JP2000170095A - Rust-proof paper - Google Patents
Rust-proof paperInfo
- Publication number
- JP2000170095A JP2000170095A JP35101098A JP35101098A JP2000170095A JP 2000170095 A JP2000170095 A JP 2000170095A JP 35101098 A JP35101098 A JP 35101098A JP 35101098 A JP35101098 A JP 35101098A JP 2000170095 A JP2000170095 A JP 2000170095A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- rust
- layer
- proof
- moisture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、例えば金属コイル
等の金属製品の包装等に用いられる防錆紙に関するもの
である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to rust-proof paper used for packaging metal products such as metal coils.
【０００２】[0002]
【従来の技術】鉄鋼材料、銅合金材料等からなる金属製
品が紙製包装材、段ボール箱等で包装されて保管、流通
等されると、紙製包装材、段ボール箱等が吸湿し、水分
によって金属製品に錆が発生することがある。また、潜
熱の大きな金属製品の場合には結露が生じ、同様に水分
によって金属製品に錆が発生することがある。2. Description of the Related Art When a metal product made of a steel material, a copper alloy material, or the like is packaged in a paper packaging material, a cardboard box, or the like, and stored or distributed, the paper packaging material, the cardboard box, etc., absorb moisture and water. Rust may occur on metal products due to this. In the case of a metal product having a large latent heat, dew condensation occurs, and similarly, rust may be generated on the metal product due to moisture.
【０００３】金属製品の錆発生を防止するため、出荷時
に金属製品の表面に防錆油等が塗布されることがある。
この方法により錆発生を防止することはできるが、防錆
油の塗工作業が必要であるため金属製品の製造コストが
上昇してしまう。また、金属製品を使用する前には防錆
油除去作業が必要であるため、金属製品の利用者からも
敬遠される。[0003] In order to prevent the generation of rust on a metal product, rust-preventive oil or the like may be applied to the surface of the metal product at the time of shipment.
Although this method can prevent the generation of rust, it requires the application of rust-preventive oil, which increases the production cost of metal products. In addition, since it is necessary to remove rust-preventive oil before using metal products, users of metal products are also shunned.
【０００４】紙に防錆剤を含浸させた防錆紙を用いて金
属製品を包装する手段も提案されている。この方法で
は、防錆紙から気化した防錆剤が金属製品の表面に付着
することにより、金属製品の錆発生が防止される。しか
し、気化した防錆剤の一部は防錆紙の外部にも飛散する
ので、気化速度が速すぎる場合は防錆効果が長続きしな
い。そして、包装された金属製品が長期間保管された際
に、防錆紙を通じて外部から侵入した水分によって錆が
発生してしまうことがある。[0004] Means for packaging metal products using rustproof paper in which paper is impregnated with a rustproofing agent has also been proposed. According to this method, the rust preventive vaporized from the rust-proof paper adheres to the surface of the metal product, thereby preventing rust of the metal product. However, a part of the vaporized rust preventive scatters to the outside of the rust preventive paper. Therefore, if the vaporization speed is too high, the rust preventive effect does not last long. Then, when the packaged metal product is stored for a long period of time, rust may be generated due to moisture that has entered from outside through the rust-proof paper.
【０００５】防錆剤が含浸された紙の片面にポリエチレ
ン、ポリプロピレン等からなる合成樹脂層が積層された
防錆紙も提案されている。この防錆紙では、合成樹脂層
により防錆剤の外部への飛散が防止され、防錆効果が長
続きする。また、合成樹脂層により外部からの水分の侵
入が防止されるので、包装される金属製品の錆発生を防
止することができる。[0005] A rust-proof paper in which a synthetic resin layer made of polyethylene, polypropylene or the like is laminated on one side of paper impregnated with a rust-preventive agent has also been proposed. In this rustproof paper, the synthetic resin layer prevents the rustproofing agent from scattering to the outside, and the rustproofing effect lasts long. Further, since the penetration of moisture from the outside is prevented by the synthetic resin layer, it is possible to prevent the generation of rust in the metal product to be packaged.
【０００６】[0006]
【発明が解決しようとする課題】近年、省資源、環境保
護等の気運の高まりとともに、リサイクル可能な防錆紙
が望まれつつある。ところが、合成樹脂層が積層された
前述の防錆紙では、再生紙として利用しようとしても合
成樹脂が水中でほとんど離解しないので、再生紙中に合
成樹脂が不純物として混入し、再生紙の品質を低下させ
てしまうこととなる。このため、この防錆紙は再利用が
ほとんどなされていないのが実状である。また、やむな
くこの防錆紙が焼却処分された場合は合成樹脂の酸化に
より多量の二酸化炭素が発生してしまうので、地球温暖
化防止の観点から好ましくない。さらに防錆紙が廃棄さ
れた場合は、自然環境中で合成樹脂が分解しないため環
境中に残存し続け、環境破壊を起こしてしまうこととな
る。In recent years, with the rise of resources such as resource saving and environmental protection, recyclable rustproof paper has been desired. However, in the above-mentioned rust-proof paper having a laminated synthetic resin layer, the synthetic resin hardly disintegrates in water even if it is used as recycled paper. It will lower it. For this reason, this rust-proof paper is hardly reused. Further, if the rust-proof paper is inevitably incinerated, a large amount of carbon dioxide is generated due to oxidation of the synthetic resin, which is not preferable from the viewpoint of preventing global warming. Further, when the rust-proof paper is discarded, the synthetic resin does not decompose in the natural environment, so that the synthetic resin continues to remain in the environment, causing environmental destruction.
【０００７】本発明はこの問題に鑑みてなされたもので
あり、再生紙として再利用することができる防錆紙を提
供することをその目的とするものである。[0007] The present invention has been made in view of this problem, and an object of the present invention is to provide a rust-proof paper that can be reused as recycled paper.
【０００８】[0008]
【課題を解決するための手段】前述の目的を達成するた
めになされた本発明は、紙素材に防錆剤が付着した紙層
と、水離解性の防湿剤からなる防湿剤層とを備えた防錆
紙、である（請求項１）。SUMMARY OF THE INVENTION The present invention, which has been made to achieve the above-mentioned object, comprises a paper layer in which a rust inhibitor is attached to a paper material and a moisture-proof layer made of a water-disintegrating moisture-proof agent. (Corresponding to claim 1).
【０００９】この発明の防錆紙は防錆剤が付着した紙層
を備えているので、これを用いて金属製品を包装すれ
ば、紙層から気化した防錆剤が金属製品表面に付着して
錆の発生が防がれる。防錆剤を付着させる方法として
は、防錆剤を含浸させたり、塗工したりすればよい。Since the rust-preventive paper of the present invention has a paper layer to which a rust-preventive agent has adhered, if a metal product is wrapped using this, the rust-preventive agent vaporized from the paper layer will adhere to the surface of the metal product. Rust is prevented. As a method of attaching the rust inhibitor, the rust inhibitor may be impregnated or coated.
【００１０】この防錆紙は防湿剤層を備えているので、
気化した防錆剤の外部への飛散が防止され、防錆効果が
長続きする。また、防湿剤層により外部からの水分の侵
入が防止されるので、包装される金属製品の錆発生を防
止することができる。[0010] Since this rustproofing paper has a moistureproofing layer,
The vaporized rust preventive is prevented from scattering to the outside, and the rust preventive effect lasts long. In addition, since the moisture barrier layer prevents moisture from entering from outside, it is possible to prevent rust from occurring in the packaged metal product.
【００１１】この防錆紙の防湿剤層は水離解性の防湿剤
から構成されており、また紙層は元来水離解性であるの
で、防湿紙全体が水離解可能である。このため、防錆紙
を再生紙とすることができる。水に離解した防湿剤は水
と共にそのまま投棄されるか、微生物等の処理を経て投
棄される。従って、再生紙中に合成樹脂成分が混入する
ことがなく、再生紙の品質が低下してしまうことがな
い。なお、ここで水離解性の防湿剤とは、水溶性の防湿
剤又は水分散性の防湿剤を意味する。The moisture-proofing agent layer of the rust-proof paper is composed of a water-disintegrating moisture-proofing agent, and the paper layer is originally water-disintegrating, so that the entire moisture-proofing paper can be water-disintegrated. Therefore, the rust-proof paper can be used as the recycled paper. The moisture-proofing agent disintegrated in water is discarded as it is with water or is subjected to treatment with microorganisms and the like. Therefore, the synthetic resin component does not mix into the recycled paper, and the quality of the recycled paper does not deteriorate. Here, the water disintegrating desiccant means a water-soluble desiccant or a water-dispersible desiccant.
【００１２】この発明において、紙素材に防錆剤が付着
した紙層と、水離解性の防湿剤からなる防湿剤層と、紙
素材からなる他の紙層とを順次積層して防錆紙を構成す
れば、防錆紙の強度が向上し、しかも、防湿剤層が表面
に現れることがないために防湿剤中の成分が他に転移す
るのが抑制される（請求項３）。また、他の紙層を紙素
材に防錆剤が付着した紙層とすれば、防錆効果がより向
上する（請求項３）。In the present invention, a paper layer having a rust preventive agent adhered to a paper material, a moisture proof agent layer formed of a water disintegrating moisture proof agent, and another paper layer formed of a paper material are sequentially laminated to form a rustproof paper. With this configuration, the strength of the rust-proofing paper is improved, and furthermore, since the moisture-proofing agent layer does not appear on the surface, the transfer of components in the moisture-proofing agent to other components is suppressed (claim 3). Further, when the other paper layer is a paper layer in which a rust inhibitor is attached to a paper material, the rust prevention effect is further improved (claim 3).
【００１３】この発明において、紙素材に防錆剤が付着
した紙層と、水離解性の防湿剤からなる防湿剤層と、補
強材層とを順次積層して防錆紙を構成すれば、防錆紙の
強度を向上させることができる（請求項４）。さらに、
この補強材層を水離解性とすれば、補強材層を取り除く
ことなく防錆紙を再生することができる（請求項５）。In this invention, if a paper layer having a rust inhibitor attached to a paper material, a moisture proof agent layer made of a water disintegrating moisture proof agent, and a reinforcing material layer are sequentially laminated to form a rust-proof paper, The strength of the rust-proof paper can be improved (claim 4). further,
If this reinforcing material layer is made water disintegratable, the rust-proof paper can be recycled without removing the reinforcing material layer (claim 5).
【００１４】[0014]
【発明の実施の形態】以下、適宜図面を参照しつつ、本
発明を詳説する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in detail with reference to the drawings.
【００１５】図１は、本発明の一実施形態にかかる防錆
紙１の一部が示された断面図である。この防錆紙１は、
紙層３の下面に防湿剤層５が積層されることにより構成
されている。FIG. 1 is a cross-sectional view showing a part of a rust-proof paper 1 according to one embodiment of the present invention. This antirust paper 1
It is configured by laminating a moisture barrier layer 5 on the lower surface of the paper layer 3.
【００１６】紙層３には、紙素材が用いられている。用
いられる紙素材としては、例えば上質紙、中質紙、晒ク
ラフト紙、未晒クラフト紙、片艶未晒クラフト紙、ライ
ナー紙、紙管原紙、中性クラフト紙、コート紙、クレー
プ紙、再生紙等が挙げられる。なかでも、包装する金属
製品の錆発生を防止する観点から、そのｐＨが６．５以
上７．５以下であり、その塩素イオン濃度が０．０１重
量％以下であり、その硫酸イオン濃度が０．０１重量％
以下の中性紙を用いるのが好ましい。紙素材の秤量は特
には限定されないが、例えば３０ｇ／ｍ2以上１０００
ｇ／ｍ2以下のものの中から、使用目的に応じ適宜選択
されて用いられる。The paper layer 3 is made of a paper material. As the paper material used, for example, high quality paper, medium quality paper, bleached kraft paper, unbleached kraft paper, unbleached unbleached kraft paper, liner paper, paper tube base paper, neutral kraft paper, coated paper, crepe paper, recycled Paper etc. are mentioned. Among them, from the viewpoint of preventing rusting of the metal product to be packaged, the pH is 6.5 or more and 7.5 or less, the chloride ion concentration is 0.01% by weight or less, and the sulfate ion concentration is 0% or less. 0.01% by weight
It is preferable to use the following neutral paper. Although the weighing of the paper material is not particularly limited, for example, 30 g / m 2 or more and 1000
g / m 2 or less and appropriately selected and used according to the purpose of use.
【００１７】紙層３を構成する紙素材には、防錆剤が含
浸されている。用いられる防錆剤の種類は、包装される
金属製品の材質等に応じて適宜選定される。防錆剤の具
体例としては、例えば脂肪酸塩、安息香酸塩、亜硝酸塩
等の水溶液又はアルコール（例えばメタノール、イソプ
ロピルアルコール、エタノール等）溶液等が挙げられ
る。これらの水溶液及び溶液の濃度は、例えば１０重量
％以上５０重量％以下程度とされる。防錆剤の含浸は、
一般的には紙素材に防錆液が塗工又は侵漬されることに
より行われる。防錆剤の塗工量は、固形分換算で８ｇ／
ｍ2以上３０ｇ／ｍ2以下が好ましく、１０ｇ／ｍ2以上
１５ｇ／ｍ2以下が特に好ましい。塗工量が上記範囲未
満であると、防錆効果が不十分となってしまうことがあ
る。逆に、塗工量が上記範囲を越えると、紙層３の上面
がべとついたり、防錆剤が結晶化したりしてしまうこと
がある。The paper material constituting the paper layer 3 is impregnated with a rust inhibitor. The type of rust preventive used is appropriately selected according to the material of the metal product to be packaged. Specific examples of the rust preventive include, for example, an aqueous solution of a fatty acid salt, a benzoate, a nitrite, or the like, or an alcohol (eg, methanol, isopropyl alcohol, ethanol, etc.) solution. The concentrations of these aqueous solutions and solutions are, for example, about 10% by weight or more and 50% by weight or less. Impregnation of rust inhibitor
Generally, it is performed by applying or immersing a rust preventive liquid to a paper material. The coating amount of the rust inhibitor is 8 g / solid equivalent.
m 2 or more 30 g / m 2 or less is preferable, 10 g / m 2 or more 15 g / m 2 or less is particularly preferred. If the coating amount is less than the above range, the rust prevention effect may be insufficient. Conversely, if the coating amount exceeds the above range, the upper surface of the paper layer 3 may be sticky or the rust preventive may be crystallized.
【００１８】防湿剤層５は、紙層３の下面に水離解性の
防湿剤が塗工されることにより形成されている。用いら
れる水離解性の防湿剤としては、ワックスエマルジョ
ン、樹脂エマルジョン、ラテックス、これらの混合物等
の既知のものが用いられる。防湿剤には、必要に応じ炭
化水素系オリゴマー、界面活性剤、分散剤、安定剤、顔
料等が配合されてもよい。防湿剤の塗工量は、固形分換
算で５ｇ／ｍ2以上５０ｇ／ｍ2以下が好ましく、１０ｇ
／ｍ2以上３０ｇ／ｍ2以下が特に好ましい。塗工量が上
記範囲未満であると、防湿効果が不十分となり、外部か
ら防錆紙１を通して水分が内部に侵入してしまうことが
ある。逆に、塗工量が上記範囲を越えると、防湿剤の費
用が嵩む割には防湿効果が頭打ちとなって不経済となっ
てしまうことがある。The moisture-proofing agent layer 5 is formed by applying a water-disintegrating moisture-proofing agent to the lower surface of the paper layer 3. As the water disintegration desiccant used, known ones such as wax emulsion, resin emulsion, latex, and a mixture thereof are used. If necessary, a hydrocarbon oligomer, a surfactant, a dispersant, a stabilizer, a pigment, and the like may be blended in the desiccant. The coating amount of the desiccant is preferably 5 g / m 2 or more and 50 g / m 2 or less in terms of solid content, and 10 g / m 2 or less.
/ M 2 or more and 30 g / m 2 or less is particularly preferable. If the coating amount is less than the above range, the moisture-proof effect becomes insufficient, and moisture may enter the inside through the rust-proof paper 1 from the outside. Conversely, if the coating amount exceeds the above range, the moisture-proofing effect may reach a ceiling and the economy may become uneconomical even though the cost of the moisture-proofing agent increases.
【００１９】防湿剤の紙素材への塗工方法は既知の各種
方法を採用することができ、例えばキスロールコータ
ー、バーコーター、ロールコーター、ブレードコータ
ー、キスコーター等により行えばよい。Various known methods can be used for applying the moisture proofing agent to the paper material. For example, a kiss roll coater, a bar coater, a roll coater, a blade coater, a kiss coater or the like may be used.
【００２０】この防錆紙１を用いて金属製品を包装する
場合は、紙層３が内側とされる。すると、紙層３から防
錆剤が気化して金属製品の表面に付着し、錆の発生が防
止される。外側に位置する防湿剤層５は、外部からの水
分の侵入を防止すると共に、防錆剤の外部への飛散を防
止する。When wrapping a metal product using the rust-proof paper 1, the paper layer 3 is set inside. Then, the rust inhibitor vaporizes from the paper layer 3 and adheres to the surface of the metal product, thereby preventing rust. The moistureproofing agent layer 5 located on the outside prevents moisture from entering from outside and also prevents the rustproofing agent from scattering to the outside.
【００２１】この防錆紙１を使用後再生紙に加工する場
合は、まず防錆紙１を所定寸法に裁断し、水中で攪拌す
る。すると、紙層３及び防湿剤層５が離解する。次ぎ
に、これを抄いて乾燥し、再生紙を得る。防湿剤は水に
離解しているので再生紙中にはほとんど混入しない。従
って、再生紙の品質を高めることができる。水に離解し
た防湿剤は、水と共に投棄される。When the rustproof paper 1 is processed into recycled paper after use, the rustproof paper 1 is first cut into a predetermined size and stirred in water. Then, the paper layer 3 and the desiccant layer 5 disintegrate. Next, it is made and dried to obtain recycled paper. Since the desiccant disintegrates in water, it hardly mixes with recycled paper. Therefore, the quality of the recycled paper can be improved. The desiccant disintegrated in water is discarded together with the water.
【００２２】図２は、本発明の他の実施形態にかかる防
錆紙７の一部が示された断面図である。この防錆紙７
は、紙素材に防錆剤が付着した紙層９、防湿剤層１１及
び他の紙層１３が積層されることにより構成されてい
る。紙層９及び防湿剤層１１の構成は、それぞれ図１に
示された防錆紙１の紙層３及び防湿剤層５の構成と同等
である。FIG. 2 is a sectional view showing a part of the rust-proof paper 7 according to another embodiment of the present invention. This rust-proof paper 7
Is constructed by laminating a paper layer 9 having a rust preventive agent attached to a paper material, a moistureproof layer 11 and another paper layer 13. The configurations of the paper layer 9 and the moisture barrier layer 11 are the same as the configurations of the paper layer 3 and the moisture barrier layer 5 of the rust-proof paper 1 shown in FIG. 1, respectively.
【００２３】他の紙層１３は、紙素材に防錆剤が含浸さ
れることにより構成されている。用いられる紙素材の材
質及び秤量並びに用いられる防錆剤の成分及び塗工量
は、図１に示された防錆紙１の紙層３と同等である。The other paper layer 13 is formed by impregnating a paper material with a rust inhibitor. The material and weighing of the paper material used, and the components and coating amount of the rust preventive used are the same as those of the paper layer 3 of the rust preventive paper 1 shown in FIG.
【００２４】この防錆紙７は、金属製品の個包装に好適
に用いられる。複数の個包装体は、さらに段ボール箱等
の外包装材中に収納される。例えば、紙層９を内側とし
て金属製品が個包装されると、この紙層９から気化した
防錆剤が金属製品の錆発生を防止するとともに、外側と
なる他の紙層１３からも防錆剤が気化して外包装材中に
充満する。従って、もし一部の個包装体の防錆紙７が破
断しても、外包装材中に充満した防錆剤により、金属製
品の錆発生が防止される。This rust-proof paper 7 is suitably used for individual packaging of metal products. The plurality of individual packages are further housed in an outer packaging material such as a cardboard box. For example, when a metal product is individually wrapped with the paper layer 9 inside, the rust preventive vaporized from the paper layer 9 prevents rust on the metal product and also prevents rust from the other paper layer 13 outside. The agent vaporizes and fills the outer packaging. Therefore, even if the rust preventive paper 7 of a part of the individual package breaks, the rust preventive agent filled in the outer wrapping material prevents the rust of the metal product.
【００２５】この防錆紙７では、上面及び下面が紙素材
であるため、防湿剤層１１が表面に現れない。このた
め、被包装体や外包装材に防湿剤中の成分が転移するこ
とが抑えられる。また、上面及び下面に紙素材が設けら
れているため、防錆紙７の強度が向上する。同様の効果
は、他の紙層１３として防錆剤が含浸されていない紙素
材を用いた場合でも得ることができる。Since the upper and lower surfaces of the rustproof paper 7 are made of paper, the moistureproof layer 11 does not appear on the surface. For this reason, transfer of the components in the desiccant to the packaged object and the outer packaging material is suppressed. Further, since the paper material is provided on the upper surface and the lower surface, the strength of the rust-proof paper 7 is improved. The same effect can be obtained even when a paper material not impregnated with a rust inhibitor is used as the other paper layer 13.
【００２６】この防錆紙７において、紙層９及び他の紙
層１３にシワ加工を施しても良い。こうすれば、防錆紙
７に応力緩和性を付与することができ、例えば帯状の防
錆紙７で環状の金属製品を螺旋状に巻き上げる際に防錆
紙７が金属製品の形状に追従し、隙間なく防錆紙７で金
属製品を覆うことができるようになる。In the rust-proof paper 7, the paper layer 9 and the other paper layer 13 may be subjected to a wrinkle process. In this way, it is possible to impart stress relaxation to the rust-proof paper 7. For example, when the annular metal product is spirally wound with the belt-like rust-proof paper 7, the rust-proof paper 7 follows the shape of the metal product. Thus, the metal product can be covered with the rust-proof paper 7 without any gap.
【００２７】図３は、本発明のさらに他の実施形態にか
かる防錆紙１５の一部が示された断面図である。この防
錆紙１５は、紙素材に防錆剤が付着した紙層１７、防湿
剤層１９及び補強材層２１が積層されることにより構成
されている。紙層１７及び防湿剤層１９の構成は、それ
ぞれ図１に示された防錆紙１の紙層３及び防湿剤層５の
構成と同等である。FIG. 3 is a sectional view showing a part of the rust-proof paper 15 according to still another embodiment of the present invention. The rust-proof paper 15 is formed by laminating a paper layer 17 having a rust-preventive agent adhered to a paper material, a moisture-proof agent layer 19, and a reinforcing material layer 21. The configurations of the paper layer 17 and the desiccant layer 19 are the same as the configurations of the paper layer 3 and the desiccant layer 5 of the rust-proof paper 1 shown in FIG. 1, respectively.
【００２８】補強材層２１は、例えば樹脂クロス、ワリ
フ、樹脂フィルム、不織布等の補強材から構成されてい
る。補強材層２１を設けることにより、防錆紙１５の強
度を向上させることができる。補強材層２１を備えた防
錆紙１５を再生紙とする場合でも、防湿剤層１９が水離
解性して補強材層２１が離脱するので、容易に補強材層
２１を取り除くことができる。従って、補強材層２１が
再生紙中に混入することがない。補強材層２１は、水離
解性の補強材から構成されるのが好ましい。こうすれ
ば、防湿剤層１９とともに補強材層２１も水に離解する
ので、補強材層２１を取り除くことなく防錆紙１５を再
生紙とすることができる。水離解性の補強材としては、
例えばポリビニルアルコール製の補強材（具体例として
は、クラレ社の「クラロンＫ−」IIが挙げられる）等が
挙げられる。The reinforcing material layer 21 is made of a reinforcing material such as a resin cloth, a warif, a resin film, and a nonwoven fabric. By providing the reinforcing material layer 21, the strength of the rust-proof paper 15 can be improved. Even when the rust-proof paper 15 provided with the reinforcing material layer 21 is made of recycled paper, the moisture-proofing agent layer 19 disintegrates in water and the reinforcing material layer 21 is separated, so that the reinforcing material layer 21 can be easily removed. Therefore, the reinforcing material layer 21 does not mix into the recycled paper. The reinforcing material layer 21 is preferably made of a water disintegrating reinforcing material. In this case, since the reinforcing material layer 21 is disintegrated into water together with the moisture-proofing agent layer 19, the rust-proof paper 15 can be used as recycled paper without removing the reinforcing material layer 21. As a water disintegration reinforcing material,
For example, a reinforcing material made of polyvinyl alcohol (specific examples include "Kuraron K-" II from Kuraray Co., Ltd.) and the like.
【００２９】本発明の防錆紙の構成は、図１、図２及び
図３に示された構成のみには限られない。例えば、印刷
層を設けたり、他の補強層を設けたり、他の紙層を設け
る等、本発明の要旨を変更しない範囲で種々の仕様変更
が可能である。The configuration of the rust-proof paper of the present invention is not limited to the configuration shown in FIGS. 1, 2 and 3. For example, various specifications can be changed, such as providing a printing layer, providing another reinforcing layer, or providing another paper layer, without changing the gist of the present invention.
【００３０】[0030]
【発明の効果】以上説明したように、本発明によれば、
再生紙として再利用することができる防錆紙を提供する
ことができる。As described above, according to the present invention,
An antirust paper that can be reused as recycled paper can be provided.
【図１】図１は、本発明の一実施形態にかかる防錆紙の
一部が示された断面図である。FIG. 1 is a cross-sectional view showing a part of a rust-proof paper according to one embodiment of the present invention.
【図２】図２は、本発明の他の実施形態にかかる防錆紙
の一部が示された断面図である。FIG. 2 is a cross-sectional view showing a part of a rust-proof paper according to another embodiment of the present invention.
【図３】図３は、本発明のさらに他の実施形態にかかる
防錆紙の一部が示された断面図である。FIG. 3 is a cross-sectional view showing a part of a rust-proof paper according to still another embodiment of the present invention.
１、７、１５・・・防錆紙 ３、９、１７・・・紙層 ５、１１、１９・・・防湿剤層 １３・・・他の紙層 ２１・・・補強材層 1, 7, 15: Rustproof paper 3, 9, 17: Paper layer 5, 11, 19: Moistureproof layer 13: Other paper layer 21: Reinforcement layer
【手続補正書】[Procedure amendment]
【提出日】平成１２年２月１０日（２０００．２．１
０）[Submission date] February 10, 2000 (2000.2.1
0)
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】特許請求の範囲[Correction target item name] Claims
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【特許請求の範囲】[Claims]
【手続補正２】[Procedure amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】０００８[Correction target item name] 0008
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【０００８】[0008]
【課題を解決するための手段】前述の目的を達成するた
めになされた本発明は、紙素材に防錆剤が付着した紙層
と、水離解性の防湿剤からなる防湿剤層と、紙素材から
なる他の紙層とが順次積層された防錆紙、である。SUMMARY OF THE INVENTION In order to achieve the above-mentioned object, the present invention provides a paper layer in which a rust inhibitor is attached to a paper material, a moisture-proof layer made of a water-disintegrating moisture-proof agent, and a paper layer. Rust-proof paper in which other paper layers made of a material are sequentially laminated.
【手続補正３】[Procedure amendment 3]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１２[Correction target item name] 0012
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００１２】この発明の防錆紙は、紙素材に防錆剤が付
着した紙層と、水離解性の防湿剤からなる防湿剤層と、
紙素材からなる他の紙層とを順次積層しているので、防
錆紙の強度が向上し、しかも、防湿剤層が表面に現れる
ことがないために防湿剤中の成分が他に転移するのが抑
制される。また、他の紙層を紙素材に防錆剤が付着した
紙層とすれば、防錆効果がより向上する。The rust-proofing paper of the present invention comprises a paper layer having a rust-preventive agent attached to a paper material;
Since the paper layer is sequentially laminated with another paper layer made of paper material, the strength of the rust-proof paper is improved, and the components in the moisture-proof agent are transferred to the other because the moisture-proof layer does not appear on the surface. Is suppressed. Further, when the other paper layer is a paper layer in which a rust inhibitor is attached to a paper material, the rust prevention effect is further improved.
【手続補正４】[Procedure amendment 4]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１３[Correction target item name] 0013
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００１３】また別の発明として、紙素材に防錆剤が付
着した紙層と、水離解性の防湿剤からなる防湿剤層と、
補強材層とを順次積層した防錆紙も可能であり、防錆紙
の強度を向上させることができる。この補強材層を水離
解性とすれば、補強材層を取り除くことなく防錆紙を再
生することができる。また補強材層としてはワリフが好
ましい。As another invention, a paper layer in which a rust inhibitor is attached to a paper material, a moisture barrier layer made of a water disintegrating moisture barrier,
Rust-proof paper in which a reinforcing material layer is sequentially laminated is also possible, and the strength of the rust-proof paper can be improved. If the reinforcing material layer is made water disintegratable, the rust-proof paper can be recycled without removing the reinforcing material layer. Warif is preferred as the reinforcing material layer.
【手続補正５】[Procedure amendment 5]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００１８[Correction target item name] 0018
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００１８】防湿剤層５は、紙層３の下面に水離解性の
防湿剤が塗工されることにより形成されている。水離解
性の防湿剤としては、ワックスエマルジョン等の既知の
ものが用いられる。防湿剤には、必要に応じ炭化水素系
オリゴマー、界面活性剤、分散剤、安定剤、顔料等が配
合されてもよい。防湿剤の塗工量は、固形分換算で５ｇ
／ｍ2以上５０ｇ／ｍ2以下が好ましく、１０ｇ／ｍ2以
上３０ｇ／ｍ2以下が特に好ましい。塗工量が上記範囲
未満であると、防湿効果が不十分となり、外部から防錆
紙１を通して水分が内部に侵入してしまうことがある。
逆に、塗工量が上記範囲を越えると、防湿剤の費用が嵩
む割には防湿効果が頭打ちとなって不経済となってしま
うことがある。The moisture-proofing agent layer 5 is formed by applying a water-disintegrating moisture-proofing agent to the lower surface of the paper layer 3. As the water disintegrating desiccant, a known one such as a wax emulsion is used. If necessary, a hydrocarbon oligomer, a surfactant, a dispersant, a stabilizer, a pigment, and the like may be blended in the desiccant. The coating amount of the desiccant is 5 g in terms of solid content.
/ M is preferably 2 or more 50 g / m 2 or less, 10 g / m 2 or more 30 g / m 2 or less is particularly preferred. If the coating amount is less than the above range, the moisture-proof effect becomes insufficient, and moisture may enter the inside through the rust-proof paper 1 from the outside.
Conversely, if the coating amount exceeds the above range, the cost of the desiccant may increase, but the moisture-proof effect may reach a ceiling and become uneconomical.
フロントページの続き Ｆターム(参考） 3E067 AA11 AB48 AB49 BA06A BB01A BB25A BB26A EE25 EE33 EE34 GB12 4F100 AA01H AH02H AH08H AJ11B AK01D AR00D BA02 BA03 BA07 BA10A BA10C BA10D CA14A CA14C DG10A DG10C DG11D DG15D GB15 JB09B JB09D JD04B JL00 JM01B 4L055 AG04 AG34 AG61 AG97 AH23 AH28 AJ02 BE08 BE10 FA30 GA05 GA47 GA50 Continued on the front page F-term (reference) 3E067 AA11 AB48 AB49 BA06A BB01A BB25A BB26A EE25 EE33 EE34 GB12 4F100 AA01H AH02H AH08H AJ11B AK01D AR00D BA02 BA03 BA07 BA10A BA10C BA10D J14 AG10B14 J14 AG14B AG97 AH23 AH28 AJ02 BE08 BE10 FA30 GA05 GA47 GA50
Claims (5)
解性の防湿剤からなる防湿剤層とを備えた防錆紙。1. A rustproofing paper comprising a paper layer having a rustproofing agent attached to a paper material and a moistureproofing layer made of a water disintegrating moistureproofing agent.
解性の防湿剤からなる防湿剤層と、紙素材からなる他の
紙層とが順次積層された請求項１に記載の防錆紙。2. The paper layer according to claim 1, wherein a paper layer having a rust inhibitor adhered to the paper material, a moisture-proof layer made of a water-disintegrating moisture-proof agent, and another paper layer made of the paper material are sequentially laminated. Rust-proof paper.
た紙層である請求項２に記載の防錆紙。3. The rust-proof paper according to claim 2, wherein the other paper layer is a paper layer in which a rust inhibitor is attached to a paper material.
解性の防湿剤からなる防湿剤層と、補強材層とが順次積
層された請求項１に記載の防錆紙。4. The rustproofing paper according to claim 1, wherein a paper layer having a rustproofing agent adhered to the paper material, a moistureproofing layer made of a water disintegrating moistureproofing agent, and a reinforcing material layer are sequentially laminated.
に記載の防錆紙。5. The method according to claim 4, wherein the reinforcing material layer is water disintegrating.
Anti-rust paper described in 1.