GB1371723A - Catalytic structure and method of same - Google Patents

Catalytic structure and method of same

Info

Publication number
GB1371723A
GB1371723A GB3295372A GB3295372A GB1371723A GB 1371723 A GB1371723 A GB 1371723A GB 3295372 A GB3295372 A GB 3295372A GB 3295372 A GB3295372 A GB 3295372A GB 1371723 A GB1371723 A GB 1371723A
Authority
GB
United Kingdom
Prior art keywords
hydroxide
support
prepared
copper
ammonium hydroxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB3295372A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Texaco Development Corp
Original Assignee
Texaco Development Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Texaco Development Corp filed Critical Texaco Development Corp
Priority to GB3295372A priority Critical patent/GB1371723A/en
Publication of GB1371723A publication Critical patent/GB1371723A/en
Expired legal-status Critical Current

Abstract

1371723 Copper compounds: bromine: sulphur trioxide TEXACO DEVELOPMENT CORP 14 July 1972 32953/72 Heading C1A [Also in Divisions B1 C2 C5 and F1] Catalytically-active crystalline material having a specified X-ray diffraction pattern and the empirical formula, expressed in terms of oxides, xCuO.yAl2O3.nH2O wherein x is from 1 to 3, y is from 1 to 4 and n is a positive number, is prepared, in the form of a layer adherent on a support, by a procedure wherein the support is contacted, at a temperature preferably of from 100 to 212‹ F., with a solution which is prepared from an aluminate, an ammoniacal reagent, for example ammonia or ammonium hydroxide, and a copper oxide, hydroxide or salt, for example carbonate nitrate, sulphate, chromate, acetate, benzoate or oxalate, and which has a Cu to Al molar ratio of from 1À5 to 5 and a NH3 to Cn molar ratio of at least 4. The aluminate may be prepared from aluminium chips or fragments and a base, for example lithium hydroxide, sodium hydroxide, potassium hydroxide or a quaternary organic hydroxide such as tetramethyl ammonium hydroxide. Contacting may be effected in water, methyl alcohol, ethyl alcohol or propyl alcohol; the resulting coated support may be calcined at a temperature of from 300 to 1000‹F. As exemplified, the crystalline material is prepared fom aluminium chips, sodium hydroxide, ammonium hydroxide and either copper sulphate (Example I) or copper nitrate (Example II or III). The structure comprising the catalyticallyactive layer, which may have a thickness of from 1 to 100 mils., and the support, which may be contained in a casing or tube, may be in the form of bells, bars, chain, mesh, plates, saddle, sheet, tubes or wire and may be formed of steel, stainless steel, nickel, titanium, a sintered metal material or a refractory or ceramic material, for example silica, a high melting glass or a refractory metal carbide, silicate or oxide such as magnesia, may be used in the conversion of sulphur dioxide to sulphur trioxide in stack gases; Example II refers to the use of a structure comprising a nickel-chromium-iron alloy mesh support in the oxidation of hydrogen bromide to bromine.
GB3295372A 1972-07-14 1972-07-14 Catalytic structure and method of same Expired GB1371723A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
GB3295372A GB1371723A (en) 1972-07-14 1972-07-14 Catalytic structure and method of same

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB3295372A GB1371723A (en) 1972-07-14 1972-07-14 Catalytic structure and method of same

Publications (1)

Publication Number Publication Date
GB1371723A true GB1371723A (en) 1974-10-23

Family

ID=10346455

Family Applications (1)

Application Number Title Priority Date Filing Date
GB3295372A Expired GB1371723A (en) 1972-07-14 1972-07-14 Catalytic structure and method of same

Country Status (1)

Country Link
GB (1) GB1371723A (en)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0044444A1 (en) * 1980-07-23 1982-01-27 BASF Aktiengesellschaft Use of hydrogenation catalysts for the production of propanediols and process for the production of propanediols with such catalysts
EP0061891A1 (en) * 1981-03-26 1982-10-06 Gallaher Limited Catalysts and their production
US4677234A (en) * 1985-02-04 1987-06-30 Union Carbide Corporation Process for the preparation of ethylene glycol
EP0548481A1 (en) * 1991-12-23 1993-06-30 Süd-Chemie Ag Use of copperoxide-aluminium oxide-magnesium oxide catalysts for converting carbon monoxide

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0044444A1 (en) * 1980-07-23 1982-01-27 BASF Aktiengesellschaft Use of hydrogenation catalysts for the production of propanediols and process for the production of propanediols with such catalysts
EP0061891A1 (en) * 1981-03-26 1982-10-06 Gallaher Limited Catalysts and their production
US4677234A (en) * 1985-02-04 1987-06-30 Union Carbide Corporation Process for the preparation of ethylene glycol
EP0548481A1 (en) * 1991-12-23 1993-06-30 Süd-Chemie Ag Use of copperoxide-aluminium oxide-magnesium oxide catalysts for converting carbon monoxide

Similar Documents

Publication Publication Date Title
US4565803A (en) Methanol synthesis catalyst
US4189405A (en) Intermetallic catalysts
EP0205102B1 (en) Perovskite-type oxidation catalysts and method for preparing the catalysts
GB1288638A (en)
GB1318157A (en) Process for preparation of high-silica zeolites
KR960706453A (en) Composition Precursor and Cerium and Zirconium Mixed Oxied Based Composition, Method for Its Preparation and Use Thereof
GB1325392A (en) Method for preparing a metallic catalyst
ES2000171A6 (en) Process for the preparation of a silver-containing catalyst.
GB1371723A (en) Catalytic structure and method of same
RU2007114583A (en) COMPOUND HAVING THE STRUCTURE OF PYROCHLOR, AND ITS USE AS THE CARRIER OF THE CATALYST IN THE REACTION OF CONVERSION OF WATER GAS
US4060500A (en) Preparation of mixed metal oxides by decomposition of carbonate solid solutions having the calcite structure
JPH02280836A (en) Preparation of catalyst for dimethyl ether synthesis
KR870005946A (en) Method for preparing 5-ethylidene-2-norbornene of high quality
KR880001328A (en) Silver-containing catalyst and preparation method thereof
GB1378269A (en) Electrolytic method of preparing a coated material useful as an catalyst
JPS5531428A (en) Production of copper-aluminum oxide catalyst for hydrogenation
GB1126169A (en) Process for the conversion of hydrocarbons
JPS6261640A (en) Sulfur resistant methanation catalyst
GB985556A (en) Thallium-containing catalysts
GB1245349A (en) Extended zeolitic structures
SU331649A1 (en) Chlorine production method
JPS62153158A (en) Heat resistant composition and manufacture
US2894046A (en) Manufacture of para-xylene
JP2559718B2 (en) Heat resistant catalyst for catalytic combustion reaction and method for producing the same
GB1271710A (en) Treatment of exhaust gases from leaded motor fuels

Legal Events

Date Code Title Description
PS Patent sealed
PLNP Patent lapsed through nonpayment of renewal fees