JP2001089980A - Knit fabric showing metallic gloss - Google Patents
Knit fabric showing metallic glossInfo
- Publication number
- JP2001089980A JP2001089980A JP26693599A JP26693599A JP2001089980A JP 2001089980 A JP2001089980 A JP 2001089980A JP 26693599 A JP26693599 A JP 26693599A JP 26693599 A JP26693599 A JP 26693599A JP 2001089980 A JP2001089980 A JP 2001089980A
- Authority
- JP
- Japan
- Prior art keywords
- knitted fabric
- yellow
- knit fabric
- yarn
- dyed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ゴールド調の金属
光沢を呈する編地に関するものであり、更に詳しくは、
特定の色相に染色された糸条を編地の表面と裏面とに選
択的に配置することにより、あたかもゴールドの如き金
属光沢を呈する編地に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a knitted fabric exhibiting a gold-like metallic luster.
The present invention relates to a knitted fabric having a metallic luster such as gold by selectively arranging yarns dyed in a specific hue on the front and back surfaces of the knitted fabric.
【０００２】[0002]
【従来の技術】従来より、布帛にゴールドの如き光沢を
付与する方法としては、布帛を赤及び黄色の混合カチオ
ン染料で染色する方法が採用されているが、このような
染料による混色のみでは充分な光沢を付与することがで
きないという問題があった。2. Description of the Related Art Conventionally, a method of dyeing a cloth with a mixed cationic dye of red and yellow has been adopted as a method for imparting a luster such as gold to the cloth. There was a problem that it was not possible to impart a high gloss.
【０００３】一方、光沢に優れた、鮮明な色彩効果を呈
する布帛の製造方法として、下記の様な方法が知られて
いる（吉川和志著「新しい繊維の知識 改訂第３版」、
１９９４年４月１５日鎌倉書房発行など）。 異色に染め分けた糸を経／緯に用いて平織又は綾織
し、併置混色を起こさせる。 スパッタリングにより、布帛表面に光の反射層と透過
層の薄膜を形成させる。 偏光フィルムと分子配向異方性フィルムを貼合わせた
箔糸を製編織する。On the other hand, the following methods are known as a method for producing a fabric having excellent gloss and a vivid color effect (Kazushi Yoshikawa, "Knowledge of New Fibers, Third Edition,"
Published by Kamakura Publishing on April 15, 1994). Plain weave or twill weave using yarns dyed in different colors for warp / weft to cause juxtaposition color mixing. A thin film of a light reflection layer and a light transmission layer is formed on the fabric surface by sputtering. Weaving and weaving a foil yarn in which a polarizing film and a molecular orientation anisotropic film are bonded.
【０００４】しかしながら、上記の方法では、経糸と
緯糸の区別が不明瞭で、糸間の空隙が大きい編地には適
用できず、用途が限定されるという問題点がある。ま
た、やの方法では、布帛の製造に特別な装置が必要
となり、多大の手間とコストが掛かる上、硬い風合の布
帛しか得られないという欠点がある。[0004] However, in the above method, there is a problem that the distinction between the warp and the weft is unclear, and the method cannot be applied to a knitted fabric having a large gap between the yarns, and the application is limited. In addition, in the case of the method, a special apparatus is required for fabric production, which requires a great deal of labor and cost, and has a drawback that only a fabric having a hard feel can be obtained.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、上記
従来技術の有する問題点を解消し、あたかもゴールドの
如き光沢を呈する編地を、通常の製編工程を用いた簡便
な方法により提供することを目的とする。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned problems of the prior art and to provide a knitted fabric exhibiting a gloss like gold by a simple method using a usual knitting process. The purpose is to do.
【０００６】[0006]
【課題を解決するための手段】本発明者らは上記目的を
達成するために鋭意検討した結果、特定の色相に染色さ
れた糸条を編地の表面と裏面とに選択的に配置すると
き、あたかもゴールドの如き金属光沢が呈されることを
究明した。Means for Solving the Problems The inventors of the present invention have made intensive studies to achieve the above object, and have found that when a yarn dyed in a specific hue is selectively arranged on the front and back surfaces of a knitted fabric. It was clarified that a metallic luster like gold is exhibited.
【０００７】かくして本発明によれば、黄色の分散染料
により染色された糸条が主として編地の表面に配置さ
れ、且つ黄色及び赤色のカチオン染料により染色された
糸条が主として編地の裏面に配置されるよう交編されて
なる編地であって、該編地のＣＩＥ測色系におけるＬ、
ａ、ｂの値が下記範囲を同時に満足することを特徴とす
る金属光沢を呈する編地が提供される。 ７０≦Ｌ≦７５ ３≦ａ≦６．０ ３５≦ｂ≦６０Thus, according to the present invention, the yarn dyed with the yellow disperse dye is mainly arranged on the surface of the knitted fabric, and the yarn dyed with the yellow and red cationic dye is mainly formed on the back surface of the knitted fabric. A knitted fabric knitted so as to be arranged, wherein the knitted fabric has L,
A knitted fabric exhibiting metallic luster, characterized in that the values of a and b simultaneously satisfy the following ranges: 70 ≦ L ≦ 75 3 ≦ a ≦ 6.0 35 ≦ b ≦ 60
【０００８】[0008]
【発明の実施の形態】本発明で使用する、黄色の分散染
料により染色された糸条とは、ポリエステルやアセテー
トなど、分散染料により染色可能な合成繊維や半合成繊
維を言い、中でも、ポリエチレンテレフタレートを主た
る繰り返し単位とするポリエステル繊維が好ましく例示
できる。DESCRIPTION OF THE PREFERRED EMBODIMENTS The yarn dyed with a yellow disperse dye used in the present invention refers to synthetic fibers or semi-synthetic fibers which can be dyed with a disperse dye, such as polyester and acetate. A preferred example is a polyester fiber having (a) as a main repeating unit.
【０００９】該糸条を染色するための分散染料として
は、ベンゼンアゾ系（モノアゾ、ジスアゾなど）、複素
環アゾ系（チアゾールアゾ、ベンゾチアゾールアゾ、キ
ノリンアゾ、ピリジンアゾ、イミダゾールアゾ、チオフ
ェンアゾなど）、アントラキノン系、縮合系（キノフタ
リン、スチリル、クマリンなど）分散染料のうち、黄色
の色相を呈するものを、単独又は併用して使用できる。
中でも、Ｃ．Ｉ．Ｄｉｓｐｅｒｓｅ Ｙｅｌｌｏｗ ２
３１が好ましく例示できる。Disperse dyes for dyeing the yarn include benzene azo (monoazo, disazo, etc.), heterocyclic azo (thiazole azo, benzothiazole azo, quinoline azo, pyridine azo, imidazole azo, thiophen azo, etc.), anthraquinone Among these disperse dyes, such as quinophthaline, styryl and coumarin, disperse dyes exhibiting a yellow hue can be used alone or in combination.
Among them, C.I. I. Disperse Yellow 2
31 can be preferably exemplified.
【００１０】上記の染色は糸条の状態で実施しても良い
し、編地に編成した後、布帛の状態で実施しても構わな
い。また、浸染や捺染など従来公知の任意の方法が採用
できる。さらに、染色の際に使用する分散染料の濃度は
０．０８〜０．３％ｏｗｆが好ましい。The above-mentioned dyeing may be carried out in the state of a thread, or may be carried out in the state of a fabric after knitting into a knitted fabric. In addition, any conventionally known method such as dip dyeing or printing can be adopted. Further, the concentration of the disperse dye used for dyeing is preferably 0.08 to 0.3% owf.
【００１１】また、本発明で使用する、黄色及び赤色の
カチオン染料により染色された糸条とは、カチオン染料
可染性ポリエステル繊維ポリエステルやアクリルなど、
カチオン染料により染色可能な合成繊維や半合成繊維を
言い、中でも、ポリエチレンテレフタレートに５−スル
ホイソフタル酸ナトリウムなどの第３成分を少量共重合
させた、カチオン染料可染性ポリエステル繊維が好まし
く例示できる。The yarn dyed with the yellow and red cationic dyes used in the present invention refers to a cationic dye dyeable polyester fiber such as polyester or acrylic.
Synthetic fibers and semi-synthetic fibers that can be dyed with a cationic dye, and among these, cationic dye dyeable polyester fibers obtained by copolymerizing polyethylene terephthalate with a small amount of a third component such as sodium 5-sulfoisophthalate can be preferably exemplified.
【００１２】該糸条は、糸条の状態で、或いは編地に編
成した後布帛の状態で、黄色及び赤色の色相を呈するカ
チオン染料を併用して染色される。中でも、Ｃ．Ｉ．Ｃ
ａｔｉｏｎ Ｙｅｌｌｏｗ ２１やＣ．Ｉ．Ｃａｔｉｏ
ｎ Ｙｅｌｌｏｗ ６７及びＣ．Ｉ．Ｃａｔｉｏｎ Ｒ
ｅｄ ２９が好ましく例示できる。染色の際に使用する
カチオン染料の濃度は黄色が１．０〜４．０％ｏｗｆ、
赤色が０．２〜１．０％ｏｗｆであることが好ましい。The yarn is dyed in the state of a yarn or in the state of a fabric after knitting into a knitted fabric, using a cationic dye exhibiting yellow and red hues in combination. Among them, C.I. I. C
ation Yellow 21 and C.I. I. Catio
n Yellow 67 and C.I. I. Cation R
ed 29 can be preferably exemplified. The concentration of the cationic dye used at the time of dyeing is 1.0 to 4.0% owf for yellow,
The red color is preferably 0.2 to 1.0% owf.
【００１３】上記各糸条の繊度等には特に制限はない
が、黄色の分散染料により染色された糸条が異形断面
糸、或いは０．１重量％以下の艶消剤を含む、いわゆる
ブライト光沢糸条であれば、光沢の発現効果がより強調
されるので好ましい。The fineness of each of the above-mentioned yarns is not particularly limited, but the yarn dyed with a yellow disperse dye has a modified cross-section yarn or a so-called bright luster containing 0.1% by weight or less of a matting agent. A yarn is preferable because the effect of developing gloss is further emphasized.
【００１４】本発明においては、黄色の分散染料により
染色された糸条が主として編地の表面に配置され、黄色
及び赤色のカチオン染料により染色された糸条が主とし
て編地の裏面に配置されるよう交編されていることが必
要である。In the present invention, the yarn dyed with the yellow disperse dye is mainly arranged on the surface of the knitted fabric, and the yarn dyed with the yellow and red cationic dye is mainly arranged on the back of the knitted fabric. Must be knitted together.
【００１５】編地をこのような構成とすることにより、
編地の表面から見た場合、表面に存在する糸条間空隙か
ら裏面の糸条の色相が視認され、編地においても前述の
併置混色の効果が発現して、あたかも干渉色が発現した
かの如き金属光沢が呈される。By forming the knitted fabric in such a configuration,
When viewed from the surface of the knitted fabric, the hue of the yarn on the back surface is visually recognized from the gap between the yarns present on the surface, and the above-described side-by-side color mixing effect also appears on the knitted fabric, as if an interference color appeared. A metallic luster such as
【００１６】かくして得られた編地は、ＣＩＥ測色系に
おけるＬ、ａ、ｂの値がそれぞれ、７０≦Ｌ≦７５、３
≦ａ≦６．０、３５≦ｂ≦６０を同時に満足することが
必要である。Ｌ、ａ、ｂの値が上記範囲を外れる場合
は、良好な金属光沢が得られない。The knitted fabric thus obtained has L, a, and b values of 70 ≦ L ≦ 75, 3
It is necessary to simultaneously satisfy ≦ a ≦ 6.0 and 35 ≦ b ≦ 60. When the values of L, a, and b are out of the above ranges, good metallic luster cannot be obtained.
【００１７】[0017]
【実施例】以下、本発明を実施例により具体的に説明す
るが、本発明はこれらに限定されるものではない。EXAMPLES Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited thereto.
【００１８】［実施例１］福原精機（株）製、２８ゲー
ジの３４インチダブル編機を用い、ポリエチレンテレフ
タレートに５−スルホイソフタル酸ナトリウム成分を
２．６モル％共重合させた、カチオン染料可染性ポリエ
ステル仮撚加工糸（７５デニール／３６フィラメン
ト）、及び酸化チタンの含有量が０．０７重量％の三角
断面ポリエステルフィラメント糸（７５デニール／３６
フィラメント）を供給して図１に示す組織を有する編地
を得た。Example 1 Using a 28 gauge 34 inch double knitting machine manufactured by Fukuhara Seiki Co., Ltd., a cationic dye was prepared by copolymerizing polyethylene terephthalate with 2.6 mol% of sodium 5-sulfoisophthalate component. Dyeable polyester false twisting yarn (75 denier / 36 filaments) and triangular cross section polyester filament yarn having a titanium oxide content of 0.07% by weight (75 denier / 36 filaments)
Filament) was supplied to obtain a knitted fabric having a structure shown in FIG.
【００１９】該編地を１ｇ／１のスコアロール４００
（花王（株）製）水溶液中で、８０℃で２０分間精練し
た。次に水洗、乾燥した後、１９０℃で１分間プレセッ
トした。The knitted fabric is score roll 400 of 1 g / 1.
In an aqueous solution (manufactured by Kao Corporation), scouring was performed at 80 ° C. for 20 minutes. Next, after washing with water and drying, it was preset at 190 ° C. for 1 minute.
【００２０】次いで、該編地を下記染浴で１３０℃で６
０分間、浴比１：３０で染色した。 ・染料 C.I.Disperse Yellow 231 ０．１２％ｏｗｆ ・分散均染剤 ディスパーＶＧ（明成化成（株）製） ０．５ｇ／ｌ ・酢酸 ０．２ｃｃ／ｌNext, the knitted fabric is subjected to the following dye bath at 130 ° C. for 6 hours.
Stained for 0 min at a bath ratio of 1:30. -Dye CIDisperse Yellow 231 0.12% owf-Dispersion leveling agent Disper VG (manufactured by Meisei Kasei Co., Ltd.) 0.5 g / l-Acetic acid 0.2 cc / l
【００２１】さらに、該編地を下記染浴で１３０℃で６
０分間、浴比１：３０で染色した。 ・染料 C.I.Catilon Yellow 67 ０．８％ｏｗｆ ・染料 C.I.Catilon Yellow 21 ０．８％ｏｗｆ ・染料 C.I.Catilon Red 29 ０．５％ｏｗｆ ・酢酸 ０．２ｃｃ／ｌFurther, the knitted fabric is subjected to the following dyeing bath at 130 ° C. for 6 hours.
Stained for 0 min at a bath ratio of 1:30.・ Dye CICatilon Yellow 67 0.8% owf ・ Dye CICatilon Yellow 21 0.8% owf ・ Dye CICatilon Red 29 0.5% owf ・ Acetic acid 0.2cc / l
【００２２】次いで、染色された編地を下記洗浄浴で６
５℃×２０分間還元洗浄した。 ・ＮａＯＨ ２ｇ／ｌ ・ハイトロサルファイト ２ｇ／ｌ ・アミラジンＤ （非イオン活性剤） ２ｇ／ｌ 還元洗浄後、十分水洗して乾燥、ファイナルセット（１
６０℃×１分間）を行った。Next, the dyed knitted fabric is washed in the following washing bath for 6 hours.
Reduction washing was performed at 5 ° C for 20 minutes.・ NaOH 2g / l ・ Hytrosulfite 2g / l ・ Amilazine D (non-ionic activator) 2g / l After reducing and washing, thoroughly wash with water and dry, final set (1
60 ° C. × 1 minute).
【００２３】得られた編地は、黄色の分散染料により染
色された糸条が主として編地の表面に配置され、黄色及
び赤色のカチオン染料により染色された糸条が主として
編地の裏面に配置されており、Ｌ、ａ、ｂの値がそれぞ
れ、Ｌ＝７３．０４、ａ＝４．４７、ｂ＝４４．５４で
あり、あたかもゴールドの如き金属光沢を呈するもので
あった。In the obtained knitted fabric, the yarn dyed with the yellow disperse dye is mainly arranged on the surface of the knitted fabric, and the yarn dyed with the yellow and red cationic dyes is mainly arranged on the back surface of the knitted fabric. The values of L, a, and b were L = 73.04, a = 4.47, and b = 44.54, respectively, and exhibited a metallic luster as if it were gold.
【００２４】［実施例２〜１２、比較例１〜７］実施例
１において、使用する分散染料及びカチオン染料の濃度
を表１に示す如く変更した以外は実施例１と同様に実施
した。得られた編地のＬ、ａ、ｂの値及び金属光沢の発
現の有無を表２に示す。Examples 2 to 12 and Comparative Examples 1 to 7 The same procedures as in Example 1 were carried out except that the concentrations of the disperse dye and the cationic dye used were changed as shown in Table 1. Table 2 shows the values of L, a, b of the obtained knitted fabric and the presence / absence of metallic luster.
【００２５】[0025]
【表１】 [Table 1]
【００２６】[0026]
【表２】 [Table 2]
───────────────────────────────────────────────────── フロントページの続き (72)発明者 北野 佳実 石川県加賀市大聖寺上福田町ロ131番地 株式会社キタセン内 Ｆターム(参考） 4H057 AA01 BA03 BA08 DA01 DA33 EA01 GA90 HA21 4L002 AA07 AB00 AB02 AB04 DA04 EA00 EA08 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Yoshimi Kitano 131 B, Kamifukuda-cho, Daisho-ji Temple, Kaga-shi, Ishikawa F-term in Kitasen Corporation (reference) 4H057 AA01 BA03 BA08 DA01 DA33 EA01 GA90 HA21 4L002 AA07 AB00 AB02 AB04 DA04 EA00 EA08
Claims (3)
主として編地の表面に配置され、且つ黄色及び赤色のカ
チオン染料により染色された糸条が主として編地の裏面
に配置されるよう交編されてなる編地であって、該編地
のＣＩＥ測色系におけるＬ、ａ、ｂの値が下記範囲を同
時に満足することを特徴とする金属光沢を呈する編地。 ７０≦Ｌ≦７５ ３≦ａ≦６．０ ３５≦ｂ≦６０Claims 1. A yarn dyed with a yellow disperse dye is arranged mainly on the surface of a knitted fabric, and a yarn dyed with a yellow and red cationic dye is mainly arranged on a back surface of a knitted fabric. A knitted fabric having metallic luster, characterized in that the values of L, a, and b in the CIE colorimetric system of the knitted fabric simultaneously satisfy the following ranges. 70 ≦ L ≦ 75 3 ≦ a ≦ 6.0 35 ≦ b ≦ 60
異形断面糸である請求項１記載の金属光沢を呈する編
地。2. The knitted fabric having a metallic luster according to claim 1, wherein the yarn dyed with the yellow disperse dye is a modified cross-section yarn.
０．１重量％以下の艶消剤を含む糸条である請求項１又
は２記載の金属光沢を呈する編地。3. The knitted fabric having metallic luster according to claim 1, wherein the yarn dyed with the yellow disperse dye is a yarn containing 0.1% by weight or less of a matting agent.