FI58366C - KOPPAR-TENNLEGERING FOER PAPPERSMASKINSVIROR - Google Patents
KOPPAR-TENNLEGERING FOER PAPPERSMASKINSVIROR Download PDFInfo
- Publication number
- FI58366C FI58366C FI760456A FI760456A FI58366C FI 58366 C FI58366 C FI 58366C FI 760456 A FI760456 A FI 760456A FI 760456 A FI760456 A FI 760456A FI 58366 C FI58366 C FI 58366C
- Authority
- FI
- Finland
- Prior art keywords
- copper
- wires
- alloy
- paper machine
- tin
- Prior art date
Description
:1 RSäPl M mjKUULUTUSIULKAISU r q , . ": 1 RSäPl M mjAdvertisement RUL, r q,. "
l J 1 ' UTLÄGGNl NGSSKRIFT 3 O 5 O Ol J 1 'UTLÄGGNl NGSSKRIFT 3 O 5 O O
^Γ>πδ C (45) Patentti myönnetty IS 01 1081^ Γ> πδ C (45) Patent granted IS 01 1081
Patent aeddelat (51) Kv.ik.Wft3 D 21 F 1/10. C 22 C 9/02 SUOMI —FINLAND (21) PtWntUhukumw-F^enttn.eknlng 76OU56 (22) Hakmilipllvl—Anaöknlngtdai 23*02.76 (23) Alkupllvt—GHtlgh«t*dag 23.02.76 , (41) Tulkit JulkMcsI — Bllvlt offantllg 08.09.76 httnttl- |. r.kl«.ril»mtw «« .«*«1*^p™.-Patent aeddelat (51) Kv.ik.Wft3 D 21 F 1/10. C 22 C 9/02 FINLAND —FINLAND (21) PtWntUhukumw-F ^ enttn.eknlng 76OU56 (22) Hakmilipllvl — Anaöknlngtdai 23 * 02.76 (23) Alkupllvt — GHtlgh «t * dag 23.02.76, (41) Tulkit B offantllg 08.09.76 httnttl- |. r.kl «.ril» mtw ««. «*« 1 * ^ p ™ .-
Patent- och regittentyralaan v 7 amMcu utitgd eeh utUkrHtm pubiicmd 30.09.80 (32)(33)(31) Pyydttty «tuolle»»-Bugiri priority 07.03.75Patent- och regittentyralaan v 7 amMcu utitgd eeh utUkrHtm pubiicmd 30.09.80 (32) (33) (31) Pyydttty «tuolle» »- Bugiri priority 07.03.75
Saksan Liittotasavalta-Förbundsrepubliken Tyskland(DE) P 2509892.k (71) Berkenhoff & Co., Heuchelheim 2, Saksan Liittotasavalta-Förbunds-republiken Tyskland(UE) (72) Klaus Tauber, Biebertal, Erich Donnner, Heuchelheim, Saksan Liitto-tasavalta-Förbundsrepubliken Tyskland(DE) (7*0 Oy Kolster Ab (5M Kupari-tinaseos paperikoneiden viiroja varten - Koppar-tennlegering för pappersmaskinsvirorFederal Republic of Germany-Förbundsrepubliken Tyskland (DE) P 2509892.k (71) Berkenhoff & Co., Heuchelheim 2, Federal Republic of Germany-Förbunds-republiken Tyskland (UE) (72) Klaus Tauber, Biebertal, Erich Donnner, Heuchelheim, Federal Republic of Germany -Förbundsrepubliken Tyskland (DE) (7 * 0 Oy Kolster Ab (5M Copper-tin alloy for paper machine wires - Koppar-tennlegering för pappersmaskinsviror
Keksintö kohdistuu kupari-tinaseokseen varsinkin paperikoneiden viiroissa käytettävien lankojen valmistamiseksi.The invention relates to a copper-tin alloy, in particular for the manufacture of yarns for use in paper machine wires.
Kokemus on osoittanuty että paperikoneiden viiroissa käytetyn loimi-langan täytyy täyttää useita vaatimuksia. Siten täytyy langan lujuuden paperikoneiden viirojen suuren nopeuden vuoksi olla riittävän, langan täytyy kestää kitkaa, hankausta ja korrosiota sekä hyvän vaihtotaivutuslujuuden rinnalla olla riittävän hyvin venyvä. Koska paperikoneiden viirat täytyy valmistaa päättömiksi, täytyy langan lisäksi olla hyvin hitsattavissa tai juotettavissa.Experience has shown that the warp yarn used in paper machine wires must meet several requirements. Thus, due to the high speed of the wires of paper machines, the strength of the wire must be sufficient, the wire must be able to withstand friction, abrasion and corrosion, and, in addition to good alternating bending strength, must be sufficiently stretchy. Because paper machine wires must be made endless, they must be highly weldable or solderable in addition to wire.
Tunnetaan kupari-tina-seosten käyttö paperikoneiden viiroissa, jolloin seokset sisältävät 4 - 9 tinaa, 0,4 prosenttiin asti fosforia lopun ollessa kuparia. Näitä metalliseoksia voidaan käsitellä hyvin ja paperikoneiden viiroissa käytetään pääasiassa niitä. Niiden kestoaika on tavanomaisissa käyttöolosuhteissa, erikoisesti suurten kiertonopeuksien vuoksi paperinvalmistuksessa vain muutamia päiviä. Viira täytyy tällöin korvata '1 58366 uudella, inistä viiran korkean hinnan lisäksi aiheutuu kustannuksia lisääviä seisonta-aikoja paperikoneille. Tällaisten paperikoneiden viirojen käyttöaikaa on yritetty pidentää siten, että kupari-tinaseokseen lisätään mangaania joko yksinään tai yhdessä raudan kanssa. Tällöin on voitu tosin parantaa paperikoneiden viirojen kulutuskestävyyttä, mutta samanaikaisesti alenee lankojen venyminen, joka on ratkaisevaa hyvälle kudottuvuudelle ja ennenkaikkea f vaiht ot ai vut us lujuus. Seurauksena oli, että lopullisena vaikutuksena ei paperi- ....... i koneiden viirojen käyttöikää voitu mainittavasti pidentää. Sama koskee Cu-Sn- seoksia, jotka lisäseostusaineosina sisältävät vielä arseenia ja ceriumia.It is known to use copper-tin alloys in paper machine wires, where the alloys contain 4 to 9 tin, up to 0.4% phosphorus with the remainder being copper. These alloys can be handled well and are mainly used in paper machine wires. They last only a few days under normal operating conditions, especially due to the high rotational speeds in papermaking. The wire will then have to be replaced with a new 1, 58366, in addition to the high cost of the wire, there will be costly downtime for paper machines. Attempts have been made to extend the service life of the wires of such paper machines by adding manganese to the copper-tin alloy, either alone or in combination with iron. In this case, it has been possible to improve the wear resistance of the wires of paper machines, but at the same time the elongation of the yarns is reduced, which is crucial for good weaving and, above all, the strength of the interchangeable materials. As a result, the final effect was that the service life of paper machines could not be significantly extended. The same applies to Cu-Sn mixtures which also contain arsenic and cerium as additional doping ingredients.
Keksinnön tehtävänä on aikaansaada alussa mainitun laatuinen kupari-tina seos paperikoneiden viiroja varten, jonka käsittely on yksinkertaista ja jonka avulla voidaan valmistaa paperikoneiden viiroja, joiden käyttöikä tunnettuja kupari-tinaseoksia oleviin viiroihin nähden on huomattavasti pidentynyt.The object of the invention is to provide a copper-tin alloy of the kind mentioned at the beginning for paper machine wires, which is simple to handle and by means of which paper machine wires can be produced which have a considerably longer service life compared to known copper-tin alloy wires.
Tämä tehtävä ratkaistaan keksinnön mukaan kupari-tinaseoksen avulla, jolle on tunnusomaista se, että seos sisältää ä - 9 % tinaa, 0,U - 0,8 % fosforia, kobolttia ja nikkeliä yhteensä 0,8 - U % lopun ollessa kuparia, että nikkeliä ja kobolttia on seostettu kumpaakin vähintään 0,U % ja että kaikkien epäpuhtauksien summa ei ylitä arvoa 0,2 %. Keksinnön mukaisesta metalliseoksesta voidaan paperikoneen viiroja varten valmistaa lankoja, jotka riittävän hyvän kovuuden, venymisen, hankaus- ja korrosiokestävyyden lisäksi omaavat hyvän vaihtotaivutuslujuuden. Syynä keksinnön mukaisesta metalliseoksesta valmistetun paperikoneen viiran hyvään hankauskestävyyteen ja pitkään käyttöikään on nähtävissä edelläeeitettyjen ominaisuuksien keskinäisestä yhteensopivuudesta.According to the invention, this object is solved by means of a copper-tin alloy, which is characterized in that the alloy contains --9% tin, 0.1 U -0.8% phosphorus, cobalt and nickel in total 0.8- U%, the remainder being copper and nickel. and the cobalt is each doped at least 0, U% and that the sum of all impurities does not exceed 0.2%. The alloy according to the invention can be used to produce wires for paper machine wires which, in addition to sufficiently good hardness, elongation, abrasion and corrosion resistance, have good alternating bending strength. The reason for the good abrasion resistance and long service life of the wire of a paper machine made of an alloy according to the invention can be seen from the mutual compatibility of the above-mentioned properties.
Kokeet ovat osoittaneet, että koboltin ja nikkelin samanaikainen läsnäolo esitettyinä määrinä ja verrattain suuri fosforipitoisuus aiheuttavat tästä metalliseoksesta valmistetun paperikoneen viiran huomattavan pitkän käyttöiän.Experiments have shown that the simultaneous presence of cobalt and nickel in the amounts shown and the relatively high phosphorus content result in a remarkably long service life of the wire of a paper machine made from this alloy.
Tämä kasvu alkaa annetuilla nikkeli- ja kobolttipitoisuuksilla 0,U prosenttista fosforia, saavuttaa maksiminsa ja alkaa, alentua 0,6 prosentin fosforipitoisuudesta alkaen hitaasti. Fosforipitoisuuden ollessa suuremman kuin 0,8 % ei paperikoneiden viiroissa käytettyihin tunnettuihin metalliseoksiin verrattuna voitu enään havaita käyttöiän pidentymistä.This increase begins with given nickel and cobalt concentrations of 0.0 U% phosphorus, reaches its maximum, and begins to decrease slowly from a phosphorus content of 0.6 percent. With a phosphorus content of more than 0.8%, no longer an increase in service life could be observed compared to the known alloys used in paper machine wires.
Paperikoneen viiralle valmistettuna metalliseoksesta, joka sisälsi 6,5 % tinaa, 0,55 % fosforia, 0,6 % kobolttia, 0,55 % nikkeliä lopun ollessa kuparia, '' suoritetuissa kokeissa saavutettiin huomattavasti kaksinkertaista pitempi käyttöikä verrattuna tunnetuista Cu-Sn-6-8-metalliseoksista valmistettuihin viiroihin.Made on a paper machine wire made of an alloy containing 6.5% tin, 0.55% phosphorus, 0.6% cobalt, 0.55% nickel with the remainder being copper, the experiments performed significantly exceeded twice the service life of the known Cu-Sn-6 For wires made of -8 alloys.
Hitaasti toimivissa paperikoneissa havaittiin kokeissa pitempi kuin kolminkertainen käyttöikä tavanomaisiin viiroihin verrattuina.Slowly operating paper machines were found to have longer than three times the service life of conventional fabrics.
Claims (2)