DE955823C - Use of liquid methylpolysiloxanes for cements, malleable powders, etc. like - Google Patents
Use of liquid methylpolysiloxanes for cements, malleable powders, etc. likeInfo
- Publication number
- DE955823C DE955823C DES26306A DES0026306A DE955823C DE 955823 C DE955823 C DE 955823C DE S26306 A DES26306 A DE S26306A DE S0026306 A DES0026306 A DE S0026306A DE 955823 C DE955823 C DE 955823C
- Authority
- DE
- Germany
- Prior art keywords
- methylpolysiloxanes
- liquid
- cements
- malleable
- powders
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verwendung von flüssigen Methylpolysiloxanen für Zemente, verformbare Pulver u. dgl.Use of liquid methylpolysiloxanes for cements, malleable Powder and the like
Zusatz zum. Patent 906 999 Im Hauptpatent ist beschrieben, daß flüssige Methylpolysiloxane, welche die folgenden Eigenschaften aufweisen: a) Verhältnis von C H3/Si kleiner oder gleich I,4, b) Zahl der Siliciumatome zwischen 8 und 20, c) Siedetemperatur unter 8 mm zwischen 120 und 250°, d) unter der Einwirkung von kleinen Mengen von Bleinaphthenat bei gewöhnlicher Temperatur ein Gel zu ergeben, mit Vorteil bei zahlreichen Anwendungen die üblichen Siliciumharze ersetzen können,besonders in den Fällen, in denen es empfehlenswert ist, die Harze in Form sehr konzentrierter Lösungen oder selbst praktisch frei von Lösungsmitteln zu verwenden. Im Hauptpatent wird weiter ausgeführt, daß diese flüssigen Methylpolysiloxane, obwohl sie flüssig und wenig kondensiert sind, entgegen aller Erwartung Zemente ergeben, welche bei gewöhnlicher Temperatur abbinden. Die als Ausgangsmaterial dienenden flüssigen Methylpolysiloxane können z. B. nach dem Verfahren des Patents 840 395 erhalten werden. Addition to. Patent 906 999 The main patent describes that liquid Methylpolysiloxanes, which have the following properties: a) Ratio of C H3 / Si less than or equal to 1.4, b) number of silicon atoms between 8 and 20, c) boiling temperature below 8 mm between 120 and 250 °, d) under the action of small amounts of lead naphthenate to give a gel at ordinary temperature, can advantageously replace the conventional silicon resins in numerous applications, especially in those cases in which it is advisable, the resins in the form very concentrated To use solutions or even practically free of solvents. In the main patent it is further stated that these liquid methylpolysiloxanes, although they are liquid and are little condensed, contrary to all expectations, cements result, which at set at ordinary temperature. The liquid methylpolysiloxanes used as starting material can e.g. B. obtained by the method of patent 840,395.
Es wurde nun gefunden, daß auch Methylpolysiloxanharze mit einem Verhältnis CH3/Si kleiner als oder gleich I,4, welche mehr als 30 Gewichtsprozent solcher Methylpolysiloxane enthalten, welche die oben angeführten, unter a) bis d) genannten Eigenschaften besitzen, für die im Hauptpatent angegebenen Anwendungszwecke geeignet sind. Die erwähnten Methylpolysiloxanharze können z. B. nach dem Verfahren der Patentanmeldung S I9II2 IVc/39 c erhalten werden. Die nach diesem Verfahren erhaltenen Methylpolysiloxanharze sind Mischungen von Methylpolysiloxanharzen, bei denen das Verhältnis CH3/Si unter oder höchstens gleich I,4 ist, mit flüssigen Methylpolysiloxanen. It has now been found that methylpolysiloxane resins with a Ratio CH3 / Si less than or equal to 1.4, which is more than 30 percent by weight contain such methylpolysiloxanes, which the above, have the properties mentioned under a) to d) for those specified in the main patent Applications are suitable. The mentioned methylpolysiloxane resins can, for. B. can be obtained by the method of patent application S I9II2 IVc / 39 c. The after Methylpolysiloxane resins obtained by this process are mixtures of methylpolysiloxane resins, in which the ratio CH3 / Si is less than or at most equal to 1.4, with liquid Methylpolysiloxanes.
Die erwähnten Methylpolysiloxanharze können ebenso wie die im Hauptpatent verwendeten flüssigen Methylpolysiloxane mit Füllstoffen, wie z. B. Magnesia, Mennige, Bleiborat usw., versehen werden, und man kann daraus Massen herstellen, welche in unlöslicher, jedoch in der Wärme plastischer Form vorliegen. Diese Massen sind verformbar, und sie erhalten durch zusätzliches Erhitzen ihre endgültige Form und Konsistenz. The methylpolysiloxane resins mentioned, like those in the main patent used liquid methylpolysiloxanes with fillers, such as. B. Magnesia, red lead, Lead borate, etc., and can be used to produce masses which are in insoluble, but in the warmth plastic form. These masses are malleable, and additional heating gives them their final shape and consistency.
Die folgenden Beispiele sollen die Erfindung näher erläutern. Die angegebenen Teile bedeuten Gewichtsmengen. The following examples are intended to explain the invention in more detail. the specified parts mean amounts by weight.
Beispiel I Man hydrolysiert eine Lösung eines Gemisches von 104 Teilen Methylchlorsilanen der Dichte I,2I7 und mit einem Verhältnis CH3/Si gleich I,25 in 255 Teilen Äther, mit 90 Teilen Wasser. Die Hydrolyse erfolgt nach der in der Patentanmeldung S I9II2 IVc!39 c beschriebenen Weise. Nach der Isolierung des erhaltenen Harzes werden 6 Teile desselben mit 10 Teilen Bleiglätte vermischt. Die erhaltene Masse bindet innerhalb von 48 Stunden bei 250 ab und ergibt einen sehr harten Zement. Example I A solution of a mixture of 104 parts is hydrolyzed Methylchlorosilanes with a density of I, 2I7 and a CH3 / Si ratio equal to I, 25 in 255 parts of ether, with 90 parts of water. The hydrolysis takes place after in the Patent application S I9II2 IVc! 39 c described manner. After isolating the obtained Resin 6 parts of the same are mixed with 10 parts of black lead. The received Compound sets within 48 hours at 250 and makes a very hard cement.
Beispiel 2 Man vermischt 6 Teile des, wie im vorhergehenden Beispiel angegeben, hergestellten Harzes mit 10 Teilen eines Füllstoffes, der aus einer glasartigen Masse mit folgenden Bestandteilen zusammengesetzt ist: 15,6 0(o Borsäureanhydrid, 8o,6 0to Pos04 und 3,5 0/o Kaolin. Die so hergestellte Masse bindet innerhalb von 20 Stunden bei einer Temperatur von 20 bis 25° ab und ergibt einen sehr harten Zement. Example 2 6 parts of the are mixed as in the previous example indicated, produced resin with 10 parts of a filler consisting of a vitreous The mass is composed of the following components: 15.6 0 (o boric anhydride, 8o, 6 0to Pos04 and 3.5 0 / o kaolin. The mass produced in this way binds within 20 hours at a temperature of 20 to 25 ° and results in a very hard cement.
Beispiel 3 Zu einem Teil des nach Beispiel I hergestellten Harzes gibt man 3 Teile des in Beispiel 2 beschriebenen Füllstoffes. Die erhaltene Masse bindet innerhalb von 48 Stunden bei 25° ab und ergibt einen sehr harten Zement. Example 3 For a part of the resin produced according to Example I. 3 parts of the filler described in Example 2 are added. The mass obtained sets within 48 hours at 25 ° and results in a very hard cement.
PATENTANSPÜCHE: I. Weitere Ausbildung des Hauptpatents 906 999, gekennzeichnet durch die Verwendung von Methylpolysiloxanharzen, bei denen das Verhältnis CH3/Si kleiner oder gleich I,4 ist und die mehr als 30 Gewichtsprozent an Methylpolysiloxanen gemäß Patent 840 395 enthalten, als Grundlage für Zemente, verformbare Pulver und ähnliche Dichtungsmassen, die in der Wärme oder in der Kälte abbinden. PATENT CLAIMS: I. Further development of the main patent 906 999, marked through the use of methylpolysiloxane resins in which the ratio CH3 / Si is less than or equal to 1.4 and more than 30 percent by weight of methylpolysiloxanes contained according to patent 840 395, as a base for cements, malleable powders and similar sealants that set in hot or cold conditions.
Claims (1)