JP2002154865A - Cemented chip board and cemented chip laminate board - Google Patents
Cemented chip board and cemented chip laminate boardInfo
- Publication number
- JP2002154865A JP2002154865A JP2000346900A JP2000346900A JP2002154865A JP 2002154865 A JP2002154865 A JP 2002154865A JP 2000346900 A JP2000346900 A JP 2000346900A JP 2000346900 A JP2000346900 A JP 2000346900A JP 2002154865 A JP2002154865 A JP 2002154865A
- Authority
- JP
- Japan
- Prior art keywords
- cement
- wood
- wood chip
- wood chips
- fine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、外壁などの建築材
料として用いられる木片セメント板および木片セメント
積層板に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wood chip cement board and a wood chip cement laminate used as a building material for an outer wall or the like.
【０００２】[0002]
【従来の技術】従来、木片セメント板や木片セメント積
層板は、防火性や耐水性に優れていることから、主に建
物の外壁などに用いられている。2. Description of the Related Art Conventionally, wood chip cement boards and wood chip cement laminate boards have been mainly used for the outer walls of buildings because of their excellent fire resistance and water resistance.
【０００３】このうち、木片セメント板は、例えば、ポ
ルトランドセメントを主成分とするセメント組成物と木
片と水とを混合した後、これらの混合物を成形型に供給
し、加圧加熱することにより所定の形状に賦形し、硬化
させて製造されている。[0003] Among them, a wood chip cement board is prepared, for example, by mixing a wood chip and water with a cement composition mainly composed of Portland cement, supplying the mixture to a molding die and heating under pressure. It is manufactured by shaping into a shape and curing.
【０００４】このような木片セメント板や、木片セメン
ト積層板は、木片とセメントを主成分とするため、寸法
安定性に劣り、乾燥収縮によって反りを起こしやすいと
いう欠点がある。寸法安定性は、木片の含有量を減らす
ことで改善することができるが、木片の含有量を減らす
ことによって強度の低下を引き起こす。このため、木片
の含有量を増加させずに強度を向上させることができる
ように、表面に多数の切り起こしを形成した木片を含有
させることが提案されている（例えば、特開平８−２９
５７号公報参照）。[0004] Such a wood chip cement board or a wood chip cement laminate board has a drawback that it is inferior in dimensional stability and easily warps due to drying shrinkage because it mainly contains wood chips and cement. Dimensional stability can be improved by reducing the content of wood chips, but reducing the content of wood chips causes a decrease in strength. For this reason, it has been proposed to include a piece of wood with a large number of cut and raised portions on the surface so that the strength can be improved without increasing the content of the piece of wood (for example, see Japanese Patent Application Laid-Open No. 8-29).
No. 57).
【０００５】[0005]
【発明が解決しようとする課題】しかしながら、表面に
切り起こしを形成した木片を含有させたとしても、得ら
れた木片セメント板あるいは木片セメント積層板を建物
の外壁などに用いる場合、十分な強度を確保するために
は、木片の含有量を大幅に減少させることはできず、寸
法安定性は十分なものとはいえなかった。However, even if wood chips having cut-and-raised surfaces are contained, when the obtained wood chip cement board or wood chip cement laminate is used for the outer wall of a building, sufficient strength is required. In order to secure it, the content of wood chips could not be significantly reduced, and the dimensional stability was not sufficient.
【０００６】本発明は、このような問題点に鑑みてなさ
れたものであり、寸法安定性、強度に優れた木片セメン
ト板および木片セメント積層板を提供するものである。[0006] The present invention has been made in view of such problems, and provides a wood chip cement board and a wood chip cement laminate excellent in dimensional stability and strength.
【０００７】[0007]
【課題を解決するための手段】請求項１記載の発明は、
セメントおよび微細木片を主成分とする木片セメント板
であって、前記微細木片は、平均断面積０．０１〜０．
３ｍｍ2 で平均アスペクト比８以上の繊維状木片であ
り、木片セメント板中に５〜１５重量％含有されている
ことを特徴とするものである。According to the first aspect of the present invention,
A wood chip cement board mainly composed of cement and fine wood chips, wherein the fine wood chips have an average cross-sectional area of 0.01 to 0.1 mm.
It is a fibrous wood piece having an average aspect ratio of 8 or more at 3 mm 2 , and is characterized by being contained in a wood chip cement board in an amount of 5 to 15% by weight.
【０００８】請求項２記載の発明は、基材層の裏面に補
強層が積層された木片セメント積層板であって、前記基
材層は、セメント、木片および軽量骨材を主成分とする
比重０．９〜１．３の組成物からなり、補強層は、厚み
が０．５〜１０ｍｍで、セメント、微細木片および平均
粒径２００μｍ以下の微細骨材を主成分とする比重１．
４〜１．８の組成物からなり、前記微細木片は、補強層
中に５〜１５重量％含有されていることを特徴とするも
のである。According to a second aspect of the present invention, there is provided a wood chip cement laminate in which a reinforcing layer is laminated on the back surface of a base material layer, wherein the base material layer has a specific gravity mainly composed of cement, wood chips and lightweight aggregate. The reinforcing layer is composed of a composition of 0.9 to 1.3, and the reinforcing layer has a thickness of 0.5 to 10 mm, specific gravity of which is mainly composed of cement, fine wood chips and fine aggregate having an average particle diameter of 200 µm or less.
4 to 1.8, wherein the fine wood chips are contained in the reinforcing layer in an amount of 5 to 15% by weight.
【０００９】請求項１記載の発明において、木片セメン
ト板に使用されるセメントは、通常、普通ポルトランド
セメント、早強ポルトランドセメントなどのポルトラン
ドセメントを主成分とするものが好ましく用いられる。In the first aspect of the present invention, as the cement used for the wood chip cement board, a cement mainly containing Portland cement, such as ordinary Portland cement or early-strength Portland cement, is preferably used.
【００１０】成形工程にホットプレスなどの加熱硬化を
行う易合には、硬化時間を短縮できるので、ポルトラン
ドセメントに熱硬化成分を添加することが好ましい。[0010] It is preferable to add a thermosetting component to Portland cement, since the curing time can be shortened if the molding step is easily performed by heat curing such as hot pressing.
【００１１】前記熱硬化成分としては、例えば、アルミ
ナセメント、無水石膏および半水石膏から選ばれる原料
が単独または２種以上混合状態にて主成分として使用可
能である。ポルトランドセメントとこれら成分から、エ
トリンガイト（３ＣａＯ・Ａｌ2 Ｏ3 ・３ＣａＳＯ4 ・
３２Ｈ2 Ｏ）が生成してセメントを硬化させる。As the thermosetting component, for example, a raw material selected from alumina cement, anhydrous gypsum and gypsum hemihydrate can be used as a main component alone or in a mixture of two or more. From Portland cement and these components, ettringite (3CaO.Al 2 O 3 .3CaSO 4.
32H 2 O) is formed to harden the cement.
【００１２】前記セメントには、セメントの一部に代え
て、珪砂、珪石粉、フライアッシュ、珪ソウ土、マイ
カ、シリカヒュームなどの充填材や、必要に応じてパー
ライト、シラスバルーン、フライアッシュバルーン、太
平洋セメント社製の商品名「Ｅ−スフィアーズ」、ガラ
スバルーンなどの無機軽量骨材、スチレンビーズ、ポリ
エチレンビーズなどの有機軽量骨材を添加してもよい。The cement may include a filler such as quartz sand, quartzite powder, fly ash, silica sand, mica, silica fume, etc., and, if necessary, pearlite, shirasu balloon, fly ash balloon in place of part of the cement. And an inorganic lightweight aggregate such as glass balloons and the like, and organic lightweight aggregates such as styrene beads and polyethylene beads may be added.
【００１３】請求項１記載の発明において、木片セメン
ト板に使用される微細木片としては、新木材および建築
廃木材などから作製された木チップを細分化した木片が
使用でき、例えば、杉、檜、松、栂、さわら、樫、な
ら、かば、ブナ、オーク、ラワン、ひば、栗、けやき、
椎、柳、竹などの材料からなるものが使用される。According to the first aspect of the present invention, as the fine wood chip used for the wood chip cement board, there can be used a wood chip obtained by subdividing a wood chip made from new wood or construction waste wood. , Pine, toga, straw, oak, nara, birch, beech, oak, lauan, hiba, chestnut, zelkova,
Materials made of materials such as shii, willow and bamboo are used.
【００１４】微細木片を作製する方法としては、木チッ
プを、例えば、リング型ハンマーミル（パールマン社
製）で切削し、次いで、ディスクカッターミル（ホーラ
イ社製「ＨＴ−３００型」）で微粉砕することで得るこ
とができる。As a method for producing fine wood chips, wood chips are cut, for example, with a ring-type hammer mill (manufactured by Pearlman), and then finely pulverized with a disk cutter mill (“HT-300” manufactured by Horai). Can be obtained.
【００１５】前記微細木片の形状は、平均断面積０．０
１〜０．３ｍｍ2 で平均アスペクト比８以上の繊維状木
片に限定される。このような繊維状木片を使用すること
で、補強効果が増大し、少ない添加量でも高い強度を得
ることができる。[0015] The shape of the fine wood piece has an average sectional area of 0.0
It is limited to fibrous wood chips having an average aspect ratio of 8 or more at 1 to 0.3 mm 2 . By using such a fibrous wood piece, the reinforcing effect is increased, and high strength can be obtained even with a small amount of addition.
【００１６】前記繊維状木片の平均断面積が０．３ｍｍ
2 を超えると、同じ重量部で添加できる木片本数が減少
し、補強効果が減少し、強度が低下する。平均断面積が
０．０１ｍｍ2 よりも小さくなるような繊維状木片の切
削は既存の切削機では困難である。また、繊維状木片の
平均アスペクト比が８よりも小さくなると、補強効果が
減少し、高い強度が得られない。平均アスペクト比の上
限は、特に限定されないが、切削長さは切削機の能力に
より決定され、また、混合時の繊維状木片が凝集しない
範囲に限定される。The average cross-sectional area of the fibrous wood piece is 0.3 mm
If it exceeds 2 , the number of wood pieces that can be added in the same part by weight decreases, the reinforcing effect decreases, and the strength decreases. Cutting of a fibrous wood piece having an average cross-sectional area smaller than 0.01 mm 2 is difficult with an existing cutting machine. On the other hand, when the average aspect ratio of the fibrous piece of wood is smaller than 8, the reinforcing effect is reduced and high strength cannot be obtained. The upper limit of the average aspect ratio is not particularly limited, but the cutting length is determined by the capacity of the cutting machine, and is limited to a range in which the fibrous wood chips during mixing do not aggregate.
【００１７】請求項１記載の発明において、平均断面積
０．０１〜０．３ｍｍ2 で平均アスペクト比８以上の繊
維状木片は、木片セメント板中に５〜１５重量％含有さ
れることが好ましい。In the first aspect of the present invention, the fibrous wood chips having an average cross-sectional area of 0.01 to 0.3 mm 2 and an average aspect ratio of 8 or more are preferably contained in the wood chip cement board in an amount of 5 to 15% by weight. .
【００１８】前記繊維状木片が５重量％未満の場合に
は、補強効果が得られず、強度不足となるとともに、比
重が大きくなり、木片セメント板の重量が大きくなるお
それがある。また、繊維状木片が１５重量％を超える
と、木片の乾燥収縮、吸水膨張によって寸法安定性が低
下するとともに、防火性能が劣るなどの問題が生じる。When the amount of the fibrous wood pieces is less than 5% by weight, the reinforcing effect cannot be obtained, the strength becomes insufficient, the specific gravity increases, and the weight of the wood cement board may increase. On the other hand, when the fibrous wood piece exceeds 15% by weight, problems such as deterioration of dimensional stability due to drying shrinkage of the wood piece and swelling due to water absorption, and inferior fire prevention performance arise.
【００１９】請求項１記載の発明において、水の添加量
は、セメント１００重量部に対し、３０〜７０重量部で
あることが好ましい。In the first aspect of the present invention, the amount of water added is preferably 30 to 70 parts by weight based on 100 parts by weight of cement.
【００２０】前記水が３０重量部未満の場合には、セメ
ントの水和反応が不十分となり、強度低下を引き起こ
す。また、水が７０重量部を超えると、混合時におい
て、小さな固まりができて均一に混合ができなくなり、
成形された木片セメント板が不均質で強度がでなくな
る。If the amount of water is less than 30 parts by weight, the hydration reaction of the cement becomes insufficient and the strength is reduced. Further, if the water exceeds 70 parts by weight, small agglomerates are formed at the time of mixing, and uniform mixing cannot be performed.
The molded wood cement board is inhomogeneous and loses its strength.
【００２１】請求項１記載の発明において、木片セメン
ト板の製造方法としては、セメント組成物、繊維状木片
および水の混合物を型枠上に散布落下させ、ホットプレ
スにより所定時間加圧加熱して硬化させた後、脱型する
ことにより得ることができる。According to the first aspect of the present invention, as a method for manufacturing a wood chip cement board, a mixture of a cement composition, a fibrous wood chip and water is sprayed and dropped on a mold, and is heated under pressure for a predetermined time by a hot press. After curing, it can be obtained by demolding.
【００２２】混合物の調製は、公知な方法で行われ、例
えば、オムニミキサー、ヘンシェルミキサーなどを使用
して行うことができる。The preparation of the mixture is performed by a known method, for example, using an omni mixer, a Henschel mixer, or the like.
【００２３】請求項１記載の発明によれば、平均断面積
０．０１〜０．３ｍｍ2 で平均アスペクト比８以上の繊
維状木片は、繊維状で、かつ単位重量当たりの表面積が
大きいため、セメント中に添加、分散させた場合、セメ
ントとの接触面積が増大するために、補強効率が高くな
り、少ない添加量でも高い強度を得ることができる。そ
して、木片の添加量を少なくすることで、寸法安定性に
優れたものとなる。According to the first aspect of the present invention, a fibrous wood piece having an average sectional area of 0.01 to 0.3 mm 2 and an average aspect ratio of 8 or more is fibrous and has a large surface area per unit weight. When added and dispersed in the cement, the contact area with the cement increases, so that the reinforcing efficiency increases and high strength can be obtained even with a small amount of addition. By reducing the amount of wood chips added, the dimensional stability becomes excellent.
【００２４】請求項２記載の発明において、木片セメン
ト積層板に使用されるセメントは、通常、普通ポルトラ
ンドセメント、早強ポルトランドセメントなどのポルト
ランドセメントを主成分とするものが好ましく用いられ
る。In the second aspect of the present invention, as the cement used for the wood chip cement laminate, a cement mainly containing Portland cement such as ordinary Portland cement or early-strength Portland cement is preferably used.
【００２５】成形工程にホットプレスなどの加熱硬化を
行う易合には、硬化時間を短縮できるので、ポルトラン
ドセメントに熱硬化成分を添加することが好ましい。[0025] If the curing process is easily performed by hot pressing or the like in the molding step, the curing time can be shortened. Therefore, it is preferable to add a thermosetting component to Portland cement.
【００２６】前記熱硬化成分としては、例えば、アルミ
ナセメント、無水石膏および半水石膏から選ばれる原料
が単独または２種以上混合状態にて主成分として使用可
能である。ポルトランドセメントとこれら成分から、エ
トリンガイト（３ＣａＯ・Ａｌ2 Ｏ3 ・３ＣａＳＯ4 ・
３２Ｈ2 Ｏ）が生成してセメントを硬化させる。As the thermosetting component, for example, a raw material selected from alumina cement, anhydrous gypsum and gypsum hemihydrate can be used as a main component alone or in a mixture of two or more. From Portland cement and these components, ettringite (3CaO.Al 2 O 3 .3CaSO 4.
32H 2 O) is formed to harden the cement.
【００２７】前記セメントには、セメントの一部に代え
て、珪砂、珪石粉、フライアッシュ、珪ソウ土、マイ
カ、シリカヒュームなどの充填材を添加してもよい。A filler such as silica sand, silica powder, fly ash, diatomaceous earth, mica, and silica fume may be added to the cement instead of a part of the cement.
【００２８】請求項２記載の発明において、木片セメン
ト積層板の基材層に使用される木片としては、新木材お
よび建築廃木材などから作製された木チップを細分化し
た木片が使用でき、例えば、杉、檜、松、栂、さわら、
樫、なら、かば、ブナ、オーク、ラワン、ひば、栗、け
やき、椎、柳、竹などの材料からなるものが使用され
る。In the invention according to claim 2, as the wood piece used for the base material layer of the wood chip cement laminate, a wood chip obtained by subdividing a wood chip made from new wood, construction waste wood, or the like can be used. , Cedar, cypress, pine, toga, straw,
Oak, nara, birch, beech, oak, lauan, hiba, chestnut, zelkova, shii, willow, bamboo and other materials are used.
【００２９】木片を作製する方法としては、木チップ
を、例えば、リング型ハンマーミル（パールマン社製）
で切削して得ることができる。As a method for producing a wood chip, a wood chip is used, for example, by using a ring-type hammer mill (manufactured by Pearlman).
Can be obtained by cutting.
【００３０】木片の形状は、用途や強度などの必要に応
じて選択されるが、長さ６０ｍｍ以下、幅２０ｍｍ以
下、厚さ２ｍｍ以下のものが好ましく、目開き１．６８
ｍｍ以下の篩で分級された通過分を７０重量％以上含有
するものが特に好ましい。The shape of the wood piece is selected according to the needs such as the application and the strength, but it is preferably 60 mm or less in length, 20 mm or less in width, and 2 mm or less in thickness.
Those containing 70% by weight or more of the passing amount classified by a sieve of not more than mm are particularly preferable.
【００３１】請求項２記載の発明において、木片セメン
ト積層板の基材層に使用される軽量骨材としては特に限
定されず、例えば、パーライト、シラスバルーン、フラ
イアッシュ、太平洋セメント社製の商品名「Ｅ−スフィ
アーズ」、ガラスバルーンなどの無機軽量骨材、スチレ
ンビーズ、ポリエチレンビーズなどの有機軽量骨材が使
用できる。これらの軽量骨材は基材層を軽量化するため
に使用される。これら軽量骨材の中で、乾燥、湿潤の水
分変化や加熱、冷却の温度変化に伴う寸法変化の少ない
無機軽量骨材が好適である。In the invention according to the second aspect, the lightweight aggregate used for the base material layer of the wood chip cement laminate is not particularly limited, and examples thereof include pearlite, shirasu balloon, fly ash, and trade names manufactured by Taiheiyo Cement Corporation. Inorganic lightweight aggregates such as "E-Spheres" and glass balloons, and organic lightweight aggregates such as styrene beads and polyethylene beads can be used. These lightweight aggregates are used to reduce the weight of the base material layer. Among these lightweight aggregates, inorganic lightweight aggregates, which undergo little dimensional change due to changes in moisture during drying and wetting and changes in temperature during heating and cooling, are preferred.
【００３２】請求項２記載の発明において、木片セメン
ト積層板の補強層に使用される微細木片としては、前記
木片と同様の材料からなり、前記木片をディスクカッタ
ーミル（ホーライ社製「ＨＴ−３００型」）あるいはボ
ールミルなどで微粉砕することで得られる。According to the second aspect of the present invention, the fine wood piece used for the reinforcing layer of the wood chip cement laminate is made of the same material as the wood piece, and the wood piece is made of a disc cutter mill ("HT-300" manufactured by Horai Co., Ltd.). Mold ") or finely pulverized with a ball mill or the like.
【００３３】前記微細木片は、木片セメント積層板の補
強層中に５〜１５重量％含有されることが好ましい。It is preferable that the fine wood chips are contained in the reinforcing layer of the wood chip cement laminate in an amount of 5 to 15% by weight.
【００３４】前記微細木片が５重量％未満の場合には、
補強効果が得られず、強度不足となるとともに、比重が
大きくなり、補強層の重量が大きくなるおそれがある。
また、微細木片が１５重量％を超えると、木片の乾燥収
縮、吸水膨張によって寸法安定性が低下するとともに、
防火性能が劣るなどの問題が生じる。When the fine wood chips are less than 5% by weight,
There is a possibility that the reinforcing effect is not obtained, the strength becomes insufficient, the specific gravity increases, and the weight of the reinforcing layer increases.
In addition, when the fine wood chips exceed 15% by weight, the dimensional stability is reduced due to the drying shrinkage and water expansion of the wood chips,
Problems such as poor fire prevention performance occur.
【００３５】請求項２記載の発明において、木片セメン
ト積層板の補強層に使用される平均粒径２００μｍ以下
の微細骨材としては特に限定されないが、例えば、珪
砂、珪石粉、フライアッシュ、珪ソウ土、マイカ、シリ
カヒュームなどが挙げられる。これらの微細骨材を添加
することで、セメントの硬化過程に形成される空隙が充
填され、緻密な硬化体となり、強度、寸法安定性などが
向上する。平均粒径が２００μｍより大きくなると、セ
メント硬化体の空隙を充填するのには大きすぎ、十分に
緻密な硬化体とならない。In the invention according to the second aspect, the fine aggregate having an average particle size of 200 μm or less used for the reinforcing layer of the wood chip cement laminate is not particularly limited. For example, silica sand, silica stone powder, fly ash, silica sand Soil, mica, silica fume and the like. By adding these fine aggregates, the voids formed during the hardening process of the cement are filled and a dense hardened body is obtained, and the strength, dimensional stability and the like are improved. If the average particle size is larger than 200 μm, it is too large to fill the voids of the cured cement, and the cured product is not sufficiently dense.
【００３６】請求項２記載の発明において、水の添加量
は、セメント１００重量部に対し、３０〜７０重量部で
あることが好ましい。In the second aspect of the present invention, the amount of water is preferably 30 to 70 parts by weight based on 100 parts by weight of cement.
【００３７】前記水が３０重量部未満の場合には、セメ
ントの水和反応が不十分となり、強度低下を引き起こ
す。また、水が７０重量部を超えると、混合時におい
て、小さな固まりができて均一に混合ができなくなり、
成形された木片セメント板が不均質で強度がでなくな
る。If the amount of water is less than 30 parts by weight, the hydration reaction of the cement becomes insufficient and the strength is reduced. Further, if the water exceeds 70 parts by weight, small agglomerates are formed at the time of mixing, and uniform mixing cannot be performed.
The molded wood cement board is inhomogeneous and loses its strength.
【００３８】請求項２記載の発明において、木片セメン
ト積層板の製造方法としては、基材層は、セメント、木
片、軽量骨材および水の混合物を、また、補強層は、セ
メント、微細木片、平均粒径２００μｍ以下の微細骨材
および水の混合物を、それぞれ型枠上に散布落下させ、
ホットプレスにより所定時間加圧加熱して硬化させた
後、脱型することにより得ることができる。According to the second aspect of the present invention, in the method for manufacturing a wood chip cement laminate, the base material layer is a mixture of cement, wood chips, lightweight aggregate and water, and the reinforcing layer is cement, fine wood chips. A mixture of fine aggregate having an average particle size of 200 μm or less and water is sprayed and dropped on a mold, respectively.
It can be obtained by pressurizing and heating by a hot press for a predetermined time to cure, and then removing the mold.
【００３９】混合物の調製は、公知な方法で行われ、例
えば、オムニミキサー、ヘンシェルミキサーなどを使用
して行うことができる。The mixture is prepared by a known method, for example, using an omni mixer, a Henschel mixer or the like.
【００４０】請求項２記載の発明によれば、基材層は、
セメント、木片および軽量骨材を主成分とする組成物か
らなるので、寸法安定性に優れ、かつ軽量であり、一
方、補強層は、セメント、微細木片、平均粒径２００μ
ｍ以下の微細骨材を主成分とする組成物からなるので、
緻密な硬化体が得られるために強度が優れている。した
がって、基材層の裏面に補強層が積層された木片セメン
ト積層板は、軽量にして優れた強度、寸法安定性を発現
し得る。According to the second aspect of the present invention, the base material layer
Since it is composed of a composition mainly composed of cement, wood chips and lightweight aggregate, it has excellent dimensional stability and is lightweight, while the reinforcing layer is made of cement, fine wood chips, and an average particle diameter of 200 μm.
m or less as a main component of a fine aggregate,
The strength is excellent because a dense cured product is obtained. Therefore, the wood chip cement laminate in which the reinforcing layer is laminated on the back surface of the base material layer can be reduced in weight and exhibit excellent strength and dimensional stability.
【００４１】[0041]
【実施例】（実施例１−１〜１−５および比較例１−１
〜１−４）以下、本発明の木片セメント板の実施例１−
１〜１−５および比較例１−１〜１−４について説明す
る。Examples (Examples 1-1 to 1-5 and Comparative Example 1-1)
1-4) Hereinafter, Example 1 of the wood chip cement board of the present invention.
1 to 1-5 and Comparative Examples 1-1 to 1-4 will be described.
【００４２】これらの木片セメント板の実施例および比
較例は、下記の表１に示す組成を表１に示す配合で作製
したものである。The examples and comparative examples of these wood chip cement boards were prepared by mixing the compositions shown in Table 1 below with the formulations shown in Table 1.
【００４３】[0043]
【表１】 [Table 1]
【００４４】なお、表１において、木片セメント板中に
おける微細木片の含有量（重量％）を合わせて示してい
る。Table 1 also shows the content (% by weight) of the fine wood chips in the wood chip cement board.
【００４５】セメント組成物としては、早強ポルトラン
ドセメント（秩父小野田社製）７１．２重量部、アルミ
ナセメント（「デンカ２号」電気化学社製）１４．４重
量部、焼石膏（アドラ工業社製）８．６重量部、消石灰
（駒形石灰工業社製）５．８重量部を予備混合したもの
を用いた。As the cement composition, 71.2 parts by weight of early strength Portland cement (manufactured by Chichibu Onoda), 14.4 parts by weight of alumina cement (manufactured by Denka No. 2 Denki Kagaku), calcined gypsum (Adra Industries, Ltd.) 8.6 parts by weight) and 5.8 parts by weight of slaked lime (Komagata Lime Industry Co., Ltd.) were used.
【００４６】平均断面積０．０１〜０．３ｍｍ2 で平均
アスペクト比８以上の繊維状木片としては、杉、檜の混
合された木材チップを、パールマン社のリング型ハンマ
ーミルで切削し、次いで、ディスクカッターミル（「Ｈ
Ｔ−３００型」ホーライ社製）にて微粉砕して得た。こ
の場合の微粉砕された杉の平均断面積は０．０２ｍｍ 2
で、平均アスペクト比は８であった。また、微粉砕され
た檜の平均断面積は０．２６ｍｍ2 で、平均アスペクト
比は１０．５であった。Average cross-sectional area 0.01-0.3 mmTwoAverage in
As a fibrous wood piece with an aspect ratio of 8 or more, a mixture of cedar and cypress
The combined wood chips are transferred to Pearlman's ring-type hammer.
Milling, and then a disk cutter mill (“H
(T-300 type, manufactured by Horai Co., Ltd.). This
The average cross-sectional area of the finely ground cedar in case of Two
And the average aspect ratio was 8. It is also finely ground
The average cross section of the cypress is 0.26mmTwoAnd the average aspect
The ratio was 10.5.
【００４７】微細骨材としては、フライアッシュ（「ス
ーパーフロー」太平洋セメント社製）を用いた。As the fine aggregate, fly ash ("Super Flow" manufactured by Taiheiyo Cement Co., Ltd.) was used.
【００４８】セメント組成物、繊維状木片、フライアッ
シュおよび水の混合は、ヘンシェルミキサーを用いて行
った。The mixing of the cement composition, fibrous wood chips, fly ash and water was performed using a Henschel mixer.
【００４９】得られた混合物を、金属製の型上に散布落
下させ、積層状に混合物を堆積させ、圧力３．９２ＭＰ
ａ（４０ｋｇｆ／ｃｍ2 ）、温度９７℃にて１２分間ホ
ットプレスすることにより硬化させた後、脱型して厚み
約１５ｍｍの木片セメント板を得た。The obtained mixture is sprayed and dropped on a metal mold, and the mixture is deposited in a layered manner, and the pressure is 3.92 MPa.
a) (40 kgf / cm 2 ), cured by hot pressing at a temperature of 97 ° C. for 12 minutes, and then demolded to obtain a wood chip cement board having a thickness of about 15 mm.
【００５０】これらの木片セメント板の実施例１−１〜
１−５および比較例１−１〜１−４について、曲げ強
度、吸水長さ変化の各試験を行った。Examples 1-1 to 1-1 of these wood chip cement boards
Regarding 1-5 and Comparative Examples 1-1 to 1-4, each test of bending strength and change in water absorption length was performed.
【００５１】曲げ強度については、ＪＩＳ Ａ １４０
８に準じ、材齢１週間の試料で行った。Regarding the bending strength, JIS A 140
According to No. 8, the test was performed on a sample of one week old.
【００５２】吸水長さ変化については、得られた木片セ
メント板を長さ１５０ｍｍ、幅５０ｍｍのダンベル形状
に切断し、６０℃で１日乾燥した後、および、水中に１
日浸漬した後の寸法をマイクロメーターで測定し、以下
の式より吸水長さ変化率を算出した。Regarding the change in water absorption length, the obtained wood chip cement board was cut into a dumbbell shape having a length of 150 mm and a width of 50 mm, dried at 60 ° C. for 1 day, and dried in water.
The size after immersion in the sun was measured with a micrometer, and the rate of change in water absorption length was calculated from the following equation.
【００５３】吸水長さ変化率（％）＝（水中浸漬後寸法
一初期乾燥後寸法）／初期乾燥後寸法×１００ これらの結果を表２に示す。Change in water absorption length (%) = (dimension after immersion in water—dimension after initial drying) / dimension after initial drying × 100 The results are shown in Table 2.
【００５４】[0054]
【表２】 [Table 2]
【００５５】表２から木片セメント板の実施例１−１〜
１−５は、強度、寸法安定性に優れているが、木片セメ
ント板の比較例１−１〜１−３は、強度に劣り、比較例
１−４は、寸法安定性に劣る。 （実施例２−１〜２−４および比較例２−１〜２−３）
以下、本発明の木片セメント積層板の実施例２−１〜２
−４および木片セメント板の比較例１−１〜１−３につ
いて説明する。Table 2 shows that Examples 1-1 to 1 of the wood chip cement board were used.
1-5 is excellent in strength and dimensional stability, but Comparative Examples 1-1 to 1-3 of the wood chip cement board are inferior in strength, and Comparative Example 1-4 is inferior in dimensional stability. (Examples 2-1 to 2-4 and Comparative Examples 2-1 to 2-3)
Hereinafter, Examples 2-1 to 2 of the wood chip cement laminate of the present invention
-4 and Comparative Examples 1-1 to 1-3 of the wood chip cement board will be described.
【００５６】これらの木片セメント積層板の実施例２−
１〜２−４および木片セメント板の比較例２−１〜２−
３は、下記の表３に示す組成を表３に示す配合で作製し
たものである。Example 2 of these wood chip cement laminates
Comparative Examples 2-1 to 2--4 and Wood Chip Cement Board
No. 3 was prepared by mixing the composition shown in Table 3 below with the composition shown in Table 3.
【００５７】[0057]
【表３】 [Table 3]
【００５８】なお、表３において、木片セメント積層板
の補強層中における微細木片の含有量（重量％）を合わ
せて示している。Table 3 also shows the content (% by weight) of fine wood chips in the reinforcing layer of the wood chip cement laminate.
【００５９】セメント組成物としては、早強ポルトラン
ドセメント（秩父小野田社製）７１．２重量部、アルミ
ナセメント（「デンカ２号」電気化学社製）１４．４重
量部、焼石膏（アドラ工業社製）８．６重量部、消石灰
（駒形石灰工業社製）５．８重量部を予備混合したもの
を用いた。As the cement composition, 71.2 parts by weight of early strength Portland cement (manufactured by Chichibu Onoda), 14.4 parts by weight of alumina cement (manufactured by Denka No. 2 Denki Kagaku), calcined gypsum (Adra Industries, Ltd.) 8.6 parts by weight) and 5.8 parts by weight of slaked lime (Komagata Lime Industry Co., Ltd.) were used.
【００６０】木片としては、檜、杉の混合された木材チ
ップを、パールマン社のリング型ハンマーミルで切削し
て得た。上記木片の平均断面積は０．３９ｍｍ2 で、平
均アスペクト比は１０．３であった。The wood chips were obtained by cutting a wood chip in which cypress and cedar were mixed with a ring-type hammer mill manufactured by Pearlman. The average cross-sectional area of the piece of wood was 0.39 mm 2 and the average aspect ratio was 10.3.
【００６１】微細木片としては、上記木片をディスクカ
ッターミル（「ＨＴ−３００型」ホーライ社製）にて微
粉砕して微細木片Ａを得た。上記微細木片Ａの平均断面
積は０．０８ｍｍ2 で、平均アスペクト比は１０．５で
あった。As the fine wood chips, the above wood chips were finely pulverized with a disk cutter mill (“HT-300” manufactured by Horai Co., Ltd.) to obtain fine wood chips A. The average cross-sectional area of the fine wood chip A was 0.08 mm 2 , and the average aspect ratio was 10.5.
【００６２】また、上記木片をボールミルにて微粉砕
し、これを目開き１ｍｍの篩で分級し、その通過分から
微細木片Ｂを得た。上記微細木片Ｂの平均断面積は０．
０３ｍｍ2 で、平均アスペクト比は５．２であった。The above-mentioned wood chips were finely pulverized with a ball mill, and classified with a sieve having an opening of 1 mm, and fine wood chips B were obtained from the passing amount. The average cross-sectional area of the fine wood chip B is 0.
At 03 mm 2 , the average aspect ratio was 5.2.
【００６３】軽量骨材としては、太平洋セメント社製の
商品名「Ｅ−スフィアーズ」を用いた。As the lightweight aggregate, "E-Spheres" manufactured by Taiheiyo Cement Co., Ltd. was used.
【００６４】微細骨材としては、珪砂（「８号珪砂」六
呂屋鉱業社製）を用いた。As fine aggregate, silica sand (“No. 8 silica sand” manufactured by Rokuro Mining Co., Ltd.) was used.
【００６５】木片セメント積層板において、セメント組
成物、木片、軽量骨材および水の混合、セメント組成
物、微細木片、微細骨材および水の混合は、ヘンシェル
ミキサーを用いて行った。In the wood chip cement laminate, the cement composition, wood chips, lightweight aggregate and water were mixed, and the cement composition, fine wood chips, fine aggregate and water were mixed using a Henschel mixer.
【００６６】木片セメント板において、セメント組成
物、木片、軽量骨材および水の混合、セメント組成物、
微細木片、微細骨材および水の混合、セメント組成物、
木片および水の混合は、ヘンシェルミキサーを用いて行
った。In a wood chip cement board, a cement composition, wood chips, a lightweight aggregate and a mixture of water, a cement composition,
Mixture of fine wood chips, fine aggregate and water, cement composition,
The wood chips and water were mixed using a Henschel mixer.
【００６７】木片セメント積層板の基材層および補強層
ともに得られた混合物を、金属製の型上に散布落下さ
せ、積層状に混合物を堆積させ、圧力３．９２ＭＰａ
（４０ｋｇｆ／ｃｍ2 ）、温度９７℃にて１２分間ホッ
トプレスすることにより硬化させた後、脱型して基材層
と補強層が積層された厚み約１５ｍｍの木片セメント積
層板を得た。The mixture obtained for both the base material layer and the reinforcing layer of the wood chip cement laminate was sprayed and dropped on a metal mold, and the mixture was deposited in a laminated state, and the pressure was 3.92 MPa.
(40 kgf / cm 2 ), cured by hot pressing at a temperature of 97 ° C. for 12 minutes, and then demolded to obtain a wood chip cement laminate having a thickness of about 15 mm in which a base material layer and a reinforcing layer were laminated.
【００６８】これらの木片セメント積層板の実施例２−
１〜２−５および木片セメント板の比較例２−１〜２−
４について、曲げ強度、吸水長さ変化、比重の各試験を
行った。Example 2 of these wood chip cement laminates
Comparative Examples 2-1 to 2--5 and Wood Chip Cement Board
Regarding No. 4, each test of bending strength, change in water absorption length, and specific gravity was performed.
【００６９】曲げ強度については、ＪＩＳ Ａ １４０
８に準じ、材齢１週間の試料で行った。Regarding the bending strength, JIS A 140
According to No. 8, the test was performed on a sample of one week old.
【００７０】吸水長さ変化については、得られた木片セ
メント板を長さ１５０ｍｍ、幅５０ｍｍのダンベル形状
に切断し、６０℃で１日乾燥した後、および、水中に１
日浸漬した後の寸法をマイクロメーターで測定し、以下
の式より吸水長さ変化率を算出した。Regarding the change in water absorption length, the obtained wood chip cement board was cut into a dumbbell shape having a length of 150 mm and a width of 50 mm, dried at 60 ° C. for 1 day, and dried in water.
The size after immersion in the sun was measured with a micrometer, and the rate of change in water absorption length was calculated from the following equation.
【００７１】吸水長さ変化率（％）＝（水中浸漬後寸法
一初期乾燥後寸法）／初期乾燥後寸法×１００ 比重については、１０５℃で２４時間乾燥した後の絶乾
比重で評価した。Change rate of water absorption length (%) = (dimension after immersion in water—dimension after initial drying) / dimension after initial drying × 100 The specific gravity was evaluated by the absolute dry specific gravity after drying at 105 ° C. for 24 hours.
【００７２】これらの結果を表４に示す。Table 4 shows the results.
【００７３】[0073]
【表４】 [Table 4]
【００７４】表４から木片セメント積層板の実施例２−
１〜２−４は、強度、寸法安定性、軽量性に優れている
が、木片セメント板の比較例２−１は、強度に劣り、比
較例２−２は、軽量性に劣り、比較例２−３は、寸法安
定性に劣る。From Table 4, it is found that Example 2 of the wood chip cement laminate was used.
1-2-4 are excellent in strength, dimensional stability, and lightness, but Comparative Example 2-1 of the wood chip cement board is inferior in strength, and Comparative Example 2-2 is inferior in lightness, and Comparative Example 2-3 is inferior in dimensional stability.
【００７５】[0075]
【発明の効果】以上のように請求項１記載の発明によれ
ば、平均断面積０．０１〜０．３ｍｍ 2 で平均アスペク
ト比８以上の繊維状木片は、繊維状で、かつ単位重量当
たりの表面積が大きいため、セメント中に添加、分散さ
せた場合、セメントとの接触面積が増大するために、補
強効率が高くなり、少ない添加量でも高い強度を得るこ
とができる。そして、木片の添加量を少なくすること
で、寸法安定性に優れたものとなる。As described above, according to the first aspect of the present invention,
If average cross-sectional area 0.01-0.3mm TwoAverage Aspect
A fibrous wood piece with a ratio of 8 or more is fibrous and has a unit weight
Addition and dispersion in cement due to large surface area
If this occurs, the contact area with cement will increase,
High efficiency and high strength can be obtained with a small amount of addition.
Can be. And reduce the amount of wood chips added
Thus, the dimensional stability is excellent.
【００７６】また、請求項２記載の発明によれば、基材
層がセメント、木片および軽量骨材を主成分とする組成
物からなるので、寸法安定性に優れ、かつ軽量であり、
一方、補強層がセメント、微細木片および平均粒径２０
０μｍ以下の微細骨材を主成分とする組成物からなるの
で、緻密な硬化体が得られるために強度が優れている。
したがって、かかる基材層と補強層とが積層された木片
セメント積層板は、強度、寸法安定性に優れ、かつ軽量
である。According to the second aspect of the present invention, since the base material layer is made of a composition mainly composed of cement, wood chips and lightweight aggregate, it has excellent dimensional stability and is lightweight.
On the other hand, the reinforcing layer is made of cement, fine wood chips and an average particle size of 20.
Since it is composed of a composition containing a fine aggregate of 0 μm or less as a main component, a dense cured product is obtained, so that the strength is excellent.
Therefore, a wood chip cement laminate in which such a base material layer and a reinforcing layer are laminated is excellent in strength, dimensional stability, and lightweight.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｅ０４Ｃ 2/04 Ｅ０４Ｃ 2/04 Ｆ Ｅ // Ｃ０４Ｂ 111:20 Ｃ０４Ｂ 111:20 111:72 111:72 Ｆターム(参考） 2E162 CA01 CA06 FA02 FA03 FA11 FC03 4F100 AA20H AE02A AE02B AJ02A AJ02B AJ02H BA02 CA24A CA24B GB07 JA13B JA15A JA15H JK01 JL03 JL04 YY00A YY00B YY00H 4G012 PA27 PA34 PC12 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) E04C 2/04 E04C 2/04 FE // C04B 111: 20 C04B 111: 20 111: 72 111: 72 F Term (reference) 2E162 CA01 CA06 FA02 FA03 FA11 FC03 4F100 AA20H AE02A AE02B AJ02A AJ02B AJ02H BA02 CA24A CA24B GB07 JA13B JA15A JA15H JK01 JL03 JL04 YY00A YY00B YY00H 4G012 PA27 PA34 PC12
Claims (2)
木片セメント板であって、前記微細木片は、平均断面積
０．０１〜０．３ｍｍ2 で平均アスペクト比８以上の繊
維状木片であり、木片セメント板中に５〜１５重量％含
有されていることを特徴とする木片セメント板。1. A wood chip cement board containing cement and fine wood chips as main components, wherein said fine wood chips are fibrous wood chips having an average cross-sectional area of 0.01 to 0.3 mm 2 and an average aspect ratio of 8 or more, A wood chip cement board characterized in that the wood chip cement board contains 5 to 15% by weight.
セメント積層板であって、前記基材層は、セメント、木
片および軽量骨材を主成分とする比重０．９〜１．３の
組成物からなり、補強層は、厚みが０．５〜１０ｍｍ
で、セメント、微細木片および平均粒径２００μｍ以下
の微細骨材を主成分とする比重１．４〜１．８の組成物
からなり、前記微細木片は、補強層中に５〜１５重量％
含有されていることを特徴とする木片セメント積層板。2. A wood chip cement laminate in which a reinforcing layer is stacked on the back surface of a base material layer, wherein the base material layer has a specific gravity of 0.9 to 1. based on cement, wood chips and lightweight aggregate as main components. 3, the reinforcing layer has a thickness of 0.5 to 10 mm.
And a composition having a specific gravity of 1.4 to 1.8 mainly composed of cement, fine wood chips and fine aggregate having an average particle diameter of 200 μm or less, wherein the fine wood chips are contained in the reinforcing layer in an amount of 5 to 15% by weight.
A wood chip cement laminate characterized by containing: