JP2002079615A - Sheathing material - Google Patents
Sheathing materialInfo
- Publication number
- JP2002079615A JP2002079615A JP2000268352A JP2000268352A JP2002079615A JP 2002079615 A JP2002079615 A JP 2002079615A JP 2000268352 A JP2000268352 A JP 2000268352A JP 2000268352 A JP2000268352 A JP 2000268352A JP 2002079615 A JP2002079615 A JP 2002079615A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- water
- exterior material
- repellent silicone
- substance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】本発明は、住宅、ビル等用として用いられ
る外装材に関し、特に、汚れが付着しにくい性能をより
長時間保持する機能を有する外装材に関する。[0001] The present invention relates to an exterior material used for houses, buildings, and the like, and more particularly to an exterior material having a function of maintaining the ability to prevent dirt from adhering for a longer time.
【０００２】[0002]
【従来の技術】住宅とかビルの外壁を被覆する外装材と
して、アクリル樹脂系外装材、セラミック樹脂系外装材
等が用いられている。2. Description of the Related Art Acrylic resin-based exterior materials, ceramic resin-based exterior materials, and the like have been used as exterior materials for covering the outer walls of houses and buildings.
【０００３】[0003]
【発明が解決しようとする課題】住宅とかビルの外壁と
か屋根材は、屋外に露出するものであるため、排気ガス
等の燃焼生成物や大気中に浮遊する煤煙などにより汚れ
やすい。しかし外装材の清掃は住宅とかビルの外壁の比
較的低い部分の清掃は可能であるが高所の外壁とか屋根
材の清掃は専門の業者に依頼しなければならずコストが
かかり、また高所での清掃作業は危険でもある。Since houses and building exterior walls and roofing materials are exposed outdoors, they are easily contaminated by combustion products such as exhaust gas and soot floating in the atmosphere. However, cleaning of exterior materials can clean relatively low portions of houses and building outer walls, but cleaning of high-level outer walls and roofing materials must be entrusted to a specialized contractor, which is costly. Cleaning work at home is also dangerous.
【０００４】また、周期的に清掃を行っても、表面に付
着した汚れは取れにくく、そのため年月がたつにつれて
外壁が変色してしまうことがある。Further, even if cleaning is performed periodically, dirt adhering to the surface is difficult to remove, so that the outer wall may be discolored over time.
【０００５】本発明の目的は、汚れが付着しにくく、且
つ汚れを容易に洗い落とすことが可能な外装材を提供す
ることである。[0005] An object of the present invention is to provide an exterior material to which dirt hardly adheres and which can be easily washed off.
【０００６】[0006]
【課題を解決するための手段】請求項１に記載の発明
は、上記の課題を解決するもので、外装材の基材表面に
光触媒粒子を含み、該光触媒粒子の一部が表面に露出し
ている透明な耐食性樹脂層を設け、その上に多数の開口
部を有する透明な撥水性シリコーン層を設け、前記撥水
性シリコーン層は光励起による親水化を防止する物質を
含むことを特徴とする。Means for Solving the Problems The invention according to claim 1 solves the above-mentioned problems, and includes a photocatalyst particle on a surface of a base material of an exterior material, and a part of the photocatalyst particle is exposed on the surface. A transparent corrosion-resistant resin layer, and a transparent water-repellent silicone layer having a large number of openings formed thereon. The water-repellent silicone layer contains a substance that prevents hydrophilicity due to light excitation.
【０００７】請求項１に記載の発明において、多数の開
口部として多孔状の開口部又は目地状の開口部を設ける
ことができる。[0007] In the first aspect of the present invention, a porous opening or a joint-like opening can be provided as a large number of openings.
【０００８】請求項６に記載の発明は、上記の課題を解
決するもので、外装材の基材表面に、光触媒粒子と、前
記撥水性シリコーンの前記光触媒の光励起による撥水性
シリコーンの親水化を防止するための物質とを含有する
透明な撥水性シリコーン層が形成されており、前記表面
層の表面に前記光触媒粒子の一部が露出していることを
特徴とする。According to a sixth aspect of the present invention, there is provided an image forming apparatus, comprising: a photocatalytic particle and a hydrophilicity of the water-repellent silicone caused by photoexcitation of the photocatalyst; A transparent water-repellent silicone layer containing a substance for preventing the photocatalyst particles is formed, and a part of the photocatalyst particles is exposed on the surface of the surface layer.
【０００９】請求項１及び２に記載の発明において、基
材表面に印刷層を介して光触媒粒子を含む耐食性樹脂層
を設けることができる。According to the first and second aspects of the present invention, a corrosion-resistant resin layer containing photocatalyst particles can be provided on the surface of the base material via a printing layer.
【００１０】本発明において、前記光励起による親水化
を防止する物質として、コバルト又はコバルト化合物を
適用することができる。[0010] In the present invention, cobalt or a cobalt compound can be applied as the substance for preventing hydrophilization due to photoexcitation.
【００１１】請求項１に記載の外装材においては、外装
材の表面は多数の開口部を有する撥水性シリコーン層よ
りなり、前記開口部から露出する光触媒が、雨が降り、
或いは散水がかかった後に日光があたるときに酸性物質
を生じ、この酸性物質が汚れを分解する働きをするの
で、外装材の表面に付着した汚れ、特に排気ガス等の燃
焼生成物や大気中に浮遊する煤煙などによる汚れが容易
に取り除かれる。また撥水性シリコーン層の表面により
適度の撥水性が維持されるので恒久的に汚れにくくい表
面が形成される。In the exterior material according to the first aspect, the surface of the exterior material is formed of a water-repellent silicone layer having a large number of openings, and the photocatalyst exposed from the openings is rained,
Alternatively, when exposed to sunlight after watering, acidic substances are generated, and this acidic substance acts to decompose dirt, so that dirt attached to the surface of the exterior material, especially combustion products such as exhaust gas and air Dirt due to floating soot and the like is easily removed. Also, since the appropriate water repellency is maintained by the surface of the water repellent silicone layer, a surface which is hardly stained permanently is formed.
【００１２】また、請求項６に記載の外装材において
は、表面層の表面に一部露出する光触媒は、雨が降り、
或いは散水がかかった後に日光があたるときに酸性物質
を生じ、この酸性物質が汚れを分解する働きをするの
で、外装材の表面に付着した汚れ、特に排気ガス等の燃
焼生成物や大気中に浮遊する煤煙などによる汚れが容易
に取り除かれる。また撥水性シリコーン層の表面により
適度の撥水性が維持されるので恒久的に汚れにくい表面
が形成される。[0012] In the exterior material according to the present invention, the photocatalyst partially exposed on the surface of the surface layer may be rained,
Alternatively, when exposed to sunlight after watering, acidic substances are generated, and this acidic substance acts to decompose dirt, so that dirt attached to the surface of the exterior material, especially combustion products such as exhaust gas and air Dirt due to floating soot and the like is easily removed. Also, since the surface of the water-repellent silicone layer maintains an appropriate water repellency, a surface that is hardly stained permanently is formed.
【００１３】[0013]
【発明の実施の形態】図１は、本発明の外装材の第１の
実施態様を示す。基材１の上に光触媒粒子２を含む耐食
性樹脂層３が設けられ、その上に多数の開口部４を有す
る、光触媒の光励起による親水化を防止するための物質
６を含有する撥水性シリコーン層５が設けられている。
また光触媒粒子２は耐食性樹脂層３の表面に一部露出す
るように分散せしめられている。FIG. 1 shows a first embodiment of an exterior material of the present invention. A water-repellent silicone layer provided with a corrosion-resistant resin layer 3 containing photocatalyst particles 2 on a base material 1 and having a number of openings 4 thereon and containing a substance 6 for preventing hydrophilization of the photocatalyst by photoexcitation. 5 are provided.
The photocatalyst particles 2 are dispersed so as to be partially exposed on the surface of the corrosion-resistant resin layer 3.
【００１４】本発明の外装材において、基材１として、
ポリエステル樹脂、アクリル樹脂、ガラス繊維、ナイロ
ン樹脂、ガラス繊維、ポリエステル繊維、アラミド繊維
からなる織布又は不織布を用いることができる。In the exterior material of the present invention,
A woven or nonwoven fabric made of polyester resin, acrylic resin, glass fiber, nylon resin, glass fiber, polyester fiber, and aramid fiber can be used.
【００１５】耐食化性樹脂層３中に分散して含まれる光
触媒粒子２として、その結晶の伝導帯と荷電子帯の間の
エネルギーギャップよりも大きなエネルギー（即ち短い
波長）の光（励起光）を照射したときに、荷電子帯中の
電子の励起（光励起）が生じて、伝導電子と正孔を生成
し得る物質をいい、例えば、アナターゼ型酸化チタン、
酸化亜鉛、酸化錫、酸化第二鉄、三酸化二ビスマス、三
酸化タングステン、チタン酸ストロンチウム等の酸化物
が好適に利用できる。光触媒の光励起に用いる光源とし
ては、日中は太陽光線に曝されるので太陽光線が利用で
きる。また、光の比較的あたりにくい北側の壁に取り付
けた外装材に対しては、光触媒反応を促進するために、
赤外線ランプ等により光を照射して太陽光線のあたる量
の少ない分を補ってもよい。The photocatalyst particles 2 dispersed and contained in the corrosion-resistant resin layer 3 are light (excitation light) having energy (ie, shorter wavelength) larger than the energy gap between the conduction band and the valence band of the crystal. Is a substance capable of generating conduction electrons and holes by excitation of electrons (photoexcitation) in the valence band when irradiated with, for example, anatase type titanium oxide,
Oxides such as zinc oxide, tin oxide, ferric oxide, bismuth trioxide, tungsten trioxide, and strontium titanate can be suitably used. As a light source used for photoexcitation of the photocatalyst, sunlight can be used because the light is exposed to sunlight during the day. In addition, for exterior materials attached to the north wall that is relatively hard to hit with light, in order to promote the photocatalytic reaction,
Light may be irradiated by an infrared lamp or the like to compensate for a small amount of sunlight.
【００１６】次に耐食性樹脂層３を構成する樹脂とし
て、シリコーン樹脂、アクリル樹脂、アクリルシリコン
樹脂、シリコーンポリカーボネート共重合体、ナイロン
樹脂、硬質塩化ビニル樹脂等を適用することができる。Next, as the resin constituting the corrosion resistant resin layer 3, a silicone resin, an acrylic resin, an acrylic silicone resin, a silicone polycarbonate copolymer, a nylon resin, a hard vinyl chloride resin, or the like can be used.
【００１７】光触媒粒子２を含む耐食性樹脂層３は光触
媒をエタノール、プロパノール等の溶媒と共にシリコー
ン樹脂、アクリル樹脂、アクリルシリコン樹脂、シリコ
ーンポリカーボネート共重合体、ナイロン樹脂、硬質塩
化ビニル樹脂等に分散させたコーティング組成物をコー
ティングすることにより形成することができる。In the corrosion-resistant resin layer 3 containing the photocatalyst particles 2, the photocatalyst is dispersed in a silicone resin, an acrylic resin, an acrylic silicone resin, a silicone polycarbonate copolymer, a nylon resin, a hard vinyl chloride resin or the like together with a solvent such as ethanol or propanol. It can be formed by coating a coating composition.
【００１８】耐食性樹脂層３中に分散せしめられた光触
媒粒子２は太陽光線等の光があたると耐食性樹脂層中に
含まれるエタノール等と反応して或いは雨水等と反応し
て酸性物質を生じ、この酸性物質は外装材の表面、即ち
撥水性シリコーン層５の表面に流出し、外装材の表面の
汚れ成分を分解して外装材の表面を清浄にする。また撥
水性シリコーン層の表面により適度の撥水性が維持され
るので恒久的に汚れにくい外装材の表面が形成される。The photocatalyst particles 2 dispersed in the corrosion-resistant resin layer 3 react with ethanol or the like contained in the corrosion-resistant resin layer when exposed to light such as sunlight, or react with rainwater or the like to produce an acidic substance. This acidic substance flows out to the surface of the exterior material, that is, the surface of the water-repellent silicone layer 5, and decomposes dirt components on the surface of the exterior material to clean the surface of the exterior material. In addition, since the surface of the water-repellent silicone layer maintains appropriate water repellency, the surface of the exterior material that is hardly stained permanently is formed.
【００１９】第１の実施態様の外装材は基材の裏面に透
明な接着剤を塗布し、家屋、ビル等の外壁に貼着するこ
とにより恒久的に汚れにくい表面を有する壁面を構成す
ることができる。The exterior material of the first embodiment forms a wall surface having a surface which is hardly soiled permanently by applying a transparent adhesive to the back surface of the base material and sticking it to an outer wall of a house, a building or the like. Can be.
【００２０】撥水性シリコーン層５を構成する撥水性シ
リコーンには、平均組成式 Ｒp ＳｉＯ(4-p)/2 （式中、Ｒは一価の有機基の１種又は２種以上からなる
官能基、又は、一価と有機基と水産基から選ばれた２種
以上からなる官能基であり、ｐは０＜ｐ＜２を満足する
数である）で表示される樹脂が利用できる。The water-repellent silicone constituting the water-repellent silicone layer 5 has an average composition formula R p SiO (4-p) / 2 (where R is one or more monovalent organic groups) A resin represented by a functional group or a functional group consisting of two or more selected from monovalent, organic and marine groups, and p is a number satisfying 0 <p <2) can be used.
【００２１】また撥水性シリコーン層５に分散する光励
起による親水化を防止する物質６としては、コバルト、
又はコバルト合金、酸化コバルト、塩化コバルト、硫酸
コバルト、ヨウ化コバルト、臭化コバルト、酢酸コバル
ト、塩素酸コバルト、硝酸コバルト等のコバルト化合物
が好適に利用できる。The substance 6 for preventing hydrophilicity caused by light excitation dispersed in the water-repellent silicone layer 5 includes cobalt,
Alternatively, cobalt compounds such as cobalt alloy, cobalt oxide, cobalt chloride, cobalt sulfate, cobalt iodide, cobalt bromide, cobalt acetate, cobalt chlorate, and cobalt nitrate can be suitably used.
【００２２】撥水性シリコーン層５の膜厚は、０．４μ
ｍ以下にするのが望ましい。０．４μｍ以下にすること
により光の乱反射による白濁を防止することができ、表
面層は実質的に透明となる。更に表面層の膜厚を、０．
２μｍ以下にすると、光の干渉による表面層の発色を防
止することができるので、一層好ましい。また表面層は
薄ければ薄いほどその透明度は向上する。更に表面層の
膜厚を薄くすれば表面層の耐摩耗性も向上する。The water repellent silicone layer 5 has a thickness of 0.4 μm.
m or less. When the thickness is 0.4 μm or less, cloudiness due to irregular reflection of light can be prevented, and the surface layer becomes substantially transparent. Further, the thickness of the surface layer is set to 0.
When the thickness is 2 μm or less, color development of the surface layer due to light interference can be prevented, so that it is more preferable. Also, the thinner the surface layer, the higher its transparency. Further, if the thickness of the surface layer is reduced, the wear resistance of the surface layer is also improved.
【００２３】多数の開口部を有する、光励起による親水
化を防止する物質６を含む撥水性シリコーン層５は、コ
バルト又はコバルト化合物等の光触媒の光励起による親
水化を防止するための物質にシリコーンの前駆体に、
水、エタノール、プロパノール等の溶媒や塩酸、硝酸、
硫酸、酢酸、マレイン酸等のシリコーン前駆体の加水分
解を促進する触媒や、トリブチルアミン、ヘキシルアミ
ンなどの塩基性化合物類、アルミニウムトリイソプロポ
キシド、テトライソプロピルチタネートなどの酸性化合
物等のシリコーンの前駆体を硬化させる触媒や、シラン
カップリング剤等のコーティング液の分散性を向上させ
る界面活性剤を添加したコーティング組成物を用いて、
例えばシルクスクリーン印刷法、開口部に相当する部分
をマスキングした後にコーティングする方法、或いは全
面コーティングした後撥水性シリコーン層の深さに穿孔
して多孔状の開口部を形成することにより形成すること
ができる。コーティング層の硬化は熱処理等により行う
ことができる。The water-repellent silicone layer 5 having a number of openings and containing a substance 6 for preventing hydrophilicity by photoexcitation is used as a substance for preventing hydrophilicity by photoexcitation of a photocatalyst such as cobalt or a cobalt compound. On the body,
Solvents such as water, ethanol, propanol, hydrochloric acid, nitric acid,
Catalysts that promote hydrolysis of silicone precursors such as sulfuric acid, acetic acid, and maleic acid; and precursors of silicones such as basic compounds such as tributylamine and hexylamine, and acidic compounds such as aluminum triisopropoxide and tetraisopropyl titanate. By using a coating composition containing a catalyst for curing the body and a surfactant for improving the dispersibility of a coating liquid such as a silane coupling agent,
For example, it can be formed by a silk screen printing method, a method of coating after masking a portion corresponding to the opening, or a method of forming a porous opening by coating the entire surface and then piercing to the depth of the water-repellent silicone layer. it can. Curing of the coating layer can be performed by heat treatment or the like.
【００２４】ここでシリコーンの前駆体としては、平均
組成式 Ｒp ＳｉＸq Ｏ(4-p-q)/2 （式中、Ｒは一価の有機基の１種又は２種以上からなる
官能基、又は一価の有機基と水酸基から選ばれた２種以
上からなる官能基であり、Ｘはアルコキシ基、又はハロ
ゲン原子であり、ｐ及びｑは０＜ｐ＜２、０＜ｑ＜４を
満足する数である）で表されるシロキサンからなる塗膜
形成要素、又は一般式 Ｒp ＳｉＸ4-q （式中、Ｒは一価の有機基の１種又は２種以上からなる
官能基、又は、一価の有機基と水酸基から選ばれた２種
以上からなる官能基であり、ｐは１または２である）で
表される加水分解性シラン誘導体からなる塗膜形成要素
が好適に利用できる。The silicone precursor used herein has an average compositional formula of R p SiX q O (4-pq) / 2 (wherein R is a functional group comprising one or more monovalent organic groups, Or a functional group composed of two or more selected from a monovalent organic group and a hydroxyl group, X is an alkoxy group or a halogen atom, and p and q satisfy 0 <p <2 and 0 <q <4. A film-forming element composed of a siloxane represented by the following formula: or a general formula R p SiX 4-q (wherein R is a functional group comprising one or more monovalent organic groups, or , A functional group consisting of two or more kinds selected from a monovalent organic group and a hydroxyl group, and p is 1 or 2). .
【００２５】図２は、第２の実施態様を示す。基材１の
上に印刷層７及び印刷保護層８が積層され、その上に光
触媒粒子２を含む耐食性樹脂層３が設けられ、その上に
多数の開口部４を有する、光触媒の光励起による親水化
を防止するための物質６を含有する撥水性シリコーン層
５が設けられている。また光触媒粒子２は耐食制樹脂層
３の表面に一部露出するように分散せしめられている.FIG. 2 shows a second embodiment. A printing layer 7 and a printing protection layer 8 are laminated on a base material 1, a corrosion-resistant resin layer 3 containing photocatalyst particles 2 is provided thereon, and a plurality of openings 4 are provided thereon. A water-repellent silicone layer 5 containing a substance 6 for preventing aging is provided. The photocatalyst particles 2 are dispersed so as to be partially exposed on the surface of the corrosion-resistant resin layer 3.
【００２６】印刷層７を被覆する印刷保護層８は、耐食
性樹脂層３中の光触媒素子が印刷層に影響を及ぼすこと
を防止するために設けたものでこの構成材料としてアク
リル樹脂、シリコーン樹脂、ナイロン樹脂、ポリエステ
ル樹脂等を適用することができる。The print protective layer 8 covering the print layer 7 is provided to prevent the photocatalyst element in the corrosion-resistant resin layer 3 from affecting the print layer, and includes acrylic resin, silicone resin, Nylon resin, polyester resin, or the like can be used.
【００２７】印刷層７を設けることにより美観を付与し
得るのみならず多孔状に設けた撥水性シリコーン層の開
口部を目立たなくすることができる。By providing the printing layer 7, not only can the aesthetic appearance be imparted, but also the opening of the porous water-repellent silicone layer can be made inconspicuous.
【００２８】基材１、光触媒粒子２、耐食性樹脂層３、
撥水性シリコーン層５及び光触媒の光励起による親水化
を防止するための物質６に関しては第１の実施態様の説
明の中で説明した通りである。Substrate 1, photocatalyst particles 2, corrosion-resistant resin layer 3,
The water-repellent silicone layer 5 and the substance 6 for preventing the photocatalyst from becoming hydrophilic by photoexcitation are as described in the description of the first embodiment.
【００２９】耐食性樹脂層３中に分散せしめられた光触
媒粒子２は太陽光線等の光があたると耐食性樹脂層３中
に含まれるエタノール等と反応して、或いは雨水等と反
応して酸性物質を生じ、この酸性物質は外装材の表面、
即ち撥水性シリコーン層５の表面に流出し、外装材の表
面の汚れ成分を分解して外装材の表面を清浄にする。ま
た撥水性シリコーン層の表面により適度の撥水性が維持
されるので、恒久的に汚れにくい外装材の表面が形成さ
れる。The photocatalyst particles 2 dispersed in the corrosion-resistant resin layer 3 react with ethanol or the like contained in the corrosion-resistant resin layer 3 when exposed to light such as sunlight, or react with rainwater or the like to remove acidic substances. This acidic substance is generated on the surface of the exterior material,
That is, it flows out to the surface of the water-repellent silicone layer 5 and decomposes dirt components on the surface of the exterior material to clean the surface of the exterior material. Also, since the appropriate water repellency is maintained by the surface of the water repellent silicone layer, the surface of the exterior material which is hardly stained permanently is formed.
【００３０】第２の実施態様の外装材は基材の裏面に透
明な接着材を塗布し、家屋、ビル等の外壁に貼着するこ
とにより、印刷層により美観が付与され、且つ恒久的に
汚れにくい表面を有する壁面を構成することができる。The exterior material of the second embodiment is applied with a transparent adhesive on the back surface of the base material and is adhered to the outer wall of a house, a building, or the like, so that the printed layer provides an aesthetic appearance and is permanently provided. It is possible to form a wall surface having a surface that is not easily contaminated.
【００３１】図３は、本発明の外装材の第３の実施態様
を示す。基材１の表面に、光触媒粒子２と、光触媒の光
励起による撥水性シリコーンの親水化を防止するための
物質６とを含有する透明な撥水性シリコーン層５が形成
されており、前記撥水性シリコーン層５の表面に光触媒
粒子２の一部が露出している。FIG. 3 shows a third embodiment of the exterior material of the present invention. A transparent water-repellent silicone layer 5 containing photocatalyst particles 2 and a substance 6 for preventing hydrophilicity of the water-repellent silicone caused by photoexcitation of the photocatalyst is formed on the surface of the base material 1. Part of the photocatalyst particles 2 is exposed on the surface of the layer 5.
【００３２】第３の実施態様において、基材１、光触媒
粒子２、耐食性樹脂層３、撥水性シリコーン層５及び光
触媒の光励起による親水化を防止するための物質６に関
しては第１の実施態様の説明の中で説明した通りであ
る。In the third embodiment, the substrate 1, the photocatalyst particles 2, the corrosion-resistant resin layer 3, the water-repellent silicone layer 5, and the substance 6 for preventing the photocatalyst from becoming hydrophilic by photoexcitation are the same as those in the first embodiment. As described in the description.
【００３３】第３の実施態様において、光触媒粒子２及
び光触媒の光励起による親水化を防止するための物質を
含む撥水性シリコーン層５は、光触媒粒子、コバルト又
はコバルト化合物等の光触媒の光励起による親水化を防
止するための物質にシリコーンの前駆体を含み、その他
に水、エタノール、プロパノール等の溶媒や、塩酸、硝
酸、酢酸、マレイン酸等のシリコーンの前駆体に加水分
解を促進する触媒や、トリプチルアミンなどの塩基性化
合物類、アルミニウムトリイソプロポキシド、テトラシ
イソプロピルチタネートなどの酸性化合物類等のシリコ
ーンの前駆体を硬化させる触媒や、シランカップリング
剤等のコーティング液の分散性を向上させる界面活性剤
スなどを添加してなるコーティング液を、スプレーコー
ティング法、ディップコーティング法、フローコーティ
ング法、スピンコーティング法、ロールコーティング
法、刷毛塗り、スポンジ塗り等の方法により、基材にコ
ーティングすることにより形成することができる。また
コーティング層の硬化は熱処理、室温放置、紫外線照射
等により行うことができる。In the third embodiment, the water repellent silicone layer 5 containing the photocatalyst particles 2 and the substance for preventing the photocatalyst from becoming hydrophilic due to photoexcitation is made hydrophilic by photoexcitation of photocatalyst particles, photocatalyst such as cobalt or a cobalt compound. Precursors include silicone precursors, and solvents such as water, ethanol, and propanol, and catalysts that promote hydrolysis to silicone precursors such as hydrochloric acid, nitric acid, acetic acid, and maleic acid. Improves the dispersibility of coating compounds such as catalysts for curing silicone precursors such as basic compounds such as butylamine, acidic compounds such as aluminum triisopropoxide and tetracyisopropyl titanate, and silane coupling agents. The coating liquid containing surfactants is applied by spray coating Flop coating method, flow coating method, spin coating, roll coating, brush coating, by a method sponge coating, etc., it can be formed by coating on the substrate. Curing of the coating layer can be performed by heat treatment, standing at room temperature, irradiation of ultraviolet rays, or the like.
【００３４】第３の実施態様において、撥水性シリコー
ン層５中に分散せしめられた光触媒粒子２は太陽光線等
の光があたると耐食性樹脂層中に含まれるエタノール等
と反応して或いは層表面に露出する光触媒粒子２は雨水
等と反応して酸性物質を生じ、この酸性物質は外装材の
表面、即ち撥水性シリコーン層５の表面に流出し、外装
材の表面の汚れ成分を分解して外装材の表面を清浄にす
る。また撥水性シリコーン層の表面により適度の撥水性
が維持されるので、恒久的に汚れにくい外装材の表面が
形成される。In the third embodiment, the photocatalyst particles 2 dispersed in the water-repellent silicone layer 5 react with ethanol or the like contained in the corrosion-resistant resin layer when exposed to light such as sunlight, or on the surface of the layer. The exposed photocatalyst particles 2 react with rainwater or the like to generate an acidic substance, which flows out to the surface of the exterior material, that is, the surface of the water-repellent silicone layer 5, decomposes dirt components on the surface of the exterior material, and Clean the surface of the material. Also, since the appropriate water repellency is maintained by the surface of the water repellent silicone layer, the surface of the exterior material which is hardly stained permanently is formed.
【００３５】第３の実施態様の外装材は基材の裏面に透
明な接着材を塗布し、家屋、ビル等の外壁に貼着するこ
とにより恒久的に汚れにくい表面を有する壁面を構成す
ることができる。The exterior material of the third embodiment is to form a wall surface having a surface which is hardly stained permanently by applying a transparent adhesive to the back surface of the base material and sticking it to the outer wall of a house, a building or the like. Can be.
【００３６】図４は、本発明の外装材の第４の実施態様
を示す。この実施態様においては、基材１と撥水性シリ
コーン層５の間に印刷層７及び印刷保護層８が積層され
ている点を除けば第３の実施態様と同様の構成を有す
る。FIG. 4 shows a fourth embodiment of the exterior material of the present invention. This embodiment has a configuration similar to that of the third embodiment except that a printing layer 7 and a printing protection layer 8 are laminated between the substrate 1 and the water-repellent silicone layer 5.
【００３７】第４の実施態様において、基材１、光触媒
粒子２、耐食性樹脂層３、撥水性シリコーン層５及び光
触媒の光励起による親水化を防止するための物質６に関
しては第３の実施態様の説明の中で説明した通りであ
る。また印刷保護層８に関しては第２の実施態様の中で
説明した通りである。In the fourth embodiment, the substrate 1, the photocatalyst particles 2, the corrosion-resistant resin layer 3, the water-repellent silicone layer 5, and the substance 6 for preventing the photocatalyst from becoming hydrophilic by photoexcitation are the same as those in the third embodiment. As described in the description. The print protection layer 8 is as described in the second embodiment.
【００３８】撥水性シリコーン層５中に分散せしめられ
た光触媒粒子２は、太陽光線等の光があたると撥水性シ
リコーン層５中に含まれるエタノール等と反応して、或
いは雨水等と反応して酸性物質を生じ、この酸性物質は
外装材の表面、即ち撥水性シリコーン層５の表面に流出
し、表面に付着した汚れ成分を分解して外装材の表面を
清浄にする。また撥水性シリコーン層の表面により適度
の撥水性が維持されるので、恒久的に汚れにくい外装材
の表面が形成される。The photocatalyst particles 2 dispersed in the water-repellent silicone layer 5 react with ethanol or the like contained in the water-repellent silicone layer 5 when exposed to light such as sunlight, or react with rainwater or the like. An acidic substance is generated, and the acidic substance flows out to the surface of the exterior material, that is, the surface of the water-repellent silicone layer 5, and decomposes dirt components attached to the surface to clean the surface of the exterior material. Also, since the appropriate water repellency is maintained by the surface of the water repellent silicone layer, the surface of the exterior material which is hardly stained permanently is formed.
【００３９】第４の実施態様の外装材は基材の裏面に透
明な接着材を塗布し、家屋、ビル等の外壁に貼着するこ
とにより、印刷層により美観が付与され、且つ恒久的に
汚れにくい表面を有する壁面を構成することができる。The exterior material of the fourth embodiment is applied with a transparent adhesive on the back surface of the base material, and is adhered to the outer wall of a house, a building, etc., so that the printed layer provides an aesthetic appearance and is permanently provided. It is possible to form a wall surface having a surface that is not easily contaminated.
【００４０】[0040]
【発明の効果】以上詳細に説明したように、本発明によ
れば、請求項１の外装材においては、表面は多数の開口
部を有する撥水性シリコーン層よりなり、前記開口部か
ら露出する光触媒が、雨が降り、或いは散水がかかった
後に日光があたるときに酸性物質を生じ、或いは、請求
項６に記載の外装材においては、撥水性シリコーン層の
表面に一部露出する光触媒は、雨が降り、或いは散水が
かかった後に日光があたるときに酸性物質を生じ、この
生じた酸性物質が表面に付着した汚れ成分、特に排気ガ
ス等の燃焼生成物や大気中に浮遊する煤煙等の汚れ成分
を分解する働きをし外装材の表面を清浄にする。As described above in detail, according to the present invention, in the exterior material of the first aspect, the surface is made of a water-repellent silicone layer having a large number of openings, and the photocatalyst exposed from the openings is provided. However, an acid substance is generated when it is exposed to sunlight after raining or watering, or the photocatalyst partially exposed on the surface of the water-repellent silicone layer in the exterior material according to claim 6, Acid substances are generated when sunlight falls after rainfall or watering, and the generated acidic substances contaminate the surface, especially dirt such as combustion products such as exhaust gas and soot floating in the atmosphere. It works to decompose the components and cleans the surface of the exterior material.
【００４１】したがってビル等の外壁に取り付けて、壁
に散水し、或いは雨水があたった後に太陽光線があたる
ことにより排気ガス等の燃焼生成物や大気中に浮遊する
煤煙などによる外壁に付着した汚れを容易に除くことが
できる。また撥水性シリコーン層の表面により適度の撥
水性が維持されるので、その結果恒久的に汚れにくくい
壁面を形成することができる。Accordingly, dirt attached to the outer wall of a building or the like due to combustion products such as exhaust gas or soot floating in the air due to spraying water on the wall or being exposed to sunlight after being exposed to rainwater. Can be easily removed. Further, since the appropriate water repellency is maintained by the surface of the water repellent silicone layer, it is possible to form a wall surface which is hardly stained permanently as a result.
【図１】図１は、本発明の第１の実施態様を示す断面図
である。FIG. 1 is a sectional view showing a first embodiment of the present invention.
【図２】図２は、本発明の第２の実施態様を示す断面図
である。FIG. 2 is a sectional view showing a second embodiment of the present invention.
【図３】図３は、本発明の第３の実施態様を示す断面図
である。FIG. 3 is a sectional view showing a third embodiment of the present invention.
【図４】図４は、本発明の第４の実施態様を示す断面図
である。FIG. 4 is a sectional view showing a fourth embodiment of the present invention.
１ 基材 ２ 光触媒粒子 ３ 耐食性樹脂層 ４ 開口部 ５ 撥水性シリコーン層 ６ 光触媒の光励起による親水化を防止するための物
質 ７ 印刷層 ８ 印刷保護層DESCRIPTION OF SYMBOLS 1 Base material 2 Photocatalyst particle 3 Corrosion-resistant resin layer 4 Opening 5 Water-repellent silicone layer 6 Substance for preventing hydrophilicity by photoexcitation of a photocatalyst 7 Printing layer 8 Printing protection layer
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4F100 AA02C AA02H AA21 AA23 AA25 AA28 AB15C AB15H AK01B AK25 AK41 AK52C AT00A BA02 BA03 BA04 BA05 BA07 BA10A BA10C CA30C DC11C DE01B DG01 EH46 GB07 HB00 HB00D JB02B JB05C JB05H JB06C JL06 JL08B JN01B JN01C ──────────────────────────────────────────────────の Continuing on the front page F term (reference) 4F100 AA02C AA02H AA21 AA23 AA25 AA28 AB15C AB15H AK01B AK25 AK41 AK52C AT00A BA02 BA03 BA04 BA05 BA07 BA10A BA10C CA30C DC11C DE01B DG01 EH46 J07JB05B06J06J07
Claims (8)
粒子の一部が表面に露出している透明な耐食性樹脂層を
設け、その上に多数の開口部を有する透明な撥水性シリ
コーン層を設け、前記撥水性シリコーン層は光励起によ
る親水化を防止する物質を含むことを特徴とする外装
材。1. A transparent water-repellent silicone layer comprising photocatalyst particles on the surface of a base material, a transparent corrosion-resistant resin layer having a part of the photocatalyst particles exposed on the surface, and a plurality of openings formed thereon. Wherein the water-repellent silicone layer contains a substance that prevents hydrophilicity due to light excitation.
され、その上に光触媒粒子を含む耐食性樹脂層が設けら
れていることを特徴とする請求項１に記載の外装材。2. The exterior material according to claim 1, wherein a printing layer and a printing protection layer are laminated on the surface of the base material, and a corrosion-resistant resin layer containing photocatalyst particles is provided thereon.
とを特徴とする請求項１又は２に記載の外装材。3. The exterior material according to claim 1, wherein the opening is formed in a porous shape.
とを特徴とする請求項１又は２に記載の外装材。4. The exterior material according to claim 1, wherein the opening is formed in a joint shape.
は、コバルト又はコバルト化合物であることを特徴とす
る請求項１乃至４の何れか１項に記載の外装材。5. The exterior material according to claim 1, wherein the substance that prevents hydrophilicity due to light excitation is cobalt or a cobalt compound.
シリコーンの前記光触媒の光励起による撥水性シリコー
ンの親水化を防止するための物質とを含有する透明な撥
水性シリコーン層が形成されており、前記表面層の表面
に前記光触媒粒子の一部が露出していることを特徴とす
る外装材。6. A transparent water-repellent silicone layer containing photocatalyst particles and a substance for preventing hydrophilicity of the water-repellent silicone by photoexcitation of the photocatalyst of the water-repellent silicone is formed on the surface of the base material. And a part of the photocatalyst particles is exposed on the surface of the surface layer.
され、その上に前記表面層が設けられている請求項６に
記載の外装材。7. The exterior material according to claim 6, wherein a printing layer and a printing protection layer are laminated on the surface of the base material, and the surface layer is provided thereon.
は、コバルト又はコバルト化合物であることを特徴とす
る請求項６又は７に記載の外装材。8. The cladding material according to claim 6, wherein the substance that prevents hydrophilicity due to light excitation is cobalt or a cobalt compound.