FR2769185A1

FR2769185A1 - Metal wire holder, especially a key ring, made of a shape memory alloy

Info

Publication number: FR2769185A1
Application number: FR9712520A
Authority: FR
Inventors: Bernard Prandi; Bourlais Alain Le; Loic Giquel
Original assignee: Memometal Industries
Current assignee: Memometal Industries
Priority date: 1997-10-02
Filing date: 1997-10-02
Publication date: 1999-04-09
Anticipated expiration: 2017-10-02
Also published as: FR2769185B1

Abstract

An object holder made of metal wire, especially a key ring, is produced from a shape memory alloy of e.g. nickel and titanium. Preferred alloys have a martensitic transformation start temperature of 0-20 (preferably 5-15) deg C, so that the easily deformable martensitic structure can be formed by contact with cold water or ice, and an austenitic transformation finish temperature of 20-40 (preferably 25-35) deg C, so that the rigid austenitic structure can be formed by contact with the hand, hot water or a flame.

Description

La présente invention a trait à un accessoire permettant la retenue d'objets pourvus d'un orifice, notamment un porteclefs, du type comprenant au moins une zone de retenue des objets, constituée par un fil métallique replié sur lui-même le long duquel est destiné à s'enfiler chaque objet à retenir. The present invention relates to an accessory allowing the retention of objects provided with an orifice, in particular a key holder, of the type comprising at least one object retention zone, constituted by a metallic wire folded back on itself along which is intended to put on each object to retain.

Ce type d'accessoire est, de manière habituelle, réalisé sous la forme d'un fil métallique replié sur lui-même de manière à former, par exemple, plusieurs spires accollées. Pour disposer un objet, tel qu'une clef, sur cet accessoire, il faut tout d'abord engager un orifice dont est pourvu cet objet, ou bien encore un élément dont il est solidaire, autour d'une extrémité du fil, puis le déplacer le long de ce dernier. Pour désolidariser l'objet de l'accessoire, l'opération est inversée. This type of accessory is, in the usual way, produced in the form of a metal wire folded back on itself so as to form, for example, several contiguous turns. To place an object, such as a key, on this accessory, you must first engage a hole which is provided with this object, or even an element with which it is secured, around one end of the wire, then the move along the latter. To separate the object from the accessory, the operation is reversed.

Etant donné que cet accessoire est prévu pour assurer la retenue de l'objet auquel il est assujetti, le fil métallique qui le constitue est pré-contraint. De la sorte, en l'absence de toute action extérieure, les spires que forme ce fil sont jointives et présentent une résistance importante à tout effort visant à les écarter les unes des autres. De ce fait, les opérations consistant respectivement à enfiler l'objet sur l'accessoire et l'en retirer sont délicates, voire douloureuses pour l'utilisateur et susceptibles par exemple d'endommager l'ongle ou le doigt de ce dernier. Since this accessory is intended to ensure the retention of the object to which it is subject, the metal wire which constitutes it is pre-stressed. In this way, in the absence of any external action, the turns formed by this wire are contiguous and exhibit significant resistance to any effort aimed at keeping them apart from one another. As a result, the operations consisting respectively of putting the object on the accessory and removing it are delicate, even painful for the user and liable for example to damage the nail or the finger of the latter.

L'invention se propose donc de réaliser un accessoire qui permette de pallier les inconvénients de l'art antérieur évoqués ci-dessus. The invention therefore proposes to provide an accessory which overcomes the drawbacks of the prior art mentioned above.

A cet effet, elle a pour objet un accessoire du type précité, caractérisé en ce que le fil métallique qui constitue la zone de retenue des objets est réalisé en un alliage à mémoire de forme. To this end, it relates to an accessory of the aforementioned type, characterized in that the metal wire which constitutes the area for retaining objects is made of a shape memory alloy.

Comme il est bien connu, un alliage à mémoire de forme présente, de part et d'autre d'une température de transition, une structure cristalline austénitique stable à chaud, et une structure martensitique stable à froid. As is well known, a shape memory alloy has, on either side of a transition temperature, an austenitic crystalline structure stable when hot, and a martensitic structure stable when cold.

L'expression d'alliage à mémoire de forme vient du fait qu'une pièce ayant été conformée dans sa structure austénitique, puis ayant subi une transformation dans sa structure martensitique, par exemple par refroidissement audessous de la température de transition, peut prendre une forme seconde et retrouve ensuite sa forme première par retour à la structure austénitique. The expression shape memory alloy comes from the fact that a part having been shaped in its austenitic structure, then having undergone a transformation in its martensitic structure, for example by cooling below the transition temperature, can take a form second and then regains its first form by returning to the austenitic structure.

Le cycle de transformation de ces alliages à mémoire de forme est déterminé par quatre températures caractéristiques, qui sont portées sur le graphique représenté à la figure 1, dans lequel l'axe des abscisses correspond à la température, et l'axe des ordonnées correspond au pourcentage de la phase martensitique de l'alliage. The transformation cycle of these shape memory alloys is determined by four characteristic temperatures, which are plotted on the graph represented in FIG. 1, in which the abscissa axis corresponds to the temperature, and the ordinate axis corresponds to the percentage of the martensitic phase of the alloy.

Les quatre températures caractéristiques sont les suivantes
- M5 est la température de début d'apparition de
martensite à partir de l'état austénitique
- Mf est la température de fin d'apparition de
martensite à partir de l'état austénitique
- As est la température de début d'apparition
d'austénite à partir de l'état martensitique ; et
- Af est la température de fin d'apparition
d'austénite à partir de l'état martensitique.The four characteristic temperatures are as follows
- M5 is the temperature at which onset of
martensite from the austenitic state
- Mf is the temperature at the end of the appearance of
martensite from the austenitic state
- As is the onset temperature
austenite from the martensitic state; and
- Af is the temperature at the end of appearance
of austenite from the martensitic state.

Dans sa structure austénitique, l'alliage à mémoire de forme présente une résistance importante à la traction, alors que dans sa structure martensitique, il est aisément malléable. In its austenitic structure, the shape memory alloy has a high tensile strength, while in its martensitic structure, it is easily malleable.

On conçoit donc que l'accessoire de retenue conforme à l'invention permet à la fois d'assurer, dans sa structure austénitique, un maintien fiable des objets auxquels il est assujetti, et peut également être facilement déformé, dans sa structure martensitique, de manière à introduire ou à enlever ces objets.It is therefore understandable that the retaining accessory according to the invention makes it possible both to ensure, in its austenitic structure, reliable maintenance of the objects to which it is subject, and can also be easily deformed, in its martensitic structure, to way to introduce or remove these objects.

L'accessoire objet de l'invention est tout d'abord conformé dans sa structure austénitique, de sorte qu'il présente une grande rigidité. Cependant, il suffit de le porter à une température inférieure à M9 pour que ses caractéristiques martensitiques commencent à apparaître, et en particulier inférieure à Mf pour que sa structure devienne entièrement martensitique. Dans cette gamme de températures, il est aisément déformable et peut donc faire l'objet de manipulations n'entraînant pas de difficulté de la part de l'utilisateur. The object of the invention object is firstly shaped in its austenitic structure, so that it has great rigidity. However, it suffices to bring it to a temperature below M9 for its martensitic characteristics to begin to appear, and in particular below Mf for its structure to become entirely martensitic. In this temperature range, it is easily deformable and can therefore be manipulated without causing any difficulty on the part of the user.

Après avoir introduit les objets sur l'accessoire, ou les en avoir retirés, il suffit de porter le fil métallique audessus de la température As et, de préférence, au-dessus de la température Af, pour qu'il retrouve à la fois sa forme première dans laquelle il assure la retenue de l'objet, et ses propriétés de rigidité. After inserting the objects on the accessory, or having removed them, it is enough to bring the metal wire above the temperature As and, preferably, above the temperature Af, so that it finds at the same time its primary form in which it ensures the retention of the object, and its rigidity properties.

Selon une caractéristique avantageuse de l'invention, l'alliage possède une température de début d'apparition martensitique sans contrainte mécanique, comprise entre OOC et 200C, de préférence entre 50C et 150C. A cette gamme de températures, il suffit par exemple de passer l'accessoire sous l'eau froide, ou de le mettre en contact avec un glaçon, pour que sa structure devienne martensitique et qu'il soit ainsi aisément manipulable. According to an advantageous characteristic of the invention, the alloy has a temperature at the onset of martensitic appearance without mechanical stress, between OOC and 200C, preferably between 50C and 150C. At this range of temperatures, it suffices for example to pass the accessory under cold water, or to put it in contact with an ice cube, so that its structure becomes martensitic and that it is thus easily manipulated.

Selon une autre caractéristique avantageuse de l'invention, l'alliage possède une température de fin d'apparition austénitique (Af) sans contrainte mécanique comprise entre 200C et 400C, de préférence entre 250C et 350C. According to another advantageous characteristic of the invention, the alloy has an austenitic end temperature (Af) without mechanical stress between 200C and 400C, preferably between 250C and 350C.

De ce fait, exposer l'accessoire à la flamme d'un briquet, le passer sous l'eau chaude ou bien encore le prendre au creux de la main lui permet de recouvrer sa structure austénitique et donc ses propriétés de rigidité.Therefore, exposing the accessory to the flame of a lighter, passing it under hot water or even taking it in the palm of your hand allows it to recover its austenitic structure and therefore its rigidity properties.

Selon une caractéristique supplémentaire de l'invention, l'alliage se compose de titane et de nickel, et il contient entre 55,2 et 56% et, de préférence, environ 55,7% en poids de nickel. According to an additional characteristic of the invention, the alloy consists of titanium and nickel, and it contains between 55.2 and 56% and, preferably, about 55.7% by weight of nickel.

Selon une caractéristique supplémentaire de l'invention, l'alliage se compose de titane, de nickel et de cuivre, et il contient, en poids, entre 45,2 et 51% de nickel, entre 44 et 44,8% de titane et entre 5 et 10% de cuivre. According to an additional characteristic of the invention, the alloy is composed of titanium, nickel and copper, and it contains, by weight, between 45.2 and 51% of nickel, between 44 and 44.8% of titanium and between 5 and 10% copper.

Selon une caractéristique supplémentaire de l'invention, l'alliage se compose de cuivre, d'aluminium et de nickel, et il contient, en poids, 13 à 15% d'aluminium, 2 à 5% de nickel, le complément étant constitué par le cuivre. According to an additional characteristic of the invention, the alloy consists of copper, aluminum and nickel, and it contains, by weight, 13 to 15% of aluminum, 2 to 5% of nickel, the balance being constituted by copper.

Selon une caractéristique supplémentaire de l'invention, l'alliage se compose de cuivre, d'aluminium et de zinc, et il contient en poids, 15 à 25% de zinc, 5 à 7% d'aluminium, le complément étant constitué par le cuivre. According to an additional characteristic of the invention, the alloy consists of copper, aluminum and zinc, and it contains by weight, 15 to 25% of zinc, 5 to 7% of aluminum, the balance being constituted by the copper.

Selon une caractéristique supplémentaire de l'invention, la zone de retenue comprend, dans la structure austénitique de l'alliage, au moins deux séries de dents mutuellement imbriquées, ou au moins deux spires jointives. According to an additional characteristic of the invention, the retaining zone comprises, in the austenitic structure of the alloy, at least two sets of mutually nested teeth, or at least two contiguous turns.

Selon une caractéristique avantageuse de l'invention, l'accessoire comprend une zone de réception des objets, adjacente à la zone de retenue, cette zone de réception comportant, à son extrémité opposée à la zone de retenue, des moyens de butée aptes à limiter le déplacement des objets. According to an advantageous characteristic of the invention, the accessory comprises a zone for receiving objects, adjacent to the retaining zone, this reception zone comprising, at its end opposite to the retaining zone, stop means capable of limiting moving objects.

L'existence de cette zone de réception distincte de la zone de retenue permet de garantir un assujettissement fiable des objets par rapport à l'accessoire, pendant une période très longue.The existence of this reception area separate from the retention zone makes it possible to guarantee a reliable subjection of the objects relative to the accessory, for a very long period.

En effet, lorsque l'accessoire subit un grand nombre de cycles de transition entre ses structures austénitique et martensitique, et qu'à chaque fois il lui est imposé, dans sa structure martensitique, une forme différente de celle qu'il présente dans sa structure austénitique, il se produit ce qu'il est convenu d'appeler l'"éducation" de l'accessoire. Ce dernier, même en l'absence de contrainte, est susceptible de se déformer légèrement de manière spontanée lorsque sa structure devient martensitique. Ceci peut avoir pour effet que, par exemple par temps froid, le fil métallique constitutif de la zone de retenue aura tendance à se déformer, ce qui peut engendrer un risque de perte des objets. Indeed, when the accessory undergoes a large number of transition cycles between its austenitic and martensitic structures, and each time it is imposed on it, in its martensitic structure, a form different from that which it presents in its structure austenitic, what happens to be called "accessory education" occurs. The latter, even in the absence of stress, is likely to deform spontaneously slightly when its structure becomes martensitic. This may have the effect that, for example in cold weather, the metal wire constituting the retaining zone will tend to deform, which may cause a risk of loss of the objects.

L'existence de cette zone de réception, qui n'est pas sujette à des déformations successives, permet de s'affranchir d'un tel danger. Les objets solidaires de l'accessoire voient donc leur déplacement limité d'une part par les moyens de butée et d'autre part par l'extrémité de la zone de retenue adjacente à la zone de réception. The existence of this reception area, which is not subject to successive deformations, makes it possible to overcome this danger. Objects secured to the accessory therefore see their movement limited on the one hand by the stop means and on the other hand by the end of the retaining zone adjacent to the receiving zone.

La zone de réception peut être formée par le prolongement du fil métallique constitutif de la zone de retenue. Ce mode de réalisation présente une grande simplicité de fabrication. The receiving zone can be formed by the extension of the metal wire constituting the retaining zone. This embodiment has great simplicity of manufacture.

D'autre part, bien qu'étant réalisée en alliage à mémoire de forme, la zone de réception ne subit pas de modification substantielle de sa forme, lors de la mise en place et de l'extraction des clefs, de sorte qu'elle n'est pas sujette au phénomène d'éducation et n'est pas susceptible de se déformer en l'absence de contrainte extérieure.On the other hand, although being made of shape memory alloy, the reception area does not undergo a substantial modification of its shape, during the placement and extraction of the keys, so that it is not subject to the phenomenon of education and is not likely to be deformed in the absence of external constraints.

Selon une caractéristique supplémentaire de l'invention, les moyens de butée sont formés par une seconde zone de retenue des objets. L'accessoire présente alors une forme symétrique par rapport au milieu de la zone de réception des objets. According to an additional characteristic of the invention, the stop means are formed by a second object retaining zone. The accessory then has a symmetrical shape relative to the middle of the object reception area.

Selon une caractéristique avantageuse de l'invention, les moyens de butée comprennent un élément portant une inscription, par exemple publicitaire. Ce mode de réalisation permet de tirer parti du caractère ludique et original de l'accessoire conforme à l'invention. According to an advantageous characteristic of the invention, the stop means comprise an element bearing an inscription, for example advertising. This embodiment makes it possible to take advantage of the playful and original character of the accessory according to the invention.

Selon une caractéristique supplémentaire de l'invention, la zone de réception comprend au moins une zone de logement préférentiel des objets, vers laquelle ces derniers sont dirigés par gravité, au moins lorsque le dispositif est fixé à un support avec une orientation appropriée. Ceci confère un degré supplémentaire de sécurité à leur retenue par l'accessoire. En effet, l'existence de cette zone de logement préférentiel évite aux objets d'entrer en contact avec la zone de retenue de l'accessoire, en dehors des opérations consistant à les introduire et à les retirer. According to an additional characteristic of the invention, the reception zone comprises at least one zone for preferential accommodation of the objects, towards which the latter are directed by gravity, at least when the device is fixed to a support with an appropriate orientation. This gives an additional degree of security to their retention by the accessory. Indeed, the existence of this preferential housing zone prevents objects from coming into contact with the accessory retaining zone, apart from the operations consisting in introducing and removing them.

Selon une caractéristique de l'invention, la zone de logement préférentiel de l'objet comporte une portion en forme de U, dont les ailes se raccordent aux tronçons de la zone de réception qui leur sont adjacents. According to a characteristic of the invention, the preferential housing zone of the object comprises a U-shaped portion, the wings of which are connected to the sections of the reception zone which are adjacent to them.

Ce mode de réalisation permet aux objets de se diriger par gravité vers l'âme du U. This embodiment allows objects to move by gravity towards the soul of the U.

De façon avantageuse, les ailes convergent l'une vers 1 'autre. Advantageously, the wings converge towards one another.

Selon une autre caractéristique de l'invention, la zone de logement préférentiel de l'objet comporte une portion sensiblement semi-circulaire se raccordant aux tronçons de la zone de réception qui lui sont adjacents. According to another characteristic of the invention, the preferential housing zone of the object comprises a substantially semicircular portion connecting to the sections of the reception zone which are adjacent to it.

Ce mode de réalisation permet aux objets de se diriger par gravité vers la zone médiane de cette portion semi-circulaire. This embodiment allows objects to move by gravity towards the middle zone of this semi-circular portion.

L'invention va être décrite ci-dessous, en référence aux dessins annexés, donnés uniquement à titre d'exemples, et dans lesquels, outre la figure 1 précédemment évoquée
- les figures 2A et 2B sont des vues schématiques en perspective, illustrant un premier mode de réalisation d'un accessoire conforme à l'invention, dans ses structures respectivement austénitique et martensitique
- les figures 3A et 3B sont des vues de côté schématiques, illustrant un second mode de réalisation de l'accessoire conforme à l'invention, dans ses structures respectivement austénitique et martensitique, et
- les figures 4 et 5 sont des vues de côté schématiques en perspective, illustrant respectivement des troisième et quatrième modes de réalisation de l'accessoire conforme à l'invention, dans sa structure austénitique.The invention will be described below, with reference to the accompanying drawings, given only by way of examples, and in which, in addition to FIG. 1 previously mentioned
- Figures 2A and 2B are schematic perspective views, illustrating a first embodiment of an accessory according to the invention, in its respectively austenitic and martensitic structures
FIGS. 3A and 3B are schematic side views, illustrating a second embodiment of the accessory according to the invention, in its respectively austenitic and martensitic structures, and
- Figures 4 and 5 are schematic side views in perspective, respectively illustrating third and fourth embodiments of the accessory according to the invention, in its austenitic structure.

Le porte-clefs représenté aux figures 2A et 2B et désigné dans son ensemble par la référence 2, constitue un premier mode de réalisation de l'accessoire conforme à l'invention. Il comporte un unique fil 4 réalisé en un alliage à mémoire de forme composé de 55,7% en poids de nickel et de 44,3% en poids de titane. La température Af de fin d'apparition d'austénite à partir de l'état martensitique de cet alliage est d'environ 300C, alors que sa température Ms de début d'apparition de martensite à partir de l'état austénitique, est d'environ 100C. The key holder shown in Figures 2A and 2B and designated as a whole by the reference 2, constitutes a first embodiment of the accessory according to the invention. It comprises a single wire 4 made of a shape memory alloy composed of 55.7% by weight of nickel and 44.3% by weight of titanium. The temperature Af at the end of the appearance of austenite from the martensitic state of this alloy is approximately 300C, while its temperature Ms at the start of the appearance of martensite from the austenitic state, is around about 100C.

Le fil 4 est enroulé sur lui-même à partir de la première extrémité 4A, de manière à former un premier anneau 6A. Puis, le fil est cintré selon la direction axiale de l'anneau de manière à former un décrochement 8 au voisinage de sa première extrémité 4A, puis forme un second anneau 6B analogue à celui 6A, disposé à côté de celui-ci. La seconde extrémité du fil 4B est adjacente au décrochement 8. The wire 4 is wound on itself from the first end 4A, so as to form a first ring 6A. Then, the wire is bent in the axial direction of the ring so as to form a recess 8 in the vicinity of its first end 4A, then forms a second ring 6B similar to that 6A, placed next to it. The second end of the wire 4B is adjacent to the recess 8.

La mise en place de clefs 10 sur le porte-clefs 2 conforme à l'invention, est d'une grande simplicité. En effet, il suffit de porter le fil 4 à une température inférieure à sa température Ms de fin d'apparition de martensite. Ce dernier présente alors une structure cristalline sensiblement martensitique et se trouve à même d'être aisément manipulé et déformé, puisqu'il possède une grande malléabilité. The establishment of keys 10 on the key holder 2 according to the invention is very simple. Indeed, it suffices to bring the wire 4 to a temperature below its temperature Ms at the end of the appearance of martensite. The latter then has a substantially martensitic crystal structure and is able to be easily manipulated and deformed, since it has great malleability.

Cette gamme de températures, à savoir proche de 50C dans l'exemple considéré, peut être aisément atteinte en passant le porte-clefs 2 sous l'eau froide, ou en le mettant en contact avec des glaçons. On peut alors écarter les deux anneaux 6A et 6B l'un de l'autre avec une grande facilité, comme le montre la figure 2B, de manière à loger la première extrémité 4A du fil 4 dans l'orifice 12 de la clef, puis à déplacer cette dernière sur la totalité de la longueur du fil. This temperature range, namely close to 50C in the example considered, can be easily reached by passing the key ring 2 under cold water, or by putting it in contact with ice cubes. We can then separate the two rings 6A and 6B from each other with great ease, as shown in Figure 2B, so as to accommodate the first end 4A of the wire 4 in the orifice 12 of the key, then to move the latter over the entire length of the wire.

Lorsque la clef a été rendue solidaire du porte-clefs, il suffit alors de porter le fil 4 qui le constitue, au voisinage de sa température Af de fin d'apparition d'austénite, à savoir 300C dans l'exemple considéré. Pour ce faire, il suffit par exemple de prendre le porte-clefs 2 dans la main ou de le passer sous l'eau chaude. Le fil 4 retrouve alors sa géométrie et sa rigidité originelles. Les anneaux 6A, 6B se rapprochent donc l'un de l'autre et présentent à nouveau une résistance importante à tout effort tendant à les écarter l'un de l'autre. When the key has been made integral with the key holder, it then suffices to wear the wire 4 which constitutes it, in the vicinity of its temperature Af at the end of the appearance of austenite, namely 300C in the example considered. To do this, simply take the key ring 2 in your hand or pass it under hot water. The wire 4 then regains its original geometry and rigidity. The rings 6A, 6B therefore approach one another and once again exhibit significant resistance to any effort tending to separate them from one another.

Pour enlever la clef 10 du porte-clefs 2, il suffit de procéder à une opération analogue à celle précédemment exécutée par sa mise en place, tel un passage du porte-clefs sous l'eau froide. To remove the key 10 from the key holder 2, it suffices to carry out an operation similar to that previously carried out by its installation, such as passing the key holder under cold water.

Les figures 3A et 3B montrent un porte-clefs 102 constituant un second mode de réalisation de l'accessoire conforme à l'invention. Figures 3A and 3B show a key holder 102 constituting a second embodiment of the accessory according to the invention.

Ce porte-clefs est constitué par un unique fil 104 dont la composition et les températures caractéristiques sont analogues à celles du fil 4 décrit en référence aux figures 2A et 2B. Ce fil 104 forme, à partir de sa première extrémité 104A, une première série de dents 106A qui se prolonge, au-delà d'une charnière 108, par une seconde série de dents 106B de forme conjuguée de la forme des dents 106A, de sorte que les dents 106A et 106B sont mutuellement imbriquées. This keychain consists of a single wire 104 whose composition and characteristic temperatures are similar to those of wire 4 described with reference to Figures 2A and 2B. This wire 104 forms, from its first end 104A, a first series of teeth 106A which extends, beyond a hinge 108, by a second series of teeth 106B of shape conjugated with the shape of teeth 106A, so that teeth 106A and 106B are mutually nested.

Le fil 104 se prolonge au-delà des dents 106B par un tronçon 110 sensiblement rectiligne, puis par une zone 112 en forme de U dont les ailes 112B convergent l'une vers l'autre, et se termine par un tronçon rectiligne 114 symétrique du tronçon 110 par rapport à la zone en U 112. L'extrémité de ce tronçon 114, opposée à la zone 112, constitue la seconde extrémité 104B du fil. Les tronçons 110 et 114 sont dans le prolongement l'un de l'autre. The wire 104 is extended beyond the teeth 106B by a substantially straight section 110, then by a U-shaped zone 112 whose wings 112B converge towards one another, and ends in a straight section 114 symmetrical with the section 110 relative to the U-shaped region 112. The end of this segment 114, opposite to the region 112, constitutes the second end 104B of the wire. The sections 110 and 114 are in line with one another.

La zone en U 112 fait saillie à partir des tronçons 110, 114 en direction opposée à la première extrémité 104A du fil. The U-shaped area 112 projects from the sections 110, 114 in the direction opposite to the first end 104A of the wire.

Les ailes 112B de cette zone en U 112 se raccordent à ces tronçons 110, 114 par des arrondis llOA, 114A respectifs.The wings 112B of this U-shaped zone 112 are connected to these sections 110, 114 by respective rounds 110A, 114A.

La seconde extrémité 104B est fixée dans un corps 116, par exemple parallélépipédique, dont les dimensions sont très nettement supérieures à la section transversale du fil 104. Ce corps 116 peut porter une inscription publicitaire ou autre. The second end 104B is fixed in a body 116, for example parallelepiped, the dimensions of which are very much greater than the cross section of the wire 104. This body 116 may bear an advertising or other inscription.

De manière analogue à ce qui a été décrit précédemment, l'introduction d'une clef non représentée sur le porte-clefs 102, consiste tout d'abord à rendre la structure de ce dernier sensiblement martensitique, par exemple par passage sous l'eau froide. Le fil 104 est alors aisément déformable, de sorte que l'on peut agir sur sa première extrémité 104A pour écarter les deux séries de dents 106A, 106B l'une de l'autre. I1 est alors aisé d'engager cette première extrémité 104A dans un orifice de la clef ou dans un élément solidaire de cette dernière. On déplace ensuite la clef le long des dents 106A puis 106B jusqu'à la disposer au niveau de l'âme 112A de la zone en U 112. Puis, par chauffage au voisinage de la température Af de l'alliage constitutif du fil 104, à savoir 400C, on rend au porte-clefs 102 sa structure initiale représentée à la figure 3A ainsi que ses propriétés de rigidité. Similarly to what has been described above, the introduction of a key not shown on the key ring 102, consists first of all in making the structure of the latter substantially martensitic, for example by passing underwater cold. The wire 104 is then easily deformable, so that one can act on its first end 104A to separate the two sets of teeth 106A, 106B from one another. I1 is then easy to engage this first end 104A in an orifice of the key or in an element integral with the latter. The key is then moved along the teeth 106A then 106B until it is placed at the level of the core 112A of the U-shaped zone 112. Then, by heating in the vicinity of the temperature Af of the constituent alloy of the wire 104, namely 400C, the key holder 102 is returned to its initial structure shown in FIG. 3A as well as its stiffness properties.

Les deux séries de dents 106A, 106B qui sont à nouveau imbriquées l'une dans l'autre, constituent alors une zone de retenue des clefs. Le tronçon 110, la zone en U 112 et le tronçon 114 forment une zone de réception de ces clefs. De plus, le corps 116 constitue, du fait de sa dimension importante, une butée apte à limiter le déplacement des clefs. The two sets of teeth 106A, 106B which are again nested one inside the other, then constitute a zone for retaining the keys. The section 110, the U-shaped area 112 and the section 114 form a reception area for these keys. In addition, the body 116 constitutes, because of its large dimension, a stop capable of limiting the movement of the keys.

Enfin, la zone en U 112 forme une zone de logement préférentiel des clefs puisque ces dernières sont dirigées par gravité vers son âme 112A, notamment si le porte-clefs est fixé à un support suivant l'orentation représentée, avec les tronçons 110 et 114 horizontaux et la zone 112 dirigée vers le bas. L'inclinaison des ailes 112B l'une vers l'autre permet d'éviter le déplacement des clefs, depuis l'âme 112A, vers les tronçons rectilignes 110 ou 114.Finally, the U-shaped zone 112 forms a zone for preferential accommodation of the keys since the latter are directed by gravity towards its core 112A, in particular if the key holder is fixed to a support according to the orientation shown, with the sections 110 and 114 horizontal and zone 112 directed downwards. The inclination of the wings 112B towards one another makes it possible to avoid the displacement of the keys, from the core 112A, towards the rectilinear sections 110 or 114.

La présence de cette zone de logement préférentiel 112 permet d'éviter que les clefs n'exercent des efforts répétés sur la zone de retenue, ce qui pourrait, après un grand nombre de cycles de transition entre les structures martensitique et austénitique, causer la perte de ces clefs. The presence of this preferential housing zone 112 makes it possible to prevent the keys from exerting repeated efforts on the retention zone, which could, after a large number of transition cycles between the martensitic and austenitic structures, cause the loss of these keys.

Le porte-clefs 202 représenté à la figure 4 représente un troisième mode de réalisation de l'accessoire conforme à l'invention. Ce porte-clefs 202 est constitué par un unique fil 204 dont la composition et les températures caractéristiques sont analogues celles des fils 4 et 104 précédemment décrits. The key holder 202 shown in FIG. 4 represents a third embodiment of the accessory according to the invention. This keychain 202 is constituted by a single wire 204 whose composition and characteristic temperatures are similar to those of the wires 4 and 104 previously described.

Dans la structure austénitique de l'alliage qui le compose, ce fil 204 forme, à partir de sa première extrémité 204A, deux spires jointives 206 prolongées par un brin 207 radial s'étendant vers le centre des spires. Un tronçon rectiligne 208 dirigé sensiblement selon l'axe des spires s'étend à partir du brin 207. Ce tronçon 208 est prolongé par une portion sensiblement semi-circulaire 210, puis par un tronçon rectiligne 212 supplémentaire. Les extrémités de cette portion 210 se raccordent aux tronçons 208, 212 suivant des angles sensiblement égaux à 900, par l'intermédiaire d'arrondis respectifs 208A, 212A.In the austenitic structure of the alloy which composes it, this wire 204 forms, from its first end 204A, two contiguous turns 206 extended by a strand 207 radial extending towards the center of the turns. A rectilinear section 208 directed substantially along the axis of the turns extends from the strand 207. This section 208 is extended by a substantially semi-circular portion 210, then by an additional rectilinear section 212. The ends of this portion 210 are connected to the sections 208, 212 at angles substantially equal to 900, by means of respective roundings 208A, 212A.

Le tronçon 212 est terminé par un brin radial 213 et deux spires jointives 214 analogues aux éléments 206 et 207. The section 212 is terminated by a radial strand 213 and two contiguous turns 214 similar to the elements 206 and 207.

L'extrémité de ces spires 214 opposée au tronçon 212, constitue la seconde extrémité 204B du fil 204.The end of these turns 214 opposite the section 212 constitutes the second end 204B of the wire 204.

Pour introduire une clef sur le porte-clefs 202, il convient tout d'abord, comme décrit précédemment, d'amener le fil 204 dans sa structure martensitique, puis d'écarter l'une de l'autre les spires 206 ou les spires 214, suivant le côté par lequel on désire engager la clef. On déplace ensuite cette dernière le long du fil 204, jusqu'à la disposer au niveau de la portion 210 semi-circulaire. Puis on chauffe le fil de manière à rendre sa structure à nouveau austénitique, de sorte qu'il recouvre sa forme originelle représentée à la figure 4. To introduce a key on the key ring 202, it is first of all advisable, as described above, to bring the wire 204 into its martensitic structure, then to move the turns 206 or the turns apart from one another 214, according to the side by which one wishes to engage the key. The latter is then moved along the wire 204, until it is placed at the level of the semi-circular portion 210. Then the wire is heated so as to make its structure austenitic again, so that it recovers its original shape shown in FIG. 4.

Les deux paires de spires 206, 214, à nouveau jointives, constituent des zones de retenue des clefs. Les tronçons rectilignes 208, 212 forment, avec la portion semi-circulaire 210, une zone de réception des clefs, et la portion semicirculaire 210 constitue une zone de logement préférentiel des clefs, puisque celles-ci se dirigent sous l'effet de la gravité vers sa partie inférieure 210A. The two pairs of turns 206, 214, again contiguous, constitute key retention zones. The rectilinear sections 208, 212 form, with the semicircular portion 210, a zone for receiving the keys, and the semicircular portion 210 constitutes a zone for preferential accommodation of the keys, since the latter are directed under the effect of gravity towards its lower part 210A.

Le porte-clefs 302 représenté à la figure 5 représente un quatrième mode de réalisation de l'accessoire conforme à l'invention. Ce porte-clefs 302 est constitué par un unique fil 304 dont les caractéristiques sont analogues à celles des fils précédemment décrits. The key holder 302 shown in Figure 5 shows a fourth embodiment of the accessory according to the invention. This key ring 302 consists of a single wire 304 whose characteristics are similar to those of the wires described above.

Dans la structure austénitique de l'alliage qui le compose, ce fil 304 forme, à partie de sa première extrémité 304A, quatre spires jointives 306 prolongées par un tronçon rectiligne 308 se raccordant de façon sensiblement tangentielle à la spire 306A opposée à l'extrémité 304A du fil 304. In the austenitic structure of the alloy which composes it, this wire 304 forms, from its first end 304A, four contiguous turns 306 extended by a rectilinear section 308 connecting substantially tangentially to the turn 306A opposite the end 304A of wire 304.

Ce tronçon 308 est prolongé par une portion sensiblement semi-circulaire 310 dirigée vers le centre des spires, puis par un tronçon rectiligne 312 supplémentaire. L'extrémité de ce dernier, opposée à la portion 210, constitue la seconde extrémité 304B du filtre 304. This section 308 is extended by a substantially semi-circular portion 310 directed towards the center of the turns, then by an additional rectilinear section 312. The end of the latter, opposite the portion 210, constitutes the second end 304B of the filter 304.

Cette seconde extrémité 304B est fixée dans un corps 316 analogue à celui 116 décrit précédemment, disposé sensiblement selon l'axe des spires. This second end 304B is fixed in a body 316 similar to that 116 described above, arranged substantially along the axis of the turns.

Pour introduire une clef sur le porte-clefs 302, il convient, après avois amené le fil 304 dans sa structure martensitique, d'écarter les unes des autres les spires 306, et d'éloigner le corps 316 de la spire 306A de sorte que ce corps n'entrave pas le déplacement de la clef le long de cette spire 306A. On fait ensuite se déplacer la clef le long du fil 304, jusqu'à la disposer au niveau de la portion 310 semiciruclaire. Puis on chauffe le fil de sorte qu'il recouvre sa structure austénitique et sa forme originelle représentée à la figure 5. To introduce a key on the key ring 302, it is advisable, after having brought the wire 304 into its martensitic structure, to move the turns 306 apart from one another, and to move the body 316 away from the turn 306A so that this body does not hinder the movement of the key along this turn 306A. The key is then made to move along the wire 304, until it is placed at the level of the semi-circular portion 310. Then the wire is heated so that it covers its austenitic structure and its original shape shown in FIG. 5.

Les quatre spires 306, à nouveau jointives, constituent alors une zone de retenue des clefs. Les tronçons rectilignes 308, 312 forment, avec la portion semi-circulaire 310, une zone de réception des clefs. Enfin, la portion semi-circulaire 310 constitue une zone de logement préférentielle des clefs, puisque celles-ci s'y dirigent sous l'effet de la gravité. The four turns 306, again contiguous, then constitute a key retention area. The rectilinear sections 308, 312 form, with the semi-circular portion 310, a zone for receiving the keys. Finally, the semi-circular portion 310 constitutes a zone for preferential accommodation of the keys, since the latter are directed there under the effect of gravity.

Le corps 316 est représenté, sur cette figure 5, au voisinage immédiat de la spire extrême 306A, dans la structure austénitique de l'alliage constitutif du porte-clefs. The body 316 is shown, in this FIG. 5, in the immediate vicinity of the extreme turn 306A, in the austenitic structure of the alloy constituting the key holder.

Ce corps 316 peut être également disposé, dans cette structure austénitique, à distance de cette spire 306A. This body 316 can also be arranged, in this austenitic structure, at a distance from this turn 306A.

L'invention n'est pas limitée aux exemples décrits et représentés. Elle trouve son application à tout type de clefs, que ce soit dans le domaine de la serrurerie ou de l'outillage, en particulier aux clefs dites " six-pans " dont la section transversale est hexagonale. The invention is not limited to the examples described and shown. It finds its application to all types of keys, whether in the field of locksmithing or tooling, in particular to so-called "hexagonal" keys whose cross section is hexagonal.

Claims

1. Accessory (2; 102; 202; 302) allowing the retention of objects provided with an orifice, in particular a key holder, of the type comprising at least one zone (6A, 6B; 106A, 106B; 206; 306) of retaining said objects, consisting of a metal wire (4; 104; 204; 304) folded back on itself, along which is intended to thread each object (10) to be retained, characterized in that said metal wire (4 ; 104; 204; 304) is made of a shape memory alloy.

2. Accessory according to claim 1, characterized in that said alloy has a temperature of onset of martensitic appearance (mus) without mechanical stress between OOC and 200C, preferably between 50C and 150C.

3. Accessory according to claim 1 or 2, characterized in that said alloy has a temperature at the end of austenitic appearance (Af) without mechanical stress between 200C and 400C, preferably between 250C and 350C.

4. Accessory according to one of claims 1 to 3, characterized in that said alloy consists of titanium and nickel, and in that it contains between 55.2 and 56% and, preferably, about 55.7 % by weight of nickel.

5. Accessory according to one of claims 1 to 3, characterized in that said alloy consists of titanium, nickel and copper, and in that it contains, by weight, between 45.2 and 51% of nickel , between 44 and 44.8% titanium and between 5 and 10% copper.

6. Accessory according to one of claims 1 to 3, characterized in that said alloy consists of copper, aluminum and nickel, and that it contains, by weight, between 13 and 15% aluminum, between 2 and 5% nickel, the remainder being copper.

7. Accessory according to one of claims 1 to 3, characterized in that said alloy consists of copper, aluminum and zinc, and that it contains, by weight, between 15 and 25% zinc, between 5 and 7% aluminum, the remainder being copper.

8. Accessory according to one of claims 1 to 7, characterized in that the retaining zone comprises, in the austenitic structure of the alloy, at least two sets of teeth (106A, 106B) mutually nested, or at least two contiguous turns (6A, 6B; 206; 306).

9. Accessory according to one of claims 1 to 8, characterized in that it comprises an area (110, 112, 114; 208, 210, 212; 308, 310, 312) for receiving objects, adjacent to said retaining area (106A, 106B; 206; 306), said reception zone comprising, at its end (104B; 212; 312) opposite said retaining zone, stop means (116 214; 316) capable of limiting the movement of said objects .

10. Accessory according to claim 9, characterized in that said receiving zone (110, 112, 114; 208, 210, 212 308, 310, 312) is formed by the extension of said metal wire (104; 204; 304) constituting of the containment zone (106A, 106B; 206; 306).

11. Accessory according to one of claims 9 or 10, characterized in that the stop means comprise an element (116; 316) carrying an inscription, for example advertising.

12. Accessory according to one of claims 9 to 11, characterized in that said reception zone comprises at least one zone (112; 210; 310) for preferential accommodation of objects, towards which the latter are directed by gravity.

13. Accessory according to claim 12, characterized in that said preferential housing zone comprises a U-shaped portion (112), the wings (112B) of which are connected to the sections (110, 114) of the reception zone (110 , 112, 114) which are adjacent to them.

14. Accessory according to claim 13, characterized in that said wings (112B) converge towards one another.

15. Accessory according to claim 12, characterized in that said preferential housing zone comprises a substantially semi-circular portion (210; 310) connecting to the sections (208, 212; 308, 312) of the reception zone (208, 210, 212; 308, 310, 312) which are adjacent to it.