IN2012DN05089A - - Google Patents
Download PDFInfo
- Publication number
- IN2012DN05089A IN2012DN05089A IN5089DEN2012A IN2012DN05089A IN 2012DN05089 A IN2012DN05089 A IN 2012DN05089A IN 5089DEN2012 A IN5089DEN2012 A IN 5089DEN2012A IN 2012DN05089 A IN2012DN05089 A IN 2012DN05089A
- Authority
- IN
- India
- Prior art keywords
- steel material
- less
- mass
- concentration
- further containing
- Prior art date
Abstract
A high strength steel material which is excellent in delayed fracture resistance containing, by mass%, C: 0.10 5 to 0.55%, Si: 0.01 to 3%, and Mn: 0.1 to 2%, further containing one or both of V: 1.5% or less and Mo: 3.0% or less, the contents of V and Mo satisfying V+1/2Mo>0.4%, further containing one or more of Cr: 0.05 to 1.5%, Nb: 0.001 to 0.05%, Cu: 0.01 to 48, Ni: 0.01 to 4%, and B: 10 0.0001 to 0.005%, and having a balance of Fe and unavoidable impurities, the structure being a mainly tempered martensite structure, the surface of the steel material being formed with (a) a nitrided layer having a thickness from the surface of the steel material of 200 15 p or more and a nitrogen concentration of 12.0 mass% or less and higher than the nitrogen concentration of the steel material by 0.02 mass% or more and (b) a low carbon region having a depth from the surface of the steel material of 100 p or more to 1000 p or less and having 20 a carbon concentration of 0.05 mass% or more and 0.9 time or less the carbon concentration of the steel material.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2010054649 | 2010-03-11 | ||
PCT/JP2011/056481 WO2011111872A1 (en) | 2010-03-11 | 2011-03-11 | High-strength steel and high-strength bolt with excellent resistance to delayed fracture, and manufacturing method therefor |
Publications (1)
Publication Number | Publication Date |
---|---|
IN2012DN05089A true IN2012DN05089A (en) | 2015-10-09 |
Family
ID=44563661
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
IN5089DEN2012 IN2012DN05089A (en) | 2010-03-11 | 2011-03-11 |
Country Status (7)
Country | Link |
---|---|
US (1) | US20120247618A1 (en) |
EP (1) | EP2546379B1 (en) |
JP (1) | JP5177323B2 (en) |
KR (1) | KR101366375B1 (en) |
CN (1) | CN102812145A (en) |
IN (1) | IN2012DN05089A (en) |
WO (1) | WO2011111872A1 (en) |
Families Citing this family (36)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2679701B1 (en) * | 2011-02-23 | 2017-07-12 | Dowa Thermotech Co., Ltd. | Manufacturing method of a nitrided steel member |
US20130284319A1 (en) * | 2012-04-27 | 2013-10-31 | Paul M. Novotny | High Strength, High Toughness Steel Alloy |
BR112014030346B1 (en) * | 2012-06-20 | 2020-05-05 | Nippon Steel & Sumitomo Metal Corp | tubular materials from oil fields and production methods |
MX2015005321A (en) * | 2012-11-05 | 2015-07-14 | Nippon Steel & Sumitomo Metal Corp | Low-alloy steel for oil well pipes which has excellent sulfide stress cracking resistance, and method for manufacturing low-alloy steel for oil well pipes. |
CN102943210B (en) * | 2012-11-09 | 2015-02-04 | 谢亚平 | High-strength bolt and processing method thereof |
KR20140121229A (en) * | 2013-04-05 | 2014-10-15 | 태양금속공업주식회사 | A manufacturing method of steel bolt having high tensile strength |
TWI551697B (en) | 2013-06-07 | 2016-10-01 | Nippon Steel & Sumitomo Metal Corp | Heat treatment steel and its manufacturing method |
NL2011269C2 (en) * | 2013-08-05 | 2015-02-09 | Onderzoekscentrum Voor Aanwending Van Staal N V | Structure for use in a corrosive environment. |
JP6422176B2 (en) * | 2014-08-29 | 2018-11-14 | 日産自動車株式会社 | Steel for high-strength bolts and high-strength bolts |
CN104313492B (en) * | 2014-11-07 | 2017-04-12 | 广东鼎耀工程技术有限公司 | PC steel bar with high strength and toughness and heat treatment method thereof |
DE102014017275A1 (en) * | 2014-11-18 | 2016-05-19 | Salzgitter Flachstahl Gmbh | High strength air hardening multiphase steel with excellent processing properties and method of making a strip of this steel |
CN107709594B (en) * | 2015-06-29 | 2020-03-20 | 日本制铁株式会社 | Bolt |
CN105861919A (en) * | 2016-06-14 | 2016-08-17 | 江苏永昊高强度螺栓有限公司 | Production process of high-strength bolt |
JP6614349B2 (en) * | 2016-07-05 | 2019-12-04 | 日本製鉄株式会社 | Rolled wire rod |
CN106521316B (en) * | 2016-11-15 | 2018-08-07 | 江阴兴澄特种钢铁有限公司 | Carbon and low-alloy round steel and its manufacturing method in a kind of fastener high-hardenability |
CN106756516B (en) * | 2017-02-07 | 2018-06-08 | 和县隆盛精密机械有限公司 | A kind of alloy-steel casting and its casting technique suitable for mechanical arm clamping screw |
CN107058705A (en) * | 2017-02-17 | 2017-08-18 | 江苏佳杰特种螺钉有限公司 | A kind of production technology for the fastener applied in high ferro |
RU2635641C1 (en) * | 2017-03-28 | 2017-11-14 | Юлия Алексеевна Щепочкина | Cast steel |
EP3640357A4 (en) * | 2017-06-15 | 2020-09-30 | Nippon Steel Corporation | Rolled wire for spring steel |
CN107513664A (en) * | 2017-07-10 | 2017-12-26 | 安徽长江紧固件有限责任公司 | A kind of torsion shear type high tensile bolt and its processing technology |
CN107604243B (en) * | 2017-08-09 | 2019-10-08 | 宁波市镇海甬鼎紧固件制造有限公司 | A kind of high-strength bolt material and preparation method thereof |
JP2019124481A (en) * | 2018-01-12 | 2019-07-25 | 株式会社神戸製鋼所 | Residual stress measurement method |
CN111655895B (en) * | 2018-01-30 | 2023-03-14 | 日产自动车株式会社 | Bolt and fastening structure |
JP7134411B2 (en) | 2018-01-30 | 2022-09-12 | 日産自動車株式会社 | bolt |
CN109266964B (en) * | 2018-10-25 | 2021-03-05 | 青岛天赢智能工业股份有限公司 | Production and machining process of steel forging |
JP7479794B2 (en) * | 2019-04-16 | 2024-05-09 | 高周波熱錬株式会社 | PC steel with excellent delayed fracture resistance and its manufacturing method |
WO2020230872A1 (en) * | 2019-05-14 | 2020-11-19 | 日本製鉄株式会社 | Bolt and steel material for bolt |
JP7464832B2 (en) | 2019-05-14 | 2024-04-10 | 日本製鉄株式会社 | Bolts and bolt steel |
WO2021106086A1 (en) * | 2019-11-26 | 2021-06-03 | 日本製鉄株式会社 | Steel and bearing |
CN113322410B (en) * | 2020-02-28 | 2022-06-28 | 宝山钢铁股份有限公司 | High-strength bolt steel with excellent delayed fracture resistance and preparation method thereof |
CN111931309B (en) * | 2020-08-24 | 2022-09-09 | 长江水利委员会长江科学院 | Method for simulating tensile hardening softening fracture of anchor rod/anchor cable structure |
CN112795854A (en) * | 2020-12-23 | 2021-05-14 | 石家庄钢铁有限责任公司 | High-strength fastener bolt steel and production method thereof |
CN115433871B (en) * | 2021-06-02 | 2023-07-07 | 宝山钢铁股份有限公司 | High-strength steel resistant to hydrogen embrittlement delayed fracture and manufacturing method thereof |
CN114058974B (en) * | 2021-11-30 | 2022-09-13 | 马鞍山钢铁股份有限公司 | 15.9-grade corrosion-resistant high-strength bolt steel and production method and heat treatment method thereof |
CN115386803B (en) * | 2022-08-31 | 2023-07-25 | 马鞍山钢铁股份有限公司 | Non-quenched and tempered steel for high-strength and high-toughness wind power bolts and production method thereof |
CN116445829B (en) * | 2023-06-16 | 2023-09-08 | 中国矿业大学(北京) | Corrosion-resistant anchor rod and production process thereof |
Family Cites Families (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH08165557A (en) * | 1994-12-13 | 1996-06-25 | Sumitomo Metal Ind Ltd | Production of pitting resisting soft-nitrided gear |
JPH10141341A (en) * | 1996-11-13 | 1998-05-26 | Nkk Corp | High strength bolt excellent in delayed fracture |
JPH10226817A (en) * | 1996-12-11 | 1998-08-25 | Sumitomo Metal Ind Ltd | Production of steel for soft-nitriding and soft-nitrided parts using this steel |
JP3754788B2 (en) * | 1997-03-12 | 2006-03-15 | 中央発條株式会社 | Coil spring with excellent delayed fracture resistance and manufacturing method thereof |
JP2000337332A (en) * | 2000-01-01 | 2000-12-05 | Kobe Steel Ltd | High strength bolt excellent in delayed fracture resistance |
JP2000337334A (en) * | 2000-01-01 | 2000-12-05 | Kobe Steel Ltd | High structure bolt excellent in delayed fracture resistance |
JP3851533B2 (en) * | 2001-10-05 | 2006-11-29 | 株式会社神戸製鋼所 | High-strength non-tempered upset bolt wire, method for manufacturing the same, and high-strength non-tempered upset bolt |
JP5251632B2 (en) * | 2008-05-13 | 2013-07-31 | 新日鐵住金株式会社 | High strength steel material with excellent delayed fracture resistance, high strength bolt and manufacturing method thereof |
JP5251633B2 (en) * | 2008-05-13 | 2013-07-31 | 新日鐵住金株式会社 | High strength steel material with excellent delayed fracture resistance, high strength bolt and manufacturing method thereof |
-
2011
- 2011-03-11 EP EP20110753527 patent/EP2546379B1/en not_active Not-in-force
- 2011-03-11 IN IN5089DEN2012 patent/IN2012DN05089A/en unknown
- 2011-03-11 WO PCT/JP2011/056481 patent/WO2011111872A1/en active Application Filing
- 2011-03-11 US US13/515,444 patent/US20120247618A1/en not_active Abandoned
- 2011-03-11 CN CN201180013427XA patent/CN102812145A/en active Pending
- 2011-03-11 JP JP2012502334A patent/JP5177323B2/en not_active Expired - Fee Related
- 2011-03-11 KR KR1020127010100A patent/KR101366375B1/en active IP Right Grant
Also Published As
Publication number | Publication date |
---|---|
CN102812145A (en) | 2012-12-05 |
EP2546379B1 (en) | 2015-04-29 |
US20120247618A1 (en) | 2012-10-04 |
WO2011111872A1 (en) | 2011-09-15 |
JP5177323B2 (en) | 2013-04-03 |
KR20120056879A (en) | 2012-06-04 |
EP2546379A4 (en) | 2013-08-07 |
EP2546379A1 (en) | 2013-01-16 |
KR101366375B1 (en) | 2014-02-24 |
JPWO2011111872A1 (en) | 2013-06-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
IN2012DN05089A (en) | ||
EP2546380A4 (en) | High-strength steel and high-strength bolt with excellent resistance to delayed fracture, and manufacturing method therefor | |
IN2014DN10254A (en) | ||
MX2019008377A (en) | High strength seamless stainless steel pipe and production method therefor. | |
MX2017012875A (en) | Heat-treated steel sheet member, and production method therefor. | |
MX2016015580A (en) | Heat-treated steel material and method for producing same. | |
MX2017009616A (en) | Rod material for non-tempered machine component, steel rod for non-tempered machine component, and non-tempered machine component. | |
IN2015DN00769A (en) | ||
MX2017012873A (en) | Heat-treated steel sheet member, and production method therefor. | |
MX2019011443A (en) | Martensitic stainless steel material. | |
MX2015003103A (en) | Steel alloy for a low-alloy, high-strength steel. | |
MX2016015400A (en) | Heat-treated steel material and method for producing same. | |
IN2015DN00771A (en) | ||
MX2013002906A (en) | High-strength steel sheet with excellent ductility and stretch flangeability, high-strength galvanized steel sheet, and method for producing both. | |
MX2009004425A (en) | Seamless steel tube for airbag accumulators and process for production thereof. | |
MX350016B (en) | Steel sheet with high mechanical strength, ductility and formability properties, production method and use of such sheets. | |
MX2012000872A (en) | High-strength steel sheet, and process for production thereof. | |
MX2015007724A (en) | Low-yield-ratio high-strength cold-rolled steel sheet and method for manufacturing same. | |
MY176531A (en) | Austenitic stainless clad steel plate and method for producing thereof | |
MX2016001050A (en) | High-strength steel material for oil well use, and oil well pipe. | |
MX2014011470A (en) | Boron-added high strength bolt steel having excellent delayed fracture resistance and high strength bolt. | |
MX363869B (en) | Ferrite-based stainless steel plate having excellent resistance against scale peeling, and method for manufacturing same. | |
MY170336A (en) | High carbon steel wire rod having excellent wire drawability | |
WO2009025314A1 (en) | High-strength low-alloy steel excellent in the resistance to high-pressure hydrogen environment embrittlement and process for manufacturing the steel | |
MX369258B (en) | Hot-dip plated cold-rolled steel sheet and process for producing same. |