DE685788C - Plastic compound for the printing form production of boxes, lids and filler closures for electrical collectors using vegetable pitch - Google Patents
Plastic compound for the printing form production of boxes, lids and filler closures for electrical collectors using vegetable pitchInfo
- Publication number
- DE685788C DE685788C DESCH112038D DESC112038D DE685788C DE 685788 C DE685788 C DE 685788C DE SCH112038 D DESCH112038 D DE SCH112038D DE SC112038 D DESC112038 D DE SC112038D DE 685788 C DE685788 C DE 685788C
- Authority
- DE
- Germany
- Prior art keywords
- pitch
- boxes
- silicate
- lids
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Plastische Masse für die Druckforinfabrikation von Kästen, Deckeln und Einfüllverschlüssen für elektrische Sainn-der unterVerwendung von vegetabilischem Pech Die Erfindu.na bezieht sich auf die Herstellu > ng von Sammlerkästen u.dgl., wobei berücksichtigt werden muß, daß der Ausdruck Kasten in dieser Beschreibung auch die Deckel und Verschlüsse einbegreift, die dazu verwandt werden, gewisse Sammlerarten zu verschließen.Plastic mass for Druckforinfabrikation of boxes, lids and filler caps for electrical-Sainn of using pitch vegetabilischem The Erfindu.na refers to manufac> ng of collector boxes, etc., in which it must be considered that the expression box in this specification also includes the lids and closures that are used to close certain types of collectors.
Es sind bereits Herstellungsverfahren für Sammlerkästen bekanntgeworden, wobei der als Bindemittel verwendete Bestandteil au,s einer besonderen Mischung von Asphalt und Kohlenteerpech, d.h. aus rein mineralischen Körpern, besteht. Beispitlsweise kann eine Mischung unter Verwendung der als Stanolit und Gilsonit bekannten Asphaltarten und einem Zusatz von Kohlenteerpech hergestellt sein. Ferner ist vorgeschlagen worden, hierfür ein Gemisch von Mineralpech (Petroleumpech) und Bitumen unter Beimengung von Cellulose, wie Baumwollabfälle, Sägespäne,-Holzwolle u.dgl., zu verwenden. Auch hat man ein vegetabilisches Pech, nämlich Baumwollölpech, an Stelle von Erdölpech bei der Herstellung von Sammlerkästen angewandt, um die Masse geschmeidig zu machen.Manufacturing processes for collector's boxes have already become known, the constituent used as a binder being a special mixture consists of asphalt and coal tar pitch, i.e. of purely mineral bodies. For example can be a mixture using the types of asphalt known as stanolite and gilsonite and an addition of coal tar pitch. It has also been suggested that for this purpose a mixture of mineral pitch (petroleum pitch) and bitumen with admixture of cellulose, such as cotton waste, sawdust, wood wool and the like. To use. Even if you have a vegetable pitch, namely cotton oil pitch, instead of petroleum pitch used in the manufacture of collector's boxes to make the mass pliable.
Alle vorstehenden Materialzusammensetzungen weisen Nachteile auf, die darin bestehen, daß z.B. die Stoffe mineralischen Ursprungs dazu neigen, ihrer natürlichen Beschaffenheit wegen beim Fabrikationsgang an Werkzeugen und Modellen anzukleben. Sie sind außerdem nicht in der Lage, in zufriedenstellender Weise dem fortwährenden Angriff der Schwefelsäure standzuhalten. Setzt man andererseits diese mineralischen Stoffe einer besonderen Behandlung aus, um ihre Neigung zum Ankleben zu beheben, so werden die Massen leicht brüchig. Diese für die praktische Verwendung der genannten Stoffe sehr ungünstigen Eigenschaften werdendurch die Materialzusammensetzung nach der Erfindung völlig beseitigt.All of the above material compositions have disadvantages, which consist in the fact that substances of mineral origin, for example, tend to change their natural condition due to the manufacturing process on tools and models to stick. They are also unable to do this in a satisfactory manner to withstand constant attack by sulfuric acid. On the other hand, if you set this Mineral substances undergo a special treatment to reduce their tendency to stick to fix, the masses are easily brittle. These for practical use of the substances mentioned have very unfavorable properties due to the material composition completely eliminated according to the invention.
Gemäß der Erfindung besteht der Werkstoff aus unmittelbar aus den Hölzern der Laubbäume gewonnenem Pech, das frei von natürlichen Harzen ist, einem faserigen Bindungsstoff und einem Silicat als Füllmaterial. Es hat sich gezeigt, daß von den verschiedenen Holzpechsorten vornehmlich das von der Buche stammende Pech dem Werkstoff,#, die Die gewünschten durch die plastische Eigenschaften Masse verleiht' gemäß Erfindung erzielten Vorteile bestehen viDr allem darin, daß ein Ankleben des Preßmaterials* an die Druckformen vermieden wird, wobei trotzdem die völlige Geschmeidigkeit des -Materials erhalten bleibt.According to the invention, the material consists of pitch obtained directly from the woods of the deciduous trees, which is free of natural resins, a fibrous binding substance and a silicate as a filler material. It has been shown that of the various types of wood pitch, primarily the pitch from the beech tree, the material, #, which gives the desired mass through the plastic properties' advantages achieved according to the invention mainly consist in the fact that the pressing material * adheres to the printing forms is avoided, yet the total flexibility of the - material is retained.
Diese gemäß der Erfindung verwendeten Peche sind frei von Fetten, und es werden vorzugsweise diejenigen Peche ausgesucht, die gleichzeitig arm an Harzen oder frei davon sind. Die obenerwähnten Holzpeche haben außerdem die sehr wichtige Eigenschaft, daß man sie einer Behandlung zur Entfernung der Harze und, dadurch zur Beseitigung jeglicher Neigung zum Kleben unterwerfen kann, ohne daß das Pech brüchig wird. Außerdem haben diese Peche denVorteil, daß sie eine den elektrischen Strom nicht leitende Masse ergeben, wenn sie aus irgendeinem Grunde verkohlen, während das mineralische Pech usw. in diesem Fall stromleitend wird.These pitches used according to the invention are free from fats, and it is preferred to choose those pitches that are poor at the same time Resins or free thereof. The wood pitch mentioned above also has the very important property that it can be subjected to a treatment to remove the resins and, can thereby be subjected to the elimination of any tendency to stick without the pitch becomes brittle. In addition, these pitches have the advantage that they have the electrical properties Electricity will result in non-conductive mass if for any reason they char while the mineral pitch etc. becomes conductive in this case.
Unter diesen Bedingungen kann man die genannten Holzpeche mit einem an sich bekannten Füllmaterial, vorzugsweise mit einem Silicat und einem faserigen Bindestoff, mischen, der organisch wie auch anorganisch sein kann. Diese Mischung kann man derart im wannen Zustande formen, daß sie Kästen ergibt, die der Einwirkung der Schwefelsäure Widerstand leisten. Die so geformten Kästen besitzen auch eine große mechanische Festigkeit und ähneln im Aussehen den Kästen, die aus Gummi oder mineralische.n Pechen hergestellt werden, unterscheiden sich aber beträchtlich von diesen durch die Form ihres Bruches und durch den Geruch, den ein ganz frischer Bruch hat.Under these conditions you can use the mentioned wood pitch with a known filling material, preferably with a silicate and a fibrous Binder, mix, which can be organic as well as inorganic. This mixture can be shaped in such a way in the tub that it gives boxes that are subject to action resist the sulfuric acid. The boxes so shaped also have one great mechanical strength and resemble in appearance the boxes made of rubber or mineral.n pitches are produced, but differ considerably from this by the shape of its break and by the smell that a very fresh one Has rupture.
Wenn auch die genannten ftolzpeciie, die frei von Harzen sind, zufriedenstellende Ergebnis.se zeitigen, -wenn, die Formmischung in der soeben erwähnten Weise hergestellt wird, hat man herausgefunden, daß man die mechanische Festigkeit des Werkstoffes noch weiter erhöhen kann, wenn man- ihm eine gewisse Menge eines künstlichen Harzes beigibt. Auch kann in gewissen Fällen vorteil hafterweise dem Holzpech bei. der Zusammensetzung der Masse eine gewisse Menge des unter der Bezeichnung Gilsonit be- kannten Asphalts beigegeben werden, ganz gleich, ob das künstliche Harz vorhanden ist oder nicht. Die Verwendun- von Gilsonit ist bei der Herstellung von Sammlerkästen unter Verwendung mineralischer Peche an sich bereits bekannt. Neu ist dagegen die Beimengung dieses Stoffes zu plastischen Massen, die Holzpech und namentlich Pech der Laubholzbäume enthalten.Even if the above-mentioned wood speciies, which are free from resins, produce satisfactory results - if the molding mixture is produced in the manner just mentioned, it has been found that the mechanical strength of the material can be increased still further if one - adding a certain amount of an artificial resin to it. In certain cases, the pitch can also be advantageous. a certain amount of the asphalt known as Gilsonite can be added to the composition of the mass, regardless of whether the artificial resin is present or not. The use of gilsonite is already known per se in the manufacture of collector's boxes using mineral pitches. What is new, however, is the addition of this substance to plastic masses that contain wood pitch and especially pitch from the hardwood trees.
Um ein Holzpech zu erhalten, das in der I #LInge ist, für unbestimmte Zeit einer Schwe-'.-i;l'säurelösung von der Dichte 1,3 bei einer "itniperatur von 4o bis 45' C Widerstand zu leisten, wie es bei Kraftfahrzeugsammlern der Fall ist, wählt man vorteilhafterweise, wie bereits oben erwähnt, unmittelbar aus Hölzern der Laubbäume gewonnene Peche, da sie an sich schon sehr arm an natürlichen Harzen bzw. vollkommen harzfrei sind. Es werden vorzugsweise diejenigen Peche verwandt, die einen Schmelzpunkt von etwa ioo' C aufweisen. Diese Peche stellen die Rückstände einer Destillation dar, die so weit geführt wird, bis die Eigenschaften der Rückstände den weiter oben angeführten Bedingungen entsprechen.In order to obtain a wood pitch which is in the length, to resist a sulfuric acid solution of a density of 1.3 at a temperature of 40 to 45 ° C for an indefinite period of time If this is the case with motor vehicle collectors, it is advantageous, as already mentioned above, to choose pitches obtained directly from wood of deciduous trees, since they are inherently very poor in natural resins or completely resin-free about 100 ° C. These pitches represent the residues of a distillation, which is carried out until the properties of the residues correspond to the conditions given above.
Besonders gut eignet sich für die Herstellung von Sammlerkästen u. dgl. das Pech der Buche in Form von Rückständen, von denen alle Stoffe, die schädlich oder ungeeignet sein könnten, abgetrennt sind.It is particularly suitable for the production of collector's boxes and the like. Like. The pitch of the beech in the form of residues, all of which are substances harmful or may be unsuitable.
Vorteilhafterweise verwendet man Rückstände, die einen Schmelzpunkt um etwa ioo' C besitzen, ohne daß die Erfindung auf diese Zahl beschränkt werden soll, da die Wahl des Schmelzpunkts ja nach den Bedingungen, unter denen das Erzeugnis gebraucht werden soll, der Fachwelt überlassen wird.It is advantageous to use residues which have a melting point of about 100 ° C. , without the invention being restricted to this number, since the choice of the melting point is left to the expert depending on the conditions under which the product is to be used.
Eine vorteilhafte Zusammensetzung der Mischung ist folgende:
Der faserige Stoff kann, -wie bereits erwähnt, anorganischen Ursprungs sein, wie beispielsweise Asbest, oder organischen, wie beispielsweise Baumwolle, Roßschweifhaare, Wolle, oder es kann auch eine Mischung anorganischer und organischer, faseriger Stoffe verwendet werden. Für den Fall, daß der Mischung ein künstliches Harz beigegeben wird, ist es vorteilhaft, dafür ein C Polymerisationsprodukt auszuwählen, das geschmolzen und wieder geschmolzen werden kann, um der plastischen Masse nicht die vorteilhafte Eigenschaft zu nehmen, die darin besteht, daß sie nach dem Pressen nochmals geschmolzen werden kann. Die in der Zusammensetzung enthaltenen Bestandteile werden in einer Mischtrommel in heißem Zustande so lange gemischt, bis eine gleichmäßige Masse entsteht. Diese Masse kann danach nötigenfalls in erwärmten und geschlossenen Behältern aufbewahrt werden,bis sie zur eigentlichen Verwendung gelangt. Man entnimmt den Behältern die notwendige Menge, um den gewünschten Kasten zu formen. Diese Menge wird geknetet, wobei Wärmeverluste vermieden werden müssen, und wird danach einer Form zugeführt, die erwärmt und gekühlt werden kann und in der die Masse unter Druck gepreßt wird. Ist die Form abgekühlt, so entnimmt man ihr den ferti-O'epreßten Kasten.The fibrous material may - be as already mentioned inorganic origin, such as asbestos, or organic, such as cotton, Roßschweifhaare, wool, or it can also be a mixture of inorganic and organic, fibrous materials are used. In the event that an artificial resin is added to the mixture, it is advantageous to select a C polymerization product that can be melted and remelted so as not to deprive the plastic mass of the advantageous property that it is after Pressing can be melted again. The ingredients contained in the composition are mixed in a hot mixer drum until a uniform mass is obtained. If necessary, this mass can then be stored in heated and closed containers until it is actually used. The necessary quantity is removed from the containers to form the desired box. This amount is kneaded, whereby heat losses must be avoided, and is then fed to a mold which can be heated and cooled and in which the mass is pressed under pressure. Once the mold has cooled down, the ready-made box is removed from it.
Wie bereits erwähnt, kleben die auf Grund der erfindungsgemäßen Zusammensetzung nach dem beschriebenen Verfahren hergestellten Kästen während des Abdrückens weder an der Form noch an den Werkzeugen an. Gleichzeitig sind sie säurebeständig, lichtbeständig und widerstandsfähig gegen mechanische Stöße. Sie besitzen einen metallischen Klang, wenn sie angestoßen werden, und haben eine verhältnismäßig hohe Druckfestigkeit und Härte.As already mentioned, due to the composition according to the invention, they stick boxes manufactured according to the method described neither during the pressing on the mold or on the tools. At the same time, they are acid-resistant, lightfast and resistant to mechanical shocks. They have a metallic sound when they are hit and have a relatively high compressive strength and hardness.
Claims (2)