JP2000106764A - Agricultural mulching and agricultural mulching agent - Google Patents
Agricultural mulching and agricultural mulching agentInfo
- Publication number
- JP2000106764A JP2000106764A JP10286962A JP28696298A JP2000106764A JP 2000106764 A JP2000106764 A JP 2000106764A JP 10286962 A JP10286962 A JP 10286962A JP 28696298 A JP28696298 A JP 28696298A JP 2000106764 A JP2000106764 A JP 2000106764A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- mulching
- agricultural mulching
- agricultural
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、農用マルチング方
法及び農用マルチング剤に関する。さらに詳しくは、本
発明は、施工に手間がかからず、保温性と遮光性に優
れ、使用後は農地に鋤き込んで施肥効果を発揮させるこ
とができる農用マルチング方法及び農用マルチング剤に
関する。TECHNICAL FIELD The present invention relates to an agricultural mulching method and an agricultural mulching agent. More specifically, the present invention relates to an agricultural mulching method and an agricultural mulching agent that require no labor for construction, are excellent in heat retention and light-shielding properties, and are capable of plowing into farmland after use to exert a fertilizing effect.
【０００２】[0002]
【従来の技術】農作物の栽培に当たって、農地の表面を
フィルムで覆って遮光し、地温を上昇させ、保湿するこ
とにより、農作物の生育を促進し、雑草を抑制するマル
チングが広く行われている。マルチフィルムとしては、
黒色のポリ塩化ビニルフィルムが多く用いられている。
しかし、マルチフィルムを用いると、マルチフィルムを
農地に設置し、押さえ土などにより固定し、農作物の収
穫後に取り外すのに多大の労力を要する。マルチフィル
ムは、強風により飛散し、その際に農作物を傷つけるお
それもある。さらに、ポリ塩化ビニル製のマルチフィル
ムは、使用後は廃棄物となり、焼却処理もダイオキシン
などの有害物質の発生のために困難となっている。この
問題を解決するために、ポリ塩化ビニルフィルムに代え
て、マルチング材料として紙を使用する試みがなされて
いる。例えば、特開平１０−９４３３５号公報には、エ
ンボス加工などにより伸長性を付与し、デンプンと紙用
ポリマーを含有させたマルチング紙が提案され、さら
に、特開平１０−１１７６０５号公報には、リン酸デン
プン粉をバインダーとして、表面は黒色カーボンによ
り、裏面はヨウ化カリウムを加えてヨウ素デンプン反応
により黒色としたマルチング紙が提案されている。これ
らのマルチング紙は、農作物収穫後に撤去する必要はな
いが、高価である上に、農地に設置し、固定する手間が
かかる、開口部より風が入った際に破損のおそれがある
といった点においては、従来のマルチフィルムと同様の
問題を有している。そこで新たに１片の面積が９００cm
2以下、もしくはスラリー状の紙で農地を被覆する方法
が提案されている（特開平７−２３１７２５号公報）。
この方法は、紙を散布して農地を被覆するため、設置が
比較的容易で（バインダーを使用した場合は土壌への固
着性もよく）、使用後に撤去の必要がない、といった利
点がある。しかし故紙だけを被覆材料としているため、
黒味が多い新聞紙を利用した場合でも材の色は薄い灰色
にしかならず、黒色度は高くなり、遮光性、保温性は黒
色フィルムに比べて十分でない。また、埋立地向けの土
壌被覆材料としては、故紙、ヒドロキシエチルセルロー
ス、ベントナイトなどを含有する覆土剤、アニオン性界
面活性剤、リン酸、アミノ系樹脂などを含有する覆土
剤、α−オレフィンスルホン酸塩、ステアリン酸などを
含有する覆土剤などが知られているが、これらの覆土剤
は比較的白色度が高く、界面活性剤などの生分解を受け
にくい成分を含んでいるので、農用マルチング剤には適
していない。このために、施工に手間がかからず、黒色
で農作物の生育を促進する効果が大きく、しかも公害源
となるおそれのない農用マルチング方法及び農用マルチ
ング剤が求められている。2. Description of the Related Art In the cultivation of agricultural products, mulching is widely practiced to cover the surface of agricultural land with a film to shield light, raise the soil temperature, and moisturize to promote the growth of the agricultural products and suppress weeds. As a multi-film,
Black polyvinyl chloride films are often used.
However, if a multi-film is used, a great deal of labor is required to install the multi-film on the farmland, fix it with holding soil, and remove it after harvesting the crop. The multi-film is scattered by the strong wind, and may damage the crops at that time. Furthermore, the multi-film made of polyvinyl chloride becomes waste after use, and it is difficult to incinerate it due to the generation of harmful substances such as dioxin. In order to solve this problem, an attempt has been made to use paper as a mulching material instead of a polyvinyl chloride film. For example, Japanese Patent Application Laid-Open No. H10-94335 proposes a mulching paper in which extensibility is imparted by embossing or the like and a starch and a paper polymer are contained. Further, Japanese Patent Application Laid-Open No. H10-117605 discloses a mulching paper. A mulching paper has been proposed in which acid starch powder is used as a binder, the surface is made of black carbon, and the back surface is made black by adding an iodine starch reaction by adding potassium iodide. These mulching papers do not need to be removed after harvesting crops, but they are expensive, take time to install and fix on farmland, and may be damaged when wind enters from the openings. Have the same problem as the conventional multi-film. So the area of one piece is 900cm newly
There has been proposed a method of coating agricultural land with two or less or slurry paper (JP-A-7-231725).
This method has an advantage that it is relatively easy to install (the binder is well adhered to the soil when a binder is used) because the paper is sprayed to cover the farmland, and there is no need to remove it after use. However, since only waste paper is used as the coating material,
Even when newspaper paper with a lot of blackness is used, the color of the material is only light gray, the blackness is high, and the light-shielding property and the heat retention are not sufficient as compared with the black film. Further, as a soil covering material for landfills, soil covering materials containing waste paper, hydroxyethyl cellulose, bentonite, etc., anionic surfactants, soil covering agents containing phosphoric acid, amino resin, etc., α-olefin sulfonate Although soil covering agents containing stearic acid and the like are known, these covering agents have relatively high whiteness and contain components that are not easily biodegradable such as surfactants. Is not suitable. For this reason, there is a need for an agricultural mulching method and an agricultural mulching agent which are black, have a large effect of promoting the growth of agricultural crops, do not require much labor for construction, and are not likely to be a source of pollution.
【０００３】[0003]
【発明が解決しようとする課題】本発明は、施工に手間
がかからず、保温性と遮光性に優れ、使用後は農地に鋤
き込んで施肥効果を発揮させることができる農用マルチ
ング方法及び農用マルチング剤を提供することを目的と
してなされたものである。SUMMARY OF THE INVENTION The present invention provides an agricultural mulching method which does not require much labor for construction, is excellent in heat insulation and light-shielding properties, and which can be plowed into farmland after use to exert a fertilizing effect. The purpose of the present invention is to provide an agricultural mulching agent.
【０００４】[0004]
【課題を解決するための手段】本発明者らは、上記の課
題を解決すべく鋭意研究を重ねた結果、フィルムや紙な
どの平面的材料を使用することなく、農地に直接マルチ
ング層を形成することにより、設置と固定に要する労力
を軽減することができ、ペーパースラッジなどの廃棄物
再生品、天然高分子などからなる結合剤、解繊故紙など
の繊維含有物質及び水を含有する材料により、効果的に
マルチング層を形成し得ることを見いだし、この知見に
基づいて本発明を完成するに至った。すなわち、本発明
は、（１）（Ａ）有機性汚泥の炭化物及び有機性廃棄物
から得られるコンポストから選ばれる１種又は２種以上
の廃棄物再生品、（Ｂ）半合成高分子又は天然高分子か
らなる結合剤、（Ｃ）解繊故紙及びおからから選ばれる
１種又は２種以上の繊維含有物質及び（Ｄ）水を含有す
る混合物を農地に散布することを特徴とする農用マルチ
ング方法、及び、（２）（Ａ）有機性汚泥の炭化物及び
有機性廃棄物から得られるコンポストから選ばれる１種
又は２種以上の廃棄物再生品、（Ｂ）半合成高分子又は
天然高分子からなる結合剤、（Ｃ）解繊故紙及びおから
から選ばれる１種又は２種以上の繊維含有物質及び
（Ｄ）水を含有することを特徴とする農用マルチング
剤、を提供するものである。さらに、本発明の好ましい
態様として、（３）（Ａ）廃棄物再生品の含有量が固形
分として１〜３０重量％、（Ｂ）結合剤の含有量が固形
分として１〜２０重量％、（Ｃ）繊維含有物質の含有量
が固形分として３〜３０重量％、（Ｄ）水の含有量が
(Ａ)成分、(Ｂ)成分及び(Ｃ)成分に由来する水分の量を
含めて５０〜９５重量％である混合物を用いる第(１)項
記載の農用マルチング方法、及び、（４）（Ａ）廃棄物
再生品の含有量が固形分として１〜３０重量％、（Ｂ）
結合剤の含有量が固形分として１〜２０重量％、（Ｃ）
繊維含有物質の含有量が固形分として３〜３０重量％、
（Ｄ）水の含有量が(Ａ)成分、(Ｂ)成分及び(Ｃ)成分に
由来する水分の量を含めて５０〜９５重量％である第
(２)項記載の農用マルチング剤、を挙げることができ
る。Means for Solving the Problems The present inventors have made intensive studies to solve the above-mentioned problems, and as a result, formed a mulching layer directly on farmland without using planar materials such as films and papers. By doing so, the labor required for installation and fixing can be reduced, and recycled materials such as paper sludge, binders composed of natural polymers, etc., fiber-containing substances such as defibrated waste paper and water-containing materials The present inventors have found that a mulching layer can be formed effectively, and have completed the present invention based on this finding. That is, the present invention provides (1) (A) one or two or more kinds of waste recycle products selected from charcoal of organic sludge and compost obtained from organic waste, (B) semi-synthetic polymer or natural Agricultural mulching characterized by spraying a mixture containing a binder comprising a polymer, (C) one or more fiber-containing substances selected from defibrated waste paper and okara, and (D) water on agricultural land. And (2) (A) one or two or more types of recycled waste products selected from charcoal of organic sludge and compost obtained from organic waste, (B) semi-synthetic polymer or natural polymer And (C) an agricultural mulching agent comprising: (C) one or more fiber-containing substances selected from defibrated waste paper and okara, and (D) water. . Further, as a preferred embodiment of the present invention, (3) (A) the content of the recycled waste product is 1 to 30% by weight as a solid content, (B) the content of the binder is 1 to 20% by weight as a solid content, (C) The content of the fiber-containing substance is 3 to 30% by weight as a solid content, and (D) the content of water is
(4) The agricultural mulching method according to (1), wherein the mixture is 50 to 95% by weight including the amount of water derived from the components (A), (B) and (C). A) The content of the recycled waste product is 1 to 30% by weight as a solid content, (B)
The content of the binder is 1 to 20% by weight as a solid content, (C)
The content of the fiber-containing substance is 3 to 30% by weight as a solid content,
(D) The water content is 50 to 95% by weight including the amount of water derived from the components (A), (B) and (C).
The agricultural mulching agent described in (2) can be exemplified.
【０００５】[0005]
【発明の実施の形態】本発明の農用マルチング方法は、
(Ａ)有機性汚泥の炭化物及び有機性廃棄物から得られる
コンポストから選ばれる１種又は２種以上の廃棄物再生
品、(Ｂ)半合成高分子又は天然高分子からなる結合剤、
(Ｃ)解繊故紙及びおからから選ばれる１種又は２種以上
の繊維含有物質及び(Ｄ)水を含有する混合物を農地に散
布するものである。また、本発明の農用マルチング剤
は、(Ａ)有機性汚泥の炭化物及び有機性廃棄物から得ら
れるコンポストから選ばれる１種又は２種以上の廃棄物
再生品、(Ｂ)半合成高分子又は天然高分子からなる結合
剤、(Ｃ)解繊故紙及びおからから選ばれる１種又は２種
以上の繊維含有物質及び(Ｄ)水を含有するものである。
本発明に用いる有機性汚泥の炭化物は、製紙プロセスか
ら排出される短繊維パルプ、炭酸カルシウム、硫酸バン
ドなどを含有するペーパースラッジを乾燥し、蒸し焼き
することにより得られるものや、下水などの活性汚泥処
理の余剰汚泥を炭化させることにより得られるもの、下
水や廃水中の汚泥を脱水、炭化させることにより得られ
るものなどである。本発明に用いる有機性廃棄物から得
られるコンポストは、わら、落ち葉、都市塵芥などの有
機性廃棄物を堆積発酵させることにより得られるもので
ある。(Ａ)成分として、有機性汚泥の炭化物及び有機性
廃棄物から得られるコンポストから選ばれる１種又は２
種以上の廃棄物再生品を含有させることにより、マルチ
ング層の吸熱性と遮光性を高め、農作物の生育を促進
し、雑草の発芽と生育を抑制することができる。ペーパ
ースラッジ、余剰汚泥、都市塵芥などは、従来は廃棄物
として処分されていたものであり、本発明は、これらの
廃棄物を有効に活用する点においても、大きい効果を有
するものである。DETAILED DESCRIPTION OF THE INVENTION The agricultural mulching method of the present invention comprises:
(A) one or more reclaimed waste products selected from organic sludge charcoal and compost obtained from organic waste, (B) a binder comprising a semi-synthetic polymer or a natural polymer,
A mixture containing (C) one or more fiber-containing substances selected from defibrated waste paper and okara and (D) water is sprayed on farmland. Further, the agricultural mulching agent of the present invention comprises (A) one or two or more kinds of recycled waste products selected from charcoal of organic sludge and compost obtained from organic waste, (B) a semi-synthetic polymer or It contains a binder comprising a natural polymer, (C) one or more fiber-containing substances selected from defibrated waste paper and okara, and (D) water.
The organic sludge carbide used in the present invention is obtained by drying and steaming paper sludge containing short fiber pulp, calcium carbonate, sulfate band and the like discharged from the papermaking process, and activated sludge such as sewage. Examples thereof include those obtained by carbonizing excess sludge of the treatment, and those obtained by dehydrating and carbonizing sludge in sewage and wastewater. The compost obtained from the organic waste used in the present invention is obtained by depositing and fermenting organic waste such as straw, fallen leaves, and municipal waste. Component (A) is one or two selected from charcoal of organic sludge and compost obtained from organic waste.
By containing more than one kind of regenerated waste, the endothermic and light-shielding properties of the mulching layer can be enhanced, the growth of agricultural crops can be promoted, and the germination and growth of weeds can be suppressed. Paper sludge, surplus sludge, municipal refuse, and the like have been conventionally disposed of as wastes, and the present invention has a great effect in terms of effectively utilizing these wastes.
【０００６】ペーパースラッジ炭化物の組成の一例を示
すと、水分１〜２重量％、灰分６５〜７５重量％を含
み、灰分の内訳は、ＳｉＯ2１５〜２０重量％、Ａｌ2Ｏ
3２０〜２５重量％、Ｆｅ2Ｏ3２重量％以下、ＣａＯ１
５〜２０重量％、ＭｇＯ３〜８重量％、Ｎａ2Ｏ１重量
％以下、Ｋ2Ｏ１重量％以下、Ｐ2Ｏ5２重量％以下、Ｃ
ｌ０.１重量％以下である。ペーパースラッジ炭化物
は、従来より土壌改良材として使用されているので、安
全上の問題はなく、アルカリ分、カリウム、リンなどを
適度に含有するので施肥効果を有し、農作物の生育促進
にも有用である。本発明の農用マルチング剤において、
(Ａ)成分として用いる有機性汚泥の炭化物及び有機性廃
棄物から得られるコンポストから選ばれる１種又は２種
以上の廃棄物再生品の含有量は、固形分として１〜３０
重量％であることが好ましく、固形分として５〜２０重
量％であることがより好ましい。(Ａ)成分の含有量が固
形分として１重量％未満であると、マルチング層の吸熱
性と遮光性が不足するおそれがある。(Ａ)成分の含有量
が固形分として３０重量％を超えると、マルチング層の
強度が不十分となるおそれがある。[0006] An example of the composition of the paper sludge carbide includes water of 1 to 2% by weight, ash of 65 to 75% by weight, and the ash content is 15 to 20% by weight of SiO 2 and Al 2 O.
3 20-25 wt%, Fe 2 O 3 2 wt% or less, CaO1
5 to 20 wt%, MgO3～8 wt%, Na 2 O1 wt% or less, K 2 O1% by weight, P 2 O 5 2% by weight, C
l0.1% by weight or less. Paper sludge carbide is conventionally used as a soil conditioner, so there is no safety problem.It contains an appropriate amount of alkali, potassium, phosphorus, etc. and has a fertilizing effect, and is also useful for promoting the growth of agricultural crops. It is. In the agricultural mulching agent of the present invention,
(A) The content of one or more kinds of recycled waste products selected from organic sludge carbide and compost obtained from organic waste used as the component is 1 to 30 as solid content.
%, More preferably 5 to 20% by weight as a solid content. If the content of the component (A) is less than 1% by weight as a solid content, the heat absorbing property and the light shielding property of the mulching layer may be insufficient. If the content of the component (A) exceeds 30% by weight as a solid content, the strength of the mulching layer may be insufficient.
【０００７】本発明に用いる半合成高分子又は天然高分
子からなる結合剤に特に制限はなく、例えば、カルボキ
シメチルセルロース又はその塩、ヒドロキシエチルセル
ロース、カルボキシメチルヒドロキシエチルセルロース
又はその塩、ヒドロキシプロピルセルロース、メチルセ
ルロース、ヒドロキシプロピルメチルセルロース、エチ
ルヒドロキシエチルセルロース、カチオン性セルロース
エーテルなどのセルロース誘導体や、にかわ、ゼラチ
ン、カゼイン、アルブミンなどのタンパク質や、コンニ
ャク粉などを挙げることができる。これらの結合剤は、
１種を単独で用いることができ、あるいは、２種以上を
組み合わせて用いることもできる。(Ｂ)成分として、結
合剤を含有させることにより、農地に適用したとき(Ｃ)
成分は(Ａ)成分とよく結合し、十分な強度を有するマル
チング層を形成することができる。本発明の農用マルチ
ング剤において、(Ｂ)成分として用いる半合成高分子又
は天然高分子からなる結合剤の含有量は、固形分として
１〜２０重量％であることが好ましく、固形分として５
〜１０重量％であることがより好ましい。(Ｂ)成分の含
有量が固形分として１重量％未満であると、マルチング
層の強度が不十分となるおそれがある。(Ｂ)成分の含有
量が固形分として２０重量％を超えると、粘度が高くな
りスムーズな噴霧散布ができにくくなるおそれがある。[0007] The binder comprising a semi-synthetic polymer or a natural polymer used in the present invention is not particularly limited, and examples thereof include carboxymethyl cellulose or a salt thereof, hydroxyethyl cellulose, carboxymethyl hydroxyethyl cellulose or a salt thereof, hydroxypropyl cellulose, methyl cellulose, and the like. Examples include cellulose derivatives such as hydroxypropylmethylcellulose, ethylhydroxyethylcellulose, and cationic cellulose ether; glue, gelatin, casein, albumin, and other proteins; and konjac powder. These binders
One kind may be used alone, or two or more kinds may be used in combination. (B) When applied to agricultural land by including a binder as a component, (C)
The component is well bonded to the component (A) and can form a mulching layer having sufficient strength. In the agricultural mulching agent of the present invention, the content of the binder composed of a semi-synthetic polymer or a natural polymer used as the component (B) is preferably 1 to 20% by weight as a solid content, and 5 to 5% as a solid content.
More preferably, it is 10 to 10% by weight. When the content of the component (B) is less than 1% by weight as a solid content, the strength of the mulching layer may be insufficient. When the content of the component (B) exceeds 20% by weight as a solid content, the viscosity may increase, and smooth spraying may not be easily performed.
【０００８】本発明に用いる解繊故紙に特に制限はな
く、例えば、故紙をパルパー、高濃度パルパー、ファイ
バーフローなどを用いて解繊することにより、あるい
は、地球釜、水平回転釜などを用いて蒸煮解繊すること
により得ることができる。解繊された故紙原質は、遠心
式クリーナーや、リバースクリーナーを用いて夾雑物を
除去することができる。おからは、豆腐製造所におい
て、豆汁を布漉ししたときに発生する繊維質を含有する
搾りかすとして得ることができる。(Ｃ)成分として、解
繊故紙及びおからから選ばれる１種又は２種以上の繊維
含有物質を含有させることにより、農地へ適用してマル
チング層を形成したとき、繊維どうしが絡み合って固結
し、マルチング層の強度を高め、土壌を保護し、保温
し、保湿する効果を高めることができる。本発明の農用
マルチング剤において、(Ｃ)成分として用いる解繊故紙
及びおからから選ばれる１種又は２種以上の繊維含有物
質の含有量は、固形分として３〜３０重量％であること
が好ましく、固形分として１５〜２５重量％であること
がより好ましい。(Ｃ)成分の含有量が固形分として３重
量％未満であると、マルチング層の強度が不十分となる
とともに、土壌の保護、保温、保湿効果が不足するおそ
れがある。(Ｃ)成分の含有量が固形分として３０重量％
を超えると、解繊故紙が分離して散布ノズルをつまらせ
るおそれがある。本発明の農用マルチング剤において、
(Ｄ)成分として用いる水の量は、(Ａ)成分、(Ｂ)成分及
び(Ｃ)成分に由来する水分の量を含めて、５０〜９５重
量％であることが好ましく、５５〜７５重量％であるこ
とがより好ましい。(Ｄ)成分の含有量が５０重量％未満
であると、粘度が高くなりすぎて、農用マルチング剤の
農地への散布が困難となるおそれがある。(Ｄ)成分の含
有量が９５重量％を超えると、粘度が低くなりすぎて、
所定の位置にマルチング層を形成することが困難とな
り、必要な厚みのマルチング層を形成するための農用マ
ルチング剤の量が過大となるおそれがある。There is no particular limitation on the defibrated waste paper used in the present invention. For example, the defibrated waste paper is defibrated using a pulper, a high-concentration pulper, a fiber flow, or the like, or an earth pot, a horizontal rotary pot or the like. It can be obtained by fibrillation. The defibrated waste paper raw material can remove impurities using a centrifugal cleaner or a reverse cleaner. Okara can be obtained as pomace containing fibrous material generated when a soybean juice is strained at a tofu mill. (C) By containing one or more kinds of fiber-containing substances selected from defibrated waste paper and okara as a component, when applied to farmland to form a mulching layer, the fibers are intertwined and consolidated. In addition, the strength of the mulching layer can be increased, and the effect of protecting the soil, keeping warm, and keeping moisture can be enhanced. In the agricultural mulching agent of the present invention, the content of one or more fiber-containing substances selected from defibrated waste paper and okara used as the component (C) may be 3 to 30% by weight as a solid content. More preferably, the solid content is 15 to 25% by weight. When the content of the component (C) is less than 3% by weight as a solid content, the strength of the mulching layer is insufficient, and the effects of protecting, warming, and moisturizing the soil may be insufficient. The content of the component (C) is 30% by weight as a solid content.
If it exceeds 300, the defibrated waste paper may be separated and the spray nozzle may be pinched. In the agricultural mulching agent of the present invention,
The amount of water used as the component (D) is preferably 50 to 95% by weight, including the amount of water derived from the components (A), (B) and (C), and is preferably 55 to 75% by weight. % Is more preferable. If the content of the component (D) is less than 50% by weight, the viscosity may be too high, and it may be difficult to spray the agricultural mulching agent on farmland. When the content of the component (D) exceeds 95% by weight, the viscosity becomes too low,
It is difficult to form a mulching layer at a predetermined position, and the amount of the agricultural mulching agent for forming a mulching layer having a required thickness may be excessive.
【０００９】本発明の農用マルチング方法において、
(Ａ)成分、(Ｂ)成分、(Ｃ)成分及び(Ｄ)成分を含有する
混合物はスラリー状となるので、農地に散布して土壌面
にマルチング層を形成する。混合物中に含まれる水は、
地中への浸透と大気中への蒸発により失われ、乾燥した
マルチング層が形成される。形成するマルチング層の厚
さに特に制限はなく、対象とする農作物の種類、気象条
件、立地条件、栽培期間などに応じて適宜選択すること
ができるが、通常は１〜１０mmであることが好ましく、
２〜８mmであることがより好ましい。(Ａ)成分、(Ｂ)成
分、(Ｃ)成分及び(Ｄ)成分を含有する混合物の農地への
散布は、ポンプ、スプレーノズルなどを用いて機械的に
行うことができるので、少人数で広い農地にマルチング
層を施工することができ、マルチフィルムを設置して固
定する場合に比べて、大幅に労力を節減することができ
る。また、農地の表面に形成されたマルチング層は、土
壌に密着しているので、押さえ土などにより固定する必
要がなく、強風が吹いても飛散するおそれがない。播種
に際しては、播種箇所のマルチング層をスコップなどの
農具を用いて除去することにより、播種に必要な土壌面
を露出させることができるので、農地現場において、的
確な位置に播種箇所を設定することができる。本発明方
法により形成されるマルチング層は、有機性汚泥の炭化
物又は有機性廃棄物から得られるコンポストのために黒
色度が高く、吸熱性、遮光性及び保湿性に優れ、土壌温
度を上昇して農作物の生育を促進する効果と、遮光して
雑草を抑制する効果が大きい。また、本発明の農用マル
チング剤は、有害物質を含有せず、生分解性を有するの
で、農作物の収穫後は、そのまま農地に鋤き込むことが
でき、回収して廃棄物として処分する必要がない。さら
に、本発明の農用マルチング剤には、カリウム、リンな
どの肥料成分を含む場合が多いので、農地に鋤き込まれ
たのちは施肥効果を発揮する。[0009] In the agricultural mulching method of the present invention,
Since the mixture containing the component (A), the component (B), the component (C) and the component (D) is in a slurry state, it is sprayed on farmland to form a mulching layer on the soil surface. The water contained in the mixture is
Loss due to infiltration into the ground and evaporation to the atmosphere, forming a dry mulching layer. The thickness of the mulching layer to be formed is not particularly limited, and can be appropriately selected depending on the type of the target crop, weather conditions, location conditions, cultivation period, and the like, but is preferably 1 to 10 mm. ,
More preferably, it is 2 to 8 mm. The spraying of the mixture containing the components (A), (B), (C) and (D) on farmland can be performed mechanically using a pump, a spray nozzle, etc. A mulching layer can be constructed on a large farmland, and labor can be greatly reduced as compared with a case where a multi-film is installed and fixed. In addition, since the mulching layer formed on the surface of the farmland is in close contact with the soil, it is not necessary to fix the mulching layer with holding soil or the like, and there is no possibility that the mulching layer will be scattered even when a strong wind blows. At the time of sowing, by removing the mulching layer at the sowing point using an agricultural tool such as a scoop, it is possible to expose the soil surface required for sowing, so at the farmland site, set the sowing point at an accurate position Can be. The mulching layer formed by the method of the present invention has a high blackness due to compost obtained from organic sludge charcoal or organic waste, and has excellent heat absorption, light-shielding properties and moisture retention, and increases soil temperature. The effect of promoting the growth of crops and the effect of suppressing weeds by shading are great. Further, since the agricultural mulching agent of the present invention does not contain harmful substances and has biodegradability, it can be plowed into farmland as it is after harvesting the crop, and it is necessary to collect and dispose it as waste. Absent. Furthermore, since the agricultural mulching agent of the present invention often contains fertilizer components such as potassium and phosphorus, it exhibits a fertilizing effect after being plowed into farmland.
【００１０】[0010]
【実施例】以下に、実施例を挙げて本発明をさらに詳細
に説明するが、本発明はこれらの実施例によりなんら限
定されるものではない。なお、実施例及び比較例におい
ては、農地の一角に同一条件となるように、実施例１、
比較例１、実施例２、比較例２、実施例３のマルチング
をこの順に設置し、それぞれのマルチングに１列１０カ
所の播種箇所を２列に設けた。各マルチングそれぞれ２
０カ所の播種箇所にダイコンの種子を播種し、２０本中
１８本が発芽するまでの日数を記録した。また、播種１
カ月後に２０本の苗の重量を測定し、比較例１の苗重量
に対する比率を求めるとともに、１ｍ2当たりに発生し
ている雑草数を数え、同様に比較例１の雑草数に対する
比率を求めた。 実施例１ ペーパースラッジ１５重量部、ヒドロキシエチルセルロ
ース８重量部、水分率５０重量％の解繊新聞故紙４０重
量部及び水３７重量部を混合してスラリー状とし、農用
マルチング剤を調製した。この農用マルチング剤を農地
に散布して、乾燥後の厚さ約５mmのマルチング層を形成
した。マルチング層の一部をスコップで取り除いて２０
カ所の播種箇所を設け、ダイコン（種子名：天風）の種
子を播種した。播種後６日で、１８本が発芽した。播種
１カ月後の苗の重量は、後述する比較例１の苗の１.１
倍であった。また、１ｍ2当たりの雑草数は、比較例１
の１.１倍であった。 実施例２ 下水処理場の余剰汚泥の炭化物１０重量部、カルボキシ
メチルセルロース１０重量部、水分率５０重量％の解繊
新聞故紙３０重量部及び水５０重量部を混合してスラリ
ー状とし、農用マルチング剤を調製した。この農用マル
チング剤を農地に散布して、乾燥後の厚さ約５mmのマル
チング層を形成した。実施例１と同様にして、２０カ所
の播種箇所にダイコン（種子名：天風）の種子を播種し
た。播種後６日で、１８本が発芽した。播種１カ月後の
苗の重量は、後述する比較例１の苗の１.１倍であっ
た。また、１ｍ2当たりの雑草数は、比較例１の１.０倍
であった。 実施例３ ペーパースラッジ３０重量部、コンニャク粉１０重量
部、水分率８０重量％のおから５０重量部及び水１０重
量部を混合してスラリー状とし、農用マルチング剤を調
製した。この農用マルチング剤を農地に散布して、乾燥
後の厚さ約５mmのマルチング層を形成した。実施例１と
同様にして、２０カ所の播種箇所にダイコン（種子名：
天風）の種子を播種した。播種後７日で、１８本が発芽
した。播種１カ月後の苗の重量は、後述する比較例１の
苗の１.２倍であった。また、１ｍ2当たりの雑草数は、
比較例１の１.１倍であった。 比較例１ ポリ塩化ビニル製の黒色マルチフィルム［ＪＡ製］に２
列に２０個の穴をあけて播種箇所とし、農地に設置、固
定した。実施例１と同様にして、２０カ所の播種箇所に
ダイコン（種子名：天風）の種子を播種した。播種後６
日で、１８本が発芽した。播種１カ月後の１本の苗の重
量は、平均４０ｇであった。また、１ｍ2当たりの雑草
数は、平均４.６本であった。 比較例２ 白色覆土剤［栗田工業(株)、コンカバー］を農地に散布
して、乾燥後の厚さ約５mmのマルチング層を形成した。
実施例１と同様にして、２０カ所の播種箇所にダイコン
（種子名：天風）の種子を播種した。播種後８日で、１
８本が発芽した。播種１カ月後の苗の重量は、比較例１
の苗の０.８倍であった。また、１ｍ2当たりの雑草数
は、比較例１の１.３倍であった。実施例１〜３及び比
較例１〜２の結果を、第１表に示す。EXAMPLES The present invention will be described in more detail with reference to the following Examples, which should not be construed as limiting the present invention. In Examples and Comparative Examples, Example 1,
The mulchings of Comparative Example 1, Example 2, Comparative Example 2, and Example 3 were installed in this order, and each mulching was provided with 10 sowing locations in one row in two rows. 2 for each mulching
Radish seeds were sown at 0 sowing locations, and the number of days until 18 out of 20 germinated were recorded. Seeding 1
After a month, the weight of 20 seedlings was measured, the ratio to the weight of the seedling of Comparative Example 1 was determined, the number of weeds generated per 1 m 2 was counted, and the ratio to the number of weeds of Comparative Example 1 was similarly determined. . Example 1 An agricultural mulching agent was prepared by mixing 15 parts by weight of paper sludge, 8 parts by weight of hydroxyethyl cellulose, 40 parts by weight of waste paper of fibrillated newspaper having a water content of 50% by weight, and 37 parts by weight of water. This agricultural mulching agent was sprayed on farmland to form a mulching layer having a thickness of about 5 mm after drying. Remove a part of the mulching layer with a scoop and remove
Two sowing points were provided, and seeds of radish (seed name: Tenfu) were sowed. Six days after sowing, 18 germinated. The weight of the seedling one month after sowing was 1.1 for the seedling of Comparative Example 1 described later.
It was twice. In addition, the number of weeds per 1 m 2 is shown in Comparative Example 1.
It was 1.1 times. Example 2 10 parts by weight of excess sludge charcoal, 10 parts by weight of carboxymethylcellulose, 30 parts by weight of defibrated newspaper waste paper having a water content of 50% by weight and 50 parts by weight of water in a sewage treatment plant to form a slurry, and an agricultural mulching agent was used. Was prepared. This agricultural mulching agent was sprayed on farmland to form a mulching layer having a thickness of about 5 mm after drying. In the same manner as in Example 1, radish (seed name: Tenfu) seeds were sown at 20 sowing locations. Six days after sowing, 18 germinated. The weight of the seedling one month after sowing was 1.1 times that of the seedling of Comparative Example 1 described later. The number of weeds per 1 m 2 was 1.0 times that of Comparative Example 1. Example 3 An agricultural mulching agent was prepared by mixing 30 parts by weight of paper sludge, 10 parts by weight of konjac powder, 50 parts by weight of okara of 80% by weight, and 10 parts by weight of water. This agricultural mulching agent was sprayed on farmland to form a mulching layer having a thickness of about 5 mm after drying. In the same manner as in Example 1, radish (seed name:
Seeds). Seven days after sowing, 18 germinated. One month after sowing, the weight of the seedling was 1.2 times that of the seedling of Comparative Example 1 described later. In addition, weed per 1m 2 is,
It was 1.1 times that of Comparative Example 1. Comparative Example 1 Black multi-film made of polyvinyl chloride [manufactured by JA]
20 holes were drilled in the row to form a sowing site, which was installed and fixed on farmland. In the same manner as in Example 1, radish (seed name: Tenfu) seeds were sown at 20 sowing locations. 6 after sowing
By day, 18 germinated. One month after seeding, the weight of one seedling was 40 g on average. Furthermore, weeds per 1 m 2 was an average 4.6 present. Comparative Example 2 A white soil covering agent [Kurita Kogyo Co., Ltd., Concover] was sprayed on farmland to form a mulching layer having a thickness of about 5 mm after drying.
In the same manner as in Example 1, radish (seed name: Tenfu) seeds were sown at 20 sowing locations. 8 days after sowing, 1
Eight germinated. The weight of the seedling one month after sowing was determined according to Comparative Example 1.
0.8 times that of the seedlings. In addition, the number of weeds per 1 m 2 was 1.3 times that of Comparative Example 1. Table 1 shows the results of Examples 1 to 3 and Comparative Examples 1 and 2.
【００１１】[0011]
【表１】 [Table 1]
【００１２】第１表に見られるように、本発明の農用マ
ルチング剤を用いた実施例１〜３においては、９０％発
芽日数は、黒色マルチフィルムを用いた比較例１と同じ
又は１日遅れであって、白色覆土剤を用いた比較例２よ
りも早い。実施例１〜３の１カ月後の苗重量は、比較例
１、比較例２のいずれの苗重量よりも重く、ダイコンの
生育が促進されている。また、１カ月後の雑草本数は、
黒色マルチフィルムを用いた比較例１と同等又はわずか
に多い程度で、白色覆土剤を用いた比較例２よりは明ら
かに少ない。As shown in Table 1, in Examples 1 to 3 using the agricultural mulching agent of the present invention, 90% germination days were the same as or 1 day behind Comparative Example 1 using a black mulch film. Which is faster than Comparative Example 2 using a white soil covering agent. The weight of the seedlings after one month of Examples 1 to 3 is heavier than the weight of both seedlings of Comparative Example 1 and Comparative Example 2, and the growth of radish is promoted. Also, the number of weeds one month later is
It is equivalent to or slightly more than that of Comparative Example 1 using a black multi-film, and is clearly smaller than Comparative Example 2 using a white soil covering agent.
【００１３】[0013]
【発明の効果】本発明の農用マルチング方法及び農用マ
ルチング剤によれば、マルチング層の形成のための労力
が少なく、農作物収穫後の廃棄物処理を行う必要がな
く、保温性及び遮光性に優れたマルチング層を土壌面に
形成し、農作物の発芽と生育を促進し、雑草を抑制する
ことができる。According to the agricultural mulching method and agricultural mulching agent of the present invention, the labor for forming the mulching layer is small, there is no need to carry out waste treatment after harvesting the crops, and the heat retention and light shielding properties are excellent. A mulching layer is formed on the soil surface to promote germination and growth of crops and to suppress weeds.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 柴田 健 東京都新宿区西新宿三丁目４番７号 栗田 工業株式会社内 Ｆターム(参考） 2B024 DA03 DA06 DB10 DC03 ──────────────────────────────────────────────────続 き Continuation of the front page (72) Inventor Ken Shibata F-term (reference) in Kurita Kogyo Co., Ltd. 3-4-7 Nishishinjuku, Shinjuku-ku, Tokyo 2B024 DA03 DA06 DB10 DB10 DC03
Claims (2)
物から得られるコンポストから選ばれる１種又は２種以
上の廃棄物再生品、（Ｂ）半合成高分子又は天然高分子
からなる結合剤、（Ｃ）解繊故紙及びおからから選ばれ
る１種又は２種以上の繊維含有物質及び（Ｄ）水を含有
する混合物を農地に散布することを特徴とする農用マル
チング方法。1. A regenerated product of one or more kinds of waste materials selected from (A) charcoal of organic sludge and compost obtained from organic waste, and (B) a semi-synthetic polymer or a natural polymer. An agricultural mulching method comprising spraying a mixture containing a binder, (C) one or more fiber-containing substances selected from defibrated waste paper and okara, and (D) water on agricultural land.
物から得られるコンポストから選ばれる１種又は２種以
上の廃棄物再生品、（Ｂ）半合成高分子又は天然高分子
からなる結合剤、（Ｃ）解繊故紙及びおからから選ばれ
る１種又は２種以上の繊維含有物質及び（Ｄ）水を含有
することを特徴とする農用マルチング剤。2. A regenerated product of one or more kinds of waste materials selected from (A) charcoal of organic sludge and compost obtained from organic waste, and (B) a semi-synthetic polymer or a natural polymer. An agricultural mulching agent comprising: a binder; (C) one or more fiber-containing substances selected from defibrated waste paper and okara; and (D) water.