IT202000002683A1 - Vernice - Google Patents
Vernice Download PDFInfo
- Publication number
- IT202000002683A1 IT202000002683A1 IT102020000002683A IT202000002683A IT202000002683A1 IT 202000002683 A1 IT202000002683 A1 IT 202000002683A1 IT 102020000002683 A IT102020000002683 A IT 102020000002683A IT 202000002683 A IT202000002683 A IT 202000002683A IT 202000002683 A1 IT202000002683 A1 IT 202000002683A1
- Authority
- IT
- Italy
- Prior art keywords
- paint
- fire
- bis
- fraction
- test
- Prior art date
Description
Titolo VERNICE Domanda di brevetto per invenzione avente per titolo ?VERNICE?
DESCRIZIONE
Forma oggetto della presente invenzione una vernice particolarmente adatta alla sua applicazione su una superficie, allo scopo di rendere incombustibile, in caso di incendio, la superficie stessa.
Il trovato oggetto della presente domanda di brevetto trova applicazione nel settore della finitura di elementi, prevalentemente destinati all?edilizia, che presentino caratteristiche compatibili con quanto richiesto dalla normativa vigente, in particolare per ci? che attiene le caratteristiche di reazione al fuoco.
Notoriamente con l?espressione ?reazione al fuoco? si intende il grado di partecipazione di un materiale combustibile al fuoco al quale ? sottoposto.
La reazione al fuoco ? una caratteristica del materiale che viene convenzionalmente espressa in ?classi di reazione al fuoco?.
La definizione di queste classi ? regolamentata da un quadro normativo ben preciso e ben definito e da una serie di prove di laboratorio che tengono conto dell'infiammabilit?, della velocit? di propagazione della fiamma, del gocciolamento, della post-incandescenza e dello sviluppo di calore.
La reazione al fuoco consiste pertanto in una delle misure antincendio di protezione da perseguire per garantire un adeguato livello di sicurezza in condizioni di incendio, ed in particolare nella fase di prima propagazione dell'incendio (pre-flashover).
L?espressione ?reazione al fuoco? identifica quindi il comportamento di un materiale che, con la sua decomposizione, partecipa al fuoco al quale ? stato sottoposto, in specifiche condizioni e ne verifica il comportamento in caso di innesco di fiamma..
In relazione al suddetto grado di partecipazione, ai materiali viene assegnata una Classificazione con valori variabili tra 0 e 5, dove al valore ?0? si attribuisce la caratteristica di non partecipazione al fuoco e quindi caratteristica di materiale non combustibile.
La Classificazione italiana ? stata sostituita da una omonima europea definita dalla norma UNI EN 13501-1 ?Classificazione al fuoco dei prodotti e degli elementi da costruzione ? Parte 1 ? Classificazione in base ai risultati delle prove di reazione al fuoco?; la norma individua le cosiddette ?Euroclassi? dalla A1 (materiale o prodotto incombustibile) alla F con l?aumentare della partecipazione alla combustione.
La Classificazione di reazione al fuoco di un materiale non dipende solo dalle caratteristiche intrinseche del materiale stesso, ma anche dal suo impiego e dalla sua posa in opera, con eccezione dei materiali incombustibili (classe A1).
Con l?espressione ?protezione dal fuoco? si intendono invece tutti quegli interventi atti a contenere i danni derivanti da un incendio e tali interventi possono essere attivi o passivi. Con il termine ?attivi? si intendono gli interventi che mirano a ridurre gli effetti dell?incendio prevenendolo mediante una serie di dispositivi rilevatori o mediante interventi tempestivi per estinguere l?incendio stesso.
Con il termine ?passivi? si intendono quegli interventi che si pongono l?obiettivo di limitare gli effetti dell?incendio per consentire l?evacuazione e la messa in sicurezza delle persone. Nelle progettazioni antincendio viene data una grande importanza alle fasi di innesco dell'incendio e pertanto viene richiesto che i materiali in vista siano difficilmente infiammabili o meglio incombustibili.
Stato dell?arte
Allo stato dell?arte risultano note vernici ignifughe ottenute miscelando emulsioni di resina con ritardanti di fiamma.
Allo stato dell?arte risultano note soluzioni relative alla realizzazione di vernici schiumabili per l?uso in telai di ferro o vernici ignifughe e termoisolanti formate da scisti, carburo di silicio e aggregati di polverosi insieme a un legante al silicato alcalino.
La domanda di brevetto GB2203157 descrive una composizione di vernice ignifuga a base di silicati che si scioglie progressivamente in condizioni di incendio per fornire uno strato protettivo fuso che impedisce l'accesso dell'ossigeno ai dintorni del fuoco.
Allo stato dell?arte risulta inoltre nota la prassi di aggiungere alle composizioni delle vernici delle quantit? di zeolite secca finemente polverizzata al fine di ridurne la conduttivit? termica e ridurre la propagazione della fiamma in caso di incendio.
Il principale svantaggio dello soluzioni sopra esposta risulta essere sostanzialmente la necessit? di una miscelazione con elevato grado di precisione nel sito di applicazione oltre al fatto che sono composizioni costose.
Inoltre, molte delle soluzioni note risultano idonee per determinate superfici o materiali e presentano significative limitazioni nel rallentare la propagazione della fiamma durante un evento di incendio reale quando esistono temperature medie, alte o molto alte.
Risulta, comunque, che le vernici intumescenti attualmente in commercio, essendo composte da resine, presentano comunque un certo grado di infiammabilit? e quindi una certa partecipazione all'incendio.
Ne consegue che si renda necessario la realizzazione di rivestimenti che presentino il minimo grado di partecipazione all'incendio e, soprattutto, non producano fiamme qualora sottoposti ad elevate temperature o a fiamme di innesco.
Scopo del trovato oggetto della presente domanda di brevetto ? pertanto quello di realizzare una vernice che abbia di per s? caratteristiche di incombustibilit? del tipo Classe A1.
Ulteriore scopo del trovato oggetto della presente domanda di brevetto ? quello di realizzare una composizione di vernice, detta vernice essendo applicabile a diversi materiali, al fine di ottenere una serie di superfici aventi caratteristiche in incombustibilit? (Classe A1).
Ulteriore scopo del trovato oggetto della presente domanda di brevetto ? quello di realizzare una composizione di vernice applicabile a diversi materiali, che consenta di migliorare le caratteristiche di reazione al fuoco del materiale stesso.
Questo e ulteriori scopi verranno dedotti dalla descrizione di una composizione di vernice le cui componenti combustibili sono presenti in minima percentuale, detta vernice essendo sostanzialmente costituita da una prima frazione liquida e da una seconda frazione solida, dette prima frazione liquida e seconda frazione solida essendo miscelate in situ.
Come per qualsiasi vernice nota allo stato dell?arte, la applicazione della stessa su qualsiasi supporto comporta la creazione di uno strato sottile adeso alla superficie stessa e successivo indurimento.
La vernice oggetto della presente domanda di brevetto risulta pertanto composta da una un prima frazione liquida e da una seconda frazione solida.
In particolare, la prima frazione liquida ? costituita da una soluzione acquosa di vinilversatato, idrossietilcellulosa, 2-amminoetanolo, calce idrata, miscela di bis (2-metil propil) pentanoato e bis (2-metilpropil) esandioato, glicole propilenico, sali di acidi policarbossilici, benzene e mono C10-13-alchil derivati, inerte liquido non volatile (non VOC), carbonato di calcio e biossido di titanio.
Oltre ai componenti primari sopra elencati, la prima frazione liquida pu? comprendere una miscela di metilcloroisotiazolinone e metilisotiazolinone oppure acido acrilico, dette sostanze essendo presenti nella soluzione al massimo per lo 0,1% del totale.
La seconda frazione solida della vernice, oggetto della presente domanda di brevetto, ? costituita da cemento, particolarmente ma non esclusivamente cemento portland.
In particolare, la composizione della prima frazione liquida e della seconda frazione solida della vernice oggetto della presente domanda di brevetto, ? variabile nelle percentuali elencate nella Tabella 1 di seguito riportata:
Tabella 1
La soluzione acquosa comprendente le sostanze sopra elencate pu? comprendere una miscela di metilcloroisotiazolinone e metilisotiazolinone oppure acido acrilico al massimo per lo 0,1% sul totale.
In una modalit? applicativa esemplificativa, ma non esclusiva, la prima frazione liquida comprendente le componenti sopra elencate viene inserita in un primo contenitore mentre la seconda frazione solida comprendente il cemento viene inserito in un secondo contenitore.
A necessit?, il cemento viene inserito nel primo contenitore e quindi mescolato nella prima frazione liquida.
Successivamente, la miscela di ?cemento ? prima frazione liquida? viene applicata alla superficie da trattare e viene atteso il tempo di indurimento della miscela stessa.
Validazione sperimentale
Per la valutazione della bont? ed efficacia della reazione al fuoco di un materiale a cui la vernice ? stata applicata, la vernice ? stata sottoposta alla prova di reazione al fuoco di non combustibilit? secondo la norma UNI EN ISO 1182:2010.
Come da procedura, i campioni sono costituiti da una serie di provette cilindriche, diametro 45 mm altezza 50 mm nominali di pittura.
Le provette sono state condizionate per almeno due settimane ad una temperatura di (23+-2) ?C ed al (50+-5)% di umidit? relativa, come previsto dalla norma UNIEN 13238:2010.
Successivamente le provette sono state condizionate in stufa ventilata alla temperatura di (60+-5) ?C per 24h e poi raffreddate a temperatura ambiente in essiccatoio a sali di cloruro di calcio, fino al momento della prova.
La prova consiste nell'introduzione della miscela ?cemento ? prima fazione liquida? in una serie di provette; ciascuna provetta viene quindi inserita in un apposito forno avente temperatura pari a (50+-5)?C, dopo il periodo di condizionamento.
La prova viene ripetuta cinque volte, ottenendo poi un dato medio utile alla classificazione. Durante la prova sono rilevate le temperature finali e massime del forno e della provetta, la massa iniziale e finale della provetta e la produzione di fiamme, al fine di determinare i seguenti parametri:
? la durata di eventuali fiamme continue;
? l'aumento di temperatura del forno registrato dalle termocoppie previste;
? la perdita di massa di ciascuna provetta.
I risultati sono:
? media Atf 3 ?C
? media fiamme persistenti 0 s
? media perdita massa 21%
Nello stesso periodo ? stata fatta un'altra prova di reazione al fuoco con determinazione del potere calorifico secondo la norma UNI EN ISO 1716:2010.
L'oggetto della prova ? costituito da 3 provette di circa 0,5 g ciascuna con finemente macinata la vernice.
Le provette sono state condizionate fino al raggiungimento della massa costante ad una temperatura di (23+-2) ?C ed al (50+-5)% di umidit? relativa, come previsto dalla norma UNI EN 13238:2010.
Claims (3)
- La prova consiste dell'introduzione di ciascuna provetta, dopo il periodo di condizionamento e misurazione della massa, in un crogiolo contenuto all'interno del calorimetro automatico di Mahler, il quale viene chiuso ermeticamente e riempito con 3 Mpa di ossigeno. Dopo aver stabilizzato la temperatura del sistema all'interno di un bagno d'acqua, si procede alla combustione della provetta mediante un collegamento elettrico. Il sistema automatico determina il potere calorifico superiore misurando l'aumento di temperatura del bagno d'acqua. I risultati sono classificati in ?PCS 0,1 MJ/kg? secondo la norma UNI EN ISO 1716:2010. Dopo le due prove effettuate si ? proceduto, alla classificazione della vernice determinata sulla base dei valori ottenuti mediante misurazione, in linea al paragrafo 2,6 della guida ILAC G8:03/2009 ?Guidelines on the reporting of compliance with specification?, avendo soddisfatto i requisiti sulle misure e sulle apparecchiature definiti nella norma della prova. Stante i risultati delle prove sopra riportate, la vernice oggetto della presente domanda di brevetto in relazione al suo comportamento di reazione al fuoco ? stata classificata in Classe A1/A1 FL in accordo con la norma UNI EN 13501-1:2009. RIVENDICAZIONI 1) Vernice costituita da una prima frazione liquida acquosa e da una seconda frazione solida caratterizzata dal fatto che - la prima frazione liquida acquosa comprende vinil-versatato, idrossietilcellulosa, 2-amminoetanolo, calce idrata, una miscela di bis (2-metil propil) pentanoato e bis (2-metilpropil) esandioato, glicole propilenico, sali di acidi policarbossilici, benzene e mono C10-13-alchil derivati, inerte liquido non volatile, carbonato di calcio e biossido di titanio; - la seconda frazione solida ? costituita da cemento.
- 2) Vernice come alla rivendicazione 1 caratterizzata dal fatto che le componenti della prima frazione acquosa e della seconda frazione solida sono presenti negli intervalli di valori espressi in percentuale sul totale: - 30-40% acqua; - 2-3% vinil-versatato; - 0,2-0,6% idrossietilcellulosa; - 0-0,8% 2-amminoetanolo; - 8-11% calce idrata; - 0,2-1% miscela di bis (2-metil propil) pentanoato e bis (2-metilpropil) esandioato; - 0,1-0,5% di glicole propilenico; - 0-0,2% di sali di acidi policarbossilici; - 0,1-0,3% di benzene e mono C10-13-alchil derivati; - 0-0 ,2% di inerte liquido non volatile; - 30-40% di carbonato di calcio; - 1-3% di titanio biossido; - 14-20% di cemento.
- 3) Vernice come alla rivendicazioni precedenti caratterizzata dal fatto che