DE435913C - Acid-proof putty - Google Patents
Acid-proof puttyInfo
- Publication number
- DE435913C DE435913C DESCH74712D DESC074712D DE435913C DE 435913 C DE435913 C DE 435913C DE SCH74712 D DESCH74712 D DE SCH74712D DE SC074712 D DESC074712 D DE SC074712D DE 435913 C DE435913 C DE 435913C
- Authority
- DE
- Germany
- Prior art keywords
- water glass
- solution
- acid
- putty
- barium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Säurefester Kitt. Gegenstand der Erfindung ist ein säurefester Kitt und ein Verfahren zur Herstellung des bei diesem Kitt benutzten Mittels zum Anrühren der Grundstoffe.Acid-proof putty. The invention relates to an acid-resistant putty and a method of manufacturing the mixing agent used in this putty of the raw materials.
Die bekannten säurefesten Kitte bestehen aus einer Grundlage von mehr oder weniger fein gemahlenem Quarz, Quarzit oder anderen säurefesten Gesteinsarten oder sonstigen Grundstoffen. Diese Grundstoffe enthalten; teils von Natur Beimengungen von Tonerde, Eisen, Kalk, Magnesia o. dgl., teils «erden solche Beimengungen absichtlich zugesetzt.. Diesc Grundstoffe werden mit einer Wasserglaslösung angerührt, deren Grädigkeit je nach der gewünschten $eschalfenheit des Kitts wechseln kann. Man erhält dann einen mehr oder weniger streichfähigen Kitt, der langsam abbindet und schließlich mit Säure ausgestrichen wird, um überschüssige oder nicht mit den Grundstoffen des Kitts in Reaktion getretene Alkalilauge, die bei der Dissoziation des Wasserglases entstanden ist, in leichter lösliche Salze überzuführen, die von der Inbetriebnahme der mit den Kitten verfügten oder ausgestrichenen Behälter o. dgl. durch Auswaschen mit Wasser oder verdünnten Säuren entfernt werden.The well-known acid-proof putties consist of a basis of more or less finely ground quartz, quartzite or other acid-fast rock types or other raw materials. These raw materials contain; partly natural admixtures of clay, iron, lime, magnesia or the like, in some cases such admixtures are deliberately grounded added .. These basic materials are mixed with a water glass solution, the Gravity can change depending on the desired flatness of the putty. You get then a more or less spreadable putty that sets slowly and finally Acid smeared to remove excess or not with the raw materials of the Putty reacts with alkali, which occurs during the dissociation of the water glass arose, to be converted into more soluble salts by the commissioning the container or the like with the putty or the like by washing it out can be removed with water or diluted acids.
Die in dieser Weise hergestellten Kitte zeigen alle den Nachteil, daß sich an der Oberfläche aus dem nicht mit den Grundstoffen in Reaktion getretenen Wasserglas eine feste Haut ausscheidet, die die weitere Verdunstung des im Kitt enthaltenen Wassers er-Schwert; hierdurch wird die Abbindezeit außerordentlich verlängert, so daß die Kitte manchmal noch nach 4. Wochen unter der Oberfläche weich und unverändert bleiben.The putties produced in this way all show the disadvantage that on the surface it has not come into reaction with the basic substances Water glass exudes a firm skin, which further evaporation of the putty contained water he-sword; this extends the setting time considerably, so that the putty sometimes remains soft and unchanged under the surface after 4 weeks stay.
Dieser übeistand wird gemäß der Erfindung dadurch vermieden, daß als Mittel zum Anrühren der Grundstoffe an Stelle einer einfachen Wasserglaslösung eine kolloidale Lösung benutzt wird, die Wasserglas, insbesondere Natronwasserglas, und Bariumhydroxyd enthält. Gewünschtenfalls können der Lösung noch geringe Mengen von organischen Hilfs-oder Schutzkolloiden zugesetzt werden.This support is avoided according to the invention in that as Means for mixing the raw materials instead of a simple water glass solution colloidal solution is used, the water glass, especially soda water glass, and Contains barium hydroxide. If desired, small amounts of can be added to the solution organic auxiliary or protective colloids are added.
Die Herstellung einer solchen Lösung geschieht in der Weise, daß man gleiche Volumina einer Wasserglaslösung, vorzugsweise einer Natronwasserglaslösung, von etwa 3¢ bis 36° B. und einer kalt ;gesättigten Bariumhydroxydlösung unter Kühlung und schnellem Umrühren miteinander mischt. Die Bariumhydroxydlösung darf keine sichtbaren Ausscheidungen von Bariunicarbonat enthalten. Bis zu etwa So Volumenprozent der Wasserglaslösung kann man ohne besondere Vorsichtsmaßregeln schnell zu der Bariumhydroxydlösung hinzufügen, ohne da.ß eine merkliche Trübung entsteht; es bildet sich höchstens eine opalisierende Lösung. Der Rest von etwa zo Volumenprozent muß dagegen sehr vorsichtig und langsam zugesetzt werden, um ein Ausflocken der Lösung zu vernieiden. Gänzlich vermieden kann eine solche Ausflockun:g werden, wenn man ganz geringe Mengen von organischen Hilfs- oder Schutzkolloiden, z. B. Eiweiß, Kasein, Leim, zusetzt.The preparation of such a solution is done in such a way that one equal volumes of a water glass solution, preferably a soda water glass solution, from about 3 ¢ to 36 ° B. and a cold, saturated barium hydroxide solution with cooling and rapid stirring together. The barium hydroxide solution must not be visible Contains excretions of barium carbonate. Up to about 50 percent by volume Waterglass solution can be quickly added to the barium hydroxide solution without special precautionary measures add without causing any noticeable cloudiness; at most it is formed an opalescent solution. The rest of about ten percent by volume, on the other hand, must be very high added carefully and slowly to avoid flocculation of the solution. Such flocculation can be avoided entirely if you use very little amounts of organic auxiliary or protective colloids, e.g. B. egg white, casein, glue added.
Wenn man mit einer solchen Lösung an' Stelle der einfachen Wasserglaslösung fein gemahlenes Quarzit oder einen der anderen vorher ;genannten Grundstoffe zu einem Kitt anrührt, so ergibt sich, daß man bei gleicher :Mahlfeinheit des Quarzits nur etwa die Hälfte bis 2/.; der bei gewöhnlicher Wassergla;slösung erforderlichen Menge des Grundstoffs braucht, um einen Kitt von .gleicher Konsistenz zu erhalten.If one uses such a solution instead of the simple water glass solution finely ground quartzite or one of the other raw materials mentioned above If you touch a putty, the result is that with the same: the fineness of the fineness of the quartzite only about half to 2 / .; that required with ordinary water glass solution Amount of the basic material needed to obtain a putty of the same consistency.
Die kolloidale Lösung wird durch den Quarzit schnell und gleichmäßig ausgeflockt, ohne dar die Ausflockung beim Ausstreichen des Kitts, insbesondere in den Fugen,, hinderlich ist. Natürlich darf man nicht allzu große Kittmengen auf einmal herstellen, sondern bei Normaltemperatur nur solche Mengen, die für einen Bedarf von etwa. 6 bis 8 Stunden ausreichen.The quartzite makes the colloidal solution quickly and evenly flocculated without causing the flocculation when spreading the putty, in particular in the joints ,, is a hindrance. Of course, you shouldn't apply too large amounts of putty produce once, but at normal temperature only those quantities that are for you Need of about. 6 to 8 hours are sufficient.
Die Abbindezeit des so hergestellten Kitts beträgt nur q. bis 8 Tage. Die Trocknung des Kitts erfolgt dabei in äußerst gleichmäßiger Weise durch die ganze Kittschicht hindurch, ohne daß sich die vorher erwähnte, bei den bisher üblichen Wasserglaskitten auftretende, die Verdunstung störende Haut bildet.The setting time of the putty produced in this way is only q. up to 8 days. The putty is dried in an extremely even manner throughout Putty layer through without affecting the previously mentioned one with the previously usual Water glass kitten forms skin that interferes with evaporation.
Die neuen Kitte haben auch noch den Vorzug .einer höheren Säurefestigkeit. Bei gleichen Prüfungsbedingungen verhalten sich die Säurefestigkeiten eines mit Natronwasserglas und eines mit der beschriebenen Bariumhydroxyd-Wasserglaslösung erhaltenen Kitts unter sonst gleichen Verhältnissen wie 1-2. d. h. bei den, mit Natronwasserglas hergestellten, Kitten löst sich bei dem Versuch eine doppelt so große Menge wie bei dem gemäß der Erfindung hergestellten. In dem Säureauszug läßt sich kein Barium nachweisen, es muß also in eine Säure unlösliches Silikat übergeführt worden sein. .The new putties also have the advantage of being more acid-resistant. If the test conditions are the same, the acid strengths behave with one another Soda water glass and one with the barium hydroxide water glass solution described obtained putty under otherwise the same conditions as 1-2. d. H. at the, with Soda waterglass made, putty dissolves twice as much when trying large amount as that made according to the invention. Leaves in the acid extract no barium can be detected, so it must be converted into an acid-insoluble silicate have been. .
Claims (2)