DE674626C - Process for the separate production of tantalum and niobium from alloys containing tantalum, niobium and other metals - Google Patents
Process for the separate production of tantalum and niobium from alloys containing tantalum, niobium and other metalsInfo
- Publication number
- DE674626C DE674626C DES131185D DES0131185D DE674626C DE 674626 C DE674626 C DE 674626C DE S131185 D DES131185 D DE S131185D DE S0131185 D DES0131185 D DE S0131185D DE 674626 C DE674626 C DE 674626C
- Authority
- DE
- Germany
- Prior art keywords
- niobium
- tantalum
- metals
- alloys containing
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zur getrennten Gewinnung von Tantal und Niob aus Tantal, Niob und andere Metalle enthaltenden Legierungen Die vorliegende Erfindung bezieht sich auf die Behandlung von Tantal und Niob enthaltenden Ausgangsstoffen.Process for the separate extraction of tantalum and niobium from tantalum, The present invention relates to alloys containing niobium and other metals on the treatment of raw materials containing tantalum and niobium.
Das Ziel der Erfindung ist die Trennung des Tantal von dem Niob oder mindestens eine wesentliche Anreicherung jedes einzelnen der beiden Elemente in zwei verschiedenen Erzeugnissen.The aim of the invention is to separate the tantalum from the niobium or at least a substantial enrichment of each of the two elements in two different products.
Gemäß der Erfindung wird eine Tantal und Niob sowie ein anderes Metall oder Metalle enthaltende Legierung geschmolzen, und darauf wird eine bestimmte Menge Oxyde oder oxydierter Verbindungen, welche befähigt sind, das Tantal selektiv in bezug auf das Niob zu verdrängen, zugefügt, so daß nach Schmelzen dieser letzteren und erfolgter Reaktion einerseits eine Nioblegierung und andererseits eine Tantalschlacke erhalten wird.According to the invention, a tantalum and niobium as well as another metal or alloy containing metals is melted, and a certain amount is put on it Oxides or oxidized compounds which are capable of selectively converting the tantalum into with respect to the niobium, added, so that after melting the latter and a reaction that has taken place, on the one hand, a niobium alloy and, on the other hand, a tantalum slag is obtained.
Als Oxyde oder oxydierte Verbindungen, welche befähigt sind, die besagte selektive Verdrängung zu bewirken, kann man die oxydierten Verbindungen von Niob- und/oder die oxydierten Verbindungen eines oder mehrerer Metalle der Eisengruppe Eisen, Mangan, Chrom, Kobalt, Nickel anführen.As oxides or oxidized compounds which are capable of the said To bring about selective displacement, one can use the oxidized compounds of niobium and / or the oxidized compounds of one or more metals of the iron group List iron, manganese, chromium, cobalt, nickel.
Das Ausgangsgut kann vor dem Schmelzen mit oxydierten Verbindungen, welche fein zerkleinert worden sind, vermischt werden.Before melting, the starting material can be mixed with oxidized compounds, which have been finely ground, are mixed.
Wenn man Oxyde des Niobs verwendet, so ist die Menge dieser Oxyde, welche zugefügt wird, vorzugsweise derart zu wählen, daß das Tantal der Legierung im wesentlichen durch die Nioboxyde oder oxydierten Verbindungen verdrängt wird. Man erhält auf diese Weise eine Nioblegierung sowie eine Tantalschlacke, und diese Schlacke kann irgendeiner bekannten metallurgischen Behandlung unterworfen werden, mit dem Ziel, ihr das Tantal. in Form eines handelsgängigen Erzeugnisses (als Metall, Legierung, Carbid oder Oxyd) zu:entziehen. Das Ausgangsgut kann in einem Eisentantalniob bestehen, und in diesem Falle wird es wie oben beschrieben behandelt.If one uses oxides of niobium, the quantity of these oxides is which is added, preferably to be selected in such a way that the tantalum of the alloy is essentially displaced by the niobium oxides or oxidized compounds. In this way, a niobium alloy and a tantalum slag are obtained, and these Slag can be subjected to any known metallurgical treatment, with the aim of you the tantalum. in the form of a commercially available product (as metal, Alloy, carbide or oxide) to: withdraw. The initial material can consist in an iron tantalum niobium, and in this case it becomes as described above treated.
Das Ausgangsgut kann auch aus oxydierten Verbindungen des Tantals und Niobs bestehen, und es kann dann einer reduzierenden Schmelzung unterworfen werden, die durch irgendein bekanntes Mittel bewirkt wird, um die Elemente Tantal und Niob in einer Tantal-Niob-Legierung anzureichern. Diese Legierung wird dann dem oben beschriebenen Verfahren unterworfen.The starting material can also consist of oxidized compounds of tantalum and niobium exist, and it can then be subjected to a reducing fusion which is effected by any known means to produce the elements tantalum and enrich niobium in a tantalum-niobium alloy. This alloy is then subject to the procedure described above.
Das Schmelzen kann in jedem geeigneten metallurgischen Ofen erfolgen, vorzugsweise in einem elektrischen Ofen.Melting can be done in any suitable metallurgical furnace, preferably in an electric oven.
Die oxydierten Verbindungen können in Form von Schlacke verwendet werden. Wenn man oxydierte Verbindungen aus der Eisengruppe verwendet, geht das oxydierte Tantal während der Behandlung in eine Schlacke. über, und man erhält andererseits eine Nioblegierung, z. B. Eisenniob, welche an Tantal verarmt ist.The oxidized compounds can be used in the form of slag will. If you use oxidized compounds from the iron group, you can oxidized tantalum into a slag during treatment. over, and one obtains on the other hand a niobium alloy, e.g. B. iron niobium, which is depleted in tantalum.
Die oxydierten Verbindungen können in festem Zustande oder in geschmolzenem Zustande der vorher geschmolzenen Beschickung hinzugefügt werden, oder es können auch die Bestandteile der Beschickung der Schmelzung in inniger Mischung unterworfen werden, nachdem sie auf die gewünschte Feinheit gebracht worden sind.The oxidized compounds can be in the solid state or in the molten state States may or may not be added to the previously melted charge the constituents of the charge are also subjected to the melting in an intimate mixture after they have been brought to the desired fineness.
Die durch die obenerwähnte Behandlung erzeugte tantalhaltige Schlacke kann darauf jedwedem geeigneten bekannten metallurgischen Verfahren unterworfen werden, um daraus das Tantal in Form eines handelsgängigen Erzeugnisses (als Metall, Legierung, Carbid oder Oxyd) zu entziehen.The tantalum-containing slag produced by the above-mentioned treatment may then be subjected to any suitable known metallurgical process in order to produce the tantalum in the form of a commercially available product (as metal, Alloy, carbide or oxide).
Claims (1)