JP2001120248A - Filter tip - Google Patents
Filter tipInfo
- Publication number
- JP2001120248A JP2001120248A JP30175799A JP30175799A JP2001120248A JP 2001120248 A JP2001120248 A JP 2001120248A JP 30175799 A JP30175799 A JP 30175799A JP 30175799 A JP30175799 A JP 30175799A JP 2001120248 A JP2001120248 A JP 2001120248A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- filter
- fiber
- tobacco
- tobacco filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、喫煙用のたばこフ
ィルター、さらに詳しくは、濾過率が高く、喫味に優れ
たたばこフィルターに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a tobacco filter for smoking, and more particularly, to a tobacco filter having a high filtration rate and excellent taste.
【０００２】[0002]
【従来の技術】近年の健康指向にともない、たばこ喫煙
者の嗜好が高タール製品から低タール製品へ移行してい
る。このような低タール製品用のたばこフィルターとし
ては、繊維比表面積を大きくするために単繊維繊度のよ
り細いトウ繊維を使用する方法やパルプ素材を用いて高
濾過を狙ったもの等が挙げられる。また、これらトウ繊
維とパルプ素材の両方を使用したフィルター素材として
は、特開昭５５−１４１１８５号公報が知られている。2. Description of the Related Art Tobacco smokers are shifting from high tar products to low tar products in accordance with recent health trends. Examples of such tobacco filters for low tar products include a method using a finer tow fiber having a single fiber fineness in order to increase the specific surface area of the fiber, and a filter aiming at high filtration using a pulp material. JP-A-55-141185 discloses a filter material using both tow fiber and pulp material.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、特開昭
５５−１４１１８５号公報に記載の発明では、フィルタ
ーを構成する木材パルプ繊維を主とするシート状物の物
性に関して、比容積が６〜２５ｃｍ3／ｇ、比表面積０.
８ｍ2／ｇ以上の嵩高性シート状物を掲げられている。
この数値範囲のシート状物を用いれば通気抵抗が低く、
濾過効率の高いフィルター素材を得ることはできるが、
有害性分と共に香喫味成分の除去効果も高くなり、香喫
味に優れたフィルターとはなりにくい。また、比容積の
大きなシート状物を使用することは、フィルターとした
ときの硬度の発現性が低くなり、たばこフィルターとし
ての機能を発揮できず、さらに、その硬度の発現性を補
うために可塑剤添着量を増やすことは、ますます喫味を
悪くする原因となり問題である。本発明は前記課題を解
決するためになされたもので、香喫味を損なわずに、有
害成分の濾過効率が高く、硬度の発現性にも優れたたば
こフィルターを目的とする。However, in the invention described in Japanese Patent Application Laid-Open No. 55-141185, the specific volume of the sheet-like material mainly composed of wood pulp fibers constituting the filter is 6 to 25 cm 3. / G, specific surface area
A bulky sheet material having a volume of 8 m 2 / g or more is listed.
If a sheet-like material in this numerical range is used, the ventilation resistance is low,
Although it is possible to obtain a filter material with high filtration efficiency,
The effect of removing flavor components is increased together with the harmful components, and it is difficult to obtain a filter having excellent flavor. In addition, the use of a sheet-shaped material having a large specific volume results in a low degree of expression of hardness when used as a filter, cannot function as a tobacco filter, and has a plasticity to supplement the expression of hardness. Increasing the amount of agent impregnated causes a worsening of the taste, which is a problem. The present invention has been made in order to solve the above-mentioned problems, and an object of the present invention is to provide a tobacco filter which has high filtering efficiency of harmful components and excellent hardness development without impairing flavor.
【０００４】[0004]
【課題を解決するための手段】本発明のたばこフィルタ
ーは、厚さが５０〜１４０μｍで、坪量が２５〜４０ｇ
／ｍ2である木材パルプ繊維からなるシート状物と、繊
維トウからなるシート状物とがバインダーを介して接合
された複合シート状物よりなることを特徴とするもので
ある。ここで、木材パルプ繊維からなるシート状物は、
紙、特に、クレープ紙が望ましい。また、繊維トウから
なるシート状物は、セルロースアセテート繊維からなる
ものが望ましい。また、バインダーはトリアセチンが望
ましい。複合シート状物はコルゲート加工されたものが
望ましい。木材パルプ繊維からなるシート状物の質量／
繊維トウからなるシート状物の質量の割合は、４／６〜
６／４であることが望ましい。バインダーの添加量は、
複合シート状物の質量に対して２〜６％であることが望
ましい。The tobacco filter of the present invention has a thickness of 50 to 140 μm and a basis weight of 25 to 40 g.
/ M 2 , and a composite sheet formed by bonding a sheet made of wood pulp fiber and a sheet made of fiber tow with a binder interposed therebetween. Here, the sheet-like material made of wood pulp fiber is
Paper, especially crepe paper, is preferred. The sheet-like material made of fiber tow is preferably made of cellulose acetate fiber. The binder is preferably triacetin. The composite sheet is desirably corrugated. Weight of sheet material made of wood pulp fiber /
The ratio of the mass of the sheet-like material made of fiber tow is 4/6 to
It is preferably 6/4. The amount of binder
It is desirable that the content is 2 to 6% based on the mass of the composite sheet.
【０００５】[0005]
【発明の実施の形態】［木材パルプ繊維からなるシート
状物］たばこフィルター材として用いるシート状物とし
ては、木材パルプ繊維を抄紙して得られる紙や、湿紙を
プレスロール又はヤンキードライヤーなどの上で、ドク
ターを用いてしわを付けたクレープ紙、ニードルパン
チ、ウォータージェットなどによる不織シートが使用で
き、フィルターとしての濾過機能を有する点から好まし
いのは嵩高性のある紙や、クレープ紙が好ましい。ま
た、シート状物の厚さ、坪量がフィルターとして用いた
ときの性能に影響を及ぼし、好ましいのは、フィルター
の通気抵抗と硬度の発現性が良好となる点から、厚さが
５０〜１４０μｍで、坪量が２５〜４０ｇ／ｍ2である
シート状物が好ましい。さらに、使用するシート状物が
複数枚からなるものであっても、重ねた状態で、上記範
囲内にあるものであれば、用いることは可能である。DESCRIPTION OF THE PREFERRED EMBODIMENTS [Sheet-like material made of wood pulp fiber] As a sheet-like material used as a tobacco filter material, a paper obtained by making wood pulp fiber or a wet paper such as a press roll or a Yankee dryer is used. On the above, crepe paper wrinkled with a doctor, non-woven sheet by needle punch, water jet, etc. can be used, and from the viewpoint of having a filtering function as a filter, bulky paper or crepe paper is preferable. preferable. Further, the thickness of the sheet-like material, the basis weight affects the performance when used as a filter, and the thickness is preferably from 50 to 140 μm from the viewpoint that the airflow resistance and hardness of the filter become more favorable. And a sheet-like material having a basis weight of 25 to 40 g / m 2 is preferable. Further, even if a plurality of sheets are used, they can be used as long as they are within the above range in a stacked state.
【０００６】［繊維トウからなるシート状物］繊維トウ
からなるシート状物とは、繊維の束である繊維トウを開
繊してシート状物としたものであり、たばこフィルター
材として用いる繊維トウとしては、フィルター製造の安
定性、たばこの喫味の点からセルロースアセテート繊維
トウであることが好ましい。 ［バインダー］パルプ繊維からなるシート状物と繊維ト
ウからなるシート状物を接合するために使用されるバイ
ンダーとしては、繊維トウを開繊したシート状物に均一
にスプレー、転写等により添着させることにより繊維ト
ウを可塑化させ、パルプ繊維からなるシート状物と全面
的に接合することができるものであれば、特に制限はな
いが、均一に付着することの容易性から液状のものが好
ましく、特にトリアセチンがたばこの喫味の点から好ま
しい。バインダーの添加量は、複合シート状物となった
ときの質量に対して２〜６％の質量を有することが好ま
しい。上記範囲より少ない場合には、接合が弱く、パル
プ繊維からなるシート状物と繊維トウからなるシート状
物が分離してしまい、たばこフィルターを製造すること
が困難となるか、製造できたとしてもフィルター中に２
つの素材が分離した状態で存在するため、フィルターの
性能が均一なたばこフィルターとはならない。また、上
記範囲より多い場合には、複合シート状物のシート化が
進みすぎるため、フィルター中に空隙部が発生し、品質
のバラツキが大きくなり好ましくない。また、喫味の点
からもバインダーの添加量は少ない方がよい。[Sheet-like material made of fiber tow] The sheet-like material made of fiber tow is obtained by opening fiber tow, which is a bundle of fibers, into a sheet-like material, and is used as a tobacco filter material. From the viewpoint of filter production stability and tobacco taste, cellulose acetate fiber tow is preferred. [Binder] As a binder used for joining a sheet made of pulp fiber and a sheet made of fiber tow, the fiber tow is uniformly attached to the opened sheet by spraying, transferring, or the like. There is no particular limitation as long as it can plasticize the fiber tow and can be entirely bonded to the sheet-like material made of pulp fiber, but a liquid material is preferable because of its ease of uniform attachment. In particular, triacetin is preferred from the viewpoint of tobacco taste. The amount of the binder to be added is preferably 2 to 6% by mass based on the mass of the composite sheet. If less than the above range, the bonding is weak, the sheet-like material made of pulp fiber and the sheet-like material made of fiber tow are separated, and it becomes difficult to produce a tobacco filter, or even if it can be produced. 2 in the filter
Since the two materials are present in a separated state, the filter performance is not a uniform tobacco filter. On the other hand, when the amount is larger than the above range, the composite sheet is excessively formed into a sheet, so that voids are generated in the filter, and the variation in quality is unfavorably increased. Also, from the viewpoint of taste, the smaller the amount of the binder added, the better.
【０００７】［複合シート状物］パルプ繊維からなるシ
ート状物と繊維トウからなるシート状物が接合して形成
された複合シート状物は、円棒状のフィルターに賦形す
る際の安定性からコルゲート加工された複合シート状物
であることが好ましい。図１に、コルゲート加工した複
合シート状物１０の断面を示す。このコルゲート加工し
たシート状物の深さｄは、例えば０.２〜２ｍｍ、また
隣接する溝同士の間隔である溝間ピッチｐは０.５〜３
ｍｍとされる。前記ｄが０.２ｍｍ未満であったり、あ
るいは、前記ｐが０.５ｍｍ未満である場合、波が細か
すぎてコルゲート化することが困難となる。また、前記
ｄが２ｍｍを越えて深いもの、あるいは、前記ｐが３ｍ
ｍを越えて大きいものは収束性良好なコルゲート加工し
た複合構造シート状物となりにくい。また、本発明にお
いて、パルプ繊維からなるシート状物６と繊維トウから
なるシート状物３とは種々の割合で接合することができ
るが、濾過効率が高く、香喫味に優れたたばこフィルタ
ーとする場合は、木材パルプ繊維からなるシート状物の
質量／繊維トウからなるシート状物の質量の割合が４／
６〜６／４で接合されていることが好ましい。[Composite sheet-like material] A composite sheet-like material formed by joining a sheet-like material composed of pulp fibers and a sheet-like material composed of a fiber tow has a high stability in shaping into a circular filter. It is preferably a corrugated composite sheet. FIG. 1 shows a cross section of a corrugated composite sheet material 10. The depth d of the corrugated sheet is, for example, 0.2 to 2 mm, and the pitch p between the adjacent grooves is 0.5 to 3, for example.
mm. If d is less than 0.2 mm or p is less than 0.5 mm, the waves are too fine to corrugate. Further, the above-mentioned d is deeper than 2 mm, or the above-mentioned p is 3 m
Those larger than m are unlikely to be corrugated composite structure sheets having good convergence. In addition, in the present invention, the sheet-like material 6 made of pulp fiber and the sheet-like material 3 made of fiber tow can be joined at various ratios, but a tobacco filter having high filtration efficiency and excellent flavor and taste can be obtained. In this case, the ratio of the mass of the sheet made of wood pulp fiber / the mass of the sheet made of fiber tow is 4 /
It is preferable that they are joined at 6 to 6/4.
【０００８】［製法例］本発明のたばこフィルターは例
えば以下のようにして製造することができる。図２にた
ばこフィルターを製造する装置例を概略図で示す。繊維
トウ１はベール１２より引き出され、開繊装置２によっ
てシート状に開繊されシート状物３となり、デリベリー
ロール４により送り出され、その際にトリアセチン等の
バインダーをロール転写により均一に添着した後、別に
設置されたロール支持装置５から供給される木材パルプ
繊維からなるシート状物６と同じ幅で接合される。次い
でコルゲート加工装置７に送られてコルゲート加工され
る。コルゲート加工装置７は、多数の溝を有する上下２
本のニップロールより成り立っており、上下のロールの
溝が互いに噛合し、約１ｍｍ以下の厚さでそのクリアラ
ンスを調整できる機能を有するとともに、所定の圧力で
加圧する能力と、所定の温度で熱成型する能力を備えて
いるものならば、いずれの装置をも用いることができ
る。コルゲート加工された複合シート状物はエキストラ
ロール８により引き出され、フィルタープラグマシン９
にて本発明のたばこフィルターに加工されるコルゲート
加工装置７のロール間のクリアランス、圧力、および温
度、図１に示す複合シート状物の溝ピッチｐおよび溝深
さｄは、得られるたばこフィルターの特性を決めるの
で、製造するたばこフィルターの特性に合わせて決定す
るのがよい。コルゲートロール間のクリアランスは０.
５ｍｍ以下、ロール間圧力は０.０５〜０.６ＭＰａの範
囲、温度は６０〜１８０℃の範囲とするのが好ましく、
コルゲート加工した複合シート状物の溝ピッチｐが０.
５〜３ｍｍ、溝深さｄが０.２〜２ｍｍなる範囲が好ま
しい。コルゲート加工装置７のロール間のクリアランス
が０.５ｍｍを越える場合、温度が８０℃未満の場合に
は、コルゲート加工した複合シート状物とするのが困難
であり、コルゲート熱成型装置の温度が１８０℃を越え
る場合には、逆にシート化が進みすぎ、十分な吸引抵抗
を保ったフィルター部材とすることが困難になるととも
に、コルゲートシートの製造安定性が悪くなり、結果と
してフィルター素材としての性能が低下するので好まし
くない。[Example of Production Method] The tobacco filter of the present invention can be produced, for example, as follows. FIG. 2 is a schematic view showing an example of an apparatus for manufacturing a tobacco filter. The fiber tow 1 is pulled out from the bale 12 and spread into a sheet by the fiber opening device 2 to form a sheet material 3, which is sent out by a delivery roll 4, and in which a binder such as triacetin is uniformly applied by roll transfer. After that, it is joined with the same width as the sheet material 6 made of wood pulp fiber supplied from the separately installed roll supporting device 5. Next, it is sent to the corrugating device 7 and corrugated. The corrugating device 7 has an upper and lower 2 having a large number of grooves.
It consists of nip rolls, and the grooves of the upper and lower rolls mesh with each other and have the function of adjusting the clearance with a thickness of about 1 mm or less, the ability to pressurize at a predetermined pressure, and the thermoforming at a predetermined temperature. Any device that has the ability to do so can be used. The corrugated composite sheet material is pulled out by the extra roll 8 and the filter plug machine 9
The clearance, pressure, and temperature between the rolls of the corrugating apparatus 7 to be processed into the tobacco filter of the present invention, the groove pitch p and the groove depth d of the composite sheet shown in FIG. Since the characteristics are determined, it is preferable to determine the characteristics according to the characteristics of the tobacco filter to be manufactured. Clearance between corrugated rolls is 0.
5 mm or less, the pressure between the rolls is preferably in the range of 0.05 to 0.6 MPa, and the temperature is preferably in the range of 60 to 180 ° C.
The groove pitch p of the corrugated composite sheet is 0.
Preferably, the range is 5 to 3 mm and the groove depth d is 0.2 to 2 mm. When the clearance between the rolls of the corrugating device 7 exceeds 0.5 mm, and when the temperature is less than 80 ° C., it is difficult to obtain a corrugated composite sheet-like material. If the temperature exceeds ℃, the sheeting will progress too much, and it will be difficult to make a filter member with sufficient suction resistance, and the production stability of the corrugated sheet will deteriorate, resulting in the performance as a filter material. Is undesirably reduced.
【０００９】[0009]
【実施例】以下のようにして、フィルターを製造し、こ
れを用いてたばこを構成し、その特性を評価した。尚、
実施例における測定項目は、それぞれ以下に示す方法に
よって測定したものである。EXAMPLES A filter was manufactured in the following manner, a tobacco was constructed using the filter, and its characteristics were evaluated. still,
The measurement items in the examples were measured by the following methods.
【００１０】＜シート状物の厚さ＞シート状物の厚さ
は、ＪＩＳ Ｐ８１１８に基づき測定した。 ＜シート状物の坪量＞シート状物の坪量は、ＪＩＳ Ｐ
８１２４に基づき測定した。 ＜フィルタープラグ物性（通気抵抗、硬度）＞通気抵抗
及び硬度は、コレスタ法に基づき、フィルトロナ社製
「フィルターテストステーションＦＴＳ４００」を用い
て測定した。 ＜フィルター及びシガレット通気抵抗＞通気抵抗は、コ
レスタ法に基づき、加藤工業製「ＯＴＩＣ式吸引抵抗測
定器」を用いて測定した。 ＜たばこの煙中のＴＰＭ、タール、ニコチンの測定＞喫
煙による煙中のタールとニコチンの喫煙量をボルグワル
ト社製回転型喫煙器「ＲＭ２０／ＣＳ」を用い、コレス
タ法に基づき実施した。<Thickness of Sheet> The thickness of the sheet was measured according to JIS P8118. <Basic weight of sheet-like material>
8124. <Physical Properties of Filter Plug (Airflow Resistance, Hardness)> Airflow resistance and hardness were measured using a filter test station FTS400 manufactured by Filtrona Corporation based on the Coresta method. <Filter and Cigarette Permeation Resistance> The permeation resistance was measured based on the Coresta method using an “OTIC suction resistance measurement device” manufactured by Kato Kogyo. <Measurement of TPM, tar, and nicotine in cigarette smoke> The amount of smoking of tar and nicotine in smoke due to smoking was measured based on the Coresta method using a rotary smoker “RM20 / CS” manufactured by Borgwald.
【００１１】（実施例１〜５）図２に示す方法で、開繊
した後にトリアセチンを添着したセルロースアセテート
繊維トウと、木材パルプ繊維シート紙とを重ね合わせ、
複合シート状物とし、さらに、溝ピッチ１ｍｍ、溝の深
さ０.５ｍｍのコルゲート加工により得られたコルゲー
ト加工した複合シート状物を通常の方法で巻き上げフィ
ルタープラグ（円周２４.６ｍｍ、長さ１２０ｍｍ）を
製造した。製造したフィルタープラグから長さ２５ｍｍ
に切断したものを、本発明のたばこフィルターとした。
得られたたばこフィルターとたばこの巻部とをセロハン
テープを巻いて接続し、たばこを製造した。たばこの巻
部には、PHILIP MORRIS社製商品名「Marlboro」のフィ
ルター部分を除いたものと同様の構成のものを用いた。
得られたたばこフィルターの構成及び物性とたばこの評
価結果を表１に示した。(Examples 1 to 5) According to the method shown in FIG. 2, a cellulose acetate fiber tow to which triacetin has been impregnated after being spread and a wood pulp fiber sheet are overlapped.
A corrugated composite sheet obtained by corrugating with a groove pitch of 1 mm and a groove depth of 0.5 mm as a composite sheet is wound up by a usual method using a filter plug (24.6 mm in circumference, length 24.6 mm). 120 mm). 25mm length from manufactured filter plug
The tobacco filter of the present invention was cut into pieces.
The obtained tobacco filter and the tobacco winding part were connected by winding cellophane tape to produce a tobacco. The cigarette roll used had the same configuration as that except for the filter part of "Marlboro" manufactured by PHILIP MORRIS.
Table 1 shows the structure and physical properties of the obtained tobacco filter and the evaluation results of the tobacco.
【００１２】（比較例１）通常のたばこフィルターとし
てセルロースアセテート繊維トウからなる均一構造のた
ばこフィルターを製造した。得られたたばこフィルター
は、実施例１〜５と同様にたばこの巻部と接続し、たば
こを製造した。得られたたばこフィルターの構成及び物
性とたばこの評価結果を表１に示した。 （比較例２）トリアセチンが未添着のセルロースアセテ
ート繊維トウを用いた以外は、実施例１〜５と同様にフ
ィルタープラグを製造しようとしたが、木材パルプ繊維
シート紙とセルロースアセテート繊維トウが分離した状
態になるため、プラグマシンで巻き上げることはできな
かった。 （比較例３〜４）厚さ及び坪量が表１に示す値の木材パ
ルプ繊維シート紙を用いた以外は、実施例１〜５と同様
にフィルタープラグを製造した。得られたフィルタープ
ラグの物性は、硬度が低く、たばこの使用に適していな
かった。得られたたばこフィルターの構成及び物性を表
１に示した。Comparative Example 1 A tobacco filter having a uniform structure made of cellulose acetate fiber tow was manufactured as an ordinary tobacco filter. The obtained tobacco filter was connected to the tobacco roll in the same manner as in Examples 1 to 5, to produce a tobacco. Table 1 shows the structure and physical properties of the obtained tobacco filter and the evaluation results of the tobacco. (Comparative Example 2) A filter plug was manufactured in the same manner as in Examples 1 to 5 except that a cellulose acetate fiber tow to which triacetin was not attached was used, but the wood pulp fiber sheet paper and the cellulose acetate fiber tow were separated. Because of the state, it could not be wound up with a plug machine. (Comparative Examples 3 to 4) A filter plug was manufactured in the same manner as in Examples 1 to 5, except that wood pulp fiber sheet paper having the thickness and basis weight shown in Table 1 was used. The physical properties of the obtained filter plug were low in hardness and were not suitable for use in tobacco. Table 1 shows the structure and physical properties of the obtained tobacco filter.
【００１３】[0013]
【表１】 [Table 1]
【００１４】[0014]
【発明の効果】以上説明したように本発明のたばこフィ
ルターは、従来のセルロースアセテートフィルターと同
じ通気抵抗水準でありながら、それよりも濾過率が高
く、硬度の発現性に優れ、また良好な喫味が得られるた
ばこフィルターである。特に、木材パルプ繊維からなる
シート状物として、紙、クレープ紙を用いることで濾過
機能がより好適になる。繊維トウからなるシート状物と
して、セルロースアセテート繊維を用いることで、製造
安定性や喫味が向上する。さらにバインダーとしてトリ
アセチンを用いることで、喫味が向上する。また、複合
シート状物がコルゲート加工されたものであると、賦形
安定性が向上する。また、木材パルプ繊維からなるシー
ト状物の質量／繊維トウからなるシート状物の質量の割
合が４／６〜６／４とすることで、濾過効率と香喫味が
共に向上する。バインダーの添加量を複合シート状物の
質量に対して２〜６％とすることで、フィルター性能の
均一化、喫味をより向上できる。As described above, the tobacco filter of the present invention has the same ventilation resistance as the conventional cellulose acetate filter, but has a higher filtration rate, excellent hardness development, and good taste. Is obtained. In particular, the use of paper or crepe paper as the sheet-like material made of wood pulp fiber makes the filtering function more suitable. By using cellulose acetate fibers as the sheet-like material made of the fiber tow, the production stability and the taste are improved. Further, the taste is improved by using triacetin as a binder. When the composite sheet is corrugated, the shaping stability is improved. In addition, when the ratio of the mass of the sheet-like material made of wood pulp fiber / the mass of the sheet-like material made of the fiber tow is 4/6 to 6/4, both the filtration efficiency and the flavor are improved. By setting the amount of the binder to 2 to 6% based on the mass of the composite sheet, the filter performance can be made uniform and the taste can be further improved.
【図１】 本発明のコルゲート加工された複合シート状
物の例の断面図である。FIG. 1 is a cross-sectional view of an example of a corrugated composite sheet according to the present invention.
【図２】 本発明のたばこフィルターを製造する装置の
例の概略図である。FIG. 2 is a schematic view of an example of an apparatus for producing a tobacco filter of the present invention.
１ 繊維トウ ２ 開繊装置 ３ 繊維トウからなるシート状物 ４ デリベリーロール ５ ロール支持装置 ６ 木材パルプ繊維からなるシート状物 ７ コルゲート加工装置 ８ エキストラロール ９ プラグマシン １０ コルゲート成形された複合シート状物 REFERENCE SIGNS LIST 1 fiber tow 2 opening device 3 sheet material made of fiber tow 4 delivery roll 5 roll supporting device 6 sheet material made of wood pulp fiber 7 corrugating device 8 extra roll 9 plug machine 10 corrugated composite sheet object
───────────────────────────────────────────────────── フロントページの続き (72)発明者 前田 和生 東京都港区虎ノ門三丁目８番21号 日本フ ィルター工業株式会社内 (72)発明者 松井 和宏 埼玉県朝霞市栄町三丁目２番34号 日本フ ィルター工業株式会社内 (72)発明者 平野 孝憲 高知県吾川郡伊野町3380番地 日本板紙株 式会社内 (72)発明者 倉石 伸一 高知県吾川郡伊野町3380番地 日本板紙株 式会社内 (72)発明者 松本 鶴義 富山県富山市海岸通３番地 三菱レイヨン 株式会社富山事業所内 (72)発明者 高瀬 栄一 富山県富山市海岸通３番地 三菱レイヨン 株式会社富山事業所内 Ｆターム(参考） 4B045 AA45 AB16 BC02 BC07 ──────────────────────────────────────────────────続 き Continued on the front page (72) Inventor Kazuo Maeda 3-8-21 Toranomon, Minato-ku, Tokyo Japan Filter Industry Co., Ltd. (72) Inventor Kazuhiro Matsui 2-34 Sakaemachi, Asaka-shi, Saitama No. Nippon Filter Industry Co., Ltd. (72) Inventor Takanori Hirano 3380 Ino-cho, Agawa-gun, Kochi Prefecture Nippon Paperboard Corporation (72) Inventor Shinichi Kuraishi 3380 Ino-cho, Agawa-gun, Kochi Prefecture Nippon Paperboard Corporation (72) Inventor Tsuruyoshi Matsumoto 3 Kaigan-dori, Toyama City, Toyama Prefecture Mitsubishi Rayon Co., Ltd. Toyama Works (72) Inventor Eiichi Takase 3 Kaigan-dori Toyama City, Toyama Prefecture F-term in Toyama Works, Mitsubishi Rayon Co., Ltd. (Reference) 4B045 AA45 AB16 BC02 BC07
Claims (8)
〜４０ｇ／ｍ2である木材パルプ繊維からなるシート状
物と、繊維トウからなるシート状物とがバインダーを介
して接合された複合シート状物よりなることを特徴とす
るたばこフィルター。(1) a thickness of 50 to 140 μm and a basis weight of 25;
A tobacco filter comprising a composite sheet formed by bonding a sheet made of wood pulp fiber of up to 40 g / m 2 and a sheet made of fiber tow via a binder.
が紙であることを特徴とする請求項１に記載のたばこフ
ィルター。2. The tobacco filter according to claim 1, wherein the sheet made of the wood pulp fiber is paper.
がクレープ紙であることを特徴とする請求項２記載のた
ばこフィルター。3. The tobacco filter according to claim 2, wherein the sheet made of the wood pulp fiber is crepe paper.
ルロースアセテート繊維からなるものであることを特徴
とする請求項１〜３のいずれかに記載のたばこフィルタ
ー。4. The tobacco filter according to claim 1, wherein the sheet-like material made of the fiber tow is made of cellulose acetate fiber.
とを特徴とする請求項１〜４のいずれかに記載のたばこ
フィルター。5. The tobacco filter according to claim 1, wherein the binder is triacetin.
れたものであることを特徴とする請求項１〜５のいずれ
かに記載のたばこフィルター。6. The tobacco filter according to claim 1, wherein the composite sheet is corrugated.
量／繊維トウからなるシート状物の質量の割合が４／６
〜６／４であることを特徴とする請求項１〜６のいずれ
かに記載のたばこフィルター。7. The ratio of the mass of the sheet made of wood pulp fiber / the mass of the sheet made of fiber tow is 4/6.
The tobacco filter according to any one of claims 1 to 6, wherein the ratio is from ６ to ／.
物の質量に対して２〜６％であることを特徴とする請求
項１〜７のいずれかに記載のたばこフィルター。8. The tobacco filter according to claim 1, wherein the amount of the binder is 2 to 6% based on the mass of the composite sheet.