JP2002000639A - Pad for first-aid adhesive tape and first-aid adhesive tape using the same - Google Patents
Pad for first-aid adhesive tape and first-aid adhesive tape using the sameInfo
- Publication number
- JP2002000639A JP2002000639A JP2000190674A JP2000190674A JP2002000639A JP 2002000639 A JP2002000639 A JP 2002000639A JP 2000190674 A JP2000190674 A JP 2000190674A JP 2000190674 A JP2000190674 A JP 2000190674A JP 2002000639 A JP2002000639 A JP 2002000639A
- Authority
- JP
- Japan
- Prior art keywords
- pad
- adhesive
- layer
- backing material
- bandage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は救急絆創膏用パッ
ド、およびそれを用いた救急絆創膏に関するものであ
り、詳しくは切り傷や擦り傷などの創傷部位に貼付し、
痛みの軽減や創傷の治癒を行うための粘着パッドを有す
る救急絆創膏に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a first-aid bandage pad and a first-aid bandage using the same, and more specifically, is applied to a wound site such as a cut or abrasion.
The present invention relates to an emergency bandage having an adhesive pad for reducing pain and healing a wound.
【０００２】[0002]
【従来の技術】従来から救急絆創膏としては、粘着シー
トの粘着面の中央域にガーゼなどの布帛をパッドとして
載置し、このパッドを創傷部位に接するように貼着使用
している。しかしながら、創傷部位からの体液の滲出量
が多い場合には、このようなパッドでは吸液性が不充分
であり、吸液性の高い救急絆創膏の開発が要望されてい
る。2. Description of the Related Art Conventionally, as an emergency bandage, a cloth such as gauze is placed as a pad in the central area of the adhesive surface of an adhesive sheet, and this pad is used so as to be in contact with a wound site. However, when the amount of bodily fluid exuding from the wound site is large, such pads have insufficient liquid absorbability, and there is a demand for the development of an emergency bandage having high liquid absorbency.
【０００３】一方、このような体液滲出部に適した吸液
性の高い皮膚用貼付材として、ハイドロコロイド層を皮
膚接触部に用いたハイドロコロイドドレッシング材が開
発され、使用されている。On the other hand, a hydrocolloid dressing material using a hydrocolloid layer for a skin contacting part has been developed and used as a skin adhering material having a high liquid absorbing property suitable for such a body fluid exuding part.
【０００４】ハイドロコロイドドレッシング材は、支持
フィルムの片面に膏体層として体液吸液性を有する皮膚
接着層を有するものである。膏体層はその吸液性によっ
て貼付部位から滲出する体液を速やかに吸収するだけで
なく、貼付中に体温によって流動する性質、所謂コール
ドフロー性を有しているので、貼付部位の皮膚面形状に
次第に密着するようになり、皮膚接着性も良好なもので
ある。[0004] The hydrocolloid dressing material has a skin adhesive layer having a body fluid absorbing property as a plaster layer on one side of a support film. The plaster layer not only absorbs body fluid exuding from the application site due to its liquid absorption property, but also has a property of flowing due to body temperature during application, so-called cold flow property, so that the skin surface shape of the application site It gradually comes into close contact with the skin and has good skin adhesion.
【０００５】しかしながら、一般に市販されているハイ
ドロコロイドドレッシング材は、皮膚面に接触する膏体
層の吸液特性を重要視して開発されたものであるが、救
急絆創膏のパッド部に従来から用いられているハイドロ
コロイド層を用いると、一般にハイドロコロイド層と粘
着剤との接着性（投錨性）に欠け、また、支持体とハイ
ドロコロイド層が予め積層されたハイドロコロイドドレ
ッシング材を救急絆創膏のパッドに用いると、ハイドロ
コロイド層が多量に吸液すると、ハイドロコロイド層が
凝集破壊するだけでなく、支持体とハイドロコロイド層
との間の接着力（投錨力）が低下して、皮膚面から剥離
除去した際に、ハイドロコロイド層が皮膚面に残留する
という問題がある。[0005] However, a commercially available hydrocolloid dressing material has been developed with an emphasis on the liquid absorption properties of a plaster layer which comes into contact with the skin surface, but is conventionally used for a pad portion of an emergency bandage. When a hydrocolloid layer is used, the adhesive (anchoring property) between the hydrocolloid layer and the adhesive is generally lacking, and when a hydrocolloid dressing material in which a support and a hydrocolloid layer are preliminarily laminated is used for a pad of a rescue bandage, When the layer absorbs a large amount of liquid, not only does the hydrocolloid layer undergo cohesion and destruction, but also the adhesive force (anchoring force) between the support and the hydrocolloid layer decreases. There is a problem that it remains on the skin surface.
【０００６】[0006]
【発明が解決しようとする課題】以上のように、ハイド
ロコロイド層は救急絆創膏用のパッドとして優れた吸液
性を期待できるものではあるが、多量吸液した際、支持
体との投錨力の低下が著しいため、このような投錨力低
下を改善したパッドの開発が切望されている。As described above, although the hydrocolloid layer can be expected to have excellent liquid absorbency as a pad for an emergency bandage, when a large amount of liquid is absorbed, the hydrocolloid layer decreases the anchoring force with the support. Therefore, the development of a pad with an improved anchorage reduction has been desired.
【０００７】[0007]
【課題を解決するための手段】そこで、本発明者らは、
上記従来の課題を解決すべく鋭意検討を行なった結果、
特定の材質からなる支持体を用いることによって、吸液
後に皮膚面から救急絆創膏を剥離する時においてもハイ
ドロコロイド層が皮膚に残留せず、優れた投錨性を発揮
するパッドが得られることを見い出し、本発明を完成す
るに至った。Means for Solving the Problems Accordingly, the present inventors have:
As a result of intensive studies to solve the above conventional problems,
By using a support made of a specific material, the hydrocolloid layer does not remain on the skin even when the first-aid bandage is peeled off from the skin after liquid absorption, and it has been found that a pad that exhibits excellent anchoring properties can be obtained. The present invention has been completed.
【０００８】即ち、本発明は、裏打ち材としてのポリウ
レタンまたは合成ゴムからなる伸縮性布帛、もしくは線
状飽和ポリエステルからなる伸縮性フィルムの片面に、
自重の５０〜２５０重量％の吸水率を有するハイドロコ
ロイド層を形成したことを特徴とする救急絆創膏用パッ
ドを提供するものである。[0008] That is, the present invention relates to a stretchable fabric made of polyurethane or synthetic rubber as a backing material, or a stretchable film made of linear saturated polyester.
It is intended to provide an emergency bandage pad characterized by forming a hydrocolloid layer having a water absorption of 50 to 250% by weight of its own weight.
【０００９】さらに、本発明は、塩化ビニルフィルム、
ポリオレフィンフィルム、プラスチック製布帛などから
なる支持体の片面に、アクリル系またはゴム系の疎水性
粘着剤層を有する粘着シートの粘着剤塗布面の中央域
に、上記救急絆創膏用パッドを裏打ち材が粘着剤層に接
するように載置してなる救急絆創膏を提供するものであ
る。Further, the present invention provides a vinyl chloride film,
One side of a support made of polyolefin film, plastic cloth, etc., the backing material adheres the pad for emergency rescue plaster to the central area of the adhesive applied surface of the adhesive sheet having an acrylic or rubber-based hydrophobic adhesive layer. It is intended to provide an emergency bandage which is placed so as to be in contact with the agent layer.
【００１０】[0010]
【発明の実施の形態】本発明の救急絆創膏用パッドは、
ハイドロコロイド層を保持する裏打ち材として、ポリウ
レタンまたは合成ゴムからなる伸縮性布帛、もしくは線
状飽和ポリエステルからなる伸縮性フィルムが用いられ
る。ここで布帛とは、織布、不織布、編布などの布状の
ものを意味する。布帛は表面に凹凸を有して平面ではな
いので、膏体層が布帛表面から内部に食い込んで一般的
に投錨性が良好となる。しかしながら、その中でも上記
特定の素材からなる布帛がハイドロコロイド成分との馴
染みが良好であり、投錨性の向上が期待されるものであ
る。BEST MODE FOR CARRYING OUT THE INVENTION
As the backing material holding the hydrocolloid layer, a stretchable fabric made of polyurethane or synthetic rubber, or a stretchable film made of linear saturated polyester is used. Here, the cloth means a cloth-like material such as a woven fabric, a nonwoven fabric, and a knitted fabric. Since the cloth has irregularities on the surface and is not flat, the plaster layer cuts into the inside of the cloth from the surface to generally improve the anchoring property. However, among them, the cloth made of the above-mentioned specific material has good compatibility with the hydrocolloid component, and is expected to improve the anchoring property.
【００１１】一方、裏打ち材としてフィルムを用いた場
合には、表面が平滑であるので投錨性の向上は布帛の場
合ほど期待できないのが通例である。事実、ポリプロピ
レンやポリエチレン、エチレン／酢酸ビニル共重合体な
どの汎用されているポリオレフィンフィルムや、ポリエ
ーテル系ポリウレタンやポリエステル系ポリウレタンな
どのポリウレタンフィルム、ポリエーテルポリアミドな
どの熱可塑性エラストマーフィルムではハイドロコロイ
ド層との間で実用的な投錨性を得ることができず、フィ
ルムとしては線状飽和ポリエステルフィルムのみが本発
明の効果を発揮できるのである。On the other hand, when a film is used as the backing material, the surface is smooth, so that the anchoring property cannot be expected to be improved as much as that of a fabric. In fact, polyolefin films such as polypropylene, polyethylene, and ethylene / vinyl acetate copolymer, polyurethane films such as polyether-based polyurethane and polyester-based polyurethane, and thermoplastic elastomer films such as polyether-polyamide, have a hydrocolloid layer. Practical anchoring properties cannot be obtained between films, and only linear saturated polyester films can exhibit the effects of the present invention.
【００１２】また、ポリエステルフィルムは本発明に用
いるハイドロコロイド層との投錨性は良好であるが、ポ
リエチレンテレフタレートに代表される芳香族ポリエス
テルフィルムは伸縮性や柔軟性に乏しい傾向があり、本
発明のような湾曲部や屈曲部などの皮膚面に貼付する救
急絆創膏に用いた場合には、貼付中の密着性が悪く、ま
た、浮きや剥がれ、違和感などが生じて好ましくない。
また、芳香族ポリエステルフィルムの厚みを薄くして柔
軟性を付与することもできるが、製造工程における取扱
性に劣ると共に、機械的強度も不足するようになるので
好ましくない。従って、本発明で裏打ち材として用いる
ことができるフィルムとしては、伸縮性および柔軟性、
適度な機械的強度を兼備した線状飽和ポリエステルフィ
ルムを用いることが好ましいのである。Although the polyester film has a good anchoring property with the hydrocolloid layer used in the present invention, the aromatic polyester film represented by polyethylene terephthalate tends to have poor stretchability and flexibility. When used in an emergency bandage to be applied to the skin surface such as a curved portion or a bent portion, the adhesiveness during application is poor, and floating, peeling, uncomfortable feeling, etc. occur, which is not preferable.
In addition, flexibility can be imparted by reducing the thickness of the aromatic polyester film, but it is not preferable because handleability in the manufacturing process is poor and mechanical strength is insufficient. Therefore, as a film that can be used as a backing material in the present invention, stretchability and flexibility,
It is preferable to use a linear saturated polyester film having appropriate mechanical strength.
【００１３】上記のように本発明で用いることができる
線状飽和ポリエステルとしては、特に限定されるもので
はないが、具体的には東洋紡社製、商品名バイロンの溶
剤可溶グレードに代表されるガラス転移温度が８０℃以
下、好ましくは５〜７０℃の範囲のものが望ましく、ま
た、伸縮性や柔軟性、しなやかな風合いを付与するため
に非結晶性であることが好ましい。As described above, the linear saturated polyester which can be used in the present invention is not particularly limited, but is specifically represented by a solvent-soluble grade of trade name of Byron manufactured by Toyobo Co., Ltd. The glass transition temperature is desirably 80 ° C. or lower, preferably in the range of 5 to 70 ° C., and is preferably non-crystalline in order to impart elasticity and flexibility and a supple texture.
【００１４】さらに、線状飽和ポリエステルは一種類を
用いるのではなく、ガラス転移温度の異なる二種類をブ
レンドして用いることが好ましく、具体的にはガラス転
移温度が５〜１５℃の低ガラス転移温度の線状飽和ポリ
エステルと、ガラス転移温度が４５〜８０℃の高ガラス
転移温度の線状飽和ポリエステルとを１：９〜９：１、
最も好ましくは５：５の比率（重量比）でブレンドして
用いることが望ましいのである。Further, it is preferable that two kinds of linear saturated polyesters which are different in glass transition temperature be blended and used instead of using one kind. Specifically, a low glass transition temperature having a glass transition temperature of 5 to 15 ° C. is used. Temperature linear saturated polyester and a high glass transition temperature linear saturated polyester having a glass transition temperature of 45 to 80 ° C. in a ratio of 1: 9 to 9: 1,
Most preferably, it is desirable to use them in a blending ratio of 5: 5 (weight ratio).
【００１５】また、布帛として本発明の裏打ち材に用い
ることができる材質は、ポリウレタンおよび合成ゴムか
ら選ぶことができ、具体的にはポリウレタンとしては、
ポリエーテルポリウレタン、ポリエステルポリウレタン
などを用いることができる。合成ゴムとしては、スチレ
ン−イソプレン−スチレンブロック共重合体、スチレン
−ブタジエン−スチレンブロック共重合体、ポリエーテ
ルポリエステル、ポリエーテルポリアミドなどのゴム成
分を用いることができる。The material which can be used for the backing material of the present invention as a fabric can be selected from polyurethane and synthetic rubber.
Polyether polyurethane, polyester polyurethane, or the like can be used. As the synthetic rubber, rubber components such as styrene-isoprene-styrene block copolymer, styrene-butadiene-styrene block copolymer, polyether polyester, and polyether polyamide can be used.
【００１６】上記のような裏打ち材は布帛状のもので
は、坪量が１０〜７０ｇ／ｍ2 、好ましくは３０〜５０
ｇ／ｍ2 の範囲のものを、フィルム状のものでは１０〜
５０μｍ、好ましくは１５〜３５μｍの範囲のものを用
いることが、投錨性や柔軟性の維持などの点から望まし
いものである。The backing material as described above is a cloth-like material having a basis weight of 10 to 70 g / m 2 , preferably 30 to 50 g / m 2 .
g / m 2 range, and 10 to 10
It is desirable to use one having a thickness of 50 μm, preferably 15 to 35 μm, from the viewpoint of anchoring properties and maintenance of flexibility.
【００１７】本発明において上記裏打ち布帛または裏打
ちフィルムの片面に形成されるハイドロコロイド層は、
吸液性およびコールドフロー性を有するものである。本
発明においてコールドフロー性とは、人体の皮膚体温に
近い温度での「塑性流れ性」を有して皮膚に密着する性
質を云う。本発明において好ましいコールドフロー性を
有する膏体とは、以下に記載する試験方法において、７
２時間後に荷重負荷前の厚さの４０〜８０％、好ましく
は５０〜８０％に変化する程度の塑性変形を生じるもの
である。In the present invention, the hydrocolloid layer formed on one side of the backing fabric or backing film is
It has liquid absorbing properties and cold flow properties. In the present invention, cold flow refers to the property of having "plastic flow" at a temperature close to the skin temperature of a human body and adhering to the skin. In the present invention, a plaster having a preferable cold flow property is defined as 7 in the test method described below.
After 2 hours, plastic deformation occurs to a degree that changes to 40 to 80%, preferably 50 to 80% of the thickness before the load is applied.
【００１８】コールドフロー性の試験方法は、約３６ｍ
ｍφ×０．８〜２．５ｍｍ厚さに裁断した膏体サンプル
（ハイドロコロイド層）を、４０℃の雰囲気下、膏体の
厚み方向に２０ｇの荷重（１４ｇｆ／ｃｍ2 、１３．５
ｍｍφのオモリ）を負荷し、７２時間後の厚みを１０ｍ
ｍφの端子のダイヤルゲージで計測する。なお、計測時
には荷重を除いてからクリープ回復の起こらない１０秒
以内の測定を行う。The test method for the cold flow property is about 36 m
The plaster sample (hydrocolloid layer) cut to a thickness of 0.8 mm to 2.5 mm in thickness was applied with a load of 20 g (14 gf / cm 2 , 13.5) in the thickness direction of the plaster under an atmosphere of 40 ° C.
mmφ weight), and the thickness after 72 hours is 10 m
Measure with a dial gauge of mφ terminal. At the time of measurement, the measurement is performed within 10 seconds after the load is removed and no creep recovery occurs.
【００１９】本発明におけるハイドロコロイド層は自重
の５０〜２５０重量％、好ましくは１００〜２５０重量
％の吸水率を有するものを採用する。つまり、救急絆創
膏として体液を滲出する創傷部位に貼付した際に、ハイ
ドロコロイド層が上記のように多量の吸水率を発揮する
ことで、内部凝集力の低下が防止でき、皮膚面へのハイ
ドロコロイド層の残留や裏打ち材との投錨力が防止でき
る。The hydrocolloid layer used in the present invention has a water absorption of 50 to 250% by weight, preferably 100 to 250% by weight of its own weight. In other words, when applied to a wound site that exudes bodily fluids as an emergency bandage, the hydrocolloid layer exhibits a large amount of water absorption as described above, thereby preventing a decrease in internal cohesion and preventing the hydrocolloid layer from being applied to the skin surface. Residual and anchoring forces with the backing material can be prevented.
【００２０】ハイドロコロイド層の吸水率が自重の５０
重量％に満たない場合、即ち、飽和吸水時の重量が吸水
前の重量の１．５倍に満たない場合には、創傷部から滲
出する体液を充分に吸収しきれず、創傷部位が蒸れた状
態（白化状態）となり、治癒が遅れることがある。一
方、ハイドロコロイド層の吸水率が自重の２５０重量％
を超える場合、即ち、飽和吸水時の重量が吸水前の重量
の３．５倍を超えると、体液を吸収しすぎて、創傷部が
所謂、乾燥状態に近くなり、ハイドロコロイド層特有の
ウェットヒーリング効果を充分に発揮できなくなり、し
かも皮膚面との接着力も高くなる傾向を示し、救急絆創
膏を剥離する際に創傷部へダメージを与える恐れが生じ
る。The water absorption of the hydrocolloid layer is 50% of its own weight.
When the weight is less than 1.5% by weight, that is, when the weight at the time of saturated water absorption is less than 1.5 times the weight before water absorption, the body fluid exuding from the wound cannot be sufficiently absorbed, and the wound site is in a humid state. (Whitening) and healing may be delayed. On the other hand, the water absorption of the hydrocolloid layer is 250% by weight of its own weight.
In other words, when the weight at the time of saturated water absorption is more than 3.5 times the weight before water absorption, the body fluid is absorbed too much, and the wound part becomes close to a so-called dry state, and the wet healing effect peculiar to the hydrocolloid layer is obtained. And the adhesive strength to the skin surface tends to increase, and the wound may be damaged when the emergency bandage is peeled off.
【００２１】本発明における上記ハイドロコロイド層
は、吸液性や凝集力維持（糊残り防止性）の点から０．
１〜２ｍｍ、好ましくは０．２〜１ｍｍの厚みを有する
ように形成する。また、ハイドロコロイド層はその平面
的に見て中央部を厚く、周縁部は中央部よりも薄くし
て、厚みを異にするように形成することによって、周縁
側面部からの無用な吸湿を防止する点からも好ましい。
特に、中央部の厚みは０．２〜１ｍｍ、好ましくは０．
３〜０．７ｍｍとする。中央部の厚みが厚すぎると、皮
膚面に貼付した際に皮膚面の動きに追従するだけの柔軟
性がなく、使用中に浮きを起こすことがある。また、あ
まりに薄すぎると、体液の滲出部位に貼付した場合、充
分な吸液性を発揮しないおそれがある。一方、周縁部の
厚みがあまりに厚すぎると、側面部からの吸湿が大きく
なって、ハイドロコロイド層の体液などの吸液性が低下
したり、貼付中に端縁部がめくれやすく、また薄すぎる
と皮膚面に対する充分な接着性を確保できなくなった
り、貼付中に皺が入りやすくなる。The above-mentioned hydrocolloid layer in the present invention has a water-absorbing property and a cohesive strength maintenance (adhesive residue-preventing property).
It is formed so as to have a thickness of 1 to 2 mm, preferably 0.2 to 1 mm. In addition, the hydrocolloid layer is thicker at the central part when viewed in plan, and the peripheral part is made thinner than the central part so as to have a different thickness, thereby preventing unnecessary moisture absorption from the peripheral side part. It is also preferable from the viewpoint.
In particular, the thickness at the center is 0.2 to 1 mm, preferably 0.1 mm.
3 to 0.7 mm. If the thickness of the central portion is too large, there is no flexibility enough to follow the movement of the skin surface when applied to the skin surface, and the film may float during use. On the other hand, if it is too thin, it may not exhibit sufficient liquid absorbency when applied to a site where body fluids exude. On the other hand, if the thickness of the peripheral portion is too large, the moisture absorption from the side portion increases, and the liquid absorbing property of the body fluid and the like of the hydrocolloid layer is reduced, and the edge portion is easily turned up during application and is too thin. Sufficient adhesiveness to the skin surface cannot be ensured or wrinkles tend to occur during application.
【００２２】また、この周縁部に形成するハイドロコロ
イド層の厚みは均一にしてもよいが、貼付中の端縁部の
めくれを防ぎ、しかも貼付時や貼付中に皺などを生じず
に皮膚面に充分に密着固定させるためには、周縁部に形
成する皮膚接着層の厚みは端縁に向かって徐々に薄くな
るように傾斜させておくことが好ましい。The thickness of the hydrocolloid layer formed on the peripheral portion may be uniform, but it is possible to prevent the edge portion from being turned up during application and to prevent wrinkles or the like during application or application to the skin surface. In order to sufficiently adhere and fix the skin adhesive layer, it is preferable that the thickness of the skin adhesive layer formed on the peripheral portion is inclined so as to gradually decrease toward the edge.
【００２３】上記ハイドロコロイド層は吸液性およびコ
ールドフロー性を付与するために、所謂ハイドロコロイ
ドドレッシング材と同様の材料から形成することが好ま
しい。具体的には、エラストマー成分と吸湿性物質との
混合分散体とすることが望ましく、その比率はエラスト
マー成分４０〜７０重量％に対して吸湿性物質３０〜６
０重量％、好ましくは５０〜６５重量％：３５〜５０重
量％のように略同量、もしくは若干吸水性物質を多く配
合することが、皮膚貼着性や適度な保形性（側面からの
膏体のはみだし防止性）の点から望ましい。The above-mentioned hydrocolloid layer is preferably formed of a material similar to a so-called hydrocolloid dressing material in order to impart liquid absorbing property and cold flow property. Specifically, it is desirable to be a mixed dispersion of the elastomer component and the hygroscopic substance, and the ratio thereof is 40 to 70% by weight of the elastomer component and 30 to 6% by weight of the hygroscopic substance.
0% by weight, preferably 50 to 65% by weight: approximately the same amount such as 35 to 50% by weight, or a slight increase in the amount of the water-absorbing substance is sufficient for the adhesion to the skin and the appropriate shape retention (from the side). It is desirable from the viewpoint of preventing the plaster from protruding).
【００２４】このようなエラストマー成分は、ハイドロ
コロイド層に適度な凝集性と保形性を付与する成分であ
り、具体的にはポリイソブチレンやポリイソプレン、ア
クリル系重合体、スチレン／イソプレン／スチレンブロ
ック共重合体などが挙げられ、これらのうちの一種もし
くは二種以上を用いることができる。これら以外に使用
できるエラストマー成分としては、ポリブタジエン、ス
チレン／ブタジエン／スチレンブロック共重合体、天然
ゴム、ポリメチルシロキサンなどを主成分としたシリコ
ーン系重合体、ポリビニルエーテル系重合体などがあ
る。Such an elastomer component is a component for imparting appropriate cohesiveness and shape retention to the hydrocolloid layer. Specifically, polyisobutylene, polyisoprene, an acrylic polymer, and styrene / isoprene / styrene block copolymers are used. Examples thereof include polymers, and one or more of these can be used. Other elastomer components that can be used include polybutadiene, styrene / butadiene / styrene block copolymer, natural rubber, silicone-based polymer containing polymethylsiloxane as a main component, and polyvinyl ether-based polymer.
【００２５】一方、吸湿性物質はハイドロコロイド層に
吸液性を付与する成分であり、具体的にはカルボキシメ
チルセルロースナトリウム、デキストリン、ペクチン、
ゼラチンなどが挙げられ、これらのうちの一種もしくは
二種以上を用いることができる。これら以外に使用でき
る吸湿性物質としては、カルボキシメチルセルロースカ
ルシウム、ヒドロキシプロピルセルロース、グアーガ
ム、ローカストビーンガム、キサンタンガム、アルギン
酸ナトリウム、アルギン酸カルシウム、カラギーナン、
コラーゲン、ポリビニルピロリドンなどがある。On the other hand, the hygroscopic substance is a component that imparts a liquid absorbing property to the hydrocolloid layer, and specifically, sodium carboxymethylcellulose, dextrin, pectin,
Examples thereof include gelatin, and one or more of these can be used. Other hygroscopic substances that can be used include carboxymethylcellulose calcium, hydroxypropylcellulose, guar gum, locust bean gum, xanthan gum, sodium alginate, calcium alginate, carrageenan,
There are collagen, polyvinylpyrrolidone and the like.
【００２６】また、本発明におけるハイドロコロイド層
は、上記したようにエラストマー成分と吸湿性物質とを
含む混合分散体から形成されるが、内部凝集力を高める
ために架橋剤を適宜配合したり、γ線などの放射線を照
射してハイドロコロイド層全体に架橋処理を施してもよ
い。The hydrocolloid layer according to the present invention is formed from a mixed dispersion containing an elastomer component and a hygroscopic substance as described above. The entire hydrocolloid layer may be subjected to a crosslinking treatment by irradiating radiation such as a line.
【００２７】本発明におけるハイドロコロイド層には、
必要に応じてアクリノールや塩化ベンザルコニウム、銀
系化合物などの各種殺菌剤や抗菌剤などを適宜配合する
ことができる。これらの成分を配合することによって、
外部からの雑菌の侵入による化膿などを有効に防止する
ことができるのである。In the hydrocolloid layer of the present invention,
If necessary, various bactericides and antibacterial agents such as acrinol, benzalkonium chloride, and silver compounds can be appropriately compounded. By combining these components,
It is possible to effectively prevent suppuration caused by invasion of various bacteria from the outside.
【００２８】本発明の救急絆創膏用パッドは、上記構成
を必須成分とし、ハイドロコロイド層を保持する裏打ち
材が伸縮性と柔軟性を兼備した素材からなるものである
ので、救急絆創膏として皮膚面に貼付した場合に違和感
を与えずに貼付、使用することができる。The pad for an emergency bandage of the present invention has the above-mentioned composition as an essential component, and the backing material holding the hydrocolloid layer is made of a material having both elasticity and flexibility. It can be attached and used without giving a feeling of incompatibility.
【００２９】また、本発明では上記パッドを粘着シート
の粘着剤塗布面の中央域に載置することによって救急絆
創膏として用いることができる。つまり、従来の救急絆
創膏はパッド部がガーゼや不織布などからなるものが一
般的に用いられているが、吸液性や創傷部との癒着防止
性、雑菌の進入防止性が充分なものとはいえず、改善が
要望されており、本発明ではこれらの問題点を解決した
のである。In the present invention, the above-mentioned pad can be used as an emergency bandage by placing it on the central area of the pressure-sensitive adhesive applied surface of the pressure-sensitive adhesive sheet. In other words, conventional first-aid bandages generally use gauze or non-woven cloth as the pad, but it is not enough to absorb liquid, prevent adhesion to wounds, and prevent bacteria from entering. However, improvement has been demanded, and the present invention has solved these problems.
【００３０】上記の構成からなる本発明の救急絆創膏
は、ハイドロコロイド層を有する創傷部接触用パッドを
用いているので、優れた吸液性を有すると共に、コール
ドフロー性を有するために皮膚面に密着固定でき、外部
からの雑菌の進入を阻止することができる。また、ハイ
ドロコロイド層は吸液して皮膚接触面を湿潤状態に保つ
ので、所謂ウエットヒーリング効果が働き、創傷部の治
癒を促進すると共に、創傷部をきれいに治癒できる。さ
らに、ハイドロコロイド層は創傷部に癒着することがな
いので、皮膚面からの剥離もスムースであり、創傷部の
再損傷を起こすことがないのである。The first-aid bandage of the present invention having the above-mentioned structure uses a pad for contacting a wound portion having a hydrocolloid layer. It can be fixed and can prevent entry of various germs from outside. In addition, since the hydrocolloid layer absorbs the liquid and keeps the skin contact surface in a wet state, a so-called wet healing effect works to promote the healing of the wound and clean the wound. Further, since the hydrocolloid layer does not adhere to the wound, the exfoliation from the skin surface is smooth, and the wound is not re-damaged.
【００３１】上記本発明の救急絆創膏に用いる粘着シー
トは、支持体の片面にアクリル系もしくはゴム系の疎水
性粘着剤層を有するものであり、支持体としては特に限
定されず、ポリ塩化ビニルフィルムやポリエチレンフィ
ルム、ポリプロピレンフィルム、エチレン／プロピレン
共重合体フィルム、エチレン／酢酸ビニル共重合体フィ
ルムなどのポリオレフィンフィルム、ポリウレタンフィ
ルム、各種プラスチックからなる発泡体や布帛などを用
いることができる。これらのうち、衣服やシーツなどが
接触した際の滑り性、防水性などの点からポリ塩化ビニ
ルフィルム、ポリオレフィンフィルム、プラスチック製
布帛から選ばれる支持体を採用することが好ましい。支
持体の厚みは、通常、３０〜１５０μｍ、好ましくは５
０〜１００μｍ程度の範囲のものを用いることによって
柔軟性を阻害せず、貼付時の違和感を極力抑えた救急絆
創膏を得ることができる。The pressure-sensitive adhesive sheet used for the first-aid bandage of the present invention has an acrylic or rubber-based hydrophobic pressure-sensitive adhesive layer on one side of a support, and the support is not particularly limited. And polyethylene films, polypropylene films, polyolefin films such as ethylene / propylene copolymer films, ethylene / vinyl acetate copolymer films, polyurethane films, foams and fabrics made of various plastics, and the like. Among these, it is preferable to employ a support selected from a polyvinyl chloride film, a polyolefin film, and a plastic fabric in terms of slipperiness and waterproofness when clothes or sheets come into contact. The thickness of the support is usually 30 to 150 μm, preferably 5 to 150 μm.
By using one having a range of about 0 to 100 μm, it is possible to obtain an emergency bandage that does not impair flexibility and minimizes discomfort at the time of application.
【００３２】また、粘着シートに形成される粘着剤は、
一般に医療用粘着剤として用いられるものであれば特に
限定されるものではなく、例えばアクリルエステル系粘
着剤やゴム系粘着剤、シリコーン系粘着剤、ビニルエー
テル系粘着剤などの疎水性粘着剤を適宜用いることがで
きる。The pressure-sensitive adhesive formed on the pressure-sensitive adhesive sheet is
It is not particularly limited as long as it is generally used as a medical adhesive, and for example, a hydrophobic adhesive such as an acrylic ester adhesive or a rubber adhesive, a silicone adhesive, or a vinyl ether adhesive is appropriately used. be able to.
【００３３】以下に、本発明の救急絆創膏用パッドおよ
び救急絆創膏を得るための具体的な製造方法の一例を示
す。The following is an example of a specific production method for obtaining an emergency bandage pad and an emergency bandage of the present invention.
【００３４】片面を剥離処理したプラスチックシートや
紙などからなるセパレータの片面に、前記したハイドロ
コロイド層を形成するための材料を棒状に押し出した
り、一定の厚みで押し出すことにより押出塗工する。The material for forming the above-mentioned hydrocolloid layer is extruded in a bar shape or extruded to a certain thickness on one side of a separator made of a plastic sheet or paper having one side subjected to a release treatment, thereby performing extrusion coating.
【００３５】次いで、この押出塗工面に、ポリウレタン
または合成ゴムからなる伸縮性布帛や、線状飽和ポリエ
ステルフィルムなどの伸縮性裏打ち材を貼着加圧して、
セパレータから裏打ち材の片面にハイドロコロイド層を
転着してパッド用原反を作製する。このとき、ハイドロ
コロイド層が裏打ち材面へ充分に接着して強固な投錨性
をさらに発揮するように、裏打ち材のハイドロコロイド
層に接する側の表面をコロナ放電処理や下塗り処理など
によって４００μＮ／ｃｍ以上の濡れ性を有するように
処理しておくことが好ましい。なお、セパレータはハイ
ドロコロイド層の表面を被覆保護するために使用するま
で貼着状態とすることが好ましい。Next, a stretchable backing material such as a stretchable fabric made of polyurethane or synthetic rubber or a linear saturated polyester film is stuck on the extrusion coated surface and pressed.
A hydrocolloid layer is transferred from the separator to one surface of the backing material to produce a pad material. At this time, the surface of the backing material in contact with the hydrocolloid layer is subjected to a corona discharge treatment or an undercoating treatment so that the hydrocolloid layer adheres sufficiently to the backing material surface to exhibit a strong anchoring property. It is preferable to perform treatment so as to have wettability. In addition, it is preferable that the separator be in an adhered state until it is used to cover and protect the surface of the hydrocolloid layer.
【００３６】次に、別途粘着シートを作製しておき、こ
の粘着剤層面の中央域に上記パッド用原反から裁断した
救急絆創膏用パッドを載置し、裏打ち材背面を貼着、積
層して粘着補強された救急絆創膏を得ることができる。Next, a pressure-sensitive adhesive sheet is prepared separately, a pad for rescue adhesive bandage cut from the pad material is placed in the central area of the surface of the pressure-sensitive adhesive layer, and the back of the backing material is attached and laminated. An adhesively reinforced first aid bandage can be obtained.
【００３７】[0037]
【実施例】以下に本発明の実施例について具体的に説明
する。なお、以下の文中において部とあるのは重量部を
示すものである。DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of the present invention will be specifically described below. In the following description, “parts” means “parts by weight”.
【００３８】＜実施例１＞下記の表１にて示される配合
によって各原材料をニーダーで均一に混練し、Ｔダイ押
出加工機にて４００μｍ厚のハイドロコロイド層を作製
した。Example 1 Each raw material was uniformly kneaded with a kneader according to the composition shown in Table 1 below, and a 400 μm-thick hydrocolloid layer was prepared using a T-die extruder.
【００３９】[0039]
【表１】 [Table 1]
【００４０】次に、ガラス転移温度６７℃の線状飽和ポ
リエステル（東洋紡社製、商品名バイロン２０ＳＳ）
と、ガラス転移温度７℃の線状飽和ポリエステル（東洋
紡社製、商品名バイロン３０ＳＳ）を、トルエン／メチ
ルエチルケトンの混合溶剤にて等量で配合、溶解し、セ
パレータ上に塗工、乾燥させて、２０μｍ厚のフィルム
状の伸縮性裏打ち材を作製した。Next, a linear saturated polyester having a glass transition temperature of 67 ° C. (manufactured by Toyobo Co., Ltd., trade name: Byron 20SS)
And a linear saturated polyester having a glass transition temperature of 7 ° C. (manufactured by Toyobo Co., Ltd., trade name: Byron 30SS) is mixed and dissolved in an equal amount with a mixed solvent of toluene / methyl ethyl ketone, coated on a separator, and dried. A 20 μm thick film-like stretchable backing material was produced.
【００４１】上記のようにして得られたハイドロコロイ
ド層を、線状飽和ポリエステルフィルムからなる伸縮性
裏打ち材の片面に貼り合わせて、本発明の救急絆創膏用
パッド原反を作製した。The hydrocolloid layer obtained as described above was bonded to one side of a stretchable backing material composed of a linear saturated polyester film to prepare a raw material for a rescue bandage of the present invention.
【００４２】上記のようにして得られたパッド原反を１
５ｍｍ×３０ｍｍ角の大きさに打ち抜き加工し、これを
アクリル酸２−エチルヘキシルエステル／アクリル酸共
重合体からなるアクリル酸アルキルエステル系粘着剤層
（５０μｍ厚）をポリウレタンフィルム（５０μｍ厚）
の片面に形成した粘着シートの粘着剤層の中央部に載置
し、セパレータをハイドロコロイド層の表面に被覆し、
これを図１に示す形状（外寸２４ｍｍ×７２ｍｍ）に打
ち抜き加工して、本発明の救急絆創膏を作製した。The pad material obtained as described above was
Punched to a size of 5 mm x 30 mm square, and this was used to form a 2-ethylhexyl acrylate / acrylic acid copolymer-based alkyl acrylate-based pressure-sensitive adhesive layer (50 μm thick) into a polyurethane film (50 μm thick).
Placed on the center of the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet formed on one side of, the separator is coated on the surface of the hydrocolloid layer,
This was stamped into the shape shown in FIG. 1 (outside dimensions 24 mm × 72 mm) to produce an emergency bandage of the present invention.
【００４３】＜実施例２＞実施例１におけるゼラチン／
ペクチン／カルボキシメチルセルロースＮａの量を１７
部／１７部／１７部とした以外は、実施例１と同様にし
て本発明の救急絆創膏を作製した。<Example 2> The gelatin /
Reduce the amount of pectin / carboxymethylcellulose Na to 17
A first-aid bandage of the present invention was prepared in the same manner as in Example 1, except that the parts / 17 parts / 17 parts were used.
【００４４】＜実施例３＞実施例１におけるゼラチン／
ペクチン／カルボキシメチルセルロースＮａの量を８部
／８部／８部とした以外は、実施例１と同様にして本発
明の救急絆創膏を作製した。<Example 3> The gelatin /
An emergency bandage of the present invention was produced in the same manner as in Example 1, except that the amount of pectin / carboxymethylcellulose Na was changed to 8 parts / 8 parts / 8 parts.
【００４５】＜実施例４＞実施例１における伸縮性裏打
ち材を、坪量２５ｇ／ｍ2 のポリウレタン不織布とした
以外は、実施例１と同様にして、本発明の救急絆創膏を
作製した。Example 4 An emergency bandage of the present invention was produced in the same manner as in Example 1 except that the elastic backing material in Example 1 was a polyurethane nonwoven fabric having a basis weight of 25 g / m 2 .
【００４６】＜実施例５＞実施例１における伸縮性裏打
ち材を、坪量２５ｇ／ｍ2 の合成ゴム系不織布（ＳＥＢ
Ｓ：スチレン−エチレン−ブチレン−スチレンブロック
共重合体）とした以外は、実施例１と同様にして、本発
明の救急絆創膏を作製した。<Example 5> The elastic backing material of Example 1 was replaced with a synthetic rubber nonwoven fabric (SEB) having a basis weight of 25 g / m 2.
S: Styrene-ethylene-butylene-styrene block copolymer) was prepared in the same manner as in Example 1 to prepare an emergency bandage of the present invention.
【００４７】＜比較例１＞実施例１におけるゼラチン／
ペクチン／カルボキシメチルセルロースＮａの量を２０
部／２０部／２０部とした以外は、実施例１と同様にし
て救急絆創膏を作製した。<Comparative Example 1>
The amount of pectin / carboxymethylcellulose Na is 20
A first-aid bandage was prepared in the same manner as in Example 1 except that parts / 20 parts / 20 parts were used.
【００４８】＜比較例２＞実施例１におけるゼラチン／
ペクチン／カルボキシメチルセルロースＮａの量を５部
／５部／５部とした以外は、実施例１と同様にして救急
絆創膏を作製した。<Comparative Example 2>
An emergency bandage was prepared in the same manner as in Example 1 except that the amount of pectin / carboxymethylcellulose Na was changed to 5 parts / 5 parts / 5 parts.
【００４９】＜比較例３＞実施例１における伸縮性裏打
ち材を、２０μｍ厚のポリウレタンフィルムとした以外
は、実施例１と同様にして、救急絆創膏を作製した。Comparative Example 3 An emergency bandage was prepared in the same manner as in Example 1 except that the elastic backing material in Example 1 was a polyurethane film having a thickness of 20 μm.
【００５０】＜比較例４＞実施例１におけるパッドをハ
イドロコロイド層ではなく、一般低に用いられているガ
ーゼとし、粘着シートの支持体をポリウレタンフィルム
ではなく、穴あけ加工を施した８０μｍ厚のポリエチレ
ンフィルムとした以外は、実施例１と同様にして救急絆
創膏を作製した。<Comparative Example 4> The pad in Example 1 was not a hydrocolloid layer, but gauze commonly used, and the support of the pressure-sensitive adhesive sheet was not a polyurethane film but a perforated polyethylene film of 80 μm thickness. Except for that, an emergency bandage was prepared in the same manner as in Example 1.
【００５１】上記各実施例および各比較例にて作製した
救急絆創膏について、以下の方法で吸水率を測定し、そ
の結果を表２に記載した。The water absorption of the first-aid bandages prepared in the above Examples and Comparative Examples was measured by the following method. The results are shown in Table 2.
【００５２】＜吸水率測定＞一定重量のハイドロコロイ
ド層を吸水前に秤量し、大容量の３７℃生理食塩水中に
投入し、４時間経過後の重量変化率を測定し、これを吸
水率とした。なお、生理食塩水中へ４時間投入すると、
吸水は略平衡状態になっていた。<Water Absorption Measurement> A constant weight hydrocolloid layer was weighed before water absorption, poured into a large volume of physiological saline at 37 ° C., and the weight change after 4 hours was measured. . In addition, when put into physiological saline for 4 hours,
Water absorption was in a substantially equilibrium state.
【００５３】さらに、上記吸水率測定した後の救急絆創
膏について、裏打ち材との投錨性、皮膚面への接着性、
皮膚面への糊残り性、皮膚面の白化性を、以下の基準で
調べて結果を表２に併記した。Further, with respect to the first-aid bandage after measuring the water absorption, the anchoring property with the backing material, the adhesive property to the skin surface,
The adhesive residue on the skin and the whitening of the skin were examined according to the following criteria, and the results are shown in Table 2.
【００５４】 〇 ：良好。 〇△：やや良好。 △ ：やや不良。 × ：不良。〇: good. 〇 △: Somewhat good. Δ: Somewhat poor. X: defective.
【００５５】なお、皮膚面への接着性、糊残り性、白化
性は、吸水率測定をした後の救急絆創膏を、ボランティ
アの下腕部内側の皮膚面に２４時間貼付したときの状態
を観察した。The adhesiveness to the skin, adhesive residue, and whitening were evaluated by observing the condition when the emergency bandage after measuring the water absorption was applied to the skin inside the lower arm of the volunteer for 24 hours. did.
【００５６】[0056]
【表２】 [Table 2]
【００５７】上記表２の結果から明らかなように、実施
例品は比較例品と比べて、評価した全ての特性の何れか
で優位性を示し、比較例品よりも劣る特性はなかった。
また、実施例１品と比較例４品を用いて、擦り傷部位に
実際に貼付使用したところ、実施例１品はパッド内への
水の侵入は全くなく、擦り傷も３日ほどで完治した。一
方、比較例４品ではパッド内に水が侵入するために、貼
付中は傷口がジクジクした状態であり、治りが遅く、比
較例４品を剥離して自然乾燥させることで完治したが、
きれいに治らなかった。As is clear from the results shown in Table 2, the product of the example exhibited superiority in any of the evaluated properties as compared with the product of the comparative example, and there was no characteristic inferior to the product of the comparative example.
In addition, when the product of Example 1 and the product of Comparative Example 4 were actually applied to the abrasion site and used, the product of Example 1 did not invade water into the pad at all, and the abrasion was completely cured in about 3 days. On the other hand, in the case of the product of Comparative Example 4, since the water penetrated into the pad, the wound was in a state of being jerky during the application, healing was slow, and the product was completely cured by peeling off the product of Comparative Example 4 and allowing it to dry naturally.
Did not heal cleanly.
【００５８】[0058]
【発明の効果】本発明の救急絆創膏用パッドおよび救急
絆創膏は以上のように、極めて優れた投錨性の向上効果
を発揮する特定の支持体の片面にハイドロコロイド層を
形成してなるものであるので、皮膚面、特に創傷部位の
ような体液滲出部位に対して優れた密着性、および吸液
性を有すると共に、貼付使用後に皮膚面から剥離除去す
る際にもハイドロコロイド層のみが皮膚面に残らない
（糊残り現象を生じない）という効果を発揮するもので
ある。As described above, the pad for emergency bandage and the bandage of the present invention are formed by forming a hydrocolloid layer on one surface of a specific support exhibiting an extremely excellent anchoring property improving effect. It has excellent adhesiveness to the skin surface, especially to the bodily fluid exudation site such as a wound site, and liquid absorption, and only the hydrocolloid layer does not remain on the skin surface when peeled off from the skin surface after application. (No adhesive residue phenomenon occurs).
【００５９】[0059]
【図１】 本発明の救急絆創膏の一実例を示す平面図で
ある。FIG. 1 is a plan view showing an example of an emergency bandage of the present invention.
【図２】 図１に示す救急絆創膏のＸ−Ｘ’線での断面
図である。FIG. 2 is a cross-sectional view taken along line XX ′ of the emergency bandage shown in FIG.
１ 裏打ち材 ２ ハイドロコロイド層 ３ 粘着シート（支持体と粘着剤層との積層体） ３１ 粘着シートの支持体 ３２ 粘着剤層 REFERENCE SIGNS LIST 1 backing material 2 hydrocolloid layer 3 adhesive sheet (laminated body of support and adhesive layer) 31 support of adhesive sheet 32 adhesive layer
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4C081 AA03 AA12 BB01 BB04 BC02 CA031 CA062 CA121 CB012 CB042 CB051 CD012 CD022 CD032 CD042 CD152 DA02 DA12 DC03 DC12 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 4C081 AA03 AA12 BB01 BB04 BC02 CA031 CA062 CA121 CB012 CB042 CB051 CD012 CD022 CD032 CD042 CD152 DA02 DA12 DC03 DC12
Claims (6)
成ゴムからなる伸縮性布帛、もしくは線状飽和ポリエス
テルからなる伸縮性フィルムの片面に、自重の５０〜２
５０重量％の吸水率を有するハイドロコロイド層を形成
したことを特徴とする救急絆創膏用パッド。An elastic fabric made of polyurethane or synthetic rubber as a backing material or an elastic film made of a linear saturated polyester is coated on one side with a weight of 50 to 2%.
A pad for an emergency bandage, wherein a hydrocolloid layer having a water absorption of 50% by weight is formed.
分と吸湿性物質とを含む混合分散体である請求項１記載
の救急絆創膏用パッド。2. The pad for emergency bandage according to claim 1, wherein the hydrocolloid layer is a mixed dispersion containing an elastomer component and a hygroscopic substance.
ン、ポリイソプレン、スチレン／イソプレン／スチレン
ブロック共重合体から選ばれる少なくとも一種である請
求項２記載の救急絆創膏用パッド。3. The adhesive bandage pad according to claim 2, wherein the elastomer component is at least one selected from polyisobutylene, polyisoprene, and styrene / isoprene / styrene block copolymer.
ースナトリウム、ポリビニルピロリドン、アルギン酸ナ
トリウム、デキストリン、ペクチン、ゼラチンから選ば
れる少なくとも一種である請求項２記載の救急絆創膏用
パッド。4. The pad for emergency bandage according to claim 2, wherein the hygroscopic substance is at least one selected from sodium carboxymethylcellulose, polyvinylpyrrolidone, sodium alginate, dextrin, pectin, and gelatin.
の疎水性粘着剤層を有する粘着シートの粘着剤塗布面の
中央域に、請求項１記載の救急絆創膏用パッドを、裏打
ち材が粘着剤層に接するように載置してなる救急絆創
膏。5. An adhesive sheet having an acrylic or rubber-based hydrophobic pressure-sensitive adhesive layer on one surface of a support, a central area of the pressure-sensitive adhesive applied surface of the pressure-sensitive adhesive sheet, and the backing material is adhered to the adhesive bandage pad according to claim 1. Emergency bandage placed in contact with the drug layer.
フィンフィルム、プラスチック製布帛から選ばれる請求
項５記載の救急絆創膏。6. The emergency bandage according to claim 5, wherein the support is selected from a vinyl chloride film, a polyolefin film, and a plastic fabric.