JP2000327800A - Synthetic resin sheet - Google Patents
Synthetic resin sheetInfo
- Publication number
- JP2000327800A JP2000327800A JP11137518A JP13751899A JP2000327800A JP 2000327800 A JP2000327800 A JP 2000327800A JP 11137518 A JP11137518 A JP 11137518A JP 13751899 A JP13751899 A JP 13751899A JP 2000327800 A JP2000327800 A JP 2000327800A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- synthetic resin
- resin sheet
- resin
- ultraviolet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、デスクマットやテ
ーブルマットとして好適に使用される、合成樹脂製シー
トまたはフィルムに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a synthetic resin sheet or film suitably used as a desk mat or a table mat.
【０００２】[0002]
【従来の技術】従来より、デスクマットやテーブルマッ
トとして、ポリオレフィン製の合成樹脂シートが提案さ
れている。しかし、ポリオレフィン製シートは、手脂等
の人の皮膚から分泌される脂分を吸収して変形してしま
うという問題点があった。2. Description of the Related Art Polyolefin synthetic resin sheets have been proposed as desk mats and table mats. However, the polyolefin sheet has a problem in that it absorbs fats secreted from human skin such as hand fat and is deformed.
【０００３】そこで、紫外線硬化型塗料を塗布して、ポ
リオレフィン製シート表面に紫外線硬化型皮膜を形成す
るということが試みられたが、ポリオレフィン製シート
と紫外線硬化型皮膜の接着性が悪く、シートを折り曲げ
たりすると、紫外線硬化型皮膜が剥がれてしまうという
問題が生じた。[0003] Therefore, it has been attempted to form an ultraviolet-curable film on the surface of a polyolefin sheet by applying an ultraviolet-curable coating material. However, the adhesion between the polyolefin sheet and the ultraviolet-curable film is poor, and the sheet has to be formed. When bent, the problem that the ultraviolet-curable film was peeled off occurred.
【０００４】[0004]
【発明が解決しようとする課題】したがって本発明は、
上記問題点を解決するために、ポリオレフィン樹脂シー
トとして、シート表面に塗工した紫外線硬化型塗料によ
る皮膜との接着性が良好であり、添加剤等のブリードの
生じにくい合成樹脂製シートを提供することを課題とす
る。Accordingly, the present invention provides
In order to solve the above problems, as a polyolefin resin sheet, there is provided a synthetic resin sheet which has good adhesiveness to a film formed by an ultraviolet curable coating applied to the sheet surface and does not easily cause bleeding of additives and the like. That is the task.
【０００５】[0005]
【課題を解決するための手段】かかる課題を解決するた
めに、本発明はその一つの態様として、ポリオレフィン
樹脂を主体とし、これにエチレン・アクリル酸エステル
および／またはメタクリル酸エステル・不飽和結合を有
するカルボン酸無水物の多元共重合体を含有してなる樹
脂組成物から形成される合成樹脂製シートを提供するも
のである。Means for Solving the Problems In order to solve the above-mentioned problems, the present invention provides, as one embodiment thereof, a polyolefin resin as a main component, to which ethylene / acrylate and / or methacrylate / unsaturated bonds are added. An object of the present invention is to provide a synthetic resin sheet formed from a resin composition containing a carboxylic anhydride multi-component copolymer having the same.
【０００６】本発明は、特にポリオレフィン樹脂を主体
とし、そこに接着樹脂として特異的なエチレン・アクリ
ル酸エステルおよび／またはメタクリル酸エステル・不
飽和結合を有するカルボン酸無水物の多元共重合体を配
合した点に特徴を有するものであり、かかる多元共重合
体を配合することにより、樹脂シート表面に塗工した紫
外線硬化型塗料による皮膜との接着性がより向上し、か
つ添加剤のブリードも抑制された合成樹脂製シートが得
られるのである。The present invention particularly comprises a polyolefin resin as a main component and a specific copolymer of ethylene, acrylate and / or methacrylate, and a carboxylic anhydride having an unsaturated bond as an adhesive resin. By blending such a multi-component copolymer, the adhesiveness with the UV-curable coating applied to the resin sheet surface is further improved, and the bleeding of additives is also suppressed. The synthetic resin sheet thus obtained is obtained.
【０００７】したがって、本発明は更なる別の態様とし
て、上記した樹脂組成物から形成されるシートの少なく
とも片面に、紫外線硬化型塗料を塗布した合成樹脂製シ
ートを提供するものでもある。Accordingly, the present invention provides, as yet another aspect, a sheet made of a synthetic resin in which at least one surface of a sheet formed from the above-mentioned resin composition is coated with an ultraviolet curable paint.
【０００８】[0008]
【発明の実施の形態】本発明が提供する合成樹脂製シー
トを構成する組成としてのポリオレフィン樹脂成分とし
ては、例えばポリエチレン樹脂であり、従来からデスク
マット等の素材として使用されているものであれば、い
ずれのものであってもよい。BEST MODE FOR CARRYING OUT THE INVENTION The polyolefin resin component as a composition constituting the synthetic resin sheet provided by the present invention is, for example, a polyethylene resin, as long as it is conventionally used as a material for a desk mat or the like. , Any of them.
【０００９】本発明にあっては、そのようなポリオレフ
ィン樹脂として、低密度ポリエチレン、線状低密度ポリ
エチレン、中密度ポリエチレン、高密度ポリエチレン、
メタロセン触媒を用いて重合したポリエチレン等のポリ
エチレン；ランダム重合ポリプロピレン、ブロック重合
ポリプロピレン、シンジオタクチックポリプロピレン、
軟質ポリプロピレン等のポリプロピレン及びこれらの共
重合体または混合物等が使用できるが、なかでもメタロ
セン触媒を用いて重合したポリエチレンが、好結果を与
えることが判明した。In the present invention, such polyolefin resins include low-density polyethylene, linear low-density polyethylene, medium-density polyethylene, and high-density polyethylene.
Polyethylene such as polyethylene polymerized using a metallocene catalyst; random-polymerized polypropylene, block-polymerized polypropylene, syndiotactic polypropylene,
Polypropylene such as soft polypropylene and copolymers or mixtures thereof can be used, and it has been found that polyethylene polymerized using a metallocene catalyst gives good results.
【００１０】本発明にあっては、ポリオレフィン樹脂に
対するエチレン・アクリル酸エステルおよび／またはメ
タクリル酸エステル・不飽和結合を有するカルボン酸無
水物の多元共重合体の添加量は、例えば、ポリオレフィ
ン樹脂１００重量部に対して、エチレン・アクリル酸エ
ステルおよび／またはメタクリル酸エステル・不飽和結
合を有するカルボン酸無水物の多元共重合体の添加量
を、０．５〜１５重量部とするのが好ましく、紫外線硬
化型皮膜との接着性およびコストの面から、さらに好ま
しくは１〜１０重量部とするのがよい。In the present invention, the amount of the multi-component copolymer of ethylene / acrylate and / or methacrylate / carboxylic acid anhydride having an unsaturated bond to the polyolefin resin is, for example, 100% by weight of the polyolefin resin. Parts by weight of the ethylene / acrylate and / or methacrylate / carboxylic acid anhydride-containing multicomponent copolymer having an unsaturated bond is preferably 0.5 to 15 parts by weight. From the viewpoints of adhesiveness to the curable coating and cost, the amount is more preferably 1 to 10 parts by weight.
【００１１】上記の本発明の樹脂製シートを構成するポ
リオレフィン樹脂には、必要に応じて、帯電防止剤、酸
化防止剤、滑剤、無機充填剤、着色剤等の各種添加剤を
添加することもできる。この種の添加剤の種類およびそ
の添加量は、特に限定されるものではなく、従来からこ
の種のポリオレフィン樹脂シートに使用されている添加
剤を従来と同様の添加量にて添加すればよい。If necessary, various additives such as an antistatic agent, an antioxidant, a lubricant, an inorganic filler, and a coloring agent may be added to the polyolefin resin constituting the resin sheet of the present invention. it can. The type and the amount of this kind of additive are not particularly limited, and the additive conventionally used for this kind of polyolefin resin sheet may be added in the same amount as the conventional one.
【００１２】滑剤としては、流動パラフィン、ポリエチ
レンワックス等の炭化水素系滑剤；ステアリン酸亜鉛、
ステアリン酸バリウム、ステアリン酸カルシウム等の金
属石鹸；ステアリン酸アマイド、パルミチン酸アマイド
等のモノアマイド系滑剤；エチレンビスアマイド、メチ
レンビスアマイド等のビスアマイド系滑剤が使用できる
が、滑性の面から、ビスアマイド系滑剤が好ましい。Examples of the lubricant include hydrocarbon lubricants such as liquid paraffin and polyethylene wax; zinc stearate;
Metal soaps such as barium stearate and calcium stearate; monoamide-based lubricants such as stearic acid amide and palmitic acid amide; bis-amide-based lubricants such as ethylene bisamide and methylene bis-amide can be used, but from the aspect of lubricity, bis-amide-based lubricants Is preferred.
【００１３】また、本発明が提供する合成樹脂製シート
にあっては、紫外線硬化型の塗料による皮膜を設けるこ
とができる。そのような紫外線硬化型塗料としては、例
えば、ウレタン系、アクリル系、ウレタン−アクリル
系、アクリル−エポキシ系、メルカプト誘導体系、エポ
キシ系などの塗料を挙げることができる。Further, in the synthetic resin sheet provided by the present invention, a film made of a UV-curable paint can be provided. Examples of such UV-curable paints include urethane-based, acrylic-based, urethane-acryl-based, acrylic-epoxy-based, mercapto derivative-based, and epoxy-based paints.
【００１４】このような紫外線硬化型塗料による皮膜の
形成は、本発明のポリオレフィン樹脂製シートの表面の
みならず、その両面に皮膜を施したものであってもよ
い。The formation of the film with such an ultraviolet-curable coating material may be performed not only on the surface of the polyolefin resin sheet of the present invention, but also on both surfaces thereof.
【００１５】かかる紫外線硬化型塗料による皮膜を形成
したことにより、本発明の樹脂シートをデスクマットや
テーブルマットとして使用した場合に、人の皮膚から分
泌される手脂や汗等を吸収して、デスクマットやテーブ
ルマットが変形し、波打つことが抑制できる。When the resin sheet of the present invention is used as a desk mat or a table mat, it absorbs hand grease and sweat secreted from human skin by forming a film of such an ultraviolet curable paint, The deformation of the desk mat or the table mat and the waving can be suppressed.
【００１６】一方、本発明が提供する樹脂製シートは、
高周波ウェルダー適性が比較的良好なため、押出法等に
より製造した樹脂製シートを高周波ウェルダー接着によ
り、複数枚つなげて、広幅のシートとすることもでき
る。On the other hand, the resin sheet provided by the present invention is:
Since the suitability for the high frequency welder is relatively good, a wide sheet can be formed by connecting a plurality of resin sheets manufactured by an extrusion method or the like by high frequency welder bonding.
【００１７】本発明が提供する合成樹脂製シートまたは
フィルムは、上記の樹脂成分および必要に応じて添加さ
れる各種添加剤等からなる樹脂組成物を、カレンダー法
や押出法等の一般に使用されている公知の製造方法によ
り、適宜所望の厚さに成形することによって得ることが
できる。なお、シート自体の厚さは一概に特定できない
が、得られるシートの用途等によって異なり、例えば、
デスクマットやテーブルマットとして使用する場合に
は、０．３〜３ｍｍ程度の厚さを有するシートとすれば
よい。The sheet or film made of a synthetic resin provided by the present invention is obtained by subjecting a resin composition comprising the above-mentioned resin components and various additives to be used as necessary to a general method such as a calendering method or an extrusion method. It can be obtained by appropriately molding to a desired thickness by a known manufacturing method. Although the thickness of the sheet itself cannot be specified unconditionally, it differs depending on the use of the obtained sheet and the like.
When used as a desk mat or a table mat, a sheet having a thickness of about 0.3 to 3 mm may be used.
【００１８】[0018]
【実施例】以下に実施例により本発明をさらに詳細に説
明するが、本発明はかかる実施例のみに限定されず、種
々の変形も本発明の範囲に包含されるものである。EXAMPLES The present invention will be described in more detail with reference to the following Examples, which, however, are not intended to limit the scope of the present invention.
【００１９】実施例：下記の表中に記載の樹脂組成、な
らびにその配合量に、滑剤を加え、押出法によりシート
を製造し、さらにドクターナイフコーターにより紫外線
硬化型塗料を塗布し、紫外線照射により皮膜を形成さ
せ、本発明の樹脂製シートを得た。得られたシートにつ
いて、滑剤のブリードの程度ならびに紫外線硬化型皮膜
との接着性を一定の基準により評価し、その結果を合わ
せて表中に記載した。Example: A resin was added to the resin composition shown in the table below, and a compounding amount thereof, a lubricant was added, a sheet was produced by an extrusion method, a UV-curable coating was applied by a doctor knife coater, and UV irradiation was performed. A film was formed to obtain a resin sheet of the present invention. With respect to the obtained sheet, the degree of bleeding of the lubricant and the adhesiveness to the ultraviolet curable film were evaluated according to a certain standard, and the results were combined and described in the table.
【００２０】[0020]
【表１】 [Table 1]
【００２１】 ＊１ メタロセン触媒を用いて重合したポリエチレン ＊２ 軟質ポリプロピレン ＊３ エチレン−アクリル酸エチル−無水マイレン酸
の三元共重合体 住友化学工業社製 ボンダイン ＊４ エチレンビスアマイド ＊５ ○ ほとんどブリードを起こさない × ブリードが起こりやすい ＊６ ◎ 爪でひっかいても紫外線硬化型皮膜が剥げ
ない ○ 爪でひっかいても紫外線硬化型皮膜がなかなか剥げ
ない × 爪でひっかくと簡単に剥げる ＊７ ○ 適度に硬い × 非常に硬い* 1 Polyethylene polymerized using a metallocene catalyst * 2 Soft polypropylene * 3 Terpolymer of ethylene-ethyl acrylate-maleic anhydride Bondyne manufactured by Sumitomo Chemical Co., Ltd. * 4 Ethylene bisamide * 5 ○ Almost bleed Does not cause bleeding. * 6 ◎ UV-curable coating does not peel off even when nailed. ○ UV-curable coating does not easily peel off even when nailed. × Easy to peel off with nail. * 7 ○ Moderate. Hard x very hard
【００２２】上記した表中に記載の結果からも明らかな
ように、本発明の合成樹脂製シートは、シートからの滑
剤のブリードが認められず、また紫外線硬化型塗料によ
る皮膜との接着性に優れたものであることが判明する。
これに対し多元共重合体を配合しない比較例のシートに
あっては、シート自体からの滑剤のブリードが顕著に認
められ、紫外線硬化型塗料による皮膜との接着性もあま
りよいものではなかった。As is clear from the results shown in the above table, the synthetic resin sheet of the present invention shows no bleeding of the lubricant from the sheet, and has a poor adhesion to the film formed by the ultraviolet-curable paint. It turns out to be excellent.
On the other hand, in the sheet of the comparative example in which the multi-component copolymer was not blended, the bleeding of the lubricant from the sheet itself was remarkably observed, and the adhesiveness to the film formed by the ultraviolet curable paint was not so good.
【００２３】[0023]
【発明の効果】上記のように、本発明によれば、ポリオ
レフィン樹脂を主体とし、そこにエチレン・アクリル酸
エステルおよび／またはメタクリル酸エステル・不飽和
結合を有するカルボン酸無水物の多元共重合体配合させ
た構成にすることによって、添加剤のブリードも抑える
ことができ、さらに紫外線硬化型塗料による硬化皮膜と
の接着性が良好な合成樹脂製シートが得られる。As described above, according to the present invention, a multi-component copolymer of a polyolefin resin as a main component and a carboxylic acid anhydride having an ethylene / acrylate and / or methacrylate / unsaturated bond therein. By using the mixed composition, bleeding of the additive can be suppressed, and a synthetic resin sheet having good adhesion to a cured film formed by an ultraviolet curable paint can be obtained.
フロントページの続き Ｆターム(参考） 4F006 AA12 AB01 BA02 DA04 EA03 4F071 AA14 AA15 AA15X AA33X AA36X AH19 BC01 4J002 BB031 BB072 BB092 BB121 BP021 FD170 GC00 4J038 DB001 FA111 FA112 FA221 FA251 FA281 GA13 NA04 NA05 PA17 PC08 Continued on the front page F-term (reference) 4F006 AA12 AB01 BA02 DA04 EA03 4F071 AA14 AA15 AA15X AA33X AA36X AH19 BC01 4J002 BB031 BB072 BB092 BB121 BP021 FD170 GC00 4J038 DB001 FA111 FA112 FA221 FA251 FA281 GA281
Claims (3)
エチレン・アクリル酸エステルおよび／またはメタクリ
ル酸エステル・不飽和結合を有するカルボン酸無水物の
多元共重合体を含有してなる樹脂組成物から形成される
合成樹脂製シート。1. A resin composition comprising a polyolefin resin as a main component and a multicomponent copolymer of ethylene / acrylate and / or methacrylate / carboxylic anhydride having an unsaturated bond. Sheet made of synthetic resin.
である請求項１に記載の合成樹脂製シート。2. The synthetic resin sheet according to claim 1, wherein the polyolefin resin is a polyethylene resin.
布した請求項１または２項に記載の合成樹脂製シート。3. The synthetic resin sheet according to claim 1, wherein an ultraviolet curable paint is applied on at least one surface.