GB930368A - Process for the production of disintegrated clinker containing alumina - Google Patents

Process for the production of disintegrated clinker containing alumina

Info

Publication number
GB930368A
GB930368A GB30008/59A GB3000859A GB930368A GB 930368 A GB930368 A GB 930368A GB 30008/59 A GB30008/59 A GB 30008/59A GB 3000859 A GB3000859 A GB 3000859A GB 930368 A GB930368 A GB 930368A
Authority
GB
United Kingdom
Prior art keywords
fe2o3
al2o3
clinker
disintegrated
content
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB30008/59A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Filmfabrik Wolfen VEB
Original Assignee
Filmfabrik Wolfen VEB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Filmfabrik Wolfen VEB filed Critical Filmfabrik Wolfen VEB
Publication of GB930368A publication Critical patent/GB930368A/en
Expired legal-status Critical Current

Abstract

Disintegrated clinker containing alumina is produced by melting at 1500 DEG C.-1680 DEG C. in air a mixture of clay or other angillaceous material, a calcium containing material consisting predominantly of calcium sulphate, or optionally a carbonaceous material, the clinker being slowly cooled and having a silcate modulus SiO2/Al2O3 + Fe2O3 selected within the range of (a) 0,61-0,83 at an (Al2O3 + Fe2O3) content of 25%-30% or (b) 0,39-0,48 at an (Al2O3 + Fe2O3) content of 30%-35% or (c) 0,31-0,35 at an (Al2O3 + Fe2O3) content of 35%-40%. A metal oxide such as Fe2O3 and/or Co2O3 is preferably added to the mixture so that the calcium sulphate decomposes at 900 DEG C.-1100 DEG C. before melting occurs. Alumina may be prepared from the clinker by extraction with sodium hydroxide.
GB30008/59A 1958-09-02 1959-09-02 Process for the production of disintegrated clinker containing alumina Expired GB930368A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DEV14978A DE1145984B (en) 1958-09-02 1958-09-02 Process for the production of alumina-containing trickle clinker for further processing on Portland cement in addition to alumina

Publications (1)

Publication Number Publication Date
GB930368A true GB930368A (en) 1963-07-03

Family

ID=7574809

Family Applications (1)

Application Number Title Priority Date Filing Date
GB30008/59A Expired GB930368A (en) 1958-09-02 1959-09-02 Process for the production of disintegrated clinker containing alumina

Country Status (2)

Country Link
DE (1) DE1145984B (en)
GB (1) GB930368A (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014089592A1 (en) * 2012-12-12 2014-06-19 Baumit Beteiligungen Gmbh Clinker substitute

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014089592A1 (en) * 2012-12-12 2014-06-19 Baumit Beteiligungen Gmbh Clinker substitute

Also Published As

Publication number Publication date
DE1145984B (en) 1963-03-21

Similar Documents

Publication Publication Date Title
GB1029154A (en) í¡í¡od of manufacturing articles by crystallizing glass materials
GB930368A (en) Process for the production of disintegrated clinker containing alumina
JPS5416398A (en) Production of low soda alumina
FI800685A (en) BLYLEGERING SAMT FOERFARANDE FOER DESS FRAMSTAELLNING
ES402068A1 (en) Method of manufacturing high fire-proof aluminous cement
ES386444A1 (en) Sintered preformed slag for the steel industry
ES402003A1 (en) Method of manufacturing a mixture for a borosilicate glass
GB848296A (en) Improvements in the manufacture of glass
US2231024A (en) Calcium oxide-chromium oxide refractory
GB890257A (en) Process for the manufacture of magnesium hydroxide
GB526002A (en) Improvements in and relating to spark plug insulators and method of making the same
GB686876A (en) Method of manufacture of cristobalite
GB733604A (en) Improvements in the purification of sulphur
AU205951A (en) Improvements in or relating to compounds containing two to five linearly fused bicyclo - (2, 2, 1) - heptane rings and method of forming the same
GB455236A (en) Improvements in or relating to refractory articles
GB721073A (en) Improvements in or relating to a water-quenched slag and a cement formed therefrom
GB199017A (en) Method of manufacturing pure alumina
GB697779A (en) A method of manufacturing valuable rubber mixtures
GB765602A (en) Improvements in or relating to the manufacture of alkali metal carbonates
ES429428A3 (en) Procedure for the manufacture of a hydraulic binding based on granulated scoring. (Machine-translation by Google Translate, not legally binding)
GB526146A (en) Improvements relating to the formation of co-precipitated calcium sulphate and ferrous hydroxide
GB765349A (en) A process for the manufacture of filters of siliceous material
ES402226A1 (en) Process of producing refractory magnesia-chrome bricks and compositions
GB880531A (en) Process for the production of a ceramic article
GB816606A (en) Method for the production of sintered magnesia articles from finely divided magnesium compounds