EA019216B1 - Anticorrosion packaging

Info

Publication number: EA019216B1
Application number: EA200901649A
Authority: EA
Inventors: Юрий Анатольевич Блик; Александр Исаевич Ласкевич
Original assignee: Юрий Анатольевич Блик; Александр Исаевич Ласкевич
Priority date: 2009-11-13
Filing date: 2009-11-13
Publication date: 2014-02-28
Also published as: EA200901649A1

Abstract

The invention relates to an anticorrosion packaging of engineering articles and can be used for protection of machines and equipment against corrosion that is preservation thereof during transportation, long time storage prior to erection. The anticorrosion packaging comprises a packing material and a corrosion inhibitor. According to the invention the packing material comprises polyethylene including a corrosion inhibitor, and lauric acid, morpholine and caprylic acid as a corrosion inhibitor with the following component ratio, mass %: lauric acid – 20.5; caprylic acid – 44.0; morpholine – 35.5.

Description

Изобретение относится к упаковке изделий машиностроения и может использоваться для защиты машин и оборудования от коррозии, т.е. консервации их при перевозках, длительном хранении перед установкой в эксплуатацию.The invention relates to the packaging of engineering products and can be used to protect machinery and equipment from corrosion, i.e. their conservation during transportation, long-term storage before installation in operation.

Известными антикоррозионными ингибиторами, или консерваторами для зашиты машин и оборудования при упаковке от атмосферной коррозии, являются защитные смазки и масла, механически отделяющие защищаемую поверхность от влаги и кислорода воздуха.Known anticorrosive inhibitors, or conservatives for the protection of machines and equipment during packaging against atmospheric corrosion, are protective lubricants and oils, which mechanically separate the protected surface from moisture and oxygen from the air.

Недостатком известных антикоррозионных упаковочных ингибиторов является высокая трудоемкость при их нанесении на обрабатываемую металлическую поверхность, а также возможность нарушения слоя покрытия за счет неравномерности покрытия или возможного механического удаления участка смазки и т.д., и они уже не обеспечивают защиту металла от коррозии.A disadvantage of the known anti-corrosion packaging inhibitors is the high labor intensity when applied to the metal surface to be treated, as well as the possibility of breaking the coating layer due to uneven coating or possible mechanical removal of the lubricant area, etc., and they no longer protect the metal from corrosion.

Также известна антикоррозионная упаковка, включающая в качестве упаковочного материала бумагу, обработанную антикоррозионным составом в виде микровоска. Это смесь твердых углеводородов в основном технических парафинов и церезинов.Also known anticorrosion packaging, including as a packaging material paper, treated with an anticorrosive composition in the form of microvosk. It is a mixture of solid hydrocarbons, mainly technical paraffins and ceresins.

Недостатком известной антикоррозионной упаковки является высокая трудоемкость при упаковке крупногабаритных изделий, невысокая герметичность упаковки и, как следствие, низкая степень защиты от коррозии упаковываемых металлических изделий.A disadvantage of the known anti-corrosion packaging is the high labor intensity in the packaging of large-sized products, the low tightness of the packaging and, as a consequence, the low degree of protection against corrosion of the packaged metal products.

Наиболее близкой антикоррозионной упаковкой к предлагаемой является герметичная антикоррозионная упаковка, в которой упаковочным материалом является полиэтилен, а антикоррозионной добавкой, осушающей воздух в герметичной упаковке, являются твердые адсорбенты, расфасованные в матерчатые мешочки - активированный уголь, алюмогель или силикогель.The closest anti-corrosion packaging to the offer is a sealed anti-corrosion package in which the packaging material is polyethylene, and the anti-corrosion additive drying the air in the sealed packaging is solid adsorbents, packaged in fabric bags - activated carbon, alumogel or silica gel.

Недостатком прототипа является высокая трудоемкость при упаковке, а также недостаточно высокая степень антикоррозионной защиты упаковываемого металлического оборудования.The disadvantage of the prototype is the high complexity during packaging, as well as the insufficiently high degree of corrosion protection of the metal equipment being packaged.

Задачей предлагаемого изобретения является высокая степень защиты от коррозии упаковочного оборудования с низкими трудозатратами.The task of the invention is a high degree of protection against corrosion of packaging equipment with low labor costs.

Поставленная задача решается следующим образом. Антикоррозионная упаковка состоит из упаковочного материала и ингибитора коррозии. Согласно изобретению в качестве упаковочного материала используют полиэтилен, включающий в свой состав ингибитор коррозии, а в качестве ингибитора коррозии лауриновую кислоту, каприловую кислоту и морфолин при следующем соотношении компонентов, мас.%:The problem is solved as follows. Anticorrosion packaging consists of packaging material and a corrosion inhibitor. According to the invention, polyethylene is used as a packaging material, which includes a corrosion inhibitor in its composition, and lauric acid, caprylic acid and morpholine as a corrosion inhibitor in the following ratio, wt.%:

лауриновая кислота - 20,5, каприловая кислота - 44,0, морфолин - 35,5.lauric acid - 20.5, caprylic acid - 44.0, morpholine - 35.5.

Существенными отличиями предлагаемого изобретения в отличие от прототипа является следующее.The essential differences of the invention in contrast to the prototype is the following.

Использование в качестве упаковочного материала полиэтилена, включающего в своем составе лауриновую кислоту, каприловую кислоту и морфолин при следующем соотношении компонентов, мас.%:Use as a packaging material polyethylene, comprising in its composition lauric acid, caprylic acid and morpholine in the following ratio, wt.%:

лауриновая кислота - 20,5, каприловая кислота - 44,0, морфолин - 35,5, позволяет достичь высокой степени защиты от коррозии упаковываемых в нее металлических изделий, за счет экспериментально подобранного антикоррозионного сочетания летучих кислот, обеспечивающих защитное действие в водяной пленке на защищаемой поверхности, адсорбируясь на этой поверхности и отделяя ее от атмосферной влаги.lauric acid - 20.5, caprylic acid - 44.0, morpholine - 35.5, allows to achieve a high degree of protection against corrosion of metal products packaged in it, due to the experimentally selected anti-corrosion combination of volatile acids, which provide a protective effect in a water film on the protected surface, adsorbing on this surface and separating it from atmospheric moisture.

Предлагаемое изобретение поясняется следующим примером.The invention is illustrated by the following example.

Пример.Example.

Берут 44 кг каприловой кислоты, 35,5 кг морфолина и 20,5 кг лауриновой кислоты, все тщательно перемешивают. Из полученной смеси делают гранулы, которые добавляют в расплав полиэтилена. Соотношение добавки к полиэтилену следующее: 6% добавки на 25 кг полиэтилена. Из этого состава изготавливают антикоррозионную упаковочную полиэтиленовую пленку.Take 44 kg of caprylic acid, 35.5 kg of morpholine and 20.5 kg of lauric acid, everything is thoroughly mixed. Granules are made from the resulting mixture, which are added to the polyethylene melt. The ratio of additives to polyethylene is as follows: 6% of additives per 25 kg of polyethylene. This composition is made of anti-corrosion packaging polyethylene film.

Испытания полученной антикоррозионной упаковочной полиэтиленовой пленки производили на металлах, которые показали, что содержание влаги в герметичной упаковке составляет 30%. Срок хранения металлических изделий в такой упаковке от 1 до 3-х лет.Tests of the obtained anti-corrosion packaging polyethylene film were made on metals, which showed that the moisture content in a sealed package is 30%. The shelf life of metal products in such packaging is from 1 to 3 years.

Поскольку защитные свойства ингибиторов проявляются только при постоянном контакте его паров с защищаемой поверхностью, длительность действия ингибитора возможна лишь в герметичной упаковке, исключающей выветривание или вымывание ингибитора.Since the protective properties of the inhibitors are manifested only with the constant contact of its vapors with the protected surface, the duration of the inhibitor's action is possible only in a sealed package, eliminating weathering or leaching of the inhibitor.

Использование летучих ингибиторов, входящих в состав заявляемой антикоррозионной упаковки, упрощает процесс консервации, сокращает его трудоемкость, исключает необходимость расконсервации, облегчает наблюдение за состоянием защищаемой поверхности (прозрачность полиэтилена), что позволяет своевременно принять соответствующие меры в случае появляемой коррозии.The use of volatile inhibitors that make up the inventive anti-corrosion packaging simplifies the process of conservation, reduces its complexity, eliminates the need for re-opening, makes it easier to monitor the condition of the surface to be protected (transparency of polyethylene), which allows you to take appropriate measures in the event of corrosion.

- 1 019216- 1 019216

Источники информацииInformation sources

1. Павлов А.И., Цыганова В.И. Упаковка, транспортирование, хранение машин и оборудования.1. Pavlov A.I., Tsyganov V.I. Packaging, transportation, storage of machines and equipment.

- М.: Машиностроение, 1984, с. 47-58- M .: Mashinostroenie, 1984, p. 47-58

2. Павлов А.Н., Цыганова В.И. Упаковка, транспортирование, хранение машин и оборудования.2. Pavlov A.N., Tsyganov V.I. Packaging, transportation, storage of machines and equipment.

- М.: Машиностроение, 1984, с. 58-66- M .: Mashinostroenie, 1984, p. 58-66

Claims

CLAIM

Anticorrosive packaging, consisting of a packaging material and a corrosion inhibitor, characterized in that it contains polyethylene as a packaging material, which includes a corrosion inhibitor, and as an inhibitor it contains lauric acid, caprylic acid and morpholine, in the following ratio, wt.% :

lauric acid - 20.5, caprylic acid - 44.0, morpholine - 35.5.