GB1502114A - Alloy treatment - Google Patents
Alloy treatmentInfo
- Publication number
- GB1502114A GB1502114A GB13649/75A GB1364975A GB1502114A GB 1502114 A GB1502114 A GB 1502114A GB 13649/75 A GB13649/75 A GB 13649/75A GB 1364975 A GB1364975 A GB 1364975A GB 1502114 A GB1502114 A GB 1502114A
- Authority
- GB
- United Kingdom
- Prior art keywords
- alloy
- minutes
- hours
- cooled
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1502114 Extruding at specified temperatures SOC DE VENTE DE L'ALUMINIUM PECHINEY 3 April 1975 [4 April 1974] 13649/75 Headings B3P B3V and B3Q A method of shaping an alloy at a higher than normal forming ratio and/or speed and with reduced tool wear comprises heating the alloy to a temperature between the solidus and liquidus points until less than 40% by weight of the alloy has liquefied, maintaining the temperature for between 5 minutes and 4 hours so that the solid dentritic phase has at least begun to change into a globular form, Fig. 2 (not shown), and working the alloy in this condition. Profiles of various section, bar, wire and tubes may be formed by operations such as drawings, extrusion, rolling, stamping, swaging and forging. The heat treatment permanently modifies the alloy structures so that a billet cooled after the heat treatment may have the improved, "rheotropic" working properties restored merely by heating to the solidus-liquidus range. In an example aluminium alloy billets were heated to 585-605 C. for 15 minutes to give a liquid content of 6-13%. The billets were extruded from a container heated to 420- 450 C., through a water-cooled die at an exit temperature of 450 C. Tests were carried out immediately after extrusion, after ageing for 8 hours at 175 C. and following water quenching after 2 hours at 505 C. and the above ageing. In numerous other aluminium alloy examples temperatures ranged between 572-625 C., times between 15 and 30 minutes and liquid content between 4 and 25%. The work may be cooled with air or water as it issues from a die to solidify substantially all of the liquid fraction.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
LU69788A LU69788A1 (en) | 1974-04-04 | 1974-04-04 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1502114A true GB1502114A (en) | 1978-02-22 |
Family
ID=19727630
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB13649/75A Expired GB1502114A (en) | 1974-04-04 | 1975-04-03 | Alloy treatment |
GB13650/75A Expired GB1499934A (en) | 1974-04-04 | 1975-04-03 | Alloy treatment |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB13650/75A Expired GB1499934A (en) | 1974-04-04 | 1975-04-03 | Alloy treatment |
Country Status (17)
Country | Link |
---|---|
JP (2) | JPS5615454B2 (en) |
BE (2) | BE827496A (en) |
CA (2) | CA1045783A (en) |
CH (2) | CH603805A5 (en) |
DD (2) | DD117372A5 (en) |
DE (2) | DE2514386B2 (en) |
ES (2) | ES436216A1 (en) |
FR (2) | FR2266749B1 (en) |
GB (2) | GB1502114A (en) |
IL (2) | IL47001A (en) |
IT (2) | IT1034784B (en) |
LU (1) | LU69788A1 (en) |
NL (2) | NL182415C (en) |
NO (2) | NO141943C (en) |
SE (2) | SE420801B (en) |
SU (1) | SU722494A3 (en) |
ZA (2) | ZA752150B (en) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5037489A (en) * | 1986-05-12 | 1991-08-06 | The University Of Sheffield | Thixotropic materials |
US5849115A (en) * | 1994-05-17 | 1998-12-15 | Honda Giken Kogyo Kabushiki Kaisha | Alloy material for thixocasting, process for preparing semi-molten alloy material for thixocasting and thixocasting process |
CN103103401A (en) * | 2012-12-11 | 2013-05-15 | 芜湖恒坤汽车部件有限公司 | Smelting preparation method for anti-yielding aluminum alloy section bar |
Families Citing this family (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0004174B1 (en) * | 1978-03-08 | 1983-04-27 | Massachusetts Institute Of Technology | A process for refining a non-eutectic metal alloy |
US4694881A (en) * | 1981-12-01 | 1987-09-22 | The Dow Chemical Company | Method for making thixotropic materials |
US4694882A (en) * | 1981-12-01 | 1987-09-22 | The Dow Chemical Company | Method for making thixotropic materials |
US4415374A (en) * | 1982-03-30 | 1983-11-15 | International Telephone And Telegraph Corporation | Fine grained metal composition |
US4524820A (en) * | 1982-03-30 | 1985-06-25 | International Telephone And Telegraph Corporation | Apparatus for providing improved slurry cast structures by hot working |
US4569218A (en) * | 1983-07-12 | 1986-02-11 | Alumax, Inc. | Apparatus and process for producing shaped metal parts |
EP0139168A1 (en) * | 1983-09-20 | 1985-05-02 | Alumax Inc. | Fine grained metal composition |
US4938052A (en) * | 1986-07-08 | 1990-07-03 | Alumax, Inc. | Can containment apparatus |
US4687042A (en) * | 1986-07-23 | 1987-08-18 | Alumax, Inc. | Method of producing shaped metal parts |
US4712413A (en) * | 1986-09-22 | 1987-12-15 | Alumax, Inc. | Billet heating process |
FR2665654B1 (en) * | 1990-08-09 | 1994-06-24 | Armines | PRESSURE CASTING MACHINE OF A THIXOTROPIC METAL ALLOY. |
CH683267A5 (en) * | 1991-06-10 | 1994-02-15 | Alusuisse Lonza Services Ag | A method for heating a workpiece of a metal alloy. |
DE4420533A1 (en) * | 1994-06-14 | 1995-12-21 | Salzburger Aluminium Ag | Process for the production of castings from aluminum alloys |
US5571346A (en) * | 1995-04-14 | 1996-11-05 | Northwest Aluminum Company | Casting, thermal transforming and semi-solid forming aluminum alloys |
US5758707A (en) * | 1995-10-25 | 1998-06-02 | Buhler Ag | Method for heating metallic body to semisolid state |
FR2746414B1 (en) * | 1996-03-20 | 1998-04-30 | Pechiney Aluminium | THIXOTROPE ALUMINUM-SILICON-COPPER ALLOY FOR SHAPING IN SEMI-SOLID CONDITION |
FR2747327B1 (en) * | 1996-04-11 | 1998-06-12 | Pechiney Recherche | METHOD AND TOOL FOR HIGH SPEED SPINNING OF ALUMINUM ALLOYS AND PROFILE OBTAINED |
EP0839589A1 (en) * | 1996-11-04 | 1998-05-06 | Alusuisse Technology & Management AG | Method for producing a metallic profiled strand |
US7591913B2 (en) * | 2004-04-06 | 2009-09-22 | Massachusetts Institute Of Technology | Thermoelectric properties by high temperature annealing |
CN103103414B (en) * | 2012-12-11 | 2016-05-18 | 芜湖恒坤汽车部件有限公司 | A kind of chromaking is processed the smelting preparation method of aluminium alloy extrusions |
CN103103413B (en) * | 2012-12-11 | 2016-06-08 | 芜湖恒坤汽车部件有限公司 | A kind of smelting preparation method of high-strength aluminum alloy section |
CN103103416B (en) * | 2012-12-11 | 2016-12-07 | 黄娜茹 | A kind of smelting preparation method of heat insulated shape bar of aluminum alloy |
CN103103402B (en) * | 2012-12-11 | 2016-05-18 | 芜湖恒坤汽车部件有限公司 | The smelting preparation method of a kind of static material end spraying aluminium alloy extrusions |
CN103103399B (en) * | 2012-12-11 | 2016-06-08 | 芜湖恒坤汽车部件有限公司 | A kind of smelting preparation method of the aluminium alloy extrusions of good stability |
CN103103398B (en) * | 2012-12-11 | 2016-06-08 | 芜湖恒坤汽车部件有限公司 | A kind of smelting preparation method of resistant to rust aluminium alloy extrusions |
CN103103415B (en) * | 2012-12-11 | 2016-06-08 | 芜湖恒坤汽车部件有限公司 | A kind of smelting preparation method of aluminium alloy extrusions |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CA957180A (en) * | 1971-06-16 | 1974-11-05 | Massachusetts, Institute Of Technology | Alloy compositions containing non-dendritic solids and process for preparing and casting same |
-
1974
- 1974-04-04 LU LU69788A patent/LU69788A1/xx unknown
-
1975
- 1975-02-27 FR FR7506954A patent/FR2266749B1/fr not_active Expired
- 1975-02-27 FR FR7506953A patent/FR2266748B1/fr not_active Expired
- 1975-04-01 SU SU752125297A patent/SU722494A3/en active
- 1975-04-02 DD DD185170A patent/DD117372A5/xx unknown
- 1975-04-02 DE DE19752514386 patent/DE2514386B2/en active Granted
- 1975-04-02 IT IT21922/75A patent/IT1034784B/en active
- 1975-04-02 DD DD185168A patent/DD117486A5/xx unknown
- 1975-04-02 IT IT21921/75A patent/IT1034783B/en active
- 1975-04-02 IL IL47001A patent/IL47001A/en unknown
- 1975-04-02 NO NO75751115A patent/NO141943C/en unknown
- 1975-04-02 SE SE7503776A patent/SE420801B/en not_active IP Right Cessation
- 1975-04-02 DE DE2514355A patent/DE2514355C3/en not_active Expired
- 1975-04-02 NO NO751114A patent/NO141942C/en unknown
- 1975-04-02 ES ES436216A patent/ES436216A1/en not_active Expired
- 1975-04-02 SE SE7503775A patent/SE7503775L/en unknown
- 1975-04-02 ES ES436217A patent/ES436217A1/en not_active Expired
- 1975-04-03 BE BE155030A patent/BE827496A/en not_active IP Right Cessation
- 1975-04-03 BE BE155031A patent/BE827497A/en not_active IP Right Cessation
- 1975-04-03 NL NLAANVRAGE7503992,A patent/NL182415C/en not_active IP Right Cessation
- 1975-04-03 JP JP4077675A patent/JPS5615454B2/ja not_active Expired
- 1975-04-03 NL NLAANVRAGE7503994,A patent/NL182416C/en active Search and Examination
- 1975-04-03 GB GB13649/75A patent/GB1502114A/en not_active Expired
- 1975-04-03 CA CA223,752A patent/CA1045783A/en not_active Expired
- 1975-04-03 GB GB13650/75A patent/GB1499934A/en not_active Expired
- 1975-04-03 CA CA223,751A patent/CA1047223A/en not_active Expired
- 1975-04-03 IL IL47002A patent/IL47002A/en unknown
- 1975-04-03 JP JP4077775A patent/JPS5615455B2/ja not_active Expired
- 1975-04-03 CH CH421375A patent/CH603805A5/xx not_active IP Right Cessation
- 1975-04-03 CH CH411275A patent/CH602928A5/xx not_active IP Right Cessation
- 1975-04-04 ZA ZA00752150A patent/ZA752150B/en unknown
- 1975-04-04 ZA ZA00752151A patent/ZA752151B/en unknown
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5037489A (en) * | 1986-05-12 | 1991-08-06 | The University Of Sheffield | Thixotropic materials |
US5133811A (en) * | 1986-05-12 | 1992-07-28 | University Of Sheffield | Thixotropic materials |
US5849115A (en) * | 1994-05-17 | 1998-12-15 | Honda Giken Kogyo Kabushiki Kaisha | Alloy material for thixocasting, process for preparing semi-molten alloy material for thixocasting and thixocasting process |
CN103103401A (en) * | 2012-12-11 | 2013-05-15 | 芜湖恒坤汽车部件有限公司 | Smelting preparation method for anti-yielding aluminum alloy section bar |
CN103103401B (en) * | 2012-12-11 | 2016-04-20 | 芜湖恒坤汽车部件有限公司 | A kind of smelting preparation method of anti-surrender aluminium alloy extrusions |
Also Published As
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB1502114A (en) | Alloy treatment | |
DE112005000511B4 (en) | Magnesium wrought alloy with improved extrudability and moldability | |
US4106956A (en) | Method of treating metal alloys to work them in the state of a liquid phase-solid phase mixture which retains its solid form | |
KR910009976B1 (en) | Method for manufacturing tubes | |
CN101151119B (en) | Method of manufacturing a consumable filler metal for use in a welding operation | |
US3613767A (en) | Continuous casting and rolling of 6201 aluminum alloy | |
KR840004183A (en) | Manufacturing process of the fine particle metal composition and its composition | |
US2249349A (en) | Method of hot working an aluminum base alloy and product thereof | |
ES418116A1 (en) | Aluminium alloys | |
US3990922A (en) | Processing aluminum alloys | |
US4140549A (en) | Method of fabricating an aluminum alloy electrical conductor | |
DE2060605A1 (en) | Sintered, heat- and corrosion-resistant, precipitation hardenable nickel-chromium alloy with a content of a hard-to-melt carbide produced by powder metallurgy | |
US6120625A (en) | Processes for producing fine grained metal compositions using continuous extrusion for semi-solid forming of shaped articles | |
DE2242235C3 (en) | Superplastic aluminum alloy | |
US3561105A (en) | Method of producing a hot-formed aluminum base product | |
US3960607A (en) | Novel aluminum alloy, continuously cast aluminum alloy shapes, method of preparing semirigid container stock therefrom, and container stock thus prepared | |
KR101400140B1 (en) | Preparing method for magnesium alloy extrudate and the magnesium alloy extrudate thereby | |
KR102393119B1 (en) | Method for producing semi-finished products deformed from aluminum-based alloys | |
GB1504421A (en) | Extrusion of aluminium alloys | |
US4404025A (en) | Process for manufacturing semifinished product from a memory alloy containing copper | |
US3920411A (en) | Aluminum alloy electrical conductor and method for making same | |
EP2395119A1 (en) | Method for shaping a magnesium-based alloy by means of extrusion | |
ES395972A1 (en) | Process of manufacturing forged or rolled rod steel from ledeburitic tool steel | |
GB2291431B (en) | Improvements in or relating to the production of extruded aluminium-lithium alloys | |
US5119660A (en) | Method for manufacturing metal objects |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PS | Patent sealed [section 19, patents act 1949] | ||
PE20 | Patent expired after termination of 20 years |
Effective date: 19950402 |