ES2088515T5 - Procedimiento para el tratamiento termoquimico homogeneo de piezas estructurales de acero que tienen superficies dificilmente accesibles. - Google Patents

Procedimiento para el tratamiento termoquimico homogeneo de piezas estructurales de acero que tienen superficies dificilmente accesibles.

Info

Publication number
ES2088515T5
ES2088515T5 ES92105758T ES92105758T ES2088515T5 ES 2088515 T5 ES2088515 T5 ES 2088515T5 ES 92105758 T ES92105758 T ES 92105758T ES 92105758 T ES92105758 T ES 92105758T ES 2088515 T5 ES2088515 T5 ES 2088515T5
Authority
ES
Spain
Prior art keywords
procedure
chemical treatment
structural steel
thermal chemical
steel pieces
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
ES92105758T
Other languages
English (en)
Other versions
ES2088515T3 (es
Inventor
Friedrich Dr Dipl-Phy Preisser
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ALD Vacuum Technologies GmbH
Original Assignee
ALD Vacuum Technologies GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=6431301&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=ES2088515(T5) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by ALD Vacuum Technologies GmbH filed Critical ALD Vacuum Technologies GmbH
Application granted granted Critical
Publication of ES2088515T3 publication Critical patent/ES2088515T3/es
Publication of ES2088515T5 publication Critical patent/ES2088515T5/es
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

PARA EL TRATAMIENTO TERMOQUIMICO UNIFORME DE COMPONENTES DE ACERO CON SUPERFICIES EXTERIORES DIFICILMENTE ACCESIBLES SE UTILIZA GAS REACTIVO CON TEMPERATURA POR ENCIMA DE 540 ESION POR ENCIMA DE 0,2 MPA.
ES92105758T 1991-05-08 1992-04-03 Procedimiento para el tratamiento termoquimico homogeneo de piezas estructurales de acero que tienen superficies dificilmente accesibles. Expired - Lifetime ES2088515T5 (es)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DE4115135A DE4115135C1 (es) 1991-05-08 1991-05-08

Publications (2)

Publication Number Publication Date
ES2088515T3 ES2088515T3 (es) 1996-08-16
ES2088515T5 true ES2088515T5 (es) 2000-05-01

Family

ID=6431301

Family Applications (1)

Application Number Title Priority Date Filing Date
ES92105758T Expired - Lifetime ES2088515T5 (es) 1991-05-08 1992-04-03 Procedimiento para el tratamiento termoquimico homogeneo de piezas estructurales de acero que tienen superficies dificilmente accesibles.

Country Status (10)

Country Link
EP (1) EP0512254B2 (es)
JP (1) JP3258071B2 (es)
AT (1) ATE139579T1 (es)
CZ (1) CZ288263B6 (es)
DE (2) DE4115135C1 (es)
ES (1) ES2088515T5 (es)
HU (1) HU209457B (es)
PL (1) PL291528A1 (es)
RU (1) RU2052535C1 (es)
TW (1) TW223128B (es)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4445154A1 (de) * 1994-12-17 1996-06-20 Fischer Artur Werke Gmbh Verfahren zur Herstellung eines aus korrosionsbeständigem Stahl bestehenden Spreizankers
DE10062862C2 (de) * 2000-12-16 2003-03-27 Ald Vacuum Techn Ag Vorrichtung zur gleichmässigen thermochemischen Behandlung von metallischen Werkstücken mit einem Reaktivgas
DE10109565B4 (de) 2001-02-28 2005-10-20 Vacuheat Gmbh Verfahren und Vorrichtung zur partiellen thermochemischen Vakuumbehandlung von metallischen Werkstücken
DE10139620A1 (de) * 2001-08-11 2003-02-27 Bosch Gmbh Robert Kraftstoffeinspritzventil für Brennkraftmaschinen und ein Verfahren zur Härtung desselben
DE102004058838B4 (de) * 2004-12-06 2007-11-29 Schramm, Armin Düseneinsatz aus Stahl
DE102005061781A1 (de) * 2005-12-23 2007-06-28 Schaeffler Kg Injektor eines Kraftstoff-Einspritzsystems
DE102013006589A1 (de) * 2013-04-17 2014-10-23 Ald Vacuum Technologies Gmbh Verfahren und Vorrichtung für das thermochemische Härten von Werkstücken
RU2651841C2 (ru) * 2015-12-23 2018-04-24 Олег Владимирович Ольшанский Способ обработки металлических деталей в условиях акустического резонансного воздействия потоком смеси сжатого воздуха и газообразных химических реагентов и устройство для его осуществления

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB114446A (en) * 1917-01-27 1918-03-27 British Carbonizing Company Lt Improvements in or relating to the Carburization and Case-hardening of Iron and Steel Articles.
GB749992A (en) * 1951-09-21 1956-06-06 United States Steel Corp Methods for nitriding metallic surfaces
US2779697A (en) * 1955-09-26 1957-01-29 United States Steel Corp Method of nitriding metallic surfaces
GB1309257A (en) * 1970-02-18 1973-03-07 Millingford Eng Co Ltd Method of nitriding hollow bodies
JPS52145343A (en) * 1976-05-29 1977-12-03 Kiyoichi Ogawa Pressurized nitriding
US4160680A (en) * 1976-11-05 1979-07-10 Sola Basic Industries, Inc. Vacuum carburizing
DE2851983B2 (de) * 1978-12-01 1980-11-06 Deutsche Gold- Und Silber-Scheideanstalt Vormals Roessler, 6000 Frankfurt Verfahren zum Aufkohlen von Hohlkörpern, insbesondere von Düsen
DE4036381C1 (es) * 1990-11-15 1991-08-14 Degussa Ag, 6000 Frankfurt, De

Also Published As

Publication number Publication date
HU209457B (en) 1994-06-28
JP3258071B2 (ja) 2002-02-18
EP0512254A3 (en) 1993-03-24
EP0512254A2 (de) 1992-11-11
EP0512254B2 (de) 2000-01-19
DE59206595D1 (de) 1996-07-25
TW223128B (es) 1994-05-01
DE4115135C1 (es) 1992-02-27
JPH05132753A (ja) 1993-05-28
HU913870D0 (en) 1992-02-28
CZ288263B6 (en) 2001-05-16
PL291528A1 (en) 1992-11-16
ATE139579T1 (de) 1996-07-15
HUT61056A (en) 1992-11-30
RU2052535C1 (ru) 1996-01-20
CS137592A3 (en) 1992-12-16
EP0512254B1 (de) 1996-06-19
ES2088515T3 (es) 1996-08-16

Similar Documents

Publication Publication Date Title
DK1000181T3 (da) Fremgangsmåde til behandling af austenitiske rustfrie stålartikler
ES2088515T3 (es) Procedimiento para el tratamiento termoquimico homogeneo de piezas estructurales de acero que tienen superficies dificilmente accesibles.
DE69902169D1 (de) Verfahren zum niederdrück-nitrocarburieren metallischer werkstücke
KR960041404A (ko) 강의 질화방법
AU2001284359A1 (en) Surface-hardened precision weight and process of making same
Edenhofer Technology, advantages and applications of direct-feed atmospheres for carburising
KR910019688A (ko) 고상의 그리고 액상의 코팅재료들의 유동화, 운반 그리고/혹은 분무를 위한 방법
JPS572826A (en) Quenching method for steel
Preisser et al. Method of Nitriding Work Pieces of Steel Under Pressure
Hoffmann The use of oxygen probes for nitriding processes: theory and practice
Bil'chenko et al. Nitriding Capability of Martensite--Austenite Steel Depending on the Phase and Structural States
Luiten et al. Vacuum Heat Treatment Equipment in Practical Application
Bannykh The development of nitriding in Russia
Taki et al. Plasma Nitriding of Pure Iron and Stainless Steel
Wang et al. Study on Quenching After Prenitriding and High Temperature Diffusion of Nitrogen Atoms and Quenching After Prenitriding and Intercritical Temperature Diffusion of Nitrogen Atoms of Steel 20 CrMnSiA
Lakhtin et al. Nitrogen Case Hardening at 700 deg C With Subsequent Quench Hardening of the Surface Layer
Yasumaru et al. Nitrogen-induced Phase Transformations in Austenitic Stainless Steels
Stratton Controlled Atmospheres for Thermochemical Surface Engineering
Kulka et al. The Influence of Carburizing Parameters on the Carbon Profile in LH 15(52100) Steel at 1173 K
Ostrowski et al. Austenitic Carbonitriding of Low-Carbon Steels in Fluidized Bed
Pourtalet et al. ANALT 1: a new way to supply heat treatment atmospheres
JPS5263812A (en) Martensitic stainless steel for nitriding
Edenhofer et al. Effect of Nitriding Conditions and Steel Composition on the Hardness of Nitrided Surfaces
SE8902365L (sv) Saett att behandla staal
Dubnyakov et al. The Role of the Martensitic Transformation in Steel Hardening During Laser Treatment and Subsequent Deformation

Legal Events

Date Code Title Description
FG2A Definitive protection

Ref document number: 512254

Country of ref document: ES