DE837369C - Process for the production of colored floor and wall coverings - Google Patents
Process for the production of colored floor and wall coveringsInfo
- Publication number
- DE837369C DE837369C DEG275A DEG0000275A DE837369C DE 837369 C DE837369 C DE 837369C DE G275 A DEG275 A DE G275A DE G0000275 A DEG0000275 A DE G0000275A DE 837369 C DE837369 C DE 837369C
- Authority
- DE
- Germany
- Prior art keywords
- binder
- emulsifier
- mineral
- mixture
- colored
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zur Herstellung farbiger Boden- und Wandbelagmassen Es ist bereits bekannt, unter Verwendung bestimmter Harze, Wachse und Alkalien, gegebenenfalls unter Zusatz von Pech, Bitumen und staubfeinem Mineral, ein festes, konzentriertes Emulgierungsmittel herzustellen, (las so zusammengesetzt ist, daß es nach dem #\liederaufschmelzen am Ort der Verwendung die Herstellung auch auf feuchtem Gestein gut haftender, in der Kälte viskoser, bituminöser, wäßriger Emulsionen erlaubt. Gegebenenfalls wird dem Emulsionskonzentrat Pech oder Bitumen, evtl. auch Mineralstaub, zugesetzt, damit es zu bestimmten Formkörpern, z. 13. ähnlich den Mastixbroten, vergossen «werden kann. Beim Versand in Blechtrommeln ist diese Maßnahme nicht notwendig, jedoch erscheint es auch dann zweckmäßig, das Konzentrat vor der Zugabe zum erwärmten, bituminösen Bindemittel aufzuschmelzen, um unter Rühren eine möglichst schnelle und gleichmäßige Verteilung im Teer oder Bitumen vor der Beimischung des Emulsionswassers zu ermöglichen.Process for the production of colored floor and wall coverings It is already known, using certain resins, waxes and alkalis, if appropriate with the addition of pitch, bitumen and dust-fine mineral, a solid, concentrated one To produce emulsifying agent, (read is composed in such a way that after melting it is At the place of use the production also adheres well to damp rock, in the cold of viscous, bituminous, aqueous emulsions. If necessary, will Pitch or bitumen, possibly also mineral dust, added to the emulsion concentrate, so that it to certain moldings, z. 13. Similar to the mastic bread, "potted" can. When shipping in tin drums, this measure is not necessary, but appears it is then also advisable to add the concentrate to the heated, bituminous Melt the binding agent in order to achieve a rapid and uniform process while stirring To enable distribution in the tar or bitumen before adding the emulsion water.
Nach der Erfindung wurden in Weiterentwicklung des bekannten Verfahrens die überraschenden Feststellungen gemacht; dlaß Erdöl-, Bitumen-, Teer-und Pechextrakte sowie Harze und' Wachse in gleicher oder ähnlicher Art emulgiert werden können, und ferner, daß es zum Umhüllen feuchten und durchnäßten Gesteins, vornehmlich staubhaltiger, feinkörniger Mineralmassen, nicht notwendig ist, die Bindemittel-in-Wasser-Emulsion vor dem Vermischen mit dem Gestein fertigzustellen, sondern daß diese während des Mischvorganges mit dem Gestein zugleich entwickelt wird'.According to the invention, in a further development of the known method the surprising findings made; dlaß petroleum, bitumen, tar and pitch extracts as well as resins and waxes can be emulsified in the same or a similar manner, and further that it is used to cover damp and soaked rock, especially dusty, Fine-grain mineral masses, the binder-in-water emulsion is not necessary to be completed before mixing with the rock, but rather that this is developed simultaneously with the rock during the mixing process'.
Es braucht also nur das Gemisch von Emulsionskonzentrat und bituminösen oder anderen klebenden I')iiicleniittelri dein nassenGestein unter evtl. weiterer \\'asserzug.ihe beigemischt werden, und es entsteht während des Umhüllungsvorganges zugleich unter Ein«-irkung des Emulgators, gvgel)enenfalls auch zusätzlich des Gesteinsstaubes die Bindemittelernulsion auf der Gesteinsoberfläche. Hierbei kann zweckmäßig erst ein Teil des mit dem Emulgator verrührten 13itideniittels und nach weitereinWasserxu,:atz der restliche Teil zugesetzt werden.So all you need is the mixture of emulsion concentrate and bituminous or other adhesive I ') iiicleniittelri your wet rock under possibly other \\ 'asserzug.ihe are added, and it arises during the wrapping process at the same time with the effect of the emulsifier, possibly also of the rock dust the binder emulsion on the rock surface. This can only be useful a part of the 13itideniittels mixed with the emulsifier and afterwards in waterxu,: atz the remaining part can be added.
Nach der Erfindung ist es auch möglich, bei .\nwendung von Natur aus gefärbter Gesteinsinaterialien und ausreichend heller bzw. aufgehellter llindernittel auf Harz- oder \\'achsbasis bzw. 1'olymerisationsprodukte auf Kunststoffbasis, selbst \-i>ri durch Extraktion von unlöslichen schwarzen und farbstoffschluckenden, kohlenstoffartigen Bestanciteilen befreitem Teer, Pech oder Bitumen farbige \'lirieral-13indemittel-\\'asser-Gemisclie auf Vniulsionsbasis herzustellen, deren Farbton durch l,'eiiniscliurig von anorganischen oder organischen l#arlistoffl>ulvern oder Farbstofflösungen verstärkt werden kann.According to the invention, it is also possible to use it by nature colored rock materials and sufficiently lighter or lightened emollients on a resin or axis basis or polymerisation products on a plastic basis, even \ -i> ri by extraction of insoluble black and dye-swallowing, carbon-like ones Components of freed tar, pitch or bitumen colored lirieral binders - water mixtures on the basis of emulsions, the hue of which is unique to inorganic ones or organic l # arlistoffl> ulvers or dye solutions can be strengthened.
Ks werden so außerordentlich leicht im kalten Zustand vierteilbare, breiartige, farbige Massen erzeugt, die nach dem Brechen der labilen Emulsion und Abdunsten des Wassers einen absolut dichten, festen, wasserundurchlässigen und wasserabweisenden Belag, der auf jedem Untergrund fest hält, ergelren. Das Brechungsvermögen kann durch die Ztisainniensetzurig und die Menge des, Emulgaxors variiert werden. Es wird auf diese Weise ermöglicht, daß der farbige bittiniinös-wäßrige Emulsionsbrei sowohl am Ort der Verwendung, wie an einer zentralen Aufbereitungsstelle, hergestellt werden kann. Vorbedingung für die Anwendung im Freien ist trockenes, möglichst sonniges Wetter, wie es auch bei normalen Straßenbau- oder Anstricharbeiten mit Bitumenemulsionen der Fall ist. Der farbige Emulsionsbrei darf nicht zu stark aufgetragen werden, damit keine Schwindrisse entstehen. Bei stärkeren Schichten als 3 bis 4 mm ist mehrmaliges Auftragen zweckmäßig. Die zweite Schicht haftet fest auf der abgebundenen unteren Schicht und bildet mit dieser ein einheitliches Ganzes. Beispiele Beispiel für die Herstellung eines Emulsionskonzentrates 0% rnittelliartes, ausreichend helles Kumaronharz werden mit 4o% Holzharz derselben Beschaffenheit und 2o% Sulfatpech (Destillationsrückstand des rohen "rall('ils) unter Ruhren zusaininengeschmolzen, worauf mit einer 30%igen, aus gleichere Teilen Ätznatron und Ätzkali bestehenden Alkalilauge verseift wird. Es wird nach dem Verdampfen des Wassers so viel überschüssiges Harzgemisch zugegelyen, daß eine im heißflüssigen Zustand in Trommeln oder sonstigen Gefäßen bzw. in Formen vergießbare gelbe bis braune zähe Masse entsteht.In this way, Ks are extremely easy to divide into four parts when cold, pasty, colored masses produced after breaking the unstable emulsion and Evaporation of the water creates an absolutely tight, solid, water-impermeable and water-repellent The surface that sticks to any surface will settle. The refractive power can can be varied by the Ztisainnienetzurig and the amount of, emulsifier. It in this way enables the colored bitinous-aqueous emulsion slurry both at the place of use and at a central processing point can be. A prerequisite for outdoor use is dry and as sunny as possible Weather, as it is with normal road construction or painting work with bitumen emulsions the case is. The colored emulsion paste must not be applied too heavily, so that no shrinkage cracks occur. In the case of thicker layers than 3 to 4 mm, several times are required Apply appropriately. The second layer adheres firmly to the tied lower one Layer and forms with it a unified whole. Examples example of the Production of an emulsion concentrate of 0% medium-sized, sufficiently light-colored coumarone resin are made with 4o% wood resin of the same consistency and 2o% sulphate pitch (distillation residue of the raw "rall ('ils) melted together with stirring, whereupon with a 30%, alkali lye consisting of equal parts caustic soda and caustic potash is saponified. After the water has evaporated, so much excess resin mixture is added, that one in the hot liquid state in drums or other vessels or in forms Pourable yellow to brown viscous mass is created.
z. Beispiel für die Herstellung eines Gemisches von färbbarem bituminösem Bindemittel und Eniulsionskonzentrat nach Beispiel i 75% eines licißflüssig gemachten, gleichmäßigen Gemisches von 8o% durch Extraktion von unlöslichen farbstoffschluckenden Bestandteilen befreiten Steinkohlenteerpechs oder Erdölbitumens und 20% Kolophonium oder Holzharz werden zwecks Herabsetzung des Erweichungspuriktes mit 25% über 200° C siedendem Teer, im Fall der Anwendung von Extraktbitumen, auch -Nlirieralölen vermischt, so .daß ein für die Herstellung farbiger bituminöswäßriger Massen geeignetes, ausreichend 'helles klebendes Bindemittel von der Konsistenz eines zähflüssigen Straßenteers oder @erschnittbitum@ens entsteht. In dieses auf etwa 7o bis 8o° erwärmte Bin@deniittelgernisch werden 2% durch Erhitzen verflüssigtes Emulsionskonzentrat von im Beispiel i angegebener Zusammensetzung gleichmäßig eingerührt. 3. Beispiel für die Herstellung eines liitumitiös-wäßrigen, emulgierten und gefärbten Mineralgemisches unter Verwendung des mit Emulsionskonzentrat nach Beispiel i versetzten Bindemittelgemisches nach Beispiel 2 4o% staubhaltiger, kornabgestufter und gelbroter Porphyrbrechsand der Körnung o bis 2 mm werden mit 2o% Kalksteinbrechsand derselben Kornabstufung, 20% feinkörnigem und lehmfreiem Quarzgrubensand, i S % Kalksteinmehl und 50/0 rotem Farbstoffpulver, z. B. Eisenoxydrot, in einer Mischmaschine, die mit Knetflügeln versehen ist, gründlichst durcheinandergemischt, worauf io bis 12% des nach Beispiel 2 mit 2% Emulsionskonzentrat vermischten Bindemittels zugesetzt werden. Darauf wird das \lineral-Farl>stoff-Bindemittel-Gemisch mit 20% Wasser so lange nachgemischt, bis ein vollständig homogenes, breiartiges Gemenge entstanden ist.z. Example of the preparation of a mixture of colorable bituminous Binder and emulsion concentrate according to Example i 75% of a liquefied, uniform mixture of 80% by extraction of insoluble dye-swallowing substances Components freed coal tar pitch or petroleum bitumen and 20% rosin or wood resin to reduce the softening purictes with 25% over 200 ° C boiling tar, in the case of using extract bitumen, also -Nlirieral oils mixed so .that a suitable for the production of colored bituminous aqueous masses, Sufficiently light-colored adhesive binder with the consistency of a viscous one Road tar or @ cutting bitum @ ens is created. In this heated to about 7o to 8o ° Bin @ deniittelgernisch 2% emulsion concentrate liquefied by heating of the composition given in example i, stirred in evenly. 3rd example for the production of a liitumitiös-aqueous, emulsified and colored mineral mixture using the binder mixture mixed with emulsion concentrate according to Example i according to example 2 40% dusty, grain-graded and yellow-red porphyry crushed sand the grain size o to 2 mm are mixed with 2o% crushed limestone sand of the same grain size, 20% fine-grain and clay-free quartz pit sand, i S% limestone powder and 50/0 red Dye powder, e.g. B. iron oxide red, in a mixer with kneading blades is provided, thoroughly mixed up, whereupon io to 12% of the example 2 binders mixed with 2% emulsion concentrate are added. On it will the \ lineral-dye-binder-mixture with 20% water is mixed up for so long until a completely homogeneous, pulpy mixture has arisen.
Um den Mischvorgang zu beschleunigen, wird zweckmäßig erst die Hälfte des Bindemittels, dann die Hälfte des Wassers zugegeben, worauf nacheinander eine Zugabe der restlichen Mengen an Bindemittel und Wasser erfolgt. Die auf diese Art und Weise in einem einzigen Misch- und Knetvorgang hergestellte wäßrige Mineral-Farbstoff-Bindiemittelpaste ist infolge der stabilisierenden Wirkung des Emulgators längere Zeit haltbar und braucht deshalb nicht am Ort der -Verwendung hergestellt zu werden. Sie verträgt mehrstündige Transporte von einer zentralen Aufbereitungsstellie, insbesondere, wenn die 1\löglichkeit besteht während des Transportes das Gemenge durchzuführen, ähnlich wie es bei Gußasphalt- und \-lastixmassen der Fall ist.In order to speed up the mixing process, it is expedient to only use half of the binder, then half of the water is added, whereupon one after the other The remaining amounts of binder and water are added. That way and aqueous mineral-dye-binder paste produced in a single mixing and kneading process is stable for a long time due to the stabilizing effect of the emulsifier and therefore does not need to be produced at the place of use. She tolerates Transports lasting several hours from a central processing point, in particular, if the possibility exists to carry out the batch during the transport, similar to what is the case with mastic asphalt and plastic compounds.
Das Brechen der Emulsion und damit Abscheiden des 1\'assers geschieht unmittelbar nach dem Verteilen auf Boden- oder Wandflächen. Eine Reemulgierung tritt nicht ein.The breaking of the emulsion and thus separation of the 1 \ 'water occurs immediately after distributing on floor or wall surfaces. One Re-emulsification does not occur.
Claims (12)