ES2627318T3 - Composición a base de material hidráulico y/o puzolánico - Google Patents
Composición a base de material hidráulico y/o puzolánico Download PDFInfo
- Publication number
- ES2627318T3 ES2627318T3 ES09752200.7T ES09752200T ES2627318T3 ES 2627318 T3 ES2627318 T3 ES 2627318T3 ES 09752200 T ES09752200 T ES 09752200T ES 2627318 T3 ES2627318 T3 ES 2627318T3
- Authority
- ES
- Spain
- Prior art keywords
- cationic
- hydraulic
- pozzolana
- pozzolanic material
- composition based
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Mezcla que comprende por lo menos un material puzolánico y por lo menos un polímero catiónico hidrosoluble, presentando dicho polímero catiónico una densidad de cargas catiónicas superior a 0,5 meq/g, y una viscosidad intrínseca inferior a 1 dl/g, y no formando parte de los materiales puzolánicos la cal como tal.
Description
5
15
25
35
45
55
El nitrógeno puede ser cuaternizado después de la polimerización de manera conocida, por ejemplo, por alquilación con la ayuda de un compuesto alquilante, por ejemplo, por cloruro de metilo, o en medio ácido, por protonación.
Los polímeros catiónicos que contienen unos grupos catiónicos de amina cuaternaria son particularmente apropiados.
Entre los monómeros que ya llevan una función amina cuaternaria catiónica, se pueden citar, en particular, las sales de dialildialquil amonio, los (met)acrilatos de dialquilaminoalquilo cuaternizados, y las (met)acrilamidas Nsustituidas por un dialquilaminoalquilo cuaternizado.
La polimerización se puede llevar a cabo con unos monómeros no iónicos, preferentemente con cadena corta, que comprenden de 2 a 6 átomos de carbono. Unos monómeros aniónicos también pueden estar presentes, en la medida en que no afecten a los grupos catiónicos.
En el marco de la modificación de polímeros por injerto, se pueden citar los polímeros naturales injertados, tales como los almidones catiónicos.
Ventajosamente, el polímero catiónico según la invención contiene unos grupos cuyo carácter catiónico sólo se manifiesta en medio ácido. Los grupos aminas terciarias, catiónicos por protonación en medio ácido, son particularmente preferidos. La ausencia de carácter iónico en las composiciones hidráulicas de tipo hormigón o mortero que tienen un pH alcalino permite mejorar aún más su robustez con respecto a otros compuestos iónicos, en particular aniónicos.
A modo de ejemplo, se pueden citar los polímeros catiónicos de la familia de las polivinilaminas, que se pueden obtener por polimerización de N-vinilformamida, seguida de una hidrólisis. Las polivinilaminas cuaternizadas se pueden preparar como se describe en la patente US nº 5.292.441. Los polímeros de tipo polietilenimina también son adecuados. Estos últimos son cuaternizados por protonación.
Particularmente preferidos son los polímeros catiónicos obtenidos por policondensación de epiclorhidrina con una mono o dialquilamina, en particular, la metilamina o la dimetilamina. Su preparación ha sido descrita por ejemplo en patentes US nº 3.738.945 y nº 3.725.312.
Preferentemente, los polímeros catiónicos pueden ser unos polímeros de origen natural. Se pueden citar, en particular, el quitosano protonado o cuaternizado.
El motivo del polímero catiónico obtenido por policondensación de dimetilamina y de epiclorhidrina se puede representar de la siguiente manera:
N
Me HO
n
Cl
También son adecuados los polímeros de tipo poliacrilamida modificados por reacción de Mannich tal como la poliacrilamida N-sustituida por un grupo dimetilaminometilo.
También son adecuados los polímeros catiónicos obtenidos por policondensación de diciandiamida y de formaldehído. Estos polímeros y el procedimiento de obtención se describen en la patente FR 1 042 084.
Preferentemente, los polímeros catiónicos según la invención puede ser cuaternizados por una sal de amonio que no sea el cloruro de amonio.
Ventajosamente, el polímero catiónico según la invención puede tener otras propiedades, además de las descritas en la presente solicitud. En particular, el polímero catiónico según la invención puede ser un agente de ayuda a la trituración del Clinker o de los materiales hidráulicos y/o puzolánicos según la invención, también denominado agente de molienda.
Superplastificante
Preferentemente, la mezcla según la invención comprende, además de un polímero catiónico específico, también por lo menos un superplastificante.
6
12
Ejemplos con una puzolana natural: Puzolana de Milos -Grecia
Tabla 2
- Puzolana
- Tasa desustitucion (1) DosificaciónTratamientoPuzolana Dosificaciónadyuvante W/Aglomerante Esparcido5 minutos Resistenciacompresión1d Resistenciacompresión28d
- %
- ppm seco/puzolana % seco/aglomerante(2) mm MPA MPA
- 1
- Puzolana -Grecia 0 - 0,1 0,63 340 18,1 41,6
- 2
- Puzolana -Grecia 30 - 0,1 0,63 200 9,3 27,9
- 3
- Puzolana -Grecia 30 - 0,1 0,89 320 4,0 16,0
- 4
- Puzolana -Grecia 30 - 0,3 0,63 360 9,4 29,8
- 5
- Puzolana -Grecia 30 3000 0,1 0,79 335 5,6 19,1
- 6
- Puzolana -Grecia 30 3000 0,2 0,63 335 9,8 30,1
- 7
- Puzolana -Grecia 30 3000 0,3 0,53 320 11,2 32,8
13
Ejemplos con una arcilla calcinada (procedente de Francia -Malet)
Tabla 3
- Arcilla
- Tasa deSustitucion (1) DosificacionTratamiento arcilla Dosificacionadyuvante W/Aglomerante Esparcido5 minutos Resistenciacompresión1d Resistenciacompresión28d
- %
- ppm seco/arcilla % seco/aglomerante(2) mm MPA MPA
- 8
- Arcilla calcinada 0 - 0,1 0,63 340 18,1 42,6
- 9
- Arcilla calcinada 30 - 0,1 0,63 155 6,9
- 10
- Arcilla calcinada 30 - 0,1 0,87 345 3,2 24,1
- 11
- Arcilla calcinada 30 - 0,4 0,63 350 6,4 37,4
- 12
- Arcilla calcinada 30 2000 0,1 0,75 330 4,7 32,7
- 13
- Arcilla calcinada 30 2000 0,3 0,63 335 7,3 37,1
Claims (1)
-
imagen1