FR2728673A1 - NEW ARTIFICIAL TARGET, PARTICULARLY FOR THE BALL-TRAP GAME, NON-TOXIC TO THE ENVIRONMENT AND METHOD FOR PRODUCING SUCH A TARGET - Google Patents
NEW ARTIFICIAL TARGET, PARTICULARLY FOR THE BALL-TRAP GAME, NON-TOXIC TO THE ENVIRONMENT AND METHOD FOR PRODUCING SUCH A TARGET Download PDFInfo
- Publication number
- FR2728673A1 FR2728673A1 FR9415573A FR9415573A FR2728673A1 FR 2728673 A1 FR2728673 A1 FR 2728673A1 FR 9415573 A FR9415573 A FR 9415573A FR 9415573 A FR9415573 A FR 9415573A FR 2728673 A1 FR2728673 A1 FR 2728673A1
- Authority
- FR
- France
- Prior art keywords
- artificial target
- target according
- binder
- chosen
- target
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
La présente invention concerne une nouvelle cible artificielle, non toxique vis-à-vis de l'environnement, utile notamment pour le jeu de ball-trap, en matériau divisé, aggloméré par un liant, et un procédé de production de telles cibles artificielles. The present invention relates to a new artificial target, non-toxic vis-à-vis the environment, useful in particular for clay pigeon shooting, made of divided material, agglomerated by a binder, and a method for producing such artificial targets.
Le jeu de ball-trap est bien connu des chasseurs, car il constitue un moyen efficace d'entrainement en période de fermeture de la chasse. II est également l'objet de concours très prisé de ces mêmes chasseurs. The game of clay pigeon shooting is well known to hunters because it constitutes an effective means of training during the closed hunting season. It is also the object of highly prized competitions by these same hunters.
Sous son aspect sportif, le jeu de ball-trap requiert l'utilisation de cibles normalisées qui ont la forme d'un disque incurve ou assiette" dont la face convexe est munie de nervures circulaires. In its sporting aspect, the game of clay pigeon shooting requires the use of standardized targets which have the shape of a curved disc or plate "whose convex face is provided with circular ribs.
Traditionnellement ces cibles sont à base de matériaux finement divisés (en anglais ou dans le jargon technique fluer") agglomérés au moyen de liants, propres à assurer une cohésion suffisante de la cible afin de résister à l'énergie communiquée au projectile lors du lancement. Traditionally, these targets are based on finely divided materials (in English or in technical jargon fluer ") agglomerated by means of binders, capable of ensuring sufficient cohesion of the target in order to resist the energy communicated to the projectile during launching.
Les matériaux finement divisés qui conviennent pour la réalisation de tels objets sont en général de nature minérale et proviennent en particulier du concassage ou du broyage de roches massives (matériaux siliceux ou calcaires ...), du sciage de certains matériaux (ardoise, marbre...) ou d'autres matériaux pulvérulents comme le talc ou les farines. Ces matériaux ne doivent pas présenter un caractère toxique ou dangereux xis-å- vis de l'environnement. The finely divided materials which are suitable for the production of such objects are generally mineral in nature and come in particular from the crushing or grinding of massive rocks (siliceous or limestone materials ...), from the sawing of certain materials (slate, marble. ..) or other powdery materials such as talc or flour. These materials must not be toxic or dangerous in the environment.
De tels matériaux sont couramment utilisés et sont largement décrits dans de nombreux brevets relatifs à des cibles notamment pour jeu de ball-trap. On pourra citer par exemple la demande de brevet FR-A-2 685 4( > 5 déposée par la demanderesse. Such materials are commonly used and are widely described in numerous patents relating to targets in particular for clay pigeon shooting. We can cite for example the patent application FR-A-2 685 4 (> 5 filed by the applicant.
De nombreux liants ont été proposés afin d'agglomérer les matériaux divisés mentionnés précédemment. Parmi les liants les plus couramment employés dans l'art antérieur, on peut citer le brai de houille ou de pétrole ainsi que le bitume. Numerous binders have been proposed in order to agglomerate the divided materials mentioned above. Among the binders most commonly used in the prior art, there may be mentioned coal or petroleum pitch as well as bitumen.
Le brevet américain 3 376 O4() décrit ainsi une cible fragmentable constituée de 8 à 25 % en poids de brai de houille ayant un point de fusion compris entre 75 et 177nu, le reste de la cible étant constitué par le matériau divisé. US Patent 3,376,04 () thus describes a fragmentable target consisting of 8 to 25% by weight of coal pitch having a melting point of between 75 and 177 nm, the rest of the target being constituted by the divided material.
Le brevet suédois 76 04126 décrit également des cibles dont le liant est à base d'un brai de pétrole. The Swedish patent 76 04126 also describes targets whose binder is based on a pitch of petroleum.
La demande de brevet EP-A-592 502 mentionne pour la réalisation de cibles fragmentables des liants tels que le brai de houille ou du bitume associé à des particules absorbants l'eau permettant la désintégration finale des cibles par absorption d'humidité. Patent application EP-A-592 502 mentions binders such as coal tar or bitumen associated with water-absorbent particles for the production of fragmentable targets, allowing the final disintegration of the targets by absorption of moisture.
Le brevet canadien 1 260 653 décrit des liants à base de brai de pétrole modifié par un dérivé bis-stéréolamide. Canadian Patent 1,260,653 describes binders based on petroleum pitch modified with a bis-stereolamide derivative.
Toutes les réalisations décrites précédemment présentent l'inconvénient majeur d'utiliser des liants contenant, en plus ou moins grande proportion, des composés polynucléaires aromatiques tels que les benzo-alpha-pyrènes pouvant etre toxiques ou dangereux vis-à-vis de l'environnement. Le brai de houille est le plus chargé en composés polynucléaires mais les brais de pétrole ou le bitume présentent une proportion encore trop élevée de ces polynucléaires aromatiques. All of the embodiments described above have the major drawback of using binders containing, in greater or lesser proportion, aromatic polynuclear compounds such as benzo-alpha-pyrenes which can be toxic or dangerous with regard to the environment. . Coal pitch is the most loaded with polynuclear compounds, but petroleum pitches or bitumen have an excessively high proportion of these aromatic polynuclear materials.
Pour pallier cet inconvénient, plusieurs solutions ont été envisagées préconisant le remplacement des liants précités par d'autres liants plus acceptables du point de vue écologique. To overcome this drawback, several solutions have been envisaged recommending the replacement of the above-mentioned binders by other binders which are more acceptable from an ecological point of view.
Par exemple, la demande de brevet W09 1/12817 décrit une cible dont le matériau divisé est a base de gypse en poudre et le liant est du tpe hydraulique comme la chaux éteinte ou l'argile. For example, patent application WO 09/112817 describes a target whose divided material is based on gypsum powder and the binder is of hydraulic type such as slaked lime or clay.
De même, la demande de brevet EP 487 381 décrit des cibles artificielles dont le liant est constitué par du plâtre. Likewise, patent application EP 487 381 describes artificial targets the binder of which consists of plaster.
On a également proposé d'utiliser en tant que liant du silicate de soude éventuellement en association avec des dextrines. It has also been proposed to use, as binder, sodium silicate, optionally in combination with dextrins.
Ces réalisations sont notamment décrites dans le brevet US S 316 313 et dans la demande de brevet danois 93 00165. These embodiments are described in particular in US patent S 316,313 and in Danish patent application 93 00165.
Ces cibles sont réalisées par mélange préalable du liant du matériau divisé et d'un solvant, notamment l'eau, ce solvant étant ensuite éliminé par traitement thermique. These targets are produced by premixing the binder of the divided material and a solvent, in particular water, this solvent then being removed by heat treatment.
On a également proposé de remplacer les liants issus de brai par des liants organiques. Par exemple, la demande de brevet W092/2()635 préconise l'utilisation de liants dégradables à base de sucre et d'amidon. It has also been proposed to replace the binders from pitch with organic binders. For example, patent application WO92 / 2 () 635 recommends the use of degradable binders based on sugar and starch.
Le brevet US 5 317 037 mentionne comme liants les sucres, notamment les mélanges de dextrose et de fructose, le polydextrose, le maltose, le manitol, la gélatine, le glutène, l'hydroxyméthylcellulose, la gomme arabique et l'amidon. Le liant est renforcé par des fibres choisies parmi le lin, le coton, la viscose, la rayonne ou le bois. US Patent 5,317,037 mentions as binders sugars, in particular mixtures of dextrose and fructose, polydextrose, maltose, manitol, gelatin, glutene, hydroxymethylcellulose, gum arabic and starch. The binder is reinforced with fibers chosen from linen, cotton, viscose, rayon or wood.
Ces liants nécessitent également une étape supplémentaire de traitement thermique pour permettre d'éliminer le solvant, notamment l'eau. These binders also require an additional heat treatment step to make it possible to remove the solvent, in particular water.
On a également proposé dans le brevet US 4 623 150 de remplacer les liants traditionnels par des cires ou des paraffines solubles. La préparation de telles cibles nécessite également l'utilisation d'un solvant qui doit être éliminé par la suite. Parmi les solvants sont cités notamment les solvants organiques comme le xylène, le toluène, les alcools ainsi que l'eau
La demande de brevet japonais 57-178732 décrit une cible composée d'un matériau aggloméré et d'un liant constitué d'une résine thermoplastique notamment la colophane, la colophane estérifiée ou hydrogénée, les résines polyterpéniques, les polystyrènes de bas poids moléculaire, les résines xylènes, les résines coumarone-indène, les résines de pétrole ou les résines de pétrole modifiées ou les cires.Ces résines présentent un poids moléculaire compris entre 200 et 3o < )(). It has also been proposed in US Pat. No. 4,623,150 to replace traditional binders with soluble waxes or paraffins. The preparation of such targets also requires the use of a solvent which must be removed subsequently. Among the solvents are mentioned in particular organic solvents such as xylene, toluene, alcohols as well as water
Japanese patent application 57-178732 describes a target composed of an agglomerated material and a binder consisting of a thermoplastic resin, in particular rosin, rosin esterified or hydrogenated, polyterpene resins, low molecular weight polystyrenes, xylene resins, coumarone-indene resins, petroleum resins or modified petroleum resins or waxes. These resins have a molecular weight of between 200 and 30% ().
De même, la demande japonaise 53-007765 décrit une cible artificielle dont le liant est à base d'une résine de pétrole. Likewise, Japanese application 53-007765 describes an artificial target whose binder is based on a petroleum resin.
Enfin, la demande de brevet FR 2 316 574 décrit un liant à base de résine terpénique dont le poids moléculaire est compris entre 300 et 3000 et le point de ramollissement entre 60 et 200"C. Finally, patent application FR 2 316 574 describes a binder based on terpene resin whose molecular weight is between 300 and 3000 and the softening point between 60 and 200 "C.
Bien que toutes les résines mentionnées précédemment pour remplacer les brais satisfassent aux exigences des Sociétés modernes en ce qui concerne l'environnement, les cibles artificielles obtenues ne présentent pas toutes les caractéristiques de fragilité qui sont nécessaires au déroulement satisfaisant du jeu de ball-trap. En effet, lors de l'impact avec le plomb ou un métal équivalent, les cibles doivent être fragmentées en d'innombrables morceaux et, littéralement, "partir en fumée". Avec les résines citées ci-dessus, la fragmentation est incomplète et la cible est simplement cassée en quelques morceaux ce qui les rend tout à fait inopérantes pour le jeu considéré. Although all of the resins mentioned above to replace pitches meet the requirements of modern societies with regard to the environment, the artificial targets obtained do not have all the brittleness characteristics which are necessary for the satisfactory operation of the game of clay pigeon shooting. Indeed, upon impact with lead or an equivalent metal, the targets must be fragmented into innumerable pieces and, literally, "go up in smoke". With the resins mentioned above, the fragmentation is incomplete and the target is simply broken into a few pieces which makes them completely ineffective for the game in question.
D'ailleurs à la connaissance de la demanderesse, aucune des cibles décrites dans les brevets cités (à part celles dont le liant est à base de brai de houille, de pétrole ou de bitume) n'a été commercialisée. Moreover, to the knowledge of the applicant, none of the targets described in the cited patents (apart from those whose binder is based on coal tar, petroleum or bitumen) have been marketed.
L'objet de la présente invention est de proposer des cibles qui répondent simultanément à plusieurs critères tels qu'ils peuvent être définis ci-dessous:
- elles doivent respecter l'environnement, c'est-à-dire qu'elles doivent etre exemptes de composés polyaromatiques,
- elles doivent être suffisamment solides lors du lancement pour ne pas être fissurées à cette occasion,
- lors de l'impact elles doivent être fragmentées en d'innombrables morceaux et donc présenter un caractère de fragilité suffisant,
- en outre, ces cibles étant fabriquées à des cadences très élevées pour un coût nécessairement très modique, elles doivent pouvoir être produites selon le procédé traditionnel sans étape supplémentaire de séchage et sans faire intervenir de solvant.En outre, la présence d'un solvant à moins qu'il ne s'agisse d'eau, cause d'autres problèmes de pollution étant donné que ce solvant doit être ensuite récupéré, traité et éventuellement recyclé.The object of the present invention is to propose targets which simultaneously meet several criteria as they can be defined below:
- they must respect the environment, that is to say they must be free of polyaromatic compounds,
- they must be strong enough at launch not to be cracked on this occasion,
- upon impact they must be fragmented into innumerable pieces and therefore have a sufficient fragility character,
- In addition, these targets being manufactured at very high rates for a necessarily very low cost, they must be able to be produced according to the traditional method without additional drying step and without involving solvent. In addition, the presence of a solvent unless it is water, causes other pollution problems since this solvent must then be recovered, treated and possibly recycled.
Les buts définis ci-dessus sont atteints grâce aux cibles selon l'invention. The goals defined above are achieved thanks to the targets according to the invention.
La cible artificielle selon l'invention est caractérisée en ce que le liant permettant d'agglomérer le matériau divisé comprend une matière hydrocarbonée aliphatique dont le point de fusion est compris entre 5() et 150"C et un additif, améliorant la fragilité de la cible lors de l'impact, comprenant une résine thermoplastique. The artificial target according to the invention is characterized in that the binder for agglomerating the divided material comprises an aliphatic hydrocarbon material whose melting point is between 5 () and 150 "C and an additive, improving the brittleness of the target upon impact, comprising a thermoplastic resin.
Parmi les matériaux finement divisés qui peuvent convenir dans le cadre de la présente invention, on utilisera avantageusement les charges minérales provenant du concassage ou du broyage de roches massives (charges siliceuses ou calcaire, bauxite, alumine ...) ou provenant du sciage de certains matériaux tels que l'ardoise ou le marbre. On peut également utiliser d'autres matériaux pulvérulents susceptibles d'être agglomérés (talc, cendres volantes de centrales thermiques ou de cimenterie ...). Among the finely divided materials which may be suitable in the context of the present invention, use will advantageously be made of mineral fillers originating from the crushing or grinding of massive rocks (siliceous or limestone fillers, bauxite, alumina, etc.) or originating from the sawing of certain materials such as slate or marble. It is also possible to use other pulverulent materials capable of being agglomerated (talc, fly ash from thermal power plants or from cement works, etc.).
On peut également utiliser des matériaux organiques comme la cellulose, la farine ou la sciure de bois. You can also use organic materials such as cellulose, flour or sawdust.
Parmi les charges de préférence utilisées dans le cadre de la présente invention, on mentionnera tout particulièrement les charges calcaires. Among the fillers preferably used in the context of the present invention, particular mention will be made of limestone fillers.
La proportion de matériaux divisés et de liants peut varier selon celle communément en usage dans l'art considéré. The proportion of divided materials and binders may vary according to that commonly used in the art considered.
En général, les cibles selon l'invention comprendront en pourcentage en poids de 5 à 30 % de liants et 70 à 95 % de matériaux divisés. In general, the targets according to the invention will comprise, in percentage by weight, from 5 to 30% of binders and 70 to 95% of divided materials.
Selon une première variante préférée, la cible artificielle est caractérisée en ce que ledit liant comprend en partie en poids:
- matière hydrocarbonée 80 à 99
- additif 1 à 20. According to a first preferred variant, the artificial target is characterized in that said binder partly comprises by weight:
- hydrocarbon material 80 to 99
- additive 1 to 20.
De préférence ledit liant comprend en partie en poids:
- matière hydrocarbonée 88 à 98
- additif2à12. Preferably, said binder partly comprises by weight:
- hydrocarbon material 88 to 98
- additive 2 to 12.
Par l'expression matière hydrocarbonée aliphatique", on désignera celle qui ne contient sensiblement que des atomes de carbone et d'hydrogène et qui provient, notamment, du pétrole. Il s'agit donc de matière essentiellement hydrophobe et non aromatique. The expression “aliphatic hydrocarbon material” denotes that which contains substantially only carbon and hydrogen atoms and which comes, in particular, from petroleum. It is therefore essentially a hydrophobic and non-aromatic material.
On a déjà indiqué que les paraffines ou les cires employées seules conduisaient à des cibles présentant un degré de fragilité inférieur aux cibles traditionnelles. De façon surprenante, la demanderesse a trouvé qu'en mélangeant les matières hydrocarbonées aliphatiques mentionnées ci-dessus avec une faible proportion de résine thermoplastique, il était possible d'obtenir des cibles similaires à celles de l'art antérieur relatif aux liants a base de brai ou de bitume, sans avoir les inconvénients de tosicité liés à ces derniers. It has already been indicated that paraffins or waxes used alone lead to targets having a lower degree of brittleness than traditional targets. Surprisingly, the applicant has found that by mixing the aliphatic hydrocarbon materials mentioned above with a small proportion of thermoplastic resin, it was possible to obtain targets similar to those of the prior art relating to binders based on pitch or bitumen, without having the tosicity drawbacks linked to these.
En ce qui concerne les additifs, ceux < i sont de préférence choisis parmi les résines thermoplastiques de poids moléculaire compris entre Z(X) et 3000 et un point de ramollissement compris entre 5() et 150oC. As regards the additives, those <i are preferably chosen from thermoplastic resins of molecular weight between Z (X) and 3000 and a softening point between 5 () and 150oC.
Avantageusement la résine est choisie parmi la colophane et ses dérivés estérifiés ou hydrogénés. Advantageously, the resin is chosen from rosin and its esterified or hydrogenated derivatives.
Selon une autre variante préférée, la résine est choisie parmi les résines de pétrole ou les résines de pétrole modifiées. According to another preferred variant, the resin is chosen from petroleum resins or modified petroleum resins.
L'invention concerne également un procédé de production de cibles artificielles telles que décrites précédemment caractérisé en ce que
a) on mélange le matériau divisé et les constituants du liant à une température appropriée,
b) on moule sous pression la quantité appropriée du mélange obtenu en a),
c) on récupère la cible artificielle.The invention also relates to a method for producing artificial targets as described above, characterized in that
a) the divided material and the constituents of the binder are mixed at an appropriate temperature,
b) the appropriate quantity of the mixture obtained in a) is pressure molded,
c) the artificial target is recovered.
La fabrication des cibles se fait de façon traditionnelle en mélangeant à chaud dans un malaxeur, en continu, 5 à 30 % de liant, notamment de paraffine ou de cire additivées de colophane ou de résines de pétrole et 70 à 95 % d'un matériau divisé, notamment une charge calcaire. Le mélange est effectué à une température égale ou supérieure au point de fusion de la matière hydrocarbonée puis pompé et injecté dans les moules d'une presse afin de former les cibles. The manufacturing of the targets is done in the traditional way by hot mixing in a kneader, continuously, 5 to 30% of binder, in particular paraffin or wax additive with rosin or petroleum resins and 70 to 95% of a material divided, in particular a calcareous charge. The mixing is carried out at a temperature equal to or higher than the melting point of the hydrocarbon material, then pumped and injected into the molds of a press in order to form the targets.
Les cibles sont refroidies puis démoulées, elles peuvent étre utilisées brutes ou peintes avant leur utilisation. The targets are cooled and then removed from the mold, they can be used raw or painted before use.
A titre d'exemples non limitatifs, I'invention est maintenant illustrée par les deux exemples suivants:
Exemple 1
Dans un malaxeur industriel on mélange à lOOnC:
- 900 kg d'un filler calcaire de granulométrie 0 à 120,
- 100 kg d'un mélange constitué de 95 kg de paraffme de point de fusion 63"C et 5 kg de colophane.By way of nonlimiting examples, the invention is now illustrated by the following two examples:
Example 1
In an industrial mixer we mix with lOOnC:
- 900 kg of a limestone filler with grain sizes 0 to 120,
- 100 kg of a mixture consisting of 95 kg of paraffin with melting point 63 "C and 5 kg of rosin.
Après malaxage, le mélange est envoyé dans une presse à mouler et les cibles fabriquées sont testées avec succès en résistance au lancement et au tir aux armes de chasse. After mixing, the mixture is sent to a molding press and the manufactured targets are successfully tested for launch and firing resistance to hunting weapons.
Exemple 2
Les 5 kg de colophane sont remplacés par une résine de pétrole fournie par la société E?cuon sous la marque Escorez. Le reste du mode opératoire est identique à l'exemple 1.Example 2
The 5 kg of rosin are replaced by a petroleum resin supplied by the company E? Cuon under the brand Escorez. The rest of the procedure is identical to Example 1.
Les cibles fabriquées et testées se sont comportées comme les cibles traditionnelles. The targets manufactured and tested behaved like traditional targets.
Bien entendu, I'invention n'est pas limitée aux formes de réalisation décrites précédemment mais s 'étend au contraire à tous les équivalents permettant d'atteindre le même résultat. Of course, the invention is not limited to the embodiments described above but, on the contrary, extends to all equivalents making it possible to achieve the same result.
Claims (7)