GB1406870A - Method of forming an economic optical waveguide fibre - Google Patents

Method of forming an economic optical waveguide fibre

Info

Publication number
GB1406870A
GB1406870A GB5996972A GB5996972A GB1406870A GB 1406870 A GB1406870 A GB 1406870A GB 5996972 A GB5996972 A GB 5996972A GB 5996972 A GB5996972 A GB 5996972A GB 1406870 A GB1406870 A GB 1406870A
Authority
GB
United Kingdom
Prior art keywords
glass
coating
silica
fibre
forming
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB5996972A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Corning Glass Works
Original Assignee
Corning Glass Works
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corning Glass Works filed Critical Corning Glass Works
Publication of GB1406870A publication Critical patent/GB1406870A/en
Expired legal-status Critical Current

Abstract

1406870 Glass fibre optical waveguides CORNING GLASS WORKS 29 Dec 1972 [3 Jan 1972] 59969/72 Addition to 1322993 Heading C1M A glass fibre for an optical waveguide is formed by applying a first coating 12 of glass to the inside wall of a glass tube 10, applying a second coating 14 of glass over the first coating 12, the second glass 14 having an index of refraction higher than that of the first glass 12, heating the composite structure as in a furnace 16 and drawing the heated structure to reduce the cross-sectional area and collapse the second coating 14 to form the core 20 of a clad fibre 26 of solid cross-section. Preferably fused silica is used, the tube 10 being of normal, impure, silica which is drawn down to a comparatively thick outer layer 24, the coating 12 being of pure silica and forming the usual cladding 22 for the waveguide and the coating 14 being of doped silica, dopants being as in the parent case, with the additional suggested material of germanium oxide.
GB5996972A 1970-05-11 1972-12-29 Method of forming an economic optical waveguide fibre Expired GB1406870A (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US3626770A 1970-05-11 1970-05-11
US21484272A 1972-01-03 1972-01-03

Publications (1)

Publication Number Publication Date
GB1406870A true GB1406870A (en) 1975-09-17

Family

ID=26712995

Family Applications (1)

Application Number Title Priority Date Filing Date
GB5996972A Expired GB1406870A (en) 1970-05-11 1972-12-29 Method of forming an economic optical waveguide fibre

Country Status (2)

Country Link
DE (1) DE2300061B2 (en)
GB (1) GB1406870A (en)

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1434977A (en) * 1972-10-13 1976-05-12 Sumitomo Electroc Ind Ltd Method of manufacturing an optical waveguide
US3884550A (en) * 1973-01-04 1975-05-20 Corning Glass Works Germania containing optical waveguide
DE2463016C2 (en) * 1973-08-21 1982-05-06 International Standard Electric Corp., 10022 New York, N.Y. Method of manufacturing a fiber optic light guide
GB2039880B (en) * 1978-08-18 1983-04-20 Western Electric Co Fabrication of optical fibres utilizing thermophoretic deposition of glass precursor particulates
US4425146A (en) * 1979-12-17 1984-01-10 Nippon Telegraph & Telephone Public Corporation Method of making glass waveguide for optical circuit
DE3136429C2 (en) * 1980-09-16 1987-01-22 Nippon Telegraph And Telephone Corp., Tokio/Tokyo Process for producing doped SiO↓2↓ glass
DE10134382B4 (en) * 2001-07-14 2006-01-19 Degussa Ag Erbium oxide doped fumed oxides

Also Published As

Publication number Publication date
DE2300061B2 (en) 1978-08-24
DE2300061A1 (en) 1973-07-26

Similar Documents

Publication Publication Date Title
GB1418112A (en) Optical waveguide fibres
GB1425681A (en) Germania-containing optical waveguide
US4832720A (en) Method for producing multi-core optical fiber
GB1427826A (en) Method of producing an optical transmission line
ES8103390A1 (en) High bandwidth optical waveguides and method of fabrication
JPS5727203A (en) Optical fiber waveguide
GB1322993A (en) Method of producing optical waveguides
GB1496788A (en) Optical fibre manufacture
GB1466496A (en) Method of making glass optical waveguide
ES8103389A1 (en) High bandwidth optical waveguide having B2O3 free core and method of fabrication
IL62006A (en) Gradient refractive index optical waveguide filament
GB1427327A (en) Glass optical fibres
GB1412884A (en) Light-conducting fibre
GB1403450A (en) Method of manufacturing an optical fibre light waveguide
JPS5678441A (en) Manufacture of single mode optical fiber
ES8201322A1 (en) Single mode fibre and method of manufacture
GB1406870A (en) Method of forming an economic optical waveguide fibre
GB1322992A (en) Optical waveguides
FR2428618A1 (en) Optical fibre preform mfr. - by depositing glass soot on rod of same compsn. and diffusion of fluorine into the rod
GB1394535A (en) Fibre optics
GB1213603A (en) Method of improving light transmission in glasses
GB1459199A (en) Optical fibres and processes for their production-
GB1340849A (en) Optical fibres
JPS6240301B2 (en)
FR2307639A1 (en) Optical fibres with low attenuation - drawn from fused silica blank contg. multilayer core of doped silica and flux (NL191076)

Legal Events

Date Code Title Description
PS Patent sealed
PLE Entries relating assignments, transmissions, licences in the register of patents