DK155658C - Process for preparing a hydrothermal curing, asbestos-free, refractory mold body - Google Patents

Process for preparing a hydrothermal curing, asbestos-free, refractory mold body Download PDF

Info

Publication number
DK155658C
DK155658C DK678774AA DK678774A DK155658C DK 155658 C DK155658 C DK 155658C DK 678774A A DK678774A A DK 678774AA DK 678774 A DK678774 A DK 678774A DK 155658 C DK155658 C DK 155658C
Authority
DK
Denmark
Prior art keywords
mixture
mica
fibers
weight
plates
Prior art date
Application number
DK678774AA
Other languages
Danish (da)
Other versions
DK678774A (en
DK155658B (en
Inventor
Ernest Barrable Victor
Original Assignee
Cape Board And Panels Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cape Board And Panels Ltd filed Critical Cape Board And Panels Ltd
Priority to DK678774AA priority Critical patent/DK155658C/en
Publication of DK678774A publication Critical patent/DK678774A/da
Publication of DK155658B publication Critical patent/DK155658B/da
Application granted granted Critical
Publication of DK155658C publication Critical patent/DK155658C/en

Description

1DK 155658 B1DK 155658 B

Opfindelsen angår en fremgangsmåde ved fremstilling af en hydrotermisk hærdende, asbestfri, ildfast byggeplade af kalkholdige og kiseljordholdige komponenter, cellulosefibre og i givet fald uorganiske fibre. 5 De ved fremgangsmåden fremstillede formlegemer er især byggeplader.The invention relates to a process for the production of a hydrothermal-curing, asbestos-free, refractory building plate of calcareous and silica-containing components, cellulose fibers and, where appropriate, inorganic fibers. The moldings produced by the process are especially building boards.

DE patentskrift nr. 1.239.608 beskriver en fremgangsmåde ved fremstilling af formlegemer, ved hvilken perlit og vermiculit røres op med cellulosefibre under 10 anvendelse af et hydraulisk eller bituminøst bindemiddel til frembringelse af en opslæmning, som afvandes og under anvendelse af tryk og i givet fald under indvirkning af varme presses til formlegemer. De ifølge denne fremgangsmåde fremstillede formlegemer har kun ringe 15 bøjestyrke og en hel utilstrækkelig ildfasthed.U.S. Patent No. 1,239,608 discloses a process for preparing mold bodies in which perlite and vermiculite are agitated with cellulose fibers using a hydraulic or bituminous binder to produce a slurry which is dewatered and using pressure and, as appropriate. under the influence of heat is pressed into molds. The moldings made according to this method have only 15 bending strength and a very insufficient refractory.

Fra DE offentliggørelsesskrift nr. 2.411.864 kendes en .fremgangsmåde ved fremstilling af ildbestandige pladeprodukter ved hvilken korte og lange stabelglasfibre, hydraulisk cement, siliciumdioxid, cellu-20 losefibre i givet fald perlit og/eller diatomit og vand blandes indbyrdes til en opslæmning. Opslæmningen formes derefter til plader, som komprimeres, ældes, behandles i autoklave og tørres. Disse plader har ganske vist en forbedret bøj estyrke i forhold til de i følge 25 DE patentskrift 1.239.608 fremstillede formlegemer, men deres ildfasthed er dog ikke tilfredsstillende.DE Publication No. 2,411.864 discloses a method of producing fire-resistant sheet products in which short and long stack glass fibers, hydraulic cement, silica, cellulose fibers, where appropriate, perlite and / or diatomite and water are mixed into a slurry. The slurry is then formed into plates which are compressed, aged, treated in autoclave and dried. Although these plates have an improved flexural strength compared to the moldings produced in accordance with 25 DE patent specification 1,239,608, their fireproof is not satisfactory.

En fremgangsmåde af den indledningsvis nævnte art er kendt fra DE fremlæggelsesskrift nr. 1.646.962. Det ifølge denne fremgangsmåde fremstillede formlegeme 30 har en stor termisk krympning, hvilket fører til brud i formlegemet ved høje temperaturer og dermed til en ringe ildfasthed.A method of the kind mentioned at the outset is known from DE Publication No. 1,646,962. The mold body 30 produced by this method has a large thermal shrinkage which leads to fracture of the mold body at high temperatures and thus to a low refractory.

Formålet med den foreliggende opfindelse er at tilvejebringe en fremgangsmåde af den indledningsvis 35 nævnte art, ved hvilken der kan fremstilles byggeplader med høj bøjningsstyrke og ildfasthed.The object of the present invention is to provide a method of the kind mentioned in the preamble to which building boards with high bending strength and fireproof can be manufactured.

22

2DK 155658 B2DK 155658 B

Dette formål er opfyldt ved den i krav 1 angivne fremgangsmåde.This object is fulfilled by the method of claim 1.

Fremgangsmåden ifølge opfindelsen anvendes til fremstilling af byggeplader. Det bemærkes dog, at udtrykket "byggeplade" anvendes i den videste forstand dvs. som betegnelse for plader, som kan anvendes til ethvert ønsket byggeformål. Således omfatter dette udtryk eksempelvis også plader, som anvendes i skibe og er kendt som skibsplader.The method according to the invention is used for the production of building boards. However, it should be noted that the term "building board" is used in the broadest sense ie. as a term for boards which can be used for any desired construction purpose. Thus, for example, this term also includes plates used in ships and is known as ship plates.

Cellulosefibrene til forstærkningen er eksempelvis fibre fremstillet af pulp til papirfremstilling, eksempelvis pulp fremstillet ved sulfatfremgangsmåden eller sulfitfremgangsmåden eller ved en mekanisk fremgangsmåde og pulp af alle arter fra affaldstræ, jute, hør, bomuld, halm, espartogræs, hamp, "ramle" og bagas-se.The reinforcing cellulose fibers are, for example, fibers made from pulp for papermaking, for example, pulp made by the sulphate or sulphite process or by a mechanical process and pulp of all species from waste wood, jute, flax, cotton, straw, esparto grass, hemp, "rattle" and baggage. see.

Blandingen kan endvidere tilsættes uorganiske fiberformige forstærkningsmaterialer. I afhængighed af de yderligere forstærkningsmaterialer og også af den anvendelse, hvortil de ifølge opfindelsen fremstillede byggeplader skal anvendes, kan det forstærkende materiale indeholde hvad som helst fra 5 til 100 vægtprocent cellulosefibre. Selv om cellulosefibrene hovedsageligt anvendes til forstærkningsformål, bibringer de dog en del af ildfastheden ved de ifølge opfindelsens fremgangsmåde fremstillede byggeplader. En forbedret ildfasthed kan opnås ved yderligere uorganiske fiber-formige forstærkningsmaterialer, som anvendes i forbindelse med cellulosefibrene og omfatter mineralfibre såsom glasfibre (indbefattende alkalibestandige glasfibre), slaggeuldsfibre og stenuldsfibre, keramiske fibre, som zirkoniumoxidfibre og alimuniumoxidfibre, kvarts-aluminiumoxidfibre, aluminiumsilikatfibre og metaltråde. Vilkårlige af disse fibre eller tråde eller alle disse fibre eller tråde kan være belagte eksempelvis med alkalibestandige materialer. Når disse yderli- 3In addition, the mixture can be added to inorganic fibrous reinforcing materials. Depending on the additional reinforcing materials and also the application to which the building boards of the invention are to be used, the reinforcing material may contain anything from 5 to 100% by weight cellulose fibers. However, although the cellulose fibers are mainly used for reinforcing purposes, they impart some of the fireproof to the building boards made according to the method of the invention. An improved refractory may be obtained by additional inorganic fibrous reinforcing materials used in conjunction with the cellulose fibers and comprising mineral fibers such as glass fibers (including alkali-resistant glass fibers), slag wool fibers and alumina fibers, ceramic fibers, alumina fibers, zirconium oxide fibers, and zirconia fibers. Any of these fibers or yarns or all of these fibers or yarns may be coated, for example, with alkali resistant materials. When these additional 3

3DK 155658 B3DK 155658 B

gere fiberformige forstærkningsmaterialer anvendes, tilsættes de fortrinsvis i en mængde på 95-0,5 vægtprocent og fortrinsvis 40-10 vægtprocent i forhold til den samlede vægt af fiberformige forstærkningsmaterialer.When fibrous reinforcing materials are used, they are preferably added in an amount of 95-0.5% by weight and preferably 40-10% by weight relative to the total weight of fibrous reinforcing materials.

Det med vand hærdende uorganiske bindemiddel er en autoklavebehandlet eller ikke-autoklavebehandlet kombination af kiseljordholdige komponenter (dvs. et materiale indeholdende reaktionsdygtig kiseljord eksempelvis PFA (pulveriseret flyveaske), kvartssand, ler eller diatomit) og kalkholdige komponenter (dvs. et vilkårligt mineral, råmateriale eller affaldsprodukt, som indeholder mere end 30% CaO, eksempelvis brændt kalk). Blandingen kan endvidere tilsættes cement.The water-curing inorganic binder is an autoclave-treated or non-autoclave-treated combination of silica-containing components (i.e., a material containing reactive silica such as PFA (powdered fly ash), quartz sand, clay or diatomite) and calcareous components (i.e., any mineral, raw material) waste product containing more than 30% CaO, eg burnt lime). The mixture can also be added to cement.

Det uorganiske bindemiddel tilsættes fortrinsvis i en mængde på 70-90 vægtprocent af den samlede vægt af bindemiddel og fibre.The inorganic binder is preferably added in an amount of 70-90% by weight of the total weight of binder and fiber.

Ved fremgangsmåden ifølge opfindelsen tilsættes glimmer og/eller vermiculit til blandingen i en mængde indtil 50 vægtprocent i forhold til det samlede faststofindhold i blandingen. Et særligt vigtigt resultat af anvendelsen af vermiculit og/eller glimmer ved den opfindelsesmæssige fremgangsmåde er forbedrede krympe-egenskaber ved den dannede byggeplade. En mindre krympning ved høje temperaturer er et karaktertræk, som gør de ifølge opfindelsens fremgangsmåde fremstillede plader særlig interessante for byggeindustrien.In the process of the invention, mica and / or vermiculite are added to the mixture in an amount up to 50% by weight relative to the total solids content of the mixture. A particularly important result of the use of vermiculite and / or mica in the inventive method is improved shrinkage properties of the resulting building board. A slight shrinkage at high temperatures is a characteristic which makes the sheets made according to the method of the invention particularly interesting for the construction industry.

Andre fyldstoffer som kan være indeholdt i den ved fremgangsmåden anvendte blanding omfatter granulerede, celleformede eller fiberformede fyldstoffer såsom perlit, kieselguhr, ler og leraffald, karbonat, såsom kalk, dolomit og magnesiumkarbonat, wollastonit og andre kalciumsilikat fy Idstof fer. Disse kan være til stede i en mængde på 1-50 vægtprocent i forhold til det samlede faststofindhold. Det skal også påpeges, at kieselguhr, ler og leraffald når de indeholer reaktionsdygtig kieseljord kan udgøre en komponent af bindemidlet.Other fillers which may be contained in the blend used in the process include granulated, cellular or fibrous fillers such as perlite, silica, clay and clay waste, carbonate such as lime, dolomite and magnesium carbonate, wollastonite and other calcium silicate compounds. These may be present in an amount of 1-50% by weight relative to the total solids content. It should also be noted that silica, clay and clay wastes when they contain reactive silica can be a component of the binder.

44

4DK 155658B4DK 155658B

Ved fremgangsmåden ifølge opfindelsen kan der ifølge en variant først fremstilles en vandig opslæmning af blandingen. Denne vandige opslæmning har normalt et faststofindhold på 3-20 vægtprocent eller mere, eksempelvis 30 vægtprocent. Opslæmningen kan opvarmes noget, eksempelvis til 25-45°C og kan indeholde små mængder af sådanne tilsætninger som flokkulanter til regulering af tilbageholdelse af udgangsmateriale og som filtrationshjælpemidler (såsom polyacrylamider), vandtilbageholdelseshjælpemidler, modifikatorer til vandindholdet (eksempelvis carboxymethylcellulosederi-vater,polyethylenoxider), befugtningsmidler (eksempelvis detergenter), og hærdereguleringsmidler (eksempelvis kalciumchlorid og lignosulfonater).In the process of the invention, according to a variant, an aqueous slurry of the mixture can first be prepared. This aqueous slurry usually has a solids content of 3-20% by weight or more, for example 30% by weight. The slurry may be heated somewhat, for example to 25-45 ° C, and may contain small amounts of such additives as flocculants for controlling retention of starting material and as filtration aids (such as polyacrylamides), water retention aids, modifiers to the water content (e.g. carboxymethyl cellulose ethylene, wetting agents (e.g., detergents), and hardening agents (e.g., calcium chloride and lignosulfonates).

Opslæmningen kan derefter formes til plader ved enhver fremgangsmåde til fremstilling af byggeplader af fiberforstærket cement. Disse fremgangsmåder er eksempelvis (a) Hatschek-fremgangsmåden, (b) Magnani-fremgangsmåden, (c) anvendelse af en enkel presse og (d) Fourdrinier-fremgangsmåden, hvor pladerne ved alle fremgangsmåder afvandes i en grad, således at de er lette at håndtere. Ved Magnani-processen påføres opslæmningen et ubrudt stykke filt mellem to drevne fordelervalser. Fordelervalserne er anbragt på en vogn, som bevæges frem og tilbage over en bestemt længde af indretningen. Under filten findes en række indbyrdes forbundne vacuumkasser og disse bevæges frem med det ubrudte filt. Medens vandet ved vacuummet fjernes fra opslæmningen på filten, øges materialets volumen yderligere under hver passage af fordelervalserne, som bevæges frem og tilbage. Når de således dannede plader forlader det område, som er dækket af fordelervalsernes bevægelse, dræneres de yderligere af vacuumkasserne. Pladerne løber derefter gennem et sæt oscillerende ka-landervalser, som glatter pladernes overflader og gennem hvilke pladerne får deres endelige tykkelse. Pia- 5The slurry can then be molded into sheets by any method of manufacturing fiber reinforced cement building boards. These methods are, for example, (a) the Hatschek method, (b) the Magnani method, (c) the use of a single press, and (d) the Fourdrinier method, in which the plates are dewatered to a degree so that they are easy to handle. In the Magnani process, the slurry is applied to a continuous piece of felt between two driven distributor rollers. The distributor rollers are arranged on a trolley which is moved back and forth over a certain length of the device. Below the felt are a number of interconnected vacuum boxes and these are moved forward with the unbroken felt. While the water in the vacuum is removed from the slurry on the felt, the volume of the material is further increased during each passage of the distributor rollers which move back and forth. When the plates thus formed leave the area covered by the movement of the distributor rollers, they are further drained by the vacuum boxes. The plates then run through a set of oscillating caster rolls which smooth the surfaces of the plates and through which the plates get their final thickness. Pia- 5

5DK 155658 B5DK 155658 B

derne færdiggøres derefter og afskæres på den ønskede længde.they are then completed and cut to the desired length.

Efter at pladerne er fremstillet ved en vilkårlig af disse i princippet kendte fremgangsmåder gives 5 bindemidlet og i givet fald cementen lejlighed til at hærde eller afbinde. Dette sker ved en autoklavebehandling. Pladerne kan da i givet fald straks tørres.After the sheets are made by any of these generally known methods, the binder and, where appropriate, the cement is given the opportunity to harden or bond. This is done by an autoclave treatment. The plates can then be dried immediately.

Udgangsopslæmningen fremstilles normalt ved formaling (vandpulpdannelse) og dispergering af det fi-10 brøse matriale, som massen skal indeholde, i vand efterfulgt af tilsætning af de andre pulverformede materialer til dannelse af en opslæmning med et tilnærmet forhold mellem vand og fast stof på 5:1 til 10:1. Opslæmningen fortyndes derefter yderligere med vand til 15 tilvejebringelse af et vand/faststofforhold på ca. 25:1. Der fremstilles derefter plader af denne opslæmning ved afvanding på den anvendte maskine til tilvejebringelse af et vand/faststofforhold på ca. 1:1.The starting slurry is usually prepared by grinding (water pulping) and dispersing the fibrous material to contain the pulp in water, followed by addition of the other powdery materials to form a slurry having an approximate water-solid ratio of 5: 1 to 10: 1. The slurry is then further diluted with water to provide a water / solid ratio of approx. 25: 1st Plates of this slurry are then prepared by dewatering on the machine used to provide a water / solids ratio of approx. 1: 1.

Når der tilsigtes fremstilling af andre formede 20 genstande end byggeplader sammensættes massen således, at den får en viskositet, der egner sig til den specielle påtænkte fremstilling. Ved fremstilling af rørlængder, skal massen således være væsentligt mere viskos end ved fremstilling af plader.When intended to produce shaped articles other than building boards, the pulp is composed so as to obtain a viscosity suitable for the particular intended manufacture. Thus, in the manufacture of pipe lengths, the mass must be substantially more viscous than in the manufacture of sheets.

25 Ved en anden variant af fremgangsmåden ifølge opfindelsen formes det uorganiske bindemiddel lige før det blandes med fibrene. Således kan eksempelvis brændt kalk (den kalkholdige komponent) og kvarts (den kisel-jordholdige komponent) omsættes eller blive bragt til 30 reaktion forud i en autoklave med omrøring under dannelse af tobermorit. Det fibrøse fyldmateriale glimmer og/eller vermiculit og ethvert andet fyldmateriale røres derefter ud i det vandige system af tobermorit, som derefter bringes i den ønskede facon, eventuelt auto-35 klaveres yderligere, drænes og tørres.In another variant of the process according to the invention, the inorganic binder is formed just before it is mixed with the fibers. Thus, for example, burnt lime (the calcareous component) and quartz (the siliceous earth component) can be reacted or reacted prior to an autoclave with stirring to form tobermorite. The fibrous filler material mica and / or vermiculite and any other filler material is then stirred into the aqueous system of tobermorite which is then brought into the desired shape, optionally further autoclaved, drained and dried.

Ved en yderligere udførelsesform fremstilles en opslæmning af de kalciumsilikatdannende komponenter, 6In a further embodiment, a slurry of the calcium silicate forming components, 6, is prepared

6DK 155658 B6DK 155658 B

forstærkende fibermateriale, glimmer og/eller vermicu-lit og vand og denne opslæmning tilsættes friskfrem-stillet tobermorit eller xonotlit. Blandingen formes derefter, afvandes, autoklaveres og tørres. Som det tidligere er beskrevet.reinforcing fiber material, mica and / or vermiculite and water and this slurry is added to freshly made tobermorite or xonotlite. The mixture is then formed, dewatered, autoclaved and dried. As previously described.

Opfindelsen vil i det følgende blive nærmere beskrevet ved hjælp af eksempler, hvori alle de angivne andele er efter vægt.The invention will now be described in more detail by way of example, in which all of the stated proportions are by weight.

EKSEMPEL 1EXAMPLE 1

En blanding af 6 dele cellulosefibre og 6 dele alkalibestandige glasfibre dispergeres i vand, derefter tilsættes 37,7 dele brændt kalk, 15,8 dele kvarts, 21,5 dele diatomit og 13,0 dele vermicult til frembringelse af en opslæmning med et vand: faststof forhold på ca. 10:1. Opslæmningen formes til plader ved afvanding på en Hatschek-maskine, hvorved der opnås et vand faststof forhold på 1:1. De formede plader behandes i autoklave ved 10,5 atm i 18 timer og slutproduktet har en massefylde på 710 kg/m3 og en brudstyrke på 8,6 N/mm2.A mixture of 6 parts cellulose fibers and 6 parts alkali resistant glass fibers is dispersed in water, then 37.7 parts of burnt lime, 15.8 parts of quartz, 21.5 parts of diatomite and 13.0 parts of vermicult are added to produce a slurry with a water: solids ratio of approx. 10: 1. The slurry is formed into plates by dewatering on a Hatschek machine, thereby obtaining a water solids ratio of 1: 1. The shaped plates are treated in autoclave at 10.5 atm for 18 hours and the final product has a density of 710 kg / m3 and a breaking strength of 8.6 N / mm2.

Lignende resultater opnås når pladerne fremstilles på en Magnani-maskine eller i en presse.Similar results are obtained when the plates are manufactured on a Magnani machine or in a press.

EKSEMPEL 2EXAMPLE 2

Under anvendelse af en lignende fremgangsmåde som i førnævnte eksempel blev fremstillet byggeplader på en presse ud fra en vandig opslæmning, som indeholdt 10 dele cellulosefibre, 50 dele vermiculit, 21 dele brændt kalk og 19 dele kvarts. Pladerne blev behandlet i en autoklave i 36 timer ved 10,5 at og de havde en massefylde på 600 kg/m3 og en brudstyrke på 6,5 N/mm2. EKSEMPEL 3 oq 4Using a similar method as in the aforementioned example, building boards were prepared on a press from an aqueous slurry containing 10 parts of cellulose fibers, 50 parts of vermiculite, 21 parts of burnt lime and 19 parts of quartz. The plates were treated in an autoclave for 36 hours at 10.5 at and they had a density of 600 kg / m 3 and a breaking strength of 6.5 N / mm 2. EXAMPLES 3 AND 4

Under anvendelse af den i eksempel 1 beskrevne grundfremgangsmåde blev fremstillet byggeplader af de i den følgende tabel II angivne bestanddele under anvendelse af de der ligeledes angivne betingelser for autoklavebehandlingen. Cellulosefibrene blev dispergeret i vand og formalet (underkastet vandpulpdannelse), de øv- 7Using the basic method described in Example 1, building boards of the ingredients listed in the following Table II were prepared using the conditions also set out for the autoclave treatment. The cellulose fibers were dispersed in water and ground (subjected to water pulping), the other 7

DK 155658 BDK 155658 B

rige bestanddele blev tilsat og den resulterende opslæmning grundigt gennemblandet og yderligere fortyndet. Den blev formet til plader under anvendelse af de anførte metoder og pladerne blev autoklaveret. De såle-5 des frembragte plader besad de angivne egenskaber.Rich ingredients were added and the resulting slurry thoroughly mixed and further diluted. It was formed into plates using the methods indicated and the plates were autoclaved. The plates thus produced possessed the specified properties.

Den angivne "MFT"-revneprøve (micro fire test) blev udført som følger: En blok af hvert produkt med en diameter på ca. 100 mm og en tykkelse på ca. 10 mm blev opvarmet med den i den britiske norm BSS 476, Part 8 10 (1972) angivne hastighed. Denne hastighed er angivet i den følgende tabel I, i hvilken.T er ovntemperaturen i °C til tiden t og T0 er ovnudgangs temperaturen, som skal ligge mellem 10°C og 40°C:The indicated "MFT" crack test (micro fire test) was performed as follows: One block of each product with a diameter of approx. 100 mm and a thickness of approx. 10 mm was heated at the rate specified in British Standard BSS 476, Part 8 10 (1972). This rate is given in the following Table I, in which.T is the oven temperature in ° C at time t and T0 is the furnace exit temperature, which should be between 10 ° C and 40 ° C:

TABEL ITABLE I

15 __15 __

Tid t TemperaturforøgeIse min i ovn (T - Tq) 20 25 10 15 30 60 90 120 180 240 360 556 659 718 821 925 986 1029 1090 1133 1193Time t Temperature increase min in oven (T - Tq) 20 25 10 15 30 60 90 120 180 240 360 556 659 718 821 925 986 1029 1090 1133 1193

Den tid det tog fra begyndelsen af opvarmningen til fremkomsten af den første revne blev konstateret er angivet i sidste linie i tabel II nedenfor.The time taken from the onset of heating to the appearance of the first crack was noted in the last line of Table II below.

30 830 8

DK 155658 BDK 155658 B

TABEL IITABLE II

Bestanddele og egenskaber Eksempel 3 Eksempel 4 Cellulose (vægtprocent) 12,0 10,0 Kalk (%) 31,8 • 42,0 Kvarts (%) 29,2 21,0 Vermiculit (%) 12,0 12,0 Cement (%) 15,0 15,0 Fremstillingsmetode Hatschek eller Magnani Hatschek eller Magnani Autoklaveringsbetingelser ca.9i~10at/24h ca.9i~10at/24h 3 Tæthed (kg/m ) 725 715 2 Brudstyrke (N/mm ) 12 5,5 MFT revne (minutter) 15 20 EKSEMPEL 5Ingredients and Properties Example 3 Example 4 Cellulose (% by weight) 12.0 10.0 Lime (%) 31.8 • 42.0 Quartz (%) 29.2 21.0 Vermiculite (%) 12.0 12.0 Cement ( %) 15.0 15.0 Method of preparation Hatschek or Magnani Hatschek or Magnani Autoclaving conditions ca.9i ~ 10at / 24h ca.9i ~ 10at / 24h 3 Density (kg / m) 725 715 2 Fracture strength (N / mm) 12 5.5 MFT crack (minutes) EXAMPLE 5

Der blev fremstillet et vandholdigt kalciumsilikat af tobermorit-typen ved at formalet kvarts og hydratkalk i et molært forhold på Ca0:Si02 på 0,9 til 1,0 reagerede i en autoklave med omrøring og under et damptryk på 9,44 atm.Tobermorite-type aqueous calcium silicate was prepared by reacting ground quartz and hydrate lime at a molar ratio of Ca0: SiO2 of 0.9 to 1.0 in a stirred autoclave and under a vapor pressure of 9.44 atm.

Der blev tilsat 16 vægtprocent stenuldfibre, 1 vægtprocent hakket glasfiber, 1 vægtprocent cellulosepulp og 20 vægtprocent formalet glimmer til det således fremstillede bindemiddel. Blandingen blev grundigt omrørt og derefter presset til plader ved hjælp af en hydraulisk presse og en afvandingsform. Pladerne blev tørret ved 150°C.16% by weight of stone wool fibers, 1% by weight of chopped fiberglass, 1% by weight cellulose pulp and 20% by weight of ground mica were added to the binder thus produced. The mixture was thoroughly stirred and then pressed into plates by a hydraulic press and a dewatering mold. The plates were dried at 150 ° C.

Disse pladers egenskaber blev målt ligesom egenskaberne af plader, som blev fremstillet på samme måde men uden noget glimmerindhold. Resultaterne er vist i nedenstående tabel III. Som det ses af værdierne forThe properties of these boards were measured as were the properties of boards which were made in the same way but without any mica content. The results are shown in Table III below. As can be seen from the values for

Claims (3)

9DK 155658B krympning ved høje temperaturer giver det glimmerholdi-ge materiale en væsentlig forbedring, som igen fører til forbedret TABEL III ildfasthed. Egenskaber Materiale Materiale uden glimmer med Glimmer Massefylde (kg/m^) 270 285 Trykstyrke (bar) 18,6 17,9 Bøjestyrke (bar) 4,68 4,13 Varmekrympning (%) 950°C 2,95 1,30 1000°C O to "tf 2,20 PATE NTRRAV9GB 155658B shrinkage at high temperatures gives the mica-containing material a significant improvement, which in turn leads to improved TABLE III refractory. Properties Material Material without mica with Mica Density (kg / m ^) 270 285 Compressive strength (bar) 18.6 17.9 Flexural strength (bar) 4.68 4.13 Heat shrinkage (%) 950 ° C 2.95 1.30 1000 ° CO to "tf 2.20 PATE NTRRAV 1. Fremgangsmåde ved fremstilling af en hydrotermisk hærdende, asbestfri, ildfast byggeplade af 20 kalkholdige og kiseljordholdige komponenter, cellulosefibre og i givet fald uorganiske fibre, kendetegnet ved, at blandingen tilsættes vermiculit og/eller glimmer i en mængde indtil 50 vægt% i forhold til det samlede faststofindhold i blandingen, og at de 25 kalkholdige og de kiseljordholdige komponenter reageres i en autoklave før og/eller efter blandingen og formningen .A process for preparing a hydrothermally curing, asbestos-free, refractory building board of 20 calcareous and siliceous components, cellulose fibers and, where appropriate, inorganic fibers, characterized in that the mixture is added to vermiculite and / or mica in an amount up to 50% by weight. the total solids content of the mixture, and that the calcareous and silicon-containing components are reacted in an autoclave before and / or after the mixing and molding. 2. Fremgangsmåde ifølge krav l, kendetegnet ved, at blandingen tilsættes cement.Process according to claim 1, characterized in that the mixture is added to cement. 3. Fremgangsmåde ifølge krav 1 eller 2, ken detegnet ved, at det uorganiske bindemiddel er tilstede i blandingen i en mængde, der andrager 70-90 vægtprocent af den samlede mængde af bindemiddel og fibre.Process according to claim 1 or 2, characterized in that the inorganic binder is present in the mixture in an amount of 70-90% by weight of the total amount of binder and fiber.
DK678774AA 1974-12-23 1974-12-23 Process for preparing a hydrothermal curing, asbestos-free, refractory mold body DK155658C (en)