JP2002322572A - Method and apparatus for suppressing uneven appearance of steel sheet - Google Patents
Method and apparatus for suppressing uneven appearance of steel sheetInfo
- Publication number
- JP2002322572A JP2002322572A JP2001123905A JP2001123905A JP2002322572A JP 2002322572 A JP2002322572 A JP 2002322572A JP 2001123905 A JP2001123905 A JP 2001123905A JP 2001123905 A JP2001123905 A JP 2001123905A JP 2002322572 A JP2002322572 A JP 2002322572A
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- roll
- amount
- shift
- warpage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、亜鉛メッキ鋼板製
造ラインにおいて、ケミカル処理セクションで発生する
外観むらを抑制する方法及びその装置に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method and an apparatus for suppressing uneven appearance occurring in a chemical treatment section in a galvanized steel sheet manufacturing line.
【０００２】[0002]
【従来の技術】従来から、亜鉛めっき鋼板製造ラインに
おいて、亜鉛めっき後のクロメートを付着する工程、い
わゆるケミカルセクションでクロメートの付着量がばら
つくと鋼板の外観むらが発生するとの問題があった。こ
の外観むらの要因の一つとして図１（ｃ）に示したよう
に鋼板の幅方向に反りが発生すると、付着したクロメー
ト液の付着量を制御する工程（図ではエアナイフ工程）
でエアが図のように幅方向に流れ、鋼板の凹面では、セ
ンタ部にクロメート液が集中し、エッジ部では拡散して
しまい、反対側の凸面では、逆の現象が発生し、これに
よってクロメート液の付着量にばらつきが発生してい
る。これをを防止するため、シフトロールを使用し、外
観むらの原因である幅方向の鋼板反り量を抑制しようと
してきた。従来は、鋼板サイズや材質に応じて、手動で
押込量を設定することにより、鋼板の反りを矯正してい
た。2. Description of the Related Art Conventionally, in a galvanized steel sheet production line, there has been a problem in that the variation in the amount of chromate deposited in a step of depositing chromate after galvanization, that is, in a so-called chemical section, causes uneven appearance of the steel sheet. As one of the factors of the appearance unevenness, when the warp occurs in the width direction of the steel sheet as shown in FIG. 1C, a step of controlling the amount of the attached chromate liquid (an air knife step in the figure).
As shown in the figure, air flows in the width direction as shown in the figure, and on the concave surface of the steel plate, the chromate liquid concentrates at the center, and diffuses at the edge, and the opposite phenomenon occurs on the convex surface on the opposite side. Fluctuations in the amount of liquid adhered. To prevent this, shift rolls have been used to suppress the amount of steel sheet warpage in the width direction, which is a cause of uneven appearance. Conventionally, the warpage of the steel sheet has been corrected by manually setting the indentation amount according to the steel sheet size and material.
【０００３】[0003]
【発明が解決しようとする課題】しかしこの方法のみで
は、ライン通板時において避けられない、鋼板張力変動
や原板形状変動等の操業条件の変動により発生する幅方
向鋼板反り量の変化に十分対応することができなかっ
た。また、手動でシフトロールの押込量を変更するた
め、変更のタイミングがずれたり、或いは変更し忘れと
いう問題が発生し、特に鋼板のロットが変わる時点での
外観むらが多くなっていた。However, this method alone can sufficiently cope with a change in the warp amount in the width direction of the steel sheet caused by a change in operating conditions such as a change in the steel sheet tension and a change in the shape of the original sheet, which cannot be avoided during line passing. I couldn't. Further, since the pushing amount of the shift roll is manually changed, a problem occurs in which the timing of the change is shifted or the change is forgotten, and the appearance unevenness particularly at the time of changing the steel sheet lot has increased.
【０００４】更に、本発明者らが調査したところ、クロ
メート液付着量調整後の鋼板の乾燥時において、特にク
ロメート液付着量が多い条件では乾燥するまでの時間が
長くなり、乾燥が完了するまでにクロメート液が垂れて
鋼板外観むらの原因となっているケースもあった。Further, the inventors of the present invention have investigated that when the steel sheet is dried after the adjustment of the amount of chromate liquid attached, especially when the amount of chromate liquid adhered is large, the time until the drying becomes longer, and until the drying is completed. In some cases, the chromate solution dripped, causing unevenness in the appearance of the steel sheet.
【０００５】従って、鋼板の外観むらを抑制するために
は、ケミカル処理セクションでの幅方向鋼板反りに起因
して、鋼板凹部へのクロメート液集中により発生する鋼
板外観むらを抑制するため、シフトロールの鋼板への押
込量を常に最適位置に維持する必要がある。また、更に
は、乾燥むら防止のため、クロメート液付着量調整後
に、短時間で鋼板表面を乾燥させる必要があることに着
目した。本発明は、鋼板反り矯正用ロールを用いて幅方
向反り量を制御し、または、高温かつ短時間で鋼板を乾
燥させることにより、鋼板外観むらの発生を抑制するこ
とを課題とする。Accordingly, in order to suppress the unevenness of the appearance of the steel sheet, it is necessary to use a shift roll to suppress the unevenness of the appearance of the steel sheet caused by the concentration of the chromate liquid in the recess of the steel sheet due to the warpage of the steel sheet in the width direction in the chemical treatment section. It is necessary to always maintain the pushing amount into the steel plate at the optimum position. Furthermore, in order to prevent uneven drying, the inventors focused on the fact that it is necessary to dry the surface of the steel sheet in a short time after adjusting the amount of the attached chromate solution. An object of the present invention is to control the amount of warpage in the width direction using a roll for correcting warpage of a steel sheet or to dry the steel sheet at a high temperature and in a short time to suppress the occurrence of unevenness in the appearance of the steel sheet.
【０００６】[0006]
【課題を解決するための手段】本発明は、上記目的を達
成するものであり、その趣旨は、下記である。 （１）亜鉛めっき鋼板製造ラインのケミカル処理セクシ
ョンにおいて、鋼板の幅方向反り量を検知し、当該反り
量に応じて、デフレクターロールとパスラインロールと
の中間位置で、且つ、当該鋼板を挟んで反対側に設置さ
れたシフトロールを前記両ロール側に鋼板を押し込む際
の押し込み量を自動制御することを特徴とする鋼板の外
観むらの抑制方法。 （２）前記鋼板の幅方向反り量を鋼板の幅方向に１個あ
るいは複数の変位計により求めることを特徴とする
（１）記載の鋼板外観むらの抑制方法。 （３）前記ケミカル処理セクションにおけるクロメート
液の付着量を制御するエアナイフ工程の後、熱風による
鋼板乾燥炉において、鋼板温度５５℃までの昇温速度を
２３℃/sec以上とすることを特徴とする（１）又は
（２）記載の鋼板外観むらの抑制方法。 （４）亜鉛めっき鋼板を水平方向から垂直方向に搬送方
向を変化させるデフレクターロールと、前記デフレクタ
ーロールの上に鋼板のパスラインを調整するパスライン
ロールと、前記デフレクターロールとパスラインロール
との間に前記両ロールと鋼板を挟んで反対側に鋼板方向
に移動可能なシフトロールを設置し、且つ、鋼板の幅反
り量を検知する検知手段を設け、当該検知手段からのデ
ータにより前記シフトロールの押し込み量を求めその値
により前記シフトロールの移動量を制御するシフトロー
ル押し込み量制御装置とを備えたことを特徴とする鋼板
の外観むらの抑制装置。 （５）前記装置に更に、クロメート液を乾燥する乾燥工
程における乾燥炉に鋼板温度の昇温速度及び鋼板温度を
制御する機能を有した乾燥温度制御装置を設けたことを
特徴とする（４）記載の鋼板の外観むらの抑制装置。 本発明は、鋼板の幅方向反りによる、幅方向へのクロメ
ート液流れが原因で発生する鋼板外観むらを抑制するた
め、鋼板の反り量を検知し、その反り量に応じて、シフ
トロールの鋼板への最適押し込み量を求め、その値に従
ってシフトロールを鋼板に対して押込むことにより、鋼
板の反りを抑制し、かつクロム付着量調整後の鋼板乾燥
時に、昇温速度を一定以上の値にして高温短時間で行う
ことにより、鋼板外観むらの発生を抑制するものであ
る。The present invention achieves the above-mentioned object, and has the following effects. (1) In the chemical treatment section of the galvanized steel sheet production line, the amount of warpage in the width direction of the steel sheet is detected, and in accordance with the amount of warpage, at an intermediate position between the deflector roll and the pass line roll and across the steel sheet. A method for suppressing uneven appearance of a steel sheet, comprising automatically controlling a pushing amount of a shift roll installed on opposite sides when the steel sheet is pushed into both roll sides. (2) The method for suppressing unevenness in appearance of a steel sheet according to (1), wherein the amount of warpage in the width direction of the steel sheet is obtained in the width direction of the steel sheet by one or a plurality of displacement meters. (3) After the air knife step of controlling the amount of chromate liquid adhering in the chemical treatment section, in a steel sheet drying furnace using hot air, a heating rate up to a steel sheet temperature of 55 ° C. is 23 ° C./sec or more. (1) The method for suppressing unevenness in appearance of a steel sheet according to (2). (4) A deflector roll for changing the conveying direction of the galvanized steel sheet from a horizontal direction to a vertical direction, a pass line roll for adjusting a pass line of the steel sheet on the deflector roll, and between the deflector roll and the pass line roll. A shift roll capable of moving in the direction of the steel sheet is provided on the opposite side of the both rolls and the steel sheet, and a detecting means for detecting a width warpage amount of the steel sheet is provided, and the shift roll of the shift roll is provided by data from the detecting means. A shift roll push-in amount control device that obtains a push-in amount and controls a shift amount of the shift roll according to the value. (5) The apparatus further comprises a drying temperature control device having a function of controlling a temperature rising rate of the steel sheet temperature and the steel sheet temperature in a drying furnace in a drying step of drying the chromate liquid. (4) An apparatus for suppressing uneven appearance of a steel sheet as described in the above. The present invention detects the amount of warpage of a steel sheet to suppress unevenness in the appearance of the steel sheet caused by the flow of chromate liquid in the width direction due to the warp in the width direction of the steel sheet, and according to the amount of warp, the steel sheet of the shift roll. Calculate the optimal indentation amount into the steel sheet, and press the shift roll against the steel sheet according to the value to suppress the warpage of the steel sheet, and set the heating rate to a certain value or more when drying the steel sheet after adjusting the chromium adhesion amount. By performing the process at high temperature for a short time, the occurrence of unevenness in the appearance of the steel sheet is suppressed.
【０００７】[0007]
【発明の実施の形態】以下、図によって詳細に説明す
る。図１（ａ）は本発明を適用したラインの一実施例を
説明する図である。めっきを施された鋼板１は、デフレ
クターロール２によって水平方向から垂直方向に搬送方
向を変え垂直に立ち上がり、その上には、鋼板のパスラ
インを制御するパスラインロール４がある。そして、デ
フレクターロール２とパスラインロール４との間には、
鋼板１をはさんでシフトロール３が設置されている。図
１（ａ）の例では、２個であるが、もちろん１個でも良
い。シフトロール３は、水平方向に移動可能な構造とな
っており、鋼板をデフレクターロール２及びパスライン
ロール４に対し押し付け可能で、且つ、その押し付け量
も調整できるようになっている。それらロール群の上に
はめっき鋼板表面にクロメート液を付着するためのクロ
メート液スプレー装置５が設けてある。そして、その上
に付着したクロメート液の付着量を調整するためのエア
ナイフ６が設置されている。この調整装置としては、必
ずしもエアナイフでなくても本発明の効果に影響はな
い。BRIEF DESCRIPTION OF THE DRAWINGS FIG. FIG. 1A is a diagram illustrating an embodiment of a line to which the present invention is applied. The plated steel sheet 1 changes its transport direction from a horizontal direction to a vertical direction by a deflector roll 2 and rises vertically, and there is a pass line roll 4 for controlling a pass line of the steel sheet. And, between the deflector roll 2 and the pass line roll 4,
A shift roll 3 is provided with a steel plate 1 interposed therebetween. In the example of FIG. 1A, the number is two, but of course one may be used. The shift roll 3 has a structure capable of moving in the horizontal direction, is capable of pressing a steel plate against the deflector roll 2 and the pass line roll 4, and is capable of adjusting the pressing amount. A chromate liquid spray device 5 for attaching a chromate liquid to the surface of the plated steel sheet is provided on the roll group. An air knife 6 for adjusting the amount of chromate liquid adhering thereon is provided. Even if the adjusting device is not necessarily an air knife, the effect of the present invention is not affected.
【０００８】エアナイフ６の上には、本発明で使用する
鋼板の幅方向の反り量を検知するための検知手段、図で
は変位計１０が設置されている。この変位計の設置方法
は、多種考えられるが、例えば、鋼板の幅方向に、セン
ターに１個、両エッジ部に各１個、計３個設置し、その
変位差から鋼板の幅方向の反り量を求める方法や、ある
いは１個の変位計が鋼板の幅方向に移動可能な構造と
し、１個でセンタ及び両エッジ部の変位をそれぞれ測定
し、両者から反り量を求めることもできる。更には、セ
ンタ部に１個の変位計を設置し、例えば両エッジは、パ
スロールの位置にあると仮定し、センタ部の変位のみか
ら鋼板の反り量を検知する方法も可能である。いずれに
しても要求される鋼板むら防止の精度などに応じて変位
計の設置方法を決めれば良い。また、変位計設置位置も
エアナイフ６の上に限定されるものではなく、設置設備
スペースなどから決めても良い。図１の例では、（ｂ）
に示す如く変位計１０は幅方向に可動式で３台配置し、
出力値偏差により、亜鉛メッキ鋼板１の反り量を検出す
る方式を示している。On the air knife 6, a detecting means for detecting the amount of warpage in the width direction of the steel plate used in the present invention, in the figure, a displacement gauge 10 is provided. There are various possible methods for installing this displacement meter. For example, three pieces of one piece are installed at the center and one piece at each of both edges in the width direction of the steel sheet. It is also possible to determine the amount or warp amount from both by measuring the displacement of the center and both edge portions by using a single displacement gauge that is movable in the width direction of the steel plate. Further, a method is also possible in which one displacement meter is installed at the center, and for example, both edges are assumed to be at the position of the pass roll, and the amount of warpage of the steel sheet is detected only from the displacement of the center. In any case, the method of installing the displacement meter may be determined according to the required accuracy of preventing unevenness of the steel sheet. Further, the displacement meter installation position is not limited to the position above the air knife 6, and may be determined from the installation facility space or the like. In the example of FIG. 1, (b)
As shown in the figure, three displacement meters 10 are arranged in a movable manner in the width direction,
A method of detecting the amount of warpage of the galvanized steel sheet 1 based on the output value deviation is shown.
【０００９】そして、変位計１０から送られた変位デー
タはシフトロール押し込み制御装置１１に送られ、鋼板
の反り量を求め、更に反り量から最適なシフトロール押
し込み量を求めて、その値をシフトロール３に伝達す
る。伝達された押し込み量に従ってシフトロール３は鋼
板１を押し込む。The displacement data sent from the displacement meter 10 is sent to the shift roll push-in control device 11, which calculates the amount of warpage of the steel sheet, further calculates the optimum shift roll push-in amount from the warp amount, and shifts the value. Transfer to Roll 3. The shift roll 3 pushes the steel plate 1 in accordance with the transmitted pushing amount.
【００１０】変位計１０の上には、乾燥炉７があり、鋼
板に吹きつけられたクロメート液を乾燥する。乾燥炉７
は、例えば炉温の制御領域が前段と後段との２領域に分
かれており、昇温速度の制御可能で、かつ乾燥炉出側の
鋼板温度を一定範囲に管理可能としている。A drying furnace 7 is provided above the displacement meter 10 for drying the chromate solution sprayed on the steel plate. Drying oven 7
For example, the furnace temperature control region is divided into two regions, a former stage and a latter stage, so that the heating rate can be controlled, and the temperature of the steel sheet on the exit side of the drying furnace can be managed within a certain range.
【００１１】[0011]
【実施例】次に、本発明の具体的実施例について説明す
る。鋼板反り矯正用ロール押込量と幅方向鋼板反り量と
の関係についての調査結果を図２に示す。図示する如
く、下段及び上段のシフトロールの押込量を最適化する
ことにより、幅方向の鋼板反りを矯正できることがわか
る。Next, specific examples of the present invention will be described. FIG. 2 shows the results of an investigation on the relationship between the roll pushing amount for correcting the steel sheet warpage and the warpage amount in the width direction steel sheet. As shown in the drawing, it can be understood that the steel sheet warpage in the width direction can be corrected by optimizing the pushing amounts of the lower and upper shift rolls.
【００１２】鋼板外観むら評点と幅方向鋼板反り量との
関係についての調査結果を図３に示す。この時、乾燥炉
での鋼板昇温速度は１５℃/sec一定の条件で行った。鋼
板外観むら評点が４以下であれば、実質的に問題のない
範囲であり、幅方向鋼板反り量が５mm以内であれば、外
観むら評点が良好であることがわかる。従って、鋼板の
反り量は、５mm以下に制御する必要がある。FIG. 3 shows the results of an investigation on the relationship between the evaluation score of the appearance unevenness of the steel sheet and the amount of warpage in the width direction steel sheet. At this time, the heating rate of the steel sheet in the drying furnace was kept constant at 15 ° C./sec. When the score of the unevenness of the steel sheet is 4 or less, it is in a range where there is substantially no problem. When the warpage of the steel sheet in the width direction is 5 mm or less, the score of the unevenness of the steel sheet is good. Therefore, it is necessary to control the warpage of the steel sheet to 5 mm or less.
【００１３】鋼板反り量を変化させた場合の、幅方向ク
ロム付着量の分布を図４に示す。この時、狙いのクロム
付着量は全ての条件で３０mg/m2 とし、同等条件で実施
した。鋼板反り量が大きい程、クロム付着量のばらつき
も大きくなっていることがわかり、これが鋼板外観むら
の一因となっている。反り量５mm以下ではクロム付着量
がほぼ均一となっているのがわかる。FIG. 4 shows the distribution of the chromium adhesion amount in the width direction when the warpage amount of the steel sheet is changed. At this time, the target chromium deposition amount was 30 mg / m 2 under all conditions, and the same conditions were used. It can be seen that the greater the amount of warpage of the steel sheet, the greater the variation in the amount of chromium attached, which contributes to the unevenness of the appearance of the steel sheet. It can be seen that when the warpage is 5 mm or less, the amount of deposited chromium is substantially uniform.
【００１４】鋼板乾燥時において、鋼板外観むら評点と
鋼板温度が５５℃まで上昇する間の昇温速度との関係に
ついての調査結果を図５に示す。この時、幅方向鋼板反
り量は、±５mm以内の条件範囲とした。鋼板昇温速度が
２３℃/sec以上の条件で、外観むら評点が良好であるこ
とがわかる。FIG. 5 shows the results of an investigation on the relationship between the evaluation score of the unevenness of the steel sheet appearance and the rate of temperature increase while the steel sheet temperature rises to 55 ° C. when the steel sheet is dried. At this time, the warp amount in the width direction steel sheet was set within a condition range of ± 5 mm or less. It can be seen that under the condition that the temperature of the steel sheet is 23 ° C./sec or more, the score of the uneven appearance is good.
【００１５】[0015]
【発明の効果】以上説明したように、本発明により、鋼
板反り矯正用ロールを用いて幅方向鋼板反り量を一定範
囲内に制御することにより、幅方向クロム付着量ばらつ
きが低減され、かつ乾燥炉においては昇温速度を制御し
て、短時間で鋼板を乾燥させることにより乾燥むらを防
止でき、鋼板外観むらの発生を抑制できる。As described above, according to the present invention, by controlling the amount of warpage in the width direction of the steel sheet within a certain range by using the roll for correcting the warpage of the steel sheet, the variation in the amount of chromium adhering in the width direction is reduced, and drying is performed. In the furnace, by controlling the rate of temperature rise and drying the steel sheet in a short time, uneven drying can be prevented, and the occurrence of unevenness in the appearance of the steel sheet can be suppressed.
【図１】本発明の一実施例の全体構成図である。FIG. 1 is an overall configuration diagram of an embodiment of the present invention.
【図２】幅方向鋼板反り量と鋼板反り矯正用ロールの鋼
板への押込量との関係を示したグラフである。FIG. 2 is a graph showing a relationship between a width-direction steel sheet warpage amount and a pressing amount of a steel sheet warpage correcting roll into a steel sheet.
【図３】鋼板外観むら評点と幅方向鋼板反り量との関係
を示したグラフである。FIG. 3 is a graph showing a relationship between a steel sheet appearance unevenness rating and a width direction steel sheet warpage amount.
【図４】幅方向鋼板反り量による、幅方向クロム付着量
分布への影響を示したグラフである。FIG. 4 is a graph showing the influence on the chromium deposition amount distribution in the width direction by the warpage amount of the width direction steel sheet.
【図５】鋼板外観むら評点と乾燥時における鋼板昇温速
度との関係を示したグラフである。FIG. 5 is a graph showing a relationship between a score of unevenness in appearance of a steel sheet and a heating rate of the steel sheet during drying.
１ 亜鉛メッキ鋼板 ２ デフレクターロール ３ シフトロール（上段が＃１，下段が＃２） ４ パスラインロール ５ クロメート液スプレー装置 ６ エアナイフ ７ 乾燥炉 ８ クロメート液流れの向き ９ 亜鉛メッキ鋼板とエアナイフとの間の距離の差
異 １０ 変位計 １１ シフトロール押し込み量制御装置DESCRIPTION OF SYMBOLS 1 Galvanized steel plate 2 Deflector roll 3 Shift roll (upper stage is # 1, lower stage is # 2) 4 Pass line roll 5 Chromate liquid spray device 6 Air knife 7 Drying furnace 8 Chromate liquid flow direction 9 Between galvanized steel plate and air knife Difference in distance 10 Displacement meter 11 Shift roll pushing amount control device
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｇ０１Ｂ 21/20 Ｇ０１Ｂ 21/20 Ａ Ｇ (72)発明者 浜口 勝洋 千葉県君津市君津１番地 新日本製鐵株式 会社君津製鐵所内 (72)発明者 森川 謙太 千葉県君津市君津１番地 新日本製鐵株式 会社君津製鐵所内 Ｆターム(参考） 2F069 AA61 BB19 GG04 GG58 HH09 JJ19 PP06 4K026 AA07 AA12 AA13 AA22 BA06 BB10 DA06 DA07 DA09 DA10 DA11 DA16 EB11 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification FI FI Theme Court ゛ (Reference) G01B 21/20 G01B 21/20 AG (72) Inventor Katsuhiro Hamaguchi 1 Kimitsu, Kimitsu-shi, Chiba Prefecture New Japan-made (72) Inventor Kenta Morikawa No. 1 Kimitsu, Kimitsu-shi, Chiba F-term (reference) 2N0 Nippon Steel Corporation Kimitsu Works (Reference) BB10 DA06 DA07 DA09 DA10 DA11 DA16 EB11
Claims (5)
理セクションにおいて、鋼板の幅方向反り量を検知し、
当該反り量に応じて、デフレクターロールとパスライン
ロールとの中間位置で、且つ、当該鋼板を挟んで反対側
に設置されたシフトロールを前記両ロール側に鋼板を押
し込む際の押し込み量を自動制御することを特徴とする
鋼板の外観むらの抑制方法。In a chemical treatment section of a galvanized steel sheet manufacturing line, a width direction warpage of a steel sheet is detected,
According to the amount of warpage, a shift roll installed at an intermediate position between the deflector roll and the pass line roll, and a shift roll installed on the opposite side of the steel plate is automatically controlled when the steel plate is pushed into the two rolls. A method for suppressing uneven appearance of a steel sheet, characterized in that:
に１個あるいは複数の変位計により求めることを特徴と
する請求項１記載の鋼板外観むらの抑制方法。2. The method according to claim 1, wherein the amount of warpage in the width direction of the steel sheet is determined in the width direction of the steel sheet using one or a plurality of displacement gauges.
ロメート液の付着量を制御するエアナイフ工程の後、熱
風による鋼板乾燥炉において、鋼板温度５５℃までの昇
温速度を２３℃/sec以上とすることを特徴とする請求項
１又は２記載の鋼板外観むらの抑制方法。3. The method according to claim 1, wherein after the air knife step of controlling the amount of chromate liquid adhering in the chemical treatment section, in a steel sheet drying furnace using hot air, a heating rate up to a steel sheet temperature of 55 ° C. is 23 ° C./sec or more. The method for suppressing appearance unevenness of a steel sheet according to claim 1 or 2.
に搬送方向を変化させるデフレクターロールと、前記デ
フレクターロールの上に鋼板のパスラインを調整するパ
スラインロールと、前記デフレクターロールとパスライ
ンロールとの間に前記両ロールと鋼板を挟んで反対側に
鋼板方向に移動可能なシフトロールを設置し、且つ、鋼
板の幅反り量を検知する検知手段を設け、当該検知手段
からのデータにより前記シフトロールの押し込み量を求
めその値により前記シフトロールの移動量を制御するシ
フトロール押し込み量制御装置とを備えたことを特徴と
する鋼板の外観むらの抑制装置。4. A deflector roll for changing a conveying direction of a galvanized steel sheet from a horizontal direction to a vertical direction, a pass line roll for adjusting a pass line of the steel sheet on the deflector roll, and the deflector roll and the pass line roll. A shift roll capable of moving in the direction of the steel sheet is installed on the opposite side of the both rolls and the steel sheet in between, and a detecting means for detecting the width warpage amount of the steel sheet is provided, and the shift is performed based on data from the detecting means. A shift roll pushing amount control device that obtains the roll pushing amount and controls the shift roll moving amount based on the value.
る乾燥工程における乾燥炉に鋼板温度の昇温速度及び鋼
板温度を制御する機能を有した乾燥温度制御装置を設け
たことを特徴とする請求項４記載の鋼板の外観むらの抑
制装置。5. The apparatus according to claim 1, further comprising a drying temperature control device having a function of controlling a heating rate of a steel sheet temperature and a steel sheet temperature in a drying furnace in a drying step of drying the chromate liquid. Item 4. An apparatus for suppressing uneven appearance of a steel sheet according to Item 4.