GB2066850A - Annealing Steels - Google Patents

Abstract

A process for the annealing of hypoeutectoid steels wherein a steel is rapidly heated e.g. by electrical resistance means, to a temperature above the upper tranformation temperature of the steel to convert the steel to austenite and carbides, followed by cooling of the steel. The rate of heating of the steel is such as to cause dissolution of most of the carbides in the austenite thus formed, thereby leaving small particles of undissolved carbide in an amount sufficient to serve as nuclei for the precipitation of upper transformation products on cooling. Steels processed in accordance with the process of this invention are characterized by improved ductility and toughness as well as good machinability characteristics. <IMAGE>

Description

SPECIFICATION Process for Annealing Steels This invention relates to the annealing of steels, and more particularly to a process for the annealing of steels to improve the forming and machining characteristics of the steel.

Annealing is a well-known process in the treatment of steels, and is used primarily to soften the steel so that it can be machined or formed into a part having the desired configuration in an economical manner. In general, annealing is carried out by heating the steel in a furnace maintained at the austenitizing temperature, from which the steel is removed and cooled in a controlled manner. The steel is heated to a temperature above the austenitizing temperature (i.e., the A5 temperature) and then cooled so that the micro-structure of the steel contains the so-called upper transformation products, namely pearlite, blocky ferrite, spheroidal carbides and combinations thereof.The upper transformation products are to be distinguished from the equally well-known lower transformation products, namely bainite, acicular ferrite and martensite, in that the upper transformation products are softer and more ductile than the lower transformation products. Thus, for annealing to improve machinability, the goal in the annealing process is to form upper transformation products to the substantial exclusion of lower transformation products.

Annealing is frequently carried out with respect to hot rolled steel, using large annealing furnaces.

Just the size of the furnaces required in terms of space requirements and capital investment represents a significant drawback to their use. As is well known to those skilled in the art, there are several further disadvantages associated with the use of such annealing furnaces. In the first place, furnace heating efficiency is generally quite low, with the result that increasing fuel costs make it desirable to provide a more efficient means of heating the steel. In addition, furnace heating takes place by radiation, conduction and by convection as the mechanism for heat transfer, thus necessitating long cycles to insure that a load of steel in the furnace has been subjected to uniform processing in a given heating cycle.Such long cycles are themselves disadvantageous, for the elevated temperatures used require the use of a known non-oxidizing atmosphere (i.e., a protective atmosphere or vacuum), which requires additional energy to produce.

It is thus desirable to avoid the use of such large annealing furnaces provided that the physical properties of the annealed steel fall within acceptable limits. It has been proposed, as described in U.S.

Patent Nos. 3,908,431, 4,040,872 and 4,088,51 1 to treat steels using various thermal cycles by use of electrical resistance heating techniques. Those techniques have the advantage of providing very rapid heating of steel workpieces with high efficiencies, including uniform heating over the entire cross section of the steel workpiece.

Electrical resistance heating has been used in annealing processes, as described in U.S. Patent No. 3,855,013. In that process, a cold worked steel is rapidly heated by electrical resistance heating to a temperature above the A1 temperature, in which the ferrite present in the steel is converted to austenite. The carbides present to not dissolve in the austenite thus formed, but remain as a separate phase. The steel is then quenched to room temperature to convert the austenite back to ferrite, in essence resulting in elimination of the cold work in the steel leaving the carbides unchanged.

It has now been found that annealing of steels can be significantly modified to provide steels having improved ductility and toughness when the heating to a temperature above the austenitizing temperature is rapidly carried out at a rate such that most of the carbides dissolve in the austenite thus formed, while leaving small particles of carbide in undissolved form. The small carbide particles which remain are of sufficient quantity to serve as nuclei for the growth of upper transformation products during cooling, thereby resulting in an overall acceleration of the annealing process.

It is accordingly an object of the present invention to provide an improved process for the annealing of steels.

It is a more specific object of the present invention to provide an improved process for the annealing of steels in which a steel is rapidly heated to a temperature above the A3 temperature such that small particles of carbide remain in an undissolved state to serve as nuclei for growth of upper transformation products to provide an annealed steel having high levels of ductility and toughness.

It is yet another object of this invention to provide improved steels which have been annealed to yield high ductility, formability and toughness characteristics.

Figure 1 is a graph of temperature versus time, representing the heating and cooling of two steel specimens to show the temperature dependence of accelerated annealing in accordance with the present invention; Figure 2 is a graph of temperature versus time, representing the heating and cooling of several steel specimens to show the time dependence of accelerated annealing in accordance with the present invention; Figure 3A is a photomicrograph showing the micro-structure of 4142 steel prior to processing in accordance with the present invention (Heat A); Figure 3B is a photomicrograph showing the micro-structure of 4142 steel after heating to 141 50F followed by quenching (Heat A); Figure 3C is a photomicrograph showing the micro-structure of 4142 steel after heating to 14150F and air cooling (Heat A);; Figure 4 is a graph of mechanical properties (hardness and tensile strength) versus austenitizing temperature of 8640 steel (Heat B); Figure 5 is a schematic illustration of apparatus used for annealing in accordance with the concepts of this invention; Figure 6A is a photomicrograph showing the micro-structure of 4140 steel prior to treatment in accordance with the present invention (Heat C); Figure 6B is a photomicrograph showing the micro-structure of 4140 steel after furnace annealing (Heat C); Figure 6C is a photomicrograph showing the micro-structure of 4140 steel which has been annealed in accordance with the process of this invention (Heat C); Figure 7 is a graph of Charpy impact energy versus temperature for 4140 steel which has been furnace annealed and annealed by the process of this invention (Heat C);; Figure 8 illustrates the results of machinability testing (in the form of a plot of part growth versus parts produced in running time) for 4140 steels which have been furnace annealed and annealed in the process of this invention (Heat C); Figure 9A is a photomicrograph showing the micro-structure of 4140 steel prior to processing in accordance with the present invention (Heat D); Figure 9B is a photomicrograph showing the micro-structure of 4140 steel after furnace annealing (Heat D); Figure 9C is a photomicrograph of 4140 steel as annealed by the process of this invention (Heat Dì; Figure 10 is a plot of Charpy impact energy versus temperature for 4140 steel which has been furnace annealed and annealed by the process of this invention (Heat D);; Figure 11 is a graph (in the form of time versus speed as determined by a modified Taylor life test) of 4140 steel which has been furnace annealed and annealed by the process of this invention (Heat D); Figure 1 2A is a photomicrograph showing the micro-structure of 8640 steel prior to processing in accordance with the present invention (Heat B); Figure 1 2B is a photomicrograph showing the micro-structure of 8640 steel which has been furnace annealed (Heat B); Figure 1 2C is a photomicrograph showing the micro-structure of 8640 steel which has been annealed in accordance with the process of this invention (Heat B); Figure 13 is a graph of Charpy impact energy versus temperature for 8640 steel which has been furnace annealed and annealed by the process of this invention (Heat B);; Figure 1 4A is a photomicrograph showing the micro-structure of 61 50 steel prior to treatment in accordance with the process of this invention (Heat G); Figure 148 is a photomicrograph showing the micro-structure of 61 50 steel which has been furnace annealed (Heat G); Figure 1 4C is a photomicrograph showing the micro-structure of 61 50 steel which has been annealed by the process of this invention (Heat G); Figure 15 is a graph of Charpy impact energy versus testing temperature for 6150 steel which has been annealed in a furnace and 61 50 steel which has been annealed in accordance with the process of this invention (Heat G);; Figure 1 6A is a photomicrograph showing the micro-structure of a 1144 steel prior to processing in accordance with the process of this invention (Heat H); Figure 1 6B is a photomicrograph showing the micro-structure of the 1144 steel shown in Figure 1 6A after annealing in a furnace (Heat H); Figure 1 6C is a photomicrograph showing the micro-structure of the 1144 steel after it has been annealed in accordance with the process of this invention (Heat H); Figure 1 7A is a photomicrograph showing the micro-structure of an 86L20 steel prior to processing (Heat I);; Figure 1 7B is a photomicrograph showing the micro-structure of the 86L20 steel of Figure 1 7A after it has been furnace annealed (Heat I); and, Figure 1 7C is a photomicrograph showing the micro-structure of the 86L2ú steel of Figure 1 7A after it has been annealed in accordance with the process oF ghis invention (Heat I).

The concepts of the present invention reside in the dissovery that high levels of ductility and toughness can be achieved with hypoeutectoid steels by annealing where the steel is rapidly heated to a temperature above the upper transformation temperature of to form austenite and retained iron carbides, with the rate of heating being sufficiently rapid such that most of the carbides are dissolved in the austenite leaving small particles, usually spheroidal in form, of carbide in an undissolved state.

Following that heating, the steel is cooled at a rate such that the small particles of retained carbide which are undissolved in the austenite serve as nuclei for the growth of upper transformaion products, notably including pearlite and blocky ferrite as well as fine spheroids of iron carbide. It has been found that carbides thus formed on cooling are characterized by particle sizes which are much finer than those formed during furnace annealing, with the result that the refined microstructure of the annealed steel provides improved ductility, formability and toughness when compared to steel subjected to furnace annealing.

The concepts of the present invention are applicable to the processing of hypoeutectoid steels having a carbon content ranging up to 0.7% by weight, and preferably containing between 0.1 to 0.7% carbon by weight. Such steels may contain relatively small quantities of the common alloying elements such as chromium, molybdenum, nickel and manganese. By a widely used convention, a steel containing less than 5% by weight of such alloying elements is referred to in the art as a "low alloy steel".Representative hypoeutectoid steels which can be used in accordance with the present invention are shown in the following table: Table 1 Bar Heat Grade Diameter C Mn P S Si Ni Cr Mo Al A 4142 1.063 0.41 0.93 0.01 0.04 0.27 0.17 0.98 0.15 0.03 B 8640 1.062 0.41 1.03 0.01 0.04 0.28 0.46 0.59 0.18 0.04 C 4140 1.062 0.41 0.92 0.01 0.02 0.26 0.18 0.98 0.20 0.04 D 4140 1.125 0.42 0.96 0.01 0.02 0.29 0.20 1.09 0.18 0.03 E 4140 1.062 0.43 0.82 0.01 0.01 0.27 0.01 0.98 0.20 0.04 F 4142 1.000 0.44 0.78 0.01 0.01 0.32 0.04 0.94 0.17 0.05 G* 6150 1.062 0.50 0.80 0.01 0.02 0.28 0.17 0.93 0.06 0.01 H 1144 1.062 0.44 1.37 0.01 0.25 0.15 - 0.09 0.02 - I** 86L20 1.375 0.20 0.86 0.01 0.03 0.25 0.43 0.53 0.15 0.03 *Also contains 0.12 V **Also contains 0.16 Pb In the preferred practice of this invention, the steel is in the form of a workpiece which can be heated separately so that the heating process can be precisely controlled. For that purpose, it is frequently preferred to employ workpieces in a form having a repeating cross section such as bars, rods tubes and the like.

In accordance with the preferred embodiment, the individual workpieces are rapidly heated by direct electrical resistance heating or by electrical induction heating, preferably while the temperature of the workpiece is monitored by a suitable sensing device. The rapidity of the heating process, while permitting the economic processing of large quantities of workpieces, causes the austenitizing transformation to proceed very rapidly. The most preferred method for rapid heating in accordance with the present invention is by direct electrical resistance heating. That technique, described in detail by Jones et al. in U.S.Patent No.3,908,431 (the disclosure of which is incorporated herein by reference) involves a precedure whereby an electrical current is passed through the steel workpiece; the electrical resistance of the workpiece to the flow of electrical current causes rapid heating of the workpiece uniformly throughout its entire cross section.

In heating according to the technique of Jones et al., the workpiece is connected to a source of electrical current, with the connection being made at both ends of the workpiece so that the current flows completely through the workpiece. Because of the uniform flow of the current through the workpiece, the temperature of the workpiece, usually in the form of a bar or rod, increases uniformly, both axially and radially. Thus, the interior as weil as the exterior of the workpiece are heated simultaneously, without introducing thermal strains.In contrast, in a conventional furnace, the exterior of the furnace load is heated much more rapidly than the interior, with the result that the steel near the exterior of the load is completely transformed to austenite while the interior of the load may not have, at the same point in time, undergone transformation to austenite.

Such furnace techniques thus involve a significant disadvantage since it is difficult, if not impossible, to control the rate of heating such that austenitic transformation along with dissolution of only part of the carbides is achieved. In other words, there is a tendency, when heating in a furnace, to dissolve all of the carbide, and hence fine particles of retained carbides are not available to serve as nuclei for the formation of the upper trasformation products on cooling.

In the practice of this invention, the steel workpiece is heated to a temperature above the A3 or upper transformation temperature at a very rapid rate, usually within the range of one second to ten minutes. The control of the heating step may be effected within relatively narrow limits by making use of the well-known endothermic character of austenite transformation. As is now well established, the temperature of the workpiece at the onset of austenitic transformation remains constant, or even decreases slightly for a period ranging from a few seconds to several minutes, depending somewhat on the heating rate. A typical heating curve for the austenitizing step used in the practice of this invention is shown in Figure 1 of the drawing, which is a plot of temperature versus time for heat A of 4142 steel. (The chemistry for that particular heat is shown in Table 1, supra).As can be seen from the figure, two steel workpieces were rapidly heated in less than five minutes to austenitizing temperatures of 141 20F for sample (1) and 1 5500F for sample (2). The heating curve indicates that carbide dissolution is taking place when the rate of temperature increase remains constant, that is at the so-called heating arrest point. Care must be taken when that point is reached to insure that all of the carbides do not dissolve in the austenite thus formed. It is an important concept of this invention that sufficient quantities of carbide be retained in undissolved state to serve as nuclei for precipitation of the upper transformation products on cooling of the workpiece.

Thus, heating to the austenitization temperature is continued for a short time above the heating arrest point. During this time, austenitization of most of the structure is completed, and the structure which exists at the point of maximum temperature consists essentially of austenite and undissolved carbide particles. Following the austenitizing, the workpieces are allowed to air cool at their own rate.

As shown in Figure 1, the steels exhibit a cooling arrest (1 2200F for sample (1) and 880CF for sample (2)) at which point precipitation of transformation products begins. The cooling arrest point is thus determined by the austenitizing temperature employed. In the case of sample (1), the austenitiziny temperature was such that the sample cooled to form upper transformation products, while sample (2), austenitized at the higher temperature, cooled to form lower transformation products.

The complete data on this phenomenon is shown in the following table: Table 2 Mechanical Properties of 41 42-Austenitized and Air Cooled Specimens Hardness Tensile Yield EL RA Specimen (Bhn) (ksi) (ksi) (o/o) {%) As Received Steel 311 153.0 77.3 14.1 37.2 Austenitized at 14129F(Time: 3 min. -36 sec.) 212 110.4 63.9 24.0 59.7 Austenitized at 1430CF (Time: 3 min. -58 sec.) 235 127.1 70.4 18.5 41.6 Austenitized at 14800F (Time: 4 min. -26 sec.) 266 135.2 74.3 17.9 40.2 Austenitized at 1 5500F (Time:: 5 min. -2 sec.) 282 147.3 95.9 16.1 42.2 The data show that the hardness of the steel increased (accompanied by a decrease in ductility) as the austenitizing temperature increased.

The foregoing data demonstrate that accelerated annealing in accordance with the present invention is dependent on austenitization temperature. If the temperature is too high, all of the carbide dissolves, and hence no nuclei are available to accelerate the rate of precipitation of upper transformation products.

It has also been found that time affects the annealing process of this invention as well, with longer heating times resulting in dissolution of all of the carbide particles present. This effect is shown in Figure 2, which is another plot of temperature versus time for a series of samples held for varying lengths of time prior to air cooling. (The heating and cooling portions of this curve have been cut off at 1 1 OOOF so that only the temperature where upper transformation products form are shown. The hardness values for each sample are also shown in the graph).

As shown in Figure 2, as the time at which the various samples are held at the austenitizing temperature is increased, the cooling arrest point decreases; as a result, there is a tendency for lower transformation products to form instead of the upper transformation products in accordance with the practice of this invention. Thus, the hardness values increase as the austenitizing time increased.

Indeed, after 12 minutes at the austenitizing temperature, there is no cooling arrest within the temperature range shown in Figure 2, and the hardest air-cooled specimens are produced.

The foregoing tests with 4142 specimens demonstrated that the accelerated annealing phenomenon of this invention is dependent upon both austenitizing temperature and austenitizing time. To demonstrate how the accelerated annealing phenomenon occurs, the microstructures of the steel prior to austenitization, at the austenitizing temperature, and after air cooling, were examined.

The as received structure and the air cooled structure could be examined using standard metallographic techniques. To observe the condition of the austenite at the austenitizing temperature, a classical metallurgical quenching technique was used. A specimen from Heat A was rapidly heated to 141 50F and quenched in agitated water. The parts of the structure that were austenite prior to the quench were converted to martensite. Consequently, the austenitized structure could be observed at room temperature with standard metallographic techniques by using an etchant that would not reveal the martensite.

Figures 3A, 3B and 3C show the as received structure, the austenitized-quenched structure, and ihe austeriized-air cooled structre of samples iron Heat A. The scanning electron microscope (SEA) was used for these photomicrngraphs due to the fine nature of these structures.

This technique clearly revealed the structure of the steel before austenitizing, at the austenitizing temperature and after air cooling.

It can be clearly seen from these photomicrographs that the as received structure (before processing) was austenitized during the rapid heating cycle, but some particles of carbide remained undissolved in the austenite. Since nuclei already existed in the austenitized structure, there was no time required at the annealing temperature for nucleation of upper transformation products. The retained carbide particles simply began to grow as the temperature dropped below the A, temperature, and eventually pearlite began to grow from the carbide nuclei. Consequently, the time required to anneal the steel was shortened considerably. Several other grades of steel were tested in a similar manner, and, in each case, it was discovered that the austenitized structure consisted of austenite with fine spheroidal carbides.This retention of carbide in the austenitized structure due to rapid heating is believed to be the basis of the accelerated annealing phenomenon of this invention.

The retention of carbide in the austenitized structure of steel has been noted in the literature.

However, with slower heating, the amount of carbide retained in the austenitized structure is small.

Consequently, a steel which is slowly heated to the austenitizing temperature is less likely to display the accelerated annealing phenomenon. Comparison tests with furnace austenitizing treatments and rapid austenitizing treatments revealed that the accelerated annealing phenomenon did not occur with furnace treatments.

In one of these tests, bars of 8640 from Heat B were austenitized at various temperatures in a furnace and allowed to air cool. Then another set of bars from the same heat was austenitized with electric resistance heating and allowed to air cool. The mechanical properties which resulted from this treatment are shown in Figure 4. All of the furnace treated specimens cooled to a relatively high hardness. However, the rapidly heated specimens show a noticeable transition between hard and soft air cooled specimens. Table 3 shows the mechanical properties of one set of specimens from this test.

The furnace austenitized specimen had mechanical properties very similar to those of the as received steel while the rapidly austenitized specimen was significantly softer. It is clear frorn that data that 8640 responded to the rapid austenitization in the same manner as the 4142 had responded.

However, the accelerated annealing phenomenon is more apparent in 8640 because this steel has lower hardenability than 4142.

liable 3 ab al iFiroi3eP-kiss of sQ40--aeosleniPiaed and Aie Cooled Specimens Hardness Tensile Yield EL RA Specimen (Bun) (ksi (ksi) (%) {%J Ac Received 8640 256 132.7 94.3 15.1 39.1 Furnace Austenitized at 1 5000F, Air Cooled (Tlme: 1 hr.) 254 132.1 96.2 15.5 47.0 Rapidly Austenitized at 1 5000 F, Air Cooled (Time: 4 min.) 205 111.1 71.1 20.0 50.8 The test demonstrate that the accelerated annealing phenomenon is sensitive to austenitizing temperatilre because the specimens which were rapidly austenitized above 1 5500F did not selfanneal. These tusks also demonstrate that the accelerated annealing phenomenon is dependent upon austenitizing time as well because none of the furnace austenitized specimens annealed during air cooling regardless of the austenitizing temperature. Furnace treatments are simply too slow to permit the accelerated annealing phenomenon to occur.The relatively long time at the austenitizing temperature permits the retained carbide to be dissolved or reduced in size to the point where there is not enough carbide left to be effective as nuclei for carbide growth during cooling.

In accordance with one variation in the practice of this invention, it is sometimes desirable to insure uniformity in cooling rates in large batches of workplaces being processed. If, for example, steel bars were simply heated and piled in a rack to cool, the first bar might cool at a much faster rate than the last, and hence lack of uniformly within a batch of steel processed at one time might develop.

Accordingly, to avoid lack of uniformly of batches, use can be made of an insulated cooling queue of the sort illustrated in Figure 5 of the drawing. When using this type of equipment it is possible to pass bars through the queue with a dwell or residence time of, for example, 1 0 minutes. No external source of heat need be used in equipment of that type, and hence no energy is consumed. Tests with respect to uniformity of mechanical properties have demonstrated that the insulated cooling queue is effective.

Having described the basic concepts of the present invention, reference is now made to the following examples, which are provided by way of illustration and not by way of limitation, of the practice of the present invention in the annealing of steel bars having a length of 7 feet. In each example, the steel was examined in three conditions, namely as received or prior to any treatment, after furnace annealing, and after annealing by the process of this invention, with comparisons having been made between the furnace annealed steel and steel annealed by way of this invention.

Example 1 This example illustrates the annealing of a 4140 steel from heat C as shown in Table 1.

Twenty bars of 4140 from Heat C were furnace annealed using a roller hearth furnace. The furnace austenitizing temperature was 1 5500 F, and the annealing cycle was a total of 16 hours long.

Twenty bars from the same heat were also annealed by the process of this invention. The austenitizing temperature was 14500 F, and each bar was austenitized in 33 seconds. The total annealing time for all 20 bars was less than one hour.

Both lots of steel were cleaned, cold drawn and straightened after annealing. Then the two lots were extensively tested, and the steel that remained after testing was used for a machinability test.

Table 4 shows the mechanical properties of the steel used in these tests. The mechanical properties of the as received steel and the as annealed steel are shown for comparison purposes.

The steel annealed by the process of this invention has a better combination of properties than the furnace annealed steel. The hardness of the the steel annealed by the present process is slightly higher, but the significant difference between the two products is the improved ductility of the steel annealed by the process of the invention. The elongation was 13.3% for the furnace annealed steel after complete processing, and the elongation for the steel annealed by this process was 1 7.0%. This is an improvement of 28%. The reduction of area for the furnace annealed steel was 39.0% and the reduction of area for the steel annealed by the present process was 59.3%. This is an improvement of 52%.The elongation and reduction of area are a basis for estimating the ductility of a steel, and these improvements over the furnace annealed steel indicate a dramatic improvement in ductility and formability.

Table 4 Mechanical Properties of 4140 - Heat C Hardness Tensile Yield EL RA Specimen (bin) (ksi) (ksi) (%) (%) As received 4140 315 151.0 120.5 13.0 39.4 Furnace Annealed 197 99.7 46.6 21.5 40.8 Annealed by the Present Process 217 108.0 58.7 23.5 60.9 Furnace Annealed & old Colt Drawn 226 111.5 81.2 13.3 39.0 Annealed by the Present Process & Cold Drawn 238 119.4 93.9 17.0 59.3 The reason for the improved ductility of the product annealed by the present process can be clearly seen in the microstructure of these steel samples. Figures 6A, 6B, and 6C show the microstructures of samples from this heat of 4140 in three conditions: as received, furnace annealed, and annealed by the process.The as received structure consists of lower transformation products: upper bainite and acicularferrite. The furnace annealed structure consists of pearlite and ferrite. The steel annealed by the present process has a structure which consists essentially of ferrite, pearlite and fine carbide spheroids. Ferrite areas are not distinct, and the ferrite contains spheroidal carbides. Also, the grain size is finer for the steel annealed by the present process. It is the fine nature of this structure which gives the steel its improved ductility and formability over the coarse furnace annealed structure.

The fine microstructure also gives the annealed product improved toughness. Figure 7 shows the Charpy impact curves for bars taken from the two lots of annealed steel. The steel annealed by the present process has a lower transition temperature, and an upper shelf energy which is almost three times that of the furnace annealed steel. Improved toughness is valuable for applications where the part is machined or formed, and then only surface hardened. In such applications, improved core toughness would give the part higher resistance to fracture.

To demonstrate that the improved toughness and ductility of steel annealed by the instant process did not adversely affect its machinability as compared to that of furnace annealed steel, a comprehensive machinability test was carried out. The screw machine test was selected because it tests the machinability of the steel with several different types of tools. Figure 8 shows the results of machinability testing of the two annealed lots of 4140 from Heat C. In this type of test, part growth is measured and plotted against time or the number of parts produced. Steels which machine well have part growth curves which are relatively flat and near the time axis. Steels which machine poorly have curves which have steep slopes. The part growth curves shown in Figure 8 indicate that the two annealed steels machined about the same.The steel annealed by the present process was slightly better than the furnace annealed steel, but the difference is not considered significant.

Example 2 This example illustrates the annealing at a 4140 steel from heat D.

Twenty bars from Heat D were furnace annealed using a 1 6 hour cycle with an austenitization temperature of 1 5500 F. Then 20 additional bars from the same heat were annealed by the present process. For this treatment each bar was austenitized at 1 5000F in approximately 36 seconds, and the entire lot was annealed in less than one hour.

Table 7 Mechanical Properties of 41 42Heat F Hardness Tensile Yield EL RA Specimen (Bhn) (ksi) (ksi) {%) {%) As received 4142 268 141.0 99.1 15.5 46.5 Furnace Annealed Steel 194 101.8 50.3 20.8 46.6 Annealed by the present process 196 102.3 86.2 25.0 68.3 Example 5 Ten bars of 8640 from Heat B were annealed using the roller heath furnace. The furnace austenitizing temperature was 1 5500F and the furnace cycle was a total of 16 hours. Then ten bars from the same heat were annealed using the present process. The austenitizing temperature was 14500 F, and each bar was austenitized in 35 seconds.The total annealing cycle with the process of this invention was approximately 30 minutes. Table 8 shows the mechanical properties of the steel in three conditions: as received, furnace annealed and annealed by the instant process. Once again, the steel annealed by the process of this invention had significantly better ductility than the furnace annealed steel.

Table 8 Mechanical Properties of 8640-Heat B Hardness Tensile Yield EL RA Specimen (Bhn) (ksi) (ksi) (%) (%) As received 8640 258 132.1 102.8 16.7 46.9 Furnace Annealed Steel 176 98.9 49.3 22.8 47.0 Annealed by the present process 180 98.9 60.4 28.1 64.6 The microstr;.lcures of the as received steel, the furnace annealed steei, and the steel annealed by the process of this invention are shown in Figures 1 2A, 1 2B and 12C. The steel annealed by the present process had a more spheroidal structure than the furnace annealed steel, and it was somewhat finer.This difference in microstructure is similar to what was observed in the 4140 tests. The 8640 was also tested for toughness using the Charpy impact test. The results of Impact testing of the two annealed lots is shown in Figure 13. Once again the steel annealed by the present process had far superior toughness. (It should be noted that the annealed 8640 was not cold drawn prior to testing.

Consequently, it was somewhat softer and tougher than the 4140 heats that were mentioned earlier).

Example 6 Twenty bars of 6150 from Heat G were annealed using a roller hearth furnace. The furnace austenitizing temperature was 1 5500F and the cycle was 16 hours.

Then twenty bars from the same heat were annealed with the process of this invention using an austenitizing temperature of 1 5000F. Each bar was austenitized in 34 seconds, and the total annealing time was approximately one hour. Table 9 shows the mechanical properties of the as received steel, furnace annealed steel, and steel annealed by the present process.

The two annealed lots were then cold drawn and straightened to duplicate one type of typical commercial processing. The cold drawn and straightened properties are also given in Table 9. For this particular grade, the steel treated with the present process was slightly harder than the furnace annealed steel, but it was still more ductile. This superior ductility is evident both before and after cold drawing.

Table 9 Mechanical Propsrtis of 81 50-lea- Hardness Tensile Yield EL RA Specimen (Bhn) (ksi) (ksi) (%) (%) As Received 6150 299 151.0 11.6 12.0 37.8 Furnace Annealed Steel 195 100.8 63.0 20.7 44.1 Annealed by the present process 925 109.8 81.2 25.5 6Ô.4 Furnace annealed cold drawn straightened 240 120.4 86.0 9.6 31.3 Annealed by the present process cold drawn straightened 263 130.9 103.8 13.0 48.3 The rnicrnstructures of the as received steel, the furnace annealed steel. and the steel annealed Both lots were then descaled, cold drawn and straightened. Extensive testing was conducted on each lot, and the steel that remained after this testing was used for a machinability test. The mechanical properties of the as received steel, the furnace annealed steel and the steel annealed by the new process are shown in Table 5. Once again, the steel annealed by the present process had greater ductility and was slightly harder than the furnace annealed steel. Figures 9A. 9B and 9C show the microstructure of this heat of steel in three conditions: as received, furnace annealed, and annealed by the present invention, respectively. Just as before, the steel annealed by the present process has a microstructure which is much finer than the furnace annealed steel.

Table 5 Mechanical Properties of 4140 -- Heat D Hardness Tensile Yield EL RA Specimen (BUN) (ksi) (ksi) (%) (%) As Received 4140 311 151.4 109.6 13.3 41.9 Furnace Annealed and Cold Drawn 231 119.1 102.3 12.1 42.8 Annealed by the Present Process and Cold Drawn 241 127.4 105.9 13.8 53.1 Figure 10 shows the Charpy impact curves for the furnace annealed steel and the steel annealed by the present process. The superiority of the steel annealed by the present process is again obvious.

The transition temperature is lower and the upper shelf energy is higher for the steel annealed by the present process.

Machinability testing of the two annealed lots of steel was accomplished using a Modified Taylor Life test. In this type of machinability test, the bar is turned at various speeds and feeds until the machining tool fails. Then the data points representing the time to failure at various speeds are plotted on log-log paper. The result is a straight line which represents the relationship between machining speed and time to tool failure. Figure 11 shows the results of this type of machinability testing on the two annealed lots produced from Heat D. The two lines cross, indicating that there is some difference between the way these two annealed steels machined. However, at the lower machining speeds, where alloy steels are usually machined, the steel annealed by the present process is slightly better.

Once again, even though the steel annealed by the present process was harder, tougher, and more ductile, it machined better than the furnace annealed steel. These differences in ductility, toughness and machinability are in the aggregate, a significant improvement in the mechanical properties of this steel.

Example 3 Ten bars of 4140 steel from Heat E were furnace annealed using a 16 hour cycle with an austenitization temperature of 1 5500 F. Then ten bars from the same heat were annealed by the present process using an austenitization temperature of 14500 F. The bars were each austenitized in 35 seconds, and the entire annealing cycle was 45 minutes long. Table 6 shows the results of this processing. The specimens made in this test were not cold drawn after annealing. This heat responded to annealing by the present process almost exactly as the other heats had responded. The superior ductility of the steel annealed by the process of this invention is apparent from the data in Table 6.

Table 6 Mechanical Properties of 4140 -- Heat E Hardness Tensile Yield EL RA Specimen (Bhn) (ksiJ (ksi) lO/oJ (%J As Received 4140 269 141.6 99.2 15.7 50.2 Furnace Annealed Steel 186 103.7 49.6 19.7 42.6 Annealed by the process of this invention 194 104.5 97.1 24.6 60.5 Example 4 1 5 bars of 4142 from Heat F were annealed using a furnace. The austenitizing temperature for the furnace treatment was 1 5500F and the cycle was 16 hours long. Then 15 more bars from the same heat were annealed by the process of this invention. An austenitizing temperature of 1 4500F was used, and each bar was austenitized in 60 seconds. The entire cycle was less than one hour long.

Table 7 shows the mechanical properties of the steel in three conditions: as received, furnace annealed, and annealed by the process of this invention. Once again, the steel annealed by the present process had superior ductility as compared to that of the furnace annealed steel.

by the present process are shown in Figure.i 14R 1 4E and 1 4C, respectively. The steel annealed by the present process has a finer carbide structure than the furnace annealed steel. Charpy impact testing was also accomplished on the two annealed samples and the results are shown in Figure 1 5. The curves shown are For the 6150 after cold drawing. Once again the steel annealed by the present process had a finer microstructure, improved ductility and improved toughness as compared to the furnace annealed steel.

Example 7 Several bars of 1144 from Heat H were furnace annealed using a five hour cycle. The austenitization temperature was 1 5500F for the furnace treatment.

Then five bars from the same heat were annealed using the present process. The austenitization temperature was 1 4500F and the annealing time for she five bars was 20 minutes. Each bar was austenitized in 30 seconds.

Table 1 0 shows the mechanical properties of the as received steel, the furnace annealed steel and the steel annealed by the process of the invention. In this case, the hardness of the steel annealed by the present process was very near that of the furnace annealed steel. As with the previous examples, the steel annealed by the present process has superior ductility. Figures 1 6A, 1 68 and 1 6C show the microstructure of this steel in three conditions: as received, furnace annealed, and annealed by the present process, respectively.

Table 10 Mechanical Properties of 114WHeat H r-/ardness Tensile Yield EL RA Sar-r7ple (bin) (ksi) (ksi) {%) {%) As Received Steel Hot Polled 1144 190 99.0 60.9 19.5 41.4 Furnace Annealed 162 89.5 51.3 23.1 41.1 Anneaied by the present process 165 89.1 57.4 25.0 48.5 Example 8 Several bars of 86L20 from Heat i were furnace annealed using a five hour cycle. The austenitizing temperature used for the furnace anneal was 1625"F.

Then 1 5 bars from the same heat were annealed using the present annealing process. The austenitizing temperature used was 1 6000b=, and each bar was austenitized in 31 seconds. The total annealing cycle was 47 minutes.

Table 11 shows the mechanical properties of the as received steel, the furnace annealed steel, and the steel annealed by the present process. For this grade of steel, the improvement in ductility for the steel annealed by the present process is relatively small. Also, the hardness of the steel annealed by the presen-t process was rather high. The reason for these differences is clear from the photomicrographs of the structures of this heat of steel (Figures 1 7A, 178 and 1 7C). The grain size of the steel annealed by the present process is much finer than the grain size of the furnace annealed steel.In a ,ew carbon steel like 86L20, the fine grain size which results from the new annealing process is the domincnt factor. There is not enough carbon in the steel for the carbides to play a dominant role, and the grain size effect makes the steel annealed by the present process somewhat harder than the furnace annealed product. Consequently, only marginal impovements in ductility were achieved with the present annealing process.

Table 11 Mechoieal Properties of 86L20-Heat I Hardness Tensile Yield EL RA Sample (Bhn) (ksi) (ksi) (%) (%) As received 86L20 172 83.2 53.3 25.2 62.4 Furnace Annealed 141 74.9 49.5 29.7 62.1 Annealed by the present process 160 81.9 60.1 30.0 65.2 The foregoing examples denonstrate that the present annealing process is applicable to a wide variety of carbon and alloy steels. Each grade that was tested responded to the present annealing process in about the same way. For each alloy, a finer carbide morphology was produced which gave the steel improved ductility, formability and toughness it is important to note that these improved properties were achieved with no loss cf strength or loss of machinability. This combination of improved ductility formability and toughness with no loss of machinability is an unexpected phenomenon. Usually when ductility and toughness increase at a given hardness level, the machinability decreases. However, the new annealing process creates a structure which does not follow this general trend.

It will be apparent from the foregoing that the present invention provides a significant improvement in the annealing of hypoeutectoid steel. It affords improved energy efficiency through the use of direct electrical resistance heating, and, at the same time, eliminates the need for long controlled cooling cycles of the sort that have been required in the furnace annealing of steels. In addition, the process of this invention eliminates the need for protective or non-oxidizing atmospheres of the sort required with furnace annealing procedures heretofore used by the prior art.

It will be apparent that various changes and modifications can be made in the procedures of carrying out the present invention as well as the equipment employed without departing from the spirit of the invention, especially as defined in the following claims.

Claims (20)

Claims

1. A process for annealing steel comprising the steps of: (a) rapidly heating a hypoeutectoid steel to a temperature above the upper transformation temperature of the steel to form austenite and carbides, with the rate of heating being such as to cause dissolution of most of the carbides in the austenite, leaving in undissolved form small particles of carbide in an amount sufficient to serve as nuclei for the precipitation of upper transformation products, and (b) cooling the steel to precipitate said upper transformation products and form an annealed steel.

2. A process as defined in claim 1 wherein the hypoeutectoid steel contains up to 0.7% carbon by weight.

3. A process as defined in claim 1 wherein the steel contains between 0.1 to 0.7% carbon by weight.

4. A process as defined in any one of the preceding claims wherein the steel contains less than 5% by weight of an alloying element.

5. A process as defined in claim 4 wherein the alloying element is selected from the group consisting of chromium, molybdenum, nickel, manganese and combinations thereof.

6. A process as defined in any one of the preceding claims wherein the steel is heated to the upper transformation temperature in less than ten minutes.

7. A process as defined in any one of the preceding claims wherein the steel is heated by direct electrical resistance heating.

8. A process as defined in any one of the preceding claims wherein the steel is in the form of a workpiece having a repeating cross section.

9. A process as defined in any one of the preceding claims wherein the heating of the steel takes place in the absence of an inert atmosphere.

10. A process for annealing steel comprising the steps of: (a) heating a hypoeutectoid steel to a temperature above the upper transformation temperature of the steel to form austenite and carbides, with the rate of heating being less than ten minutes to cause dissolution of most of the carbides in the austenite while leaving in undissolved form small particles of carbide present in an amount sufficient to serve as nuclei for the precipitation of upper transformation products, and (b) cooling the steel at a rate sufficient to precipitate upper transformation products and form an annealed steel having improved ductility, formability and toughness.

11. A process for annealing steel comprising the steps of: (a) heating a hypoeutectoid steel uniformly across its cross section to a temperature above the upper transformation temperature of the steel to form austenite and carbides, with the rate of heating being such as to cause dissolution of most of the carbides in the austenite, leaving in undissolved form small particles of carbides to serve as nuclei for the precipitation of upper transformation products, and (b) cooling the steel to precipitate said upper transformation products.

12. A thermally efficient process for the annealing of steel comprising the steps of: (a) heating a hypoeutectoid steel by passing an electrical current through the steel to a temperature above the upper transformation temperature of the steel to form austenite and carbides, with the heating taking place in less than ten minutes to cause dissolution of most of the carbides in the austenite, leaving in undissolved form small particles of carbide present in an amount sufficient to serve as nuclei for the precipitation of upper transformation products, and (b) cooling the steel to precipitate said upper transformation products.

13. A process as defined in claim 12 wherein the steel is air cooled.

14. A process for annealing steel comprising the steps of: (a) rapidly heating a hypoeutectoid steel to a temperature above the upper transformation temperature of the steel for a time sufficient to form austenite and carbides, with the carbides being undissolved in the austenite and being present in an amount sufficient to serve as nuclei for the precipitation of upper transformation products, and (b) cooling the steel to precipitate said upper transformation products and form an annealed steel.

1 5. A process as defined in claim 14 wherein the steel is rapidly heated in less than ten minutes by direct electrical resistance heating.

1 6. A process for annealing steel comprising the steps of: (a) rapidly heating a hypoeutectoid steel containing ferrite and carbides to a temperature above the upper transformation temperature of the steel to convert the ferrite to austenite, with the rate of heating being such as to cause dissolution of most of the carbides in the austenite thus formed while leaving the undissolved form small particles of carbide present in an amount sufficient to serve as nuclei for the precipitation of upper transformation products, and (b) cooling the steel to precipitate said upper transformation products and form an annealed steel.

1 7. A process as defined in claim 1 6 wherein the annealed steel contains pearlite, ferrite and spheroidal carbides.

1 8. A process for annealing steel comprising the steps of: (a) rapidly heating a hypoeutectoid steel containing ferrite and carbides to a temperature above the upper transformation temperature of the steel to convert the ferrite to austenite, with the heating being carried out at a rate to form small particles of carbide dissolved in austenite whereby the carbides are present in an amount sufficient to serve as nuclei for the precipitation of upper transformation products, and (b) cooling the steel to precipitate said upper transformation products.

1 9. A process as defined in claim 1 and substantially as described herein in any one of the Examples.

20. Steel when produced by a process as defined in any one of the preceding claims.