GB829263A - Method of making printed circuits - Google Patents

Method of making printed circuits

Info

Publication number
GB829263A
GB829263A GB4093/58A GB409358A GB829263A GB 829263 A GB829263 A GB 829263A GB 4093/58 A GB4093/58 A GB 4093/58A GB 409358 A GB409358 A GB 409358A GB 829263 A GB829263 A GB 829263A
Authority
GB
United Kingdom
Prior art keywords
board
resist
nickel
copper
printed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB4093/58A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sperry Corp
Original Assignee
Sperry Rand Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sperry Rand Corp filed Critical Sperry Rand Corp
Publication of GB829263A publication Critical patent/GB829263A/en
Expired legal-status Critical Current

Abstract

In a method of making a printed circuit (see Group XXXVI), the printed conductors are formed by coating an insulating board (e.g. an epoxy laminate) with nickel by an electroless process, and subsequently depositing a conductor on to the nickel. In one embodiment, the surfaces of the board are first cleaned by sand blasting and a negative pattern of resist material is applied. The board is then immersed successively in aqueous stannous chloride and palladium chloride solutions, and then in an electroless neckel plating bath which deposits a thin film of nickel on the surface not covered by the resist, and also on the walls of holes through the board. The resist material is then removed and a layer of copper electro-deposited on to the remaining exposed portions of the nickel. The complete board is then immersed in a molten tin-lead solder bath. In an alternative embodiment, nickel is deposited on the walls of holes in a copper-clad board as a separate process, the faces of the board being masked by a resist. After removing the resist, the whole board is electroplated with copper over which a negative pattern of resist is printed leaving exposed only the areas which are to form the printed circuit. Tin-lead is plated over all the exposed surfaces, and after removing the resist, the unwanted copper is removed by etching. Specifications 712,687, 749,824 and 761,556 are referred to.
GB4093/58A 1957-02-08 1958-02-07 Method of making printed circuits Expired GB829263A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US829263XA 1957-02-08 1957-02-08

Publications (1)

Publication Number Publication Date
GB829263A true GB829263A (en) 1960-03-02

Family

ID=22174338

Family Applications (1)

Application Number Title Priority Date Filing Date
GB4093/58A Expired GB829263A (en) 1957-02-08 1958-02-07 Method of making printed circuits

Country Status (1)

Country Link
GB (1) GB829263A (en)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2457621A1 (en) * 1979-05-21 1980-12-19 Schering Ag METHOD FOR MANUFACTURING PRINTED CIRCUITS
DE3008434A1 (en) * 1980-03-03 1981-09-17 Schering Ag Berlin Und Bergkamen, 1000 Berlin METHOD FOR SELECTIVE CHEMICAL AND / OR GALVANIC DEPOSITION OF METAL COATINGS, ESPECIALLY FOR THE PRODUCTION OF PRINTED CIRCUITS
EP0090900A1 (en) * 1982-04-05 1983-10-12 Kanto Kasei Co., Ltd. Process of manufacturing printed wiring boards and printed wiring boards manufactured by the same
CN103597916A (en) * 2012-03-27 2014-02-19 松下电器产业株式会社 Built-up substrate, method for manufacturing same, and semiconductor integrated circuit package

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2457621A1 (en) * 1979-05-21 1980-12-19 Schering Ag METHOD FOR MANUFACTURING PRINTED CIRCUITS
DE3008434A1 (en) * 1980-03-03 1981-09-17 Schering Ag Berlin Und Bergkamen, 1000 Berlin METHOD FOR SELECTIVE CHEMICAL AND / OR GALVANIC DEPOSITION OF METAL COATINGS, ESPECIALLY FOR THE PRODUCTION OF PRINTED CIRCUITS
EP0090900A1 (en) * 1982-04-05 1983-10-12 Kanto Kasei Co., Ltd. Process of manufacturing printed wiring boards and printed wiring boards manufactured by the same
CN103597916A (en) * 2012-03-27 2014-02-19 松下电器产业株式会社 Built-up substrate, method for manufacturing same, and semiconductor integrated circuit package

Similar Documents

Publication Publication Date Title
US4705592A (en) Process for producing printed circuits
US4336100A (en) Method of production of electrically conductive panels and insulating base materials
GB829789A (en) Process of making improved printed wiring boards
GB1266000A (en)
JPS60207395A (en) Method of producing through-hole plated electric printed circuit board
GB1268317A (en) Improvements in or relating to the manufacture of conductor plates
US3357099A (en) Providing plated through-hole connections with the plating resist extending to the hole edges
US3475284A (en) Manufacture of electric circuit modules
US3457638A (en) Manufacture of printed circuits
US3798060A (en) Methods for fabricating ceramic circuit boards with conductive through holes
JPS59215790A (en) Method of producing printed circuit board
GB1208337A (en) Method to produce printed circuits
IE50821B1 (en) Process for the selective chemical deposition and/or electrodeposition of metal coatings,especially for the production of printed circuits
GB829263A (en) Method of making printed circuits
US3306830A (en) Printed circuit boards and their fabrication
GB724379A (en) A method for making a predetermined metallic pattern on an insulating base
JPH04100294A (en) Manufacture of printed wiring board
DE69316750D1 (en) METHOD FOR PRODUCING A CIRCUIT BOARD.
ES487017A1 (en) Printed circuits
ES347873A1 (en) Improvements in manufacture of printed circuit boards
GB892451A (en) Improvements in and relating to the manufacture of printed circuits
FR2307438A1 (en) Printed circuits with conducting transverse bores - starting with thin copper sheets as thin layers
GB1207444A (en) Method of manufacturing printed circuits having metallised holes
GB2017416A (en) Circuit board manufacturing method
GB1497312A (en) Production of printed circuit arrangements