FI20095872A - Steel sheet with low welding fracture tendency and yield strength of 800 MPa and method for its manufacture - Google Patents

Steel sheet with low welding fracture tendency and yield strength of 800 MPa and method for its manufacture Download PDF

Info

Publication number
FI20095872A
FI20095872A FI20095872A FI20095872A FI20095872A FI 20095872 A FI20095872 A FI 20095872A FI 20095872 A FI20095872 A FI 20095872A FI 20095872 A FI20095872 A FI 20095872A FI 20095872 A FI20095872 A FI 20095872A
Authority
FI
Finland
Prior art keywords
mpa
manufacture
steel sheet
yield strength
low welding
Prior art date
Application number
FI20095872A
Other languages
Finnish (fi)
Swedish (sv)
Other versions
FI127175B (en
Inventor
Liandeng Yao
Xiaoting Zhao
Sixin Zhao
Original Assignee
Baoshan Iron & Steel
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baoshan Iron & Steel filed Critical Baoshan Iron & Steel
Publication of FI20095872A publication Critical patent/FI20095872A/en
Application granted granted Critical
Publication of FI127175B publication Critical patent/FI127175B/en

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21B—ROLLING OF METAL
    • B21B1/00—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations
    • B21B1/22—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length
    • B21B1/24—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length in a continuous or semi-continuous process
    • B21B1/26—Metal-rolling methods or mills for making semi-finished products of solid or profiled cross-section; Sequence of operations in milling trains; Layout of rolling-mill plant, e.g. grouping of stands; Succession of passes or of sectional pass alternations for rolling plates, strips, bands or sheets of indefinite length in a continuous or semi-continuous process by hot-rolling, e.g. Steckel hot mill
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Steel (AREA)
FI20095872A 2007-10-26 2009-08-25 Steel sheet, whose tendency to weld failure is small and tensile strength is 800 MPa, as well as process for manufacturing thereof FI127175B (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN2007100941772A CN101418416B (en) 2007-10-26 2007-10-26 Low welding crack sensitivity steel plate with yield strength of 800MPa grade and method for producing the same
PCT/CN2008/072807 WO2009056055A1 (en) 2007-10-26 2008-10-24 Steel plate with yield strength of 800mpa grade and low weld cracking sensitivity, and manufacture method thereof

Publications (2)

Publication Number Publication Date
FI20095872A true FI20095872A (en) 2009-08-25
FI127175B FI127175B (en) 2017-12-29

Family

ID=40590559

Family Applications (1)

Application Number Title Priority Date Filing Date
FI20095872A FI127175B (en) 2007-10-26 2009-08-25 Steel sheet, whose tendency to weld failure is small and tensile strength is 800 MPa, as well as process for manufacturing thereof

Country Status (11)

Country Link
US (1) US8702876B2 (en)
EP (1) EP2218801B1 (en)
JP (1) JP5233020B2 (en)
KR (1) KR101563929B1 (en)
CN (1) CN101418416B (en)
DE (1) DE112008000562B4 (en)
ES (1) ES2424009T3 (en)
FI (1) FI127175B (en)
SE (1) SE535302C2 (en)
WO (1) WO2009056055A1 (en)
ZA (2) ZA200901450B (en)

Families Citing this family (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102162061B (en) * 2010-02-23 2013-09-04 宝山钢铁股份有限公司 Low-carbon bainite thick steel plate with high strength and toughness and manufacturing method thereof
CN102260823B (en) * 2010-05-27 2013-04-24 宝山钢铁股份有限公司 Economic high-strength steel plate with yield strength of 690MPa, and manufacture method thereof
CN102337482B (en) * 2010-07-23 2013-11-20 宝山钢铁股份有限公司 Bainite high strength and toughness steel plate with yield strength of 900 MPa and manufacture method thereof
CN102051522A (en) * 2010-12-21 2011-05-11 南阳汉冶特钢有限公司 Steel plate made of bainite structure high-strength toughness structural steel Q550D(E) and production method thereof
CN102560045B (en) * 2010-12-22 2014-10-01 中国科学院金属研究所 Block nano structure low-carbon steel and manufacturing method thereof
RU2458751C1 (en) * 2011-02-25 2012-08-20 Открытое акционерное общество "Магнитогорский металлургический комбинат" Method of producing low-alloy k52-k60-grade pipe steel
RU2458754C1 (en) * 2011-03-17 2012-08-20 Открытое акционерное общество "Магнитогорский металлургический комбинат" Method of producing low-alloy x70-grade pipe steel
CN102839319B (en) * 2011-06-24 2014-12-10 宝钢特钢有限公司 1,100 MPa-grade high strength steel and production method thereof
JP2013227624A (en) * 2012-04-25 2013-11-07 Jfe Steel Corp Method of manufacturing high strength cold rolled steel sheet excellent in workability
KR101579415B1 (en) 2012-12-28 2015-12-21 신닛테츠스미킨 카부시키카이샤 670870n/ 780940n/ steel sheet having yield strength of 670-870n/ and tensile strength of 780-940n/
CN103060690A (en) * 2013-01-22 2013-04-24 宝山钢铁股份有限公司 High-strength steel plate and manufacturing method thereof
CN103233179B (en) * 2013-05-13 2015-08-19 湖南华菱湘潭钢铁有限公司 A kind of production method of easy-formation high-strength medium plate
CN103305752B (en) * 2013-06-20 2015-04-15 舞阳钢铁有限责任公司 Large-thickness high-performance SA302GrC steel plate and production method thereof
CN103695773B (en) * 2013-12-11 2015-10-28 武汉钢铁(集团)公司 Yield strength is 690MPa level fire resistant and weather resistant anti-shock construction(al)steel and production method thereof
CN103695772B (en) * 2013-12-11 2015-12-30 武汉钢铁(集团)公司 Yield strength is 550MPa level fire resistant and weather resistant anti-shock construction(al)steel and production method thereof
CN103898406B (en) * 2014-03-25 2016-08-24 宝山钢铁股份有限公司 A kind of yield strength 890MPa level low welding crack sensitivity steel plate and manufacture method thereof
CN103952643B (en) * 2014-05-13 2017-01-18 莱芜钢铁集团有限公司 Low-yield ratio steel plate with yield strength of 690MPa and preparation method of steel plate
CN104152818A (en) * 2014-08-12 2014-11-19 昆明理工大学 Duplex stainless steel and preparation method thereof
CN106319343B (en) * 2016-10-10 2021-08-17 宝钢德盛不锈钢有限公司 Low-cost high-strength stainless steel and welded pipe manufacturing method thereof
CN108103398B (en) * 2017-12-07 2021-06-25 新疆八一钢铁股份有限公司 Production method of 460Mpa high-strength high-weather-resistance steel plate
CN108315666A (en) * 2018-02-12 2018-07-24 舞阳钢铁有限责任公司 Low-welding crack-sensitive Q500GJE steel plates and its production method
CN110195193B (en) * 2018-02-27 2021-03-12 宝山钢铁股份有限公司 800 MPa-grade quenched and tempered steel plate with low cost, high toughness and excellent weldability and manufacturing method thereof
CN110004358B (en) * 2019-03-29 2021-05-25 山东钢铁集团日照有限公司 Marine steel plate with low Pcm value, large thickness and easy welding and production method thereof
CN110117754B (en) * 2019-05-20 2020-10-02 北京科技大学 Multi-medium corrosion resistant steel with yield strength of 500MPa and preparation method thereof
CN115537681B (en) * 2021-06-30 2023-10-17 宝山钢铁股份有限公司 High-toughness low-yield ratio low-longitudinal-transverse-strength anisotropic 500 MPa-grade steel plate and manufacturing method thereof
CN114395691A (en) * 2021-12-16 2022-04-26 南阳汉冶特钢有限公司 Production method of low-welding-crack-sensitivity crack arrest steel SX780CF for hydroelectric engineering
CN114480961B (en) * 2021-12-24 2023-03-10 安阳钢铁集团有限责任公司 620MPa grade high-strength steel with cold crack sensitivity coefficient less than or equal to 0.19 and production method thereof
CN114657458B (en) * 2022-02-18 2022-10-25 山东钢铁集团日照有限公司 Crude oil storage tank steel plate for large-thickness high-strength high-toughness high-heat input welding and preparation method thereof
CN115351094A (en) * 2022-06-28 2022-11-18 武安市裕华钢铁有限公司 Production method of carbon structural steel for pipe making with low welding crack sensitivity

Family Cites Families (33)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS54132421A (en) 1978-04-05 1979-10-15 Nippon Steel Corp Manufacture of high toughness bainite high tensile steel plate with superior weldability
JPS5696054A (en) 1979-12-28 1981-08-03 Kobe Steel Ltd Hot rolled steel plate for flash butt welding and cold working
JPS5719321A (en) 1980-07-08 1982-02-01 Nippon Steel Corp Improvement for sulfide stress corrosion cracking of low alloy steel
JPS5877528A (en) * 1981-10-31 1983-05-10 Nippon Steel Corp Manufacture of high tensile steel with superior toughness at low temperature
JPS61147812A (en) 1984-12-19 1986-07-05 Nippon Kokan Kk <Nkk> Production of high strength steel superior in delayed breaking characteristic
JPS6210240A (en) 1985-07-08 1987-01-19 Sumitomo Metal Ind Ltd Steel for seamless drawn oil well pipe excellent in corrosion resistance and collapsing strength
JPS62103347A (en) 1985-10-30 1987-05-13 Nippon Steel Corp High toughness and high tension thick steel of more than 25mm thickness and its manufacture
JP3208495B2 (en) * 1992-01-28 2001-09-10 新日本製鐵株式会社 Manufacturing method of 80kgf / mm2 class high strength steel with excellent weldability
JPH07305113A (en) * 1994-05-11 1995-11-21 Kobe Steel Ltd Production of low yield ratio thick fire resistant steel for building excellent in weldability
US5545270A (en) * 1994-12-06 1996-08-13 Exxon Research And Engineering Company Method of producing high strength dual phase steel plate with superior toughness and weldability
JPH08232017A (en) * 1994-12-28 1996-09-10 Nkk Corp Production of heat treated type 60kgf/mm2 class steel excellent in weldability and acoustic anisotropy
JPH08209237A (en) * 1995-01-31 1996-08-13 Nkk Corp Production of high tensile strength steel excellent in weldability and acoustic anisotropy
JPH10298706A (en) * 1996-06-21 1998-11-10 Nkk Corp High tensile strength steel excellent in high heat input weldability and weld crack sensitivity and its production
JPH10237583A (en) 1997-02-27 1998-09-08 Sumitomo Metal Ind Ltd High tensile strength steel and its production
US6264760B1 (en) 1997-07-28 2001-07-24 Exxonmobil Upstream Research Company Ultra-high strength, weldable steels with excellent ultra-low temperature toughness
CN1088474C (en) * 1997-07-28 2002-07-31 埃克森美孚上游研究公司 Method for producing ultra-high strength, weldable steels with superior toughness
ES2216301T3 (en) 1997-07-28 2004-10-16 Exxonmobil Upstream Research Company STEELS CONTAINING BORO, SOLDABLE, ULTRA-HIGH RESISTANCE, WITH SUPERIOR TENACITY.
JP2000192140A (en) * 1998-10-16 2000-07-11 Nkk Corp Production of low yield ratio high tensile strength steel excellent in weld cracking sensitivity
JP3972553B2 (en) * 1999-02-15 2007-09-05 住友金属工業株式会社 Tapered steel sheet and manufacturing method thereof
JP4071906B2 (en) 1999-11-24 2008-04-02 新日本製鐵株式会社 Manufacturing method of steel pipe for high tension line pipe with excellent low temperature toughness
JP3770106B2 (en) * 2001-06-20 2006-04-26 住友金属工業株式会社 High strength steel and its manufacturing method
JP2003147477A (en) * 2001-11-07 2003-05-21 Kawasaki Steel Corp OVER 700 MPa CLASS NON-HEATTREATED LOW YIELD RATIO THICK STEEL PLATE, AND PRODUCTION METHOD THEREFOR
CN1210431C (en) * 2002-05-22 2005-07-13 武汉钢铁(集团)公司 Steel series with high linear energy and low weld crack sensitivity and its preparing process
US20040118489A1 (en) 2002-12-18 2004-06-24 Weiping Sun Dual phase hot rolled steel sheet having excellent formability and stretch flangeability
CN100368582C (en) 2003-01-28 2008-02-13 鞍钢股份有限公司 Production method of ultra-low carbon bainite steel
JP4259374B2 (en) 2004-03-30 2009-04-30 Ｊｆｅスチール株式会社 High strength steel sheet with excellent low temperature toughness and weld heat affected zone toughness and method for producing the same
JP4193757B2 (en) * 2004-06-08 2008-12-10 住友金属工業株式会社 Steel sheet for ultra-high-strength line pipe, manufacturing method thereof and welded steel pipe
CN100494451C (en) * 2005-03-30 2009-06-03 宝山钢铁股份有限公司 Superhigh strength steel plate with yield strength more than 960Mpa and method for producing same
EP1951519A4 (en) * 2005-10-24 2008-12-31 Exxonmobil Upstream Res Co High strength dual phase steel with low yield ratio, high toughness and superior weldability
JP4770415B2 (en) * 2005-11-15 2011-09-14 Ｊｆｅスチール株式会社 High tensile steel plate excellent in weldability and method for producing the same
CN100439545C (en) * 2006-03-27 2008-12-03 宝山钢铁股份有限公司 800 MPa level thick steel plate with high toughness and low yield ratio and its making process
JP2007270194A (en) * 2006-03-30 2007-10-18 Jfe Steel Kk Method for producing high-strength steel sheet excellent in sr resistance property
CN100412223C (en) 2006-07-20 2008-08-20 武汉钢铁(集团)公司 Ultra-high strength steel with excellent corrosion resistance and fatigue resistance and its making process

Also Published As

Publication number Publication date
ES2424009T3 (en) 2013-09-26
EP2218801A4 (en) 2012-02-01
WO2009056055A1 (en) 2009-05-07
ZA200904458B (en) 2010-10-27
SE0900863L (en) 2009-07-27
KR101563929B1 (en) 2015-10-28
US20100032062A1 (en) 2010-02-11
EP2218801A1 (en) 2010-08-18
JP5233020B2 (en) 2013-07-10
EP2218801B1 (en) 2013-05-01
DE112008000562T5 (en) 2010-01-28
FI127175B (en) 2017-12-29
KR20100070310A (en) 2010-06-25
CN101418416B (en) 2010-12-01
SE535302C2 (en) 2012-06-19
JP2010516895A (en) 2010-05-20
DE112008000562B4 (en) 2013-05-29
ZA200901450B (en) 2010-08-25
US8702876B2 (en) 2014-04-22
CN101418416A (en) 2009-04-29

Similar Documents

Publication Publication Date Title
FI20095872A (en) Steel sheet with low welding fracture tendency and yield strength of 800 MPa and method for its manufacture
EP2233597A4 (en) High-strength hot-dip-galvanized steel sheet having excellent moldability, and method for production thereof
EP2272994A4 (en) High-tensile strength steel and manufacturing method thereof
EP2053140A4 (en) High-strength steel sheets and processes for production of the same
BR112012004303A2 (en) High strength galvanized steel sheet and production method thereof.
BRPI0905378A2 (en) High strength steel sheet and its production method
EP2097548A4 (en) High manganese high strength steel sheets with excellent crashworthiness, and method for manufacturing of it
EP2325346A4 (en) High-strength steel plate and manufacturing method thereof
EP2505681A4 (en) Welded steel pipe for linepipe with superior compressive strength and superior toughness, and process for producing same
TWI340170B (en) High strength thick steel sheet and producing method therefor
EP2240618A4 (en) High-strength steel sheet with excellent low temperature toughness and manufacturing method thereof
EP2505682A4 (en) Welded steel pipe for linepipe with superior compressive strength, and process for producing same
EP2105514A4 (en) High-strength steel sheet
EP2350332A4 (en) High-strength steel sheet and the method for production therefor
EP2039791A4 (en) High-strength steel sheet and process for producing the same
EP2371978A4 (en) Steel sheet, surface-treated steel sheet, and method for producing the same
EP2453032A4 (en) High-strength steel sheet and manufacturing method therefor
EP2322680A4 (en) Environmentally-friendly, pb-free free-machining steel, and manufacturing method for same
BRPI0909012A2 (en) high tensile strength steel for container and production method
EP2184373A4 (en) Thick hot-rolled steel sheet having excellent processability and excellent strength/toughness after thermal treatment, and method for production of the steel sheet
EP2224029A4 (en) High-strength steel sheet, automotive strengthening member comprising the same, and process for producing automotive strengthening member
EP2085318A4 (en) Laminate steel sheet for two-piece can body, two-piece can body made of laminate steel sheet, and method for production of the two-piece can body
TWI366252B (en) Substrate with high fracture strength, structure for increasing the fracture strength of a substrate and the method thereof
GB2445749B (en) High strength steel sheet and method for producing the same
EP2313535B8 (en) High strength, high toughness steel alloy

Legal Events

Date Code Title Description
FG Patent granted

Ref document number: 127175

Country of ref document: FI

Kind code of ref document: B