FR2973025B1 - PULVERULENT MATERIAL COMPRISING AN ACTIVATOR GLASS FOR CEMENTITIOUS PRODUCTS - Google Patents

PULVERULENT MATERIAL COMPRISING AN ACTIVATOR GLASS FOR CEMENTITIOUS PRODUCTS

Info

Publication number
FR2973025B1
FR2973025B1 FR1156200A FR1156200A FR2973025B1 FR 2973025 B1 FR2973025 B1 FR 2973025B1 FR 1156200 A FR1156200 A FR 1156200A FR 1156200 A FR1156200 A FR 1156200A FR 2973025 B1 FR2973025 B1 FR 2973025B1
Authority
FR
France
Prior art keywords
cement
alkaline
grains
glass
activator
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
FR1156200A
Other languages
French (fr)
Other versions
FR2973025A1 (en
Inventor
Joumana Yammine
Emmanuel Lecomte
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Saint Gobain Weber SA
Original Assignee
Saint Gobain Weber SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Saint Gobain Weber SA filed Critical Saint Gobain Weber SA
Priority to FR1156200A priority Critical patent/FR2973025B1/en
Priority to PCT/FR2012/050611 priority patent/WO2012131241A1/en
Publication of FR2973025A1 publication Critical patent/FR2973025A1/en
Application granted granted Critical
Publication of FR2973025B1 publication Critical patent/FR2973025B1/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to a powder material including grains of an activating glass including: at least 20 wt % of SiO2; more than 20 wt % and less than 50 wt % of an alkaline oxide selected from among Na2O, Li2O or K2O; 0.1 to 60 wt % alkaline-earth oxide selected from among CaO or MgO; and at least one of the following two ingredients a) and b): a) grains of a cement selected from among Portland cement, aluminous cement, sulfo-aluminous cement, and quick-setting cement; and b) grains of a solid inorganic compound, the sum of the silica, alumina, and alkaline-earth oxide contents of which is more than 50 wt % and which contains less than 20 wt % of an alkaline oxide. The activating glass enhances the developmental kinetics of the mechanical properties of the hardened hydrated material made from the hydraulic binder powder material.
FR1156200A 2011-03-25 2011-07-08 PULVERULENT MATERIAL COMPRISING AN ACTIVATOR GLASS FOR CEMENTITIOUS PRODUCTS Active FR2973025B1 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
FR1156200A FR2973025B1 (en) 2011-03-25 2011-07-08 PULVERULENT MATERIAL COMPRISING AN ACTIVATOR GLASS FOR CEMENTITIOUS PRODUCTS
PCT/FR2012/050611 WO2012131241A1 (en) 2011-03-25 2012-03-23 Powder material including activating glass for cement products

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
FR1152499A FR2973022B1 (en) 2011-03-25 2011-03-25 GLASS FOR CEMENTITIOUS MATERIALS
FR1156200A FR2973025B1 (en) 2011-03-25 2011-07-08 PULVERULENT MATERIAL COMPRISING AN ACTIVATOR GLASS FOR CEMENTITIOUS PRODUCTS

Publications (2)

Publication Number Publication Date
FR2973025A1 FR2973025A1 (en) 2012-09-28
FR2973025B1 true FR2973025B1 (en) 2013-03-15

Family

ID=44785954

Family Applications (2)

Application Number Title Priority Date Filing Date
FR1152499A Active FR2973022B1 (en) 2011-03-25 2011-03-25 GLASS FOR CEMENTITIOUS MATERIALS
FR1156200A Active FR2973025B1 (en) 2011-03-25 2011-07-08 PULVERULENT MATERIAL COMPRISING AN ACTIVATOR GLASS FOR CEMENTITIOUS PRODUCTS

Family Applications Before (1)

Application Number Title Priority Date Filing Date
FR1152499A Active FR2973022B1 (en) 2011-03-25 2011-03-25 GLASS FOR CEMENTITIOUS MATERIALS

Country Status (2)

Country Link
FR (2) FR2973022B1 (en)
WO (1) WO2012131241A1 (en)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3061734A4 (en) * 2013-10-21 2017-06-21 Envirocem, S.L. Lightweight concretes and mortars
GB201501307D0 (en) * 2015-01-27 2015-03-11 Knauf Insulation And Knauf Insulation Doo Skofja Loka And Knauf Insulation Gmbh And Knauf Insulation Process for the preparation of a silica melt
CN114477924A (en) * 2021-12-28 2022-05-13 重庆重通成飞新材料有限公司 Wind power blade recycled fiber reinforced fiber sulphoaluminate cement wallboard formula

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1379085A (en) * 1972-10-05 1975-01-02 Gnii Stekla Production of aggregates or fillers suitable for use in construction mixes
DE2407538B2 (en) * 1974-02-16 1976-04-01 Jenaer Glaswerk Schott & Gen., 6500 Mainz GLASSES BASED ON SIO TIEF 2 - ZNO AS A REINFORCEMENT AGENT IN CONCRETE AND FOR INSTALLATION IN LIGHTWEIGHT CONCRETE
JPH11209130A (en) * 1998-01-22 1999-08-03 Kamaike Yutaka Manufacture of super-lightweight aggregate
FR2818358B1 (en) * 2000-12-15 2006-03-10 Saint Gobain METHOD FOR DESTRUCTION AND / OR INERTING WASTE
DE112004000094A5 (en) * 2003-02-25 2008-04-03 Schott Ag Antimicrobial borosilicate glass
EP1856003A2 (en) * 2005-02-24 2007-11-21 James Hardie International Finance B.V. Alkali resistant glass compositions
EP1724242A1 (en) * 2005-05-18 2006-11-22 I.C.R.S. Industrial Ceramic Reinforcement Solution S.r.L. Process for making expanded glass products, and the products obtained by means of said process
US20080276652A1 (en) * 2007-05-11 2008-11-13 Jon Frederick Bauer Submerged combustion for melting high-temperature glass

Also Published As

Publication number Publication date
FR2973025A1 (en) 2012-09-28
WO2012131241A1 (en) 2012-10-04
FR2973022A1 (en) 2012-09-28
FR2973022B1 (en) 2022-04-01

Similar Documents

Publication Publication Date Title
PH12017500021A1 (en) Ultra-high performance concretes having a low cement content
MA30306B1 (en) GLAZING COMPOSITIONS
JP2013537163A5 (en)
MX2017008284A (en) BINDER BASED ON A SOLID MINERAL COMPOUND RICH IN ALKALINE-EARTH OXIDE WITH PHOSPHATE-CONTAINING<i/>ACTIVATORS.
PT1091913E (en) SUPERSULFATATED BINDING AGENT ACTIVATED BY ALKALINE AGENTS
WO2009025313A1 (en) Glass composition for sealing
BR112016028666A2 (en) cement composite and a method for producing this
RU2012125390A (en) ABRASIVE PRODUCT (OPTIONS) AND METHOD FOR ITS FORMATION
KR20130128559A (en) Powder type alkali activator for cementless concrete
GB2459398A (en) Binder composition for waste materials
EP2224895A4 (en) Aluminous cement-based composition for application in endodontics and cementitious product obtained thereof
MX2020006076A (en) Control of time of setting of geopolymer compositions containing high-ca reactive aluminosilicate materials.
RU2018112445A (en) Improved friction materials for brake pads based on binding compositions and related brake pads
FR2973025B1 (en) PULVERULENT MATERIAL COMPRISING AN ACTIVATOR GLASS FOR CEMENTITIOUS PRODUCTS
JP4942949B2 (en) Cement composition
KR20130094968A (en) Alkali-activated binder with no cement including slaked dolomite
KR101375279B1 (en) Ultra high strength concrete
KR101746518B1 (en) Crack Repair Performance
US20190055165A1 (en) Precast refractory block for coke oven
PL415929A1 (en) Raw material batch for production of portland cement clinker
SU1321704A1 (en) Glass
PL415930A1 (en) Raw material batch intended for production of portland cement clinker
CN106116432A (en) A kind of fireproof high-temperature resistant plasterboard
PL430217A1 (en) Slag-containing cement, method of producing slag-containing cement, method of producing concrete and use of slag from ferroalloy production
PL427833A1 (en) Composition of high-strength pozzolan mixture

Legal Events

Date Code Title Description
PLFP Fee payment

Year of fee payment: 6

PLFP Fee payment

Year of fee payment: 7

PLFP Fee payment

Year of fee payment: 8

PLFP Fee payment

Year of fee payment: 10

PLFP Fee payment

Year of fee payment: 11

PLFP Fee payment

Year of fee payment: 12

PLFP Fee payment

Year of fee payment: 13