JP2003071154A - Sheet-form blade member, and its manufacturing method - Google Patents
Sheet-form blade member, and its manufacturing methodInfo
- Publication number
- JP2003071154A JP2003071154A JP2001263511A JP2001263511A JP2003071154A JP 2003071154 A JP2003071154 A JP 2003071154A JP 2001263511 A JP2001263511 A JP 2001263511A JP 2001263511 A JP2001263511 A JP 2001263511A JP 2003071154 A JP2003071154 A JP 2003071154A
- Authority
- JP
- Japan
- Prior art keywords
- ions
- alloy
- blade member
- solution
- thin plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、電気かみそり用外
刃等の薄板状刃物部材、及びその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a thin plate member such as an outer blade for an electric shaver, and a method for manufacturing the same.
【0002】[0002]
【従来の技術】電気かみそり用外刃としては、純Ni、
Ni合金の電鋳材からなるものや、マルテンサイト系ス
テンレス鋼の圧延薄板をプレス打ち抜き加工したものが
従来から知られている。例えば、特公昭59−3554
号公報には、電鋳法によって形成したNi−Co−P合
金外刃が開示されている。また、特開平9−38349
号公報及び特公昭58−8860号公報には、プレス打
ち抜き法で形成したステンレス鋼外刃が開示されてい
る。2. Description of the Related Art As an outer blade for an electric shaver, pure Ni,
BACKGROUND ART Conventionally, a material made of an Ni alloy electroformed material and a material obtained by press punching a rolled thin plate of martensitic stainless steel have been known. For example, Japanese Examined Patent Publication Sho 59-3554
The publication discloses a Ni-Co-P alloy outer blade formed by an electroforming method. Also, Japanese Patent Laid-Open No. 9-38349
Japanese Patent Publication No. 58-88860 and Japanese Patent Publication No. 58-8860 disclose a stainless steel outer blade formed by a press punching method.
【0003】[0003]
【発明が解決しようとする課題】しかしながら、純Ni
やNi合金の電鋳材、ステンレス鋼等からなる上記従来
の電気かみそり用外刃は、いずれもHv500〜600
程度で、表面硬度が十分でないため、摩耗進行度合いが
大きくて、良好な切れ味を長時間保つことができず、ま
た、強度不足で、折れや破れが発生しやすい等の問題が
あった。また、純NiやNi合金の電鋳材の場合は、N
iアレルギーの問題もあった。[Problems to be Solved by the Invention] However, pure Ni
The above-mentioned conventional outer blades for electric razors made of electroformed material of Ni, Ni alloy, stainless steel, etc. are all Hv500-600.
However, since the surface hardness is not sufficient, there is a problem that the degree of progress of wear is large and good sharpness cannot be maintained for a long period of time, and the strength is insufficient and breakage or breakage easily occurs. In the case of pure Ni or Ni alloy electroformed material, N
There was also a problem of i allergy.
【0004】一方、硬度の高い電鋳材としては、Ni−
W合金の電鋳材も知られているが、電気かみそり用外刃
をNi−W合金電鋳材で形成すると、やはりNiアレル
ギーの問題が発生する。On the other hand, as an electroformed material having high hardness, Ni-
Although a W alloy electroformed material is also known, if the outer blade for an electric razor is made of a Ni—W alloy electroformed material, the problem of Ni allergy still occurs.
【0005】本発明は、加工性が良く、高い硬度および
強度が得られ、かつ、Niアレルギーの恐れのない電気
かみそり用外刃等の薄板状刃物部材を得ることを目的と
する。An object of the present invention is to obtain a thin plate-like blade member such as an outer blade for an electric shaver which has good workability, high hardness and strength, and is free from the risk of Ni allergy.
【0006】[0006]
【課題を解決するための手段】本発明は、前記課題を解
決するため、Co(コバルト)−W(タングステン)合
金の電鋳材からなり、ビッカース硬度(Hv)で700
以上の硬度を有することを特徴とする、電気かみそり用
外刃等の薄板状刃物部材を提供するものである。In order to solve the above problems, the present invention comprises an electroformed material of Co (cobalt) -W (tungsten) alloy and has a Vickers hardness (Hv) of 700.
A thin plate-shaped blade member such as an outer blade for an electric razor having the above hardness.
【0007】この薄板状刃物部材は、CoイオンとWイ
オンの総和が0.1〜0.3モル/リットルで、全金属
イオンに対するCoイオンの含有率が20〜40%の範
囲にある組成の電界液を用いて、40〜80℃で電鋳
し、得られた電鋳材を、500〜700℃で焼鈍するこ
とにより製造することができる。This thin plate member has a composition in which the total amount of Co ions and W ions is 0.1 to 0.3 mol / liter, and the content ratio of Co ions to all metal ions is in the range of 20 to 40%. It can be manufactured by electroforming at 40 to 80 ° C. using an electrolytic solution and annealing the obtained electroformed material at 500 to 700 ° C.
【0008】電気かみそり用外刃等の薄い刃物部材をC
o−W合金の電鋳材で形成することは、従来、均一な電
解折出を得ることが困難で、実現不可能であるとされて
きたが、本発明者は、研究の結果、CoイオンとWイオ
ンの総和が0.1〜0.3モル/リットルで、全金属イ
オンに対するCoイオンの含有率が20〜40%の範囲
にある組成の電界液を用いて、40〜80℃で電鋳した
場合に、電気かみそり用外刃等に使用可能な薄板状刃物
部材とするための均一な電鋳が可能であることが判明し
た。A thin blade member such as an outer blade for an electric razor is C
The formation of an o-W alloy electroformed material has heretofore been considered to be impossible because it is difficult to obtain a uniform electrolytic protrusion, but as a result of research, the present inventors have found that Co ion And the total amount of W ions are 0.1 to 0.3 mol / liter, and the content of Co ions to the total metal ions is in the range of 20 to 40%. It has been found that, when cast, uniform electroforming is possible to obtain a thin plate-shaped blade member that can be used as an outer blade for an electric razor.
【0009】こうして得られたCo−W合金電鋳材から
なる刃物部材は、そのままでは硬度が低く、加工性に優
れている。そして、焼鈍することによって、高い硬度お
よび強度が得られ、Hv800以上の硬度とすることも
可能で、そのため、摩耗進行度合いが小さくて長時間良
好な切れ味を保つことができるとともに、折れや破れが
発生しにくいものとすることができる。勿論、Niアレ
ルギーの問題も生じない。The blade member made of the Co-W alloy electroformed material thus obtained has a low hardness as it is and is excellent in workability. Then, by annealing, a high hardness and strength can be obtained, and a hardness of Hv 800 or more can be obtained. Therefore, the degree of progress of wear is small and good sharpness can be maintained for a long time, and breakage or breakage is also possible. It can be hard to occur. Of course, the problem of Ni allergy does not occur.
【0010】[0010]
【発明の実施の形態】本発明の実施の形態の一例として
の電気かみそり用外刃及びその製造方法を次に説明す
る。BEST MODE FOR CARRYING OUT THE INVENTION An outer blade for an electric shaver and a method for manufacturing the same will be described below as an example of an embodiment of the present invention.
【0011】この例では、CoイオンとWイオンの総和
が0.1〜0.3モル/リットルで、全金属イオンに対
するCoイオンの含有率が20〜40%の範囲にある組
成の水溶液中に、金属錯化剤としてクエン酸イオンとア
ンモニウムイオンを添加した電解水溶液を用いて、40
〜80℃で電解折出させることにより、厚さ50μmの
均一な厚さのCo−W合金電鋳材を得た。In this example, the total amount of Co ions and W ions is 0.1 to 0.3 mol / liter, and the content of Co ions to the total metal ions is in the range of 20 to 40%. , Using an electrolytic aqueous solution to which citrate ion and ammonium ion are added as a metal complexing agent,
By electrolysis at 80 ° C, a Co-W alloy electroformed material with a uniform thickness of 50 µm was obtained.
【0012】こうして得られたCo−W合金電鋳材は、
常温で硬度が低く、加工性に優れたものであるため、必
要に応じて打ち抜き加工等の加工を施すことができる。The Co-W alloy electroformed material thus obtained is
Since it has low hardness at room temperature and excellent workability, it can be subjected to punching or the like as necessary.
【0013】そして、このCo−W合金電鋳材電鋳材
を、500〜700℃で焼鈍することにより、硬度が高
く、強度の大きい外刃が得られる。Then, this Co--W alloy electroformed material is annealed at 500 to 700 ° C. to obtain an outer blade having high hardness and high strength.
【0014】図1は、前記条件によるCo−W合金電鋳
材を異なる温度で焼鈍し、その硬度を測定した結果を示
している。このデータが示すように、焼鈍温度が500
〜700℃の範囲では、従来の純NiやNi合金の電鋳
材、ステンレス鋼等からなる電気かみそり用外刃の場合
(Hv500〜600程度)以上の硬度(強度)が得ら
れ、特に、焼鈍温度600℃の場合に、Hv800以上
の高い硬度(強度)が得られた。FIG. 1 shows the results of measuring the hardness of a Co--W alloy electroformed material under the above conditions, which was annealed at different temperatures. As the data show, annealing temperatures of 500
In the range of up to 700 ° C, a hardness (strength) higher than that of a conventional outer blade for an electric shaver (Hv500 to 600) made of pure Ni or Ni alloy electroformed material, stainless steel or the like can be obtained. When the temperature was 600 ° C., a high hardness (strength) of Hv 800 or higher was obtained.
【0015】以上、電気かみそり用外刃の例を説明した
が、本発明は、他の薄板状刃物部材にも適用することが
できる。Although the example of the outer blade for the electric shaver has been described above, the present invention can be applied to other thin plate-shaped blade members.
【0016】[0016]
【発明の効果】以上の説明から明らかなように、本発明
によれば、Co−W合金電鋳材からなり、加工性が良好
で、焼鈍により高い硬度および強度が得られ、Niアレ
ルギーの恐れもない電気かみそり用外刃等の薄板状刃物
部材を得ることができる。As is apparent from the above description, according to the present invention, it is made of a Co-W alloy electroformed material, has good workability, can obtain high hardness and strength by annealing, and is susceptible to Ni allergy. It is possible to obtain a thin plate-like blade member such as an outer blade for an electric razor.
【図1】本発明の実施の形態の一例におけるCo−W合
金電鋳材を異なる温度で焼鈍し、その硬度を測定した結
果を示すグラフである。FIG. 1 is a graph showing the results of measuring the hardness of a Co—W alloy electroformed material according to an example of an embodiment of the present invention, which is annealed at different temperatures.
Claims (3)
ース硬度で700以上の硬度を有することを特徴とする
薄板状刃物部材。1. A thin plate-like blade member made of a Co-W alloy electroformed material and having a Vickers hardness of 700 or more.
の薄板状刃物部材。2. A thin plate blade member according to claim 1, which is an outer blade for an electric shaver.
0.3モル/リットルで、全金属イオンに対するCoイ
オンの含有率が20〜40%の範囲にある組成の電解液
を用いて、40〜80℃で電鋳し、得られた電鋳材を、
500〜700℃で焼鈍することを特徴とする薄板状刃
物部材の製造方法。3. The total sum of Co ions and W ions is 0.1 to 10.
An electroformed material obtained by electroforming at 40 to 80 ° C. using an electrolytic solution having a composition of 0.3 mol / liter and having a Co ion content relative to all metal ions in the range of 20 to 40%. ,
A method for manufacturing a thin plate-shaped blade member, which comprises annealing at 500 to 700 ° C.