GB1144176A - Polyurethane sheet materials - Google Patents

Polyurethane sheet materials

Info

Publication number
GB1144176A
GB1144176A GB17128/66A GB1712866A GB1144176A GB 1144176 A GB1144176 A GB 1144176A GB 17128/66 A GB17128/66 A GB 17128/66A GB 1712866 A GB1712866 A GB 1712866A GB 1144176 A GB1144176 A GB 1144176A
Authority
GB
United Kingdom
Prior art keywords
curing
polyurethane
components
groups
belt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB17128/66A
Inventor
Kenneth Norcross
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nairn Williamson Ltd
Original Assignee
Nairn Williamson Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to NL272890D priority Critical patent/NL272890A/xx
Priority to GB44800/60A priority patent/GB929442A/en
Priority claimed from GB44800/60A external-priority patent/GB929442A/en
Application filed by Nairn Williamson Ltd filed Critical Nairn Williamson Ltd
Priority to GB17128/66A priority patent/GB1144176A/en
Publication of GB1144176A publication Critical patent/GB1144176A/en
Expired legal-status Critical Current

Abstract

1,144,176. Polyurethane films; sheet casting polyurethane. NAIRN-WILLIAMSON Ltd. 13 April, 1967 [19 April, 1966], No. 17128/66. Addition to 929,442. Headings B5A and B5B. [Also in Divisions B2 and C3] A process for reproducing a fine pattern in relief comprises the steps of feeding a liquid mixture of components which will react to form a solid flexible polyurethane, with pigment, fillers or other additives as desired, on to an endless belt of a silicone elastomer bearing a negative of the fine pattern, running the belt with the mixture on it through a heating chamber to cause the mixture to emerge as a cured layer on the belt, cooling the layer while it is still on the belt, and then stripping it off the belt. The mixture of components which will form a polyurethane on curing normally contains a polyisocyanate together with a polyol or a polyamine or both. The polyisocyanate may be a di- or tri-isocyanate or an isocyanate adduct bearing, e.g., both isocyanate and urethane groups, or a pre-polymer having two or more active isocyanate groups per molecule. Examples of suitable pre-polymers contain urethane and ester groups or urethane and ether groups. The polyisocyanate component must contain at least two isocyanate groups per molecule, and the polyol or polyamine components at least two hydroxyl or amine groups per molecule. The polyol may be a simple diol or triol or a pre-polymer containing urethane groups and ester or ether groups in addition to the active hydroxyl groups. The thermoplasticity of the polyurethane formed may be varied by the choice of the components and their proportions, up to a state of complete non- thermo-plasticity. The curing conditions used to form the polyurethane from the mixture of components depend on the components, and the presence or absence of curing catalysts. Curing may be effected at 120‹ to 180‹ C. for from 3 to 30 mins.; or a two-stage curing process may be used in which the layer is first heated to 120‹ to 180‹ C. for from 2 to 5 mins. to effect partial curing, followed by a second stage curing at 120‹ to 180‹ C. for a further 2 to 30 mins. The endless belt of silicone elastomer is formed as described in the parent Specification. Examples are given.
GB17128/66A 1960-12-30 1966-04-19 Polyurethane sheet materials Expired GB1144176A (en)

Priority Applications (3)

Application Number Priority Date Filing Date Title
NL272890D NL272890A (en) 1966-04-19
GB44800/60A GB929442A (en) 1966-04-19 1960-12-30 Improvements relating to the manufacture of sheet materials from polyvinyl chloride
GB17128/66A GB1144176A (en) 1960-12-30 1966-04-19 Polyurethane sheet materials

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB44800/60A GB929442A (en) 1966-04-19 1960-12-30 Improvements relating to the manufacture of sheet materials from polyvinyl chloride
GB17128/66A GB1144176A (en) 1960-12-30 1966-04-19 Polyurethane sheet materials

Publications (1)

Publication Number Publication Date
GB1144176A true GB1144176A (en) 1969-03-05

Family

ID=26252495

Family Applications (1)

Application Number Title Priority Date Filing Date
GB17128/66A Expired GB1144176A (en) 1960-12-30 1966-04-19 Polyurethane sheet materials

Country Status (1)

Country Link
GB (1) GB1144176A (en)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0050514A1 (en) * 1980-10-22 1982-04-28 Smith and Nephew Associated Companies p.l.c. Wound dressings and processes for their preparation
EP1059379A2 (en) * 1999-06-07 2000-12-13 Benecke-Kaliko AG Laminates with one or more polyurethane layers, method of manufacture and their use
DE102009003680A1 (en) 2009-03-26 2010-09-30 Benecke-Kaliko Ag polymer mixture
EP1927466B1 (en) 2006-11-30 2016-01-06 Benecke-Kaliko AG Composite structure with a polyurethane coating, method for its manufacture and application
CN108301221A (en) * 2017-12-28 2018-07-20 凤阳加松新型材料科技有限公司 A kind of macromolecule silicon synthetic leather that resistance to acid and alkali is fabulous

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0050514A1 (en) * 1980-10-22 1982-04-28 Smith and Nephew Associated Companies p.l.c. Wound dressings and processes for their preparation
EP1059379A2 (en) * 1999-06-07 2000-12-13 Benecke-Kaliko AG Laminates with one or more polyurethane layers, method of manufacture and their use
EP1059379A3 (en) * 1999-06-07 2003-07-23 Benecke-Kaliko AG Laminates with one or more polyurethane layers, method of manufacture and their use
EP1927466B1 (en) 2006-11-30 2016-01-06 Benecke-Kaliko AG Composite structure with a polyurethane coating, method for its manufacture and application
EP1927466B2 (en) † 2006-11-30 2024-05-15 Benecke-Kaliko AG Composite structure with a polyurethane coating, method for its manufacture and application
DE102009003680A1 (en) 2009-03-26 2010-09-30 Benecke-Kaliko Ag polymer mixture
EP2236662A1 (en) 2009-03-26 2010-10-06 Benecke-Kaliko AG Polymer mixture containing a prepolymer having isocyanate groups
CN108301221A (en) * 2017-12-28 2018-07-20 凤阳加松新型材料科技有限公司 A kind of macromolecule silicon synthetic leather that resistance to acid and alkali is fabulous

Similar Documents

Publication Publication Date Title
BR8402217A (en) PROCESS FOR THE PREPARATION OF POLYURETHANE PRE-POLYMERS WITH TERMINAL ISOCIANATE GROUPS, COMPOSED ON THE BASIS OF SUCH PRE-POLYMERS, USABLE FOR THE PRODUCTION OF POLYURETHANE FOAMS OF UNIQUE COMPONENT HARDENED IN HUMIDITY CONDITIONS AND APPLICATION OF SUCH CONDITIONS
DE3174756D1 (en) Process for preparing integral skin microcellular polyester base polyurethane elastomers, the elastomers per se isocyanate curable compositions and two component combinations for producing the elastomers and cast shoe soles attached to shoe uppers
KR910014487A (en) Unfilled low boiling urethane structural adhesives with sagging resistance
DE1120691B (en) Process for the production of thermoplastic or crosslinked, optionally foamed polyurethanes
US3440223A (en) Polyurethanes and method of making
KR890002363A (en) Polyurethane adhesive
GB1312589A (en) Liquid castable elastomers
GB1286422A (en) Curable polyurethane composition
GB1144176A (en) Polyurethane sheet materials
ES477660A1 (en) Process for the preparation of moulded foams on the basis of polyisocyanate.
AU548332B2 (en) Polyurethane compositions and processes
FR2548956B1 (en) HIGH OPTICAL QUALITY TRANSPARENT PLASTIC SHEET
ES232597A1 (en) Polymeric materials and method of producing same
EP0210566A3 (en) Process for the fabrication of light resistant, elastic polyurethane molded parts
GB1045806A (en) Process for the production of synthetic resins containing urethane groups
GB1042858A (en) Process for the production of polyisocyanate compositions
GB1441110A (en) Shuttlecocks
FR2083453A1 (en) Hydrolysis-resistant polyurethanes
GB1299242A (en) Method of making a polyurethane article having a resilient mass bonded to a rigid structure
GB938868A (en) Material suitable for use in upholstery
GB1313565A (en) Polyurethanes
KR920002702A (en) Plural liquid packaged, thermosetting polyisocyanate-polyol-polyepoxy resin blends and process for producing molding resin products therefrom
GB907230A (en) Process for producing cellular polyurethane elastomers