artificial nail, characterized in that a plurality of silk fabrics are laminated with a resin solution and molded into a nail shape.